JPS59150186A - Coloring of water repellent cloth - Google Patents

Coloring of water repellent cloth

Info

Publication number
JPS59150186A
JPS59150186A JP58025250A JP2525083A JPS59150186A JP S59150186 A JPS59150186 A JP S59150186A JP 58025250 A JP58025250 A JP 58025250A JP 2525083 A JP2525083 A JP 2525083A JP S59150186 A JPS59150186 A JP S59150186A
Authority
JP
Japan
Prior art keywords
water
repellent
parts
colored
paste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP58025250A
Other languages
Japanese (ja)
Inventor
弘 北村
安藤 「けい」一
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Industries Inc
Original Assignee
Toray Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Industries Inc filed Critical Toray Industries Inc
Priority to JP58025250A priority Critical patent/JPS59150186A/en
Publication of JPS59150186A publication Critical patent/JPS59150186A/en
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 本発明は撥水性布帛、特に撥水加工された布帛に対して
1面」人件ならびに鮮明性のすぐれた着色模様を付力す
る方法に関する。
DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for imparting a colored pattern with excellent appearance and sharpness on one side to a water-repellent fabric, particularly a water-repellent fabric.

近年、撥水性布帛が雨具の他にスポーツ衣料。In recent years, water-repellent fabrics have been used not only for rain gear but also for sports clothing.

防寒衣料5作業衣料すどの分野にも広く適用されるよう
になった。かかる衣料の模様づけ、特にマーキングなと
は通常後加工により付与されるものである。しかしかか
る撥水性布帛、特に撥水加工された布帛に着色糊を印捺
しても、撥水性のために布帛に糊がのりに<<1%に水
性糊では模様が形成せず、たとえ着色しても離脱し易い
もので実用にならないなどの問題があった。
It has come to be widely applied in all fields, including cold weather clothing and work clothing. Patterns, especially markings, on such clothing are usually applied through post-processing. However, even if colored paste is printed on such water-repellent fabrics, especially fabrics that have been treated with water-repellent, water-based glue will not form a pattern if the glue is applied to the fabric at <<1% due to water repellency, and even if colored However, there were problems such as the fact that it was easy to separate, making it impractical.

かかる技術的背景に鑑み、撥水性布帛に耐久性ある着色
を達成する技術について検討したところ。
In view of this technical background, we investigated a technology to achieve durable coloring of water-repellent fabric.

特定な化合物を介して化学的に着色材料を固着すること
により、すぐれた鮮明性と耐久性を達成し得ることを究
明し9本発明に到達した。
The present invention was achieved by discovering that excellent clarity and durability can be achieved by chemically fixing a colored material through a specific compound.

すなわち1本発明は次のような構成を有する。That is, one aspect of the present invention has the following configuration.

「撥水性布帛の表面に9重合性ビニル基含有化合物層を
介して着色材料ならびに撥水剤を固着することを特徴と
する撥水性布帛の着色法。」本発明はかかる技術構成を
採用したことにより。
"A method for coloring a water-repellent fabric, which is characterized by fixing a coloring material and a water-repellent agent to the surface of the water-repellent fabric via a layer of a 9-polymerizable vinyl group-containing compound."The present invention employs such a technical configuration. By.

初めて撥水性布帛に鮮明で、かつ耐久性にすぐれた着色
模様を安定して伺与せしめ得だものである。
This is the first time that a water-repellent fabric can stably produce a clear and durable colored pattern.

本発明の撥水性布帛とは、水に対してぬれ性を有さない
ものであって2通常撥水剤により加工された布帛である
。たとえばシリコン系撥水剤やフッ素系撥水剤で加工さ
れた布帛があげられる。
The water-repellent fabric of the present invention is a fabric that does not have wettability with water and is usually treated with a water-repellent agent. Examples include fabrics treated with silicone-based water repellents or fluorine-based water repellents.

本発明は重合性ビニル基含有化合物がかかる撥水剤とぬ
れ性ならびに反応性にすぐれていることを究明し、かか
る化合物に着目した着色方法を完成したものである。
The present invention has revealed that polymerizable vinyl group-containing compounds have excellent wettability and reactivity with such water repellents, and has completed a coloring method that focuses on such compounds.

