JPH07266764A - Medium having security function - Google Patents
Medium having security functionInfo
- Publication number
- JPH07266764A JPH07266764A JP6063237A JP6323794A JPH07266764A JP H07266764 A JPH07266764 A JP H07266764A JP 6063237 A JP6063237 A JP 6063237A JP 6323794 A JP6323794 A JP 6323794A JP H07266764 A JPH07266764 A JP H07266764A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- recording layer
- medium
- security function
- card
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、高度なセキュリティ性
を要求されるカード等の媒体に係り、特にその媒体自体
が本物であるかどうかの真偽判別を即座に行なえるよう
にしたセキュリティ機能を有する媒体に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a medium, such as a card, which is required to have a high level of security, and in particular, a security function which can immediately determine whether or not the medium itself is genuine. The present invention relates to a medium having.
【０００２】[0002]
【従来の技術】近年、株券・債券・小切手・通帳・宝ク
ジ・乗車券・回数券・定期券等の証券類の他、ＩＤカー
ド、クレジットカード、キャッシュカード、ギフトカー
ド等のプラスチックカード、テレホンカードに代表され
るプリペイドカードといった金券に代わる証券関連商品
の発展はめざましいものがあり、必然的に、それらの偽
造を効果的に防止する方法、および容易にそれらの真偽
の判別を行なえる技術の重要性が非常に高まってきてい
る。2. Description of the Related Art Recently, securities such as stock certificates, bonds, checks, passbooks, treasure lottery tickets, boarding tickets, coupons, commuter passes, etc., plastic cards such as ID cards, credit cards, cash cards, gift cards, telephones The development of securities-related products such as prepaid cards, which are typified by cards, as an alternative to cash vouchers is remarkable, and inevitably, a method of effectively preventing their forgery and a technology that can easily discriminate their authenticity. Is becoming very important.
【０００３】そして、従来から、このようなセキュリテ
ィ性を目的としたカード自体の真偽の判別方法として
は、カードに設けられた磁気記録層に記録された磁気情
報やバーコードデータ等のデータ内容を確認する方法、
あるいはカードに施された印刷画像やホログラム等の意
匠情報による外観を確認する方法等が、一般に知られて
きている。Conventionally, as a method of discriminating the authenticity of the card itself for the purpose of such security, data contents such as magnetic information and bar code data recorded on a magnetic recording layer provided on the card are used. How to check,
Alternatively, a method of confirming the appearance by design information such as a printed image or a hologram provided on a card has been generally known.
【０００４】ところで、このような磁気記録層を用いた
記録方式では、磁気ヘッドを用いて磁気記録層上に磁気
データを書き込みまたは読み取りを行なうことによっ
て、そのカードの有効性を判別するが、磁気記録方式で
は、磁気記録層に磁石等を近付けると、記録されていた
磁気情報が消失するという問題点がある。In the recording method using such a magnetic recording layer, the validity of the card is determined by writing or reading magnetic data on the magnetic recording layer using a magnetic head. The recording method has a problem that when a magnet or the like is brought close to the magnetic recording layer, the recorded magnetic information is lost.
【０００５】従って、記録情報の消失したカードを提示
された場合、あるいは磁気情報を改竄したカードを提示
された場合等には、その提示されたカードが本物である
のかどうかの真偽判別を行なうことが非常に難しいとい
う問題がある。Therefore, when a card in which recorded information is lost is presented or a card in which magnetic information is falsified is presented, it is determined whether or not the presented card is genuine. The problem is that it is very difficult.
【０００６】また、バーコードや印刷画像等を用いた方
法においては、近年におけるコピー機や簡易写真製版技
術等の向上、一般化に伴ない、比較的容易に偽造するこ
とが可能となってきているという問題がある。Further, in the method using a bar code, a printed image, etc., it has become possible to forge relatively easily with the improvement and generalization of copying machines and simple photoengraving technology in recent years. There is a problem that
【０００７】さらに、ホログラム画像等を用いた方法に
おいても、金属箔上に透明インキで絵柄を印刷し、一見
あたかもホログラム画像のように見せる偽造技術等も出
てきており、必ずしも有効な手段であるとは言えなくな
ってきているのが実情である。Further, even in the method using a hologram image or the like, a forgery technique or the like in which a pattern is printed on a metal foil with a transparent ink to make it look like a hologram image has come out, and it is not always an effective means. The reality is that it cannot be said that.
【０００８】[0008]
【発明が解決しようとする課題】以上のように、従来の
カード等の媒体においては、媒体自体が本物であるかど
うかの真偽判別を行なうのが困難であるという問題があ
った。As described above, in the conventional medium such as a card, it is difficult to determine whether the medium itself is genuine or not.
【０００９】本発明は、上記のような問題点を解消する
ために成されたもので、媒体自体が本物であるかどうか
の真偽判別を即座にしかも比較的容易に行ない、磁気記
録情報等の消失や改竄に対して有効にかつ素早く対応す
ることが可能なセキュリティ機能を有する媒体を提供す
ることにある。The present invention has been made in order to solve the above-mentioned problems, and makes a genuine / counterfeit judgment as to whether the medium itself is genuine or not immediately and relatively easily. An object of the present invention is to provide a medium having a security function capable of effectively and quickly responding to the disappearance and tampering of data.
