JPH10193326A - Manufacture of concrete product, and decorative mold used therein - Google Patents
Manufacture of concrete product, and decorative mold used thereinInfo
- Publication number
- JPH10193326A JPH10193326A JP9000969A JP96997A JPH10193326A JP H10193326 A JPH10193326 A JP H10193326A JP 9000969 A JP9000969 A JP 9000969A JP 96997 A JP96997 A JP 96997A JP H10193326 A JPH10193326 A JP H10193326A
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- decorative
- acid
- uneven pattern
- concrete product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、コンクリート表面
に対する凹凸模様成形法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for forming a concavo-convex pattern on a concrete surface.
【０００２】[0002]
【従来の技術】従来、コンクリート表面に自然石調の凹
凸模様を表現する場合、つぎのような方法が行われてい
る。すなわち、まず、図６に示すような硬質ウレタン製
の化粧マット（化粧型枠）１２を準備する。この化粧マ
ット１２は、その表面が凹凸模様転写面１３に形成さ
れ、裏面が平坦面１４に形成されている。そして、施工
現場で上記凹凸模様転写面１３に離型剤が塗布され、つ
いで、図７に示すように、型枠１６に対して所定の間隔
で配置し、上記型枠１６と化粧マット１２との側方の開
口（図示せず）と底部の開口を板材１７等で塞ぎ、上部
開口からコンクリート材料１５を流し込む。そして、上
記コンクリート材料１５が養生硬化されてコンクリート
化したのち、上記化粧マット１２を、図８に示すよう
に、コンクリート製品１８から剥離させる。このように
して得られたコンクリート製品１８の表面には上記化粧
マット１２の凹凸模様が転写され、この凹凸模様面に吹
き付け塗装等が行われ、自然石調の凹凸模様を有したコ
ンクリート製品１８が完成する。2. Description of the Related Art Conventionally, the following method has been used to express a natural stone-like uneven pattern on a concrete surface. That is, first, a decorative mat (decorative formwork) 12 made of hard urethane as shown in FIG. 6 is prepared. The face of the decorative mat 12 is formed on an uneven pattern transfer surface 13, and the back surface is formed on a flat surface 14. Then, a release agent is applied to the uneven pattern transfer surface 13 at the construction site, and then, as shown in FIG. The side opening (not shown) and the bottom opening are closed with a plate 17 or the like, and the concrete material 15 is poured from the upper opening. Then, after the concrete material 15 is cured and hardened into concrete, the decorative mat 12 is peeled off from the concrete product 18 as shown in FIG. The concavo-convex pattern of the decorative mat 12 is transferred to the surface of the concrete product 18 thus obtained, and the concavo-convex pattern surface is spray-painted or the like, so that the concrete product 18 having the natural stone-like concavo-convex pattern is obtained. Complete.
【０００３】また、コンクリート製品の表面をさらに表
情豊かに表現する方法として、図９に示すように、上記
化粧マット１２の凹凸模様転写面１３に、粘着剤層２３
を設けるとともに、この粘着剤層２３上に着色粒子２２
を分布させ、図１０に示すように、上記凹凸模様転写面
１３を接触面にしてコンクリート材料１５を打設し、養
生硬化させた後に、図１１に示すように、上記化粧マッ
ト１２を剥離させることにより、コンクリート材料１５
を打ち込むのと同時にコンクリート製品１８の表面１８
ａに着色粒子２２を転写埋設させて着色する方法も提案
され実施されている。As a method for expressing the surface of a concrete product with more expressiveness, as shown in FIG. 9, an adhesive layer 23 is provided on the uneven pattern transfer surface 13 of the decorative mat 12.
And the colored particles 22 on the adhesive layer 23.
10, the concrete material 15 is cast with the uneven pattern transfer surface 13 as a contact surface as shown in FIG. 10, cured and cured, and then the decorative mat 12 is peeled off as shown in FIG. The concrete material 15
Simultaneously with the surface 18 of the concrete product 18
A method of coloring by transferring and embedding the colored particles 22 in a is also proposed and implemented.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上記各
方法で行われる方法では、塗料や着色粒子２２に自然界
にない色が用いられたり、自然石とは異なる色表現が行
われる場合があり、多少の違和感が生じることが避けら
れない。また、上記のようにして得られたコンクリート
製品１８の凹凸模様面は、化粧マット１２の凹凸模様転
写面１３が転写されたもので、表面状態が自然石とは異
なるため、人工的な印象を与え、多少の不自然さが残る
のが実情である。そこで、今まで以上に自然に近い表現
ができるコンクリート製品の製法の開発が望まれてい
た。However, in the method performed by each of the above methods, there are cases where a color not present in the natural world is used for the paint or the colored particles 22, or a color expression different from that of natural stone is performed. It is inevitable that discomfort will occur. In addition, the uneven pattern surface of the concrete product 18 obtained as described above is obtained by transferring the uneven pattern transfer surface 13 of the decorative mat 12 and the surface state is different from natural stone, so that an artificial impression is obtained. The fact is that some unnaturalness remains. Therefore, there has been a demand for the development of a method for producing a concrete product that can express more naturally than before.
【０００５】本発明は、このような事情に鑑みなされた
もので、コンクリート製品の表面に、コンクリートの素
材感を活かした自然石調の凹凸模様を形成しうるコンク
リート製品の製法およびそれに用いる化粧型枠の提供を
その目的とする。The present invention has been made in view of such circumstances, and a method of manufacturing a concrete product capable of forming a natural stone-like uneven pattern utilizing the texture of concrete on the surface of the concrete product, and a decorative mold used therefor. Its purpose is to provide a frame.
【０００６】[0006]
【課題を解決するための手段】上記の目的を達成するた
め、本発明のコンクリート製品の製法は、表面に凹凸模
様が形成された化粧型枠を準備し、上記凹凸模様面にコ
ンクリート硬化遅延剤層を形成し、この凹凸模様面を接
触面にしてコンクリート材料を打設し、養生硬化後上記
化粧型枠を剥離し、得られたコンクリート製品の表面に
対して洗い出しを施し、内部の骨材を露出させることを
要旨とする。In order to achieve the above object, a method of manufacturing a concrete product according to the present invention comprises preparing a decorative form having an uneven pattern formed on the surface thereof, and setting a concrete hardening retarder on the uneven pattern surface. A layer is formed, a concrete material is poured with this uneven pattern surface as a contact surface, and after the curing and curing, the decorative form is peeled off, and the surface of the obtained concrete product is washed out, and the inner aggregate is formed. Is to be exposed.
【０００７】また、本発明の化粧型枠は、表面に凹凸模
様が形成され、この凹凸模様面を接触面にしてコンクリ
ート材料を打設する化粧型枠であって、上記凹凸模様面
にコンクリート硬化遅延剤層を形成させたことを要旨と
する。Further, the decorative formwork of the present invention is a decorative formwork in which an uneven pattern is formed on the surface, and a concrete material is cast with the uneven pattern surface as a contact surface. The gist is that a retarder layer is formed.
【０００８】すなわち、本発明のコンクリート製品の製
法は、表面に凹凸模様が形成された化粧型枠の上記凹凸
模様面にコンクリート硬化遅延剤層を形成し、この凹凸
模様面を接触面にしてコンクリート材料を打設し、得ら
れたコンクリート製品の表面に対して洗い出しを施し、
内部の骨材を露出させる。したがって、コンクリート製
品の表面に化粧型枠の凹凸模様が転写形成されるだけで
なく、コンクリート硬化遅延剤の作用によって形成され
る凹凸模様形成面の表面未硬化層が水等による洗い出し
によって除去される。この除去により、コンクリート中
の骨材が露呈されるとともに、骨材以外の表面は微小凹
凸の粗面に形成される。このように、化粧型枠の凹凸模
様が転写形成され、しかも、この凹凸模様形成面に骨材
が露呈するとともに、粗面に形成されることにより、コ
ンクリートの素材感が活かされた自然石調の凹凸模様が
形成され、従来にない自然に近い表現がされたコンクリ
ート製品が得られる。That is, in the method for producing a concrete product of the present invention, a concrete hardening retardant layer is formed on the above-mentioned irregular pattern surface of a decorative form having an irregular pattern formed on its surface, and the irregular pattern pattern is used as a contact surface to make concrete. Pour the material, wash out the surface of the resulting concrete product,
Expose the aggregate inside. Therefore, not only the concave and convex pattern of the decorative form is transferred and formed on the surface of the concrete product, but also the uncured surface of the concave and convex pattern forming surface formed by the action of the concrete setting retarder is removed by washing out with water or the like. . By this removal, the aggregate in the concrete is exposed, and the surface other than the aggregate is formed as a rough surface with minute irregularities. In this way, the uneven pattern of the decorative form is transferred and formed, and the aggregate is exposed on the surface on which the uneven pattern is formed, and is formed on the rough surface. Thus, a concrete product with an expression close to nature, which has never been seen before, can be obtained.
【０００９】また、本発明の化粧型枠は、表面に凹凸模
様が形成され、この凹凸模様面を接触面にしてコンクリ
ート材料を打設する化粧型枠であって、上記凹凸模様面
にコンクリート硬化遅延剤層が形成されている。このた
め、上記コンクリート製品の製法により、コンクリート
の素材感が活かされた自然石調の凹凸模様のあるコンク
リート製品を容易につくることができる。Further, the decorative formwork of the present invention is a decorative formwork in which an uneven pattern is formed on the surface, and a concrete material is poured with the uneven pattern surface as a contact surface. A retarder layer is formed. Therefore, a concrete product having a natural stone-like uneven pattern utilizing the texture of concrete can be easily produced by the above-described method for producing a concrete product.
【００１０】[0010]
【発明の実施の形態】つぎに、本発明の実施の形態を説
明する。Next, an embodiment of the present invention will be described.
【００１１】本発明のコンクリート製品の製法は、表面
に凹凸模様が形成された化粧型枠を準備し、上記凹凸模
様面にコンクリート硬化遅延剤層を形成し、この凹凸模
様面を接触面にしてコンクリート材料を打設し、養生硬
化後上記化粧型枠を剥離し、得られたコンクリート製品
の表面に洗い出しを施し、内部の骨材を露出させる。According to the method for producing a concrete product of the present invention, a decorative formwork having an uneven pattern formed on its surface is prepared, a concrete hardening retardant layer is formed on the uneven pattern surface, and the uneven pattern surface is used as a contact surface. After the concrete material is cast and cured and cured, the decorative form is peeled off, and the surface of the obtained concrete product is washed out to expose the internal aggregate.
