JPH08323921A - Fluoroplastic laminated heat-proof panel - Google Patents
Fluoroplastic laminated heat-proof panelInfo
- Publication number
- JPH08323921A JPH08323921A JP13547595A JP13547595A JPH08323921A JP H08323921 A JPH08323921 A JP H08323921A JP 13547595 A JP13547595 A JP 13547595A JP 13547595 A JP13547595 A JP 13547595A JP H08323921 A JPH08323921 A JP H08323921A
- Authority
- JP
- Japan
- Prior art keywords
- heat insulating
- fluororesin
- laminated
- plate
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、特に厨房のいわゆるコ
ンロ前壁部材に好適な、清掃性、防熱性、さらには軽量
で現場施工性に優れたフッ素樹脂積層の防熱板に関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heat-insulating plate of a fluororesin laminate, which is suitable for a so-called front wall member of a kitchen in particular, which is easy to clean, heat-resistant, lightweight and excellent in on-site construction.
【０００２】[0002]
【従来の技術】現在、厨房のコンロ前壁部材には、タイ
ル面材が使用されることが多い。また、ステンレス等の
金属板を張った場合も見受けられる。2. Description of the Related Art At present, a tile surface material is often used for a front wall member of a kitchen stove. It can also be seen when a metal plate such as stainless steel is stretched.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、タイル
面材を使用した場合には、耐熱性は良好であるが、施
工、下地処理等に労力を要し、現場施工性に難点があ
り、施工費用の抑制が困難である。また、タイル表面、
目地に油汚れが付きやすく、掃除が大変である。一方、
コンロ前壁部材に金属板を使用した場合には、耐熱性に
は問題はないが、汚れが付着しやすい上に金属板がコン
ロ等の熱源により局所的に高温となりやすく、極端な場
合金属板の内側における建材等が低温発火するおそれが
ある。本発明は、以上のような課題を解決するために提
案されたものであって、清掃性、防熱性に優れ、さらに
は軽量で現場施工性に優れた、特に厨房のコンロ前壁部
材に好適なフッ素樹脂積層の防熱板を提供することを目
的とする。However, when the tile surface material is used, heat resistance is good, but labor is required for construction, surface treatment, etc., and there is a difficulty in construction workability at the site. Is difficult to control. Also, the tile surface,
It is difficult to clean the joints because oil stains easily adhere to them. on the other hand,
When a metal plate is used for the stove front wall member, there is no problem with heat resistance, but dirt easily adheres and the metal plate easily becomes locally hot due to the heat source such as the stove. There is a risk of low temperature ignition of building materials inside. The present invention has been proposed in order to solve the above problems, excellent in cleanability and heat insulation, further lightweight and excellent in on-site workability, particularly suitable for a stove front wall member of a kitchen An object of the present invention is to provide a heat-insulating plate laminated with another fluororesin.
【０００４】[0004]
【課題を解決するための手段】前記した課題を解決する
ために、本発明は、伝熱性の高い金属板にフッ素樹脂を
積層したことを特徴とする。また、本発明は、伝熱性の
高い金属板にフッ素樹脂を積層すると共に、この金属板
を、断熱材の少なくとも片面に積層したことを特徴とす
る。前述の構成において、断熱材は不燃材によって構成
したことを特徴とする。また、断熱材は石膏ボードであ
ることを特徴とする。また、前記断熱材はロックウール
であることを特徴とする。また、前記断熱材はグラスウ
ールであることを特徴とする。また、前記断熱材は発泡
プラスチック系断熱材であることを特徴とする。また、
前記断熱材は木質繊維系断熱材であることを特徴とす
る。また、前記断熱材は中間に断熱空間を備えたもので
あることを特徴とする。また、前記断熱材はハニカム構
造基材であることを特徴とする。また、前記フッ素樹脂
を金属板に熱溶着したことを特徴とする。また、前記フ
ッ素樹脂を金属板に接着したことを特徴とする。また、
前記フッ素樹脂の金属板との積層面に模様を施したこと
を特徴とする。また、前記金属板のフッ素樹脂との積層
面に模様を施したことを特徴とする。また、前記フッ素
樹脂の金属板との積層面に文字を付したことを特徴とす
る。また、前記金属板のフッ素樹脂との積層面に文字を
付したことを特徴とする。また、前記フッ素樹脂積層の
防熱板を厨房におけるコンロ周りの壁面に適用したこと
を特徴とする。さらに、前記フッ素樹脂積層の防熱板を
防火扉に適用したことを特徴とする。In order to solve the above-mentioned problems, the present invention is characterized in that a fluororesin is laminated on a metal plate having high heat conductivity. Further, the present invention is characterized in that a fluororesin is laminated on a metal plate having high heat conductivity, and that this metal plate is laminated on at least one surface of a heat insulating material. In the above configuration, the heat insulating material is made of a non-combustible material. The heat insulating material is a gypsum board. Further, the heat insulating material is rock wool. Further, the heat insulating material is glass wool. The heat insulating material is a foamed plastic heat insulating material. Also,
