JPH11269031A - Transparent sheet-form cosmetic material, production thereof and makeup method - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain the subject cosmetic material having excellent appearance effects such as touch feeling, high adhesion and visible improving effect of a state of the skin, and also improving effects of small wrinkles, skin roughness and moisture holding by including a thickening agent, a humectant, a physiologically active component and water, and also making its appearance as a transparent gel state sheet. SOLUTION: This transparent sheet-form cosmetic material contains (A) a thickening agent, (B) a humectant, (C) a physiologically active component and (D) water and consists of a gel state sheet having a colorless transparent or a colored transparent outlook. Preferably, as the component (A), 3-10 wt.% carrageenan, as the component (B), 1-30 wt.% one or more kinds a polyhydric alcohol, a saccharide and a sugar alcohol, as the component (C), 0.001-1 wt.% hyaluronic acid and/or its salt and as the component (D), the rest amount of a purified water are contained therein. The thickness of the sheet is preferably 0.1-3 mm. The objective cosmetic material is obtained by filling a liquid material consisting of the components (A)-(D) in recessed parts having 0.1-3 mm depth formed on a sheet member such as a polyethylene and then solidifying the filled material by heat polymerization, etc.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

TECHNICAL FIELD The present invention relates to a touch,
A non-lip transparent sheet-shaped cosmetic which is excellent in appearance, has an effect of improving fine wrinkles, an effect of improving skin turnover, a slimming effect, a massage effect, a moisturizing effect, an effect of improving a bear, etc. About the method.

[0002]

2. Description of the Related Art The present inventors have disclosed in Japanese Patent Application No. 9-231799.
Proposed a transparent sheet pack for the lips. The lip sheet-like pack material can observe the improved state of the adhered lips by color change of the lips, and has various effects such as a moisturizing effect and an effect of improving lipstick glue. On the other hand, recently, a sheet-like product in which a plaster is applied to a nonwoven fabric, which is applied to the entire face, cheeks, legs, and the like, has attracted attention.
These products are characterized by a cool sensation and excellent use sensation.

[0003]

However, a sheet-like product in which a plaster is held on a support such as a non-woven fabric has a somewhat satisfactory feel, but the appearance is poor due to the presence of the support. If the rigidity of the body is high, there is a problem that the body does not conform to the shape of the sticking portion and floats from the skin.

[0004]

Means for Solving the Problems The present inventors have made intensive studies on these problems, and as a result, have developed a transparent sheet cosmetic for skin utilizing the technology of a lip sheet pack. It was prepared and applied to the skin of the face, arms, legs, chest, abdomen, etc., and the excellent touch, high adhesion, and transparency made it possible to confirm the area where the skin was stuck and easy to stick. In addition to the excellent appearance effect that the skin condition improvement effect is visible during application, it also has the effect of improving fine wrinkles, improving skin turnover (such as improving rough skin), slimming effect, massage effect, and moisturizing. It was found that the effect and the effect of improving the bear were improved.

That is, a first aspect of the present invention is a non-lip transparent lip comprising a gel sheet which contains a viscous agent, a wetting agent, a physiologically active ingredient and water and has a colorless transparent or colored transparent appearance. The present invention relates to a sheet cosmetic.

A second aspect of the present invention is to provide a copolymer of acrylamide and a crosslinkable monomer, a polyacrylamide crosslinked by an epoxy crosslinking agent, carrageenan, hyaluronic acid and salts thereof, deoxyribonucleic acid and salts thereof. And at least one kind selected from the group consisting of the above-mentioned transparent sheet-shaped cosmetics.

A third aspect of the present invention is that the humectant is glycerin,
The present invention relates to the above transparent sheet-shaped cosmetic, which is one or more selected from the group consisting of diglycerin, polyethylene glycol, 1,3-butylene glycol, sorbitol, and malvit.

A fourth aspect of the present invention is to fill a concave portion having a depth of 0.1 to 3 mm formed in a sheet member with a liquid material comprising a raw material of a tackifier, a wetting agent, a physiologically active ingredient, and water, and then heat the liquid. The present invention relates to a method for producing the transparent sheet-like cosmetic, characterized in that the filler in the concave portion is solidified by applying and then cooling, or by heating and polymerizing, or by irradiating light.