【００１２】上記化粧型枠は、硬質発泡ウレタン樹脂製
のもの等が用いられる。例えば、図１に示すように、上
記化粧型枠１として、硬質のウレタン発泡体で構成さ
れ、一方の面が、コンクリート材料に接触してコンクリ
ート表面に凹凸模様を転写する凹凸模様転写面２に、他
方の面が平坦面３に形成されたものが用いられる。この
ような化粧型枠１は、例えば、上記凹凸模様と逆の凸凹
模様を有する金型内に、液状発泡ウレタン樹脂を注入し
硬化させることにより製造され、内部が発泡層に、金型
の凸凹模様に接する表面が緻密なインテグラルスキン層
に形成されている。このインテグラルスキン層は、実質
的に気泡が存在せず高密度で緻密に形成され、表面平滑
性に富んでいる。このインテグラルスキン層の平滑な表
面で上記凹凸模様転写面２が形成されている。As the decorative mold, one made of hard urethane foam resin or the like is used. For example, as shown in FIG. 1, the decorative form 1 is made of a hard urethane foam, and one surface of the decorative form 1 is provided on an uneven pattern transfer surface 2 which contacts a concrete material and transfers the uneven pattern to the concrete surface. And the other surface formed on the flat surface 3 is used. Such a decorative mold 1 is manufactured, for example, by injecting a liquid urethane resin into a mold having a concavo-convex pattern opposite to the above concavo-convex pattern and curing the resin. The surface in contact with the pattern is formed on a dense integral skin layer. This integral skin layer is formed densely and densely with substantially no bubbles, and has excellent surface smoothness. The uneven pattern transfer surface 2 is formed on the smooth surface of the integral skin layer.
【００１３】上記コンクリート硬化遅延剤は、コンクリ
ート材料の硬化を遅らせるものであれば各種のものが用
いられ、特に限定されるものではない。例えば、紫外線
硬化型樹脂，アルカリにより加水分解する物質，カルシ
ウムイオンを吸着する物質等を使用することができる。As the concrete hardening retardant, various ones can be used as long as they slow the hardening of the concrete material, and are not particularly limited. For example, a UV-curable resin, a substance hydrolyzed by an alkali, a substance that adsorbs calcium ions, and the like can be used.
【００１４】上記紫外線硬化型樹脂としては、例えば、
１・６−ヘキサンジオールジアクリレート，ネオペンチ
ルグリコールジアクリレート，トリメチロールプロパン
トリアクリレート，ペンタエリスリトールトリアクリレ
ート，ペンタエリスリトールテトラメタクリレート等の
アクリレート、α，α−テトラアクリル−ビストリメチ
ロールプロパンテトラヒドロフタレート，α，α−ジメ
タクリル−ビスジエチレングリコールフタレート等のフ
タレート、トリレンジイソジアネート，イソホロンジイ
ソシアネート等に２−ヒドロキシエチルアクリレート
（ＨＥＡ）を反応させた化合物，ヘキサンジオールとイ
ソホロンジイソシアネートにＨＥＡを反応させた化合
物，ビスフェノールＡ−ジグリシジルエーテルのジアク
リレート，トリメチロールプロパンポリグリシジルエー
テルポリアクリレート，スピログリコールジグリシジル
エーテルジアクリレート，シリコーンアクリレート，ト
リアクリロイルオキシエチルイソシアヌレート等があげ
られる。[0014] Examples of the UV-curable resin include:
Acrylates such as 1,6-hexanediol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetramethacrylate, α, α-tetraacryl-bistrimethylolpropane tetrahydrophthalate, α, α Phthalate such as -dimethacryl-bisdiethylene glycol phthalate, a compound obtained by reacting 2-hydroxyethyl acrylate (HEA) with tolylene diisodianate, isophorone diisocyanate, a compound obtained by reacting HEA with hexanediol and isophorone diisocyanate, bisphenol A -Diacrylates of diglycidyl ether, trimethylolpropane polyglycidyl ether polyacrylate, Pyro glycol diglycidyl ether diacrylate, silicone acrylate, triacryloyl oxyethyl isocyanurate and the like.
【００１５】また、アルカリにより加水分解してコンク
リートの硬化を抑制する物質としては、例えば、ポリ酢
酸ビニル等のエステル類やヘミセルロース等があげられ
る。また、カルシウムイオンを吸着してコンクリートの
硬化を抑制する物質としては、例えば、イオン化傾向が
カルシウムよりも大きいカリウム，ナトリウムの塩類，
フェノール類，セルロースおよびリグニン等があげられ
る。Examples of the substance which inhibits the hardening of concrete by being hydrolyzed by an alkali include, for example, esters such as polyvinyl acetate and hemicellulose. Examples of the substance that inhibits hardening of concrete by adsorbing calcium ions include, for example, potassium and sodium salts, which have a higher ionization tendency than calcium,
Examples include phenols, cellulose, and lignin.
【００１６】また、上記以外に、コンクリートの硬化を
抑制する物質として、不飽和ポリエステル樹脂，エポキ
シ（メタ）アクリレート等のビニルエステル樹脂，ホス
ホン酸基を有する樹脂等の樹脂材料や、各種の有機物，
無機物が用いられる。上記有機物としては、グルコヘプ
トン酸，グルコン酸，ガラクトン酸，粘液酸，クエン
酸，アラボン酸，エリスロン酸，酒石酸，リンゴ酸，ト
レオニン（アミノ酸），コハク酸，マレイン酸，グリセ
リン酸，グリコール酸，シュウ酸，乳酸等のオキシカル
ボン酸およびジカルボン酸またはその塩、２ケトグルコ
ン酸，ピルビン酸等のケトカルボン酸、カプロン酸，吉
草酸，酪酸，プロピオン酸，酢酸等の脂肪酸、ペルセイ
トール，ソルビトール，アラビトール，エリスリトー
ル，グリセロール，エチレングリコール等の糖アルコー
ル類、グルコヘプトース，グルコース，マンノース，ガ
ラクトース，フラクトース，アラビノース，エリスロー
ス，グリセルアルデヒド，サッカロース（ショ糖），ラ
クトース，マルトース，ラフィノース，デキストリン等
の糖類、リグニンスルホン酸、アミノジ（メチレンホス
ホン酸），アミノトリ（メチレンホスホン酸），１−ヒ
ドロキシエチリデン−１，１−ジホスホン酸，エチレン
ジアミンテトラ（メチレンホスホン酸），ジエチレント
リアミンペンタ（メチレンホスホン酸），ヘキサメチレ
ンジアミンテトラ（メチレンホスホン酸），またはそれ
らの塩等のホスホン酸系硬化遅延剤、シュウ酸，マロン
酸等の飽和多価カルボン酸、フマル酸，イタコン酸等の
不飽和多価カルボン酸、グルコヘプタノン酸等の多価カ
ルボン酸又はその塩、ポリマレイン酸，ポリフマル酸，
スチレン−マレイン酸共重合体，ポリアクリル酸，ポリ
メタクリル酸，スチレン−（メタ）アクリル酸共重合
体，（メタ）アクリル酸エステル−（メタ）アクリル酸
共重合体，エチレンスルホン酸−アクリル酸コポリマー
等のカルボシキル基を有するモノマーの単独または共重
合体もしくはそれらの塩、アスコルビン酸，イソアスコ
ルビン酸等の酸化防止剤、ポリヒドロキシシラン，ポリ
アクリルアミド等のポリマー、フミン酸、リグノスルホ
ネート、ケルトカルボン酸類，水溶性でんぷん，ライ麦
の粉末，アラビアゴム，アルコール類等があげられる。
また、無機物としては、珪フッ化マグネシウム，トリポ
リリン酸ナトリウム，酸化亜鉛，ホウ素化合物，ホウ酸
塩，リン酸塩（特にヘキサメタリン酸ソーダ），ヘキサ
フルオロケイ酸塩等があげられる。[0016] In addition to the above, as a substance that suppresses the hardening of concrete, resin materials such as unsaturated polyester resin, vinyl ester resin such as epoxy (meth) acrylate, resin having phosphonic acid group, various organic substances,
Inorganic substances are used. Examples of the organic substances include glucoheptonic acid, gluconic acid, galactonic acid, mucous acid, citric acid, arabic acid, erythronic acid, tartaric acid, malic acid, threonine (amino acid), succinic acid, maleic acid, glyceric acid, glycolic acid, and oxalic acid. , Oxycarboxylic acids such as lactic acid and dicarboxylic acids or salts thereof, ketocarboxylic acids such as ketogluconic acid and pyruvic acid, fatty acids such as caproic acid, valeric acid, butyric acid, propionic acid and acetic acid, perseitol, sorbitol, arabitol, erythritol, glycerol , Sugar alcohols such as ethylene glycol, glucoheptose, glucose, mannose, galactose, fructose, arabinose, erythrose, glyceraldehyde, saccharose (sucrose), lactose, maltose, raffinose, dex. Sugars such as trines, ligninsulfonic acid, aminodi (methylenephosphonic acid), aminotri (methylenephosphonic acid), 1-hydroxyethylidene-1,1-diphosphonic acid, ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylenephosphonic acid) , Hexamethylenediaminetetra (methylenephosphonic acid) or their salts, etc., phosphonic acid-based curing retarders, oxalic acid, saturated polycarboxylic acids such as malonic acid, and unsaturated polycarboxylic acids such as fumaric acid and itaconic acid , Polycarboxylic acids such as glucoheptanonic acid or salts thereof, polymaleic acid, polyfumaric acid,
Styrene-maleic acid copolymer, polyacrylic acid, polymethacrylic acid, styrene- (meth) acrylic acid copolymer, (meth) acrylate- (meth) acrylic acid copolymer, ethylenesulfonic acid-acrylic acid copolymer Homo- or copolymers of monomers having a carboxy group such as, or salts thereof, antioxidants such as ascorbic acid, isoascorbic acid, polymers such as polyhydroxysilane, polyacrylamide, humic acid, lignosulfonate, celtic carboxylic acids, Examples include water-soluble starch, rye powder, gum arabic, and alcohols.
Examples of the inorganic substance include magnesium fluorosilicate, sodium tripolyphosphate, zinc oxide, boron compounds, borates, phosphates (particularly sodium hexametaphosphate), and hexafluorosilicates.
