JPS60106864A - Paint which prevents trace of sticked paper from remaining - Google Patents
Paint which prevents trace of sticked paper from remainingInfo
- Publication number
- JPS60106864A JPS60106864A JP18851884A JP18851884A JPS60106864A JP S60106864 A JPS60106864 A JP S60106864A JP 18851884 A JP18851884 A JP 18851884A JP 18851884 A JP18851884 A JP 18851884A JP S60106864 A JPS60106864 A JP S60106864A
- Authority
- JP
- Japan
- Prior art keywords
- paint
- parts
- weight
- wax
- silicone oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
本発明は、建造物に貼付けられた貼紙が容易に剥離でき
、かつその痕跡をとどめない貼紙痕跡防止用塗料に関す
るものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a paint for preventing stickers from being pasted on buildings, which can be easily peeled off and do not leave any traces.
電柱、街灯柱、配電塔、歩道橋、橋脚、門扉等の建造物
に貼付けられた広告、宣伝ビラ等の貼紙は、美観を損な
うばかりでなく、これを剥離するための人手及び費用も
莫大なものになる。しかも、貼紙の痕跡を残さずに完全
に剥離することは困難で一部分貼紙が貼付けられたま\
であることが多い。Advertisements, promotional flyers, etc. pasted on utility poles, lampposts, distribution towers, pedestrian bridges, bridge piers, gates, and other structures not only detract from the aesthetics, but also require a huge amount of labor and expense to remove them. become. Moreover, it is difficult to remove the sticker completely without leaving traces of the sticker, so some parts of the sticker remain attached.
Often.
そこで、本発明者等は、貼紙が貼付けられても容易に剥
離でき、かつ貼紙の痕跡を残さないような塗料を検討し
た結果、本発明に到達した。即ち、本発明は、特定の常
温乾燥形塗料中の樹脂分100重量部に対しシリコンオ
イルおよび(または)ワックスを10〜70重量部添加
してなる貼紙痕跡防止用塗料に関するものである。Therefore, the present inventors investigated a paint that can be easily peeled off even if a sticker is pasted and does not leave traces of the sticker, and as a result, the present invention was achieved. That is, the present invention relates to a paint for preventing pasting marks, which is made by adding 10 to 70 parts by weight of silicone oil and/or wax to 100 parts by weight of the resin in a specific room-temperature-drying paint.
本発明は、建造物に従来から塗装されている特定の常温
乾燥形塗料にシリコンオイルおよび(または)ワックス
を添加して目的を達成したのである。シリコンオイルお
よび(または)ワックスの添加量は常温乾燥形塗料の樹
脂分100重量部に対して10〜70重量部の範囲であ
る。添加量が10重量部より少ないと貼紙痕跡防止に顕
著な効果を呈さず、70重量部をこえると塗料との相溶
性が悪くなるので好ましくない。従来、塗料分野におい
てシリコンオイルあるいはワックスを添加剤に用いる場
合、塗料の色分れ防止剤、塗膜の表面平滑調整剤等を意
図して使用されているが、その添加量はせいぜい塗料中
に数重量%以下である。The present invention achieves this objective by adding silicone oil and/or wax to certain room temperature drying paints that are conventionally applied to buildings. The amount of silicone oil and/or wax added is in the range of 10 to 70 parts by weight based on 100 parts by weight of the resin content of the paint that dries at room temperature. If the amount added is less than 10 parts by weight, it will not have a significant effect on preventing paper sticker marks, and if it exceeds 70 parts by weight, the compatibility with the paint will deteriorate, which is not preferable. Conventionally, when silicone oil or wax is used as an additive in the paint field, it is intended to be used as a color separation prevention agent for paints, a surface smoothing agent for paint films, etc. It is several percent by weight or less.
一方、本発明ではシリコンオイルあるいはワックスの添
加量を大幅に増すことで予期せぬ効果がもたらされた。On the other hand, in the present invention, an unexpected effect was brought about by significantly increasing the amount of silicone oil or wax added.
ワックスとしては、流動パラフィン、ポリエチレンワッ
クス等、溶液状のものが使用される。As the wax, liquid paraffin, polyethylene wax, or the like is used.
本発明に用いる特定の常温乾燥形塗料とは、アクリルラ
ッカー、ニトロセルロースラッカー、アクリルエマルジ
巨ン塗料およびエポキシエマルジョン塗料から選ばれた
塗料である。The specific room temperature drying paint used in the present invention is a paint selected from acrylic lacquers, nitrocellulose lacquers, acrylic emulsion coatings and epoxy emulsion coatings.
