JPS58167670A - 難燃性組成物及びその調製法 - Google Patents
難燃性組成物及びその調製法Info
- Publication number
- JPS58167670A JPS58167670A JP3926982A JP3926982A JPS58167670A JP S58167670 A JPS58167670 A JP S58167670A JP 3926982 A JP3926982 A JP 3926982A JP 3926982 A JP3926982 A JP 3926982A JP S58167670 A JPS58167670 A JP S58167670A
- Authority
- JP
- Japan
- Prior art keywords
- pbw
- ammonium
- sodium
- sulfate
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
大発明は1紙、綿紗物及び木材の如舞セル四−スを含む
材料1合成ポリマー製織物及びフィルムの如きポリマー
材料を含む各種材料に難燃性を付与すh9に用いる。水
を基剤とする組成物及び有機物質を基剤とする組成物の
双方に関する7可燃材料の離燃性け、短燃剤を以て該材
料を被榎あるいけ難燃物質を物品自身内に組込むことに
よって、これを向上−+r【2めることができることは
。
材料1合成ポリマー製織物及びフィルムの如きポリマー
材料を含む各種材料に難燃性を付与すh9に用いる。水
を基剤とする組成物及び有機物質を基剤とする組成物の
双方に関する7可燃材料の離燃性け、短燃剤を以て該材
料を被榎あるいけ難燃物質を物品自身内に組込むことに
よって、これを向上−+r【2めることができることは
。
画業においては周知のことである一文字通ね長子にのほ
る難燃性組成物及び難燃剤は文献に記載されているが、
この工業技術の重要性に鑑み、難燃性の向上を与える如
き組成物は依然としてこれを[1すべもものである。
る難燃性組成物及び難燃剤は文献に記載されているが、
この工業技術の重要性に鑑み、難燃性の向上を与える如
き組成物は依然としてこれを[1すべもものである。
とわわけ、火炎に直接当たった際に物品の燃焼に対する
耐性ケ増太し、且つ同時に強度、物理的外観ならびに物
理的取扱い、吸収その他の性質の如き、その他の望まれ
る特性に有害が影響を及ぼすことのない難燃性組成物に
注量が向けられて来た。
耐性ケ増太し、且つ同時に強度、物理的外観ならびに物
理的取扱い、吸収その他の性質の如き、その他の望まれ
る特性に有害が影響を及ぼすことのない難燃性組成物に
注量が向けられて来た。
今や一出願人は天然材料及び合成材料のいずれを以て製
造した物品もその難燃性全、該物品の特性の重大な劣化
を伴わず、また、ある場合には若干の特性の増強を伴っ
て一向上せしめ得る一連の組成物を開発した。
造した物品もその難燃性全、該物品の特性の重大な劣化
を伴わず、また、ある場合には若干の特性の増強を伴っ
て一向上せしめ得る一連の組成物を開発した。
従って、本発明の目的は各種の物品に向上した難燃性を
付与することを得る組成物を供給することである、 本発明の第二の目的は物品の難燃性を向上ぜしめる九め
の組成物で房るが一同時に該物品の望ま1、い特性に相
当程度の悪影響を及ぼすことのないものを提供すること
である。
付与することを得る組成物を供給することである、 本発明の第二の目的は物品の難燃性を向上ぜしめる九め
の組成物で房るが一同時に該物品の望ま1、い特性に相
当程度の悪影響を及ぼすことのないものを提供すること
である。
さらに本発明は直接火炎を当てた際に物品の燃焼に対す
る耐性を向上せしめる組成物を供給することを目的とし
ている。本発明のその他の目的にはまt上述の利点を有
する離燃性組成物を調製する方法の記載をも含むもので
ある。
る耐性を向上せしめる組成物を供給することを目的とし
ている。本発明のその他の目的にはまt上述の利点を有
する離燃性組成物を調製する方法の記載をも含むもので
ある。
一般的に一8発EIJIけ製造物98来0特性及び特徴
を実質的に低下せしめずに、当該物品の難燃性を向上ぜ
しめるために、各種の基材表面の被覆及び/または物品
内への直接組込みに際して有用が一部を基剤と+石組酸
物及び有機物質を基剤とする組成物の双方の供給を含む
ものである。
を実質的に低下せしめずに、当該物品の難燃性を向上ぜ
しめるために、各種の基材表面の被覆及び/または物品
内への直接組込みに際して有用が一部を基剤と+石組酸
物及び有機物質を基剤とする組成物の双方の供給を含む
ものである。
以下に記載する本発明の範囲内の離燃性組成物のすべて
のものについては、七の毒性指数が蕪視し得る本のであ
り、そのにおいが不快なものでないことに留意す右こと
≠(重要である。このようか特徴は重要である。けだし
、水組成物を以て処理した製造物は1人間に対する熱害
性及び好ましい美的特徴が大いに望まれる如き、家庭内
、公共施設、車両などの場所においで用いられることの
多い物品であるからであゐ。
のものについては、七の毒性指数が蕪視し得る本のであ
り、そのにおいが不快なものでないことに留意す右こと
≠(重要である。このようか特徴は重要である。けだし
、水組成物を以て処理した製造物は1人間に対する熱害
性及び好ましい美的特徴が大いに望まれる如き、家庭内
、公共施設、車両などの場所においで用いられることの
多い物品であるからであゐ。
■、セルロースを含む物品に対する応用に特に適合した
一部を基剤とす石組酸物 本発明により、出願人+d−木材木材1綿、綿その他同
種のものの如きセルロースを含む物質を以て全部せたは
一部が製造されている物品の火炎に対する耐性の向上に
特に適1−でいる下記の組成物を開発した。
一部を基剤とす石組酸物 本発明により、出願人+d−木材木材1綿、綿その他同
種のものの如きセルロースを含む物質を以て全部せたは
一部が製造されている物品の火炎に対する耐性の向上に
特に適1−でいる下記の組成物を開発した。
好ましい処方は下記の通すである。
化合物番号 成 分 量
1、ラウリル硫酸トリ上 〇、5−0.6%(体積タノ
ールアξン 比) (5−6ml/l ”)2、ヨ
ウ化アンモニウム 2−0−7.0 (FBW )3、
−リン酸アンモニウ ム 1.5−
R,o (PBW )4、臭化アンモニウム 2.
