JPH08207927A - Paper carton for liquid - Google Patents
Paper carton for liquidInfo
- Publication number
- JPH08207927A JPH08207927A JP7041367A JP4136795A JPH08207927A JP H08207927 A JPH08207927 A JP H08207927A JP 7041367 A JP7041367 A JP 7041367A JP 4136795 A JP4136795 A JP 4136795A JP H08207927 A JPH08207927 A JP H08207927A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- paper
- container
- hydroxyl group
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、内容物の電子レンジに
よる加熱が可能であり、高度なガスバリヤー性を有し、
焼却が容易（無公害）な液体用紙製容器に関する。TECHNICAL FIELD The present invention is capable of heating contents in a microwave oven and has a high gas barrier property.
The present invention relates to a liquid paper container that is easily incinerated (no pollution).
【０００２】[0002]
【従来の技術】近年、女性の社会への進出が増加すると
共にスーパーストア、コンビニエンスストア等における
食品類の購入の増加、包装形式の変化に伴い、液体用紙
製容器による飲食品の販売が急速に増加している。通常
の液体用紙製容器といわれるものは、紙、プラスチック
フィルムと共に厚さ７μｍ以上のアルミニウム箔を積層
したブランクシートから製造されているので、廃棄され
焼却するときは焼却炉の耐火材にアルミニウムが反応
し、焼却炉のライフを短縮することが知られており、ま
た埋立においてもプラスチックに保護されるため分解性
がなく、このような容器からアルミニウム箔を除いた構
成とした容器への強い要望がある。2. Description of the Related Art In recent years, along with the increase in women's entry into society and the increase in purchases of food products at superstores, convenience stores, etc. It has increased. What is called a normal liquid paper container is manufactured from a blank sheet in which aluminum foil with a thickness of 7 μm or more is laminated together with paper and a plastic film, so when it is discarded and incinerated, aluminum reacts with the refractory material of the incinerator. However, it is known to shorten the life of the incinerator, and because it is protected by plastic even in landfill, it is not degradable, and there is a strong demand for a container that does not have an aluminum foil. is there.
【０００３】一般的なアルミニウム箔入り紙製容器の構
成は図２に示す如きもので、容器の内側より外側に向っ
てポリエチレン層Ｃ、ポリエチレンテレフタレート（以
下ＰＥＴという）層Ｂ、アルミニウム箔層Ａ、紙層Ｄ、
ポリエチレン層Ｃの順に積層した構成であり、アルミニ
ウム箔層Ａを容器のブランクシート中に積層することに
より、酸素ガスバリヤー性、遮光性を保持させている。
このような構成からアルミニウム箔を除いて同等の酸素
ガスバリヤー性を維持させるため、例えばエチレン−酢
酸ビニル共重合体けん化物（ＥＶＯＨ）等のガスバリヤ
ー性樹脂を用いる提案がなされているが、バリヤー性樹
脂の酸素ガスバリヤー性が環境湿度に大きく影響され、
高湿度の場合にバリヤー性を大幅に低下するため、内容
物が水性の液体であるときは、常温保存を行う容器とし
ては不充分であり、冷凍保存あるいは冷蔵保存などの場
合に限定されている。The structure of a general paper container containing aluminum foil is as shown in FIG. 2, and includes a polyethylene layer C, a polyethylene terephthalate (hereinafter referred to as PET) layer B, an aluminum foil layer A, from the inside to the outside of the container. Paper layer D,
The polyethylene layer C is laminated in this order, and the aluminum foil layer A is laminated in the blank sheet of the container to maintain the oxygen gas barrier property and the light shielding property.
In order to maintain an equivalent oxygen gas barrier property by removing the aluminum foil from such a structure, it has been proposed to use a gas barrier resin such as saponified ethylene-vinyl acetate copolymer (EVOH). Oxygen gas barrier property of the resin is greatly affected by environmental humidity,
When the content is an aqueous liquid, it is insufficient as a container to store at room temperature because the barrier property is significantly reduced in the case of high humidity, and it is limited to cases such as frozen storage or refrigerated storage. .
