JPS60127973A - Preparation of polishing plate - Google Patents
Preparation of polishing plateInfo
- Publication number
- JPS60127973A JPS60127973A JP23450283A JP23450283A JPS60127973A JP S60127973 A JPS60127973 A JP S60127973A JP 23450283 A JP23450283 A JP 23450283A JP 23450283 A JP23450283 A JP 23450283A JP S60127973 A JPS60127973 A JP S60127973A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- polishing
- head
- onto
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(A)発明の技術分野
発明は、磁気ディスクの耐久性試験に用いる試験用へノ
ド等を研摩するための研摩板の製造方法に関する。DETAILED DESCRIPTION OF THE INVENTION (A) Technical Field of the Invention The present invention relates to a method for manufacturing a polishing plate for polishing test nodules and the like used in durability tests of magnetic disks.
(B)技術の背景
基板上に磁性記録層を設け、磁気的に情報の記録を行な
い又記録された情報の読取りを行う磁気ディスク(以下
ディスクという)に対し、この情報の記録や読取り時に
は、回転するディスク上に磁気ヘッド(以下ヘッドとい
う)を対向配置して、この磁性記録層に情報の記録や、
この磁性記録層から情報の読取りを行う。(B) Background of the technology Regarding magnetic disks (hereinafter referred to as disks), which have a magnetic recording layer on a substrate and magnetically record information and read recorded information, when recording and reading this information, A magnetic head (hereinafter referred to as a head) is placed facing the rotating disk, and information is recorded on this magnetic recording layer.
Information is read from this magnetic recording layer.
記録又は読取り操作中は、ヘッドは浮上してディスクと
は接触しないが、始動時や終了時又、障害発生時には、
ヘッドとディスクが接触することがある。During a recording or reading operation, the head flies and does not make contact with the disk, but when starting up, stopping, or when a failure occurs, the head flies up and does not make contact with the disk.
The head and disk may come into contact.
このため擬似ヘッドを用いてディスクの耐衝撃性の試験
が行われるが、この試験において、ディスクのみならす
擬似ヘッドにも損傷が生じ、以後の被験ディスクはこの
傷のために、損傷を受けやすい条件となり、耐衝撃性は
低く評価されることになる。For this reason, the impact resistance of the disk is tested using a pseudo head, but in this test, not only the disk but also the pseudo head is damaged, and subsequent test disks are subject to conditions that make them susceptible to damage due to this damage. Therefore, the impact resistance is evaluated to be low.
従って耐衝撃性試験において、損傷の生じたへノドを研
摩する必要が生じる。従来はこのようなヘッドを研摩す
ることは行われていなかった。Therefore, in the impact resistance test, it is necessary to polish the damaged hemlock. Conventionally, such heads have not been polished.
(D)発明の目的
本発明ばかがる点に鑑みなされたものでヘッドに生じる
微少な凹凸をも研摩により平滑化し得る研摩板の製造方
法を提供することを目的とする。(D) Object of the Invention An object of the present invention was to provide a method of manufacturing a polishing plate that can smooth even minute irregularities occurring on a head by polishing.
(E)発明の構成
そしてこの目的は本発明によれば、研摩粒子とバインダ
の混合物の塗布層を基板上に形成した後、該塗布層を固
化せしめ、該塗布層に潤滑剤を塗布するようにしたこと
を特徴とする研摩板の製造方法を提供することによって
達成される。(E) Structure and object of the invention According to the present invention, after forming a coating layer of a mixture of abrasive particles and a binder on a substrate, the coating layer is solidified and a lubricant is applied to the coating layer. This is achieved by providing a method for manufacturing an abrasive plate characterized by the following.
(F)発明の実施例 以下図面を参照して本発明の実施例を詳述する。(F) Examples of the invention Embodiments of the present invention will be described in detail below with reference to the drawings.
アルミナ粒子を熱可塑性樹脂又は熱硬化性樹脂およびシ
ンナーに混入して混練し、これを円板状の基板13にス
ピンコードによって、一定の層厚の層、Jを形成し、焼
成する。Alumina particles are mixed and kneaded with a thermoplastic resin or a thermosetting resin and a thinner, and a layer J having a constant thickness is formed on a disc-shaped substrate 13 using a spin cord, and then fired.
樹脂組成は、エポキシ樹脂50体積%、フェノール樹脂
30体積%、メラミン樹脂20体積%であり、アルミナ
粒子は、30体積%である。The resin composition was 50% by volume of epoxy resin, 30% by volume of phenol resin, 20% by volume of melamine resin, and 30% by volume of alumina particles.