A fifth aspect of the present invention is to provide a cosmetic composition containing at least 1% by weight of an oil in a preparation after the transparent sheet-shaped cosmetic composition of the present invention is applied to a skin site other than the lips and peeled off. The present invention relates to a cosmetic method characterized by being used for cosmetics.

[0010]

BEST MODE FOR CARRYING OUT THE INVENTION The thickener used in the present invention has a higher affinity for water and has a property of thickening, and its aqueous solution is transparent or almost transparent and has almost no coloring. As long as there is no problem, tackifiers conventionally used in foods and cosmetics, particularly polymer-based tackifiers, can be used. For example, a copolymer of acrylamide and a crosslinkable monomer, polyacrylamide cross-linked by an epoxy cross-linking agent, carrageenan, hyaluronic acid and its salt, deoxyribonucleic acid and its salt, carboxyvinyl polymer and its modified product, polyacrylic acid And its salts, gellan gum, agar and the like. Among them, one or two selected from the group consisting of a copolymer of acrylamide and a crosslinkable monomer, polyacrylamide crosslinked by an epoxy crosslinker, carrageenan, hyaluronic acid and salts thereof, deoxyribonucleic acid and salts thereof The above adhesive is
It is preferable because the transparency and feel of the product are excellent.

Examples of the crosslinkable monomers include N,
N'-methylenebisacrylamide, N, N'-methylenebismethacrylamide, N, N'-ethylenebisacrylamide, N, N'-ethylenebismethacrylamide, 1,2-diacrylamideethylene glycol and the like.

Examples of the above epoxy crosslinking agent include ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, triglycidyl 2-hydroxyethyl isocyanurate, trimethylolpropane polyglycidyl ether, glycerin polyglycidyl ether, sorbitol polyglycidyl ether and the like. Is mentioned.

[0013] The carrageenan can be selected from commercially available iota type, kappa type, lambda type and a mixture thereof.

In the transparent sheet cosmetic of the present invention, when a synthetic polymer such as acrylamide is used as a thickener,
The compounding amount of the adhesive is preferably 5 to 40% by weight, more preferably 10 to 25% by weight, based on the total amount of the product. If the blending amount is less than 5% by weight, the waist strength of the gel body is too weak, and it is difficult to keep the wetting agent or water contained in the structure of the gel body in a stable state, and if it exceeds 40% by weight, the gel strength is increased. However, the polymer structure in the gel body tends to be too dense and the amount of a wetting agent, water, etc. that can be retained tends to be too small.

In the transparent sheet cosmetic of the present invention, when a crosslinkable monomer is added at the time of polymerization when a synthetic polymer is used as a thickener, the amount of the crosslinkable monomer added is the total amount of the above gel body. Is preferably 0.3% by weight or less.
If the amount is larger than this, the brittleness of the gel body increases, and the gel body tends to be cut or broken by tension or compression.

In the transparent sheet cosmetic of the present invention, when an epoxy cross-linking agent is added at the time of polymerization when a synthetic polymer is used as a thickener, the amount of the epoxy cross-linking agent to be added depends on the required adhesive performance, flexibility and gel. It may be appropriately determined according to the polymer skeleton and its composition ratio, but is preferably 3% by weight or less based on the total amount of the gel body. If it exceeds 3% by weight, there is a problem that the adhesive performance is reduced, the brittleness of the gel body is increased, and cutting or breaking due to tension or compression is apt to occur.

In the transparent sheet cosmetic of the present invention, when a natural polymer such as carrageenan is used as a sticking agent, the amount of the sticking agent is preferably 0.5 to 20% by weight, more preferably the total amount of the product. Is 1 to 10% by weight. If the amount is less than 0.5% by weight, the obtained gel is insufficient in strength and not practical. If the amount exceeds 20% by weight, the gel is very hard and has no tackiness at all, and may not be suitable for use. When carrageenan is used, K, Ca, Mg
The strength of the gel can be adjusted by adding a metal salt such as The addition amount of these salts is preferably in the range of 0.01 to 1% by weight based on the total amount of the product.

As the humectant used in the present invention, those which have been conventionally used in cosmetics, such as polyhydric alcohols, can be used. Examples of the humectant include polyhydric alcohols such as glycerin, diglycerin, polyglycerin, ethylene glycol, diethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, polypropylene glycol, 1,3-butylene glycol, isoprene glycol, and sorbitol. Saccharides, sugar alcohols and the like. Of these,
Glycerin, diglycerin, polyethylene glycol,
1,3-butylene glycol, sorbitol and malbit are preferred because they can easily ensure transparency and are excellent in wetting action.

