JPS5899908A - Mounting of artificial nail - Google Patents
Mounting of artificial nailInfo
- Publication number
- JPS5899908A JPS5899908A JP19984481A JP19984481A JPS5899908A JP S5899908 A JPS5899908 A JP S5899908A JP 19984481 A JP19984481 A JP 19984481A JP 19984481 A JP19984481 A JP 19984481A JP S5899908 A JPS5899908 A JP S5899908A
- Authority
- JP
- Japan
- Prior art keywords
- nail
- cyanoacrylate
- artificial nail
- mounting
- nails
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
本発明は人工爪を爪に装着するに当り、爪に損傷を与え
ないα−シアノアクリレート系接着剤を用いて装着する
方法に関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method of attaching an artificial nail to a nail using an α-cyanoacrylate adhesive that does not damage the nail.
α−シアノアクリレートは極めてアニオン重合を起こし
やすく、固体表面や空気中の水分、アルカリ物質等のア
ニオン活性種等により触媒の添加や加熱を行うことなく
短時間で重合硬化する性質を有するので、ゴム、プラス
チック、金属、ガラス等の接着に瞬間接着剤として広く
利用されている。このような性質を利用して、自動車、
弱電、木工分野等工業的分野に広く使用されて来た。最
近工業的分野だけでなく医療、化粧品用さしての普及も
目覚ましく、化粧品分野では、爪の補修や人工爪の装着
等に活用されている。α-Cyanoacrylate is extremely susceptible to anionic polymerization, and has the property of polymerizing and curing in a short time without adding a catalyst or heating due to anionic active species such as solid surfaces, moisture in the air, and alkaline substances. It is widely used as an instant adhesive for bonding plastics, metals, glass, etc. Taking advantage of these properties, automobiles,
It has been widely used in industrial fields such as light electrical appliances and woodworking. Recently, it has become popular not only in the industrial field but also in medical and cosmetic applications, and in the cosmetic field, it is used for nail repair, artificial nail attachment, etc.
本来爪は指先の保護の役目をするものであるが、今日の
婦人にとっては装飾の役目をも、つとめ生活態様の一部
となっている。人工爪の装着方法は爪の全面捷たに先端
に人工爪(多くの場合可撓性プラスチックシートでつく
られている)をα−シアノアクリレートで接着し、形を
整え、マニキュア等で仕Eげるものである。Originally, nails served to protect the tips of the fingers, but for women today they also serve as decoration and have become a part of their daily lives. The method for attaching artificial nails is to glue the artificial nail (often made of flexible plastic sheet) to the tip of the nail with α-cyanoacrylate, shape it, and finish it with nail polish. It is something that
しかしながら、爪の表面は常時人体体温に近い温度を保
ち、しかも適当な湿気を有するので、従来からこの用途
に使用されているメチル−α−シアノアクリレートやエ
チル−α−シアノアクリレートでは、急激に重合を開始
して発熱することがある。また人工爪を剥すときにはア
セトンなどの有機溶剤に溶解させるが、簡単に剥れない
ために爪を傷つけたり、まだ、長期間繰返し使用すると
爪の表面に筋が入ったり、表面の光沢またはなめらかさ
が損なわれる様になる事かあね、これらの問題の解決が
強く望まれている。However, because the surface of the nail always maintains a temperature close to the human body temperature and has a suitable amount of moisture, the methyl-α-cyanoacrylate and ethyl-α-cyanoacrylate traditionally used for this purpose do not polymerize rapidly. may start and generate a fever. Also, when removing artificial nails, they are dissolved in organic solvents such as acetone, but they do not peel off easily and may damage the nails, and if used repeatedly for a long period of time, the surface of the nails may become streaked or the surface may become glossy or smooth. It is strongly desired that these problems be resolved.
本発明人らは爪側α−シアノアクリレート系接着剤の前
述の問題点を解決すべく検討したところ、α−シアノア
クリレートめ種類を選定し、またはそれらを配合する事
により、前述の問題点を解決し得ることを見い出し本発
明を完成した。The inventors of the present invention investigated how to solve the above-mentioned problems with nail-side α-cyanoacrylate adhesives, and found that by selecting α-cyanoacrylate types or blending them, the above-mentioned problems could be solved. The present invention was completed by discovering a solution to the problem.
すなわち、本発明は式(T)で示される化合物中Rがn
−プロピル基、1so−プロピル基、n−ブチル基、i
so −ブチル基の化合物を一種以上含有するα−シア
ノアクリレート系接着剤を用いることを特徴とした人工
爪の装着方法である。That is, the present invention provides a compound represented by formula (T) in which R is n
-propyl group, 1so-propyl group, n-butyl group, i
This is a method for attaching artificial nails characterized by using an α-cyanoacrylate adhesive containing one or more so-butyl group compounds.
