JPH081039B2 - Clean room wallpaper - Google Patents
Clean room wallpaperInfo
- Publication number
- JPH081039B2 JPH081039B2 JP63111946A JP11194688A JPH081039B2 JP H081039 B2 JPH081039 B2 JP H081039B2 JP 63111946 A JP63111946 A JP 63111946A JP 11194688 A JP11194688 A JP 11194688A JP H081039 B2 JPH081039 B2 JP H081039B2
- Authority
- JP
- Japan
- Prior art keywords
- wallpaper
- parts
- layer
- cured resin
- clean room
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は、工業用のクリーンルームの壁に貼る壁紙の
改良に関する。TECHNICAL FIELD The present invention relates to an improvement in wallpaper applied to the wall of an industrial clean room.
工業用のクリーンルームの壁紙を施工する場合、従来
はアスベールやグラサールなどの無機質系のパネルが広
く使用されている。 この種のパネルは重量があり、施工に手間どる上にコ
ストが高い。 合成樹脂系の壁紙は軽く、施工が容易であって高価で
ないが、気流中のホコリが静電気により付着して蓄積す
るので、達成できるクリーン度は低いものである。 この点を改善した壁紙として、出願人は、壁紙基材シ
ートの上に導電性フィラーを含有する硬化樹脂の層を設
けたクリーンルーム用壁紙を発明し、すでに提案した
（特開昭63−295795号）。この壁紙は、表面が帯電せず
ホコリの付着が避けられ、達成できるクリーン度は高い
ものであって、ししかも軽くて施工が容易であり、コス
トが低廉な上に、耐汚染性、耐摩耗性、耐溶剤性などの
表面物性にすぐれている。 上記の諸物性を一層向上させ、とくに耐擦傷性をも付
与した壁紙を開発するのが、次の課題である。BACKGROUND ART In the case of applying wallpaper for an industrial clean room, inorganic panels such as asveils and glasals have been widely used in the past. This type of panel is heavy, laborious to construct and expensive. Synthetic resin wallpaper is light, easy to install and inexpensive, but the degree of cleanliness that can be achieved is low because dust in the air flow adheres and accumulates due to static electricity. As a wallpaper in which this point is improved, the applicant invented a wallpaper for a clean room in which a layer of a cured resin containing a conductive filler is provided on a wallpaper base sheet, and has already proposed (Japanese Patent Laid-Open No. 63-295795). ). This wallpaper has a high degree of cleanliness that can be achieved because the surface is not charged and dust can be avoided, and it is light and easy to install, low cost, stain resistant and abrasion resistant. Excellent surface properties such as resistance and solvent resistance. The next task is to develop a wallpaper that further improves the above-mentioned various physical properties and is particularly provided with scratch resistance.
本発明の目的は、上記課題のひとつの解決策として、
すでに提案した上記発明の効果、すなわち高いクリーン
度を達成でき、軽くて施工が容易であり、コストが低廉
な上に耐汚染性、耐摩耗性、耐溶剤性などの表面物性に
すぐれるというメリットを享受した上で、上記の諸物性
を向上させ、耐擦傷性をも付与した壁紙を提供すること
にある。An object of the present invention is to solve one of the above problems,
Advantages of the previously proposed invention, namely high cleanliness, light weight, easy construction, low cost, and excellent surface properties such as stain resistance, abrasion resistance, and solvent resistance. The object of the present invention is to provide a wallpaper that has the above-mentioned physical properties and is improved in scratch resistance.