The compounding amount of the wetting agent used in the transparent sheet cosmetic of the present invention is 0.1 to 80 with respect to the total amount of the product.
% By weight is preferred. If the amount is less than 0.1% by weight, it is difficult to sufficiently maintain the necessary water content. If the amount exceeds 80% by weight, the wetting agent may separate from the sheet and cause stickiness.

The physiologically active ingredient used in the present invention is a synergistic effect such as a fine wrinkle improving effect, a turnover improving effect, a slimming effect, a massage effect, a moisturizing effect, a bear improving effect, etc., and any effective effect on the skin. For example, ceramides, cerebrosides, vitamins, menthol, propolis, hyaluronic acid and its salts, deoxyliponucleic acid and its salts, amino acids, organic acids such as hydroxy acids, glycoproteins such as lactoferrin, enzymes , A blood circulation promoting agent, an astringent, a slimming agent, an anti-inflammatory agent, and the like. In addition, there are components derived from plants and seaweed. For example, ashitaba extract, avocado extract,
Amacha extract, Altea extract, Arnica extract, Aloe extract, Apricot extract, Apricot kernel extract, Ginkgo extract, Fennel extract, Turmeric extract, Oolong tea extract, Age extract, Echinashi leaf extract, Ohgon extract, Obaaku extract, Ouren extract, Barley extract, St. John's wort extract, Spice lily extract, Dutch mustard extract, orange extract, seawater dried product, seaweed extract, hydrolyzed elastin, hydrolyzed wheat powder, hydrolyzed silk, chamomile extract, carrot extract, sagebrush extract, licorice extract, calcade extract, kiwi extract , Kina extract, cucumber extract, guanosine, gardenia extract, kumazasa extract, clara extract,
Walnut extract, grapefruit extract, clematis extract, chlorella extract, mulberry extract, gentian extract, black tea extract, yeast extract, burdock extract, rice bran extract, rice germ oil, comfrey extract, collagen, lingonberry extract, psychin extract, psycho extract,
Sai Thai extract, Salvia extract, Soapwort extract,
Sasa extract, Hawthorn extract, Sansho extract, Shiitake mushroom extract, Jio extract, Shikon extract, Perilla extract, Shinanoki extract, Shimotsusou extract, Peony extract, Shobu root extract, Birch extract, Japanese horse chestnut extract, Acacia edulis extract, Acacia faba extract, Acacia edulis extract, Acacia edulis extract Yarrow extract, mint extract, sage extract, mallow extract, senkyu extract, assembly extract, soybean extract, syrup extract, thyme extract, tea extract, clove extract, scotch extract, chimpanzee extract, squid extract, calendula extract, tonin extract, spruce extract, dokudami Extract, tomato extract, natto extract,
Carrot extract, garlic extract, nobara extract, hibiscus extract, Bakmondou extract, parsley extract,
Honey, Hamamelis extract, Parietaria extract, Hioki sorghum extract, Bisa bolol, Loquat extract, Coltsfoot extract, Fukinotou extract, Bucurio extract, Butcher bloom extract, Grape extract, Propolis, Loofah extract, Safflower extract, Peppermint extract, Bodaiju extract, Button extract, Hop extract Extract, pine extract, horse chestnut extract, mugwort extract, mukuroji extract, melissa extract, peach extract, cornflower extract, eucalyptus extract, saxifrage extract, yuzu extract,
Yokuinin extract, mugwort extract, lavender extract,
Examples include apple extract, lettuce extract, lemon extract, astragalus extract, rose extract, rosemary extract, Roman chamomile extract, royal jelly extract and the like. Among these physiologically active components, components derived from plants and seaweeds, hyaluronic acid and salts thereof are preferable from the viewpoint of image and effect on skin.

The amount of these physiologically active ingredients cannot be specified unconditionally because the amount of the active ingredient varies depending on the material, but for example, 0.001 to 80% by weight based on the total amount of the product.
And particularly preferably 0.05 to 10% by weight.