【００１０】[0010]
【課題を解決するための手段】上記の目的を達成するた
めに、まず、請求項１に係る発明のセキュリティ機能を
有する媒体は、支持体上に、金属反射層、識別層、書き
替え可能な感熱記録層を、順次積層して成る。In order to achieve the above object, first, a medium having a security function of the invention according to claim 1 is provided with a metal reflection layer, an identification layer, and a rewritable medium on a support. The thermosensitive recording layers are sequentially laminated.
【００１１】また、請求項２に係る発明のセキュリティ
機能を有する媒体は、上記請求項１に係る発明のセキュ
リティ機能を有する媒体において、支持体上の各積層構
造物と反対側の面上、あるいは当該各積層構造物と同一
側の面上に、磁気記録層を設けて成る。Further, the medium having the security function of the invention according to claim 2 is the medium having the security function of the invention according to claim 1 above, on the surface opposite to each laminated structure on the support, or A magnetic recording layer is provided on the same surface as each laminated structure.
【００１２】ここで、特に上記書き替え可能な感熱記録
層としては、樹脂母材と、当該樹脂母材中に分散された
有機低分子物質とを主成分とし、温度に依存してその透
明度が可逆的に変化するものとする。In particular, the rewritable heat-sensitive recording layer is mainly composed of a resin base material and an organic low molecular weight substance dispersed in the resin base material, and its transparency depends on temperature. It shall change reversibly.
【００１３】また、上記識別層としては、文字、記号、
絵柄、あるいは、バーコードによる印刷層とする。As the identification layer, characters, symbols,
A print layer with a picture or bar code.
【００１４】さらに、上記識別層としては、白色とす
る。Further, the discrimination layer is white.
【００１５】[0015]
【作用】従って、本発明のセキュリティ機能を有する媒
体においては、書き替え可能な感熱記録層と金属反射層
との間に印刷層等からなる識別層を設け、この識別層を
特に白色インキを用いて設けることにより、通常の状態
では、感熱記録層を白濁状態に維持し、この媒体の真偽
判別を行なう際に、例えばＴ2 以上の温度を感熱記録層
に加えて、半濁状態になった時点で、感熱記録層の下に
設けられた識別層の情報（例えば、バーコード情報）を
読み取ることができる。Therefore, in the medium having the security function of the present invention, an identification layer made of a printing layer or the like is provided between the rewritable heat-sensitive recording layer and the metal reflection layer, and this identification layer is formed by using a white ink. In the normal state, the heat-sensitive recording layer is maintained in a cloudy state, and when determining whether the medium is true or false, for example, a temperature of T 2 or higher is added to the heat-sensitive recording layer to form a semi-turbid state. At that time, the information (for example, bar code information) in the identification layer provided under the thermal recording layer can be read.
【００１６】その後、感熱記録層をＴ0 以下の温度に冷
却すると、媒体がリーダーライターから出てきた時に
は、感熱記録層は元のように白濁状態、すなわちその光
散乱性が増大して最大遮光状態になっており、通常の状
態では、感熱記録層の下に記載された識別層の情報を判
読することはできないため、磁気情報等だけでは不十分
な媒体の真偽判別に対して、高度なセキュリティ機能を
付与することができる。After that, when the heat-sensitive recording layer is cooled to a temperature of T 0 or lower, when the medium comes out of the reader / writer, the heat-sensitive recording layer is in an opaque state as before, that is, its light-scattering property is increased and maximum light shielding is performed. In the normal state, it is not possible to read the information of the identification layer written under the thermal recording layer under normal conditions. Security functions can be added.
【００１７】これにより、媒体自体が本物であるかどう
かの真偽判別を即座にしかも比較的容易に行なうことが
できるため、磁気記録情報等の消失や改竄に対して有効
にかつ素早く対応することができるものとなる。As a result, since it is possible to determine whether the medium itself is genuine or not immediately and relatively easily, it is possible to effectively and quickly deal with the loss or alteration of the magnetic recording information. Will be possible.
【００１８】[0018]
【実施例】以下、本発明の一実施例について図面を参照
して詳細に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be described in detail below with reference to the drawings.
【００１９】（第１の実施例）図１は、本発明の第１の
実施例に係るセキュリティ機能を有するカードの構成例
を示す断面図である。(First Embodiment) FIG. 1 is a sectional view showing a structural example of a card having a security function according to the first embodiment of the present invention.
【００２０】すなわち、図１に示すように、本実施例の
カード１は、支持体１１上に、金属反射層１２、識別層
であるバーコード印刷層１３、書き替え可能な感熱記録
層１４、および保護層１５を、順次積層した構成として
いる。That is, as shown in FIG. 1, the card 1 of this embodiment comprises a support 11, a metal reflection layer 12, a bar code print layer 13 as an identification layer, a rewritable heat-sensitive recording layer 14, The protective layer 15 and the protective layer 15 are sequentially laminated.
【００２１】ここで、支持体１１としては、例えば紙、
あるいはポリエチレン、ポリプロピレン、ポリエステ
ル、スチレン等のプラスチックからなる合成紙を用いる
ことができる。Here, as the support 11, for example, paper,
Alternatively, synthetic paper made of plastic such as polyethylene, polypropylene, polyester, styrene can be used.
【００２２】また、金属反射層１２としては、真空蒸着
等の手段で製造可能な、例えばアルミニウム、錫、銀、
銅、マグネシウム、クロム、ニッケル等の金属を用いる
ことができる。Further, the metal reflection layer 12 can be manufactured by means such as vacuum deposition, and is made of, for example, aluminum, tin, silver,
Metals such as copper, magnesium, chromium and nickel can be used.