【００１７】上記コンクリート硬化遅延剤は、単独でも
しくは併せて使用することができる。また、適当な溶媒
に溶解もしくは混合分散させて液状として使用するの
が、作業性の観点から好ましい。また、粘着剤，接着
剤，樹脂液，粘度調整液，充填材，吸水膨潤剤等と混合
させてもよい。さらに、各コンクリート硬化遅延剤の性
状（固体，液体，粘度，粒度，ＰＨ等）により、洗い出
しによって除去されるコンクリート材料の量や、硬化遅
延時間等に差があるため、濃度や種類，組み合わせ，使
用法等を適宜に変更し、所望の除去量、硬化遅延時間に
設定すればよい。このとき、除去量は、コンクリート材
料を打設した表面から、約１〜３ｍｍ（最適には２ｍ
ｍ）程度の深さが除去されるのが、凹凸模様形成面の凹
凸模様の表現が消えてしまわず、しかも、骨材の露出等
の洗い出しによる表現も生きるため、好ましい。また、
液状としたコンクリート硬化遅延剤を粘着剤等と混合さ
せて塗布したり、あらかじめ化粧型枠１の表面に粘着剤
層を形成させ、そのうえにコンクリート硬化遅延剤を塗
布等するようにしてもよい。The concrete hardening retardants can be used alone or in combination. Further, it is preferable to dissolve or mix and disperse in an appropriate solvent to use as a liquid from the viewpoint of workability. Further, it may be mixed with an adhesive, an adhesive, a resin liquid, a viscosity adjusting liquid, a filler, a water-absorbing swelling agent, and the like. In addition, depending on the properties (solid, liquid, viscosity, particle size, PH, etc.) of each concrete setting retarder, there are differences in the amount of concrete material removed by washing and the setting delay time. The method of use may be appropriately changed, and the desired removal amount and curing delay time may be set. At this time, the removal amount is about 1 to 3 mm (optimally 2 m) from the surface on which the concrete material is cast.
It is preferable to remove the depth of about m), since the expression of the uneven pattern on the uneven pattern forming surface does not disappear, and the expression by washing out such as the exposure of the aggregates is preferable. Also,
A liquid concrete hardening retardant may be mixed with an adhesive or the like and applied, or an adhesive layer may be previously formed on the surface of the decorative form 1 and a concrete hardening retarder may be applied thereon.
【００１８】上記化粧型枠１の凹凸模様転写面２に、図
２（ａ）に示すように、コンクリート硬化遅延剤を刷毛
２５もしくはスプレー噴霧等で塗布し、図２（ｂ）に示
すように、乾燥硬化させ、図２（ｃ）に示すように遅延
剤層４を形成する。図２（ａ）において２６はスプレー
ノズル、図２（ｂ）において２７は乾燥炉である。As shown in FIG. 2 (a), a concrete hardening retardant is applied to the concave / convex pattern transfer surface 2 of the decorative form frame 1 by means of a brush 25 or spray spraying, as shown in FIG. 2 (b). After drying and curing, a retarder layer 4 is formed as shown in FIG. In FIG. 2A, 26 is a spray nozzle, and in FIG. 2B, 27 is a drying furnace.
【００１９】コンクリート硬化遅延剤を塗布する方法と
しては、上述した刷毛塗りやスプレー噴霧に限らず、ロ
ーラー塗布，ディッピング等各種の方法が行われ、特に
限定されるものではない。また、乾燥硬化も、自然放
置，熱風乾燥，赤外線乾燥等各種の方法が行われ、特に
限定されるものではない。乾燥条件も、使用するコンク
リート硬化遅延剤の種類等によって各種の条件で行われ
るが、おおむね、常温〜６０℃程度の温度で数十分〜数
時間かけて行われる。このようにして形成された遅延剤
層４の厚みは、０．０５〜２ｍｍ程度が好ましい。０．
０５ｍｍ未満では、充分なコンクリートの硬化抑制作用
が得られず、２ｍｍを越えると洗浄除去されるコンクリ
ート材料が多くなりすぎて歩留りが悪くなるうえ、塗布
と乾燥を何回も繰り返す必要が生じ、生産性が悪くなる
からである。The method of applying the concrete hardening retardant is not limited to the above-mentioned brush coating and spraying, but various methods such as roller coating and dipping are performed, and are not particularly limited. Various methods such as natural standing, hot air drying, and infrared drying are also used for drying and curing, and are not particularly limited. The drying condition is also performed under various conditions depending on the type of concrete hardening retardant to be used and the like, but is generally performed at room temperature to about 60 ° C. for several tens of minutes to several hours. The thickness of the retarder layer 4 thus formed is preferably about 0.05 to 2 mm. 0.
If the thickness is less than 05 mm, sufficient hardening inhibitory effect of concrete cannot be obtained. If the thickness exceeds 2 mm, the concrete material to be washed and removed becomes too large, the yield is deteriorated, and the application and drying must be repeated many times. This is because the sex becomes worse.
【００２０】そして、図３に示すように、化粧型枠１の
背面側の平坦面３が型枠５に取り付けられ、他の型枠６
に対して所定の間隔で配置され、型枠６と化粧型枠１と
の側方の開口（図示せず）と底部の開口とが板材７等で
塞がれ、上部開口からコンクリート材料１５が流し込ま
れて上記凹凸模様転写面２を接触面としてコンクリート
材料１５が打設され、上記コンクリート材料１５が養生
硬化されてコンクリート化する。図において、１０は骨
材である。このとき、化粧型枠１の凹凸模様転写面２に
形成された遅延剤層４の作用により、凹凸模様転写面２
と接触した表面層のコンクリート材料１５の硬化が抑制
もしくは遅延され、凹凸模様転写面２との接触部分が軟
らかく、内部だけが硬化したコンクリートとなる。Then, as shown in FIG. 3, the flat surface 3 on the back side of the decorative mold 1 is attached to the mold 5 and another mold 6 is formed.
Are arranged at a predetermined distance from each other, the side opening (not shown) and the bottom opening of the formwork 6 and the decorative formwork 1 are closed by the plate material 7 or the like, and the concrete material 15 flows from the upper opening. The concrete material 15 is poured with the concave-convex pattern transfer surface 2 as a contact surface, and the concrete material 15 is cured and hardened into concrete. In the figure, reference numeral 10 denotes an aggregate. At this time, the concave and convex pattern transfer surface 2 is formed by the action of the retarder layer 4 formed on the concave and convex pattern transfer surface 2 of the decorative mold 1.
The hardening of the concrete material 15 of the surface layer in contact with the surface is suppressed or delayed, the contact portion with the uneven pattern transfer surface 2 is soft, and only the inside is hardened concrete.
【００２１】そののち、上記化粧型枠１を、図４に示す
ように、コンクリート製品８から剥離させる。このよう
にして得られたコンクリート製品８の表面は上記化粧型
枠１の凹凸模様転写面２が転写された凹凸模様形成面９
となる。そして、この凹凸模様形成面９の表面層は軟ら
かい未硬化層１１となっている。このため、化粧型枠１
に、特別に離型剤等を塗布させることなく、化粧型枠１
を容易に剥離することができ、しかも化粧型枠１の損傷
も少ない。Thereafter, the decorative form 1 is peeled off from the concrete product 8 as shown in FIG. The surface of the concrete product 8 thus obtained is provided with the uneven pattern forming surface 9 to which the uneven pattern transfer surface 2 of the decorative form 1 is transferred.
Becomes The surface layer of the uneven pattern forming surface 9 is a soft uncured layer 11. For this reason, the decorative form 1
Without applying a mold release agent, etc.
Can be easily peeled off, and the decorative mold 1 is hardly damaged.
【００２２】そして、図５に示すように、上記表面の未
硬化層１１に対して洗い出しを施すことが行われる。洗
い出しは、例えば、高圧水（２〜４０ｋｇ／ｃｍ2 ）を
コンクリート製品８の表面に噴射することにより行われ
るが、これに限定されるものではない。この洗い出しに
より、表面の未硬化層１１のセメントが除去され、凹凸
模様形成面９に、コンクリート材料中の骨材１０が露呈
するとともに、骨材１０のない部分の表面は微小凹凸の
粗面２８となる。これにより、化粧型枠１によって凹凸
模様が転写形成されるとともに、骨材１０が露呈し、し
かも骨材１０のない表面が粗面２８に形成されることに
より、コンクリートの素材感が活かされた自然石調の凹
凸模様が形成され、従来にない自然に近い表現がされた
コンクリート製品８となる。しかも、養生硬化後のコン
クリート製品８が水洗い等されるため、コンクリート打
ちっぱなしの場合と比べ、最終製品がきれいになる。Then, as shown in FIG. 5, the uncured layer 11 on the surface is washed out. Washing is performed, for example, by spraying high-pressure water ( 2 to 40 kg / cm 2 ) on the surface of the concrete product 8, but is not limited thereto. By this washing, the cement of the uncured layer 11 on the surface is removed, the aggregate 10 in the concrete material is exposed on the uneven pattern forming surface 9, and the surface of the portion without the aggregate 10 has a rough surface 28 with minute unevenness. Becomes As a result, the embossed pattern is transferred and formed by the decorative mold 1, and the aggregate 10 is exposed, and the surface without the aggregate 10 is formed on the rough surface 28, so that the feel of the material of the concrete is utilized. A natural stone-like uneven pattern is formed, and the concrete product 8 expresses an unusually natural expression. In addition, since the cured and cured concrete product 8 is washed with water, the final product is cleaner than in the case where the concrete is left standing.
【００２３】なお、上記コンクリート製品８に、塗装等
を行って着色するようにしてもよい。また、コンクリー
ト材料１５中に顔料等を混合させることにより着色され
たコンクリート製品８を得るようにしてもよい。The concrete product 8 may be colored by painting or the like. Alternatively, a colored concrete product 8 may be obtained by mixing a pigment or the like into the concrete material 15.
【００２４】また、上記実施の形態では、化粧型枠１の
凹凸模様転写面２の全面に遅延剤層４を形成させたが、
部分的に遅延剤層４を形成させるようにしてもよい。例
えば、凹凸模様が石積み模様である場合には、石の部分
にだけ遅延剤層４を形成させ、石と石の間のいわゆる目
地の部分には遅延剤層４を形成させないようにすること
もできる。このようにすることにより、石の部分の表面
だけが洗い出しにより除去された自然石調の表面にな
り、目地部分は人工的なコンクリート表面となる。これ
により、目地部分と石の部分との差がはっきりと表さ
れ、コンクリートの素材感が一層活かされた表現にな
る。In the above embodiment, the retarder layer 4 is formed on the entire surface of the concave and convex pattern transfer surface 2 of the decorative mold 1.
The retarder layer 4 may be partially formed. For example, when the uneven pattern is a masonry pattern, the retarder layer 4 may be formed only on the stone portion, and the retarder layer 4 may not be formed on the so-called joint portion between the stones. it can. By doing so, only the surface of the stone portion becomes a natural stone-like surface removed by washing out, and the joint portion becomes an artificial concrete surface. Thereby, the difference between the joint portion and the stone portion is clearly shown, and the expression of the concrete material is further utilized.
【００２５】つぎに、実施例について説明する。Next, an embodiment will be described.