The amount of water used in the transparent sheet cosmetic of the present invention is 10 to 95% by weight based on the total amount of the product.
Is preferred. If the amount is less than 10% by weight, sufficient moisture cannot be given to the skin surface, and if it exceeds 95% by weight, it may be difficult for the gel body to maintain a sheet shape.

Examples of particularly preferred component combinations of the present invention are shown below. (A) 3-10% by weight of carrageenan (B) One or more of polyhydric alcohols, sugars and sugar alcohols 1 to 30% by weight (C) Hyaluronic acid and / or its salt 0.001 to 1% by weight (D) Purified Water Remaining When such a combination is used, feel, adhesion, transparency, effectiveness on skin, and the like are easily obtained.

The gel of the transparent sheet cosmetic of the present invention may be colored with a pigment or the like, but it is necessary to have a transparent to almost transparent appearance. The term "transparent" as used in the present invention means that when a sheet-shaped cosmetic is placed on white high-quality paper on which 20-point characters are printed in black, transparency is high enough to indicate that the characters are present. Is preferred.

The thickness of the sheet of the transparent sheet-shaped cosmetic of the present invention may be uniform as a whole or partially different in thickness, but the adhesion, transparency and strength are ensured. Therefore, a thickness of 0.1 to 3 mm is preferable. If it is less than 0.1 mm, the strength of the sheet is weak, and if it exceeds 3 mm, the sheet may be too heavy and lack adhesion. still,
If the entire sheet is not thick, partially cut the sheet
It is possible to increase the thickness up to m.

In the transparent sheet-shaped cosmetic of the present invention, if necessary, in addition to the tackifier, powders (dyes, resins, etc.), oils, fluorine compounds, resins, surface active agents which can be used in general cosmetics are used. Components such as an agent, an ultraviolet absorber, a preservative, a perfume, a salt, a solvent, a chelating agent, a neutralizing agent, and a pH adjuster can be simultaneously added. However, among the above additives, it is necessary not to add an additive that makes the sheet-shaped cosmetic opaque, or to use a small amount of the additive in a range that does not make the opaque additive.

As a method for producing the transparent sheet-shaped cosmetic of the present invention, for example, a sheet member made of polypropylene, polyethylene, polyester, polyvinyl chloride, or the like is used. 1-3
After filling a liquid material composed of a raw material of a viscosity agent, a wetting agent, water, etc. into a concave portion of mm, heat and then cool, or polymerize by heating, or polymerize by irradiating light. And a method of solidifying the filler in the concave portion. By this method, it is possible to produce a large amount of a gel-like sheet in a short time in a shape that fits the skin site to which the sheet-like cosmetic is to be adhered, and it is not necessary to punch and mold the gel. In addition, the generation of gel to be discarded is suppressed, and the gel does not come into contact with the extraction blade, which is advantageous in terms of hygiene.

In the case where a monomer is polymerized into a viscous agent, azobiscyanovaleric acid or azobisaminopropane dihydrochloride may be used when thermally polymerizing a monomer solution containing the above-mentioned raw materials. Azo polymerization initiators such as salts, and redox polymerization initiators composed of reducing agents such as ferrous sulfate, dithionous acid, and pyrosulfite and peroxides such as hydrogen peroxide and peroxodisulfate. It can be added and polymerized. Also,
In the case of photopolymerization, photoradical polymerization initiators such as acetophenone, benzoin ether, phosphorus, benzophenone, thioxanthone, and azo, and cationic photopolymerization initiators such as diazonium salts, diallyliodonium salts, and triarylsulfonium salts. Polymerization can be carried out by adding such a compound.

When carrageenan or the like is used, it can be obtained by heating a mixture obtained by mixing the above-mentioned raw material and powdered carrageenan and thoroughly mixing the mixture to about 80 to 100 ° C., and then cooling the mixture.

The shape of the transparent sheet-shaped cosmetic of the present invention may be elliptical, circular, heart-shaped, semi-circular, semi-elliptical, square, rectangular, trapezoidal, etc., but is not particularly limited. Further, a convex portion or a concave portion may be provided in the center portion or the peripheral portion for the purpose of alignment and improvement of usability. In addition, the center portion, the up / down direction, and the front / back direction may be specified by a method such as printing. Further, the shape, the thickness, the composition, and the adhesive strength may be changed depending on the use site.

