JPH0812482B2 - Toner for electrostatic image - Google Patents
Toner for electrostatic imageInfo
- Publication number
- JPH0812482B2 JPH0812482B2 JP2205098A JP20509890A JPH0812482B2 JP H0812482 B2 JPH0812482 B2 JP H0812482B2 JP 2205098 A JP2205098 A JP 2205098A JP 20509890 A JP20509890 A JP 20509890A JP H0812482 B2 JPH0812482 B2 JP H0812482B2
- Authority
- JP
- Japan
- Prior art keywords
- toner
- weight
- copolymer
- styrene
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 この発明は静電荷像用トナーに関し、特に熱ロール定
着による複写機での定着性の向上、自動両面コピー装
置、自動原稿送り装置付きの複写機でのコピーの汚れ防
止に関するものである。Description: TECHNICAL FIELD The present invention relates to an electrostatic charge image toner, and more particularly to improvement of fixing property in a copying machine by heat roll fixing, copying with an automatic double-sided copying device, and an automatic document feeding device. It relates to the prevention of dirt on the copy on the machine.
〔従来の技術〕 従来熱定着方式を採用している複写機においては、あ
る一定以上のトナーの定着強度を確保する必要がある。[Prior Art] In a copying machine which has conventionally adopted a heat fixing method, it is necessary to secure a fixing strength of toner of a certain level or more.
両面コピーを行なう場合、特に自動両面コピー装置や
自動原稿送り装置のある複写機においてはトナーの定着
強度に起因する両面コピー時の汚れやコピー画像を原稿
として自動原稿送り装置を使用した場合の原稿の裏汚れ
は大きな問題である。When performing double-sided copying, especially in a copying machine equipped with an automatic double-sided copy device or an automatic document feeder, the original when the automatic original feeder is used as the original and the dirt or the copy image during double-sided copying due to the fixing strength of the toner The back stain is a big problem.
このような問題を解決するために従来はポリエチレン
系ワックスやカルナウバワックスの如き天然ワックス、
エチレン・酢酸ビニル共重合体等を含有せしめたトナー
が知られている。In order to solve such problems, conventionally, natural waxes such as polyethylene wax and carnauba wax,
A toner containing an ethylene / vinyl acetate copolymer or the like is known.
上記従来の技術によるポリエチレン系ワックスや天然
ワックスを添加したトナーにおいては、これらのワック
スが結着樹脂への分散の不良やワックスの脱離などによ
って感光体やキャリヤの表面に不要な付着を起してフィ
ルム状となるいわゆるフィルミングの発生や、それに基
づくコピーの地カブリの増加等種々の悪影響を招いてい
た。In the above-mentioned conventional toners to which polyethylene wax or natural wax is added, these waxes cause unnecessary adhesion on the surface of the photoconductor or carrier due to poor dispersion in the binder resin or desorption of the wax. As a result, various adverse effects such as occurrence of so-called filming in a film form and increase of background fog of copy due to the filming are caused.
又、エチレン−酢酸ビニル共重合体を用いる場合は該
共重合体自身の接着性によるトナーの保存性の低下（粉
体が高温でブロッキングする）を招く場合が多く発生し
た。Further, when an ethylene-vinyl acetate copolymer is used, there are many cases in which the storage property of the toner is deteriorated (the powder blocks at high temperature) due to the adhesiveness of the copolymer itself.
本発明はこのような課題を解決することを目的とする
ものである。The present invention aims to solve such problems.
本発明の概要は、結着樹脂及び着色剤を主成分とする
トナー中に全体の１〜30重量％のエチレン・アクリル酸
エステル・無水マレイン酸三元共重合体樹脂を含有して
なり、該エチレン・アクリル酸エステル・無水マレイン
酸三元共重合体樹脂を構成する共重合体成分としてアク
リル酸エステル含量を１〜30重量％とした熱ロール定着
用の静電荷像用トナーである。The outline of the present invention is that a toner containing a binder resin and a colorant as a main component contains 1 to 30% by weight of the whole ethylene / acrylic ester / maleic anhydride terpolymer resin, It is a toner for fixing an electrostatic charge image for heat roll fixing, in which an acrylic acid ester content is 1 to 30% by weight as a copolymer component constituting an ethylene / acrylic acid ester / maleic anhydride terpolymer resin.