The heat insulating material is a wood fiber heat insulating material. Further, the heat insulating material is characterized by having a heat insulating space in the middle. The heat insulating material is a honeycomb structure base material. Further, it is characterized in that the fluororesin is heat-welded to a metal plate. Further, it is characterized in that the fluororesin is adhered to a metal plate. Also,
It is characterized in that a pattern is formed on a surface of the fluororesin laminated with the metal plate. In addition, the laminated surface of the metal plate with the fluororesin is patterned. Further, characters are attached to a surface of the fluororesin laminated with the metal plate. Further, a character is attached to a surface of the metal plate laminated with the fluororesin. Further, the heat insulating plate of the fluororesin laminate is applied to a wall surface around a stove in a kitchen. Furthermore, the heat insulating plate of the fluororesin laminate is applied to a fire door.
【０００５】[0005]
【作用】本発明によれば、フッ素樹脂により清掃性に優
れ、金属板に断熱材を積層したものにあっては防熱性に
優れ、さらには鋸、カッター等の工具により切断加工が
容易であり、現場施工性に優れたものとなる。なお、前
記フッ素樹脂の金属板との積層面や、金属板のフッ素樹
脂との積層面に模様を施したものにあっては、意匠性の
向上がもたらされ、さらに、金属板またはフッ素樹脂側
の積層面に文字を付すようにすると、様々な実用的な有
用性がもたらされる。EFFECTS OF THE INVENTION According to the present invention, the cleaning property is excellent with the fluororesin, the heat insulating property is excellent in the case where the heat insulating material is laminated on the metal plate, and the cutting process is easy with a tool such as a saw or a cutter. It becomes excellent in on-site workability. In addition, in the case where the laminated surface of the fluororesin with the metal plate or the laminated surface of the metal plate with the fluororesin is patterned, the design is improved, and further, the metal plate or the fluororesin is used. Marking the side laminate surface provides a variety of practical benefits.
【０００６】[0006]
【実施例】次に、本発明にかかるフッ素樹脂積層の防熱
板について、一実施例を挙げ、添付の図面を参照しなが
ら以下説明する。図１に厨房１を示し、この厨房１にお
けるコンロ２の前壁および側壁には、本発明にかかるフ
ッ素樹脂積層の防熱板３が装着されている。この防熱板
３は、図２に示すように伝熱性の高い金属板、例えばア
ルミニウム板４に非粘着性、耐熱性に優れるフッ素樹脂
フィルム５を積層した構成としている。前記アルミニウ
ム板４は、厚さが０．１〜２．０ｍｍ（好ましくは０．
３〜１．０ｍｍ）のもので、伝熱性の高い、すなわち熱
拡散性が高ければ他の金属でもよい。かかるアルミニウ
ム板４は、既に施工された厨房１の断熱性のあるコンロ
２の前壁および側壁に装着するものである。前記フッ素
樹脂フィルム５には、例えばエチレンテトラフルオロエ
チレン共重合体（ＥＴＦＥ）、テトラフルオロエチレン
パーフルオロアルキルビニルエーテル共重合体（ＰＦ
Ａ）等の四フッ化フッ素樹脂を適用することができる。
また、前記フッ素樹脂フィルム５は、厚さが５〜２００
μで、透明のものか、透明で前記アルミニウム板４との
積層面に模様等を印刷したものか、フィルム自体が着色
されたもの等、いずれでもよい。さらに、マーク、文
字、さらには、標語を印刷してもよい。また、前記アル
ミニウム板４側に、模様、文字等の印刷を施すこともで
きる。さらに、アルミニウム板４のフッ素樹脂フィルム
５との積層面に、凹凸のある模様を付してもよい。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A fluororesin laminated heat insulating plate according to the present invention will be described below with reference to the accompanying drawings. A kitchen 1 is shown in FIG. 1, and a heat insulating plate 3 of a fluororesin laminate according to the present invention is attached to a front wall and a side wall of a stove 2 in the kitchen 1. As shown in FIG. 2, the heat insulating plate 3 has a structure in which a metal plate having a high heat transfer property, for example, an aluminum plate 4 is laminated with a fluororesin film 5 having excellent non-adhesiveness and heat resistance. The aluminum plate 4 has a thickness of 0.1 to 2.0 mm (preferably 0.