かかる重合性ビニル基含有化合物としては、たとえばア
クリル酸、メタクリル酸、アクリル酸メチル、メタクリ
ル酸ブチル、アクリルアミド、メタクリルアミド、N−
メチロールアクリルアミドなどのアクリル酸系化合物、
アクリロニトリル。
Examples of such polymerizable vinyl group-containing compounds include acrylic acid, methacrylic acid, methyl acrylate, butyl methacrylate, acrylamide, methacrylamide, N-
Acrylic acid compounds such as methylol acrylamide,
Acrylonitrile.

酢酸ビニル、塩化ビニル、プロピオン酸ビニル。Vinyl acetate, vinyl chloride, vinyl propionate.

カプロン酸ビニル、メチルビニルエーテル、ブチルビニ
ルエーテル、スチレンおよびこれらの誘導体などがある
が、さらに重合性ビニル基を含有するものであれば上記
以外のものでも本発明に適用することができる。
Examples include vinyl caproate, methyl vinyl ether, butyl vinyl ether, styrene, and derivatives thereof, but substances other than the above may also be applied to the present invention as long as they further contain a polymerizable vinyl group.

かかる化合物は撥水性布帛の表面(内外部)で樹脂化さ
れ被膜を形成する性能を有するが、さらに膜性能として
接着性、柔軟性、耐候性、耐薬品性などが要求される。
Such a compound has the ability to be converted into a resin and form a film on the surface (inside and outside) of a water-repellent fabric, but further film properties such as adhesion, flexibility, weather resistance, and chemical resistance are required.

かかる膜性能の点から上記化合物を選択する必要がある
が、なかでもアクリル酸系化合物、特にアクリル酸アル
キルエステルが好ましく適用される。
It is necessary to select the above-mentioned compounds from the viewpoint of membrane performance, and among them, acrylic acid compounds, particularly acrylic acid alkyl esters, are preferably used.

かかる化合物は自つ−独で適用するよりも2種以上併用
することにより、より膜性能のすぐれたものを与える特
徴がある。たとえば弾性や柔軟性改善にはスチレンやア
クリロニトリルなどを、膜強度改善にはN−メチロール
アミドなどを配合する。
Such compounds have the characteristic that when used in combination, two or more of these compounds provide better membrane performance than when applied individually. For example, styrene or acrylonitrile is added to improve elasticity and flexibility, and N-methylolamide is added to improve membrane strength.

かかる物性改善のために配合される化合物はそれぞれ0
5〜5重量係、世上しくは1〜3重量係世上で十分であ
る。
Each of the compounds added to improve physical properties is 0.
A weight ratio of 5 to 5, preferably 1 to 3, is sufficient.

本発明でいう重合性ビニル基含有化合物は特にアクリル
酸系化合物、々かでもアクリル酸アルキルエステルを主
成分とする該化合物の併用組成のものが最適である。
The polymerizable vinyl group-containing compound referred to in the present invention is particularly an acrylic acid compound, and the most suitable one is a combination composition of such a compound having an acrylic acid alkyl ester as a main component.

本発明ではかかる化合物の他に該被膜の性能ならびに接
着性の改善のために架橋剤として通常の多官能性化合物
、たとえばトリアジン環含有化合物、尿素系化合物、ウ
レタン(インシアネート)系化合物、なかでもメラミン
系化合物で代表されるトリアジン環含有化合物を配合す
るのが好ましい。かかる架橋剤は少量でよく、01〜5
重量俸好ましくは05〜3重量係程世上合すればよい。
In addition to such compounds, in the present invention, common polyfunctional compounds such as triazine ring-containing compounds, urea compounds, urethane (incyanate) compounds, among others, are used as crosslinking agents to improve the performance and adhesion of the coating. It is preferable to blend a triazine ring-containing compound such as a melamine compound. Such a crosslinking agent may be used in a small amount, and 01 to 5
The weight salary should preferably match the 05 to 3 weight range.