0−12.0 (PBW )5、ホウ砂または四ホウ 酸ナトリウム 1.5−20.0 (PBW
)6、ホウ酸 1.Fs −7,0(P
BW )7、硫酸ナトリウム 3.5−20.0
(1’BW )8、ケイ酸ナトリウム o、i −t
、o%(体積比) (1−10m1/l ) 9.1゜2−プロピレングリ 1.5−10.0%(体
積コール 比)(15(00ml/l )1
0、水 組成物に殺菌力を与えるために、ある種の成分を任″:
#に追加してもよい、例としては。
ールアξン 比) (5−6ml/l ”)2、ヨ
ウ化アンモニウム 2−0−7.0 (FBW )3、
−リン酸アンモニウ ム 1.5−
R,o (PBW )4、臭化アンモニウム 2.
0−12.0 (PBW )5、ホウ砂または四ホウ 酸ナトリウム 1.5−20.0 (PBW
)6、ホウ酸 1.Fs −7,0(P
BW )7、硫酸ナトリウム 3.5−20.0
(1’BW )8、ケイ酸ナトリウム o、i −t
、o%(体積比) (1−10m1/l ) 9.1゜2−プロピレングリ 1.5−10.0%(体
積コール 比)(15(00ml/l )1
0、水 組成物に殺菌力を与えるために、ある種の成分を任″:
#に追加してもよい、例としては。
このようh添加物にはアクロミシン、ウンデシレン酸及
びウンデシレン酸亜鉛がある。
びウンデシレン酸亜鉛がある。
上記の処方の範囲内で特に好ましい組成は下記の通ねで
ある。
ある。
化合物番号 成 分 量 、1、ラウリル硫
酸トリ上 2.0%(体積比)タノールアミン 2、ヨウ化アンモニウム 3.5%(、P B W
’16、−リン酸アンモニウ ム 7.0%
(PBW )4、臭化アンモニウム 3.0%
(P B W )5、ホウ砂 2.0
’%(P B W )6、ホウ酸
4.0形(PBW)71硫酸アンモニウム12.0%(
pBw)8、プロピレングリコ− ル 3.3%(体積比)9、ケイ
酸ナトリウム 0.5%(体積比)10.7クロ
ミシン2.0%(FBW )11、ウンデシレン酸
1.0%(pBw)12、ウンデシレン酸亜鉛
0.5%(PBW )13、水
120.0%(PBw)上記の如き組成物全調製する
に当っては。
酸トリ上 2.0%(体積比)タノールアミン 2、ヨウ化アンモニウム 3.5%(、P B W
’16、−リン酸アンモニウ ム 7.0%
(PBW )4、臭化アンモニウム 3.0%
(P B W )5、ホウ砂 2.0
’%(P B W )6、ホウ酸
4.0形(PBW)71硫酸アンモニウム12.0%(
pBw)8、プロピレングリコ− ル 3.3%(体積比)9、ケイ
酸ナトリウム 0.5%(体積比)10.7クロ
ミシン2.0%(FBW )11、ウンデシレン酸
1.0%(pBw)12、ウンデシレン酸亜鉛
0.5%(PBW )13、水
120.0%(PBw)上記の如き組成物全調製する
に当っては。
特別の手順に従うことが重要であることが見出(れた。
下記の方法を用いるべきである。
工程1゜
この特に好ましい組成物に関しては、化合物2.3.4
.5.6及び7を一緒に混合して均質混合物を形成する
、 工程2゜ 化合物10.11及び]2を一緒に混合して均質混合物
を形成する。
.5.6及び7を一緒に混合して均質混合物を形成する
、 工程2゜ 化合物10.11及び]2を一緒に混合して均質混合物
を形成する。
工程6゜
工程1の生成物に該化合物を溶解するに足る量の水、す
なわち水の全量の50%を加え一固体が溶解するまで絶
えず攪拌しながら組成物を70’Cに加熱する。ホウ酸
の分子内の水がなどなわ、温度に応じてメタホウ酸また
は四ホウ酸力I生じ兼ねないのを避けるために−これら