本発明の貼紙痕跡防止用塗料は、上述の常温乾燥形塗料
とシリコンオイルおよび(または)ワックスとを十分撹
拌し均一に分散させてから、建造物に通常の刷毛塗り、
ローラー塗装、スプレー塗装等で塗装する。The paint for preventing pasting marks of the present invention is produced by thoroughly stirring the above-mentioned room-temperature-drying paint, silicone oil, and/or wax to uniformly disperse the paint, and then applying it to a building using a normal brush.
Paint by roller painting, spray painting, etc.
本発明では、シリコンオイルおよび(または)ワックス
を特定量塗料に添加することにより、得られた塗膜に、
貼紙が貼付されても剥離作業が容易でかつ貼紙の痕跡も
残らない。このため1本発明は市街の美観保護に貢献す
るところが大である。In the present invention, by adding a specific amount of silicone oil and/or wax to the paint, the resulting paint film has
Even if a sticker is pasted, peeling work is easy and no trace of the sticker remains. Therefore, the present invention greatly contributes to preserving the aesthetic appearance of the city.
以下、本発明を実施例および比較例により説明する。The present invention will be explained below with reference to Examples and Comparative Examples.
失族孤エ
アルミニウム板に[メタラクトH−5J(関西ペイント
■製部品名、金属前処理塗料)を塗装し。[Metalact H-5J (part name manufactured by Kansai Paint ■, metal pre-treatment paint) was applied to the aluminum plate.
2時間弊燥後、次いでシリコンKF356 (信越化学
■製部品名、シリコンオイル)を樹脂分100重量部に
対し30重量部添加した「アクリツクNα2000J
(関西ペイント@製部品名、アクリルラッカー)を20
μの乾燥膜厚になるようにスプレー塗装し、−週間乾燥
させた。After drying for 2 hours, 30 parts by weight of silicone KF356 (part name manufactured by Shin-Etsu Chemical, silicone oil) was added to 100 parts by weight of the resin.
(Kansai Paint @ part name, acrylic lacquer) 20
It was spray coated to a dry film thickness of μ and allowed to dry for - weeks.
次に、該塗面に市販の洗濯糊を塗布してから模造紙を貼
付した。そして貼付後の経時口゛数により模造紙の剥離
試験を行なった。その結果を表1に示す。Next, commercially available laundry glue was applied to the coated surface, and then imitation paper was attached. A peel test of the imitation paper was then conducted based on the number of openings over time after application. The results are shown in Table 1.
実施例2
亜鉛鉄板に「メタラクトH−5」を塗装し、2時間乾燥
後、次いで、シリコンKF−362<信越化学(lI製
製品品名シリコンオイル)および流動パラフィンを樹脂
分100重量部に対して、それぞれ10重量部および2
0重量部添加した「セル列Nα1000クリーム」 (
関西ペイント曲順商品名、ニトロセルロースラッカー)
を20μの乾燥膜厚になるようにスプレー塗装し、1週
間乾燥させた。Example 2 "Metalact H-5" was painted on a galvanized iron plate, and after drying for 2 hours, silicone KF-362 < Shin-Etsu Chemical (product name silicone oil manufactured by II) and liquid paraffin were applied to 100 parts by weight of resin. , 10 parts by weight and 2 parts by weight, respectively
"Cell row Nα1000 cream" with 0 parts by weight added (
Kansai Paint song order product name, nitrocellulose lacquer)
was spray-painted to a dry film thickness of 20μ and dried for one week.
次に、該塗面に市販の洗濯糊を塗布してから模造紙を貼
付した。そして、貼付後の経時日数により模造紙の剥離
試験を行なった。その結果を表1に示す。Next, commercially available laundry glue was applied to the coated surface, and then imitation paper was attached. Then, a peel test of the imitation paper was conducted based on the number of days after pasting. The results are shown in Table 1.
実施例3
コンクリートモルタル面に「マルタイルコンクリートプ
ライマー」 (関西ペインI−開製商品名、エポキシ樹
脂系下塗塗料)を100 g/rr?の割合で塗装し、
24時間乾燥させた。次いで、「マルチタイルラフRE
J (関西ペイント@製商品名、エポキシ樹脂エマルシ
ョン系中塗塗料)を1.0〜1 、3 kg / rd
の割合で、吹付ガン凹凸模様になるように塗装し、24
時間乾燥させた。さらに、シリコンKF362および流
動パラフィンを樹脂分100重量部に対し、それぞれ3
0重量部および20重量部添加した「エボマリンWJ
(関西ペイント@製部品名、エポキシ樹脂エマルション
系塗料)を200 g/rrrの割合でローラーで塗装
し、1週間乾燥させた。Example 3 Apply 100 g/rr of "Multile Concrete Primer" (Kansai Pain I - Kaisei product name, epoxy resin undercoat paint) to the concrete mortar surface. Paint at a ratio of
It was dried for 24 hours. Next, “Multi-tile rough RE
J (product name manufactured by Kansai Paint@, epoxy resin emulsion intermediate coating paint) 1.0 to 1.3 kg/rd
Paint with a spray gun to create an uneven pattern at a ratio of 24
Let dry for an hour. Furthermore, 3 parts of silicone KF362 and liquid paraffin were added to each 100 parts by weight of the resin.
