JPH1086284A - Deep-drawn packaging body for boiling - Google Patents
Deep-drawn packaging body for boilingInfo
- Publication number
- JPH1086284A JPH1086284A JP24936096A JP24936096A JPH1086284A JP H1086284 A JPH1086284 A JP H1086284A JP 24936096 A JP24936096 A JP 24936096A JP 24936096 A JP24936096 A JP 24936096A JP H1086284 A JPH1086284 A JP H1086284A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- composite film
- polypropylene resin
- outermost
- outermost layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、深絞り成形による
底材と中間印刷を施こした蓋材からなる包装体に係り、
ボイル殺菌等のボイル処理によりヒートシール部分のカ
ールや、波打ち現象を防止できる深絞り包装体に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a package comprising a bottom member formed by deep drawing and a lid member subjected to intermediate printing.
The present invention relates to a deep-drawn package that can prevent curling of a heat-sealed portion and waving phenomenon by boil processing such as boil sterilization.
【0002】[0002]
【従来の技術及びその課題】従来、深絞り成形による底
材と印刷を施こした蓋材からなる包装体が各種食品の包
装に使用され、その蓋材としては、二軸延伸ポリプロピ
レンフイルム、二軸延伸ポリエステルフイルム、Kコー
トセロファン等で構成されるドライラミネートフイルム
で層中間部分に印刷を施したものが主に使用されてい
る。このような包装体を内容物と共にボイル殺菌等のボ
イル処理を行なうと、底材と蓋材との面シール部分にカ
ールや、波打ちが発生するという問題があった。2. Description of the Related Art Conventionally, a package comprising a bottom material formed by deep drawing and a printed lid material has been used for packaging various foods. The lid material may be a biaxially stretched polypropylene film, A dry laminate film composed of an axially stretched polyester film, K-coated cellophane, or the like and having a printed portion in the middle of the layer is mainly used. When such a package is subjected to boil treatment such as boil sterilization together with the contents, there is a problem that curling or waving occurs in the surface seal portion between the bottom material and the lid material.
【0003】また、ドライラミネートフイルムに代え
て、共押出フイルムからなる蓋材と底材を使用した包装
体ではボイル処理による上記カールや、波打ち現象は良
くなるが、表面しか印刷できないという問題があった。In a package using a lid and a bottom made of a co-extruded film instead of a dry laminate film, the curl and waving phenomenon caused by the boil treatment are improved, but there is a problem that only the surface can be printed. Was.
【0004】[0004]
【課題を解決するための手段】本発明は、上記問題点を
解消できるボイル用深絞り包装体を見出したものであっ
て、その要旨とするところは、蓋材と底材とからなるボ
イル用深絞り包装体であって、蓋材が最外層から無延伸
ポリプロピレン樹脂層、印刷層、共押出複合フイルムを
有し、底材がポリアミド樹脂層を含み、かつ最外層に無
延伸ポリプロピレン樹脂層を有することを特徴とするボ
イル用深絞り包装体にある。SUMMARY OF THE INVENTION The present invention has found a deep-drawing package for a boil which can solve the above-mentioned problems. The gist of the present invention is to provide a deep-drawing package for a boil comprising a lid material and a bottom material. In a deep drawn package, the lid material has an unstretched polypropylene resin layer from the outermost layer, a printing layer, a coextruded composite film, the bottom material includes a polyamide resin layer, and the outermost layer has an unstretched polypropylene resin layer. A deep drawn package for boiling characterized by having
【0005】[0005]
【発明の実施の形態】本発明は蓋材と底材からなるボイ
ル用深絞り包装体であって、蓋材と底材の両方を特定の
層構成としたものである。蓋材については、最外層から
無延伸ポリプロピレン樹脂層、印刷層、共押出複合フイ
ルム層を配したものであり、最外層の無延伸ポリプロピ
レン樹脂(以下「CPP」という)層に使用する樹脂に
はホモポリマーやエチレン等とのランダムコポリマーが
使用できるが、フイルムの腰を強くするためにはホモポ
リマーを使用することが好ましい。蓋材の最外層にCP
P層を配することにより、ボイル処理によるカールや、
波打ち現象を防止できる。BEST MODE FOR CARRYING OUT THE INVENTION The present invention relates to a deep-drawing package for boil comprising a lid material and a bottom material, wherein both the lid material and the bottom material have a specific layer structure. As for the lid material, an unstretched polypropylene resin layer, a printing layer, and a co-extruded composite film layer are arranged from the outermost layer, and the resin used for the outermost unstretched polypropylene resin (hereinafter referred to as “CPP”) layer is: A homopolymer or a random copolymer with ethylene or the like can be used, but it is preferable to use a homopolymer in order to strengthen the film. CP on the outermost layer of the lid
By arranging the P layer, curling due to boiling processing,
The waving phenomenon can be prevented.