以上本発明の重合性ビニル基含有化合物層について説明
したが1本発明の上記化合物は界面活性剤により水に浮
化分散し、それにエマルジョン糊を配合して印捺される
The polymerizable vinyl group-containing compound layer of the present invention has been described above. First, the compound of the present invention is floated and dispersed in water using a surfactant, and an emulsion paste is added thereto for printing.

かかる界面活性剤としてはアニオン系、非イオン系のも
のが適用できるが、非イオン系界面活性剤が液安定性の
点から好ましい。かかる非イオン系界面活性剤のなかで
も親水性であるものが好ましい。非イオン系界面活性剤
の親油性と親水性はH,L、Bイ直 (Hydroph
ile  Lipophile  Ba1ance  
)   で表され、数値の小さ−い(最小−〇)ものほ
ど親油性で、数値の大きい(最大−20)ものほど親水
性であるが9本発明においてはかかるH、L、B、が少
なくとも10以上、好ましくは12〜18である非イオ
ン系界面活性剤が好ましい。
Although anionic and nonionic surfactants can be used as such surfactants, nonionic surfactants are preferred from the viewpoint of liquid stability. Among such nonionic surfactants, those that are hydrophilic are preferred. The lipophilicity and hydrophilicity of nonionic surfactants are H, L, and B (Hydroph).
ile Lipophile Ba1ance
), the smaller the numerical value (minimum -○), the more lipophilic it is, and the larger the numerical value (maximum -20), the more hydrophilic.9 In the present invention, such H, L, B are at least Nonionic surfactants with a molecular weight of 10 or more, preferably 12 to 18 are preferred.

かかるH、L、B、値を有する非イオン系界面活性剤は
単独の活性剤でも、2種以上の活性剤の併用で H,I
4.B、値を調整した混合活性剤であってもよい。かか
る界面活性剤により得られる水中油型浮れているととも
に水洗が容易である。
A nonionic surfactant having such H, L, B values can be used alone or in combination of two or more to achieve H, I
4. B. Mixed active agents with adjusted values may be used. The oil-in-water type obtained by such surfactants is floating and easy to wash with water.

かかる界面活性剤は1〜6重量%、好ましくは2〜6重
量%配合することにより、十分な浮化分散液を形成する
Such a surfactant can be incorporated in an amount of 1 to 6% by weight, preferably 2 to 6% by weight, to form a sufficient floating dispersion.

かかる非イオン系界面活性剤としては、たとえばポリエ
チレングリコールアルキルエーテル、ホリエチレングリ
コールアルキルフェニルエーテル。
Examples of such nonionic surfactants include polyethylene glycol alkyl ether and polyethylene glycol alkyl phenyl ether.

ポリエチレングリコール脂肪酸エステル、ポリエチレン
グリコールアルキルアミンなどのエチレンオキサイド付
加物が好適であるが、これ以外の非イオン系界面活性剤
を用いてもさしつがえない。
Ethylene oxide adducts such as polyethylene glycol fatty acid ester and polyethylene glycol alkylamine are preferred, but other nonionic surfactants may also be used.

かかる浮化分散液はエマルジョン糊で印捺に適した粘度
に調整される。
The viscosity of such a floated dispersion is adjusted to be suitable for printing using an emulsion paste.

かかるエマルジョン糊とは、ヘプタン、オクタン、ミイ
・ラルターペン2石油ベンジン、灯油、テレピン油など
の疎水性有機溶剤を、上記非イオン系界面活性剤を用い
て水に浮化した品粘度水中油型エマルジョンである。こ
のエマルジョン糊の使用量は使用粘度によって適宜増減
することができる。
Such an emulsion paste is an oil-in-water emulsion made by suspending a hydrophobic organic solvent such as heptane, octane, petroleum benzene, kerosene, or turpentine in water using the above-mentioned nonionic surfactant. It is. The amount of emulsion glue used can be increased or decreased as appropriate depending on the viscosity used.

