JPH0780741B2 - Makeup cosmetics - Google Patents
Makeup cosmeticsInfo
- Publication number
- JPH0780741B2 JPH0780741B2 JP61010790A JP1079086A JPH0780741B2 JP H0780741 B2 JPH0780741 B2 JP H0780741B2 JP 61010790 A JP61010790 A JP 61010790A JP 1079086 A JP1079086 A JP 1079086A JP H0780741 B2 JPH0780741 B2 JP H0780741B2
- Authority
- JP
- Japan
- Prior art keywords
- coated
- powder
- elastin
- pigment
- cosmetics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 <産業上の利用分野> 本発明は従来にない優れた感触を有するメークアップ化
粧料に関する。DETAILED DESCRIPTION OF THE INVENTION <Field of Industrial Application> The present invention relates to a makeup cosmetic composition having an unprecedented excellent feel.
<従来の技術> 従来、粉体を含有するメークアップ化粧料は、例えば、
ケーキ状ファンデーションの如く、顔料、色素、油分界
面活性剤、水、保温剤等より成っており、魅力的な容貌
を作る為に用いられて来た。ところが、皮膚上に塗布し
た場合には粉体の吸油性、吸水性が強すぎる為、皮膚か
ら必要以上に皮脂や水分を吸着してしまい、皮膚のかさ
つき等を生じる原因となっていたのである。又、皮膚に
塗布したときの感触がかたい感じとなり、付着性が悪く
なったり、しっとり感が失われるという欠点があり、な
めらかなタッチで塗布することができなかった。この様
なかさつき感は空気の乾燥する季節に於て、特に顕著で
あり、問題となっていたのである。<Prior Art> Conventionally, makeup cosmetics containing powder are, for example,
Like a cake foundation, it is made up of pigments, pigments, oil surfactants, water, heat retaining agents, etc., and has been used to make attractive appearances. However, when it is applied on the skin, the oil absorbency and water absorbency of the powder are too strong, which causes the skin to absorb more sebum and water than necessary, which causes the skin to become bulky. . In addition, when applied to the skin, it has a hard feeling, and there are drawbacks such as poor adhesion and loss of moist feeling, and application with a smooth touch has not been possible. Such a feeling of bulkiness was particularly noticeable and a problem in the dry season of the air.
この問題を解決する為、従来は、保湿剤などを化粧料に
添加することが試みられていた。すなわち、プロピレン
グリコール、グリセリン等の多価アルコールを化粧料に
添加し、これらの保湿能力により、前述した皮膚のかさ
つき感を解消しようと試みたのである。In order to solve this problem, it has hitherto been attempted to add a moisturizer or the like to cosmetics. That is, an attempt was made to add polyhydric alcohols such as propylene glycol and glycerin to cosmetics to eliminate the above-mentioned sensation of skin bulkiness by their moisturizing ability.
<発明が解決しようとする課題> ところが、これらの試みは以下の2つの点で不満足なも
のであった。<Problems to be Solved by the Invention> However, these attempts have been unsatisfactory in the following two points.
すなわち、第1の点としては、粉体を含有する化粧料に
於て、単に保温剤を他の成分と共に粉体と混合せしめ
て、化粧料を製造する場合には、粉体表面に付着ないし
は吸着される化粧料用原料成分が多種他雑なものとなっ
てしまうので、該粉体表面特性が不均一なものとなり、
この結果として、粉体特有の皮膚上でのかさつき感を十
分に改善することができず、又、発汗等により化粧くず
れが起こり易いものであった。That is, the first point is that, in the case of cosmetics containing powder, when the cosmetic is manufactured by simply mixing the heat retaining agent with the powder together with other components, the cosmetics do not adhere to the powder surface. Since the raw material components for cosmetics to be adsorbed become various and miscellaneous, the powder surface characteristics become non-uniform,
As a result, the feeling of bulkiness on the skin peculiar to the powder could not be sufficiently improved, and the makeup was liable to be damaged by sweating or the like.