【００２６】[0026]
【実施例１】図１に示す化粧型枠１の凹凸模様転写面２
に、コンクリート硬化遅延剤を下記の組成で調整し、そ
の調整液をエア吹き付け（ガンタイプ，エア吹き付け圧
力２〜７ｋｇ／ｃｍ2 ）によって塗布し（塗布量２０〜
６０ｇ／ｍ2 ）、２０℃で４時間乾燥硬化させて遅延剤
層４を形成させ、本発明の化粧型枠を得た。 〔組成〕 変成リグニン＋オキシカルボン酸化合物の複合体 （商品名：ポゾリス＃１００，エヌエスビー社製） １００重量部 水 １〜１０重量部 メチルセルロース （商品名：Ｈｉメトローズ４０００，信越化学工業社製） １〜５重量部Embodiment 1 An uneven pattern transfer surface 2 of a decorative mold 1 shown in FIG.
Then, a concrete hardening retardant is adjusted with the following composition, and the adjusted liquid is applied by air spraying (gun type, air spraying pressure 2 to 7 kg / cm 2 ) (coating amount 20 to 20).
60 g / m 2 ), dried and cured at 20 ° C. for 4 hours to form a retarder layer 4, thereby obtaining a decorative mold of the present invention. [Composition] Complex of modified lignin and oxycarboxylic acid compound (trade name: Pozzolith # 100, manufactured by NSB) 100 parts by weight Water 1 to 10 parts by weight methylcellulose (trade name: Hi Metroze 4000, manufactured by Shin-Etsu Chemical Co., Ltd.) 1-5 parts by weight
【００２７】[0027]
【実施例２】コンクリート硬化遅延剤の調整液の塗布方
法をハケ，ローラー塗りにする以外は、実施例１と同様
にして本発明の化粧型枠を得た。Example 2 A decorative mold of the present invention was obtained in the same manner as in Example 1, except that the method of applying the adjusting solution for the concrete hardening retardant was brushing and roller coating.
【００２８】[0028]
【実施例３】コンクリート硬化遅延剤の調整液を２回重
ね塗りにし、４０℃で１時間乾燥硬化させる以外は、実
施例１と同様にして本発明の化粧型枠を得た。Example 3 A decorative mold of the present invention was obtained in the same manner as in Example 1, except that the preparation solution of the concrete hardening retardant was applied twice and dried and hardened at 40 ° C. for 1 hour.
【００２９】[0029]
【実施例４】コンクリート硬化遅延剤として、グルコン
酸ナトリウム塩（商品名：デスパライトＤＶ，共栄化学
社製）を使用し、図１に示す化粧型枠１の凹凸模様転写
面２に、ハケ，ローラーによって塗布し（塗布量１５０
〜３５０ｇ／ｍ2 ）、６０℃で３０分乾燥硬化させて遅
延剤層４を形成させ、本発明の化粧型枠を得た。Example 4 As a concrete hardening retarder, sodium gluconate (trade name: Desparite DV, manufactured by Kyoei Chemical Co., Ltd.) was used, and the embossed pattern transfer surface 2 of the decorative mold 1 shown in FIG. Apply by roller (application amount 150
To 350 g / m 2 ), and dried and cured at 60 ° C. for 30 minutes to form a retarder layer 4, thereby obtaining a decorative mold of the present invention.
【００３０】[0030]
【実施例５】コンクリート硬化遅延剤を下記の組成で調
整し、その調整液を図１に示す化粧型枠１の凹凸模様転
写面２に、エア吹き付け（ガンタイプ，高粘度吹き付
け，圧送圧力５ｋｇ／ｃｍ2 ，エア吹き付け圧力５ｋｇ
／ｃｍ2 ）によって塗布し（塗布量１５０〜４００ｇ／
ｍ2 ，塗布厚み０．０５〜２ｍｍ）、２０℃で８時間乾
燥硬化させて遅延剤層４を形成させ、本発明の化粧型枠
を得た。 〔組成〕 酢ビ・アクリルエマルジョン （商品名：ボンコート＃９１８０，大日本インキ化学工業社製） ８０重量部 ポリビニルアルコール （商品名：デンカポバール，電気化学工業社製） ２０重量部 酸化亜鉛 １０重量部 オキシカルボン酸塩 （商品名：ポゾリス，エヌエスビー社製） ５重量部Example 5 A concrete hardening retardant was prepared according to the following composition, and the prepared liquid was sprayed by air (gun type, high-viscosity spraying, pumping pressure of 5 kg) onto the concave / convex pattern transfer surface 2 of the decorative mold 1 shown in FIG. / Cm 2 , air blowing pressure 5kg
/ Cm 2 ) (coating amount 150 to 400 g /
m 2 , coating thickness: 0.05 to 2 mm) and dried and cured at 20 ° C. for 8 hours to form a retarder layer 4, thereby obtaining a decorative mold of the present invention. [Composition] Vinyl acetate / acryl emulsion (trade name: Boncoat # 9180, manufactured by Dainippon Ink and Chemicals, Inc.) 80 parts by weight Polyvinyl alcohol (trade name: Denka Poval, manufactured by Denki Kagaku Kogyo) 20 parts by weight Zinc oxide 10 parts by weight 5 parts by weight of oxycarboxylate (trade name: POZORIS, NSB)
【００３１】[0031]
【実施例６】乾燥条件を４０℃で２時間にする以外は、
実施例５と同様にして本発明の化粧型枠を得た。Example 6 Except that the drying condition was 40 ° C. for 2 hours,
In the same manner as in Example 5, a decorative mold of the present invention was obtained.
【００３２】[0032]
【実施例７】乾燥条件を６０℃で４５分にする以外は、
実施例５と同様にして本発明の化粧型枠を得た。Example 7 Except that the drying condition was 60 ° C. for 45 minutes,
In the same manner as in Example 5, a decorative mold of the present invention was obtained.
【００３３】上記実施例１〜７の化粧型枠１を使用して
枠組みし、コンクリート材料を打設し、養生硬化させた
（図３参照）。そして、化粧型枠１等を剥離したのち、
高圧水（１０ｋｇ／ｃｍ2 ）の噴射により洗い出しを施
し、表面の未硬化層１１のセメントを除去し、コンクリ
ート製品８を得た（図５参照）。A frame was formed using the decorative formwork 1 of the above Examples 1 to 7, a concrete material was cast, and the material was cured and cured (see FIG. 3). Then, after peeling off the decorative form 1 and the like,
Washing was performed by spraying high-pressure water (10 kg / cm 2 ) to remove the cement of the uncured layer 11 on the surface, and a concrete product 8 was obtained (see FIG. 5).
【００３４】このようにして得られた各コンクリート製
品８は、洗い出しによりコンクリート中の骨材１０等が
露呈されるとともに粗面２８が形成され、コンクリート
の素材感が活かされた自然石調の凹凸模様が形成された
コンクリート製品が得られた。Each of the concrete products 8 thus obtained exposes the aggregates 10 and the like in the concrete by washing out, forms a rough surface 28, and has a natural stone-like unevenness utilizing the texture of the concrete. A patterned concrete product was obtained.
【００３５】[0035]
【発明の効果】以上のように、本発明によれば、コンク
リート製品の表面に化粧型枠の凹凸模様が転写形成され
るだけでなく、コンクリート硬化遅延剤の作用によって
形成される凹凸模様形成面の表面未硬化層が水等による
洗い出しによって除去される。この除去により、コンク
リート中の骨材が露呈されるとともに、骨材以外の表面
は微小凹凸の粗面に形成される。このように、化粧型枠
の凹凸模様が転写形成され、しかも、この凹凸模様形成
面に骨材が露呈するともに、粗面に形成されることによ
り、コンクリートの素材感が活かされた自然石調の凹凸
模様が形成され、従来にない自然に近い表現がされたコ
ンクリート製品が得られる。As described above, according to the present invention, not only the concave and convex pattern of the decorative mold is transferred to the surface of the concrete product, but also the concave and convex pattern forming surface formed by the action of the concrete setting retarder. Is removed by washing with water or the like. By this removal, the aggregate in the concrete is exposed, and the surface other than the aggregate is formed as a rough surface with minute irregularities. In this way, the concave and convex pattern of the decorative form is transferred and formed, and the aggregate is exposed on the concave and convex pattern forming surface and is formed on the rough surface. Thus, a concrete product with an expression close to nature, which has never been seen before, can be obtained.
【図１】本発明に用いる化粧マットを示す説明図であ
る。FIG. 1 is an explanatory view showing a decorative mat used in the present invention.
【図２】上記化粧マットに遅延剤層を形成させる工程を
示す図であり、（ａ）はコンクリート硬化遅延剤を塗布
する状態を示す説明図、（ｂ）は上記コンクリート硬化
遅延剤を乾燥硬化させる状態を示す説明図、（ｃ）は遅
延剤層が形成された本発明の化粧型枠を示す説明図であ
る。FIG. 2 is a view showing a step of forming a retarder layer on the decorative mat, (a) is an explanatory view showing a state in which a concrete curing retarder is applied, and (b) is a drying and curing method of the concrete curing retarder. FIG. 3C is an explanatory view showing a state in which the decorative form is formed, and FIG.
【図３】上記化粧型枠を使用してコンクリート材料を打
設した状態を示す説明図である。FIG. 3 is an explanatory view showing a state where a concrete material is cast using the decorative formwork.
【図４】コンクリート製品から化粧型枠を剥離させる状
態を示す説明図である。FIG. 4 is an explanatory view showing a state in which a decorative form is detached from a concrete product.
【図５】コンクリート製品の未硬化層を洗い出しにより
除去する状態を示す説明図である。FIG. 5 is an explanatory view showing a state in which an uncured layer of a concrete product is removed by washing out.
【図６】従来例の化粧マットの一実施例を示す説明図で
ある。FIG. 6 is an explanatory view showing one embodiment of a conventional decorative mat.
【図７】上記従来例の化粧マットを用いての模様成形法
を示す説明図である。FIG. 7 is an explanatory view showing a pattern forming method using the decorative mat of the conventional example.
【図８】上記従来例の化粧マットを用いての模様成形法
を示す説明図である。FIG. 8 is an explanatory view showing a pattern forming method using the decorative mat of the conventional example.
【図９】他の従来例の化粧マットの一実施例を示す説明
図である。FIG. 9 is an explanatory view showing an embodiment of another conventional decorative mat.
【図１０】上記他の従来例の化粧マットを用いての模様
成形法を示す説明図である。FIG. 10 is an explanatory view showing a pattern forming method using a decorative mat according to another conventional example.
【図１１】上記他の従来例の化粧マットを用いての模様
成形法を示す説明図である。FIG. 11 is an explanatory view showing a pattern forming method using a decorative mat of another conventional example.