3 to 1.0 mm), and another metal may be used as long as it has high heat conductivity, that is, high heat diffusivity. The aluminum plate 4 is attached to the front wall and the side wall of the stove 2 having heat insulation of the kitchen 1 which has already been constructed. The fluororesin film 5 includes, for example, ethylene tetrafluoroethylene copolymer (ETFE), tetrafluoroethylene perfluoroalkyl vinyl ether copolymer (PF
A tetrafluorinated fluororesin such as A) can be applied.
The fluororesin film 5 has a thickness of 5 to 200.
It may be either a transparent one, a transparent one having a pattern printed on the surface laminated with the aluminum plate 4, a colored film itself, or the like. In addition, marks, characters, and slogans may be printed. Further, it is also possible to print patterns, characters, etc. on the aluminum plate 4 side. Further, the laminated surface of the aluminum plate 4 on which the fluororesin film 5 is laminated may be provided with an uneven pattern.
【０００７】このような構成の防熱板３において、アル
ミニウム板４とフッ素樹脂フィルム５とは、熱溶着によ
り貼り合わせている。また、接着剤により貼り合わせる
ようにしてもよい。In the heat insulating plate 3 having such a structure, the aluminum plate 4 and the fluororesin film 5 are bonded together by heat welding. Alternatively, they may be attached by an adhesive.
【０００８】本発明にかかる防熱板は、以下のような構
成によっても実現することができる。すなわち、図３に
示す防熱板１０では、前述のアルミニウム板４にフッ素
樹脂フィルム５を積層したものに断熱材１１を積層した
構成としている。この場合、断熱材１１には、例えば石
膏ボード、ロックウール、グラスウール、発泡プラスチ
ック系のもの、木質繊維系のもの、周知の不燃材によっ
て構成したハニカム構造基材を適用することができる。The heat insulating plate according to the present invention can also be realized by the following structure. That is, in the heat insulating plate 10 shown in FIG. 3, the heat insulating material 11 is laminated on the aluminum plate 4 on which the fluororesin film 5 is laminated. In this case, as the heat insulating material 11, for example, gypsum board, rock wool, glass wool, foamed plastic material, wood fiber material, or a honeycomb structure base material made of a known non-combustible material can be applied.
【０００９】ここで、図４に断熱材として不燃材によっ
て構成したハニカム構造基材を適用した、防熱板２０を
示し、詳細に説明する。すなわち、この防熱板２０は、
ハニカム構造基材２１に、フッ素樹脂フィルム５によっ
て被覆したアルミニウム板４を積層する構成としてい
る。前記ハニカム構造基材２１は、厚さ５ｍｍ〜１００
ｍｍ（望ましくは８ｍｍ〜１５ｍｍ）のもので、材質と
しては、紙に難燃処理を施した難燃紙、ガラス繊維を混
入した不燃紙、無機物の粉末を充填した不燃紙他、周知
の不燃材が適用可能である。前記フッ素樹脂フィルム５
には、四フッ化フッ素樹脂（例えば、ＰＦＡ、ＥＴＦ
Ｅ）が好ましい。また、フッ素樹脂フィルム５は透明の
ものか、透明で前記アルミニウム板４との積層面に模様
等を印刷したものか、フィルム自体が着色されたもの
等、いずれでもよい。さらに、マーク、文字、さらに
は、標語を印刷してもよい。また、前記アルミニウム板
４側に、模様、文字等の印刷を施すこともできる。さら
に、アルミニウム板４のフッ素樹脂フィルム５との積層
面に、凹凸のある模様を付してもよい。前記アルミニウ
ム板４は、厚さ０．１ｍｍ〜２．０ｍｍ（望ましくは
０．３〜１．０ｍｍ）のものを使用している。なお、ア
ルミニウム板４は、伝熱性の高い、すなわち熱拡散性が
高ければ他の金属でもよい。Here, FIG. 4 shows a heat insulating plate 20 to which a honeycomb structure base material made of an incombustible material is applied as a heat insulating material, which will be described in detail. That is, the heat insulating plate 20 is
The aluminum plate 4 coated with the fluororesin film 5 is laminated on the honeycomb structure base material 21. The honeycomb structure base material 21 has a thickness of 5 mm to 100.