上記三元共重合体を結着樹脂及び着色剤を主成分とす
るトナーに１〜30重量％含有してなるトナーは定着強度
が良く両面コピー性に優れ自動原稿送り装置で汚れを発
生しないことが認められた。本発明においては、エチレ
ン・アクリル酸エステル・無水マレイン酸三元共重合体
樹脂中におけるアクリル酸エステル含量を１〜30重量％
として使用するものである。The toner containing 1 to 30% by weight of the above-mentioned terpolymer containing a binder resin and a colorant as a main component has a good fixing strength and is excellent in double-sided copyability and should not be stained by an automatic document feeder. Was recognized. In the present invention, the content of acrylic ester in the ethylene / acrylic ester / maleic anhydride terpolymer resin is 1 to 30% by weight.
Is used as.
アクリル酸エステル含量が30重量％を超えると定着画
像の硬さが低下してしまい定着強度の低下をきたす。When the acrylic acid ester content exceeds 30% by weight, the hardness of the fixed image is lowered and the fixing strength is lowered.
このようなエチレン・アクリル酸エステル・無水マレ
イン酸三元共重合体の配合量はトナー全体の１〜30重量
％であることが必要で、１重量％未満では添加による両
面コピー性の向上は得られず、自動画像原稿送り装置に
よる汚れ防止を達成できない。又、30重量％を超えると
トナーの保存安定性を悪くするので実用に供し得ない。The blending amount of the terpolymer of ethylene / acrylic acid ester / maleic anhydride is required to be 1 to 30% by weight of the whole toner. If it is less than 1% by weight, improvement of double-sided copying property can be obtained. Therefore, it is not possible to prevent stain prevention by the automatic image document feeder. On the other hand, if it exceeds 30% by weight, the storage stability of the toner will be deteriorated and it cannot be put to practical use.
本発明で使用する三元共重合体を構成するアクリル酸
エステル成分としてはアクリル酸メチル、アクリル酸エ
チル、アクリル酸プロピル、アクリル酸ｎ−オクチル、
アクリル酸ドデシル、アクリル酸ヘキサデシル、アクリ
ル酸ｎ−ブチル、アクリル酸イソブチル、アクリル酸ラ
ウリル、アクリル酸２−エチルヘキシル、アクリル酸ス
テアリル、アクリル酸２−クロルエチル、アクリル酸フ
エニル等が存する。Examples of the acrylate component constituting the terpolymer used in the present invention include methyl acrylate, ethyl acrylate, propyl acrylate, n-octyl acrylate,
There are dodecyl acrylate, hexadecyl acrylate, n-butyl acrylate, isobutyl acrylate, lauryl acrylate, 2-ethylhexyl acrylate, stearyl acrylate, 2-chloroethyl acrylate, phenyl acrylate and the like.
本発明で用いる各成分について説明する。 Each component used in the present invention will be described.