【０００４】またブランクシート中に、少なくとも片面
にけい素酸化物の薄膜層を有するプラスチック層をアル
ミニウム箔に代えて用いたブランクシートより製函され
た液体用紙製容器の提案（実公平５−２８１９０）があ
る。この紙製容器は電子レンジでそのまま内容物の加熱
ができると共に内容物を保護できる高度のバリヤー性を
有する旨述べているが、プラスチックフィルム（ＰＥ
Ｔ）に蒸着等により形成したけい素酸化物の薄膜層は、
伸びや屈曲に対して弱く、包装時の折り曲げや衝撃、包
装された品物の取扱い等におけるショック等によっても
容易に破損し、安定したバリヤー性を保持することはで
きず、酸素ガスのバリヤー性は不充分であり、常温保存
を要する内容物の容器としては好ましいものではない。Further, a proposal for a liquid paper container made from a blank sheet in which a plastic layer having a thin film layer of silicon oxide on at least one surface is used instead of an aluminum foil in the blank sheet (Jpn. Pat. Appln. KOKAI Publication No. 5-28190). ). It is stated that this paper container has a high barrier property that can heat the contents as it is in a microwave oven and protect the contents.
The thin film layer of silicon oxide formed by vapor deposition or the like on T) is
It is weak against stretching and bending, easily damaged by bending and impact during packaging, shock during handling of packaged items, etc., and it is not possible to maintain a stable barrier property. It is not sufficient and is not preferable as a container for contents requiring storage at room temperature.
【０００５】例えば、紙層との貼り合わせにポリエチレ
ン等の接着層を設ける際の熱ショックによって、或いは
その積層体ブランクシートより液体用紙製容器を製函す
る際に外部応力や罫線を入れることによって脆い該薄膜
に容易にクラックやピンホールが発生し、上記提案のよ
うなバリヤー性は維持できず、アルミニウム箔を使用し
た常温保存紙容器のごとく高度且つ安定したバリヤー性
を必要とする包装材料としては実用性がない。For example, by heat shock when an adhesive layer such as polyethylene is provided for bonding with a paper layer, or by applying external stress or ruled lines when a liquid paper container is boxed from the laminate blank sheet. Cracks and pinholes easily occur in the brittle thin film, the barrier property as proposed above cannot be maintained, and as a packaging material that requires a high and stable barrier property such as a room temperature storage paper container using aluminum foil. Is not practical.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、アルミニウ
ム箔を使用しない液体用紙製容器であって、アルミニウ
ム箔を使用した常温保存目的の液体用紙製容器と同様に
高度の酸素ガスバリヤー性を有し、また取扱いによりバ
リヤー性を失わず、焼却炉で焼却できる液体用紙製容器
の提供を目的とする。DISCLOSURE OF THE INVENTION The present invention relates to a liquid paper container which does not use an aluminum foil and has a high oxygen gas barrier property similar to a liquid paper container which uses aluminum foil and is intended to be stored at room temperature. It is also an object of the present invention to provide a liquid paper container that can be incinerated in an incinerator without losing the barrier property due to handling.
【０００７】[0007]
【課題を解決するための手段】本発明は、内層から外層
に向って順にプラスチック層（Ｉ）／プラスチック層
（II）／けい素酸化物の蒸着薄膜層／水酸基含有熱可塑
性樹脂層／紙層／接着層／厚紙層の積層体を主体とする
積層構成のブランクシートより製函してなることを特徴
とする液体用紙製容器を開発することにより上記の目的
を達成した。The present invention provides a plastic layer (I) / a plastic layer (II) / a vapor-deposited thin film of silicon oxide / a thermoplastic resin layer containing a hydroxyl group / a paper layer in order from the inner layer to the outer layer. The above object has been achieved by developing a liquid paper container which is characterized in that a blank sheet having a laminated structure mainly composed of a laminated body of / adhesive layer / cardboard layer is formed.
【０００８】本発明において、プラスチック層（Ｉ）
は、押出しコーティング可能な低密度ポリエチレン樹
脂、高密度ポリエチレン樹脂、ポリプロピレン樹脂、エ
チレン−酢酸ビニル共重合体などのヒートシールが可能
な熱可塑性樹脂層で、厚さは約１０〜６０μｍ位に形成
される。プラスチック層（II）は、ＰＥＴ、ＯＮ、ＯＰ
Ｐの如き強度のあるフィルムからなる層であり、このプ
ラスチックフィルムにけい素酸化物を蒸着させて用い
る。けい素酸化物は、通常一般式ＳｉＯx （但しｘ＝
１．４〜１．９位のものが多い。）と表されるもので、
蒸着膜の厚さとしては約２００〜２０００Å位のもの
で、普通、プラスチック（II）層に蒸着する。In the present invention, the plastic layer (I)
Is a thermoplastic resin layer that can be heat-sealed such as extrusion-coatable low-density polyethylene resin, high-density polyethylene resin, polypropylene resin, and ethylene-vinyl acetate copolymer, and has a thickness of about 10 to 60 μm. It Plastic layer (II) is PET, ON, OP
It is a layer made of a film having strength such as P, and is used by depositing silicon oxide on this plastic film. Silicon oxide is usually represented by the general formula SiO x (where x =
Most of them are in the 1.4 to 1.9th place. ),
The vapor-deposited film has a thickness of about 200 to 2000 liters and is usually vapor-deposited on a plastic (II) layer.