mm (preferably 8 mm to 15 mm), and the material is flame-retardant paper obtained by subjecting the paper to flame-retardant treatment, non-combustible paper mixed with glass fiber, non-combustible paper filled with inorganic powder, and other known non-combustible materials. Is applicable. The fluororesin film 5
Fluorine tetrafluoride resin (eg PFA, ETF
E) is preferred. The fluororesin film 5 may be transparent, transparent and has a pattern printed on the surface laminated with the aluminum plate 4, or the film itself is colored. In addition, marks, characters, and slogans may be printed. Further, it is also possible to print patterns, characters, etc. on the aluminum plate 4 side. Further, the laminated surface of the aluminum plate 4 on which the fluororesin film 5 is laminated may be provided with an uneven pattern. The aluminum plate 4 has a thickness of 0.1 mm to 2.0 mm (desirably 0.3 to 1.0 mm). The aluminum plate 4 may be made of another metal as long as it has a high heat transfer property, that is, a high heat diffusion property.
【００１０】以上、本発明にかかる防熱板３、１０、２
０によれば、非粘着性、耐熱性に富むフッ素樹脂フィル
ム５により清掃性に優れ、アルミニウム板４に断熱材１
１、すなわち、ハニカム構造基材２１を積層したものに
あっては防熱性に優れ、さらには鋸、カッター等の工具
により切断加工が容易であり、現場施工性に優れたもの
となる。さらに、フッ素樹脂フィルム５に着色を施した
り、アルミニウム板４またはフッ素樹脂フィルム５側の
積層面に模様等を施したものにあっては、意匠性の向上
をもたらすことができる。さらに、アルミニウム板４ま
たはフッ素樹脂フィルム５側の積層面に文字、標語等を
印刷するようにすれば、様々な実用的な有用性がもたら
される。As described above, the heat insulating plates 3, 10, 2 according to the present invention
According to No. 0, the fluororesin film 5 which is non-adhesive and has excellent heat resistance has excellent cleanability, and the aluminum plate 4 has a heat insulating material 1
1, that is, the honeycomb structure base material 21 having a laminated structure has excellent heat resistance, and can be easily cut by a tool such as a saw or a cutter, resulting in excellent on-site workability. Further, in the case where the fluororesin film 5 is colored or the laminated surface on the side of the aluminum plate 4 or the fluororesin film 5 is provided with a pattern or the like, the designability can be improved. Further, by printing characters, slogans, etc. on the laminated surface on the side of the aluminum plate 4 or the fluororesin film 5, various practical usefulness is brought about.
【００１１】次に、以上列挙した防熱板３、１０、２０
のうち、ハニカム構造基材２１に、フッ素樹脂フィルム
５によって被覆したアルミニウム板４を積層する構成と
した防熱板２０について、その防火性、不燃性を参考ま
でに示す。 １）試験材…………両面アルミニウム板張ガラス繊維・
けい酸マグネシウム混抄紙ハニカムコア板 形状……………平板 重量……………９．１３ｋｇ／ｍ2 厚さ……………６２．５ｍｍ 材料構成 ・表面材…アルミニウム板、厚さ１．５ｍｍ。 ・芯材……ガラス繊維・けい酸マグネシウム混抄紙ハニカムコ ア、厚さ６０ｍｍ（セルサイズ２０ｍｍ、密度３４．２ｋｇ／ｍ3） ・裏面材…表面材と同じ ・接着剤…エポキシ樹脂系 ２）試験方法 表面試験 表面を１０分間加熱する。 結果……防火上有害な変形→なし 全厚にわたる溶融→なし 亀裂の幅・長さ→ なし 裏面空間温度→ ６１℃以下 基材試験 基材（厚さ５０ｍｍ）を２０分間加熱し、表面温度を サーミスタにより測定 結果……表面温度＜８００℃ なお、前記試験材の両面アルミニウム板張ガラス繊維・
けい酸マグネシウム混抄紙ハニカムコア板の他に、水酸
化アルミニウム、けい酸マグネシウム等の無機材を主成
分とするハニカムコア板も可能である。この場合、厚さ
は９ｍｍ、もしくは１２ｍｍが好ましい。Next, the heat insulating plates 3, 10, 20 listed above are used.