の成分の溶解温度が約70℃を超えてにならかいといり
ことを述べるのけ重要である。
なわち水の全量の50%を加え一固体が溶解するまで絶
えず攪拌しながら組成物を70’Cに加熱する。ホウ酸
の分子内の水がなどなわ、温度に応じてメタホウ酸また
は四ホウ酸力I生じ兼ねないのを避けるために−これら
の成分の溶解温度が約70℃を超えてにならかいといり
ことを述べるのけ重要である。
この温度ラフ0℃以下に保つことはホウ酸が結晶するの
を防ぐのにもま九重要である、工程4゜ 工程3の生成物11に化合物9ならびにl及び残りの水
を加える。この段階において、工程2よねの、化合物1
0.11及び12の混合物をまた加える。
を防ぐのにもま九重要である、工程4゜ 工程3の生成物11に化合物9ならびにl及び残りの水
を加える。この段階において、工程2よねの、化合物1
0.11及び12の混合物をまた加える。
上記の組成物を用いるには、材料の難燃性を向上ゼしめ
る目的のために−このよつな材料の表面に通常の如何な
る方式を以てでもこれを塗布すればよい、先に述べ几如
く、上記の組成物はセルロースを含み、離燃性を向上ぐ
しめた物品の製造に特に適している。被覆な物品の浸液
、吹付け、塗布、ローラー・コーティングあするいは別
の方法で物品の表面被覆を行なえばよい。組成物を紙の
如き材料の最終製造段階、云うまでもなく組成物が洗い
流されたわ−または稀釈されたりされるかも知れかい点
の以前のある段階において加えてこの材料に組込むこと
も可能である。
る目的のために−このよつな材料の表面に通常の如何な
る方式を以てでもこれを塗布すればよい、先に述べ几如
く、上記の組成物はセルロースを含み、離燃性を向上ぐ
しめた物品の製造に特に適している。被覆な物品の浸液
、吹付け、塗布、ローラー・コーティングあするいは別
の方法で物品の表面被覆を行なえばよい。組成物を紙の
如き材料の最終製造段階、云うまでもなく組成物が洗い
流されたわ−または稀釈されたりされるかも知れかい点
の以前のある段階において加えてこの材料に組込むこと
も可能である。
紙及び織物に用いた場合−前記の組成物は燃焼試験に関
してはA、S、T、lL(American8C1ci
ety for TestingMaterialsア
メリカ材料試験協会)及びN、 IP、 ’p;ム(N
atio’nal Fire Pr0tection
As5ociationアメリカ防火協会)の基準′&
圓えるものである7離燃性の向上に加えて2殺菌剤に添
加した。
してはA、S、T、lL(American8C1ci
ety for TestingMaterialsア
メリカ材料試験協会)及びN、 IP、 ’p;ム(N
atio’nal Fire Pr0tection
As5ociationアメリカ防火協会)の基準′&
圓えるものである7離燃性の向上に加えて2殺菌剤に添
加した。
この特に好ましい組成物は、それを用い九セルロースを
含む材料の物性を向丘ゼしめることづ(ま九見出されて
いる。
含む材料の物性を向丘ゼしめることづ(ま九見出されて
いる。
処理後に、標準的な理化学試験を受けた基材は下記の如
き特性を示した。
き特性を示した。
試料1゜
試片5gを乾燥重量として水晶20.1i量%を以て処
理した。紙の本来の特性には下記の如き影響があり九。
理した。紙の本来の特性には下記の如き影響があり九。
1、強 度
a、引張り強さ一20%増強
す、ゆるみ強さ一10%増強
C6風 化 −正常た酸化に影響なし、。
a=a 収 −変化な!−0
2、物理的外観
不透明度−0,20%増加
S、浸透性
浸透性−5%影響あり。
4、色 調
色 調−分光写真法を以てのみ変化が認められ石が0.