かくして得られる処理糊(A)には、さらに必要に応じ
て重合開始剤、保護コロイド剤2分散助剤などが配合さ
れる。かかる処理糊(A)は重合性ビニル基含有化合物
の固形分で5〜60重量係の世上量であるのが、接着性
、風合の点から選択される。
The treated paste (A) thus obtained may further contain a polymerization initiator, a protective colloid agent, a dispersion aid, and the like, if necessary. The treated paste (A) is selected from the viewpoint of adhesion and texture, with a nominal amount of 5 to 60% by weight based on the solid content of the polymerizable vinyl group-containing compound.

次に着色材料について説明する。Next, the coloring material will be explained.

本発明の着色相和とは主として血判であるが。The color harmony of the present invention mainly refers to blood test.

必要に応じて染料を用いてもよい。A dye may be used if necessary.

かかる着色材料を上記非イオン系界面活性剤05〜6重
世上、好ましくは1〜4重量係世上に分散する。分散は
ボールミルやロールミル、サンドミル、アトライターな
どの方法により十分練肉するのが望ましい。
Such a coloring material is dispersed over 05 to 6 weight percent of the above-mentioned nonionic surfactant, preferably 1 to 4 weight percent. For dispersion, it is desirable to sufficiently knead the material using a ball mill, roll mill, sand mill, attritor, or other method.

この分散液に、前記処理糊(A)と同様に1重合性ビニ
ル基含有化合物からなる浮化分散液とエマルジョン糊を
配合して着色糊(B)を調合する。
A floating dispersion composed of a monopolymerizable vinyl group-containing compound and an emulsion paste are added to this dispersion to prepare a colored paste (B) in the same manner as the treated paste (A).

配合される重合性ビニル基含有化合物の浮化分散液は該
化合物の固型分で1〜10重量係、世上しくけ3〜8重
量係世上囲に調整するのが、接着性、柔軟性など膜性能
の点から好ましい。
The floating dispersion of the polymerizable vinyl group-containing compound to be blended should be adjusted to a solid content of 1 to 10% by weight, or 3 to 8% by weight, depending on adhesiveness, flexibility, etc. Preferable from the viewpoint of membrane performance.

着色糊(B)も印捺に適する粘度を有することが要求さ
れるが、かかる粘度は処理糊(A)と同様にエマルジョ
ン糊で調整する。かかる粘度はロータリースクリーン方
式、オートスクリーン方式、ノ・ンド方式などの各種プ
リント方式によって異なるので適宜選択すべきである。
The colored paste (B) is also required to have a viscosity suitable for printing, but this viscosity is adjusted by the emulsion paste in the same way as the treated paste (A). The viscosity varies depending on various printing methods such as rotary screen method, auto screen method, and no-end method, so it should be selected appropriately.

着色糊(B)において、撥水性布帛が染色品である場合
は着色模様が不鮮明になる傾向があり、その場合は隠ぺ
い剤、たとえば酸化チタン、亜鉛華などを併用すること
に、1.極めて鮮明な着色模様を付与することができる
In the colored paste (B), if the water-repellent fabric is a dyed product, the colored pattern tends to become unclear. An extremely clear colored pattern can be provided.

上記処理糊(A)ならびに着色糊(B)は、それぞれ別
別の工程で撥水性布帛に付与するが、必要に応じて両者
を混用して1工程で何カしてもさしつかえない。
The treated paste (A) and the colored paste (B) are applied to the water-repellent fabric in separate steps, but if necessary, they may be used in combination to apply any number of them in one step.

かかる糊は該布帛に何カされた後乾燥される。The glue is applied to the fabric and then dried.

必要に応じて1ろ0℃以上の熱処理を適宜施してもさし
つかえないが、接着性、柔軟性などの点から、該熱処理
は後述する撥水剤を何カした後で行なうのが好ましい。
If necessary, heat treatment at temperatures of 1-0° C. or higher may be carried out, but from the viewpoint of adhesion, flexibility, etc., it is preferable to carry out the heat treatment after applying a water repellent agent to be described later.

したがってそれまでの処理は乾燥する程度にとどめる。Therefore, the treatment up to that point is limited to drying.

特にその乾燥も重合性ビニル基含有化合物の反応を起こ
さない条件を選択するのが好ましいが、工業的には10
0〜120℃の乾燥条件が採用される。
In particular, it is preferable to select drying conditions that do not cause a reaction of the polymerizable vinyl group-containing compound, but industrially
Drying conditions of 0-120°C are employed.