（結着樹脂） 本発明においてエチレン・アクリル酸エステル・無水
マレイン酸三元共重合体と共に共用するトナーの結着樹
脂としては、例えばポリスチレン、ポリＰ−クロルスチ
レン、ポリビニルトルエンなどのスチレン及びその置換
体の単独重合体、スチレン−Ｐ−クロルスチレン共重合
体、スチレン−プロピレン共重合体、スチレン−ビニル
トルエン共重合体、スチレン−ビニルナフタレン共重合
体、スチレン−アクリル酸メチル共重合体、スチレン−
アクリル酸エチル共重合体、スチレン−アクリル酸ブチ
ル共重合体、スチレン−アクリル酸オクチル共重合体、
スチレン−メタクリル酸メチル共重合体、スチレン−メ
タクリル酸エチル共重合体、スチレン−メタクリル酸ブ
チル共重合体、スチレン−αクロルメタクリル酸メチル
共重合体、スチレン−アクリロニトリル共重合体、スチ
レン−ビニルメチルエーテル共重合体、スチレン−ビニ
ルエチルエーテル共重合体、スチレン−ビニルメチルケ
トン共重合体、スチレン−ブタジエン共重合体、スチレ
ン−イソプレン共重合体、スチレン−アクリロニトリル
−インデン共重合体、スチレン−マレイン酸共重合体、
スチレン−マレイン酸エステル共重合体などのスチレン
系共重合体、ポリメチルメタクリレート、ポリブチルメ
タクリレート、ポリ塩化ビニル、ポリ酢酸ビニル、ポリ
エチレン、ポリプロピレン、ポリエステル、ポリウレタ
ン、ポリアミド、エポキシ樹脂、ポリビニルブチラー
ル、ポリアマイド、ポリアクリル酸樹脂、ロジン、変性
ロジン、テルペン樹脂、フェノール樹脂、脂肪族又は脂
環族炭化水素樹脂、芳香族系石油樹脂、塩素化パラフィ
ン、パラフィンワックスなどが単独或いは混合して使用
できる。(Binder Resin) In the present invention, as the binder resin of the toner shared with the terpolymer of ethylene / acrylic acid ester / maleic anhydride, for example, polystyrene, poly (P-chlorostyrene), styrene such as polyvinyltoluene, or a substitution thereof is used. Homopolymer, styrene-P-chlorostyrene copolymer, styrene-propylene copolymer, styrene-vinyltoluene copolymer, styrene-vinylnaphthalene copolymer, styrene-methyl acrylate copolymer, styrene-
Ethyl acrylate copolymer, styrene-butyl acrylate copolymer, styrene-octyl acrylate copolymer,
Styrene-methylmethacrylate copolymer, styrene-ethylmethacrylate copolymer, styrene-butylmethacrylate copolymer, styrene-α-chloromethylmethacrylate copolymer, styrene-acrylonitrile copolymer, styrene-vinylmethylether Copolymer, styrene-vinyl ethyl ether copolymer, styrene-vinyl methyl ketone copolymer, styrene-butadiene copolymer, styrene-isoprene copolymer, styrene-acrylonitrile-indene copolymer, styrene-maleic acid copolymer Polymer,
Styrene-styrene copolymers such as maleic acid ester copolymers, polymethyl methacrylate, polybutyl methacrylate, polyvinyl chloride, polyvinyl acetate, polyethylene, polypropylene, polyester, polyurethane, polyamide, epoxy resin, polyvinyl butyral, polyamide, Polyacrylic acid resin, rosin, modified rosin, terpene resin, phenol resin, aliphatic or alicyclic hydrocarbon resin, aromatic petroleum resin, chlorinated paraffin, paraffin wax and the like can be used alone or in combination.
