JPH07217225A - Reinforcing method for brick wall body - Google Patents
Reinforcing method for brick wall bodyInfo
- Publication number
- JPH07217225A JPH07217225A JP1010894A JP1010894A JPH07217225A JP H07217225 A JPH07217225 A JP H07217225A JP 1010894 A JP1010894 A JP 1010894A JP 1010894 A JP1010894 A JP 1010894A JP H07217225 A JPH07217225 A JP H07217225A
- Authority
- JP
- Japan
- Prior art keywords
- crack
- brick wall
- hole
- wall body
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、レンガ壁体の補強方法
に関わるものであり、特に、レンガ造りの建物を構成す
るレンガ壁体に生じた亀裂（本発明では、目地の風化欠
落なども含むものとする）を十分に補強することが可能
なレンガ壁体の補強方法の改良に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for reinforcing a brick wall body, and in particular, cracks in the brick wall body constituting a brick building (in the present invention, the weathering of joints and the like are also lost). The improvement of the method for reinforcing a brick wall body that can sufficiently reinforce.
【０００２】[0002]
【従来の技術】レンガ造りの建物には、明治初期ごろに
建てられたものが多い。現在では、このレンガ造りの建
物を文化遺産として、また、商業的な活用などを行う目
的で、保存再生を図る要求が高まっている。しかしなが
ら、前記レンガ造りの建物は、長い間の風雪や地震など
により、その壁体（以下、『レンガ壁体』という』に、
亀裂や目地の風化欠落など（以下、『亀裂』という）が
生じ、危険な状態になっている物もある。2. Description of the Related Art Many brick buildings were built in the early Meiji era. Nowadays, there is an increasing demand for preservation and regeneration of this brick building as a cultural heritage and for commercial purposes. However, the brick building has its wall body (hereinafter referred to as "brick wall body") due to a long period of wind and snow or an earthquake.
Some things are in a dangerous state due to cracks and missing weathering of joints (hereinafter referred to as "cracks").
【０００３】そこで、このようなレンガ壁体を補強し、
保存再生を図る方法として、たとえば、図７に示すよう
に、レンガ壁体１の内側面１１（レンガ壁体１の厚さ方
向の一面）から、複数枚のレンガを貫通する水平な孔９
１を複数削孔し、この孔９１内に、エポキシ樹脂９３を
充填した後、この孔９１内に鉄筋９４を埋め込み縫合
し、その後、レンガ壁体１の表面を補修する方法があ
る。Therefore, such a brick wall is reinforced,
As a method of storing and reproducing, for example, as shown in FIG. 7, a horizontal hole 9 penetrating a plurality of bricks from an inner side surface 11 of the brick wall body 1 (one surface in the thickness direction of the brick wall body 1).
There is a method in which a plurality of holes 1 are drilled, epoxy resin 93 is filled in the holes 91, reinforcing bars 94 are embedded and sewn in the holes 91, and then the surface of the brick wall 1 is repaired.
【０００４】また、図８に示すように、レンガ壁体１の
内側面１１から、図７に示す孔９１に代えて、斜め（４
５度程度）下向きの孔９２を複数削孔し、この孔９２内
に、エポキシ樹脂９３を充填した後、この孔９２内に鉄
筋９４を埋め込み縫合し、その後、レンガ壁体１の表面
を補修する方法がある。なお、図７は、レンガ壁体１の
水平方向一部断面図であり、図８は、レンガ壁体１の垂
直方向一部断面図である。Further, as shown in FIG. 8, instead of the hole 91 shown in FIG.
A plurality of downward holes 92 are drilled, epoxy resin 93 is filled into the holes 92, and then reinforcing bars 94 are embedded and sewn in the holes 92, after which the surface of the brick wall body 1 is repaired. There is a way to do it. 7 is a horizontal partial cross-sectional view of the brick wall body 1, and FIG. 8 is a vertical partial cross-sectional view of the brick wall body 1.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、前記レ
ンガ壁体１の内側面１１から、複数枚のレンガを貫通す
る水平な孔９１を複数削孔する従来例は、レンガ壁体１
の同一高さ位置における厚さ方向の補強はできるもの
の、略垂直方向に生じた亀裂および略水平方向に生じた
亀裂を縫合することができないため、これらのレンガ壁
体の補強を行うことができないという問題がある。However, the conventional example in which a plurality of horizontal holes 91 penetrating a plurality of bricks are drilled from the inner side surface 11 of the brick wall body 1 is the brick wall body 1.
Although it is possible to reinforce in the thickness direction at the same height position, it is impossible to reinforce these brick walls because it is not possible to sew cracks that occur in a substantially vertical direction and cracks that occur in a substantially horizontal direction. There is a problem.