【0006】さらに、上記最外層としてはヤング率50
〜90kg/cm2 (測定法:JISK7127に準
拠)の範囲のCPPフイルムを使用するのが好ましく、
ヤング率が50kg/cm2 未満ではラミネート時にフ
イルムが伸びやすいため、歪みとなり、ボイル処理時の
カールや波打ちの原因となりやすく、90kg/cm2
を越えるフイルムでは、ボイル処理による波打ち現象が
発生しやすいという傾向がある。また、共押出複合フイ
ルム層に使用する共押出複合フイルムとしては、各種層
構成の複合フイルムが使用でき、ヒートシール層や、耐
ピンホール性、成形性を付与するためのポリアミド樹脂
からなる中間層を配し、さらにガスバリア性が要求され
る場合には、エチレンービニルアルコール共重合体(以
下「EVOH」という)を含む複合フイルムとするもの
である。Further, the outermost layer has a Young's modulus of 50
It is preferable to use a CPP film in a range of up to 90 kg / cm 2 (measurement method: based on JIS K7127),
Since Young's modulus film is stretchy during lamination is less than 50 kg / cm 2, becomes distorted easily cause curling or waving during boiling treatment, 90 kg / cm 2
In the case of a film having a thickness of more than, there is a tendency that a waving phenomenon due to the boil processing is likely to occur. Also, as the co-extruded composite film used for the co-extruded composite film layer, composite films having various layer configurations can be used, and a heat seal layer, an intermediate layer made of a polyamide resin for imparting pinhole resistance and moldability. When a gas barrier property is required, a composite film containing an ethylene-vinyl alcohol copolymer (hereinafter referred to as "EVOH") is obtained.
【0007】上記のポリアミド樹脂としては、ナイロン
6、ナイロン66、ナイロン6/66、ナイロン6T/
6I等が好適に使用できる。また、EVOHとしては、
エチレン含有率が30〜50モル%で、けん化度が95
%以上のものが、成形性やガスバリアー性の点から好ま
しい。The above polyamide resins include nylon 6, nylon 66, nylon 6/66, nylon 6T /
6I or the like can be suitably used. Also, as EVOH,
Ethylene content of 30 to 50 mol% and saponification degree of 95
% Or more is preferable from the viewpoint of moldability and gas barrier properties.
【0008】ここで、印刷層は上記のCPPフイルムま
たは共押出複合フイルムのいずれの表面に設けてもよ
く、印刷後、フイルムをドライラミネートすることによ
り中間印刷を可能にでき、外観に優れた蓋材が得られ
る。Here, the printing layer may be provided on any surface of the above-mentioned CPP film or the co-extruded composite film. After printing, the film can be dry-laminated to enable intermediate printing, and a lid having excellent appearance. Wood is obtained.
【0009】つぎに、本発明包装体の底材はポリアミド
樹脂層を含み、かつ最外層にCPP層を有する必要があ
り、ポリアミド樹脂、CPPについては上記蓋材に使用
したものと同一内容のものが使用できる。底材にも蓋材
と同様にEVOH層を配してもよい。Next, the bottom material of the package of the present invention must include a polyamide resin layer and have a CPP layer as the outermost layer. The polyamide resin and CPP have the same contents as those used for the lid material. Can be used. An EVOH layer may be provided on the bottom material as well as the lid material.