（着色剤） 着色剤としては、カーボンブラック、ニグロシン染料
（C.I.No.50415B）、アニリンブルー（C.I.No.5040
5）、カルコオイルブルー（C.I.No.azoec Blue3）、ク
ロムイエロー（C.I.No.14090）、ウルトラマリンブルー
（C.I.No.77103）、デュポンオイルレッド（C.I.No.261
05）、キノリンイエロー（C.I.No.47005）、メチレンブ
ルークロライド（C.I.No.52015）、フタロシアニンブル
ー（C.I.No.74160）、マラカイトグリーンオクサレート
（C.I.No.42000）、ランプブラック（C.I.No.77266）、
ローズベンガル（C.I.No.45435）、これらの混合物その
他を挙げることができる。これら着色剤は、十分な濃度
の可視像が形成されるに十分な割合で含有されることが
必要であり、通常バインダー樹脂100重量部に対して１
〜20重量部程度の割合で配合される。(Colorant) As a colorant, carbon black, nigrosine dye (CINo.50415B), aniline blue (CINo.5040)
5), Calco Oil Blue (CINo.azoec Blue3), Chrome Yellow (CINo.14090), Ultramarine Blue (CINo.77103), DuPont Oil Red (CINo.261)
05), Quinoline Yellow (CINo.47005), Methylene Blue Chloride (CINo.52015), Phthalocyanine Blue (CINo.74160), Malachite Green Oxalate (CINo.42000), Lamp Black (CINo.77266),
Rose Bengal (CI No. 45435), mixtures thereof and the like can be mentioned. It is necessary that these colorants are contained in a sufficient amount to form a visible image with a sufficient density, and usually 1 part is added to 100 parts by weight of the binder resin.
It is mixed in a ratio of about 20 parts by weight.
（添加剤） 更に本発明のトナーには必要に応じて各種の添加剤が
使用される。添加される添加剤の１例としては、電荷制
御剤、定着を接触加熱定着方式で行なう場合のオフセッ
ト防止剤、その他を挙げることができ、オフセット防止
剤としては、例えば環球法による軟化点が80〜180℃の
ポリオレフィン特にポリプロピレンが有効である。(Additive) Further, various additives are used in the toner of the present invention as necessary. Examples of the additive to be added include a charge control agent, an offset preventive agent when fixing is performed by a contact heating fixing method, and the like. Examples of the offset preventive agent include a softening point of 80 by the ring and ball method. Polyolefins of up to 180 ° C, especially polypropylene, are effective.
又、本発明は磁性体を含有させた一成分トナーにも応
用することができる。その場合の磁性体としてはフェラ
イト、マグネタイトをはじめとする鉄、コバルト、ニッ
ケルなどの強磁性を示す金属若しくは合金又はこれらの
元素を含む化合物、或いは強磁性元素を含まないが適当
な熱処理を施すことによって強磁性を示すようになる合
金、例えばマンガン−銅−アルミニウム、マンガン−銅
−錫などのマンガンと銅とを含むホイスラー合金と呼ば
れる種類の合金、又は二酸化クロム、その他を挙げるこ
とができる。これらの磁性体は平均粒径が0.1〜１ミク
ロンの微粉末の形で結着樹脂中に均一に分散される。そ
してその含有量は、トナー100重量部当り20〜70重量
部、好ましくは40〜70重量部である。The present invention can also be applied to a one-component toner containing a magnetic material. In that case, as a magnetic material, a metal or alloy exhibiting ferromagnetism such as iron, cobalt, and nickel such as ferrite and magnetite, a compound containing these elements, or a material containing no ferromagnetic element, but subjected to an appropriate heat treatment Examples thereof include alloys that exhibit ferromagnetism, such as manganese-copper-aluminum, manganese-copper-tin, and other types of alloys called Heusler alloys containing manganese and copper, or chromium dioxide. These magnetic materials are uniformly dispersed in the binder resin in the form of fine powder having an average particle size of 0.1 to 1 micron. The content is 20 to 70 parts by weight, preferably 40 to 70 parts by weight, per 100 parts by weight of the toner.
以下本発明の実施例および比較例について説明する。 Examples and comparative examples of the present invention will be described below.