【００２３】さらに、バーコード印刷層１３としては、
例えば通常の印刷インキを用いて、通常の印刷手法によ
りバーコード情報を印刷して形成することができる。本
例では、白色の印刷インキを用いて、バーコード情報を
形成している。Further, as the bar code printing layer 13,
For example, it is possible to form the bar code information by printing the bar code information by using an ordinary printing method using an ordinary printing ink. In this example, white printing ink is used to form the bar code information.
【００２４】また、保護層１５としては、耐熱性を有す
る材料により形成することができる。The protective layer 15 can be formed of a heat resistant material.
【００２５】さらに、感熱記録層１４としては、樹脂母
材と、この樹脂母材中に分散された有機低分子物質とを
主成分とし、温度に依存してその透明度が可逆的に変化
する感熱記録層であり、この感熱記録層１４の光散乱性
が温度に依存して可逆的に変化する性質を巧みに利用し
て構成しているものである。Further, the heat-sensitive recording layer 14 is mainly composed of a resin base material and an organic low molecular weight substance dispersed in the resin base material, and the transparency thereof reversibly changes depending on temperature. This is a recording layer, and is constructed by skillfully utilizing the property that the light scattering property of the thermosensitive recording layer 14 reversibly changes depending on temperature.
【００２６】すなわち、この感熱記録層１４は、室温近
傍の特定温度Ｔ0 よりも高い温度に、２つの状態転移温
度Ｔ1 ，Ｔ2 （但しＴ1 ＜Ｔ2 ）を有しており、感熱記
録層１４をＴ2 以上に加熱しかつ保持した後にＴ0 以下
に冷却すると白濁し、その光散乱性が増大して最大遮光
状態となる一方、この白濁状態にある感熱記録層１４を
Ｔ1 以上Ｔ2 未満に加熱しかつ保持した後にＴ0 以下に
冷却すると、その光散乱性が減少して透明状態になるも
のである。That is, the thermosensitive recording layer 14 has two state transition temperatures T 1 and T 2 (provided that T 1 <T 2 ) at a temperature higher than the specific temperature T 0 near room temperature. while the recording layer 14 becomes cloudy upon cooling to T 0 or less after heating and held at T 2 or more, the maximum shielding state that the light scattering is increased, the heat-sensitive recording layer 14 in this opaque state T 1 When it is heated to less than T 2 and held, and then cooled to T 0 or less, its light scattering property is reduced and it becomes a transparent state.
【００２７】しかも、これらＴ1 とＴ2 の温度幅は任意
に設定することができ、この温度幅が極めて狭く、透明
状態を維持することが殆ど困難な状態にすることも可能
であると同時に、この場合でもＴ2 以上の温度に加熱し
た時には、感熱記録層１４が半濁状態となるものであ
る。Moreover, the temperature range of these T 1 and T 2 can be set arbitrarily, and the temperature range is extremely narrow, and it is possible to make it almost difficult to maintain the transparent state. Even in this case, the heat-sensitive recording layer 14 becomes semi-turbid when heated to a temperature of T 2 or higher.
【００２８】一方、感熱記録層１４の一部を構成する樹
脂材料としては、以下に述べる有機低分子物質とその屈
折率が近似しかつ相溶性がないと共に機械的強度に優れ
しかもフィルム形成能を有する透明性良好な熱可塑性樹
脂、あるいは熱硬化性樹脂を用いることができる。On the other hand, as a resin material which constitutes a part of the heat-sensitive recording layer 14, the organic low-molecular substance described below has a refractive index close to that of the organic material and is not compatible with each other and is excellent in mechanical strength and has a film forming ability. A thermoplastic resin having good transparency or a thermosetting resin can be used.
【００２９】その具体的な例としては、例えば飽和共重
合ポリエステル等のポリエステル樹脂、ポリ塩化ビニル
樹脂、塩化ビニル−酢酸ビニル共重合体、塩化ビニル−
酢酸ビニル−ビニルアルコール共重合体、塩化ビニル−
酢酸ビニル−マレイン酸共重合体、塩化ビニル−アクリ
レート共重合体等の塩化ビニル共重合体；ポリウレタン
樹脂；ポリカーボネート樹脂；ポリ塩化ビニリデン樹
脂；塩化ビニリデン−塩化ビニル共重合体、塩化ビニリ
デン−アクリロニトリル共重合体等の塩化ビニリデン共
重合体；天然ゴム、合成ゴム等のゴム系；ポリアミド樹
脂；シリコーン樹脂；ポリアクリレートもしくはポリメ
タクリレート樹脂またはこれらの共重合体；ポリエチレ
ン樹脂等があり、これら単独あるいは２種以上混合して
適用することができる。Specific examples thereof include polyester resins such as saturated copolyester, polyvinyl chloride resin, vinyl chloride-vinyl acetate copolymer, vinyl chloride-
Vinyl acetate-vinyl alcohol copolymer, vinyl chloride-
Vinyl acetate-maleic acid copolymer, vinyl chloride-acrylate copolymer and other vinyl chloride copolymers; polyurethane resin; polycarbonate resin; polyvinylidene chloride resin; vinylidene chloride-vinyl chloride copolymer, vinylidene chloride-acrylonitrile copolymer Vinylidene chloride copolymers such as coalescing; rubbers such as natural rubber and synthetic rubber; polyamide resins; silicone resins; polyacrylate or polymethacrylate resins or copolymers thereof; polyethylene resins, etc., and these are used alone or in combination of two or more. It can be mixed and applied.