１ 化粧型枠 ２ 凹凸模様転写面 ４ 遅延剤層 １０ 骨材 １５ コンクリート材料 DESCRIPTION OF SYMBOLS 1 Make-up formwork 2 Uneven pattern transfer surface 4 Delay agent layer 10 Aggregate 15 Concrete material
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成９年７月１１日[Submission date] July 11, 1997
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】全文[Correction target item name] Full text
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【書類名】 明細書[Document Name] Statement
【発明の名称】 コンクリート製品の製法およびそれに
用いる化粧型枠Patent application title: Method for producing a concrete product and a decorative form used therefor
【特許請求の範囲】[Claims]
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【発明の属する技術分野】本発明は、凹凸模様が形成さ
れたコンクリート製品の製法およびそれに用いる化粧型
枠に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a concrete product having a concavo-convex pattern and a decorative form used for the same.
【０００２】[0002]
【従来の技術】従来、コンクリート表面に自然石調の凹
凸模様を表現する場合、つぎのような方法が行われてい
る。すなわち、まず、図６に示すような硬質ウレタン製
の化粧マット（化粧型枠）１２を準備する。この化粧マ
ット１２は、その表面が凹凸模様転写面１３に形成さ
れ、裏面が平坦面１４に形成されている。そして、施工
現場で上記凹凸模様転写面１３に離型剤が塗布され、つ
いで、図７に示すように、型枠１６に対して所定の間隔
で配置し、上記型枠１６と化粧マット１２との側方の開
口（図示せず）と底部の開口を板材１７等で塞ぎ、上部
開口からコンクリート材料１５を流し込む。そして、上
記コンクリート材料１５が養生硬化されてコンクリート
化したのち、上記化粧マット１２を、図８に示すよう
に、コンクリート製品１８から剥離させる。このように
して得られたコンクリート製品１８の表面には上記化粧
マット１２の凹凸模様が転写され、この凹凸模様面に吹
き付け塗装等が行われ、自然石調の凹凸模様を有したコ
ンクリート製品１８が完成する。2. Description of the Related Art Conventionally, the following method has been used to express a natural stone-like uneven pattern on a concrete surface. That is, first, a decorative mat (decorative formwork) 12 made of hard urethane as shown in FIG. 6 is prepared. The face of the decorative mat 12 is formed on an uneven pattern transfer surface 13, and the back surface is formed on a flat surface 14. Then, a release agent is applied to the uneven pattern transfer surface 13 at the construction site, and then, as shown in FIG. The side opening (not shown) and the bottom opening are closed with a plate 17 or the like, and the concrete material 15 is poured from the upper opening. Then, after the concrete material 15 is cured and hardened into concrete, the decorative mat 12 is peeled off from the concrete product 18 as shown in FIG. The concavo-convex pattern of the decorative mat 12 is transferred onto the surface of the concrete product 18 thus obtained, and the concavo-convex pattern surface is subjected to spray painting or the like, whereby the concrete product 18 having the natural stone-like concavo-convex pattern is obtained. Complete.
【０００３】また、コンクリート製品の表面をさらに表
情豊かに表現する方法として、図９に示すように、上記
化粧マット１２の凹凸模様転写面１３に、粘着剤層２３
を設けるとともに、この粘着剤層２３上に着色粒子２２
を分布させ、図１０に示すように、上記凹凸模様転写面
１３を接触面にしてコンクリート材料１５を打設し、養
生硬化させた後に、図１１に示すように、上記化粧マッ
ト１２を剥離させることにより、コンクリート材料１５
を打ち込むのと同時にコンクリート製品１８の表面１８
ａに着色粒子２２を転写埋設させて着色する方法も提案
され実施されている。As a method for expressing the surface of a concrete product with more expressiveness, as shown in FIG. 9, an adhesive layer 23 is provided on the uneven pattern transfer surface 13 of the decorative mat 12.
And the colored particles 22 on the adhesive layer 23.
10, the concrete material 15 is cast with the uneven pattern transfer surface 13 as a contact surface as shown in FIG. 10, cured and cured, and then the decorative mat 12 is peeled off as shown in FIG. The concrete material 15
Simultaneously with the surface 18 of the concrete product 18
A method of coloring by transferring and embedding the colored particles 22 in a is also proposed and implemented.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上記各
方法で行われる方法では、塗料や着色粒子２２に自然界
にない色が用いられたり、自然石とは異なる色表現が行
われる場合があり、多少の違和感が生じることが避けら
れない。また、上記のようにして得られたコンクリート
製品１８の凹凸模様面は、化粧マット１２の凹凸模様転
写面１３が転写されたもので、表面状態が自然石とは異
なるため、人工的な印象を与え、多少の不自然さが残る
のが実情である。そこで、今まで以上に自然に近い表現
ができるコンクリート製品の製法の開発が望まれてい
た。However, in the method performed by each of the above methods, there are cases where a color not present in the natural world is used for the paint or the colored particles 22, or a color expression different from that of natural stone is performed. It is inevitable that discomfort will occur. In addition, the uneven pattern surface of the concrete product 18 obtained as described above is obtained by transferring the uneven pattern transfer surface 13 of the decorative mat 12 and the surface state is different from natural stone, so that an artificial impression is obtained. The fact is that some unnaturalness remains. Therefore, there has been a demand for the development of a method for producing a concrete product that can express more naturally than before.
【０００５】本発明は、このような事情に鑑みなされた
もので、コンクリート製品の表面に、コンクリートの素
材感を活かした自然石調の凹凸模様を形成しうるコンク
リート製品の製法およびそれに用いる化粧型枠の提供を
その目的とする。The present invention has been made in view of such circumstances, and a method of manufacturing a concrete product capable of forming a natural stone-like uneven pattern utilizing the texture of concrete on the surface of the concrete product, and a decorative mold used therefor. Its purpose is to provide a frame.
【０００６】[0006]
【課題を解決するための手段】上記の目的を達成するた
め、本発明のコンクリート製品の製法は、表面に凹凸模
様が形成された化粧型枠を準備し、上記凹凸模様面の全
面にコンクリート硬化遅延剤層を形成し、この凹凸模様
面を接触面にしてコンクリート材料を打設し、養生硬化
後上記化粧型枠を剥離し、得られたコンクリート製品の
表面に対して洗い出しを施し、内部の骨材を露出させる
ことを要旨とする。In order to achieve the above object, a method of manufacturing a concrete product according to the present invention comprises preparing a decorative form having an uneven pattern formed on a surface thereof, and curing concrete over the entire surface of the uneven pattern. Form a retarder layer, cast a concrete material with this uneven pattern surface as the contact surface, peel off the decorative form after curing and curing, wash out the obtained concrete product surface, The point is to expose the aggregate.
【０００７】また、本発明の化粧型枠は、表面に凹凸模
様が形成され、この凹凸模様面を接触面にしてコンクリ
ート材料を打設する化粧型枠であって、上記凹凸模様面
の全面にコンクリート硬化遅延剤層を形成させたことを
要旨とする。Further, the decorative formwork of the present invention is a decorative formwork in which an uneven pattern is formed on the surface, and a concrete material is cast with the uneven pattern surface as a contact surface. The gist is that a concrete hardening retardant layer is formed.
【０００８】すなわち、本発明のコンクリート製品の製
法は、表面に凹凸模様が形成された化粧型枠の上記凹凸
模様面の全面にコンクリート硬化遅延剤層を形成し、こ
の凹凸模様面を接触面にしてコンクリート材料を打設
し、得られたコンクリート製品の表面に対して洗い出し
を施し、内部の骨材を露出させる。したがって、コンク
リート製品の表面に化粧型枠の凹凸模様が転写形成され
るだけでなく、コンクリート硬化遅延剤の作用によって
形成される凹凸模様形成面の表面未硬化層が水等による
洗い出しによって除去される。この除去により、コンク
リート中の骨材が露呈されるとともに、骨材以外の表面
は微小凹凸の粗面に形成される。このように、化粧型枠
の凹凸模様が転写形成され、しかも、この凹凸模様形成
面に骨材が露呈するとともに、粗面に形成されることに
より、コンクリートの素材感が活かされた自然石調の凹
凸模様が形成され、従来にない自然に近い表現がされた
コンクリート製品が得られる。That is, according to the method for producing a concrete product of the present invention, a concrete hardening retardant layer is formed on the entire surface of the above-mentioned uneven pattern surface of a decorative form having an uneven pattern formed on its surface, and this uneven pattern surface is used as a contact surface. Concrete material is poured in, and the surface of the obtained concrete product is washed out to expose the internal aggregate. Therefore, not only the concave and convex pattern of the decorative form is transferred and formed on the surface of the concrete product, but also the uncured surface of the concave and convex pattern forming surface formed by the action of the concrete setting retarder is removed by washing out with water or the like. . By this removal, the aggregate in the concrete is exposed, and the surface other than the aggregate is formed as a rough surface with minute irregularities. In this way, the uneven pattern of the decorative form is transferred and formed, and the aggregate is exposed on the surface on which the uneven pattern is formed, and is formed on the rough surface. Thus, a concrete product with an expression close to nature, which has never been seen before, can be obtained.
【０００９】また、本発明の化粧型枠は、表面に凹凸模
様が形成され、この凹凸模様面を接触面にしてコンクリ
ート材料を打設する化粧型枠であって、上記凹凸模様面
の全面にコンクリート硬化遅延剤層が形成されている。
このため、上記コンクリート製品の製法により、コンク
リートの素材感が活かされた自然石調の凹凸模様のある
コンクリート製品を容易につくることができる。Further, the decorative formwork of the present invention is a decorative formwork in which an uneven pattern is formed on the surface, and a concrete material is cast by using the uneven pattern surface as a contact surface. A concrete retarder layer is formed.
Therefore, a concrete product having a natural stone-like uneven pattern utilizing the texture of concrete can be easily produced by the above-described method for producing a concrete product.
【００１０】[0010]
【発明の実施の形態】つぎに、本発明の実施の形態を説
明する。Next, an embodiment of the present invention will be described.
【００１１】本発明のコンクリート製品の製法は、表面
に凹凸模様が形成された化粧型枠を準備し、上記凹凸模
様面にコンクリート硬化遅延剤層を形成し、この凹凸模
様面を接触面にしてコンクリート材料を打設し、養生硬
化後上記化粧型枠を剥離し、得られたコンクリート製品
の表面に洗い出しを施し、内部の骨材を露出させる。According to the method for producing a concrete product of the present invention, a decorative formwork having an uneven pattern formed on its surface is prepared, a concrete hardening retardant layer is formed on the uneven pattern surface, and the uneven pattern surface is used as a contact surface. After the concrete material is cast and cured and cured, the decorative form is peeled off, and the surface of the obtained concrete product is washed out to expose the internal aggregate.