又、第2の点としては、プロピレングリコール、グリセ
リン等の低分子量の保湿剤は粉体と共に混合した場合
に、粉体に吸着されるが、単なるぬれの状態となるだけ
で、粉体の表面特性を根本的に変えることはないので、
前述の問題点を解決し得ないのである。A second point is that when a low molecular weight moisturizing agent such as propylene glycol or glycerin is mixed with the powder, it is adsorbed to the powder, but it is simply wet and the surface of the powder is Since it does not change the characteristics fundamentally,
The above problems cannot be solved.
<課題を解決するための手段> そこで本発明者らは上記の問題点を解決すべく、皮膚上
での優れた感触と化粧持続性とを合わせもつ粉体の表面
処理方法を種々検討した結果、保湿性高分子物質で粉体
表面を被覆することにより、上記目的を達成することを
見出し本発明を完成するに到った。<Means for Solving the Problems> Therefore, in order to solve the above-mentioned problems, the present inventors have conducted various investigations on surface treatment methods of powder having both excellent feel on the skin and durability of makeup. The inventors have found that the above object can be achieved by coating the surface of powder with a moisturizing polymer substance, and completed the present invention.
かかる知見による本発明に係るメークアップ化粧料は、
コンドロイチン硫酸、エラスチン、エラスチン加水分解
物及びこれらのアルカリ金属塩から選択される保湿性高
分子物質の少なくとも1種以上により顔料表面を被覆し
て得られる被覆顔料を含有することを特徴とする。The makeup cosmetics according to the present invention based on such findings,
It is characterized by containing a coated pigment obtained by coating the pigment surface with at least one or more moisturizing polymer substances selected from chondroitin sulfate, elastin, elastin hydrolysates and alkali metal salts thereof.
以下本発明について詳述する。The present invention will be described in detail below.
本発明に適用される保湿性高分子物質としては、皮膚へ
の親和性や感触のなめらかさの点からコンドロイチン硫
酸、エラスチン、エラスチン加水分解及びこれらのアル
カリ金属塩から選択され、被覆物質として単独で又は2
種以上を混合した形で用いられる。The moisturizing polymer substance applied to the present invention is selected from chondroitin sulfate, elastin, elastin hydrolysis and alkali metal salts thereof in view of affinity to the skin and smoothness of touch, and alone as a coating substance. Or 2
It is used as a mixture of two or more species.
尚、上記保湿性高分子物質は、生体から抽出したもの、
また化学的合成手段で得られたもの、更には微生物的手
法によって作られたものの何れでも使用可能であり、ま
た市販されているものを用いても良い。The moisturizing polymer substance is extracted from a living body,
Further, any of those obtained by a chemical synthesis means and those produced by a microbial method can be used, and a commercially available one may be used.
本発明では、前記した保湿性高分子物質が被覆物質とし
て粉体表面に被覆されることにより、粉体が本来有して
いる吸油特性や吸水特性を変化せしめ、これにより従来
にない新規な官能特性を達成するものである。従って、
保湿性高分子物質は安定的に粉体表面を被覆することが
必要であり、通常は平均分子量が5,000以上のものが用
いられる。平均分子量が5,000より小さい場合には、粉
体表面を安定的に被覆し粉体表面特性を好ましい状態に
保つことができないため好ましいものとは言えない。In the present invention, the above-mentioned moisturizing polymer substance is coated on the surface of the powder as a coating substance to change the oil absorption property and the water absorption property originally possessed by the powder. It achieves the characteristics. Therefore,
The moisturizing polymer substance is required to stably coat the powder surface, and a substance having an average molecular weight of 5,000 or more is usually used. If the average molecular weight is less than 5,000, it cannot be said to be preferable because the powder surface cannot be stably covered and the powder surface characteristics cannot be maintained in a preferable state.
但し、被覆物質中にこけら比較的低分子量の物質が含ま
れていること自体は、目的とする効果を妨げるものでは
ない。However, the fact that the coating substance contains a relatively low molecular weight substance alone does not hinder the intended effect.