【００３０】また、上記樹脂材料中に分散される有機低
分子としては、例えば脂肪酸もしくは脂肪酸誘導体、ま
たは脂環式有機酸等を用いることができ、さらに詳しく
は、飽和もしくは不飽和のモノあるいはジカルボン酸、
またはこれらのエステル、アミド等を含むものを用いる
ことができる。As the organic low molecule dispersed in the resin material, for example, a fatty acid or a fatty acid derivative, an alicyclic organic acid or the like can be used. More specifically, a saturated or unsaturated mono- or dicarboxylic acid can be used. acid,
Alternatively, those containing these esters, amides and the like can be used.
【００３１】そして、上記飽和脂肪酸の具体的な例とし
ては、例えばウンデカン酸、ラウリン酸、ミリスチン
酸、ペンタデカン酸、パルミチン酸、ヘプタデカン酸、
ステアリン酸、ナノデカン酸、アラキン酸、ベヘン酸、
リグノセリン酸、セロチン酸、モンタン酸、メリシン
酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン
酸、セバシン酸、１−，９−ノナメチレンジカルボン
酸、１−，１０−デカメチレンジカルボン酸、１−，１
１−ウンデカメチレンジカルボン酸、１−，２−シクロ
ブタンジカルボン酸、１−，２−シクロペンタジカルボ
ン酸、１−，３−シクロペンタンジカルボン酸、１−，
２−シクロヘキサンジカルボン酸、１−，４−シクロヘ
キサンジカルボン酸等を適用することができる。Specific examples of the saturated fatty acid include undecanoic acid, lauric acid, myristic acid, pentadecanoic acid, palmitic acid, heptadecanoic acid,
Stearic acid, nanodecanoic acid, arachidic acid, behenic acid,
Lignoceric acid, cerotic acid, montanic acid, melissic acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, 1-, 9-nonamethylenedicarboxylic acid, 1-, 10-decamethylenedicarboxylic acid, 1-, 1
1-undecamethylenedicarboxylic acid, 1-, 2-cyclobutanedicarboxylic acid, 1-, 2-cyclopentadicarboxylic acid, 1-, 3-cyclopentanedicarboxylic acid, 1-,
2-Cyclohexanedicarboxylic acid, 1-, 4-cyclohexanedicarboxylic acid or the like can be applied.
【００３２】なお、脂肪酸もしくは脂肪酸誘導体または
脂環式有機酸としては、これらのものに限定されるもの
ではなく、かつこれらのうちの一種類または二種類以上
を混合させて適用することも可能である。The fatty acid or fatty acid derivative or alicyclic organic acid is not limited to these, and it is also possible to apply one kind or a mixture of two or more kinds thereof. is there.
【００３３】（具体例１）下記のような配合比により、
あらかじめ感熱記録層塗液を作成しておき、支持体１１
として透明なＰＥＴフィルム（厚さ：１８０μｍ）上
に、金属反射層１２としてアルミ蒸着を施し、この上に
バーコード印刷層１３として白色インキでバーコードを
印刷し、この上に上記感熱記録層塗液の塗工を行なっ
て、厚さ約１５μｍの感熱記録層１４を形成した。(Specific Example 1) By the following compounding ratio,
The thermosensitive recording layer coating liquid is prepared in advance, and the support 11
On the transparent PET film (thickness: 180 μm) as the metal reflection layer 12 is vapor-deposited with aluminum, and a bar code is printed thereon with a white ink as a bar code printing layer 13, and the heat-sensitive recording layer is coated thereon. The liquid was applied to form a thermosensitive recording layer 14 having a thickness of about 15 μm.
【００３４】さらに、この感熱記録層１４上に、テフロ
ン粒子を樹脂に対して０．１％〜１０．０％との間（望
ましくは２．０％）で添加した紫外線硬化樹脂を塗工
し、厚さ約２．５μｍの保護層１５を設けて、セキュリ
ティ機能を有するカード１を作成した。Further, an ultraviolet curable resin containing Teflon particles added to the resin in an amount of 0.1% to 10.0% (preferably 2.0%) is applied on the heat-sensitive recording layer 14. A card 1 having a security function was prepared by providing a protective layer 15 having a thickness of about 2.5 μm.
【００３５】 （感熱記録層塗液の構成） ベヘン酸 １．０重量部 エスレックＡ（積水化学製） ２．０重量部 イソシアネート ０．２重量部 テトラヒドロフラン １０．０重量部 次に、以上のように構成した本実施例のカード１におい
ては、書き替え可能な感熱記録層１４と金属反射層１２
との間に、識別層としてバーコード印刷層１３を設け、
このバーコード印刷層１３を特に白色インキを用いて設
けていることにより、通常の状態では、感熱記録層１４
を白濁状態に維持し、このカード１の真偽判別を行なう
際に、例えばＴ2 以上の温度を感熱記録層１４に加え
て、半濁状態になった時点で、感熱記録層１４の下に設
けられたバーコード印刷層１３の情報（バーコード情
報）を、目視または装置によって読み取ることができ
る。(Structure of coating liquid for thermosensitive recording layer) Behenic acid 1.0 part by weight S-REC A (manufactured by Sekisui Chemical Co., Ltd.) 2.0 parts by weight Isocyanate 0.2 parts by weight Tetrahydrofuran 10.0 parts by weight Next, as described above In the constructed card 1 of this embodiment, the rewritable heat-sensitive recording layer 14 and the metal reflection layer 12 are rewritable.