かくすることにより、後の熱処理段階で処理糊(A)中
の該化合物と着色糊(B)中の該化合物とがほぼ同時に
反応を開始し9両者を一体的に固着する。
By doing so, in the subsequent heat treatment step, the compound in the treated paste (A) and the compound in the colored paste (B) start reacting almost simultaneously, 9 and fix them together.

この反応は該糊(A)・(B)をサンドインチしている
撥水剤をも同時に攻撃する。かくして得られる着色布帛
は着色材Elが上記反応の結果生成される被膜により一
体的に強力に固着されているものである。
This reaction simultaneously attacks the water repellent agent sandwiching the pastes (A) and (B). The colored fabric thus obtained has the coloring material El strongly fixed integrally with the coating formed as a result of the above reaction.

かかる固着効果をさらに望む場合には2着色糊(B)を
何カした後に、さらに処理糊(A)を再度付与する。こ
れによりアンカー効果がさらに増大し、一体的固着は極
めて強くなり、11it久性は著しく向上する。このア
ンカー効果は第1層目の重合性ビニル基含有化合物の量
より多いほうが大きくなる。
If such a fixing effect is further desired, after applying several coats of the two-colored glue (B), the treated glue (A) is applied again. This further increases the anchoring effect, makes the integral fixation extremely strong, and significantly improves the 11it durability. This anchor effect becomes greater when the amount of the polymerizable vinyl group-containing compound is greater than that of the first layer.

本発明は最後に、該印捺部の耐久性を付与するだめに、
撥水剤含有糊を印捺部に伺与する。
Finally, in order to impart durability to the printed part, the present invention provides:
Apply glue containing water repellent to the printing area.

ここで適用される撥水剤は通常撥水加工に用いられるも
のでよいが9重合性ビニル基含有化合物とのぬれ性9反
応性などの点からシリコン系撥水剤ならびにフッ素系撥
水剤を選択するのが好ましい。
The water repellent used here may be one that is normally used for water repellent finishing, but from the viewpoint of wettability with polymerizable vinyl group-containing compounds and reactivity, silicone-based water repellents and fluorine-based water repellents are used. Preferably.

これらの撥水剤は通常使用されるものが適用できるが、
シリコン系撥水剤としてはジメチルポリシロキサンやエ
ポキシ変性ポリシロキサンなどが好捷しく、またフッ素
系撥水剤としてはフルオロカーボン基を有するポリアク
リル酸エステルからなる化合物、たとえばパーフルオロ
エチレンポリアクリレートなどが好ましい。
These water repellents can be commonly used, but
Preferred silicone-based water repellents include dimethylpolysiloxane and epoxy-modified polysiloxane, and preferred fluorine-based water repellents include compounds consisting of polyacrylic acid esters having fluorocarbon groups, such as perfluoroethylene polyacrylate. .

かかる撥水剤は通常の界面活性剤で水に分散して適用す
る。この場合、界面活性剤を特定化する必要はなく、ア
ニ芽ン系、カチオン系、非イオン系を問わず、撥水剤を
乳化分散できるものを適用することができるが、非イオ
ン系界面活性剤を使用するほうが、接着性、固着性の点
で好ましい。
Such a water repellent is applied by dispersing it in water using a conventional surfactant. In this case, there is no need to specify the surfactant, and any surfactant that can emulsify and disperse the water repellent can be applied, regardless of whether it is an anionic, cationic, or nonionic surfactant. It is preferable to use an agent in terms of adhesiveness and fixing properties.

との撥水剤分散液に上記エマルジョン糊を配合して印捺
する。
The above emulsion paste is blended into a water repellent dispersion liquid and printing is performed.

かかる撥水剤の塗布量は固形分で05〜15重量チ、好
ましくは1〜10重@係の範囲にあるのが風合(柔軟性
)ならびに耐久性にすぐれている。
The amount of water repellent to be applied is in the range of 0.5 to 15% by weight, preferably 1 to 10% by weight in terms of solid content, for excellent texture (flexibility) and durability.