Among them, the heatproof plate 20 having a structure in which the aluminum plate 4 coated with the fluororesin film 5 is laminated on the honeycomb structure base material 21 will be described for reference with respect to its fireproof property and nonflammability. 1) Test material ………… Double-sided aluminum-clad glass fiber
Magnesium silicate mixed paper Honeycomb core plate shape ……………… flat plate weight ………… 9.13 kg / m 2 Thickness: 62.5 mm Material composition: Surface material: Aluminum plate, thickness: 1.5 mm.・ Core material …… Glass fiber / magnesium silicate mixed paper honeycomb core, thickness 60 mm (cell size 20 mm, density 34.2 kg / m 3 ) ・ Back surface material ・ ・ ・ Same as surface material ・ Adhesive ・ ・ ・ Epoxy resin type 2) test Method Surface test Heat the surface for 10 minutes. Results: Harmful deformation for fire protection → None Melting over the entire thickness → None Crack width / length → None Backside space temperature → 61 ° C or less Substrate test Heat the substrate (thickness 50 mm) for 20 minutes to determine the surface temperature. Measurement result by thermistor: Surface temperature <800 ℃.
In addition to the magnesium silicate mixed paper-making honeycomb core plate, a honeycomb core plate containing an inorganic material such as aluminum hydroxide or magnesium silicate as a main component is also possible. In this case, the thickness is preferably 9 mm or 12 mm.
【００１２】さらに、防熱板３、１０について、従前の
タイル壁との比較から、有用性を検証してみる。比較例１ １．防熱板………厚さ９ｍｍの石膏ボード（縦横９２０
ｍｍ、横幅１２００ｍｍ）にアルミニウム板４を接着
し、アルミニウム板４に厚さ２０μのフッ素樹脂フィル
ム５を耐熱接着剤で貼り合わせた。 ２．従前のタイル壁……縦５２０ｍｍ、横幅１０００ｍ
ｍ ・切断加工……１．防熱板を２．従前のタイル壁と同一
のサイズに切断し、試作施工を行った。Further, the usefulness of the heat insulating plates 3 and 10 will be verified by comparison with the conventional tile wall. Comparative Example 1 1. Heat-insulating plate: A plaster board with a thickness of 9 mm (vertical and horizontal 920)
mm, width 1200 mm), the aluminum plate 4 was adhered, and the fluororesin film 5 having a thickness of 20 μ was bonded to the aluminum plate 4 with a heat-resistant adhesive. 2. Previous tile wall: 520 mm long and 1000 m wide
m ・ Cutting process …… １. Heat shield 2. It was cut into the same size as the conventional tile wall and prototyped.
【００１３】結果 鋸、カッター等で容易に切断加工でき、下地壁を特に予
備施工を行うことなく、平滑な新規壁とすることができ
た。これに対し、２．従前のタイル壁では、「１０ｃｍ
角のタイルと固定剤を兼ねた白色目地剤」を使用した。
壁面の平滑性を確保するため、タイル施工に先立ち、下
地壁の平滑化のため、下地処理用セメント施工を行っ
た。この結果、下地の乾燥等、養生に放置時間も必要と
したため、１．防熱板に比較して多大な労力を費やした
ことがわかる。 As a result , it was possible to easily carry out cutting work with a saw, a cutter, etc., and it was possible to make a smooth new wall without performing preparatory work on the base wall. On the other hand, 2. In the conventional tile wall, "10 cm
A white joint agent that doubles as a corner tile and a fixing agent was used.