次に、本発明に用いられる顔料としては、通常化粧料に
用いられる無機粉体及び有機粉体ともに使用可能である
が、感触の改良効果が大きいという点で無機粉体が好ま
しく用いられる。このような粉体としては例えば、タル
ク、雲母、カオリン、炭酸マグネシウム、炭酸カルシウ
ム、ケイ酸カルシウム、二酸化チタン等の白色顔料、弁
柄、黄酸化鉄、黒酸化鉄、群青、紺青、酸化クロム、二
酸化チタン被覆雲母、黄酸化鉄被覆タルク、黒酸化鉄被
覆雲母等の有色顔料などがあげられる。Next, as the pigment used in the present invention, both inorganic powders and organic powders usually used in cosmetics can be used, but the inorganic powders are preferably used because of the great effect of improving the feel. Examples of such powder include white pigments such as talc, mica, kaolin, magnesium carbonate, calcium carbonate, calcium silicate, and titanium dioxide, red iron oxide, yellow iron oxide, black iron oxide, ultramarine blue, navy blue, chromium oxide, Colored pigments such as titanium dioxide-coated mica, yellow iron oxide-coated talc, black iron oxide-coated mica and the like can be mentioned.
又、これらの顔料は平均粒子径が0.01μ〜50μの範囲の
ものが好ましく使用される。平均粒子径が50μを越える
場合は、化粧料使用時に感触面での違和感を生じ易く、
好ましくない。又、下限については特に制限的ではない
が、0.01μ未満の場合は流動性が低下し、取扱いがむず
かしい。Further, as these pigments, those having an average particle diameter in the range of 0.01 μ to 50 μ are preferably used. If the average particle size exceeds 50μ, it is easy to cause a feeling of strangeness on the touch surface when using a cosmetic,
Not preferable. The lower limit is not particularly limited, but if it is less than 0.01 μ, the fluidity is lowered and the handling is difficult.
次に、本発明に係る被覆顔料において、前記の保湿性高
分子物質と被覆される顔料との比は凡そ0.2:100〜30:10
0好ましくは0.5:100〜15:100(重量比)程度であるが、
その限界は、特定されるものではない。Next, in the coated pigment according to the present invention, the ratio of the moisturizing polymer substance to the coated pigment is about 0.2: 100 to 30:10.
0 is preferably about 0.5: 100 to 15: 100 (weight ratio),
The limit is not specified.
又、本発明に係る被覆顔料は粉体表面が保湿性高分子物
質で被覆されているものであり、従来の顔料の配合方法
と同様の方法で、メークアップ化粧料に配合することが
できる。Further, the coated pigment according to the present invention has a powder surface coated with a moisturizing polymer substance, and can be incorporated into a makeup cosmetic composition in the same manner as a conventional pigment formulation method.
従って、本発明は粉体を含有するメークアップ化粧料に
広く応用可能であり、本発明により提供される化粧料と
してはファンデーション、口紅、ほほ紅、アイライナ
ー、アイシャドー、アイブロー、まゆずみ、粉おしろ
い、フェイスパウダー、ダスティングパウダー等が挙げ
られる。そして、この際の被覆顔料の含有量は、化粧料
の性質に応じて任意に選択され、凡そ3〜95重量%好ま
しくは10〜95重量%である。Therefore, the present invention can be widely applied to make-up cosmetics containing powders, and as the cosmetics provided by the present invention, foundations, lipsticks, blushers, eyeliners, eye shadows, eyebrows, eyebrows, powders Examples include white powder, face powder and dusting powder. The content of the coating pigment at this time is arbitrarily selected according to the properties of the cosmetic, and is about 3 to 95% by weight, preferably 10 to 95% by weight.
ここで、本発明に係る被覆顔料の製造方法について詳細
に述べる。Here, the method for producing the coated pigment according to the present invention will be described in detail.