The parts to which the transparent sheet-shaped cosmetic of the present invention is applied include the face (the cheeks other than the lips, the eyes, the mouth, the upper and lower parts of the eyes), the arms, the legs, the chest, the abdomen, the neck and the like. No.
It is preferable to increase the adhesive strength of the sheet-shaped cosmetic or to make the sheet thinner at a portion where the area to be stuck is large.

The transparent sheet cosmetic of the present invention has high adhesiveness and is transparent, so that the effect of improving the skin can be seen through the adhered sheet cosmetic, and because it is transparent, it can be accurately applied to a predetermined site. Although it basically has the effect of excellent appearance, the expected effect may differ depending on the application site. For example, when applied to the face, it can be expected to improve fine wrinkles, improve skin turnover, massage effects, moisturizing effects, promote blood circulation, improve bears, and cool down, and apply to arms, legs, and abdomen If you do, you can expect a slimming effect, massage effect, moisturizing effect, cooling effect, at the neck, you can expect fine wrinkle improvement, massage effect, moisturizing effect, cooling effect, at the chest, massage effect, moisturizing effect, cooling effect, A shaping effect can be expected. These effects are obtained by synergy between the pack effect of the transparent sheet-shaped cosmetic itself and the effect of the blended physiologically active ingredient.

The method of using the transparent sheet-like cosmetic of the present invention is as follows.
It is preferable to leave for 0 minutes, particularly preferably 1-3
It is preferable to leave the sheet for 0 minutes and then peel off the sheet. The frequency of use is preferably about once a day to about three times a week. However, twice or more times a day may burden the skin.

The transparent sheet-shaped cosmetic composition of the present invention is prepared by adhering to the site of application and peeling, and then adding oil such as fats and oils, hydrocarbons, higher fatty acids, higher alcohols and esters to the preparation in an amount of 1% by weight or more. It is preferable to use a cosmetic such as a milky lotion or a cream in the site, and it is particularly preferable to perform a massage using these cosmetics. By continuing this makeup method, skin turnover and skin condition can be further improved. With a cosmetic having an oil content of less than 1% by weight, the above effect due to the massage effect is difficult to obtain.

[0035]

The present invention will be described in more detail with reference to the following Examples and Comparative Examples. The method for evaluating sensory characteristics used in the present invention is as follows.

Using 20 specialized panelists, the sensory characteristics of the prototype were evaluated by a one-month continuous test in winter. As an evaluation item, whether or not an effect corresponding to the application site was recognized was evaluated in a questionnaire format. When the effect was not recognized, it was set to 0 points, and when the effect was recognized, it was set to 5 points. During that period, the evaluation was performed in a total of 4 levels, and the evaluation result was obtained by using the total score of all the members. Therefore, the higher the score, the higher the evaluation. The transparency was determined based on whether or not the characters were found when the sheet-shaped cosmetic was placed on white high-quality paper on which 20-point characters were printed in black.

Example 1 A slimming gel sheet for abdomen was prepared by the following composition and manufacturing method.

[0038]

[Table 1]

After the above mixture is stirred to be uniform,
Heated to 95 ° C. to dissolve. One piece of this liquid is 12cm
Pour into a silicone-treated polyethylene dish (a) having a concave portion having a depth of 2 mm and a 70 μm-thick release film of a silicone-treated polyethylene film (b) on top, and The periphery of (b) was sealed by thermocompression bonding, and then cooled and solidified to obtain a transparent gel-like sheet product.

When the product was used, the release paper of (b) was peeled from the polyethylene plate of (a) to take out a transparent gel-like sheet, which was then attached to the abdomen for use. The use time was set for 15 minutes.

Example 2 A gel sheet for improving a bear was prepared by the following composition and production method.

[0042]

[Table 2]

A polymerization initiator was added to a liquid mixture of monomers and the like adjusted to 4 ° C. (well stirred), and the mixture was stirred well.
It is poured into a semicircular dish with a long diameter of 30 mm, a short diameter of 10 mm, and a depth of 0.7 mm made by thermoforming a polypropylene sheet having a thickness of 00 μm, placing a transparent polyurethane film having a thickness of 30 μm on top, and then 50 mW / cm 2 ^A polymerization reaction was performed by irradiating ultraviolet light of intensity ² for 60 seconds. The resulting transparent gel-like sheet, together with the upper film and the lower dish,
The product was obtained by punching into a semicircle, which was slightly larger than the gel portion, so that a 2 mm wide edge remained around the gel portion.