実施例１ トナーの結着樹脂としてMn＝5500、Mw＝220000、Mw/M
n＝40のスチレン−アクリル酸エステル共重合体樹脂100
重量部と、帯電制御剤としてオリエント化学社製ボント
ロンN04を1.4重量部と、カーボンブラックとして三菱化
成社製MA−600を12重量部と、添加物としてエチレン・
アクリル酸エチル・無水マレイン酸三元共重合体（住化
シーディエフ化学社製ボンダインHX8200,アクリル酸エ
ステル含量６％）を５重量部とを混合し、溶融混練後粉
砕分級して本発明の静電荷像用トナーを作成した。該ト
ナー３重量部をフェライトにシリコーン樹脂をコーティ
ングしたキャリア100重量部とよく混合して２成分系現
像剤を作成した。Example 1 As a binder resin for toner, Mn = 5500, Mw = 220,000, Mw / M
n = 40 styrene-acrylic acid ester copolymer resin 100
1.4 parts by weight of Bontron N04 manufactured by Orient Chemical Co. as a charge control agent, 12 parts by weight of MA-600 manufactured by Mitsubishi Kasei Co. as carbon black, and ethylene as an additive.
5 parts by weight of ethyl acrylate / maleic anhydride terpolymer (Bondyne HX8200 manufactured by Sumika CDF Chemical Co., Ltd., 6% acrylic acid ester content) was mixed, melt kneaded, pulverized and classified to obtain the electrostatic charge of the present invention. An image toner was prepared. 3 parts by weight of the toner was thoroughly mixed with 100 parts by weight of a carrier prepared by coating ferrite with a silicone resin to prepare a two-component developer.
実施例２ エチレン・アクリン酸エチル・無水マレイン酸三元共
重合体として、住化シーディエフ化学社製ボンダインHX
8210（アクリル酸エステル含量６％）を５重量部を用い
た他は実施例１と同様にして本発明の静電荷像用トナー
とそれを用いた２成分系現像剤を作成した。Example 2 As a terpolymer of ethylene / ethyl acrylate / maleic anhydride, Bondyne HX manufactured by Sumika CDF Chemical Co., Ltd.
A toner for electrostatic image of the present invention and a two-component developer using the same were prepared in the same manner as in Example 1 except that 510 parts by weight of 8210 (acrylic acid ester content 6%) was used.
実施例３ エチレン・アクリル酸エチル・無水マレイン酸三元共
重合体として、住化シーディエフ化学社製ボンダインHX
8060（アクリル酸エステル含量６％）を５重量部を用い
た他は実施例１と同様にして本発明の静電荷像用トナー
およびそれを用いた２成分系現像剤を作成した。Example 3 As a terpolymer of ethylene / ethyl acrylate / maleic anhydride, Bondaine HX manufactured by Sumika CDF Chemical Co., Ltd.
A toner for electrostatic charge image of the present invention and a two-component developer using the same were prepared in the same manner as in Example 1 except that 5060 parts by weight of 8060 (acrylic acid ester content 6%) was used.
比較例１ エチレン・アクリル酸エチル・無水マレイン酸三元共
重合体を添加しない他は実施例１と同様にして比較用の
２成分系現像剤を作成した。Comparative Example 1 A two-component developer for comparison was prepared in the same manner as in Example 1 except that the terpolymer of ethylene / ethyl acrylate / maleic anhydride was not added.
比較例２ エチレン・アクリン酸エチル・無水マレイン酸三元共
重合体として、住化シーディエフ化学社製ボンダインHX
8200（アクリル酸エステル含量６％）に代えてポリエチ
レンワックス（ヘキスト社製PE130）を５重量部を用い
た他は実施例１と同様にして比較用の２成分系現像剤を
作成した。Comparative Example 2 As an ethylene / ethyl acrylate / maleic anhydride terpolymer, Bondaine HX manufactured by Sumika CDF Chemical Co., Ltd.
A two-component developer for comparison was prepared in the same manner as in Example 1 except that 5 parts by weight of polyethylene wax (PE130 manufactured by Hoechst) was used instead of 8200 (acrylic acid ester content 6%).
比較例３ ポリエチレンワックスに代えてカルナウバワックスを
５重量部を用いた他は比較例２と同様にして比較用の２
成分系現像剤を作成した。Comparative Example 3 Comparative Example 2 was conducted in the same manner as Comparative Example 2 except that 5 parts by weight of carnauba wax was used instead of polyethylene wax.