【０００９】水酸基含有熱可塑性樹脂としては、酸素バ
リヤー性があるＥＶＯＨ、ポリビニルアルコール（ＰＶ
Ａ）等、分子中に水酸基を多数有する熱可塑性樹脂の少
なくとも一種或いはそれに未けん化のエチレン−酢酸ビ
ニル共重合体（未けん化のＥＶＡ）を配合した樹脂組成
物を用いる。未けん化のＥＶＡの配合量は、樹脂組成物
中多くとも９９重量％、好ましくは１０〜９０重量％で
あることが望ましい。未けん化のＥＶＡを配合すること
によって、水酸基含有熱可塑性樹脂層の柔軟性を更に向
上させることができる。ＥＶＯＨなどはそれ自体酸素バ
リヤー性があるとされているが、このような樹脂層のみ
では高度の酸素ガスバリヤー性は得ることができないた
め組合せて使用することが必要とされる。As the hydroxyl group-containing thermoplastic resin, EVOH having an oxygen barrier property, polyvinyl alcohol (PV
A resin composition containing at least one thermoplastic resin having a large number of hydroxyl groups in the molecule such as A) or an unsaponifiable ethylene-vinyl acetate copolymer (unsaponified EVA) is used. The amount of unsaponified EVA to be blended in the resin composition is at most 99% by weight, preferably 10 to 90% by weight. By blending unsaponifiable EVA, the flexibility of the hydroxyl group-containing thermoplastic resin layer can be further improved. EVOH and the like are said to have an oxygen barrier property by themselves, but a high oxygen gas barrier property cannot be obtained only with such a resin layer, and therefore it is necessary to use them in combination.
【００１０】ところが、該樹脂層中の水酸基とけい素酸
化物蒸着膜のＳｉＯx とは水和的な結合によりバリヤー
性において相乗効果が得られるのに加え、該樹脂の柔軟
性はけい素酸化物蒸着膜の脆さを解消し、ＳｉＯx 蒸着
膜を含んだ多層体の成形性、耐衝撃性を改良するもので
ある。このため、この樹脂を塗布することにより製函の
際、或いは包装品の輸送などの時における熱的応力、機
械的なショック等に対してけい素酸化物蒸着膜の破損を
防止し、酸素ガスに対する安定したバリヤー性を保持す
るためのものである。この機能を発揮するためには該樹
脂層は少なくとも１μｍの厚さを必要とし、コスト的な
面を考慮すると最大２０μｍ以下が好ましい厚さであ
る。However, the hydroxyl group in the resin layer and SiO x of the silicon oxide vapor-deposited film have a synergistic effect on the barrier property due to a hydrated bond, and the flexibility of the resin is silicon oxide. It is intended to eliminate the brittleness of the vapor deposition film and improve the formability and impact resistance of the multilayer body containing the SiO x vapor deposition film. Therefore, by coating this resin, the silicon oxide vapor deposition film is prevented from being damaged by thermal stress, mechanical shock, etc. during box making or transportation of packages, etc. It is for maintaining a stable barrier property against. In order to exert this function, the resin layer needs to have a thickness of at least 1 μm, and considering the cost, the maximum thickness is 20 μm or less.
