JPH08280290A - Material for treating feces of dog or cat and its production - Google Patents

Abstract

PURPOSE: To obtain a material for treating the feces of a dog or cat, strong in a deodorizing force, light in weight, large in absorption capacity, good in an occluding property, and large in an antimicrobial force. CONSTITUTION: 20-30wt.% of pumiceous tuff and 70-80wt.% of bentonite powder are homogeneously mixed, mixed with an antimicrobial, further mixed with water, granulated and finally dried to obtain the feces-treating material for the dog or cat.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a granular material for treating feces and urine of dogs and cats, which is used by being spread like sand in a dog and cat toilet.

[0002]

2. Description of the Related Art Granular materials for treating feces and urine of dogs and cats have been provided so far. That is, there are various types such as a bentonite simple substance, a zeolite simple substance, and a mixture of these and other materials, but the common thing to them is that the weight is large, it is inconvenient to carry and handle, and once It was also uneconomical because the amount of waste per day was large (the amount of consumption was large). The deodorizing ability is not good enough, and discomfort remains when it is housed indoors. Furthermore, since dogs and cats walk around regardless of where they are, they carry in bacteria, but no consideration is given to the treatment. In addition, a two-layer embodiment in which a surface layer of a solidification accelerator is formed on the surface of the inner layer of a granular core body obtained by blending, kneading and solidifying a zeolite containing clay particles.
129921) has been proposed, but it has not been put into practice because the production is troublesome, the cost is high.

[0003]

DISCLOSURE OF THE INVENTION The present invention has been made in view of such a conventional situation as described above, and it is mainly composed of fluffy tuff and bentonite powder, and an antibacterial agent is added to the powder to form a deodorizing agent. (EN) A material for treating feces and urine of dogs and cats, which is strong, lightweight, has a large absorption amount, has a good occlusion property, and has an antibacterial activity.

[0004]

In order to achieve the above object, the present invention uniformly mixes 20 to 40% by weight of fluffy tuff and 60 to 80% bentonite powder, and further mixes an antibacterial agent. To do. Then, a method for producing a dog-cat waste treatment material, which is characterized by being obtained by adding water to granulate (granular molding), and finally drying, and using the dog-cat waste treatment material obtained by the production method. is there. Although it is ideal to increase the proportion of fluffy tuff from the standpoint of reducing the weight and enhancing the deodorizing power, if it exceeds 40% by weight, it is not desirable because the solidifying performance is impaired.

[0005]

EXAMPLES Examples of the manufacturing method will be described below.
30% by weight of fluffy tuff produced in Fukushima Prefecture,
70% by weight of bentonite powder produced in Niigata Prefecture is mixed uniformly, and the essential oil "CENTRIS E-110" is added as an antibacterial agent.
Add "double solution". Then, while spraying water, the mixture is put into a flat-type granulator and molded and granulated. At this time, the number of revolutions of the granulator, the inclination angle, and the spraying ratio of water were adjusted to adjust the particle size distribution to 1.
5 mm to 2 mm is 20% by weight, 2 mm to 4 mm is 50% by weight, and 4 mm to 6 mm is 30% by weight. If there are less than 1.5 mm and more than 6 mm, these are removed. . Then, the granulated product containing the water was dried at 300 ° C. by a hot air dryer to obtain a treated material of the present invention having a particle diameter of 1.5 mm to 6 mm.

[0006] This treated material of the present invention, physiological saline (salt content 2
%) Was poured at 30%, and only the absorbed part became a nodular form, and only that part could be easily taken out. The bulk specific gravity was 0.72, which was light, and the weight of the hardened part could be reduced.

[0007]

As described above, the present invention is mainly composed of fluff tuff and bentonite powder, so that it is much lighter in weight and excellent in deodorizing power as compared with the conventional crushed bentonite / zeolite mixed treatment material. It is economical because it has a large amount of power, and the amount thrown away once is small. And granulation, particle size distribution 1.5mm-2mm is 20% by weight, 2mm-4mm
Is 50% by weight, and 4 mm to 6 mm is 30% by weight, fine particles of lightweight particles enter between the particles, and urine can be solidified quickly and in a small amount. Further, since an antibacterial agent is added, it is possible to maintain the property of preventing the proliferation of various bacteria, and in the embodiment using aromatic oil (essential oil) obtained from plants for this antibacterial agent, in the environment where the contaminant bacteria in the natural environment and It is possible to exert the ability to adsorb various gases, detoxify them, and clean them. From the above, the present invention is a promise to be a good news for dog and cat breeders, as it fulfills the intended purpose.

Claims (6)

[Claims] 1. A mixture of 20 to 40% by weight of fluff tuff and 60 to 80% of bentonite powder is uniformly mixed, an antibacterial agent is further added, water is added for granulation, and finally dried. A method for producing a dog-cat waste treatment material, comprising: 2. Granulation is such that a particle size distribution of 1.5 mm to 2 mm is 20% by weight, 2 mm to 4 mm is 50% by weight, and 4 mm to 6 mm.
The method for producing a fecal excrement-treating material for dogs and cats according to claim 1, wherein mm is 30% by weight. 3. The method for producing a dog-cat waste treatment material according to claim 1, wherein the antibacterial agent is an aromatic oil obtained from a plant. 4. A dog and cat obtained by uniformly mixing 20 to 30% by weight of fluffy tuff and 70 to 80% of bentonite powder, further adding an antibacterial agent, adding water and granulating and drying. Manure treatment material. 5. The granule size distribution of 1.5 mm to 2 mm is 20% by weight, 2 mm to 4 mm is 50% by weight, and 4 mm to 6
The dog man's excrement treatment material according to claim 4, wherein mm is 30% by weight. 6. The material for treating feces of dogs and cats according to claim 1, wherein the antibacterial agent is an aromatic oil obtained from plants.