本発明のクリーンルーム用壁紙は、基本的には第１図
に示すように、壁紙基材シート１の上に、導電性フィラ
ーを含有し帯電防止能を有する硬化樹脂の層２および界
面活性剤を含有する硬化樹脂の層３を、この順に設けて
なるものである。 別の態様では、第２図に示すように、壁紙基材シート
１の上に、接着剤層４、ポリエステルフィルム５、導電
性フィラーを含有し帯電防止能を有する硬化樹脂の層２
および界面活性剤を含有する硬化樹脂の層３を、この順
に設けてなる。 壁紙基剤シートとしては、第１図および第２図に示す
ように、裏打ちシート11上にポリ塩化ビニルの層12を有
するものが好適である。裏打ちシートとしては、壁紙裏
打用難燃紙が最適である。このほか、薄葉紙、晒クラフ
ト紙、チタン紙、リンター紙など、壁紙の裏打ちに常用
されているものであれば、何でもよい。 接着剤は、常用のポリウレタン、エチレン−酢酸ビニ
ル共重合体などを使用し、ドライラミネート、ウェット
ラミネート、プラスラミネートなどにより接着を行な
う。 導電性フィラーとしては、酸化スズや酸化インジウム
・スズのような、非金属で透明な導電性物質の粉末が好
適である。カーボン粉末も使用できるが、製品壁紙の色
に制約を受ける。 硬化樹脂は、エポキシ樹脂、フェノール樹脂、不飽和
ポリエステル樹脂などの熱硬化型樹脂、アクリル系樹
脂、アクリル変性樹脂、ポリエステル系樹脂などの紫外
線硬化型樹脂、およびエチレン−酢酸ビニル共重合体、
不飽和ポリエステル樹脂、アクリル系樹脂、アクリル変
性樹脂、エチレンとアクリル酸またはそのエステルとの
共重合体などの電子線硬化型樹脂から、適当なものをえ
らんで使用する。 導電性フィラーを含有する硬化樹脂の層は、導電性フ
ィラーを混合した液状の硬化性樹脂を、グラビアコー
ト、ロールコートなど任意の手段で塗布したのち、硬化
させて形成する。 界面活性剤としては、常用の陽イオン性、陰イオン
性、非イオン性または両性の、いずれのものも使用でき
る。添加量は、硬化性樹脂100重量部に対して0.1〜５重
量部、好ましくは２重量部程度である。 界面活性剤を含有する硬化樹脂の層は、上記の導電性
フィラーを含有する硬化樹脂の層と同様にして形成すれ
ばよい。 ポリエステルフィルムの厚さは、６〜38μ程度が好ま
しい。それ以上になると壁紙を施工する際、コーナー処
理がしにくくなる。The clean room wallpaper of the present invention basically comprises, as shown in FIG. 1, a cured resin layer 2 containing a conductive filler and having an antistatic ability, and a surfactant on a wallpaper base sheet 1. The layer 3 of the contained cured resin is provided in this order. In another embodiment, as shown in FIG. 2, an adhesive layer 4, a polyester film 5, and a layer 2 of a cured resin containing an electrically conductive filler and having an antistatic ability are provided on a wallpaper base sheet 1.
And a layer 3 of a cured resin containing a surfactant is provided in this order. As the wallpaper base sheet, a sheet having a polyvinyl chloride layer 12 on a backing sheet 11 as shown in FIGS. 1 and 2 is preferable. Flame-retardant paper for wallpaper lining is the most suitable backing sheet. In addition, any thin paper, bleached kraft paper, titanium paper, linter paper, or any other material commonly used for lining wallpaper can be used. As the adhesive, a commonly used polyurethane, ethylene-vinyl acetate copolymer, or the like is used, and adhesion is performed by dry lamination, wet lamination, plus lamination, or the like. As the conductive filler, powder of a non-metal and transparent conductive substance such as tin oxide or indium tin oxide is suitable. Carbon powder can also be used, but is limited by the color of the product wallpaper. The curable resin is an epoxy resin, a phenol resin, a thermosetting resin such as an unsaturated polyester resin, an acrylic resin, an acrylic modified resin, an ultraviolet curable resin such as a polyester resin, and an ethylene-vinyl acetate copolymer,
An electron beam curable resin such as an unsaturated polyester resin, an acrylic resin, an acrylic modified resin, or a copolymer of ethylene and acrylic acid or its ester is selected and used. The layer of the cured resin containing the conductive filler is formed by applying a liquid curable resin mixed with the conductive filler by an arbitrary means such as gravure coating or roll coating, and then curing it. As the surfactant, any of commonly used cationic, anionic, nonionic or amphoteric compounds can be used. The addition amount is 0.1 to 5 parts by weight, preferably about 2 parts by weight, based on 100 parts by weight of the curable resin. The layer of the cured resin containing the surfactant may be formed in the same manner as the layer of the cured resin containing the conductive filler. The thickness of the polyester film is preferably about 6 to 38 μm. If it is more than that, corner processing becomes difficult when applying wallpaper.