被覆顔料は、既知の方法、例えば、保湿性高分子物質を
あらかじめ防腐剤を含んだ水溶液に溶解させておき、こ
れに顔料を加えて混合撹拌し均一に分散させ、さらに混
合撹拌を続けながら、これに徐々にエタノール、アセト
ン等の有機溶媒を加えて、粉体表面に保湿性高分子物質
を沈着せしめ、次に、このスラリーより溶媒を留去し、
粗粉砕して被覆顔料を得る方法などにより製造すること
が可能である。The coated pigment is a known method, for example, a moisturizing polymer is dissolved in an aqueous solution containing a preservative in advance, and the pigment is added to this and mixed and stirred to uniformly disperse, while further continuing the mixing and stirring, An organic solvent such as ethanol or acetone is gradually added to this to deposit a moisturizing polymer substance on the powder surface, and then the solvent is distilled off from this slurry,
It can be produced by a method such as coarse pulverization to obtain a coated pigment.
尚、上記の製造方法において、有機溶媒や水などを一切
用いないで粉体と保湿性高分子物質を混合被覆せしめる
方法、すなわち乾式法は被覆が均一になりにくいので好
ましくない。In the above-mentioned production method, the method of mixing and coating the powder and the moisturizing polymer substance without using any organic solvent or water, that is, the dry method is not preferable because the coating is difficult to be uniform.
以下に被覆顔料の製造例を示す。The production example of the coated pigment is shown below.
製造例−1 コンドロイチン硫酸ナトリウム被覆セリサイトの製造 コンドロイチン硫酸ナトリウム50g及びメチルパラベン
2.5gを精製水5に溶解せしめ均一な溶液とし、これに
セリサイト1kgを加え均一に分散するまで十分に撹拌す
る。次に、撹拌を続けながらエタノール5を20分間に
わたり徐々に添加した後、引続き20分間ほど撹拌を続
け、得られたスラリーから遠心脱水機を用いて水及びエ
タノールを除去し、さらに60℃以下の温度で乾燥後、粉
砕してコンドロイチン硫酸ナトリウム被覆セリサイト約
1kgを得る。Production Example-1 Production of sodium chondroitin sulfate-coated sericite 50 g of sodium chondroitin sulfate and methylparaben
2.5 g is dissolved in purified water 5 to make a uniform solution, and 1 kg of sericite is added to this solution, and the mixture is sufficiently stirred until uniformly dispersed. Next, while continuously stirring, ethanol 5 was gradually added over 20 minutes, and then the stirring was continued for about 20 minutes, and water and ethanol were removed from the obtained slurry by using a centrifugal dehydrator. After drying at temperature, pulverize and pulverize sodium chondroitin sulfate coated sericite
Get 1 kg.
製造例−2 エラスチン被覆雲母チタンの製造 可溶性エラスチン100g及びメチルパラベン2.5gを精製水
5に溶解せしめ均一な溶液とし、これに雲母チタン1k
gを加え均一に分散するまで十分に撹拌する。次に、撹
拌を続けながらアセトン2を15分間にわたり徐々に添
加した後、引続き20分間ほど撹拌を続け、得られたスラ
リーから遠心脱水機を用いて水及びアセトンを除去し、
さらに60℃以下の温度で乾燥後、粉砕してエラスチン被
覆雲母チタン約1kgを得る。Production Example-2 Production of Elastin-Coated Titanium Mica 100 g of soluble elastin and 2.5 g of methylparaben are dissolved in purified water 5 to form a uniform solution, and 1 m of titanium mica is added to the solution.
Add g and stir well until uniformly dispersed. Next, while continuously stirring, acetone 2 was gradually added over 15 minutes, and then the stirring was continued for about 20 minutes, and water and acetone were removed from the obtained slurry by using a centrifugal dehydrator.
Further, after drying at a temperature of 60 ° C. or lower, it is pulverized to obtain about 1 kg of elastin-coated titanium mica.