【0010】底材の製造方法は蓋材と同様にポリアミド
樹脂層を含む共押出複合フイルムにCPPフイルムをド
ライラミネートする方法でも全層を無延伸共押出し成形
してもよい。As for the method of manufacturing the bottom material, like the lid material, a method of dry laminating a CPP film to a coextruded composite film containing a polyamide resin layer may be used, or all layers may be co-extruded without stretching.
【0011】本発明の包装体では、上述したように蓋材
と底材の両最外層にCPP層を配することにより、ボイ
ル時に底材の深絞り成形されたところに熱が加わり底材
が収縮し、その収縮が蓋材のCPP層より吸収されるこ
とによりヒートシール部分のカールや、波打ち現象を防
止できると考えられる。In the package of the present invention, by arranging the CPP layers on the outermost layers of both the lid member and the bottom member as described above, heat is applied to the portion where the bottom member is deep drawn at the time of boiling and the bottom member is heated. It is considered that the heat-sealed portion can be prevented from curling and waving by being shrunk and absorbed by the CPP layer of the lid material.
【0012】以下、本発明を実施例により説明する。Hereinafter, the present invention will be described with reference to examples.
【0013】[0013]
(実施例1) 蓋材用積層体 最外層:CPPフイルム(30μm) 共押出複合フイルム層:EVOH(エチレン含有量 4
4モル% 30μm)/ナイロン6−66(Ny 15
μm)/カルボン酸変性ポリオレフィン樹脂(AD 1
0μm)/エチレン−酢酸ビニル共重合体(EVA 酢
酸ビニル含有量 4.5% 10μm)(Example 1) Laminate for lid material Outermost layer: CPP film (30 μm) Co-extruded composite film layer: EVOH (ethylene content 4
4 mol% 30 μm) / Nylon 6-66 (Ny 15
μm) / carboxylic acid-modified polyolefin resin (AD 1
0 μm) / ethylene-vinyl acetate copolymer (EVA vinyl acetate content 4.5% 10 μm)
【0014】底材用積層体 最外層:CPPフイルム(50μm) 印刷 共押出複合フイルム層:EVOH(エチレン含有量 4
4モル% 20μm)/6−66Ny(10μm)/A
D(10μm)/EVA(60μm)Laminate for bottom material Outermost layer: CPP film (50 μm) Printing Co-extruded composite film layer: EVOH (ethylene content 4
4 mol% 20 μm) / 6-66 Ny (10 μm) / A
D (10 μm) / EVA (60 μm)
【0015】上記層構成の蓋材用積層体については、最
外層の共押出複合フイルム側に印刷した後、共押出複合
フイルム層をドライラミネートした。同様に底材用積層
体についても最外層と共押出複合フイルム層をドライラ
ミネートすることにより得た。With respect to the lid material laminate having the above-mentioned layer structure, after printing on the outermost layer of the co-extruded composite film, the co-extruded composite film layer was dry-laminated. Similarly, the laminate for bottom material was obtained by dry laminating the outermost layer and the coextruded composite film layer.
【0016】得られた底材用積層体を用い、深絞り成形
機(FV6300 大森機械工業(株)製)により底材
を深絞り成形した。ついで、上記蓋材用積層体を用い
て、ヒートシールした。その結果、ヒートシール部分の
カールや波打ち現象は見られず、また印刷面の歪み等も
なく外観も良好であった。Using the obtained laminate for a bottom material, the bottom material was deep drawn by a deep drawing machine (FV6300 manufactured by Omori Machinery Co., Ltd.). Then, heat sealing was performed using the above-mentioned lid material laminate. As a result, no curling or waving phenomenon was observed in the heat-sealed portion, and the appearance was good without any distortion on the printed surface.