N O
また、メチル−α−シアノアクリレートまたはエチル−
α−シアノアクリレートと上記化合物を配合してもよい
。添加量はメチル−α−シアノアクリレート捷たはエチ
ル−〇−シアノアクリレート100部に対し1部以上で
ある。好ましり#′i3部以上がよい。これ以下の配合
ではnf+述の問題点が生じる。N O also methyl-α-cyanoacrylate or ethyl-
α-cyanoacrylate and the above compound may be blended. The amount added is 1 part or more per 100 parts of methyl-α-cyanoacrylate or ethyl-〇-cyanoacrylate. Preferably #'i is 3 parts or more. If the composition is less than this, the problems mentioned above will occur.
本発明の爪側α−シアノアクリレート系接着剤には従来
からメチル−α−シアノアクリレートやエチル−α−シ
アノアクリレートに添加して用いられている安定剤、増
粘剤、可塑剤、溶剤、賦香剤および着色剤等も愚論使用
することができる。The nail-side α-cyanoacrylate adhesive of the present invention contains stabilizers, thickeners, plasticizers, solvents, and excipients that have been conventionally added to methyl-α-cyanoacrylate and ethyl-α-cyanoacrylate. Flavoring agents, coloring agents, etc. may also be used.
以下に実施例を挙げて本発明を具体的に説明するが実施
例に限定されるものではない。The present invention will be specifically explained below with reference to Examples, but it is not limited to the Examples.
実施例1〜7 比較例1〜2
表−1に示す各種α−シアノアクリレートに亜硫酸ガス
20ppm、ハイドロキノン5001)pmを添加して
爪側α−シアノアクリレート系接着剤を調製し、重合時
の発熱度を測定した。その方法はアンモニア蒸気雰囲気
中にIk露した温度計を20℃、55−60%RHの雰
囲気中に5分間放置し、温度計の検温部に爪側α−シア
ノアクリレート系接着剤を2滴落し重合させて温度上昇
を読み、その最高温度を記録した。Examples 1 to 7 Comparative Examples 1 to 2 Nail side α-cyanoacrylate adhesives were prepared by adding 20 ppm of sulfur dioxide gas and 5001) pm of hydroquinone to various α-cyanoacrylates shown in Table 1, and the heat generation during polymerization was The degree of The method is to leave a thermometer exposed to Ik in an ammonia vapor atmosphere for 5 minutes in an atmosphere of 20°C and 55-60% RH, and then drop two drops of α-cyanoacrylate adhesive on the nail side onto the temperature measuring part of the thermometer. The temperature rise was read during polymerization and the maximum temperature was recorded.
また、同様の接着剤を用いて人工爪([5セカンドタイ
ガーネイルズJ (−55econd Tiger N
a11s″)米国バイアム社製)同志を接着し、24時
間後剥離液(「スーパーグルーリムーバー」(” 5u
per Glue Remover ’)米国スーパー
グルー社製)に浸漬し剥離するまでの時間を測定した。In addition, artificial nails ([5 second Tiger Nails J (-55 second Tiger N
a11s") made by Byam Inc. in the United States), and after 24 hours, apply a peeling solution ("Super Glue Remover"("5u
per Glue Remover') (manufactured by Super Glue, Inc., USA) and the time taken to peel it off was measured.
これらの結果を表−1に示す。These results are shown in Table-1.
表−1の結果からもわかるように、本発明の爪側α−シ
アノアクリレート系接着剤は発熱温度も低く、剥離液で
も簡単に剥れ爪側に好適であるといえる。As can be seen from the results in Table 1, the α-cyanoacrylate adhesive for the nail side of the present invention has a low exothermic temperature and can be easily peeled off even with a release liquid, making it suitable for the nail side.
これらの接着剤を用いて20人の女性を対象に人工爪(
前記)を爪に接着し、ついで剥離液(前記)で剥離し、
これを10回繰返した。その結果比較例1では2人で合
計3ケ所の生爪に艶を失い、1ケ所にかすかに摺り傷を
認めた。比較例2では1人で1ケ所に損傷があった。実
施例1〜7では全く損傷を認めなかった。Using these adhesives, 20 women were given artificial nails (
Adhere the above) to the nail, then peel it off with the remover (see above),
This was repeated 10 times. As a result, in Comparative Example 1, the nails of two people lost their luster in a total of three places, and a faint scratch was observed in one place. In Comparative Example 2, one person was damaged in one place. No damage was observed in Examples 1 to 7.
Claims (1)
物中、Rがn−プロピル基、iso −プロピル基、
n−ブチル基およびiso −ブチル基の化合物を一
種以上含有するα−シアノアクリレート系接着剤を用い
ることを特徴とする人工爪の装着方法。 N 0[Claims] When attaching an artificial nail to a nail, in the compound represented by formula (1), R is an n-propyl group, an iso-propyl group,
A method for attaching an artificial nail, characterized by using an α-cyanoacrylate adhesive containing one or more compounds of n-butyl group and iso-butyl group. N 0