【００１２】上記化粧型枠は、硬質発泡ウレタン樹脂製
のもの等が用いられる。例えば、図１に示すように、上
記化粧型枠１として、硬質のウレタン発泡体で構成さ
れ、一方の面が、コンクリート材料に接触してコンクリ
ート表面に凹凸模様を転写する凹凸模様転写面２に、他
方の面が平坦面３に形成されたものが用いられる。この
ような化粧型枠１は、例えば、上記凹凸模様と逆の凸凹
模様を有する金型内に、液状発泡ウレタン樹脂を注入し
硬化させることにより製造され、内部が発泡層に、金型
の凸凹模様に接する表面が緻密なインテグラルスキン層
に形成されている。このインテグラルスキン層は、実質
的に気泡が存在せず高密度で緻密に形成され、表面平滑
性に富んでいる。このインテグラルスキン層の平滑な表
面で上記凹凸模様転写面２が形成されている。As the decorative mold, one made of hard urethane foam resin or the like is used. For example, as shown in FIG. 1, the decorative form 1 is made of a hard urethane foam, and one surface of the decorative form 1 is provided on an uneven pattern transfer surface 2 which contacts a concrete material and transfers the uneven pattern to the concrete surface. And the other surface formed on the flat surface 3 is used. Such a decorative mold 1 is manufactured, for example, by injecting a liquid urethane resin into a mold having a concavo-convex pattern opposite to the above concavo-convex pattern and curing the resin. The surface in contact with the pattern is formed on a dense integral skin layer. This integral skin layer is formed densely and densely with substantially no bubbles, and has excellent surface smoothness. The uneven pattern transfer surface 2 is formed on the smooth surface of the integral skin layer.
【００１３】上記コンクリート硬化遅延剤は、コンクリ
ート材料の硬化を遅らせるものであれば各種のものが用
いられ、特に限定されるものではない。例えば、紫外線
硬化型樹脂，アルカリにより加水分解する物質，カルシ
ウムイオンを吸着する物質等を使用することができる。As the concrete hardening retardant, various ones can be used as long as they slow the hardening of the concrete material, and are not particularly limited. For example, a UV-curable resin, a substance hydrolyzed by an alkali, a substance that adsorbs calcium ions, and the like can be used.
【００１４】上記紫外線硬化型樹脂としては、例えば、
１・６−ヘキサンジオールジアクリレート，ネオペンチ
ルグリコールジアクリレート，トリメチロールプロパン
トリアクリレート，ペンタエリスリトールトリアクリレ
ート，ペンタエリスリトールテトラメタクリレート等の
アクリレート、α，α−テトラアクリル−ビストリメチ
ロールプロパンテトラヒドロフタレート，α，α−ジメ
タクリル−ビスジエチレングリコールフタレート等のフ
タレート、トリレンジイソジアネート，イソホロンジイ
ソシアネート等に２−ヒドロキシエチルアクリレート
（ＨＥＡ）を反応させた化合物，ヘキサンジオールとイ
ソホロンジイソシアネートにＨＥＡを反応させた化合
物，ビスフェノールＡ−ジグリシジルエーテルのジアク
リレート，トリメチロールプロパンポリグリシジルエー
テルポリアクリレート，スピログリコールジグリシジル
エーテルジアクリレート，シリコーンアクリレート，ト
リアクリロイルオキシエチルイソシアヌレート等があげ
られる。[0014] Examples of the UV-curable resin include:
Acrylates such as 1,6-hexanediol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetramethacrylate, α, α-tetraacryl-bistrimethylolpropane tetrahydrophthalate, α, α Phthalate such as -dimethacryl-bisdiethylene glycol phthalate, a compound obtained by reacting 2-hydroxyethyl acrylate (HEA) with tolylene diisodianate, isophorone diisocyanate, a compound obtained by reacting HEA with hexanediol and isophorone diisocyanate, bisphenol A -Diacrylates of diglycidyl ether, trimethylolpropane polyglycidyl ether polyacrylate, Pyro glycol diglycidyl ether diacrylate, silicone acrylate, triacryloyl oxyethyl isocyanurate and the like.
【００１５】また、アルカリにより加水分解してコンク
リートの硬化を抑制する物質としては、例えば、ポリ酢
酸ビニル等のエステル類やヘミセルロース等があげられ
る。また、カルシウムイオンを吸着してコンクリートの
硬化を抑制する物質としては、例えば、イオン化傾向が
カルシウムよりも大きいカリウム，ナトリウムの塩類，
フェノール類，セルロースおよびリグニン等があげられ
る。Examples of the substance which inhibits the hardening of concrete by being hydrolyzed by an alkali include, for example, esters such as polyvinyl acetate and hemicellulose. Examples of the substance that inhibits hardening of concrete by adsorbing calcium ions include, for example, potassium and sodium salts, which have a higher ionization tendency than calcium,
Examples include phenols, cellulose, and lignin.
【００１６】また、上記以外に、コンクリートの硬化を
抑制する物質として、不飽和ポリエステル樹脂，エポキ
シ（メタ）アクリレート等のビニルエステル樹脂，ホス
ホン酸基を有する樹脂等の樹脂材料や、各種の有機物，
無機物が用いられる。上記有機物としては、グルコヘプ
トン酸，グルコン酸，ガラクトン酸，粘液酸，クエン
酸，アラボン酸，エリスロン酸，酒石酸，リンゴ酸，ト
レオニン（アミノ酸），コハク酸，マレイン酸，グリセ
リン酸，グリコール酸，シュウ酸，乳酸等のオキシカル
ボン酸およびジカルボン酸またはその塩、２ケトグルコ
ン酸，ピルビン酸等のケトカルボン酸、カプロン酸，吉
草酸，酪酸，プロピオン酸，酢酸等の脂肪酸、ペルセイ
トール，ソルビトール，アラビトール，エリスリトー
ル，グリセロール，エチレングリコール等の糖アルコー
ル類、グルコヘプトース，グルコース，マンノース，ガ
ラクトース，フラクトース，アラビノース，エリスロー
ス，グリセルアルデヒド，サッカロース（ショ糖），ラ
クトース，マルトース，ラフィノース，デキストリン等
の糖類、リグニンスルホン酸、アミノジ（メチレンホス
ホン酸），アミノトリ（メチレンホスホン酸），１−ヒ
ドロキシエチリデン−１，１−ジホスホン酸，エチレン
ジアミンテトラ（メチレンホスホン酸），ジエチレント
リアミンペンタ（メチレンホスホン酸），ヘキサメチレ
ンジアミンテトラ（メチレンホスホン酸），またはそれ
らの塩等のホスホン酸系硬化遅延剤、シュウ酸，マロン
酸等の飽和多価カルボン酸、フマル酸，イタコン酸等の
不飽和多価カルボン酸、グルコヘプタノン酸等の多価カ
ルボン酸又はその塩、ポリマレイン酸，ポリフマル酸，
スチレン−マレイン酸共重合体，ポリアクリル酸，ポリ
メタクリル酸，スチレン−（メタ）アクリル酸共重合
体，（メタ）アクリル酸エステル−（メタ）アクリル酸
共重合体，エチレンスルホン酸−アクリル酸コポリマー
等のカルボシキル基を有するモノマーの単独または共重
合体もしくはそれらの塩、アスコルビン酸，イソアスコ
ルビン酸等の酸化防止剤、ポリヒドロキシシラン，ポリ
アクリルアミド等のポリマー、フミン酸、リグノスルホ
ネート、ケルトカルボン酸類，水溶性でんぷん，ライ麦
の粉末，アラビアゴム，アルコール類等があげられる。
また、無機物としては、珪フッ化マグネシウム，トリポ
リリン酸ナトリウム，酸化亜鉛，ホウ素化合物，ホウ酸
塩，リン酸塩（特にヘキサメタリン酸ソーダ），ヘキサ
フルオロケイ酸塩等があげられる。[0016] In addition to the above, as a substance that suppresses the hardening of concrete, resin materials such as unsaturated polyester resin, vinyl ester resin such as epoxy (meth) acrylate, resin having phosphonic acid group, various organic substances,
Inorganic substances are used. Examples of the organic substances include glucoheptonic acid, gluconic acid, galactonic acid, mucous acid, citric acid, arabic acid, erythronic acid, tartaric acid, malic acid, threonine (amino acid), succinic acid, maleic acid, glyceric acid, glycolic acid, and oxalic acid. , Oxycarboxylic acids such as lactic acid and dicarboxylic acids or salts thereof, ketocarboxylic acids such as ketogluconic acid and pyruvic acid, fatty acids such as caproic acid, valeric acid, butyric acid, propionic acid and acetic acid, perseitol, sorbitol, arabitol, erythritol, glycerol , Sugar alcohols such as ethylene glycol, glucoheptose, glucose, mannose, galactose, fructose, arabinose, erythrose, glyceraldehyde, saccharose (sucrose), lactose, maltose, raffinose, dex. Sugars such as trines, ligninsulfonic acid, aminodi (methylenephosphonic acid), aminotri (methylenephosphonic acid), 1-hydroxyethylidene-1,1-diphosphonic acid, ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylenephosphonic acid) , Hexamethylenediaminetetra (methylenephosphonic acid) or their salts, etc., phosphonic acid-based curing retarders, oxalic acid, saturated polycarboxylic acids such as malonic acid, and unsaturated polycarboxylic acids such as fumaric acid and itaconic acid , Polycarboxylic acids such as glucoheptanonic acid or salts thereof, polymaleic acid, polyfumaric acid,
Styrene-maleic acid copolymer, polyacrylic acid, polymethacrylic acid, styrene- (meth) acrylic acid copolymer, (meth) acrylate- (meth) acrylic acid copolymer, ethylenesulfonic acid-acrylic acid copolymer Homo- or copolymers of monomers having a carboxy group such as, or salts thereof, antioxidants such as ascorbic acid, isoascorbic acid, polymers such as polyhydroxysilane, polyacrylamide, humic acid, lignosulfonate, celtic carboxylic acids, Examples include water-soluble starch, rye powder, gum arabic, and alcohols.
Examples of the inorganic substance include magnesium fluorosilicate, sodium tripolyphosphate, zinc oxide, boron compounds, borates, phosphates (particularly sodium hexametaphosphate), and hexafluorosilicates.
