JPS59102857A - Manufacture of mixture having mable-like pattern - Google Patents
Manufacture of mixture having mable-like patternInfo
- Publication number
- JPS59102857A JPS59102857A JP21175482A JP21175482A JPS59102857A JP S59102857 A JPS59102857 A JP S59102857A JP 21175482 A JP21175482 A JP 21175482A JP 21175482 A JP21175482 A JP 21175482A JP S59102857 A JPS59102857 A JP S59102857A
- Authority
- JP
- Japan
- Prior art keywords
- mixed
- mixture
- ratio
- liquid
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
本発明は大理石模様を有する混合物の製造法に関するも
のである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for producing a marbled mixture.
本発明の目的は入手容易な材料により特別の処理を経る
ことなく大理石模様を有する混合物を得ることにある。The object of the present invention is to obtain a mixture having a marble pattern using readily available materials and without special treatment.
この混合物は基礎材料、殊に建築用の内外装材用或いは
タイル用等の各種用途に使用することができる。前記の
目的を達するため本発明はアラビアゴムに略２：１の割
合でパラフィンエマルジョンを添加し適量の水とともに
混和した液Ａと、ステアリン酸カルシウムにメタノール
を略１：２の割合で混和した液Ｂとを混和液Ｂに対しＡ
を１：４〜５の割合で混合するとともに、該混合液１に
対し９の割合の水で稀釈し、該稀釈液１に対し１．５〜
２．５の割合のセメントと２〜３．５の割合の細骨材を
適宜の顔料とともに混合練り合せ、これを所定の型に流
し込み固化・養生さぜるようにしたものである。This mixture can be used in various applications such as basic materials, especially interior and exterior materials for buildings and tiles. In order to achieve the above-mentioned object, the present invention provides a solution A in which paraffin emulsion is added to gum arabic in a ratio of approximately 2:1 and mixed with an appropriate amount of water, and a solution B in which methanol is mixed in calcium stearate in a ratio of approximately 1:2. A to mixture B
are mixed in a ratio of 1:4 to 5, and diluted with water in a ratio of 9 parts to 1 part of the mixed liquid, and 1.5 to 1 part of the diluted liquid is mixed.
Cement at a ratio of 2.5 and fine aggregate at a ratio of 2 to 3.5 are mixed and kneaded together with an appropriate pigment, and the mixture is poured into a predetermined mold and allowed to solidify and cure.
而して、前記組成にアラビアゴムを含むのは最終製品に
防水性を与え、またひび割れが生ずるのを防ぐためであ
る。混合液Ｂにメタノールを混合するのはステアリン酸
カルシウムの同化を防止するためであるが、メタノール
に分散することにより後工程で水による稀釈が可能とな
る。混和液Ａ及びＢの混合液はアルカリ性であり、これ
を１；９に水で稀釈したものに固結材としてセメント、
細骨材として寒水石など白色の微妙な砕石、岩石砂を混
合し、更に締り合せて所定の型にて成形を行なうのであ
る。型は、コンクリート製品の成形型のようなもので良
いが、型面をガラス板、金属板等平滑な磨き面で形成す
れば、磨き上げた大理石をそのままの地肌をもった製品
が得られる。尚、顔料は大理石個有の緑色系の色彩、斑
紋をもたせるために混合するが主に斑紋のためで、地の
色あいはセメント（白色）及び細骨材の寒水石により得
ることができる。The reason why gum arabic is included in the composition is to provide waterproofness to the final product and to prevent cracking. The reason why methanol is mixed into the mixed solution B is to prevent assimilation of calcium stearate, but dispersing it in methanol enables dilution with water in a subsequent step. The mixed liquid of mixed liquids A and B is alkaline, and it is diluted with water to a ratio of 1:9, and cement is added as a solidifying agent.