2%増強。
2%増強。
5、用 途
a、印刷適性−インク定着20%向士。
b、接着用 −密着性10%増強。
66耐薬品性
酸、アルカリ及び溶媒に対する反応は処理後増大ゼず、
または減少。
または減少。
7、直火使用
処理済の紙の難燃性である。火災を直接当てた場合2火
災が直接接触したところでは紙は炭化するが、火災は拡
散しない。
災が直接接触したところでは紙は炭化するが、火災は拡
散しない。
火災を中断すると、炎は消失し、熱は直ちに消散する。
試料2、
合成繊維を最高40%含む綿繊維織物のスワツチを乾燥
重量と11.て20〜30重債%の難燃性組成物を以て
処理した。この織物の本来の特性は下記の如き影響を受
けた。
重量と11.て20〜30重債%の難燃性組成物を以て
処理した。この織物の本来の特性は下記の如き影響を受
けた。
1、強 度
a、引張り強さ一30%w強
す、摩耗強さ −10%増強
C1耐久性 −5〜15弊′堀強
d、風 化 −未処理の織物の同東件において影響を
受けず。
受けず。
2、物理的特徴
a、あ らさ −わずかに増加−
す、輝 き −変化なI7゜
6、浸透性及び/または吸収
重要な変化なし。
4、着色料に対する反応
外観には影響なし1着色料け15Φ定首。
5、用 途
a、捺染適性 −布の捺染は変?1せず、捺染布地に対
する洗浄作用 は繊維及びその外観に影 響せず。
する洗浄作用 は繊維及びその外観に影 響せず。
1)、 7’X耗耐性 −20%増弦。
C0耐熱性 −5〜15%増強。
6、耐薬品性
酸、アルカリ及び容媒の作用は実質的に処理の影響を受
けず。
けず。
7、直火の使用
織物は炭化するが、火災の拡散を伴わず。
火災を中断すると、炎も熱も消失する。
8、間接加熱
織物は541.2’ Fにおいて火災を伴わずに炭化す
る。
る。
■、セルロースを含む−またはプラスチック製物品への
応用用の組成物 セルロース性含む材料とプラスチックの組合わせよね出
来ている物品に蛯熱性を付与するのに用いる。本発明の
組成物は1個々の処方成分のいずれもがなし得るより高
い度合で・耐火炎性を増加l−得る。以下に記載する組
成物はセルロース性の繊維及び合成繊維のPCl3合。
応用用の組成物 セルロース性含む材料とプラスチックの組合わせよね出
来ている物品に蛯熱性を付与するのに用いる。本発明の
組成物は1個々の処方成分のいずれもがなし得るより高
い度合で・耐火炎性を増加l−得る。以下に記載する組
成物はセルロース性の繊維及び合成繊維のPCl3合。
特に酌量%の綿とFIO%の合成繊維を含む調合を以て
製造した織物に好んで用いられる。。
製造した織物に好んで用いられる。。
この調合物は個々の成分ま定行構成要素の均質混合物を
作シ2次いで混合の最終段階において水を加えてこれを
調製すbo この型の好ましい組成物は下記の処方のものである。
作シ2次いで混合の最終段階において水を加えてこれを
調製すbo この型の好ましい組成物は下記の処方のものである。
成 分 量 (PBW)塩素化
パラフィン炭化水 素(約42重量%の塩素を 含む塩素化炭化水素の如 何カるものでも用い得る。
パラフィン炭化水 素(約42重量%の塩素を 含む塩素化炭化水素の如 何カるものでも用い得る。
例えばり四ラフイン2F) 1.0− 8.0%ジ
インプロピルケトン 0.5− 5.Q%メチルク
ロロホルム 、、 0.5− 5.Q%タングステ
ン酸ナトリウ ム 0.
5 − 5.Q%メタホウ酸ナトリウム 0.
5− 5.0%ラウリル硫酸ナトリウム 0.5−
15.Q%ヒドロキシプpピルメチ ルセルロース 5.0− 15.Q%トリ
プ四ピレングリコー ル脂肪酸(普通は08〜 C0□炭素直鎖を有する如 何なる第一アルコールを 用いてもよい’l 1.0− 8.0%オ
ルトフヱニルフヱノー ル 0.1
− 2.0%酢酢酸フェニル水銀 0.2−
2.0%ニリン酸アンモニウム 1.0− 8.0
%ラウリル硫硫酸アンモタ ウ(この成分は同割合で 用いるヨウ化アンモニウ ムを以て代えることかで きる)1.0− 8.0% 水 セルロースを含む材料と合成ポリマー材料との組合わせ
または調合よシ製造した織物及びその他の物品へのこの
ような組成物の応用についての夾験の結果、特に好まれ
る調合物け下記の組成のものである。
インプロピルケトン 0.5− 5.Q%メチルク
ロロホルム 、、 0.5− 5.Q%タングステ
ン酸ナトリウ ム 0.
5 − 5.Q%メタホウ酸ナトリウム 0.