When the product was used, a transparent gel-like sheet was taken out and used by attaching it to a portion where a dark circle easily formed under the eyes. The use time was set for 15 minutes.

Example 3 A gel sheet for the chest was prepared by the following composition and manufacturing method.

[0046]

[Table 3]

After the above mixture is stirred to be uniform,
Heated to 95 ° C. to dissolve. This liquid is 13cm in diameter
Into a silicone-treated polyethylene dish (a) having a concave portion having a depth of 2 mm and placing a release paper (b) of a silicone-treated polyethylene film having a thickness of 70 μm on the top, and then (a) And (b) were sealed by thermocompression bonding, and then cooled and solidified to obtain a product.

When using the product, the film of (b) was peeled off from (a), and a transparent gel-like sheet was taken out.
It was attached to the chest and used. The use time was set at 10 minutes.

Example 4 A gel sheet for improving wrinkles around the eye was prepared by the following composition and production method.

[0050]

[Table 4]

A polymerization initiator was added to a mixture of monomers and the like adjusted to 4 ° C. (well stirred), and the mixture was stirred well.
A polypropylene sheet having a thickness of 30 μm is formed by thermoforming a polypropylene sheet having a thickness of 30 μm, and is poured into a half-moon shaped dish having a rounded periphery having a diameter of 30 mm and a depth of 0.7 mm. Milliwatt / cm
^A polymerization reaction was performed by irradiating ultraviolet light of intensity ² for 60 seconds.
The resulting transparent gel-like sheet was punched into a half-moon shape, which was slightly larger than the upper film and the lower plate, so that a 2 mm wide edge remained around the gel portion.

When the product was used, the gel-like sheet was taken out, and the gel sheet was stuck and used while well extending the wrinkled portion of the outer corner of the eye. The use time was set for 15 minutes.

Example 5 A gel sheet for a leg was prepared by the following composition and production method.

[0054]

[Table 5]

After the above mixture is stirred to be uniform,
Heated to 95 ° C. to dissolve. When this solution has a major axis of 20c
m, silicone-treated polyethylene dish having a rectangular shape with a minor axis of 10 cm and a concave portion having a depth of 2 mm (a)
And a release paper (b) of a silicone-treated polyethylene film having a thickness of 70 μm is placed on the top, and then (a)
And (b) were sealed by thermocompression bonding, and then cooled and solidified to obtain a product.

When using the product, the film of (b) was peeled off from (a), and a transparent gel-like sheet was taken out.
It was attached to the legs and used. The use time was set for 15 minutes.

Example 6 After using the slimming gel sheet for abdomen of Example 1,
The use site of the sheet was massaged well using a commercially available emulsion. This emulsion contained about 6% by weight of oil.

Example 7 After using the bear-improving gel sheet of Example 2, the site where the sheet was used was massaged well using a commercially available moisturizing cream. The moisturizing cream had an oil content of about 20% by weight.

Example 8 After using the gel sheet for improving wrinkles around the eye of Example 4, the area where the sheet was used was thoroughly massaged using a commercially available moisturizing essence. The moisturizing essence contained about 2% by weight of oil.

Comparative Example 1 The abdomen was massaged well using a commercially available emulsion.

Comparative Example 2 Using a commercially available massage cream, the area under the eyes was well massaged.

Comparative Example 3 The chest was massaged well using a commercially available body lotion.

COMPARATIVE EXAMPLE 4 A comparative example was provided with a moisturizing pack for the outer corners of the eye, in which a plaster body (a system of polyvinyl alcohol and polyhydric alcohol, not containing sodium hyaluronate) was applied to a commercially available brushed opaque nonwoven fabric. Used in the same manner as 4. Was.

Comparative Example 5 A comparative example was provided with a leg cooling sheet of a type in which a plaster body (a system of polyvinyl alcohol and polyhydric alcohol, not containing sodium hyaluronate) was applied to a commercially available brushed opaque nonwoven fabric. Used as in 5.

Tables 6 to 11 show evaluation results of Examples and Comparative Examples. In Table 6, the transparency and adhesiveness of each of the examples and comparative examples were evaluated.