本発明のクリーンルーム用壁紙は、導電性フィラーを
含有する硬化樹脂の層の上に界面活性剤を含有する硬化
樹脂の層を設けて硬化樹脂の層の総厚さを厚くしたの
で、耐摩耗性や耐溶剤性が一層向上し、耐擦傷性も付与
された。界面活性剤は、表面に付着した油性の汚れを隔
離、分散させる働きがあるので、耐汚染性も向上した。 界面活性剤を含有する硬化樹脂の層のために、導電性
フィラーを含有する硬化樹脂の層の働きである帯電防止
能が妨げられることはない。従って、表面の帯電を防止
し、ホコリの付着を避けられることは、さきに提案した
ものと異ならない。 ポリエステルフィルム上に導電性フィラーを含有する
硬化樹脂の層および界面活性剤を含有する硬化樹脂の層
を設けた態様では、熱硬化型樹脂を使用して高温で熱硬
化させても、その下の壁紙基材シートが損われることな
く十分な硬化ができ、硬化樹脂の特性をフルに利用でき
る。Since the wallpaper for a clean room of the present invention is provided with a layer of a cured resin containing a surfactant on a layer of a cured resin containing a conductive filler to increase the total thickness of the layer of the cured resin, it has abrasion resistance. And solvent resistance were further improved, and scratch resistance was also imparted. Since the surfactant has a function of separating and dispersing oily stains attached to the surface, the stain resistance is also improved. The layer of the cured resin containing the surfactant does not hinder the antistatic ability which is the function of the layer of the cured resin containing the conductive filler. Therefore, the prevention of electrostatic charge on the surface and the avoidance of dust adhesion are no different from those previously proposed. In the aspect in which the layer of the cured resin containing the conductive filler and the layer of the cured resin containing the surfactant are provided on the polyester film, even if the thermosetting resin is used to thermally cure at a high temperature, The wallpaper base sheet can be sufficiently cured without being damaged, and the characteristics of the cured resin can be fully utilized.
【実施例１】 下記の配合で、白色のポリ塩化ビニルのペーストを調
整した（「部」はいずれも重量部） ポリ塩化ビニル「Ｇ−121」（日本ゼオン） 50部 ポリ塩化ビニル「Ｇ−103ZX」（日本ゼオン） 20部 可塑剤 ジオクチルフタレート 35部 炭酸カルシウム 20部 酸化チタン 10部 安定剤 ４部 合計 139部 坪量80g/m2の壁紙裏打用難燃紙の上に、上記のペース
トをコンマコーターを用いて200μの厚さに塗布し、温
度180℃のオーブンで1.5分間加熱してゲル化させた。 導電性フィラーを含有する下記の配合の熱硬化性樹脂
のインキと硬化剤を調整した。 （インキ） 酸化スズ系導電性粉末 30 部 アクリルポリオール「サーモラックU230」（総研化学）
23 部 塩ビ−酢ビ共重合体「ビニライトVAGH」（UCC） 2.5部 メラミン樹脂「サイメル370」（サイアナミド） ３ 部 分散剤 １ 部 マイクロシリカ １ 部 メチルエチルケトン 7.5部 酢酸ブチル 12 部 トルエン 11 分 メチルイソブチルケトン 6 部 合計 97 部 （硬化剤） パラトルエンスルホン酸 40部 イソプロパノール 60部 合計 100部 前記した白色のポリ塩化ビニル層の上に、上記のイン
キ100部に上記の硬化剤５部を添加したものを用いて、
乾燥後２μの厚さとなるようにグラビアコートし、温度
150℃のオーブンで15秒間加熱して硬化させることによ
り、導電性フィラーを含有する硬化樹脂の層を形成し
た。 界面活性剤を含有する下記の配合の熱硬化性樹脂のイ
ンキを調製した。 塩ビ−酢ビ共重合体「ビニライトVAGH」（UCC） 10部 メタクリル樹脂10部 メチルエチルケトン 40部 トルエン 40部 陽イオン性界面活性剤「レジスタットSA130 ２
部 合計 102部 前記の硬化樹脂の層の上に、上記のインキ100部に前
記と同じ硬化剤５部を添加したものを、乾燥後２μｍの
厚さとなるようにグラビアコートし、温度150℃のオー
ブンで20秒間加熱して硬化させることにより、界面活性
剤を含有する硬化樹脂の層を設けた。 得られたクリーンルーム用壁紙は、表面抵抗値が6.3
×106Ω／口であった。マジックやボールペンの汚れ