5− 5.0%ラウリル硫酸ナトリウム 0.5−
15.Q%ヒドロキシプpピルメチ ルセルロース 5.0− 15.Q%トリ
プ四ピレングリコー ル脂肪酸(普通は08〜 C0□炭素直鎖を有する如 何なる第一アルコールを 用いてもよい’l 1.0− 8.0%オ
ルトフヱニルフヱノー ル 0.1
− 2.0%酢酢酸フェニル水銀 0.2−
2.0%ニリン酸アンモニウム 1.0− 8.0
%ラウリル硫硫酸アンモタ ウ(この成分は同割合で 用いるヨウ化アンモニウ ムを以て代えることかで きる)1.0− 8.0% 水 セルロースを含む材料と合成ポリマー材料との組合わせ
または調合よシ製造した織物及びその他の物品へのこの
ような組成物の応用についての夾験の結果、特に好まれ
る調合物け下記の組成のものである。
成 分 量 (PBW)塩素
化パラフィン炭化水 素 5
.0%ジインプロピルケトン 2.5%メチ
ルクロロホルム 2.5%タングステン酸
ナトリウ ム
2.θ%メタホウ酸ナトリウム 5
.0%ラウリル硫酸ナトリウム 10.0%ヒド
ロキシプロピルメチ ルセル日−ス 10.0%トリプロピ
レングリコ− ル
5.0%脂肪酸 2.0%オル
トフヱニルフヱノー ル 2
.0%酢酢酸フェニル水銀 ・1 2.0%ニリ
ン酸アンモニウム 0.2%ラウリル硫硫酸
アンモタ 入/ヨウ化アンモつウム 5.0%水
45.0%上記の
組成物の代表的か応用としては、これ全稀釈せず、シャ
ンプーとしてラックに用いればよい。椅子用織物2布地
あるいけ衣類。
化パラフィン炭化水 素 5
.0%ジインプロピルケトン 2.5%メチ
ルクロロホルム 2.5%タングステン酸
ナトリウ ム
2.θ%メタホウ酸ナトリウム 5
.0%ラウリル硫酸ナトリウム 10.0%ヒド
ロキシプロピルメチ ルセル日−ス 10.0%トリプロピ
レングリコ− ル
5.0%脂肪酸 2.0%オル
トフヱニルフヱノー ル 2
.0%酢酢酸フェニル水銀 ・1 2.0%ニリ
ン酸アンモニウム 0.2%ラウリル硫硫酸
アンモタ 入/ヨウ化アンモつウム 5.0%水
45.0%上記の
組成物の代表的か応用としては、これ全稀釈せず、シャ
ンプーとしてラックに用いればよい。椅子用織物2布地
あるいけ衣類。
カーテン等の織物への応用においては、上記の調合物は
好ましくけ約50体積%の水を以て稀釈する7すべての
混合及び稀釈操作は好ましくは室温において行う。
好ましくけ約50体積%の水を以て稀釈する7すべての
混合及び稀釈操作は好ましくは室温において行う。
III、 1M燃性ペイントまたはエナメルとして用
いる組成物 この組成物は一通常のペイント及びエナメルと同様の方
式を以て塗布し得る。難燃性被覆材として有用な、水を
基剤とする材料を供給する本のである7 この組成物は個々の構成要素を水と均質に混合して調製
する7この型の組成物は下記の処方のものである。
いる組成物 この組成物は一通常のペイント及びエナメルと同様の方
式を以て塗布し得る。難燃性被覆材として有用な、水を
基剤とする材料を供給する本のである7 この組成物は個々の構成要素を水と均質に混合して調製
する7この型の組成物は下記の処方のものである。
成 分 量 (PBW)丁クリ
ルポリマー乳濁液 23 − 28 %水
41.J(−53,6%ヒドロ
キシプロピルメ チルセルロース 1.2 − 1.4%トリブ
日ピレングリコ ール O,R−1,Q%脂脂肪酸ア
ルカノ−ル ミ ド
0.9 −
1.1 %ヱチルオキシ化ケトス テラクリルアルロール 0.9− 1.1%酢酢酸フ
ェニル水銀 0.18− 0.24%塩素化パラフ
ィン炭化 水素(約42重量%の塩 素を有する2りIラフ イン22の如き、塩素化 炭化水素社如何なるも のでも用いふこと25Xで きる) 5.1 − 6.1%タ
ングステン酸ナトリ ラム 2.0 − 2.4%ペル
クロロエチレン 2.0 − 2.4%メタホウ
酸バリウム 0.9 − L1%ジイソプロピル
ケトン 1.9 − 2.3%リン酸アンモニウム
4.5 − 5.5%ヨウ化アンモニウム 2
.7 − 3J%ケイ酸(水和シリカ) 0.27
− 0.33%上記の処方の範囲内のペイント及びエ
ナメルを以て実数を行った結果、特に好まれ為処方は下
記の如きものであること力!立証された。
ルポリマー乳濁液 23 − 28 %水
41.J(−53,6%ヒドロ
キシプロピルメ チルセルロース 1.2 − 1.4%トリブ
日ピレングリコ ール O,R−1,Q%脂脂肪酸ア