【００１１】水酸基含有熱可塑性樹脂層に隣接する紙層
の紙質は、特に限定されるものでなく、通常の坪量約３
０〜８０ｇ／ｍ2 程度の上質紙でよい。これはＳｉＯx
蒸着層に塗布した水酸基含有熱可塑性樹脂に貼り合せた
後で巻取るために必要となるものであり、これを積層す
ることは作業を容易にするものである。この紙層に酒パ
ックや牛乳パック等で用いられている坪量２００〜６０
０ｇ／ｍ2 の厚紙を貼り合せる。接着層には紙用の糊の
ようなものであっても、あるいはポリエチレン、ホット
メルト等のヒートシーラントであってもよく、ある程度
の耐熱性、耐水性があれば一層好ましい。特に本発明の
容器は主として液体用として用いるのであり、冷蔵、氷
冷などにより容器表面の結露することもあるので、厚紙
としては表面にポリエチレンラミネーション、ポリオレ
フィンワックス或いはパラフィンワックス等のコーティ
ングされたものを用いるのが好ましい。以下、図面を参
照して本発明を説明する。図１は本発明の一実施例であ
り、その一部を切り欠いた説明のための斜視図である。The paper quality of the paper layer adjacent to the hydroxyl group-containing thermoplastic resin layer is not particularly limited, and the normal basis weight is about 3
Fine paper of about 0 to 80 g / m 2 may be used. This is SiO x
It is necessary in order to wind it after bonding it to the hydroxyl group-containing thermoplastic resin applied to the vapor deposition layer, and stacking this layer facilitates the work. This paper layer has a basis weight of 200-60 used in sake packs and milk packs.
Laminate 0 g / m 2 thick paper. The adhesive layer may be like glue for paper, or may be a heat sealant such as polyethylene or hot melt, and is more preferable as long as it has heat resistance and water resistance to some extent. In particular, since the container of the present invention is mainly used for liquids, dew condensation may occur on the container surface due to refrigeration, ice cooling, etc. Therefore, as the cardboard, a surface coated with polyethylene lamination, polyolefin wax or paraffin wax is used. It is preferably used. Hereinafter, the present invention will be described with reference to the drawings. FIG. 1 is an embodiment of the present invention, and is a perspective view for explaining a part of which is cut away.
【００１２】本発明においては、これらの原材料を容器
内層から外層に向って、プラスチック層（Ｉ）／プラス
チック層（II）／けい素酸化物の蒸着薄膜層／水酸基含
有熱可塑性樹脂層／紙層／接着層／厚紙層の順に積層し
たブランクシートを主体とし、これを製函した液体用紙
製容器である。容器としては特に制限がないが、ゲーブ
ルトップ或いはブリック型の液体容器でよい。また、特
に光等で変質する内容物を入れる場合は、ブランクシー
ト中に紫外線カットフィルム層を設けるか、紫外線カッ
トインキ層を適宜設ければよい。In the present invention, these raw materials are transferred from the inner layer to the outer layer of the container in the order of plastic layer (I) / plastic layer (II) / thin film of silicon oxide vapor-deposited layer / thermoplastic group containing hydroxyl group / paper layer. It is a container made of liquid paper, which is mainly made of a blank sheet laminated in the order of / adhesive layer / cardboard layer. The container is not particularly limited, but a gable top or brick type liquid container may be used. Further, particularly when a content which is deteriorated by light or the like is put therein, an ultraviolet cut film layer may be provided in the blank sheet, or an ultraviolet cut ink layer may be appropriately provided.
【００１３】ブランクシートの製造は限定されるわけで
はないが、例えば次の如き方法により製造するのが便利
である。即ち、先ずプラスチック層（II）のフィルムの
片面にけい素酸化物を真空蒸着法などによりけい素酸化
物の薄膜層２ａを形成する。次に、このフィルムのけい
素酸化物の薄膜層２ａ面に水酸基含有熱可塑性樹脂を塗
布し、湿潤状態にて紙を貼り合せることにより水酸基含
有熱可塑性樹脂層３及び紙層４を形成する。ついで紙層
面に接着剤を塗布して接着層５を設け、厚紙層６を貼合
する。最後に、このシートの内層面または両面に溶融押
し出しにより低密度ポリエチレンをコートすることによ
り、ポリエチレン層１またはポリエチレン層１およびポ
リエチレン層７を形成する。本発明においては、両面に
ポリエチレン層を設けることが好ましい。得られたブラ
ンクシートを常法により製函して液体用紙製容器とす
る。容器に注出口を設ける場合、その穴開き部にけい素
酸化物の薄膜層／水酸基含有熱可塑性樹脂層を設けたプ
ラスチックフィルムを主体とした積層体を用いれば、内
容物保護性をより向上させることが可能である。The production of the blank sheet is not limited, but it is convenient to produce it by the following method, for example. That is, first, a thin film layer 2a of silicon oxide is formed on one surface of the film of the plastic layer (II) by vacuum evaporation of silicon oxide. Next, a hydroxyl group-containing thermoplastic resin is applied to the surface of the silicon oxide thin film layer 2a of this film, and paper is attached in a wet state to form the hydroxyl group-containing thermoplastic resin layer 3 and the paper layer 4. Next, an adhesive is applied to the paper layer surface to form the adhesive layer 5, and the cardboard layer 6 is attached. Finally, the polyethylene layer 1 or the polyethylene layer 1 and the polyethylene layer 7 are formed by coating the inner layer surface or both surfaces of this sheet with low density polyethylene by melt extrusion. In the present invention, it is preferable to provide polyethylene layers on both sides. The blank sheet thus obtained is boxed by a conventional method to prepare a liquid paper container. When a container is provided with a spout, if a laminate mainly composed of a plastic film having a silicon oxide thin film layer / hydroxyl group-containing thermoplastic resin layer provided in the perforated part is used, the content protection property is further improved. It is possible.