製造例−3 加水分解エラスチン被覆二酸化チタンの製造 水5に二酸化チタン1kgを加えて混合撹拌し、均一に
分散させる。次に、加水分解エラスチン100gを加え均一
になるまで十分に撹拌する。さらに氷冷しながら撹拌を
続け、これにメタノール5をゆっくりと滴下し、引続
き20分間ほど撹拌を続け、粉体表面に加水分解エラスチ
ンを吸着させ、その後ろ過し、さらに50℃で乾燥するこ
とにより加水分解エラスチン被覆二酸化チタン約1kgを
得た。Production Example-3 Production of Hydrolyzed Elastin-Coated Titanium Dioxide 1 kg of titanium dioxide is added to water 5 and mixed and stirred to uniformly disperse. Next, 100 g of hydrolyzed elastin is added, and the mixture is thoroughly stirred until uniform. Continue stirring with ice cooling, slowly add methanol 5 to it, continue stirring for about 20 minutes, adsorb hydrolyzed elastin on the powder surface, then filter and dry at 50 ° C. About 1 kg of hydrolyzed elastin-coated titanium dioxide was obtained.
製造例−4 加水分解エラスチン被覆二酸化チタンの製造 水3に加水分解エラスチン10gを加え、十分に撹拌
し、溶解せしめ均一な溶液とし、これに二酸化チタン1k
gを加えて混合撹拌し、均一に分散させる。次に、さら
に氷冷しながら撹拌を続け、これにメタノール4をゆ
っくりと滴下し、引続き20分間ほど撹拌を続け、粉体表
面に加水分解エラスチンを吸着させ、その後ろ過し、さ
らに50℃で乾燥することにより加水分解エラスチン被覆
二酸化チタン約1kgを得た。Production Example-4 Production of Hydrolyzed Elastin-Coated Titanium Dioxide 10 g of hydrolyzed elastin was added to water 3, stirred well and dissolved to obtain a uniform solution.
Add g, mix and stir, and disperse uniformly. Next, continue to stir while cooling with ice, slowly add methanol 4 dropwise to it, and continue stirring for about 20 minutes to adsorb hydrolyzed elastin on the powder surface, then filter and dry at 50 ° C. By doing so, about 1 kg of hydrolyzed elastin-coated titanium dioxide was obtained.
<評価試験> 次に、本発明の化粧料(後述する実施例1〜2の化粧
料)について、その優秀性を証明する為、官能評価を行
ない結果を表−1に示した。このとき対照品として各々
の化粧料について本発明に用いる被覆顔料の代りに被覆
処理をしていない顔料(被覆顔料の内芯物質)を配合し
たものを調製し、官能評価した。<Evaluation Test> Next, in order to prove the superiority of the cosmetics of the present invention (cosmetics of Examples 1 and 2 described later), sensory evaluation was performed and the results are shown in Table 1. At this time, as a control product, each cosmetic was prepared by blending an uncoated pigment (inner core substance of the coated pigment) instead of the coated pigment used in the present invention, and sensory-evaluated.
試験方法は下記の通りである。The test method is as follows.
官能テスト: 男女混合計10名のパネラーにより官能評価項目として化
粧持続性、肌への付着性、皮膚上での伸びのなめらか
さ、かさつき感の4項目について下記のような評価基準
において評価し、10名の平均値を評価点とした。Sensory test: A panel of 10 men and women mixed together evaluated the following 4 items as sensory evaluation items: makeup sustainability, skin adhesion, smoothness on the skin, and a feeling of bulkiness. The average value of 10 persons was used as the evaluation point.
以上の如く本発明の化粧料は皮膚上に塗布した場合に、
化粧持続性に優れており、肌への付着性、皮膚上での伸
びのなめらかさ、かさつき感などの官能特性にも優れて
いる。又、その安全性の高さをも考え合わせると、本発
明に係る被覆顔料は従来の化粧品用顔料には見られない
優れた特性を有する粉体であることがわかる。 As described above, when the cosmetic of the present invention is applied on the skin,
It has excellent makeup durability, and also has excellent sensory characteristics such as adhesion to the skin, smoothness of growth on the skin, and a feeling of bulkiness. Also, considering the high level of safety, it can be seen that the coated pigment according to the present invention is a powder having excellent properties not found in conventional cosmetic pigments.