は、メチルエチルケトンやベンジンで完全に拭き取れ
た。硬貨でこすっても傷がつかないし、ベンジン、メチ
ルエチルケトン、トルオール、５％塩酸、潤滑油のいず
れにも侵されることがなかった。防炎性能は、「防炎２
級」に合格するものであった。Example 1 A white polyvinyl chloride paste was prepared with the following composition (“parts” are all parts by weight): Polyvinyl chloride “G-121” (Zeon Corporation) 50 parts Polyvinyl chloride “G-” "103ZX" (Nippon Zeon) 20 parts Plasticizer Dioctyl phthalate 35 parts Calcium carbonate 20 parts Titanium oxide 10 parts Stabilizer 4 parts Total 139 parts Basis weight 80g / m 2 Flame retardant paper for wallpaper backing It was applied to a thickness of 200 μ using a comma coater and heated in an oven at a temperature of 180 ° C. for 1.5 minutes for gelation. A thermosetting resin ink and a curing agent having the following composition containing a conductive filler were prepared. (Ink) Tin oxide conductive powder 30 parts Acrylic polyol "Thermolac U230" (Soken Chemical)
23 parts Vinyl chloride-vinyl acetate copolymer "Vinylite VAGH" (UCC) 2.5 parts Melamine resin "Cymel 370" (Cyanamide) 3 parts Dispersant 1 part Microsilica 1 part Methyl ethyl ketone 7.5 parts Butyl acetate 12 parts Toluene 11 minutes Methyl isobutyl ketone 6 parts Total 97 parts (Curing agent) Paratoluene sulfonic acid 40 parts Isopropanol 60 parts Total 100 parts A mixture of 100 parts of the above ink and 5 parts of the above curing agent on the white polyvinyl chloride layer described above. make use of,
After drying, gravure coat to a thickness of 2μ and
A layer of a cured resin containing a conductive filler was formed by heating and curing in an oven at 150 ° C for 15 seconds. An ink of thermosetting resin having the following formulation containing a surfactant was prepared. Vinyl chloride-vinyl acetate copolymer "Vinylite VAGH" (UCC) 10 parts Methacrylic resin 10 parts Methyl ethyl ketone 40 parts Toluene 40 parts Cationic surfactant "Register SA130 2 "
Parts Total 102 parts Onto the above cured resin layer, 100 parts of the above ink and 5 parts of the same curing agent as described above were gravure coated to a thickness of 2 μm after drying, and the temperature of 150 ° C. A layer of cured resin containing a surfactant was provided by heating in an oven for 20 seconds to cure. The obtained clean room wallpaper has a surface resistance of 6.3.
It was × 10 6 Ω / mouth. The dirt on the magic and ballpoint pen was completely wiped off with methyl ethyl ketone or benzine. It was not scratched by rubbing with a coin and was not attacked by benzine, methyl ethyl ketone, toluene, 5% hydrochloric acid, or lubricating oil. The flameproof performance is "flameproof 2
It passed the "grade".