Finely white crushed stone such as kansui stone and rock sand are mixed as fine aggregate, which is then compacted and molded into a predetermined mold. The mold may be something like a mold for concrete products, but if the mold surface is made of a smooth polished surface such as a glass plate or metal plate, a product with the same texture as polished marble can be obtained. Pigments are mixed to give marble its unique green color and mottling, but this is mainly for the mottling, and the color of the ground can be obtained by cement (white) and Kansui stone, a fine aggregate.
以下、前記のような構成を有する本発明の実施例につい
て説明する。Embodiments of the present invention having the above configuration will be described below.
〈実施例〉アラビアゴム１００（］に、水１５００（Ｃ
Ｃ）を加えて撹拌し１、これにパラフィンエマルジョン
５０Ｑを添加して混合液Ａを作り、ステアリン酸カルシ
ウム２０ｇをメタノール５Ｑｃｃに分散し混和液Ｂを作
るとともにこれらを混合し、混合液１に対し重量比９の
割合の水で稀釈した。<Example> Gum arabic 100 (), water 1500 (C
Add C) and stir 1. Add 50Q of paraffin emulsion to this to make a mixed solution A, disperse 20 g of calcium stearate in 5 Qcc of methanol to make a mixed solution B, and mix these together. Diluted with 9 parts water.
該稀釈液３００ｃｃにセメント５６０（］、骨材として
寒水石をＱ、７ｍｍ〜３ ｍｍの粒径にした微砕石を夫
々加えて混練し、緑色の顔料を添加し底面に光沢ガラス
板を設けた型に流し込んで４８詩間養生し、厚さ約８關
のタイル状製品を製造した。To 300 cc of the diluted solution were added cement 560 (), Qansuite as aggregate, and pulverized stone with a particle size of 7 mm to 3 mm and kneaded, green pigment was added, and a glossy glass plate was provided on the bottom. The mixture was poured into a mold and cured for 48 meters to produce a tile-like product approximately 8 meters thick.
該製品は、−面を除いて全体に緑がかった白色を呈し、
前記−面は白色の地色に緑色の斑紋か入った美しい平滑
な光沢面をもった曲げ強度も強し）ものであった。即ち
、本発明により、格別の素材、処理を経ることなく、廉
価に大理石模様を有する混合物を得ることができた。The product exhibits a greenish white color throughout except for the - side,
The above-mentioned surface had a beautiful smooth glossy surface with green markings on a white background and had high bending strength. That is, according to the present invention, it was possible to obtain a mixture having a marble pattern at a low cost without using special materials or processing.
特 許 出 願 人 指 １） 義
離間 上 宇治用 徹
〒 、
代理人 弁理士 井 沢 淘−↓二′Ｅ２２
□Patent applicant 1) Righteousness
Toru Uji, agent and patent attorney Tadashi Izawa-↓2'E22 □
Claims (1)
ンを添加し適量の水とともに混和した液Ａと、ステアリ
ン酸カルシウムにメタノールを略１：２の割合で混和し
た液Ｂとを混和液Ｂに対しＡを１：４〜５の割合で混合
するとともに、該混合液１に対ｌノ９の割合の水で稀釈
し、該稀釈液１に対し１．５〜２．５の割合のセメント
と２〜３５の割合の細骨材を適宜の顔料とともに混合練
り合せ、これを所定の型に流し込み固化・養生させるこ
とを特徴とする大理石模様を有する混合物の製造法。A mixture of liquid A, in which paraffin emulsion is added to gum arabic at a ratio of approximately 2:1 and mixed with an appropriate amount of water, and liquid B, in which methanol is mixed in calcium stearate at a ratio of approximately 1:2, is mixed with liquid A. Mix at a ratio of 1:4 to 5, and dilute with water at a ratio of 1 to 9 parts of the mixed solution, and add cement at a ratio of 1.5 to 2.5 parts to 1 part of the diluted solution and 2 to 35 parts of the diluted solution. A method for producing a mixture having a marble pattern, characterized by mixing and kneading fine aggregate with a suitable pigment in a proportion of , and pouring the mixture into a predetermined mold to solidify and cure.