<実 施 例> 次に本発明の実施例を示す。<Examples> Next, examples of the present invention will be described.
実施例−1 パウダーファンデーション 重量部 (A)製造例−1のコンドロイチン硫酸ナトリウム被覆
セリサイト 66.5 製造例−2と同様に作られたエラスチン被覆タルク10.0 ヒアルロン酸ナトリウム被覆二酸化チタン 8.0 黄酸化鉄 5.0 弁 柄 2.0 スクワラン 5.0 (B)メチルポリシロキサン 3.0 エチルパラベン 0.2 香 料 0.3 (製法) 上記(A)の処方物をヘンシェルミキサーで均一に混合
し、粉砕機で粉砕する。これに上記(B)の処方物を加
えヘンシェルミキサーで均一に混合し、粉砕機で粉砕
し、中皿にプレスして製品とする。Example-1 Powder foundation (parts by weight) (A) Sodium chondroitin sulfate-coated sericite of Production Example-1 66.5 Elastin-coated talc prepared in the same manner as in Production Example-2 10.0 Sodium hyaluronate-coated titanium dioxide 8.0 Yellow iron oxide 5.0 Valve handle 2.0 Squalane 5.0 (B) Methyl polysiloxane 3.0 Ethyl paraben 0.2 Perfume 0.3 (Production method) The formulation of (A) above is uniformly mixed with a Henschel mixer and ground with a grinder. The above-mentioned formulation (B) is added thereto, and the mixture is uniformly mixed with a Henschel mixer, pulverized with a pulverizer, and pressed into a medium plate to obtain a product.
実施例−2 ケーキ状アイカラー 重量部 (A)ヒアルロン酸ナトリウム被覆タルク 46.5 カオリン 5.0 ステアリン酸亜鉛 3.5 製造例−4の加水分解エラスチン被覆二酸化チタン18.0 黒酸化鉄 4.0 弁 柄 10.0 雲母チタン 8.0 ミツロウ 1.5 (B)セタノール 0.8 流動パラフィン 2.5 (C)香 料 0.2 (製法) 上記(A)の処方物を高速混合機(ヘンシェル型ミキサ
ー)にて2分間高速混合後、粉砕機にて粉砕、混合す
る。このものを80℃にて上記(B)の処方物をヘンシェ
ルミキサー中で5分間低速混合し、20℃に冷却後、上記
(C)の香料を加えて2分間低速混合する。このものを
粉砕機にて粉砕後とり出して、プレスする。Example-2 Cake-like eye color (parts by weight) (A) Sodium hyaluronate-coated talc 46.5 Kaolin 5.0 Zinc stearate 3.5 Hydrolyzed elastin-coated titanium dioxide 18.0 of Production Example-4 Black iron oxide 4.0 Valve pattern 10.0 Mica titanium 8.0 Beeswax 1.5 ( B) Cetanol 0.8 Liquid paraffin 2.5 (C) Perfume 0.2 (Production method) The formulation of (A) above is mixed at high speed with a high speed mixer (Henschel type mixer) for 2 minutes, and then crushed and mixed with a crusher. This is mixed at 80 ° C. with the formulation of (B) at low speed in a Henschel mixer for 5 minutes, cooled to 20 ° C., the flavor of (C) is added, and the mixture is mixed at low speed for 2 minutes. This product is crushed by a crusher, then taken out and pressed.