【００１４】[0014]
【作用】本発明に於いては、ブランクシート中にけい素
酸化物の薄膜層を設け、これに水酸基含有熱可塑性樹脂
を塗布した層を設けているので、アルミニウム箔を用い
た従来の液体用紙製容器と同等のバリヤー性を有し、更
にそのけい素酸化物薄膜に水酸基含有熱可塑性樹脂層を
設けることによって、それ自身の酸素ガスバリヤー性に
加えけい素酸化物の脆さを改善することにより、充分に
成形性が持たされた上、特別に接着性ポリエチレン等を
使わずに紙層との貼り合せにも可能となった。本発明に
よってゲーブルトップ型は勿論のこと、従来の真空蒸着
されたけい素酸化物では屈曲が激しくて製函不可能とさ
れていた巻取り材料から自動製函しながら液体を充填す
るブリック型の常温保存容器にも本ブランクシートを適
用することが可能となった。当然ながら、ブランクシー
ト中にアルミニウム箔等の電子レンジのマイクロ波を遮
蔽する物質を用いていないので、そのまま電子レンジで
直接加熱することもでき、焼却処理しても炉の材質を傷
めることもない。In the present invention, since the thin film layer of silicon oxide is provided in the blank sheet and the layer coated with the thermoplastic resin containing hydroxyl group is provided, the conventional liquid paper using aluminum foil is provided. To improve the brittleness of silicon oxide in addition to its own oxygen gas barrier property by providing a hydroxyl group-containing thermoplastic resin layer on the silicon oxide thin film, which has a barrier property equivalent to that of a container. As a result, it has sufficient moldability and can be attached to a paper layer without using adhesive polyethylene. According to the present invention, not only the gable-top type but also the brick type for filling a liquid while automatically making a box from a winding material, which has been impossible to make a box by the conventional vacuum-deposited silicon oxide, which is difficult to make a box. It became possible to apply this blank sheet to a room temperature storage container. As a matter of course, since the blank sheet does not use a substance such as aluminum foil that shields microwaves from microwave ovens, it can be heated directly in the microwave oven without damaging the furnace material even if incinerated. .
【００１５】[0015]
［実施例１］前記の方法で製造した低密度ポリエチレン
層１／厚さ１２μｍのＰＥＴフィルム層２／けい素酸化
物蒸着層２ａ／水酸基含有熱可塑性樹脂（ＥＶＯＨ、ソ
アノール３０Ｌ、日本合成化学（株）製、３０重量％固
形分の水／イソプロピルアルコール系溶媒として使用）
層３／坪量５０ｇ／ｍ2 の紙層４／接着層５／坪量２６
０ｇ／ｍ2 の厚紙層６／低密度ポリエチレン層７からな
るブランクシートを幅２ｍｍ、高さ１ｍｍの形状の刃を
有する凹凸型刃を用い、圧力５０ｋｇ／ｃｍ2で圧を加
え、内容積１５００ｍｌの液体用紙製容器を作製した。[Example 1] Low-density polyethylene layer produced by the above method 1 / PET film layer 2 having a thickness of 12 μm 2 / Si oxide layer 2a / Hydroxyl group-containing thermoplastic resin (EVOH, Soarnol 30L, Nippon Synthetic Chemical Co., Ltd. ), Used as water / isopropyl alcohol-based solvent with 30 wt% solids)
Layer 3 / paper layer with basis weight 50 g / m 2 4 / adhesive layer 5 / basis weight 26
A blank sheet composed of 0 g / m 2 thick paper layer 6 / low-density polyethylene layer 7 was applied at a pressure of 50 kg / cm 2 using an uneven blade having a blade having a width of 2 mm and a height of 1 mm, and an internal volume of 1500 ml. A liquid paper container was manufactured.