撥水剤を付与しに後は、前記同様に乾燥し9次いで通常
1ろ0℃以上、好ましくは140〜1゛60℃の温度で
60秒〜10分、好ましくは1〜5分。
After applying the water repellent, it is dried in the same manner as described above, and then kept at a temperature of usually 1 to 0°C or higher, preferably 140 to 160°C for 60 seconds to 10 minutes, preferably 1 to 5 minutes.

熱処理する。ここで重要なことは上記熱処理は重合性ビ
ニル基含有化合物の反応を開始する温度以上の条件で、
かつ該反応が完結する時間が必要であるのであって、上
記条件に限定する必要はない。
Heat treatment. What is important here is that the above heat treatment is performed at a temperature higher than the temperature that starts the reaction of the polymerizable vinyl group-containing compound.
In addition, time is required for the reaction to complete, so there is no need to limit the conditions to the above conditions.

かくして得られる着色模様は洗濯やトライクリーニング
に対する耐久性にすぐれ、かつ鮮明にマーキングされた
撥水性を有するものであり、しかも本発明法によれば各
商品に適合するマークを簡単容易に伺与し得るものであ
る。
The colored pattern thus obtained has excellent durability against washing and try-cleaning, is clearly marked, and is water-repellent.Moreover, according to the method of the present invention, it is easy to apply marks suitable for each product. It's something you get.

以下本発明を実施例によりさらに説明する。The present invention will be further explained below with reference to Examples.

実施例 シリコン系撥水剤(ジメチルポリシロキサンジオール)
加工された濃糺のポリエステル繊維からなるスキーウェ
ア用ツィル(撥水度:100)を用いて、下記要領で赤
色マークを付与した。
Example silicone water repellent (dimethylpolysiloxanediol)
Using twill for ski wear (water repellency: 100) made of processed dark starched polyester fibers, a red mark was applied in the following manner.

使用薬剤は次のとおυである。The drugs used are as follows.

(1)乳化剤(非イオン系界面活性剤)ホリエチレンク
リコールノニルフェニルエ^テルイH,L、B、−12
,8)を 60部とポリエチレングリコールステアリン
酸ジエステル(H,T、。
(1) Emulsifier (nonionic surfactant) polyethylene glycol nonylphenyl ether Terui H, L, B, -12
, 8) and 60 parts of polyethylene glycol stearate diester (H,T,).

B、 =’20 ) 10部を水60部からなるH、L
、B。
B, = '20) H, L consisting of 10 parts and 60 parts of water
,B.

が146の混合活性剤。is a mixed activator with 146.

(2)  エマルジョン糊 ミネラルターペン60部に上記乳化剤4部。(2) Emulsion glue 60 parts of mineral turpentine and 4 parts of the above emulsifier.

水66部からなる粘度6’0.000 cpsの乳化分
散糊。
An emulsifying and dispersing paste with a viscosity of 6'0.000 cps consisting of 66 parts of water.

(3)重合性ビニル基含有化合物分散組成物アクリル酸
エチル20部、アクリル酸ブチル20部、スチレン1部
、アクリロニトリル1部。
(3) Polymerizable vinyl group-containing compound dispersion composition: 20 parts of ethyl acrylate, 20 parts of butyl acrylate, 1 part of styrene, and 1 part of acrylonitrile.

N−メチロールアクリルアミド1部をポリエチレングリ
コールノニルフェニルエーテル(H,L。
One part of N-methylolacrylamide was mixed with polyethylene glycol nonylphenyl ether (H,L).

B、=12.8)2部と水55部に分散した組成物。B, = 12.8) composition dispersed in 2 parts and 55 parts of water.

(4)着色材料分散物 パーマネントカーミンFB(赤色顔II > 40に分
散したもの。
(4) Coloring material dispersion Permanent Carmine FB (dispersed in Red Face II > 40).

(5)  隠ぺい材料分散物 酸化チタン70部をポリエチレングリコールノニルフェ
ニルエーテル(H,L、)3. = 12.8 )10
部と水20部に分散したもの。
(5) Hiding material dispersion 70 parts of titanium oxide was mixed with polyethylene glycol nonylphenyl ether (H,L,)3. = 12.8) 10
1 part and 20 parts of water.