A component-based developer was created.
比較例４ ポリエチレンワックスに代えてエチレン−酢酸ビニル
共重合体を５重量部を用いた他は比較例２と同様にして
比較用の２成分系現像剤を作成した。Comparative Example 4 A two-component developer for comparison was prepared in the same manner as Comparative Example 2 except that 5 parts by weight of ethylene-vinyl acetate copolymer was used instead of polyethylene wax.
比較例５ エチレン・アクリル酸エチル・無水マレイン酸三元共
重合体として住化シーディエフ化学社製ボンダインHX82
00の添加量を0.5重量部とした以外は実施例１と同様に
して比較用の２成分系現像剤を作成した。Comparative Example 5 As a terpolymer of ethylene / ethyl acrylate / maleic anhydride, Sumitomo Chemical Co., Ltd. Bondyne HX82
A two-component developer for comparison was prepared in the same manner as in Example 1 except that the addition amount of 00 was 0.5 part by weight.
比較例６ エチレン・アクリル酸エチル・無水マレイン酸三元共
重合体として住化シーディエフ化学社製ボンダインHX82
00の添加量を60重量部とした以外は実施例１と同様にし
て比較用の２成分系現像剤を作成した。Comparative Example 6 As a terpolymer of ethylene / ethyl acrylate / maleic anhydride, Bondaine HX82 manufactured by Sumika CDI Chemical Co., Ltd.
A two-component developer for comparison was prepared in the same manner as in Example 1 except that the addition amount of 00 was 60 parts by weight.
実施例１〜３および比較例１〜６で得られた２成分系
現像剤を電子複写機（シヤープ社製SF−9750）にセット
し、連続コピーを実施して第１表に示すような諸特性を
評価した。The two-component type developers obtained in Examples 1 to 3 and Comparative Examples 1 to 6 were set in an electronic copying machine (SF-9750 manufactured by Sharp Corporation), and continuous copying was carried out to obtain various properties as shown in Table 1. The characteristics were evaluated.
第１表の各評価項目の試験方法は下記のとおりであ
る。 The test methods for each evaluation item in Table 1 are as follows.
１）トナーの保存安定性；トナーを50℃の雰囲気中に８
時間放置した後のブロッキングの状態を評価。1) Storage stability of the toner; the toner is stored in an atmosphere of 50 ° C for 8 hours.
Evaluate the blocking state after leaving for a while.
◎…50℃の雰囲気に入れる前と全く同等でブロッキング
がないもの ○…若干流動性低下があるが実用上全く支障ないもの △…流動性低下がみられブロッキンの徴候あり ×…ブロッキングを生じ実用上支障をきたすもの ××…ブロッキングが著しいもの ２）定着残存率；複写機の定着ユニットの温度条件を16
0℃、180℃、200℃に変動させて定着画像（1cm四方のベ
タ画像）を作成し、消しゴム摩耗試験器にて、画像部を
1kg/cm2圧で３往復摩耗し、摩耗前後の画像濃度をマク
ベス反射濃度計にて測定し、下記の式にて算出した。摩
耗前の画像濃度をＡ、摩耗後の画像濃度をＢとすると、 定着残存率（％）＝B/A×100 ３）両面コピー汚れ；予め片面のみコピーした紙を裏面
（コピーしてない面）を上にして多数枚用紙カセットに
積層し、連続して裏面にコピーしていく過程で、給紙ロ
ーラー圧により積層してあるコピー画像がこすられて裏
面に付着する状態を評価。◎ ... Exactly the same as before being put in an atmosphere of 50 ° C and without blocking ○ ... Slightly reduced fluidity but no problem in practical use △ ... Lower fluidity and symptom of blockin x ... Problems that cause troubles XX ... Significant blocking 2) Residual fixing rate; temperature condition of fixing unit of copier is 16
A fixed image (solid image of 1 cm square) is created by changing it to 0 ° C, 180 ° C, and 200 ° C, and the image part is displayed with an eraser abrasion tester.