【００１６】［実施例２］実施例１において、ＥＶＯＨ
（ソアノール３０Ｌ）の代りにゴーセノールＧＬ０３
（ＰＶＡ、日本合成化学（株）製）を水にてポリマー濃
度が２０重量％となるように調整したものを用いた以外
は、実施例１と同様に行って液体用紙容器を作製した。[Second Embodiment] In the first embodiment, the EVOH
Gohsenol GL03 instead of (Soarnol 30L)
A liquid paper container was prepared in the same manner as in Example 1 except that (PVA, manufactured by Nippon Synthetic Chemical Industry Co., Ltd.) prepared by adjusting the polymer concentration to 20% by weight with water was used.
【００１７】［実施例３］実施例１において、ＥＶＯＨ
（ソアノール３０Ｌ）の代りにゴーセノールＧＬ０３
（ＰＶＡ、日本合成化学（株）製）とポリゾールＡＤ−
６（未けん化のＥＶＡ、昭和高分子（株）製）とをＰＶ
Ａ／未けん化のＥＶＡ＝２／８（重量比）で配合した組
成物を水にて固形分濃度が２５重量％になるように調整
したものを用いた以外は、実施例１と同様に行って液体
用紙容器を作製した。[Third Embodiment] In the first embodiment, the EVOH
Gohsenol GL03 instead of (Soarnol 30L)
(PVA, manufactured by Nippon Synthetic Chemical Industry Co., Ltd.) and Polysol AD-
6 (unsaponified EVA, Showa Highpolymer Co., Ltd.) and PV
A / Unsaponified EVA = 2/8 (weight ratio) The composition was blended in the same manner as in Example 1 except that the solid content concentration was adjusted to 25 wt% with water. To prepare a liquid paper container.
【００１８】［実施例４］実施例１において、ＥＶＯＨ
（ソアノール３０Ｌ）の代りにソアノール３０Ｌ（ＥＶ
ＯＨ、日本合成化学（株）製）とポリゾールＡＤ−６
（未けん化のＥＶＡ、昭和高分子（株）製）とをＥＶＯ
Ｈ／未けん化のＥＶＡ＝５／５（重量比）で配合した組
成物を水とイソプロピルアルコールで固形分濃度が３０
重量％になるように調整したものを用いた以外は、実施
例１と同様に行って液体用紙容器を作製した。[Embodiment 4] In the first embodiment, EVOH
Soarnol 30L (EV
OH, manufactured by Nippon Synthetic Chemical Industry Co., Ltd. and Polysol AD-6
(Unsaponified EVA, Showa Highpolymer Co., Ltd.) and EVO
The composition of H / unsaponified EVA = 5/5 (weight ratio) was added to water and isopropyl alcohol to give a solid content of 30.
A liquid paper container was produced in the same manner as in Example 1 except that the one adjusted to have a weight% was used.