And a bar code printing layer 13 as an identification layer,
Since the bar code printing layer 13 is provided by using a white ink, the thermal recording layer 14 is normally used.
Is maintained in the cloudy state, and when the authenticity of the card 1 is determined, for example, a temperature of T 2 or more is applied to the heat-sensitive recording layer 14 and when the semi-cloudy state is reached, the temperature is below the heat-sensitive recording layer 14. The information (barcode information) on the provided barcode printing layer 13 can be read visually or by a device.
【００３６】その後、感熱記録層１４をＴ0 以下の温度
に冷却すると、カード１がリーダーライターから出てき
た時には、感熱記録層１４は元のように白濁状態、すな
わちその光散乱性が増大して最大遮光状態になってお
り、通常の状態では、感熱記録層１４の下に記載された
バーコード印刷層１３の情報を判読することはできない
ため、磁気情報等だけでは不十分な媒体の真偽判別に対
して、高度なセキュリティ機能を付与することができ
る。After that, when the heat-sensitive recording layer 14 is cooled to a temperature of T 0 or lower, when the card 1 comes out of the reader / writer, the heat-sensitive recording layer 14 is opaque as in the original state, that is, its light scattering property is increased. In the normal state, the information in the bar code printing layer 13 written under the thermal recording layer 14 cannot be read, so that the magnetic information alone is not enough to detect the true content of the medium. A high security function can be added to the false discrimination.
【００３７】この時、感熱記録層１４の下に設けられた
バーコード印刷層１３は、白色としていることにより、
感熱記録層１４が白濁してその光散乱性が増大して最大
遮光状態となった時に、バーコード印刷層１３に示され
ている内容が、より判読しずらい状態となる。At this time, since the bar code print layer 13 provided under the heat sensitive recording layer 14 is white,
When the heat-sensitive recording layer 14 becomes cloudy and its light scattering property increases to reach the maximum light blocking state, the contents shown in the barcode printing layer 13 become more difficult to read.
【００３８】すなわち、より具体的には、通常時は感熱
記録層１４は白濁状態にあり、熱板またはサーマルヘッ
ドやレーザー光線、ヒーター等により、例えば摂氏８５
度以上の温度に加熱されることによって、感熱記録層１
４は半濁状態となり、感熱記録層１４の下に設けられた
それまで見ることのできなかったバーコード印刷層１３
のバーコード情報を判読することができるようになり、
一方判読完了時に、このカード１を室温近傍の適宜温度
以下に冷却することによって、感熱記録層１４は元の白
濁状態に戻り、感熱記録層１４の下に設けられたバーコ
ード印刷層１３のバーコード情報は、再び見ることがで
きなくなる。That is, more specifically, the heat-sensitive recording layer 14 is normally in a cloudy state under normal conditions, and the heat-sensitive recording layer 14 is heated to, for example, 85 degrees Celsius by a heat plate, a thermal head, a laser beam, a heater or the like.
The heat-sensitive recording layer 1 is heated by heating to a temperature of 1 degree or higher.
4 is in a semi-turbid state, and the bar code printing layer 13 provided under the thermosensitive recording layer 14 was invisible until then.
It becomes possible to read the barcode information of
On the other hand, when the reading is completed, by cooling the card 1 to an appropriate temperature near room temperature or lower, the thermosensitive recording layer 14 returns to the original white turbid state, and the bar of the bar code printing layer 13 provided under the thermosensitive recording layer 14 is returned. The code information will not be visible again.
【００３９】このような特性を利用することにより、磁
気情報が消失または改竄されたカード、あるいはコピー
ないし写真製版技術等により外観上の類似性を備えたカ
ードにおいて、そのカード自体が本物であるかどうかの
真偽判別を即座に行なうことができる。By utilizing such characteristics, in a card in which magnetic information is lost or tampered with, or a card having a similar appearance by copying or photoengraving technology, is the card itself genuine? Whether it is true or false can be immediately discriminated.
【００４０】上述したように、本実施例のカード１は、
支持体１１上に、金属反射層１２、識別層である白色の
バーコード印刷層１３、書き替え可能な感熱記録層１
４、および保護層１５を、順次積層して構成したもので
ある。As described above, the card 1 of this embodiment is
On the support 11, a metal reflective layer 12, a white bar code printed layer 13 as an identification layer, a rewritable thermal recording layer 1
4 and the protective layer 15 are sequentially laminated.
【００４１】従って、従来のカードでは十分ではなかっ
たカード自体の真偽判定、すなわちカード自体が本物で
あるかどうかの真偽判別を即座にしかも比較的容易に行
なうことができ、磁気記録情報等の消失や改竄（磁気情
報が消失または改竄されたカード、あるいはコピーない
し写真製版技術等により外観上の類似性を備えたカー
ド）に対して、有効にかつ素早く対応することが可能と
なる。Therefore, the authenticity of the card itself, which is not sufficient with the conventional card, that is, the authenticity of the card itself, can be determined immediately and relatively easily. Can be effectively and swiftly dealt with against the disappearance or tampering of a card (a card whose magnetic information has been lost or tampered with, or a card having a similarity in appearance due to copying or photomechanical technology).
【００４２】これにより、近年増加の傾向にあるカード
犯罪に対して、有効な歯止め策を提供することができ
る。As a result, it is possible to provide an effective stopping measure against card crimes, which has been increasing in recent years.