【実施例２】 実施例１と同様にして、壁紙裏打用難燃紙上に白色の
ポリ塩化ビニルの層を形成した。 下記の配合の導電性フィラーを含有する熱硬化性樹脂
のインキを調製した。 酸化スズ系導電性の粉末 30 部 ポリエステル樹脂「バイロン200」（東洋紡） 7.5部 メラミン樹脂「サイメル370」 20 部 分散剤 １ 部 マイクロシリカ １ 部 メチルエチルケトン13 部 トルオール 27.5部 合計 100 部 厚さ12μの透明なポリエステルフィルムの上に、上記
のインキ100部に実施例１と同じ硬化剤５部を添加した
ものを、乾燥後２μの厚さとなるようにグラビアコート
し、温度150℃のオーブンで20秒間加熱して硬化させる
ことにより、導電性フィラーを含有する硬化樹脂の層を
形成した。 この硬化樹脂の層の上に、実施例１と同様にして界面
活性剤を含有する硬化樹脂の層を設けた。 上記のポリエステルフィルムの他方の面に接着剤「ハ
イボン7662」（日立化成ポリマー）を30g/cm2塗布し、
この面と上記の白色ポリ塩化ビニルの面とを重ね合わせ
てドライラミネートした。得られたクリーンルーム用壁
紙は、実施例１の製品と同様な性能を示した。Example 2 In the same manner as in Example 1, a layer of white polyvinyl chloride was formed on the flame-retardant paper for backing wallpaper. A thermosetting resin ink containing a conductive filler having the following composition was prepared. Tin oxide conductive powder 30 parts Polyester resin “Vylon 200” (Toyobo) 7.5 parts Melamine resin “Cymel 370” 20 parts Dispersant 1 part Microsilica 1 part Methyl ethyl ketone 13 parts Toluol 27.5 parts Total 100 parts Thickness 12μ transparent On a polyester film, 100 parts of the above ink and 5 parts of the same curing agent as in Example 1 were added, gravure coated to a thickness of 2μ after drying, and heated in an oven at a temperature of 150 ° C for 20 seconds. And cured to form a layer of a cured resin containing a conductive filler. On the cured resin layer, a cured resin layer containing a surfactant was provided in the same manner as in Example 1. Apply 30g / cm 2 of adhesive “Hybon 7662” (Hitachi Kasei Polymer) on the other side of the above polyester film,
This surface and the surface of the above-mentioned white polyvinyl chloride were overlapped and dry laminated. The obtained wallpaper for clean rooms exhibited the same performance as the product of Example 1.
本発明のクリーンルーム用壁紙は、すでに提案した壁
紙のメリットすなわち高いクリーン度を達成でき、軽く
て施工が容易であり、コストが低廉である上に耐汚染
性、耐摩耗性、耐溶剤性などの表面物性にすぐれている
という利点をそなえ、しかも耐擦傷性も向上している。The wallpaper for the clean room of the present invention can achieve the advantages of the wallpaper already proposed, that is, high cleanliness, is light and easy to install, and is low in cost, and also has stain resistance, abrasion resistance, solvent resistance, etc. It has the advantage of excellent surface properties, and also has improved scratch resistance.
第１図は、本発明のクリーンルーム用壁紙の基本的な構
成を示す、模式的な断面図である。 第２図は、本発明のクリーンルーム用壁紙の別の態様の
構成を示す、第１図と同様な断面図である。 １……壁紙基材シート 11……裏打ちシート 12……ポリ塩化ビニルの層 ２……導電性フィラーを含有する硬化樹脂の層 ３……界面活性剤を含有する硬化樹脂の層 ４……接着剤層 ５……ポリエステルフィルムFIG. 1 is a schematic cross-sectional view showing the basic configuration of the clean room wallpaper of the present invention. FIG. 2 is a sectional view similar to FIG. 1, showing the configuration of another aspect of the clean room wallpaper of the present invention. 1 ... Wallpaper base sheet 11 ... Backing sheet 12 ... Polyvinyl chloride layer 2 ... Cured resin layer containing conductive filler 3 ... Cured resin layer containing surfactant 4 ... Adhesion Agent layer 5: Polyester film
Claims (3)
含有し帯電防止能を有する硬化樹脂の層および界面活性
剤を含有する硬化樹脂の層を、この順に設けてなるクリ
ーンルーム用壁紙。1. A wallpaper for a clean room in which a layer of a cured resin containing an electrically conductive filler and having an antistatic ability and a layer of a cured resin containing a surfactant are provided in this order on a wallpaper base sheet.
ステルフィルム、導電性フィラーを含有し帯電防止能を
有する硬化樹脂の層および界面活性剤を含有する硬化樹
脂の層を、この順に設けてなるクリーンルーム用壁紙。2. An adhesive layer, a polyester film, a layer of a cured resin containing an electrically conductive filler and having an antistatic ability, and a layer of a cured resin containing a surfactant in this order on a wallpaper base sheet. Clean room wallpaper provided.
ポリ塩化ビニルを積層したものを使用した請求項１また
は２に記載の壁紙。3. The wallpaper according to claim 1 or 2, wherein a backing sheet laminated with polyvinyl chloride is used as the wallpaper base sheet.