ルカノ−ル ミ ド
0.9 −
1.1 %ヱチルオキシ化ケトス テラクリルアルロール 0.9− 1.1%酢酢酸フ
ェニル水銀 0.18− 0.24%塩素化パラフ
ィン炭化 水素(約42重量%の塩 素を有する2りIラフ イン22の如き、塩素化 炭化水素社如何なるも のでも用いふこと25Xで きる) 5.1 − 6.1%タ
ングステン酸ナトリ ラム 2.0 − 2.4%ペル
クロロエチレン 2.0 − 2.4%メタホウ
酸バリウム 0.9 − L1%ジイソプロピル
ケトン 1.9 − 2.3%リン酸アンモニウム
4.5 − 5.5%ヨウ化アンモニウム 2
.7 − 3J%ケイ酸(水和シリカ) 0.27
− 0.33%上記の処方の範囲内のペイント及びエ
ナメルを以て実数を行った結果、特に好まれ為処方は下
記の如きものであること力!立証された。
成 分 trPBW)アク
リルポリマー乳濁液 25.5%水
48.7%ヒドロキシ
プロピルメチ ルセルロース 1.3%トリプロピレ
ングリコ− ル
0.9形脂肪酸了ル力ノール丁ミ ド
1.0%ヱチルオキシ化ケトステ ラクリルアルコール 1.0%酢酢酸フェ
ニル水銀 0.2の塩素化パラフィン炭化
水 素 5゜7%タングステ
ン酸ナトリウ ム
2.2%ベルクロロエチレン 2
.1%メタホウ酸バリウム l・0%ジイ
ソプロピルケトン 2.1%リン酸アンモニ
ウム 5.0%ヨウ化アンモニウム
3.0%ケイ酸
0,3%上記の調合品よシ製造したペイント及びエナメ
ルを木材の如き基材に塗布しfc場合の通常のペイント
及びエナメルとの比較実験を行ったところ、製品の特性
に対する下記の如き効果が示された。
リルポリマー乳濁液 25.5%水
48.7%ヒドロキシ
プロピルメチ ルセルロース 1.3%トリプロピレ
ングリコ− ル
0.9形脂肪酸了ル力ノール丁ミ ド
1.0%ヱチルオキシ化ケトステ ラクリルアルコール 1.0%酢酢酸フェ
ニル水銀 0.2の塩素化パラフィン炭化
水 素 5゜7%タングステ
ン酸ナトリウ ム
2.2%ベルクロロエチレン 2
.1%メタホウ酸バリウム l・0%ジイ
ソプロピルケトン 2.1%リン酸アンモニ
ウム 5.0%ヨウ化アンモニウム
3.0%ケイ酸
0,3%上記の調合品よシ製造したペイント及びエナメ
ルを木材の如き基材に塗布しfc場合の通常のペイント
及びエナメルとの比較実験を行ったところ、製品の特性
に対する下記の如き効果が示された。
1、物理的外観 −変化かし。
2、使用の容易さ−変化なし7
3、接 着 性 −20%増強。
4、可 塑 性 −変化なし−
5、耐 久 性 −12%増強。
6、耐 食 性 −7%増強。
7、耐風化性 −20%増強。
8、浸 透 性 −3〜7Φ増強。
9、ペイント製造の諸工程において、この組成物はペイ
ントの色彩を変質ぜしぬない、但し、予め調製したペイ
ント製品内に組込む場合は、この調合物は亀とのペイン
トの色彩をわずかに濃色にする。
ントの色彩を変質ぜしぬない、但し、予め調製したペイ
ント製品内に組込む場合は、この調合物は亀とのペイン
トの色彩をわずかに濃色にする。
10、耐火性
セルロースを含む材料に用いる場合は特に、この組成物
は直接火炎を邑でても火の拡散を防止すゐ。
は直接火炎を邑でても火の拡散を防止すゐ。
■1合成ポリマー基材に使用の組成物
下記の組成物は向上しt難燃性及び抗酸化性を有するポ
リマー製物品を得7bK際して有用である。この組成物
は浸液、吹付は被榎塗布、調合等の既知の如何なる方法
によってもポリマー製物品上に被覆、あるいはこれに浸
漬?しめてこれを用いればよい。ある種の条件化におい
ては1組成物を重合基質に加え。
リマー製物品を得7bK際して有用である。この組成物
は浸液、吹付は被榎塗布、調合等の既知の如何なる方法
によってもポリマー製物品上に被覆、あるいはこれに浸
漬?しめてこれを用いればよい。ある種の条件化におい
ては1組成物を重合基質に加え。
重合反応の完了に際して重合物を難燃性組成物とと本に
回収することによって1組成物をポリマー製物品内へ直
接組込んで本よい。
回収することによって1組成物をポリマー製物品内へ直
接組込んで本よい。
本発明の範囲内における好ましい組成物は下記の処方の
本のである。
本のである。
成 分 量 (PBW )ポリ
塩化ビニール、例え はジオン(Geon ) 121 30.0 −50
.0%フタル酸ジオクチル 18.0 −26.
0%リン酸トリクレジル 10.0 − 15.