【0017】(実施例2) 蓋材用積層体 最外層:CPPフイルム(30μm) 印刷 共押出複合フイルム層:ナイロン6(6Ny 10μ
m)/カルボン酸変性ポリオレフィン樹脂(AD10μ
m)/直鎖状低密度ポリエチレン(LL、αオレフィン
がヘキセン1 50μm)(Example 2) Laminate for lid material Outermost layer: CPP film (30 μm) Printing Co-extruded composite film layer: Nylon 6 (6Ny 10 μm)
m) / carboxylic acid-modified polyolefin resin (AD10μ
m) / linear low-density polyethylene (LL, α-olefin is hexene 150 μm)
【0018】底材用積層体 最外層:CPPフイルム(50μm) 共押出複合フイルム層:ナイロン6(6Ny 10μ
m)/カルボン酸変性ポリオレフィン樹脂(AD10μ
m)/直鎖状低密度ポリエチレン(LL、αオレフィン
がヘキセン1 60μm)Laminate for bottom material Outermost layer: CPP film (50 μm) Co-extruded composite film layer: Nylon 6 (6Ny 10 μm)
m) / carboxylic acid-modified polyolefin resin (AD10μ
m) / linear low-density polyethylene (LL, α-olefin is hexene 160 μm)
【0019】上記層構成の蓋材および底材用積層体につ
いては、実施例1と同一方法により得た。得られた蓋材
と底材用積層体を用い、実施例1と同様にヒートシール
した。その結果、ヒートシール部分のカールや波打ち現
象は見られず、また印刷面の歪み等もなく外観も良好で
あった。The lid material and the laminate for the bottom material having the above-mentioned layer constitution were obtained by the same method as in Example 1. Using the obtained lid material and bottom material laminate, heat sealing was performed in the same manner as in Example 1. As a result, no curling or waving phenomenon was observed in the heat-sealed portion, and the appearance was good without any distortion on the printed surface.
【0020】(比較例1) 蓋材用積層体 最外層:CPPフイルム(30μm) 中間層側に印刷 中間層:Kコートセロファン(KM 20μm) シール層:エチレン−酢酸ビニル共重合体(EVA 酢
酸ビニル含有量 4.5% 25μm) 上記各層をドライラミネートにより順次積層して積層体
を得た。(Comparative Example 1) Laminate for lid material Outermost layer: CPP film (30 μm) Printed on the intermediate layer side Intermediate layer: K-coated cellophane (KM 20 μm) Seal layer: Ethylene-vinyl acetate copolymer (EVA vinyl acetate) The content was 4.5% and 25 μm) The above layers were sequentially laminated by dry lamination to obtain a laminate.
【0021】底材用積層体 最外層:CPPフイルム(30μm) 共押出複合フイルム層:EVOH(エチレン含有量 4
4モル% 15μm)/6−66Ny(10μm)/A
D(10μm)/EVA(45μm) 最外層と共押出複合フイルム層をドライラミネートによ
り積層して積層体を得た。Laminate for bottom material Outermost layer: CPP film (30 μm) Co-extruded composite film layer: EVOH (ethylene content 4
4 mol% 15 μm) / 6-66 Ny (10 μm) / A
D (10 μm) / EVA (45 μm) The outermost layer and the coextruded composite film layer were laminated by dry lamination to obtain a laminate.
【0022】得られた蓋材と底材用積層体を用い、実施
例1と同様にヒートシールした。その結果、印刷面の歪
みは殆どなかったが、ヒートシール部分のカールや波打
ち現象が見られ、実用上問題があった。The obtained lid material and bottom material laminate were heat-sealed in the same manner as in Example 1. As a result, although there was almost no distortion on the printing surface, curling and waving of the heat-sealed portion were observed, and there was a problem in practical use.
【0023】(比較例2) 蓋材用積層体 最外層を二軸延伸ポリエチレンテレフタレートフイルム
(OPET)に代えた以外は実施例1と同一内容で下記
層構成、厚みとした。 OPET//EVOH/ Ny / AD / EVA 12μm 10μm 10μm 10μm 48μm(Comparative Example 2) The same layer structure as in Example 1 except that the outermost layer was replaced with a biaxially stretched polyethylene terephthalate film (OPET), and the following layer structure and thickness were used. OPET // EVOH / Ny / AD / EVA 12 μm 10 μm 10 μm 10 μm 48 μm
【0024】底材用積層体 比較例1と同一層構成及び、厚み構成の積層体 最外層と共押出複合フイルム層をドライラミネートによ
り積層して積層体を得た。Laminate for Bottom Material A laminate having the same layer configuration and thickness configuration as Comparative Example 1 was laminated by dry lamination with the outermost layer and the coextruded composite film layer to obtain a laminate.