In order to ensure the smoothness of the wall surface, cement was applied for ground treatment before the tile construction to smooth the ground wall. As a result, it took a long time for curing, such as drying the base, so that 1. It can be seen that a great deal of effort was spent in comparison with the heat insulating plate.
【００１４】比較例２ 比較例１で試作した、１．防熱板、２．従前のタイル壁
の汚れ落ち比較のため、充分な量の水性赤インク含有の
水をスプレーで吹きかけ作業を行った。COMPARATIVE EXAMPLE 2 Prototype in Comparative Example 1 Heat shield, 2. For comparison of conventional stain removal on tile walls, a sufficient amount of water containing water-based red ink was sprayed to perform work.
【００１５】結果 処理面が熱源で乾燥後、乾布で拭き取り作業を行ったと
ころ、表面に非粘着性、耐熱性に富むフッ素樹脂フィル
ム５を積層した１．防熱板は、何ら汚れが残ることはな
かった。これに対し、２．従前のタイル壁では、目地部
分に赤インクが染み込み、除去することはできなかっ
た。 As a result, the treated surface was dried with a heat source and then wiped off with a dry cloth. As a result, a fluororesin film 5 having excellent non-adhesiveness and heat resistance was laminated on the surface. No stain remained on the heat shield. On the other hand, 2. In the conventional tile wall, the red ink permeated the joints and could not be removed.
【００１６】以上、本発明にかかるフッ素樹脂積層の防
熱板について、厨房におけるコンロ前壁に適用した実施
例を挙げ説明したが、ハニカム構造基材２１に、フッ素
樹脂フィルム５によって被覆したアルミニウム板４を積
層する構成とした防熱板２０は、特に不燃材としての基
準を満たしているので、防火扉として適用することがで
きるなど、その用途は広い。The fluororesin laminated heat insulating plate according to the present invention has been described above with reference to the embodiment applied to the stove front wall in the kitchen. The honeycomb structure base material 21 is covered with the fluororesin film 5 to form the aluminum plate 4. Since the heat insulating plate 20 having a structure in which the above are laminated satisfies the standard as a non-combustible material, it can be applied as a fire door and has a wide range of uses.
【００１７】[0017]
【発明の効果】以上のとおり本発明にかかる防熱板によ
れば、フッ素樹脂により清掃性に優れ、金属板に断熱材
を積層したものにあっては防熱性に優れ、さらには鋸、
カッター等の工具により切断加工が容易であり、現場施
工性に優れたものとなる。なお、前記フッ素樹脂の金属
板との積層面や、金属板のフッ素樹脂との積層面に模様
を施したものにあっては、意匠性の向上がもたらされ、
さらに、金属板またはフッ素樹脂側の積層面に文字を付
すようにすると、様々な実用的な有用性がもたらされ
る。As described above, according to the heat insulating plate of the present invention, the cleaning property is excellent due to the fluororesin, the heat insulating property is excellent in the case where the heat insulating material is laminated on the metal plate, and the saw,
It is easy to cut with a tool such as a cutter, and it has excellent site workability. Incidentally, the laminated surface with the metal plate of the fluororesin, or in the one having a pattern on the laminated surface with the fluororesin of the metal plate, the improvement in design is brought about,
Furthermore, when a letter is attached to the metal plate or the laminated surface on the fluororesin side, various practical usefulness is brought about.
【００１８】[0018]
【図１】本発明にかかる防熱板を適用した、厨房の模式
的な斜視説明図である。FIG. 1 is a schematic perspective explanatory view of a kitchen to which a heat insulating plate according to the present invention is applied.
【図２】本発明にかかる防熱板の別の実施例を示す模式
的な断面説明図である。FIG. 2 is a schematic sectional explanatory view showing another embodiment of the heat insulating plate according to the present invention.
【図３】本発明にかかる防熱板の別の実施例を示す模式
的な断面説明図である。FIG. 3 is a schematic sectional explanatory view showing another embodiment of the heat insulating plate according to the present invention.
【図４】本発明にかかる防熱板の別の実施例を示す模式
的な斜視説明図である。FIG. 4 is a schematic perspective view showing another embodiment of the heat insulating plate according to the present invention.