0%硫酸カドミウム及び/ま たれ三塩基性硫酸鉛1例 エケフエ四エムエックス (IFerroMx M 3091 ) LO−3
,0%炭酸カルシウム 6.7 − 7.0
%可塑剤1例えばセレクタ (0ereclor )552また は70 11.0−14.0%アルミ
ニウム R,O−4,0%三酸化アンチそ
ン LO−4,0%実験の結果、上記の処方の
範囲内の下記の組成物が特に好ましいものと認められた
。
塩化ビニール、例え はジオン(Geon ) 121 30.0 −50
.0%フタル酸ジオクチル 18.0 −26.
0%リン酸トリクレジル 10.0 − 15.
0%硫酸カドミウム及び/ま たれ三塩基性硫酸鉛1例 エケフエ四エムエックス (IFerroMx M 3091 ) LO−3
,0%炭酸カルシウム 6.7 − 7.0
%可塑剤1例えばセレクタ (0ereclor )552また は70 11.0−14.0%アルミ
ニウム R,O−4,0%三酸化アンチそ
ン LO−4,0%実験の結果、上記の処方の
範囲内の下記の組成物が特に好ましいものと認められた
。
成 分 量 (p:ew )ポ
リ塩化ビニール、例え ばジオン121 3g、Q%フタン
酸ジオクチル 22.2%リン酸トリクレジ
ル 12.7%硫酸カドミウム及び/ま たは三塩基性硫酸鉛1例 エハフエ四ヱムエックス (3091)1.3% 炭酸カルシウム 6.3%可塑剤1例え
ばセレクタ 3.1%丁ルミニウム(末)3.1
% 三酸化アンチモン 3.7%上記の処方に
おいて、三酸化アンチモンは同シ割合のメチルクロ胃ホ
ルムまたけタングステン酸ナトリウムを以て代えてもよ
い。
リ塩化ビニール、例え ばジオン121 3g、Q%フタン
酸ジオクチル 22.2%リン酸トリクレジ
ル 12.7%硫酸カドミウム及び/ま たは三塩基性硫酸鉛1例 エハフエ四ヱムエックス (3091)1.3% 炭酸カルシウム 6.3%可塑剤1例え
ばセレクタ 3.1%丁ルミニウム(末)3.1
% 三酸化アンチモン 3.7%上記の処方に
おいて、三酸化アンチモンは同シ割合のメチルクロ胃ホ
ルムまたけタングステン酸ナトリウムを以て代えてもよ
い。
代理人 弁理士 辻 本 −義
手続補正書(自発)
昭和57年6月2日
1、事件の表示
昭和57年特 許 願第39269 号3、 補正を
する者 事件との関係 特許出願人 4、代理人 6、補正により増加する発明の数 7、補正の対象 =445−
する者 事件との関係 特許出願人 4、代理人 6、補正により増加する発明の数 7、補正の対象 =445−
Claims (1)
- 【特許請求の範囲】 1、下肥成分を下記に示す概算量だけ含んでいる。可燃
材料に難燃性全付与する組成物:化合物番号 1、ラウリル硫酸トリヱ 0.5−0.6%(体積タノ
ールアミン 比’) (5−6mVx )2、ヨウ
化アンモニウム 2.0−7.0% 重量比(PBW
) 3、−リン酸アンモニウ 1.5−8.0%(PBWム
)4、臭化アンモ
ニウム 2.0−12.0%(PBY) 5、ホウ砂または四ホウ 1.5−20.0%CP酸ナ
トリウム BY) 6、ホウ酸 1.Fs −7,0%(P
BW) 7、硫酸アンモニウム ?(、fi −20,0%(
PBY) 8、ケイ酸ナトリウム 9.1−1.0%(体積比)
(1−1−1O/1) 9.1.2−ブ四ピレング 1.F) −10,0%(
体リコール 積比)(15−100m1/1
) 10、水 2、下記成分を下記に示す概算量だけ含んでいる、特許
請求の範囲第1項記載の組成物:化合物番号 1、ラウリル硫酸トリエ 2.0%(体積比)タノール
アミン 2、ヨウ化アンモニウム 3.5%(PBW )3、−
リン酸了ンモニウ 7.0%(PBW )ム 4、臭化アンモニウム 3.0%(PBW )5、ホ
ウ砂 2.0%(PBW )6、ホウ酸
4.0%(PBW )7、硫酸アンモニ
ウム 12.0%(pBw)8、プロピレングリコ
3.3%(体積比)−ル 9.ケイ酸ナトリウム 0.5%(体積比)10、ア
クロミシン 2.0%(PBW )11、ウンデ
シレン酸 1.0%(PBW)12、ウンデシレン
酸亜 Q、5%(IPBW )鉛 1!1.水 120.0%(PBW )
6、下記の各工程、すなわち (a) 示された概算量の化合物2. 3. 4.
