JPS5861246A - Aluminum alloy - Google Patents
Aluminum alloyInfo
- Publication number
- JPS5861246A JPS5861246A JP15922481A JP15922481A JPS5861246A JP S5861246 A JPS5861246 A JP S5861246A JP 15922481 A JP15922481 A JP 15922481A JP 15922481 A JP15922481 A JP 15922481A JP S5861246 A JPS5861246 A JP S5861246A
- Authority
- JP
- Japan
- Prior art keywords
- alloy
- casting
- aluminum
- water
- rapidly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
この発明は、アルミニウム８０〜９０％、亜鉛０〜２０
％、銅０〜ｌ０ＩＧ、マグネシウム０〜１０ｓ・チタン
０〜５９１．或いは更にマフ４フ０ル３％、鉄０〜２−
よりなる合金をダイカストマシンで成形し、上記成形品
を急速冷却するか、ｉたは加熱した後急冷却してなるこ
とを特徴とするアル１＝ウム系合金Ｋｌｌすゐ。DETAILED DESCRIPTION OF THE INVENTION This invention consists of 80-90% aluminum and 0-20% zinc.
%, copper 0-10IG, magnesium 0-10s, titanium 0-591. Or even muff 4 full 3%, iron 0-2-
An aluminum-based alloy Kllsu is formed by molding an alloy consisting of the following in a die-casting machine, and rapidly cooling the molded product, or by heating and then rapidly cooling the molded product.
実施例 アルミニウム８５重量部、亜鉛１０重量部。Example 85 parts by weight of aluminum, 10 parts by weight of zinc.
銅２重量部、マグネシウム１重量部−チタン２ム蓋部よ
りなる合金（アルミニウム、亜鉛、マグネシウムよりな
る＃Ｉ湯の中に銅粉及びチタン繊維を入れて混合し冷却
固化したもの）をダイカストマシンで溶融し金型に射出
して成形し。An alloy consisting of 2 parts by weight of copper, 1 part by weight of magnesium and 2 parts of titanium (copper powder and titanium fibers are mixed in #I hot water made of aluminum, zinc and magnesium, mixed and cooled to solidify) is die cast machine. It is melted and injected into a mold.
成形品′に取出すと共に水中に入わて急速冷却した。It was taken out into a molded product and immersed in water for rapid cooling.
上記実施例においては、アルミニウム、亜鉛・銅、マグ
ネシウム及びチタンよりなる合金に更に鉄とマンガンの
うちの１種または２種を混合した合金（アルミニウム、
亜鉛、マグネシウムよりなる溶湯の中に銅粉、チタン繊
維、及び鉄粉とマンガン粉のうちの１種または２種を入
れて混合し冷却固化したもの）Ｖ使用してもよく。In the above embodiment, an alloy (aluminum,
A product prepared by adding copper powder, titanium fiber, and one or two of iron powder and manganese powder to a molten metal of zinc and magnesium, mixing the mixture, cooling and solidifying it may also be used.
金型から取出した成形品？２５０°〜３００°Ｃに再加
熱して水に臘急速冷却してもよい。A molded product taken out of a mold? It may be reheated to 250°-300°C and rapidly cooled in water.
この発明のアルミニウム系合金は、軽量で含有される金
属の特性を有゛するのみならず急速に冷却されて超塑性
化し１強度に優れているのみならず防振効果を有する轡
の利点も有する。The aluminum-based alloy of the present invention not only has the characteristics of being lightweight and containing metals, but also rapidly cools to become superplastic, has excellent strength, and also has the advantage of having a vibration-proofing effect. .
特許出願人 株式会社満尾総合研究所代表皐締役 満
尾 浩 治
゛＋番売オキ正ｔ（才人）
即知（”＋”＋３［−１８
特書僅毛嗜Ｎ）
（、中Ａ６克・キ 日８加計６寺本ｊ許陣か嘉（炉９２
〕（苦２、褪ｇｌｌｌｌの先キ茎 ？１シミニ＼）へ
撃４）（−３，詞と１も３も
１婆イ′＋ ｘ二も 南、矛１ ４４１ｔヤ出６４に針
ネｔとりす１版 （１）肩噂１ｒ
（２）叩印ｔ
６、楢との内申Patent Applicant Mitsuo Research Institute Co., Ltd. Representative Director Hiroshi Mitsuo Katsu・Ki Day 8 Kaku 6 Teramoto j Xu Jinka Yoshi (furnace 92
〕(Ku 2, the tip of the fallen glllll ? 1 Shimini ＼) hit 4) (-3, words and 1 and 3 and 1 ba i' + x 2 also Minami, spear 1 441t Ya out 64 and needle net Torisu 1st edition (1) Shoulder rumor 1r (2) Seal t 6, secret report with Nara
Claims (1)
９Ｇ、マグネミウム０〜ｌＯ−、チタンＯ〜５１！、或
いは更にマンガンθ〜３−・鉄０〜２−よりなる合金を
ダイカストマシンで成形し・上記成形品を急速冷却する
か、または加熱した後急速冷却してなることを特徴とす
るアルミニウム系合金。Aluminum 80~90-, Zinc θ~20% Steel θ~10
9G, magnesium 0~lO-, titanium O~51! , or an aluminum-based alloy formed by molding an alloy consisting of manganese θ~3- and iron 0-2- with a die-casting machine and rapidly cooling the molded product, or heating and then rapidly cooling it. .