１ 厨房 ２ コンロ ３、１０、２０ 防熱板 ４ アルミニウム板 ５ フッ素樹脂フィルム １１ 断熱材 ２１ ハニカム構造基材 1 Kitchen 2 Stove 3, 10, 20 Heat Insulation Plate 4 Aluminum Plate 5 Fluororesin Film 11 Heat Insulation Material 21 Honeycomb Structure Substrate
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 19/04 Ｂ３２Ｂ 19/04 33/00 33/00 Ｅ０４Ｂ 1/80 Ｅ０４Ｂ 1/80 Ｘ 1/94 1/94 Ｒ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location B32B 19/04 B32B 19/04 33/00 33/00 E04B 1/80 E04B 1/80 X 1 / 94 1/94 R
Claims (18)
層したことを特徴とするフッ素樹脂積層の防熱板。1. A heat-insulating plate of a fluororesin laminate, characterized in that a fluororesin is laminated on a metal plate having high heat conductivity.
層すると共に、この金属板を、断熱材の少なくとも片面
に積層したことを特徴とするフッ素樹脂積層の防熱板。2. A heat-insulating plate of a fluororesin laminate, characterized in that a fluororesin is laminated on a metal plate having high heat conductivity, and the metal plate is laminated on at least one surface of a heat insulating material.
ことを特徴とする請求項２記載のフッ素樹脂積層の防熱
板。3. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is made of a non-combustible material.
特徴とする請求項２記載のフッ素樹脂積層の防熱板。4. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is a gypsum board.
を特徴とする請求項２記載のフッ素樹脂積層の防熱板。5. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is rock wool.
を特徴とする請求項２記載のフッ素樹脂積層の防熱板。6. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is glass wool.
材であることを特徴とする請求項２記載のフッ素樹脂積
層の防熱板。7. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is a foamed plastic heat insulating material.
ことを特徴とする請求項２記載のフッ素樹脂積層の防熱
板。8. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is a wood fiber heat insulating material.
ものであることを特徴とする請求項２記載のフッ素樹脂
積層の防熱板。9. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material has a heat insulating space in the middle thereof.
ることを特徴とする請求項２または３記載のフッ素樹脂
積層の防熱板。10. The heat insulating plate of the fluororesin laminate according to claim 2, wherein the heat insulating material is a honeycomb structure base material.
たことを特徴とする請求項１ないし１０記載のフッ素樹
脂積層の防熱板。11. The heat insulating plate of the fluororesin laminate according to claim 1, wherein the fluororesin is heat-welded to a metal plate.
ことを特徴とする請求項１ないし１０記載のフッ素樹脂
積層の防熱板。12. The heat insulating plate of the fluororesin laminate according to claim 1, wherein the fluororesin is adhered to a metal plate.
に模様を施したことを特徴とする請求項１ないし１０、
１１または１２記載のフッ素樹脂積層の防熱板。13. A laminate surface of the fluororesin and a metal plate is patterned to provide a pattern.
11. A heat insulating plate laminated with a fluororesin according to 11 or 12.
に模様を施したことを特徴とする請求項１ないし１０、
１１または１２記載のフッ素樹脂積層の防熱板。14. The laminated surface of the metal plate on which the fluororesin is laminated is patterned.
11. A heat insulating plate laminated with a fluororesin according to 11 or 12.
に文字を付したことを特徴とする請求項１ないし１０、
１１または１２記載のフッ素樹脂積層の防熱板。15. A character is attached to a laminated surface of the fluororesin with a metal plate, wherein the characters are attached.
11. A heat insulating plate laminated with a fluororesin according to 11 or 12.
に文字を付したことを特徴とする請求項１ないし１０、
１１または１２記載のフッ素樹脂積層の防熱板。16. A character is attached to a surface of the metal plate laminated with the fluororesin, and the character is attached.
11. A heat insulating plate laminated with a fluororesin according to 11 or 12.
におけるコンロ周りの壁面に適用したことを特徴とする
請求項１ないし１６記載のフッ素樹脂積層の防熱板。17. The heat insulating plate of the fluororesin laminate according to claim 1, wherein the heat insulating plate of the fluororesin laminate is applied to a wall surface around a stove in a kitchen.
扉に適用したことを特徴とする請求項１ないし１６記載
のフッ素樹脂積層の防熱板。18. The heat insulating plate of the fluororesin laminate according to claim 1, wherein the heat insulating plate of the fluororesin laminate is applied to a fire door.