[0066]

[Table 6]

From the results shown in Table 6, it was found that each example of the present invention was excellent in transparency and was characterized by its appearance. Further, it was found that each of the examples of the present invention was also excellent in adhesion. However, it was found that if the film was left attached for a long time, the film might be gradually peeled off, but all of these occurred only when the film was used for longer than the specified time. On the other hand, in the comparative example using the nonwoven fabric, the nonwoven fabric could not adhere to the movement of the face or the like, and a phenomenon such as the sheet floating in a relatively short time was observed.

[0068]

[Table 7]

[0069]

[Table 8]

[0070]

[Table 9]

[0071]

[Table 10]

[0072]

[Table 11]

From the results of Tables 7 to 11, it was found that the sheet-like cosmetics of Examples of the present invention were transparent and easy to use, and exhibited excellent effects for all evaluation items. . Table 7 shows the evaluation results of the slimming gel sheet for abdomen and the method of applying the same. The effect of the sheet gel preparation for the purpose of slimming was obtained as compared with the case where an emulsion was used. Table 8 relates to a gel sheet for improving a bear and a method of applying the same. The result shows that the effect of improving the bear was excellent as compared with the case where a massage cream effective for promoting blood circulation was used. Table 9 relates to the gel sheet for the chest, and was excellent in the effect of adjusting the shape of the chest.
Table 10 relates to a gel sheet for improving wrinkles around the eyes and a method for making up the gel sheet, and was excellent in the effect of improving fine wrinkles and the effect of improving turnover. Especially about the feeling of use,
Each of the examples had a feature that the sense of tension was small when they were brought into close contact with each other, but the comparative example 4 was easier to use than the example 4,
The feel was also bad. Table 11 relates to the gel sheet for legs. Example 5 was excellent in the slimming effect and feel of the legs, but Comparative Example 5 was inferior in use and feel compared to Example 5.

[0074]

From the above results, the non-lip transparent sheet-shaped cosmetic of the present invention is excellent in ease of use, feel and appearance, effects of improving fine wrinkles, improvement of skin turnover, slimming effect, massage effect. It is clear that the makeup method of applying the makeup after using the transparent sheet-shaped cosmetic of the present invention is excellent in the moisturizing effect, the effect of improving the bear and the like, and it is clear that a higher effect can be obtained.

Continuation of the front page (51) Int.Cl. ⁶ Identification code FI A61K 9/70 329 A61K 9/70 329 370 370 (72) Inventor Masayuki Matsumoto 5-28-3 Kotobukicho, Odawara-shi, Kanagawa Kanebo Co., Ltd. Inside the Cosmetic Research Laboratory (72) Inventor Takashi Higashi 670 Morimoto-cho, Tenri-shi, Nara Sekisui Plastics Industry Co., Ltd. (72) Inventor ▲ Hata ▼ Atsuko 670 Morimoto-cho, Tenri-shi, Nara Sekisui Plastics Co., Ltd. Within the Research Institute

Claims (5)

[Claims] 1. A non-lip transparent sheet-like cosmetic comprising a viscous agent, a wetting agent, a physiologically active ingredient and water and comprising a colorless transparent or colored transparent gel-like sheet. 2. The adhesive is selected from the group consisting of a copolymer of acrylamide and a crosslinkable monomer, polyacrylamide crosslinked by an epoxy crosslinking agent, carrageenan, hyaluronic acid and salts thereof, deoxyribonucleic acid and salts thereof. The transparent sheet-shaped cosmetic according to claim 1, wherein the transparent sheet-shaped cosmetic is one or more kinds. 3. The humectant is glycerin, diglycerin,
The transparent sheet-like cosmetic according to claim 1 or 2, wherein the cosmetic is at least one selected from the group consisting of polyethylene glycol, 1,3-butylene glycol, sorbitol, and malvit. 4. A depth of 0.1 to 3 formed in the sheet member.
After filling a liquid material consisting of a raw material of a viscosity agent, a wetting agent, a physiologically active ingredient, and water into a concave part of mm, polymerizing by heating or cooling, or heating, or irradiating light The method for producing a transparent sheet-like cosmetic according to any one of claims 1 to 3, wherein the filler in the concave portion is solidified by doing so. 5. A cosmetic containing the oil content of 1% by weight or more in the preparation after the transparent sheet-like cosmetic according to any one of claims 1 to 3 is applied to a skin site other than the lips and peeled off. A cosmetic method, wherein the method is applied to the skin site.