【００４３】（第２の実施例）図２は、本発明の第２の
実施例に係るセキュリティ機能を有するカードの構成例
を示す断面図である。(Second Embodiment) FIG. 2 is a sectional view showing a structural example of a card having a security function according to a second embodiment of the present invention.
【００４４】すなわち、図２に示すように、本実施例の
カード２は、支持体２１上に、金属反射層２２、識別層
である絵柄印刷層２３、書き替え可能な感熱記録層２
４、および保護層２５を、順次積層した構成としてい
る。That is, as shown in FIG. 2, in the card 2 of this embodiment, a metal reflection layer 22, a pattern printing layer 23 as an identification layer, and a rewritable heat-sensitive recording layer 2 are provided on a support 21.
4 and the protective layer 25 are sequentially laminated.
【００４５】ここで、支持体２１、金属反射層２２、絵
柄印刷層２３、感熱記録層２４、保護層２５としては、
前述した第１の実施例における支持体１１、金属反射層
１２、バーコード印刷層１３、感熱記録層１４、保護層
１５と同様に形成することができる。Here, as the support 21, the metal reflection layer 22, the pattern printing layer 23, the heat-sensitive recording layer 24, and the protective layer 25,
It can be formed in the same manner as the support 11, the metal reflection layer 12, the bar code printed layer 13, the heat-sensitive recording layer 14 and the protective layer 15 in the first embodiment described above.
【００４６】（具体例２）下記のような配合比により、
あらかじめ感熱記録層塗液を作成しておき、支持体２１
として透明なＰＥＴフィルム（厚さ：１８０μｍ）上
に、金属反射層２２としてアルミ蒸着を施し、この上に
絵柄印刷層２３として白色インキで絵柄を印刷し、この
上に上記感熱記録層塗液の塗工を行なって、厚さ約１５
μｍの感熱記録層２４を形成した。(Specific Example 2) With the following compounding ratio,
The thermosensitive recording layer coating liquid is prepared in advance, and the support 21
On a transparent PET film (thickness: 180 μm) as the metal reflection layer 22 is vapor-deposited with aluminum, and a pattern is printed with a white ink as a pattern printing layer 23 on this, and the above-mentioned heat-sensitive recording layer coating liquid After coating, the thickness is about 15
A thermosensitive recording layer 24 having a thickness of μm was formed.
【００４７】さらに、この感熱記録層２４上に、炭酸カ
ルシウム、およびステアリン酸亜鉛を樹脂に対してそれ
ぞれ５％、および１％の割合で添加した紫外線硬化樹脂
を塗工し、厚さ約２．５μｍの保護層２５を設けて、セ
キュリティ機能を有するカード１を作成した。Further, an ultraviolet curable resin containing 5% and 1% of calcium carbonate and zinc stearate added to the resin is coated on the heat-sensitive recording layer 24 to have a thickness of about 2. A card 1 having a security function was prepared by providing a protective layer 25 having a thickness of 5 μm.
【００４８】 （感熱記録層塗液の構成） ベヘン酸 ４．０重量部 アジピン酸 ２．０重量部 １，４−シクロヘキサンジカルボン酸 １．０重量部 エスレックＡ（積水化学製） ２１．０重量部 イソシアネート １．０重量部 テトラヒドロフラン ８４．０重量部 トルエン ４９．０重量部 次に、以上のように構成した本実施例のカード２におい
ては、書き替え可能な感熱記録層２４と金属反射層２２
との間に、識別層として絵柄印刷層２３を設け、この絵
柄印刷層２３を特に白色インキを用いて設けていること
により、通常の状態では、感熱記録層４２を白濁状態に
維持し、このカード２の真偽判別を行なう際に、例えば
Ｔ2 以上の温度を感熱記録層２４に加えて、半濁状態に
なった時点で、感熱記録層２４の下に設けられた絵柄印
刷層２３の情報（絵柄情報）を、目視または装置によっ
て読み取ることができる。(Structure of coating liquid for heat-sensitive recording layer) Behenic acid 4.0 parts by weight Adipic acid 2.0 parts by weight 1,4-Cyclohexanedicarboxylic acid 1.0 part by weight S-REC A (manufactured by Sekisui Chemical Co., Ltd.) 21.0 parts by weight Isocyanate 1.0 parts by weight Tetrahydrofuran 84.0 parts by weight Toluene 49.0 parts by weight Next, in the card 2 of the present embodiment configured as described above, the rewritable heat-sensitive recording layer 24 and the metal reflective layer 22 are used.
By providing a pattern print layer 23 as an identification layer between the and, and by providing this pattern print layer 23 with a white ink in particular, the heat-sensitive recording layer 42 is maintained in a cloudy state in a normal state. When the authenticity of the card 2 is determined, for example, a temperature of T 2 or higher is applied to the heat-sensitive recording layer 24, and when the semi-turbid state is reached, the pattern printing layer 23 provided under the heat-sensitive recording layer 24 Information (pattern information) can be read visually or by a device.
【００４９】その後、感熱記録層２４をＴ0 以下の温度
に冷却すると、カード２がリーダーライターから出てき
た時には、感熱記録層２４は元のように白濁状態、すな
わちその光散乱性が増大して最大遮光状態になってお
り、通常の状態では、感熱記録層２４の下に記載された
絵柄印刷層２３の情報を判読することはできないため、
磁気情報等だけでは不十分な媒体の真偽判別に対して、
高度なセキュリティ機能を付与することができる。After that, when the heat-sensitive recording layer 24 is cooled to a temperature of T 0 or lower, when the card 2 comes out of the reader / writer, the heat-sensitive recording layer 24 is in a cloudy state as it was, that is, its light scattering property is increased. In the normal state, it is impossible to read the information of the pattern print layer 23 written under the heat-sensitive recording layer 24.
