PURPOSE:To provide a resin compsn. for insulation treatment of an electric apparatus which compsn. improves the moisture resistance of an electric apparatus such as a motor or a transformer. CONSTITUTION:A resin compsn. for insulation treatment of an electric apparatus comprises (A) 100 pts.wt. unsatd. polyester resin and (B) 0.2-3.0 pts.wt. carbonate of cyclohexylamine.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin composition for electrical equipment insulation treatment, and more particularly to a resin composition for electrical equipment insulation treatment which prevents rusting of metal surfaces such as motors and transformers.

[0002]

2. Description of the Related Art Unsaturated polyester resins composed of unsaturated polyester and a crosslinkable monomer are harmonized in terms of mechanical, electrical and thermal characteristics, workability and economical efficiency, and therefore FRP laminated. It is used in many applications including boards. Further, this resin is also widely used as an impregnating varnish for motors, transformers and the like because it has excellent characteristics and workability for electrical insulation. However,
Motors and transformers conventionally treated with varnish are used in high humidity, or when stored in a closed state for a long period of time, due to moisture or oxygen, they may be used in the cores of motors and transformers, or in adapter transformers. Rust occurs on the power input metal plug, which reduces product value and increases iron loss.
There was a defect that caused poor continuity of the plug.

[0003]

DISCLOSURE OF THE INVENTION The present invention eliminates the above-mentioned drawbacks of the prior art and prevents the rust of the core of an electric device or the input plug of a transformer from being rusted under high humidity. It is to provide things.

[0004]

Means for Solving the Problems As a result of intensive studies, the present inventors have found that by mixing an unsaturated polyester resin with a carbonate of cyclohexylamine, the unsaturated polyester varnish has higher humidity and a longer period of time than conventional unsaturated polyester varnishes. It has been found that it is possible to prevent rust from being generated on the surface of the core of an electric device or the plug surface of a transformer when stored in a sealed state. The present invention provides (A)
An unsaturated polyester resin and (B) a cyclohexylamine carbonate;
The present invention relates to a resin composition for electrical equipment insulation treatment, which is 0.2 to 3.0 parts by weight with respect to 0 parts by weight.

The component (A) used in the present invention contains an unsaturated polyester and a crosslinkable monomer. The unsaturated polyester can be obtained by reacting the following acid component and alcohol component and, if necessary, a modifying component. Examples of the acid component include unsaturated acids such as maleic acid, maleic anhydride and fumaric acid, phthalic acid, phthalic anhydride, isophthalic acid, terephthalic acid, tetrahydrophthalic acid, tetrahydrophthalic anhydride, hexahydrophthalic acid and hexahydroanhydride. Saturated acids such as phthalic acid, adipic acid, sebacic acid, etc., soybean oil and fat and oil, linseed oil and fat and acid, tall oil and fat and fatty acid, and the like are used. As the alcohol component,
For example, propylene glycol, ethylene glycol, dipropylene glycol, diethylene glycol, 1,3
-Butanediol, neopentyl glycol, glycerin, trimethylolpropane, pentaerythritol and the like are used. Examples of the modifying component include linseed oil, soybean oil, tall oil, dehydrated castor oil, coconut oil, dicyclopentadiene, cyclopentadiene and the like. Examples of the crosslinkable monomer include styrene, vinyltoluene, α
-Methyl styrene, tertiary butyl styrene, divinylbenzene, various acrylic acid esters and / or methacrylic acid esters, various allyl esters, various allyl ethers and the like. The amount of the crosslinkable monomer used is preferably in the range of 80 to 40 parts by weight with respect to 20 to 60 parts by weight of the unsaturated polyester, with the total amount being 100 parts by weight.

The carbonic acid salt of cyclohexylamine used as the component (B) in the present invention is a known compound, and either a reagent or an industrial one can be used. For industrial use, there is the product name Kirest VCI130 manufactured by Kirest Co., Ltd.
The amount of cyclohexylamine carbonate used is the same as in (A) above.
The amount is 0.2 to 3.0 parts by weight based on 100 parts by weight of the component. If the amount of cyclohexylamine carbonate used is less than 0.2 parts by weight, the effect of preventing corrosion of the core of electrical equipment and the effect of preventing the corrosion of the plug of the adapter transformer are insufficient. Above these values, no significant improvement in these effects is observed.

The resin composition for electrical equipment insulation treatment according to the present invention includes, as a curing agent, acyl peroxide such as benzoin peroxide and acetyl peroxide, hydroperoxide such as tertiary butyl peroxide and cumene hydroperoxide. Ketone peroxide such as oxide, methyl ethyl ketone peroxide, cyclohexanone peroxide, dialkyl peroxide such as ditertiary butyl peroxide and dicumyl peroxide, oxyperoxide such as tertiary butyl peroxyacetate, etc. are used. The amount of the curing agent added is 0.1% with respect to 100 parts by weight of the component (A).
5 to 5 parts by weight is preferable.