(6)スミテックスレジン1φろ(住友化学工業社製)
メチロールメラミン系架橋剤。
(6) Sumitex resin 1φ filter (manufactured by Sumitomo Chemical Co., Ltd.)
Methylolmelamine crosslinking agent.

(7)  ウルトラテックスESB (チバガイギー社
製)ジメチルボッシロキサンジオールからなるシリコン
系撥水剤。
(7) Ultratex ESB (manufactured by Ciba Geigy) A silicone water repellent made of dimethylbossiloxane diol.

−」二記撥水性布帛に、薬剤(3) 40部、薬剤(2
59部、薬剤(5)1部とからなる粘度10,000 
cpS  の糊を、マーク型を用いて印捺し、110℃
で乾燥した(第1工程)。次いで薬剤(4)10部、薬
剤(5)40部、薬剤[3]15部、薬剤(2134部
、薬剤(6)1部からなる粘度15.OD D cpr
−、+の着色部を、乾燥後の」二記マークの上に同−型
を用いて印捺、乾燥した(第2工程)。次に第1工程と
同−糊を用いて同様に印捺、乾燥し、最後に薬剤(71
20部と薬剤(2+ s o部からなる撥水創部を同じ
く印捺、乾燥した。この印捺布帛を130℃の熱風乾燥
機に装填し、6分間加熱処理した。
-” 40 parts of drug (3), drug (2
Viscosity 10,000 consisting of 59 parts and 1 part of drug (5)
Print cpS glue using a mark mold and heat at 110℃.
(first step). Next, viscosity 15.OD D cpr consisting of 10 parts of drug (4), 40 parts of drug (5), 15 parts of drug [3], 2134 parts of drug, and 1 part of drug (6)
The colored parts of - and + were printed on the dried marks using the same mold and dried (second step). Next, the same glue as in the first step was used to print and dry, and finally the drug (71
A water-repellent wound area consisting of 20 parts and 2+ parts of the drug was similarly printed and dried. This printed fabric was loaded into a hot air dryer at 130° C. and heat-treated for 6 minutes.

なお比較例として、第2工程で使用した着色部のみを用
いて、実施例と同じ撥水性布帛に印捺。
As a comparative example, printing was performed on the same water-repellent fabric as in the example using only the colored portion used in the second step.

乾燥し、130℃・6分熱処理した。It was dried and heat treated at 130°C for 6 minutes.

結果を表1に示す。なお表中の各項目の測定方法は下記
に従った。
The results are shown in Table 1. The measurement method for each item in the table was as follows.

摩擦堅牢度: JIS L−1048に準する。Rubbing fastness: According to JIS L-1048.

酬洗擢性:家庭用洗濯機゛銀河″′(東芝製)により、
洗剤2 g7’7gを用いて通常の洗濯処理を25分間
行なったときの2着色 部の剥離の有無で判定した。
Washability: With the home washing machine ``Ginga'' (manufactured by Toshiba),
The determination was made based on the presence or absence of peeling of the two colored areas when normal washing was carried out for 25 minutes using 7'7g of detergent 2.

耐ドライクリーニング性:J工5L−0860に従って
行なうドライクリーニングを5 回繰り返した後の着色部の剥離の有無 で判定した。
Dry cleaning resistance: Judgment was made based on the presence or absence of peeling of the colored area after dry cleaning was repeated 5 times in accordance with J-Tech 5L-0860.

Claims (1)

【特許請求の範囲】[Claims] 撥水性布帛の表面に1重合性ビニル基含有化合物層を介
して2着色材料ならびに撥水剤を固着することを特徴と
する撥水性布帛の着色法。
A method for coloring a water-repellent fabric, which comprises fixing two coloring materials and a water-repellent agent to the surface of the water-repellent fabric via a monopolymerizable vinyl group-containing compound layer.
JP58025250A 1983-02-17 1983-02-17 Coloring of water repellent cloth Pending JPS59150186A (en)