For authenticity determination of media where magnetic information etc. are insufficient,
Advanced security features can be added.
【００５０】この時、感熱記録層２４の下に設けられた
絵柄印刷層２３は、白色としていることにより、感熱記
録層２４が白濁してその光散乱性が増大して最大遮光状
態となった時に、絵柄印刷層２３に示されている内容
が、より判読しずらい状態となる。At this time, since the pattern printing layer 23 provided under the heat-sensitive recording layer 24 is white, the heat-sensitive recording layer 24 becomes cloudy and its light scattering property is increased to reach the maximum light shielding state. At times, the content shown in the pattern print layer 23 becomes more difficult to read.
【００５１】すなわち、より具体的には、通常時は感熱
記録層２４は白濁状態にあり、熱板またはサーマルヘッ
ドやレーザー光線、ヒーター等により、例えば摂氏８０
度以上で１００度未満の温度に加熱しかつ保持した後に
室温近傍の適宜温度以下に冷却すると、その光散乱性が
減少して感熱記録層２４は透明状態となり、感熱記録層
２４の下に設けられたそれまで見ることのできなかった
絵柄印刷層２３の絵柄情報を目視により確認することが
できるようになり、一方確認完了時に、このカード２を
例えば摂氏１００度以上の温度に加熱しかつ保持した後
に室温近傍の適宜温度以下に冷却することによって、感
熱記録層２４はその光散乱性が増大して元の白濁状態に
戻り、感熱記録層２４の下に設けられた絵柄印刷層２３
の絵柄情報は、再び確認することができなくなる。More specifically, more specifically, the heat-sensitive recording layer 24 is normally in a cloudy state under normal conditions, and the heat-sensitive recording layer 24 is heated to 80 degrees Celsius by a heating plate, a thermal head, a laser beam, a heater, or the like.
When heated to a temperature of not less than 100 ° C. and less than 100 ° C. and held, and then cooled to an appropriate temperature near room temperature or less, its light scattering property is reduced and the heat-sensitive recording layer 24 becomes transparent and is provided below the heat-sensitive recording layer 24. It becomes possible to visually confirm the pattern information of the pattern printing layer 23 which has been invisible until then, while the card 2 is heated and held at a temperature of, for example, 100 degrees Celsius or more when the confirmation is completed. Then, by cooling to an appropriate temperature near room temperature or lower, the light-scattering property of the heat-sensitive recording layer 24 increases and returns to the original white turbid state, and the pattern printing layer 23 provided under the heat-sensitive recording layer 24.
The picture information of can not be confirmed again.
【００５２】このような特性を利用することにより、磁
気情報が消失または改竄されたカード、あるいはコピー
ないし写真製版技術等により外観上の類似性を備えたカ
ードにおいて、そのカード自体が本物であるかどうかの
真偽判別を即座に行なうことができる。By utilizing such characteristics, whether a card in which magnetic information is lost or tampered with, or a card having a similarity in appearance by a copying or photoengraving technique is the card itself is genuine. Whether it is true or false can be immediately discriminated.
【００５３】上述したように、本実施例のカード２は、
支持体２１上に、金属反射層２２、識別層である白色の
絵柄印刷層２３、書き替え可能な感熱記録層２４、およ
び保護層２５を、順次積層して構成したものである。As described above, the card 2 of this embodiment is
A metal reflective layer 22, a white pattern printing layer 23 as an identification layer, a rewritable heat-sensitive recording layer 24, and a protective layer 25 are sequentially laminated on a support 21.
【００５４】従って、従来のカードでは十分ではなかっ
たカード自体の真偽判定、すなわちカード自体が本物で
あるかどうかの真偽判別を即座にしかも比較的容易に行
なうことができ、磁気記録情報等の消失や改竄（磁気情
報が消失または改竄されたカード、あるいはコピーない
し写真製版技術等により外観上の類似性を備えたカー
ド）に対して、有効にかつ素早く対応することが可能と
なる。Therefore, the authenticity of the card itself, which is not sufficient with the conventional card, that is, the authenticity of the card itself can be determined immediately and relatively easily. Can be effectively and swiftly dealt with against the disappearance or tampering of a card (a card whose magnetic information has been lost or tampered with, or a card having a similarity in appearance due to copying or photomechanical technology).
【００５５】これにより、近年増加の傾向にあるカード
犯罪に対して、有効な歯止め策を提供することができ
る。As a result, it is possible to provide an effective stopping measure against card crimes, which has been increasing in recent years.
【００５６】尚、本発明は上記各実施例に限定されるも
のではなく、次のようにしても同様に実施できるもので
ある。The present invention is not limited to the above embodiments, but can be implemented in the same manner as described below.
【００５７】（ａ）上記各実施例において、支持体１
１，２１上の各積層構造物と反対側の面上、あるいは当
該各積層構造物と同一側の面上に、図示しない磁気記録
層を設けるようにしてもよい。(A) In each of the above embodiments, the support 1
A magnetic recording layer (not shown) may be provided on the surface on the opposite side of the laminated structures 1 and 21 or on the surface on the same side as the laminated structures.