5゜6及び71−均質に混合すること。 (b) 該化合物を溶解するために工程(a)の混合
物に少量の水を加え、その間化じる箭液の温度fニア0
℃またはそれ以下に保つこと、及び (C)示された量の化合物9及び1ならびに残余の水を
溶解すること。 を含む、特許請求の範囲第1項記載の可燃材料に難燃性
全付与する組成物のF、I!!製法。 4、 下記成分を下記に示す概算量だけ含んでいる。可
燃材料に難燃性全付与する組成物:塩素化パラフィン炭
化水 素(約42重量%の塩素を 有する塩素化炭化水素は 如何なるものでも用い得 る1例えばクロラフイン (0LORAFIN )22 ) 1.0−
8.0%ジイソプロピルケトン 0.5−5.0q
ツメチルクロロホルム 0.5− 5.0%タン
グステン酸ナトリウ ム
0.5 − 5.0%メタホウ酸ナトリウム
0.5− 15.0%ラウリル硫酸ナトリウム 5.
0− 15.0%ヒドロキシプロピルメチ ルセルロース 5.0− 15.0%トリ
プロピレングリコ− ル i、o
−g、o%C8〜(〕、1炭素鎖を有す る第1アルコール 1.0− 8.0%オルト
フヱニルフヱノー ル 0.1−2
.0%酢酸フェニル水銀 0.2− 2.0%
ニリン酸アンモニウム 1.0− 8.0%ラウリ
ル硫硫酸アンモタ ウ(この成分は同割合で 用いるヨウ化アンモニウ ムを以て代えてもよい)1.0− 8.0%水 5、下記成分を含んでいる。特許請求の範囲第4項記載
の組成物: 塩素化パラフィン炭化水 素 5.0%ジイソプロ
ピルケトン 2.5%メチルクロロホルム
2.5%タングステン酸ナトリウ ム
2.0%メタホウ酸ナトリウム 5
.0%ラウリル硫酸ナトリウム 10.0%ヒド
ロキシプロピルメチ ルセルロース 10.0%トリプロピ
レングリコ− ルC8””C11炭素鎖を有 する第一アルコール 2.0%オルトフヱ
ニルフヱノー ル 2.
0%酢酸フェニル水銀 0.2%ニリン酸
ナトリウム 5.0%ラウリル硫酸ナトリ
ウム /ヨウ化アンモニウム 5.0%水
45.0%6、
下記成分を下記に示す概算量だけ含んでいる。可燃材料
に難燃性を付与する組成物ニアクリルポリマー乳濁液
23 −28 %水
43.8 − 53.6%ヒドロキシプロピルメチ ルセルロース 1.2− 1.4%トリプ
ロピレングリコー ル OJ
−1,0Φ脂肪酸アルカノールアミ ド
0.9 − 1.1%ヱチルオキシ化ケトステ ラクチルアルコール 0.9 −1.1%酢酢酸
フェニル水銀 0.18−0.24%塩素化パラ
フィン炭化水 素 5.1 −6
J %タングステン酸ナトリウ ム
2.0 −2.4 %ベルク目ロエチレン
2.0 −2.4%メタホン酸バリウム 0.
9 −1.1%ジイソプロピルケトン 1.9 −
2.3%リン酸アンモニウム 4.5 −5.5
%ヨウ化アンモニウム 2.7 −3.1%ケイ
酸(水和シリカ)0.27−0.93%7、 下記成分
を下記に示す概算量だけ含んでいる一特許請求の範闘第
6項記載の組成物:成 分
fJ−(PBW)アクリルポリマー乳濁液
25.5%水
48.7%ヒドロキシプロピルメチ □ ルセル覧−ス 113%トリプロピレ
ングリコ− ル 0.
9%月d肪酸アルカノールアミ ド
1.θ%ヱチルオキシ化ケトステ ラクチルアルコール 160%酢酸フヱニル
水銀 0.2%塩素化パラフィン炭化水 素 5.7%タングステ
ン酸ナトリウ ム
2.2%ベルクロロエチレン 2.
1%メタホウ酸バリウム 1.0%ジイソ
プロピルケトン 2゜1%リン酸アンモニウム
5.0%ヨウ化アンモニウム
3.0%ケイ酸 9.3形8
、下記成分を下記に示す概算量だけ含んでいる。可燃材
料に離燃性を付与する組成物:成 分
11(PBW )ポリ塩化ビニル
30.0− 50.0%フタン酸ジオクチル
18.0− 26.0%リン酸トリクレジル
10.0− 15.0%硫酸カドミウム及び/ま たは三塩基性硫酸鉛 1.0− 3.0%炭酸カ
ルシウム 6.0− 7.0%可市剤
11.0− 14.0%アルミニウム
?(,0−4,0%三酸化アンチモン
3.0− 4.0%9、 下記成分を下記に示す
概算量だけ含んでいる、特許請求の範囲第8項記載の組
成物;成 分 j敬(P
BW)ポリ塩化ビニル 38.0%フタ
ル酸ジオクチル 22.2%リン酸トリクレ
ジル 12.7%硫酸カドミウム及び/ま たは三塩基性硫酸鉛 1.3%炭酸カルシウ
ム 6.3%可塑剤
3.1%アルン二ウつ(粉末)3.1% ヨ酸化丁yチモン 3.7%