After three reciprocating abrasions at 1 kg / cm 2 pressure, the image densities before and after abrasion were measured with a Macbeth reflection densitometer and calculated by the following formula. If the image density before abrasion is A and the image density after abrasion is B, the residual fixing rate (%) = B / A x 100 3) Duplex copy stains; ) Is stacked on top of a multi-sheet paper cassette, and in the process of continuously copying on the back side, the state in which the stacked copy images are rubbed by the pressure of the paper feed roller and adhered to the back side is evaluated.
４）画像濃度および汚れ；マクベス反射濃度計による。4) Image density and stains: by Macbeth reflection densitometer.
第１表の結果から明らかなとおり、本発明の実施例１
〜３によるトナーは、トナーの保存安定性、現像剤の実
用特性全てにわたってバランスよく安定した特性が得ら
れた。As is clear from the results in Table 1, Example 1 of the present invention
The toners Nos. 3 to 3 have stable properties in a well-balanced manner over all of the storage stability of the toner and the practical properties of the developer.
これに対して比較例５に示したトナーは、エチレン・
アクリル酸エチル・マレイン酸三元共重合体樹脂の配合
量が全トナー中で１重量％未満の場合で、定着性（定着
残存率、両面コピー汚れ）に効果がない。又、比較例６
に示したトナーは、エチレン・アクリル酸エチル・マレ
イン酸三元共重合体樹脂の配合量が30重量％を超える場
合で、定着性は良好であるが、トナーの保存安定性に重
大な支障をきたすことがわかる。なお、比較例１〜４の
静電荷像用トナーは本発明で特定するエチレン・アクリ
ル酸エステル・マレイン酸三元共重合体樹脂を含有しな
いもので、トナーの保存安定性と現像剤の実用特性の全
てのバランスをより良好に保つことができなかった。On the other hand, the toner shown in Comparative Example 5 is ethylene
When the blending amount of the ethyl acrylate / maleic acid terpolymer resin is less than 1% by weight in all toners, there is no effect on the fixability (fixing residual ratio, double-sided copy stain). Comparative Example 6
The toner shown in Fig. 3 has a good fixability when the blending amount of the ethylene / ethyl acrylate / maleic acid terpolymer resin is more than 30% by weight, but the toner storage stability is seriously hindered. I understand that it will come. The toners for electrostatic images of Comparative Examples 1 to 4 do not contain the ethylene / acrylic acid ester / maleic acid terpolymer resin specified in the present invention, and have storage stability of the toner and practical properties of the developer. I couldn't keep a good balance of all of.
本発明は、以上に述べた様に、画像特性に何等の悪影
響を及ぼすことなく、従来の技術では不可能であったト
ナーの保存安定性と定着性を両立することが可能のた
め、自動両面コピー装置に適用しても実用上問題なく連
続コピーが可能である。INDUSTRIAL APPLICABILITY As described above, the present invention can achieve both storage stability and fixing property of the toner, which cannot be achieved by the conventional technology, without adversely affecting the image characteristics. Even when applied to a copying machine, continuous copying is possible without any practical problems.
Claims (1)
中に全体の１〜30重量％のエチレン・アクリル酸エステ
ル・無水マレイン酸三元共重合体樹脂を含有してなり、
該エチレン・アクリル酸エステル・無水マレイン酸三元
共重合体樹脂を構成する共重合体成分としてアクリル酸
エステル含量を１〜30重量％とした熱ロール定着用の静
電荷像用トナー1. A toner containing a binder resin and a colorant as a main component contains 1 to 30% by weight of the whole ethylene / acrylic ester / maleic anhydride terpolymer resin.
Electrostatic charge image toner for heat roll fixing having an acrylic acid ester content of 1 to 30% by weight as a copolymer component constituting the ethylene / acrylic acid ester / maleic anhydride terpolymer resin.