【００１７】上記コンクリート硬化遅延剤は、単独でも
しくは併せて使用することができる。また、適当な溶媒
に溶解もしくは混合分散させて液状として使用するの
が、作業性の観点から好ましい。また、粘着剤，接着
剤，樹脂液，粘度調整液，充填材，吸水膨潤剤等と混合
させてもよい。さらに、各コンクリート硬化遅延剤の性
状（固体，液体，粘度，粒度，ＰＨ等）により、洗い出
しによって除去されるコンクリート材料の量や、硬化遅
延時間等に差があるため、濃度や種類，組み合わせ，使
用法等を適宜に変更し、所望の除去量、硬化遅延時間に
設定すればよい。このとき、除去量は、コンクリート材
料を打設した表面から、約１〜３ｍｍ（最適には２ｍ
ｍ）程度の深さが除去されるのが、凹凸模様形成面の凹
凸模様の表現が消えてしまわず、しかも、骨材の露出等
の洗い出しによる表現も生きるため、好ましい。また、
液状としたコンクリート硬化遅延剤を粘着剤等と混合さ
せて塗布したり、あらかじめ化粧型枠１の表面に粘着剤
層を形成させ、そのうえにコンクリート硬化遅延剤を塗
布等するようにしてもよい。The concrete hardening retardants can be used alone or in combination. Further, it is preferable to dissolve or mix and disperse in an appropriate solvent to use as a liquid from the viewpoint of workability. Further, it may be mixed with an adhesive, an adhesive, a resin liquid, a viscosity adjusting liquid, a filler, a water-absorbing swelling agent, and the like. In addition, depending on the properties (solid, liquid, viscosity, particle size, PH, etc.) of each concrete setting retarder, there are differences in the amount of concrete material removed by washing and the setting delay time. The method of use may be appropriately changed, and the desired removal amount and curing delay time may be set. At this time, the removal amount is about 1 to 3 mm (optimally 2 m) from the surface on which the concrete material is cast.
It is preferable to remove the depth of about m), since the expression of the uneven pattern on the uneven pattern forming surface does not disappear, and the expression by washing out such as the exposure of the aggregates is preferable. Also,
A liquid concrete hardening retardant may be mixed with an adhesive or the like and applied, or an adhesive layer may be previously formed on the surface of the decorative form 1 and a concrete hardening retarder may be applied thereon.
【００１８】上記化粧型枠１の凹凸模様転写面２に、図
２（ａ）に示すように、コンクリート硬化遅延剤を刷毛
２５もしくはスプレー噴霧等で塗布し、図２（ｂ）に示
すように、乾燥硬化させ、図２（ｃ）に示すように遅延
剤層４を形成する。図２（ａ）において２６はスプレー
ノズル、図２（ｂ）において２７は乾燥炉である。As shown in FIG. 2 (a), a concrete hardening retardant is applied to the concave / convex pattern transfer surface 2 of the decorative form frame 1 by means of a brush 25 or spray spraying, as shown in FIG. 2 (b). After drying and curing, a retarder layer 4 is formed as shown in FIG. In FIG. 2A, 26 is a spray nozzle, and in FIG. 2B, 27 is a drying furnace.
【００１９】コンクリート硬化遅延剤を塗布する方法と
しては、上述した刷毛塗りやスプレー噴霧に限らず、ロ
ーラー塗布，ディッピング等各種の方法が行われ、特に
限定されるものではない。また、乾燥硬化も、自然放
置，熱風乾燥，赤外線乾燥等各種の方法が行われ、特に
限定されるものではない。乾燥条件も、使用するコンク
リート硬化遅延剤の種類等によって各種の条件で行われ
るが、おおむね、常温〜６０℃程度の温度で数十分〜数
時間かけて行われる。このようにして形成された遅延剤
層４の厚みは、０．０５〜２ｍｍ程度が好ましい。０．
０５ｍｍ未満では、充分なコンクリートの硬化抑制作用
が得られず、２ｍｍを越えると洗浄除去されるコンクリ
ート材料が多くなりすぎて歩留りが悪くなるうえ、塗布
と乾燥を何回も繰り返す必要が生じ、生産性が悪くなる
からである。The method of applying the concrete hardening retardant is not limited to the above-mentioned brush coating and spraying, but various methods such as roller coating and dipping are performed, and are not particularly limited. Various methods such as natural standing, hot air drying, and infrared drying are also used for drying and curing, and are not particularly limited. The drying condition is also performed under various conditions depending on the type of concrete hardening retardant to be used and the like, but is generally performed at room temperature to about 60 ° C. for several tens of minutes to several hours. The thickness of the retarder layer 4 thus formed is preferably about 0.05 to 2 mm. 0.
If the thickness is less than 05 mm, sufficient hardening inhibitory effect of concrete cannot be obtained. If the thickness exceeds 2 mm, the concrete material to be washed and removed becomes too large, the yield is deteriorated, and the application and drying must be repeated many times. This is because the sex becomes worse.
【００２０】そして、図３に示すように、化粧型枠１の
背面側の平坦面３が型枠５に取り付けられ、他の型枠６
に対して所定の間隔で配置され、型枠６と化粧型枠１と
の側方の開口（図示せず）と底部の開口とが板材７等で
塞がれ、上部開口からコンクリート材料１５が流し込ま
れて上記凹凸模様転写面２を接触面としてコンクリート
材料１５が打設され、上記コンクリート材料１５が養生
硬化されてコンクリート化する。図において、１０は骨
材である。このとき、化粧型枠１の凹凸模様転写面２に
形成された遅延剤層４の作用により、凹凸模様転写面２
と接触した表面層のコンクリート材料１５の硬化が抑制
もしくは遅延され、凹凸模様転写面２との接触部分が軟
らかく、内部だけが硬化したコンクリートとなる。Then, as shown in FIG. 3, the flat surface 3 on the back side of the decorative mold 1 is attached to the mold 5 and another mold 6 is formed.
Are arranged at a predetermined distance from each other, the side opening (not shown) and the bottom opening of the formwork 6 and the decorative formwork 1 are closed by the plate material 7 or the like, and the concrete material 15 flows from the upper opening. The concrete material 15 is poured with the concave-convex pattern transfer surface 2 as a contact surface, and the concrete material 15 is cured and hardened into concrete. In the figure, reference numeral 10 denotes an aggregate. At this time, the concave and convex pattern transfer surface 2 is formed by the action of the retarder layer 4 formed on the concave and convex pattern transfer surface 2 of the decorative mold 1.
The hardening of the concrete material 15 of the surface layer in contact with the surface is suppressed or delayed, the contact portion with the uneven pattern transfer surface 2 is soft, and only the inside is hardened concrete.
【００２１】そののち、上記化粧型枠１を、図４に示す
ように、コンクリート製品８から剥離させる。このよう
にして得られたコンクリート製品８の表面は上記化粧型
枠１の凹凸模様転写面２が転写された凹凸模様形成面９
となる。そして、この凹凸模様形成面９の表面層は軟ら
かい未硬化層１１となっている。このため、化粧型枠１
に、特別に離型剤等を塗布させることなく、化粧型枠１
を容易に剥離することができ、しかも化粧型枠１の損傷
も少ない。Thereafter, the decorative form 1 is peeled off from the concrete product 8 as shown in FIG. The surface of the concrete product 8 thus obtained is provided with the uneven pattern forming surface 9 to which the uneven pattern transfer surface 2 of the decorative form 1 is transferred.
Becomes The surface layer of the uneven pattern forming surface 9 is a soft uncured layer 11. For this reason, the decorative form 1
Without applying a mold release agent, etc.
Can be easily peeled off, and the decorative mold 1 is hardly damaged.
【００２２】そして、図５に示すように、上記表面の未
硬化層１１に対して洗い出しを施すことが行われる。洗
い出しは、例えば、高圧水（２〜４０ｋｇ／ｃｍ2 ）を
コンクリート製品８の表面に噴射することにより行われ
るが、これに限定されるものではない。この洗い出しに
より、表面の未硬化層１１のセメントが除去され、凹凸
模様形成面９に、コンクリート材料中の骨材１０が露呈
するとともに、骨材１０のない部分の表面は微小凹凸の
粗面２８となる。これにより、化粧型枠１によって凹凸
模様が転写形成されるとともに、骨材１０が露呈し、し
かも骨材１０のない表面が粗面２８に形成されることに
より、コンクリートの素材感が活かされた自然石調の凹
凸模様が形成され、従来にない自然に近い表現がされた
コンクリート製品８となる。しかも、養生硬化後のコン
クリート製品８が水洗い等されるため、コンクリート打
ちっぱなしの場合と比べ、最終製品がきれいになる。Then, as shown in FIG. 5, the uncured layer 11 on the surface is washed out. Washing is performed, for example, by spraying high-pressure water ( 2 to 40 kg / cm 2 ) on the surface of the concrete product 8, but is not limited thereto. By this washing, the cement of the uncured layer 11 on the surface is removed, and the aggregate 10 in the concrete material is exposed on the uneven pattern forming surface 9, and the surface of the portion without the aggregate 10 has a rough surface 28 with minute unevenness. Becomes As a result, the embossed pattern is transferred and formed by the decorative formwork 1, and the aggregate 10 is exposed, and the surface without the aggregate 10 is formed on the rough surface 28, so that the material feeling of the concrete is utilized. A natural stone-like uneven pattern is formed, and the concrete product 8 expresses an unusually natural expression. In addition, since the cured and cured concrete product 8 is washed with water, the final product is cleaner than in the case where the concrete is left standing.
【００２３】なお、上記コンクリート製品８に、塗装等
を行って着色するようにしてもよい。また、コンクリー
ト材料１５中に顔料等を混合させることにより着色され
たコンクリート製品８を得るようにしてもよい。The concrete product 8 may be colored by painting or the like. Alternatively, a colored concrete product 8 may be obtained by mixing a pigment or the like into the concrete material 15.
【００２４】つぎに、実施例について説明する。Next, an embodiment will be described.
【００２５】[0025]
【実施例１】図１に示す化粧型枠１の凹凸模様転写面２
に、コンクリート硬化遅延剤を下記の組成で調整し、そ
の調整液をエア吹き付け（ガンタイプ，エア吹き付け圧
力２〜７ｋｇ／ｃｍ2 ）によって塗布し（塗布量２０〜
６０ｇ／ｍ2 ）、２０℃で４時間乾燥硬化させて遅延剤
層４を形成させ、本発明の化粧型枠を得た。 〔組成〕 変成リグニン＋オキシカルボン酸化合物の複合体 （商品名：ポゾリス＃１００，エヌエスビー社製） １００重量部 水 １〜１０重量部 メチルセルロース （商品名：Ｈｉメトローズ４０００，信越化学工業社製） １〜５重量部Embodiment 1 An uneven pattern transfer surface 2 of a decorative mold 1 shown in FIG.
Then, a concrete hardening retardant is adjusted with the following composition, and the adjusted liquid is applied by air spraying (gun type, air spraying pressure 2 to 7 kg / cm 2 ) (coating amount 20 to 20).