実施例−3 チークカラー 重量部 (A)製造例−2のエラスチン被覆雲母チタン 25 ヒアルロン酸ナトリウム被覆タルク 44.6 ナイロンパウダー 10 黄酸化鉄 6 弁 柄 3 (B)メチルポリシロキサン 4 メチルパラベン 0.2 スクワラン 7 香 料 0.2 (製法) 上記(A)の処方物をヘンシェルミキサーで均一に混合
し、粉砕機で粉砕する。これに上記(B)の処方物を加
えヘンシェルミキサーで均一に混合粉砕、混合する。こ
のものを70℃にて上記(B)の処方物とヘンシェルミキ
サー中で5分間低速混合し、20℃に冷却後、上記(C)
の香料を加えて2分間低速混合する。このものを粉砕機
にて粉砕後とり出して、プレスする。Example-3 Teak color parts by weight (A) Elastin-coated titanium mica of Production Example-2 25 Sodium hyaluronate-coated talc 44.6 Nylon powder 10 Iron yellow oxide 6 Valve handle 3 (B) Methylpolysiloxane 4 Methylparaben 0.2 Squalane 7 Fragrance 0.2 (Production Method) The formulation of (A) above is uniformly mixed with a Henschel mixer and pulverized with a pulverizer. The above-mentioned formulation (B) is added to this, and uniformly mixed and pulverized by a Henschel mixer and mixed. This was slowly mixed with the formulation of (B) above at 70 ° C for 5 minutes in a Henschel mixer, and after cooling to 20 ° C, (C) above.
Add perfume and mix gently for 2 minutes. This product is crushed by a crusher, then taken out and pressed.
実施例−4 ファンデーション 重量部 (A)製造例−1のコンドロイチン硫酸ナトリウム被覆
セリサイト 25 ヒアルロン酸ナトリウム被覆タルク 25 製造例−2のエラスチン被覆雲母チタン 15 製造例−3の加水分解エラスチン被覆二酸化チタン 9 黄酸化鉄 3 弁 柄 0.8 黒酸化鉄 0.3 メチルパラベン 0.2 (B)スクワラン 10 オレイン酸オクチルドデシル 5 香 料 0.3 (製法) 実施例−1と同様にして製造した。Example-4 Foundation parts by weight (A) Sodium chondroitin sulfate-coated sericite 25 of Production Example-1 25 Talc coated with sodium hyaluronate 25 Elastin-coated titanium mica of Production Example-2 15 Hydrolyzed elastin-coated titanium dioxide of Production Example-3 9 Yellow iron oxide 3 Rouge 0.8 Black iron oxide 0.3 Methylparaben 0.2 (B) Squalane 10 Octyldodecyl oleate 5 Perfume 0.3 (Production method) Production was carried out in the same manner as in Example-1.
実施例−5 ダスティングパウダー 重量部 (A)製造例−1のコンドロイチン硫酸ナトリウム被覆
セリサイト 25 製造例−4の加水分解エラスチン被覆二酸化チタン17 製造例−4と同様にして製造された加水分解エラスチン
被覆タルク 50 (B)スクワラン 7.7 香 料 0.3 (製法) 上記(A)及び(B)の処方物をヘンシェルミキサーで
均一に混合し、粉砕機で粉砕して製品とする。Example-5 Dusting powder parts by weight (A) Sodium chondroitin sulfate-coated sericite of Production Example-1 25 Hydrolyzed elastin-coated titanium dioxide of Production Example-4 17 Hydrolyzed elastin coating produced in the same manner as Production Example-4. Talc 50 (B) Squalane 7.7 Fragrance 0.3 (Production Method) The formulations of (A) and (B) above are uniformly mixed with a Henschel mixer and ground with a grinder to obtain a product.
Claims (2)
チン加水分解物及びこれらのアルカリ金属塩から選択さ
れる保湿性高分子物質の少なくとも1種以上により顔料
表面を被覆して得られる被覆顔料を含有するメークアッ
プ化粧料。1. A make-up containing a coated pigment obtained by coating the surface of a pigment with at least one moisturizing polymer selected from chondroitin sulfate, elastin, hydrolyzate of elastin and alkali metal salts thereof. Cosmetics.
料全重量中3〜95%であることを特徴とする特許請求の
範囲第1)項記載のメークアップ化粧料。2. The makeup cosmetic according to claim 1), wherein the content of the coating pigment is 3 to 95% of the total weight of the makeup cosmetic.