【0025】得られた蓋材と底材用積層体を用い、実施
例1と同様にヒートシールした。その結果、印刷面の歪
みは殆どなかったが、ヒートシール部分のカールや波打
ち現象が見られ、実用上問題があった。Using the obtained lid material and bottom material laminate, heat sealing was carried out in the same manner as in Example 1. As a result, although there was almost no distortion on the printing surface, curling and waving of the heat-sealed portion were observed, and there was a problem in practical use.
【0026】(比較例3) 蓋材用積層体 最外層:CPPフイルム(30μm) 印刷 共押出複合フイルム層:ナイロン6(6Ny 10μ
m)/カルボン酸変性ポリオレフィン樹脂(AD10μ
m)/直鎖状低密度ポリエチレン(LL、αオレフィン
がヘキセン1 40μm)(Comparative Example 3) Laminate for lid material Outermost layer: CPP film (30 μm) Printing Co-extruded composite film layer: Nylon 6 (6Ny 10 μm)
m) / carboxylic acid-modified polyolefin resin (AD10μ
m) / linear low-density polyethylene (LL, α-olefin is hexene 140 μm)
【0027】底材用積層体 共押出複合フイルム層:ナイロン6(6Ny 40μ
m)/カルボン酸変性ポリオレフィン樹脂(AD10μ
m)/直鎖状低密度ポリエチレン(LL、αオレフィン
がヘキセン1 50μm)Laminate for bottom material Co-extruded composite film layer: Nylon 6 (6Ny 40μ)
m) / carboxylic acid-modified polyolefin resin (AD10μ
m) / linear low-density polyethylene (LL, α-olefin is hexene 150 μm)
【0028】上記層構成の蓋材は最外層と共押出複合フ
イルム層をドライラミネートし、底材用については共押
出複合フイルムのみとした。得られた積層体を用い、実
施例1と同様にヒートシールした。その結果、印刷面の
歪み等もなく外観は良好で、またヒートシール部分のカ
ールはなかったが、波打ち現象が見られ、実用上問題が
あった。The outer layer and the coextruded composite film layer were dry-laminated for the lid material having the above-mentioned layer structure, and only the coextruded composite film was used for the bottom material. The obtained laminate was heat-sealed in the same manner as in Example 1. As a result, the appearance was good without distortion of the printed surface, and there was no curl in the heat-sealed portion. However, a waving phenomenon was observed, and there was a practical problem.
【0029】[0029]
【発明の効果】上述したように本発明の包装体によれ
ば、ボイル殺菌等のボイル処理によりヒートシール部分
のカールや、波打ち現象を防止できる。As described above, according to the package of the present invention, the curling of the heat-sealed portion and the waving phenomenon can be prevented by boil treatment such as boil sterilization.
Claims (2)
装体であって、蓋材が最外層から無延伸ポリプロピレン
樹脂層、印刷層、共押出複合フイルム層を有し、底材が
ポリアミド樹脂層を含み、かつ最外層に無延伸ポリプロ
ピレン樹脂層を有することを特徴とするボイル用深絞り
包装体。1. A deep drawing package for boil comprising a lid material and a bottom material, wherein the lid material has an unstretched polypropylene resin layer, a printing layer, a co-extruded composite film layer from the outermost layer, and the bottom material is A deep drawn package for boiling comprising a polyamide resin layer and an unstretched polypropylene resin layer as an outermost layer.
50〜90kg/cm2 (JISK7127)の範囲の
無延伸ポリプロピレン樹脂フイルムからなることを特徴
とする請求項1記載のボイル用深絞り包装体。2. The deep drawn package according to claim 1, wherein the unstretched polypropylene resin layer is made of an unstretched polypropylene resin film having a Young's modulus of 50 to 90 kg / cm 2 (JIS K7127).