【００５８】この場合、磁気記録層としては、従来の磁
気カード等に適用されている磁気記録材料を適用するこ
とができる。In this case, as the magnetic recording layer, a magnetic recording material applied to a conventional magnetic card or the like can be applied.
【００５９】（ｂ）上記各実施例では、識別層として、
バーコード、あるいは絵柄による印刷層１３，２３を設
ける場合について説明したが、これに限らず、識別層と
して、文字、あるいは記号による印刷層を設けるように
してもよい。(B) In each of the above embodiments, the identification layer is
The case of providing the print layers 13 and 23 by the barcode or the pattern has been described, but the present invention is not limited to this, and a print layer by characters or symbols may be provided as the identification layer.
【００６０】（ｃ）上記各実施例において、感熱記録層
１４，２４の下に設けられる印刷層１３，２３として
は、白色であることが好ましいが、何らこれに限らず、
その他の色（例えば、白色に近い色）とするようにして
もよい。(C) In each of the above embodiments, the printing layers 13 and 23 provided under the thermosensitive recording layers 14 and 24 are preferably white, but not limited thereto.
Other colors (for example, colors close to white) may be used.
【００６１】（ｄ）上記各実施例では、セキュリティ機
能を有する媒体としてカードに適用した場合について説
明したが、セキュリティ機能を有する媒体としてカード
以外のものについても、本発明を同様に適用できるもの
である。(D) In each of the above embodiments, the case where the present invention is applied to a card as a medium having a security function has been described, but the present invention can be similarly applied to a medium other than a card as a medium having a security function. is there.
【００６２】[0062]
【発明の効果】以上説明したように本発明によれば、支
持体上に、金属反射層、識別層、書き替え可能な感熱記
録層を、順次積層し、さらに必要に応じて、支持体上の
各積層構造物と反対側の面上、あるいは当該各積層構造
物と同一側の面上に、磁気記録層を設けて構成するよう
にしたので、媒体自体が本物であるかどうかの真偽判別
を即座にしかも比較的容易に行ない、磁気記録情報等の
消失や改竄に対して有効にかつ素早く対応することが可
能なセキュリティ機能を有する媒体が提供できる。As described above, according to the present invention, a metal reflective layer, an identification layer, and a rewritable heat-sensitive recording layer are sequentially laminated on a support, and further, if necessary, on the support. Since the magnetic recording layer is provided on the surface opposite to each laminated structure or on the same surface as each laminated structure, it is possible to determine whether the medium itself is genuine or not. It is possible to provide a medium having a security function capable of making a determination immediately and relatively easily and effectively and quickly responding to loss or alteration of magnetic recording information and the like.
【図１】本発明によるセキュリティ機能を有するカード
の第１の実施例を示す断面図。FIG. 1 is a sectional view showing a first embodiment of a card having a security function according to the present invention.
【図２】本発明によるセキュリティ機能を有するカード
の第２の実施例を示す断面図。FIG. 2 is a sectional view showing a second embodiment of a card having a security function according to the present invention.
１…セキュリティ機能を有するカード、１１…支持体、
１２…金属反射層、１３…バーコード印刷層、１４…感
熱記録層、１５…保護層、２…セキュリティ機能を有す
るカード、２１…支持体、２２…金属反射層、２３…絵
柄印刷層、２４…感熱記録層、２５…保護層。1 ... Card having security function, 11 ... Support,
12 ... Metal reflective layer, 13 ... Bar code printed layer, 14 ... Thermal recording layer, 15 ... Protective layer, 2 ... Card having security function, 21 ... Support, 22 ... Metal reflective layer, 23 ... Pattern printed layer, 24 ... thermosensitive recording layer, 25 ... protective layer.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｇ０６Ｋ 19/10 Ｇ０６Ｋ 19/00 Ｒ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location G06K 19/10 G06K 19/00 R
Claims (5)
替え可能な感熱記録層を、順次積層して成ることを特徴
とするセキュリティ機能を有する媒体。1. A medium having a security function, comprising a metal reflective layer, an identification layer, and a rewritable heat-sensitive recording layer, which are sequentially laminated on a support.
を有する媒体において、 前記支持体上の各積層構造物と反対側の面上、あるいは
当該各積層構造物と同一側の面上に、磁気記録層を設け
て成ることを特徴とするセキュリティ機能を有する媒
体。2. The medium having the security function according to claim 1, wherein a magnetic field is formed on a surface of the support opposite to each laminated structure or on a surface of the same side as each laminated structure. A medium having a security function characterized by comprising a recording layer.
は、樹脂母材と、当該樹脂母材中に分散された有機低分
子物質とを主成分とし、温度に依存してその透明度が可
逆的に変化するものであることを特徴とする請求項１ま
たは請求項２に記載のセキュリティ機能を有する媒体。3. The rewritable heat-sensitive recording layer is mainly composed of a resin base material and an organic low molecular weight substance dispersed in the resin base material, and its transparency is reversible depending on temperature. The medium having the security function according to claim 1 or 2, wherein the medium has a security function.
柄、あるいは、バーコードによる印刷層であることを特
徴とする請求項１または請求項２に記載のセキュリティ
機能を有する媒体。4. The medium having a security function according to claim 1, wherein the identification layer is a print layer formed of characters, symbols, pictures, or a bar code.
特徴とする請求項１、請求項２、または請求項４のいず
れか１項に記載のセキュリティ機能を有する媒体。5. The medium having a security function according to claim 1, wherein the identification layer is white.