60 g / m 2 ), dried and cured at 20 ° C. for 4 hours to form a retarder layer 4, thereby obtaining a decorative mold of the present invention. [Composition] Complex of modified lignin and oxycarboxylic acid compound (trade name: Pozzolith # 100, manufactured by NSB) 100 parts by weight Water 1 to 10 parts by weight methylcellulose (trade name: Hi Metroze 4000, manufactured by Shin-Etsu Chemical Co., Ltd.) 1-5 parts by weight
【００２６】[0026]
【実施例２】コンクリート硬化遅延剤の調整液の塗布方
法をハケ，ローラー塗りにする以外は、実施例１と同様
にして本発明の化粧型枠を得た。Example 2 A decorative mold of the present invention was obtained in the same manner as in Example 1, except that the method of applying the adjusting solution for the concrete hardening retardant was brushing and roller coating.
【００２７】[0027]
【実施例３】コンクリート硬化遅延剤の調整液を２回重
ね塗りにし、４０℃で１時間乾燥硬化させる以外は、実
施例１と同様にして本発明の化粧型枠を得た。Example 3 A decorative mold of the present invention was obtained in the same manner as in Example 1, except that the preparation solution of the concrete hardening retardant was applied twice and dried and hardened at 40 ° C. for 1 hour.
【００２８】[0028]
【実施例４】コンクリート硬化遅延剤として、グルコン
酸ナトリウム塩（商品名：デスパライトＤＶ，共栄化学
社製）を使用し、図１に示す化粧型枠１の凹凸模様転写
面２に、ハケ，ローラーによって塗布し（塗布量１５０
〜３５０ｇ／ｍ2 ）、６０℃で３０分乾燥硬化させて遅
延剤層４を形成させ、本発明の化粧型枠を得た。Example 4 As a concrete hardening retarder, sodium gluconate (trade name: Desparite DV, manufactured by Kyoei Chemical Co., Ltd.) was used, and the embossed pattern transfer surface 2 of the decorative mold 1 shown in FIG. Apply by roller (application amount 150
To 350 g / m 2 ), and dried and cured at 60 ° C. for 30 minutes to form a retarder layer 4, thereby obtaining a decorative mold of the present invention.
【００２９】[0029]
【実施例５】コンクリート硬化遅延剤を下記の組成で調
整し、その調整液を図１に示す化粧型枠１の凹凸模様転
写面２に、エア吹き付け（ガンタイプ，高粘度吹き付
け，圧送圧力５ｋｇ／ｃｍ2 ，エア吹き付け圧力５ｋｇ
／ｃｍ2 ）によって塗布し（塗布量１５０〜４００ｇ／
ｍ2 ，塗布厚み０．０５〜２ｍｍ）、２０℃で８時間乾
燥硬化させて遅延剤層４を形成させ、本発明の化粧型枠
を得た。 〔組成〕 酢ビ・アクリルエマルジョン （商品名：ボンコート＃９１８０，大日本インキ化学工業社製） ８０重量部 ポリビニルアルコール （商品名：デンカポバール，電気化学工業社製） ２０重量部 酸化亜鉛 １０重量部 オキシカルボン酸塩 （商品名：ポゾリス，エヌエスビー社製） ５重量部Example 5 A concrete hardening retardant was prepared according to the following composition, and the prepared liquid was sprayed by air (gun type, high-viscosity spraying, pumping pressure of 5 kg) onto the concave / convex pattern transfer surface 2 of the decorative mold 1 shown in FIG. / Cm 2 , air blowing pressure 5kg
/ Cm 2 ) (coating amount 150 to 400 g /
m 2 , coating thickness: 0.05 to 2 mm) and dried and cured at 20 ° C. for 8 hours to form a retarder layer 4, thereby obtaining a decorative mold of the present invention. [Composition] Vinyl acetate / acryl emulsion (trade name: Boncoat # 9180, manufactured by Dainippon Ink and Chemicals, Inc.) 80 parts by weight Polyvinyl alcohol (trade name: Denka Poval, manufactured by Denki Kagaku Kogyo) 20 parts by weight Zinc oxide 10 parts by weight 5 parts by weight of oxycarboxylate (trade name: POZORIS, NSB)
【００３０】[0030]
【実施例６】乾燥条件を４０℃で２時間にする以外は、
実施例５と同様にして本発明の化粧型枠を得た。Example 6 Except that the drying condition was 40 ° C. for 2 hours,
In the same manner as in Example 5, a decorative mold of the present invention was obtained.
【００３１】[0031]
【実施例７】乾燥条件を６０℃で４５分にする以外は、
実施例５と同様にして本発明の化粧型枠を得た。Example 7 Except that the drying condition was 60 ° C. for 45 minutes,
In the same manner as in Example 5, a decorative mold of the present invention was obtained.
【００３２】上記実施例１〜７の化粧型枠１を使用して
枠組みし、コンクリート材料を打設し、養生硬化させた
（図３参照）。そして、化粧型枠１等を剥離したのち、
高圧水（１０ｋｇ／ｃｍ2 ）の噴射により洗い出しを施
し、表面の未硬化層１１のセメントを除去し、コンクリ
ート製品８を得た（図５参照）。A frame was formed using the decorative formwork 1 of Examples 1 to 7, a concrete material was cast, and the material was cured and cured (see FIG. 3). Then, after peeling off the decorative form 1 and the like,
Washing was performed by spraying high-pressure water (10 kg / cm 2 ) to remove the cement of the uncured layer 11 on the surface, and a concrete product 8 was obtained (see FIG. 5).
【００３３】このようにして得られた各コンクリート製
品８は、洗い出しによりコンクリート中の骨材１０等が
露呈されるとともに粗面２８が形成され、コンクリート
の素材感が活かされた自然石調の凹凸模様が形成された
コンクリート製品が得られた。Each of the concrete products 8 thus obtained exposes the aggregates 10 and the like in the concrete by washing out, forms a rough surface 28, and has a natural stone-like unevenness utilizing the texture of the concrete. A patterned concrete product was obtained.
【００３４】[0034]
【発明の効果】以上のように、本発明によれば、コンク
リート製品の表面に化粧型枠の凹凸模様が転写形成され
るだけでなく、コンクリート硬化遅延剤の作用によって
形成される凹凸模様形成面の表面未硬化層が水等による
洗い出しによって除去される。この除去により、コンク
リート中の骨材が露呈されるとともに、骨材以外の表面
は微小凹凸の粗面に形成される。このように、化粧型枠
の凹凸模様が転写形成され、しかも、この凹凸模様形成
面に骨材が露呈するともに、粗面に形成されることによ
り、コンクリートの素材感が活かされた自然石調の凹凸
模様が形成され、従来にない自然に近い表現がされたコ
ンクリート製品が得られる。As described above, according to the present invention, not only the concave and convex pattern of the decorative mold is transferred to the surface of the concrete product, but also the concave and convex pattern forming surface formed by the action of the concrete setting retarder. Is removed by washing with water or the like. By this removal, the aggregate in the concrete is exposed, and the surface other than the aggregate is formed as a rough surface with minute irregularities. In this way, the concave and convex pattern of the decorative form is transferred and formed, and the aggregate is exposed on the concave and convex pattern forming surface and is formed on the rough surface. Thus, a concrete product with an expression close to nature, which has never been seen before, can be obtained.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明の化粧型枠を示す説明図である。FIG. 1 is an explanatory view showing a decorative mold frame of the present invention.
【図２】上記化粧型枠に遅延剤層を形成させる工程を示
す図であり、（ａ）はコンクリート硬化遅延剤を塗布す
る状態を示す説明図、（ｂ）は上記コンクリート硬化遅
延剤を乾燥硬化させる状態を示す説明図、（ｃ）は遅延
剤層が形成された本発明の化粧型枠を示す説明図であ
る。FIG. 2 is a view showing a step of forming a retarder layer on the decorative mold, wherein (a) is an explanatory view showing a state of applying a concrete retarder, and (b) is a diagram showing drying of the concrete retarder. FIG. 3C is an explanatory view showing a state of curing, and FIG. 4C is an explanatory view showing a decorative mold of the present invention on which a retarder layer is formed.
【図３】上記化粧型枠を使用してコンクリート材料を打
設した状態を示す説明図である。FIG. 3 is an explanatory view showing a state where a concrete material is cast using the decorative formwork.
【図４】コンクリート製品から化粧型枠を剥離させる状
態を示す説明図である。FIG. 4 is an explanatory view showing a state in which a decorative form is detached from a concrete product.
【図５】コンクリート製品の未硬化層を洗い出しにより
除去する状態を示す説明図である。FIG. 5 is an explanatory view showing a state in which an uncured layer of a concrete product is removed by washing out.
【図６】従来例の化粧マットを示す説明図である。FIG. 6 is an explanatory view showing a conventional decorative mat.
【図７】上記化粧マットを用いたコンクリート製品の製
法を示す説明図である。FIG. 7 is an explanatory view showing a method for producing a concrete product using the decorative mat.
【図８】上記化粧マットを用いたコンクリート製品の製
法を示す説明図である。FIG. 8 is an explanatory view showing a method for producing a concrete product using the decorative mat.
【図９】他の従来例の化粧マットを示す説明図である。FIG. 9 is an explanatory view showing another conventional decorative mat.
【図１０】上記化粧マットを用いたコンクリート製品の
製法を示す説明図である。FIG. 10 is an explanatory view showing a method for producing a concrete product using the decorative mat.
【図１１】上記化粧マットを用いたコンクリート製品の
製法を示す説明図である。FIG. 11 is an explanatory view showing a method for producing a concrete product using the decorative mat.
【符号の説明】 １ 化粧型枠 ２ 凹凸模様転写面 ４ 遅延剤層 １０ 骨材 １５ コンクリート材料[Description of Signs] 1 decorative mold 2 transfer surface of uneven pattern 4 retarder layer 10 aggregate 15 concrete material
Claims (2)
準備し、上記凹凸模様面にコンクリート硬化遅延剤層を
形成し、この凹凸模様面を接触面にしてコンクリート材
料を打設し、養生硬化後上記化粧型枠を剥離し、得られ
たコンクリート製品の表面に対して洗い出しを施し、内
部の骨材を露出させることを特徴とするコンクリート製
品の製法。1. A decorative formwork having an uneven pattern formed on the surface thereof is prepared, a concrete hardening retardant layer is formed on the uneven pattern surface, and a concrete material is cast with the uneven pattern surface as a contact surface. A method for producing a concrete product, wherein the decorative form is peeled off after curing and curing, and the surface of the obtained concrete product is washed out to expose aggregates therein.
様面を接触面にしてコンクリート材料を打設する化粧型
枠であって、上記凹凸模様面にコンクリート硬化遅延剤
層を形成したことを特徴とする化粧型枠。2. A decorative formwork in which an uneven pattern is formed on a surface, and a concrete material is cast by using the uneven pattern surface as a contact surface, wherein a concrete hardening retardant layer is formed on the uneven pattern surface. Characteristic makeup frame.