焼成条件は200℃で1時間である。The firing conditions were 200° C. for 1 hour.
熱硬化性樹脂又は熱可塑性樹脂はバインダとしての機能
を果し、シンナーは溶剤として用いられる。焼成工程完
了後、樹脂層上面に弗素系潤滑剤F(例えばクライトノ
クスコ商品名)を塗布する。The thermoset or thermoplastic resin serves as a binder and the thinner is used as a solvent. After the firing process is completed, a fluorine-based lubricant F (for example, Krytonoxco brand name) is applied to the upper surface of the resin layer.
この潤滑剤は樹脂層Jに含浸する。This lubricant is impregnated into the resin layer J.
図面は、このようにして製造された研摩円板の断面図で
あって、アルミ基板B上に形成された樹脂NJにアルミ
ナ粒子N、、N2.N3−−−が、混在する。The drawing is a cross-sectional view of the abrasive disk manufactured in this manner, in which alumina particles N, N2, . N3--- is mixed.
アルミナ粒子N、、N2.N5−−−−は、その粒径に
より、樹脂層J中に埋没しているものもあり、又、粒子
の一部分が露出しているものもある。Alumina particles N,, N2. Depending on the particle size, some of the N5 particles are buried in the resin layer J, and some of the particles are partially exposed.
樹脂1ifJ表面、および露出したアルミナ粒子表面に
は潤滑剤膜Fが形成され7riJ滑剤としての役割を果
たす。A lubricant film F is formed on the resin 1ifJ surface and the exposed alumina particle surface and serves as a 7riJ lubricant.
ヘッドの研摩時には、アルミナ粒子の樹脂層、Jからの
露出部分がヘッドの凹凸部分と係触して研削して凹凸部
分を平滑面とする。この場合、潤滑剤層Fがあるため被
研摩へノドにおおきな損傷を与えることはなく、また、
この表面に表われた潤滑剤が研摩中に消失しても、樹脂
NJ中に含浸した潤滑剤が樹脂rJJ表面に、にじみ出
るため、樹脂層5表面ば常に潤滑剤層Fで覆われること
になる。When polishing the head, the exposed portions of the alumina particles from the resin layer J come into contact with the uneven portions of the head and are ground to make the uneven portions into smooth surfaces. In this case, since there is a lubricant layer F, there will be no major damage to the throat to be polished, and
Even if the lubricant appearing on the surface disappears during polishing, the lubricant impregnated in the resin NJ oozes out onto the surface of the resin rJJ, so the surface of the resin layer 5 is always covered with the lubricant layer F. .
(G)発明の効果
このように本発明に係る研摩板の製造方法は、磁気ヘッ
ドに生しる微少な凹凸を含む損傷の研摩に必要な微細な
突起を有する研摩面を形成できるので磁気ディスクの耐
摩耗性試験に用いるへ・ノドの研摩板製造に有用である
。(G) Effects of the Invention As described above, the method for manufacturing an abrasive plate according to the present invention can form a polishing surface having minute protrusions necessary for polishing damage including minute irregularities that occur on a magnetic head. It is useful for manufacturing abrasive plates for edges and throats used in abrasion resistance tests.
図は本発明に係る研摩板の断面図である。 B:基板、J:樹脂層、F:潤滑剤層、N、。 N2.N3−’−:アルミナ粒子。 「 \ ( The figure is a sectional view of a polishing plate according to the present invention. B: substrate, J: resin layer, F: lubricant layer, N. N2. N3-'-: Alumina particles. " \ (
Claims (3)
に形成した後、該塗布層を固化せしめ、該塗布層に潤滑
剤を塗布するようにしたことを特徴とする研摩板の製造
方法。(1) A method for manufacturing an abrasive plate, comprising: forming a coating layer of a mixture of abrasive particles and a binder on a substrate, solidifying the coating layer, and applying a lubricant to the coating layer. .
あるごとを特徴とする特許請求の範囲第(I)項に記載
の研摩板の製造方法。(2) The method for manufacturing an abrasive plate according to claim (I), wherein the binder is a thermosetting resin or a thermoplastic resin.
る特許請求の範囲第(1)項又は第(2)項に記載の研
摩剤の製造方法。(3) The method for producing an abrasive according to claim (1) or (2), wherein the lubricant is a fluorine-based lubricant.