"Evo Marine WJ" added 0 parts by weight and 20 parts by weight
(Part name manufactured by Kansai Paint@, epoxy resin emulsion paint) was applied with a roller at a rate of 200 g/rrr and allowed to dry for one week.
次に、該塗膜に市販の洗濯糊を塗布してから模造紙を貼
付した。そして貼付後の系時日数による模造紙の剥離試
験を行なった。その結果を表1に示す。Next, a commercially available laundry glue was applied to the coating film, and then imitation paper was attached. Then, a peel test of the imitation paper was conducted depending on the number of hours and days after pasting. The results are shown in Table 1.
実施例4
コンクリートモルタル面に「グロスターシーラー」(関
西ペイント■製部品名、アクリル樹脂エマルション系下
塗塗料)を約100 g/rdの割合で塗布し、4時間
乾燥した。次に、流動パラフィンを樹脂分100重量部
に対し、20重量部添加したグロスター(関西ペイント
@製部品名、アクリル樹脂エマルジョン系上塗塗料)を
180〜200g/ボの割合でローラ塗装し、1週間乾
燥した。Example 4 "Gloster Sealer" (part name manufactured by Kansai Paint ■, acrylic resin emulsion-based undercoat paint) was applied to the concrete mortar surface at a rate of about 100 g/rd and dried for 4 hours. Next, Gloster (part name manufactured by Kansai Paint@, acrylic resin emulsion-based topcoat paint) containing 20 parts by weight of liquid paraffin per 100 parts by weight of resin was applied with a roller at a rate of 180 to 200 g/bo for one week. Dry.
次に、模造紙に接着剤フジカラーボンドL(フジカラー
販売社製商品名)を塗布し、このものを上記塗面に貼付
した。そして、貼付後の経時日数により模造紙の剥離試
験を行なった。その結果を表1に示す。Next, adhesive Fuji Color Bond L (trade name, manufactured by Fuji Color Sales Co., Ltd.) was applied to the imitation paper, and this was attached to the above-mentioned painted surface. Then, a peel test of the imitation paper was conducted based on the number of days after pasting. The results are shown in Table 1.
比較例1
実施例1において、シリコンKP356を樹脂分100
重量部に対し5重量部添加したアクリツクNα2000
を用いた以外は実施例1と同様に行なった。試験結果は
表1に示す。Comparative Example 1 In Example 1, the resin content of silicon KP356 was 100.
Acryk Nα2000 added 5 parts by weight to parts by weight
The same procedure as in Example 1 was conducted except that . The test results are shown in Table 1.
表 1
試験方法
塗面に貼付された貼紙を、何回も手でこすりつけた後、
常温の実験室内に静置した。そして、経過日数毎に手で
剥がし、剥がした後の塗面状態を観察した。Table 1 Test method After rubbing the sticker affixed to the painted surface by hand many times,
It was left standing in a laboratory room at room temperature. Then, it was removed by hand every few days, and the condition of the coated surface after removal was observed.
評価基準 O:容易に剥がれ痕跡を認めない。Evaluation criteria O: No traces of easy peeling observed.
O:痕跡を認めない。O: No traces observed.
◎:貼紙が一部分付着している。◎: Part of the sticker is attached.
△:貼紙が半分程度付着している。△: Approximately half of the sticker was attached.
×:殆んど剥離できず紙の大部分がイ」着している。×: Almost no peeling was possible and most of the paper was stuck.
Claims (1)
塗料から選ばれた常温乾燥形塗料中の樹脂分100重量
部に対しシリコンオイルおよび(または)ワックスを1
0〜70重量部添加してなる貼紙痕跡防止用塗料。[Claims] Acrylic lacquer, nitrocellulose lacquer. Add 1 part of silicone oil and/or wax to 100 parts by weight of resin in a room temperature drying paint selected from acrylic emulsion paint and epoxy emulsion paint.
A paint for preventing paper affixation marks by adding 0 to 70 parts by weight.