【００１９】容器のガスバリヤー性測定およびその焼却
テストを実施し、その結果を下記表に示す。 ガスバリヤー性：容器１）本発明の容器（約１２０ｇ） ２）従来の容器（アルミニウム箔入り） ３）水酸基含有熱可塑性樹脂層なしの容器（アルミニウ
ム箔を入れず、けい素酸化物蒸着層を設け水酸基含有樹
脂層は設けていない。） 内容物：窒素充填（酸素濃度ほぼゼロ） 密封後室温放置：３日間 The gas barrier property of the container was measured and its incineration test was conducted, and the results are shown in the following table. Gas barrier property: Container 1) Container of the present invention (about 120 g) 2) Conventional container (with aluminum foil) 3) Container without hydroxyl group-containing thermoplastic resin layer (without aluminum foil, and with a silicon oxide vapor deposition layer) No hydroxyl group-containing resin layer is provided.) Contents: Nitrogen filling (oxygen concentration almost zero) Leave at room temperature after sealing: 3 days
【００２０】焼却テスト：容器、同上（約１２０ｇ×１
０個） 内容物、空 焼却炉にて焼却 Incineration test: Container, same as above (about 120 g x 1
(0 pieces) Contents, incinerated in an empty incinerator
【００２１】[0021]
【発明の効果】本発明は、アルミニウム箔に代えけい素
酸化物蒸着層と水酸基含有熱可塑性樹脂層を用いるた
め、耐熱的応力、耐機械的応力が充分あるため、常温保
存紙容器の製造に関してはアルミニウム箔同様の工程で
ゲーブルトップ型やブリック型液体用紙製容器の製造が
可能となり、かつ容器の後処理（焼却等）が容易な上、
アルミニウム箔を用いた従来の液体用紙製容器と同等の
バリヤー性を有し、また当然ながらパックのまま電子レ
ンジ加熱ができることも含め、食品のパッケージとして
その適用範囲は極めて広く、経済的効果も極めて高い液
体用紙製容器である。INDUSTRIAL APPLICABILITY Since the present invention uses a silicon oxide vapor-deposited layer and a hydroxyl group-containing thermoplastic resin layer in place of an aluminum foil, it has sufficient heat resistance and mechanical stress. Is a gable-top type or brick type liquid paper container that can be manufactured in the same process as aluminum foil, and after-treatment (incineration, etc.) of the container is easy.
It has the same barrier properties as conventional liquid paper containers using aluminum foil, and of course it can be heated in a microwave oven as a pack. It is a high liquid paper container.
【図１】本発明の一実施例の一部を切り欠いた説明斜視
図である。FIG. 1 is an explanatory perspective view in which a part of an embodiment of the present invention is cut away.
【図２】従来の液体用紙製容器の一部を切り欠いた説明
斜視図である。FIG. 2 is an explanatory perspective view in which a part of a conventional liquid paper container is cut away.
１ ポリエチレン層 ２ ポリエチレンテレフタレート（ＰＥＴ）層 ２ａ けい素酸化物の薄膜層 ３ 水酸基含有熱可塑性樹脂層 ４ 紙層 ５ 接着層 ６ 厚紙層 ７ ポリエチレン層 Ａ アルミニウム箔層 Ｂ ポリエチレンテレフタレート（ＰＥＴ）層 Ｃ ポリエチレン層 Ｄ 紙層 DESCRIPTION OF SYMBOLS 1 Polyethylene layer 2 Polyethylene terephthalate (PET) layer 2a Silicon oxide thin film layer 3 Hydroxyl group containing thermoplastic resin layer 4 Paper layer 5 Adhesive layer 6 Thick paper layer 7 Polyethylene layer A Aluminum foil layer B Polyethylene terephthalate (PET) layer C Polyethylene Layer D Paper layer
Claims (3)
層（Ｉ）／プラスチック層（II）／けい素酸化物の蒸着
薄膜層／水酸基含有熱可塑性樹脂層／紙層／接着層／厚
紙層の積層体を主体とする積層構成のブランクシートよ
り製函してなることを特徴とする液体用紙製容器。1. A laminate of a plastic layer (I) / a plastic layer (II) / a vapor-deposited thin film of silicon oxide / a thermoplastic resin layer containing a hydroxyl group / a paper layer / an adhesive layer / a cardboard layer in order from the inner layer to the outer layer. A container made of liquid paper, characterized in that it is made from a laminated blank sheet having a body as a main body.
チレンテレフタレートフィルム（ＰＥＴ）、二軸延伸ポ
リアミドフィルム（ＯＮ）または二軸延伸ポリプロピレ
ンフィルム（ＯＰＰ）である請求項１記載の液体用紙製
容器。2. The liquid paper container according to claim 1, wherein the plastic layer (II) is a biaxially oriented polyethylene terephthalate film (PET), a biaxially oriented polyamide film (ON) or a biaxially oriented polypropylene film (OPP).
−酢酸ビニル共重合体けん化物および／またはポリビニ
ルアルコール或いはそれらに未けん化のエチレン−酢酸
ビニル共重合体を配合した樹脂組成物である請求項１ま
たは２記載の液体用紙製容器。3. The thermoplastic resin layer containing a hydroxyl group is a resin composition in which a saponified ethylene-vinyl acetate copolymer and / or polyvinyl alcohol or an unsaponified ethylene-vinyl acetate copolymer is blended therein. The liquid paper container according to 1 or 2.