Further, if necessary, the accelerator and the polymerization inhibitor may be added in a usual amount. Examples of the accelerator include manganese naphthenate, lead naphthenate, cobalt naphthenate, cobalt octenoate, and the like. As the polymerization inhibitor, for example, quinones such as hydroquinone, tertiary butyl catechol and p-benzoquinone are used.

The resin composition of the present invention is applied to the insulation treatment of motors such as air conditioner fans, electric fans and washing machines, power transformers of televisions, stereos, compact disc players and the like, and adapter transformers equipped with a metal plug for power input. It

[0010]

The present invention will be described with reference to the following examples. The middle part of the following examples means parts by weight. Production Example 1 4474 parts (11 mol) of dipropylene glycol, 498 parts (3 mol) of isophthalic acid, 392 parts (4 mol) of maleic anhydride, 456 parts (3 mol) of tetrahydrophthalic anhydride and 0.22 part of hydroquinone were added. Put in a two-necked flask and heat-condense at 210 ° C for 10 hours to give an acid value of 21.5.
Of unsaturated polyester was synthesized. 40 parts of this unsaturated polyester, 60 parts of styrene, and 0.5 parts of 8% manganese naphthenate were dissolved by stirring to obtain unsaturated polyester resin A. Production Example 2 341 parts (5.5 mol) of ethylene glycol, 296 parts (2.0 mol) of phthalic anhydride, 196 parts (2.0 mol) of maleic anhydride, 560 parts (2.0 mol) of soybean oil and fatty acid.
And 0.24 parts of hydroquinone were placed in a four-necked flask and heated and condensed at 200 ° C. for 8 to 12 hours to give an acid value of 20.8.
Of unsaturated polyester was synthesized. 40 parts of this unsaturated polyester, 60 parts of styrene, and 0.5 parts of 8% manganese naphthenate were dissolved by stirring to obtain unsaturated polyester resin B.

Examples 1 to 6 Carbonic acid salt of cyclohexylamine on unsaturated polyester resin A or B (trade name CHIREST V, manufactured by CREST Co., Ltd.)
CI130) and benzoyl peroxide were dissolved in the compounding ratio shown in Table 1 to obtain a resin composition of the present invention. With respect to these resin compositions, gelation time, drying time, volume resistivity, plug corrosiveness, and core rust preventive ability were evaluated by the test methods described below, and the results are shown in Table 1.

Comparative Examples 1 and 2 Benzoyl peroxide was dissolved in unsaturated polyester resin A or B at the compounding ratio shown in Table 1 and evaluated in the same manner as in Examples. The results are shown in Table 1.

Test method (1) Gelation time It was measured according to the gelation time test method of JIS C 2105. (2) Drying time The drying time was measured according to the JIS C 2105 drying time test method. (3) Volume resistivity Using a 2.0 mm resin plate which was heated and cured at 120 ° C. for 2 hours, the volume resistivity at 25 ° C. was measured according to JIS C2105. (4) Corrosion of plug An adapter transformer (core size: 48 x 45 x 25 mm) equipped with a power input plug (nickel plated product) is immersed in the resin composition for 2 minutes, then pulled up and left in the air for 10 minutes. Cure at 120 ° C. for 1 hour. 500 cc of this varnished adapter transformer and 10 g of deionized water
c Put it in a glass beaker and seal it as shown in Fig. 1
The number of days until the plug was corroded was determined by leaving it in a constant temperature bath at ℃. In FIG. 1, 1 is an adapter transformer, 2 is a power input plug, 3 is ion water, and 4 is a 500 cc glass beaker. (5) Corrosion resistance of core In the test of (4), after left in a thermo-hygrostat for 5 days, the generation state of rust on the core of the power transformer was observed and evaluated according to the following criteria. ◯: No rust was generated. Δ: Rust was generated in the surface area of the core of about 10 to 20%. X: Rust was generated in the surface area of the core of about 40 to 60%.

[0014]

[Table 1]

[0015]

EFFECTS OF THE INVENTION By impregnating an electric equipment with the resin composition for electric equipment insulation treatment of the present invention and performing an insulation treatment, the rust preventive ability of the core and the plug is remarkably improved even under high humidity. It is possible to manufacture excellent electrical equipment.

[Brief description of drawings]

FIG. 1 is an apparatus for testing the corrosiveness of plugs performed in Examples and Comparative Examples.

[Explanation of symbols]

 1 Adapter transformer 2 Power input plug 3 Ion water 4 500cc glass beaker

Claims (1)

[Claims] 1. A resin containing (A) an unsaturated polyester resin and (B) a cyclohexylamine carbonate, (B)
The component is 0.2 to 100 parts by weight of the component (A).
A resin composition for electrical equipment insulation treatment, which comprises 3.0 parts by weight.