【０００６】また、前記レンガ壁体１の内側面１１か
ら、複数枚のレンガを貫通する斜め下向きの孔９２を複
数削孔する従来例は、略水平方向に生じた亀裂は、ある
程度縫合することができるが、この程度の縫合では、亀
裂が生じたレンガ壁体の補強を十分に行うことができな
いという問題がある。さらに、略垂直方向に生じた亀裂
を縫合することができず、このレンガ壁体の補強を行う
ことができないという問題がある。Further, in the conventional example in which a plurality of diagonally downward holes 92 penetrating a plurality of bricks are drilled from the inner surface 11 of the brick wall body 1, a crack generated in a substantially horizontal direction should be sewn to some extent. However, there is a problem in that the brick wall body having a crack cannot be sufficiently reinforced with this degree of stitching. Further, there is a problem that the cracks generated in the substantially vertical direction cannot be sewn, and the brick wall cannot be reinforced.
【０００７】本発明は、このような従来の問題点を解決
することを課題とするものであり、略垂直方向の亀裂が
生じたレンガ壁体および略水平方向の亀裂が生じたレン
ガ壁体の両方を効果的且つ十分に補強することが可能な
レンガ壁体の補強方法を提供することを目的とする。An object of the present invention is to solve such a conventional problem, and to provide a brick wall body having a crack in a substantially vertical direction and a brick wall body having a crack in a substantially horizontal direction. It is an object of the present invention to provide a method for reinforcing a brick wall body capable of effectively and sufficiently reinforcing both.
【０００８】[0008]
【課題を解決するための手段】この目的を達成するため
に、請求項１記載の発明は、略垂直方向に亀裂が生じた
レンガ壁体の補強方法において、前記レンガ壁体の厚さ
方向に、前記亀裂を挟んで該亀裂と壁体内外両表面に所
定の間隔をおいて互いに垂直方向に所定の間隔をおいた
位置から、前記レンガ壁体の厚さ方向略中央部で前記亀
裂の断面と交差する孔を複数削孔する工程と、前記孔内
に接着材を充填する工程と、前記接着剤が充填された孔
内に鉄筋を挿入して前記接着剤で埋め込む工程と、前記
亀裂に接着材を充填する工程と、を含んでなることを特
徴とするレンガ壁体の補強方法を提供するものである。In order to achieve this object, the invention according to claim 1 is a method for reinforcing a brick wall body in which a crack is generated in a substantially vertical direction, in the thickness direction of the brick wall body. , A cross section of the crack at a substantially central portion in the thickness direction of the brick wall from a position where the crack and the wall inside and outside the wall are spaced a predetermined distance apart from each other with a predetermined distance therebetween. A step of drilling a plurality of holes intersecting with, a step of filling the hole with an adhesive, a step of inserting a reinforcing bar into the hole filled with the adhesive and burying with the adhesive, the crack A method for reinforcing a brick wall, comprising a step of filling an adhesive material.
【０００９】また、請求項２記載の発明は、略水平方向
に亀裂が生じたレンガ壁体の補強方法において、前記レ
ンガ壁体の厚さ方向同一側面であって、前記亀裂を挟ん
で該亀裂と所定の間隔をおいた両側且つ互いに水平方向
に所定の間隔をおいた位置、または、前記レンガ壁体の
厚さ方向の両側面であって、前記亀裂から同一垂直方向
に所定の間隔をおき且つ互いに水平方向に所定の間隔を
おいた位置から、前記レンガ壁体の厚さ方向略中央部で
前記亀裂の断面と交差する孔を複数削孔する工程と、前
記孔内に接着剤を充填する工程と、前記接着剤が充填さ
れた孔内に鉄筋を挿入して前記接着剤で埋め込む工程
と、前記亀裂に接着材を充填する工程と、を含んでなる
ことを特徴とするレンガ壁体の補強方法を提供するもの
である。Further, the invention according to claim 2 is a method for reinforcing a brick wall body in which a crack is generated in a substantially horizontal direction, wherein the crack is sandwiched on the same side surface in the thickness direction of the brick wall body. Positions with a predetermined gap in both sides and with a predetermined gap in the horizontal direction, or on both sides in the thickness direction of the brick wall, with a predetermined gap in the same vertical direction from the crack. And a step of drilling a plurality of holes intersecting with the cross section of the crack at a substantially central portion in the thickness direction of the brick wall body from positions spaced apart from each other in a horizontal direction, and filling the holes with an adhesive. Brick wall body, comprising: a step of, a step of inserting a reinforcing bar into the hole filled with the adhesive and embedding it with the adhesive, and a step of filling the crack with the adhesive. It provides a method of reinforcing
【００１０】[0010]
【作用】請求項１記載の発明によれば、レンガ壁体に形
成された略垂直方向の亀裂は、レンガ壁体の厚さ方向略
中央部であって、垂直方向の複数箇所で、亀裂の生じて
いない複数枚のレンガと縫合される。すなわち、前記亀
裂の縫合を行う鉄筋を挿入する各々の孔は、レンガ壁体
の厚さ方向の同一側面であって、前記亀裂を挟んで当該
亀裂と所定の間隔をおいた両側且つ互いに垂直方向に所
定の間隔をおいた位置、または、前記レンガ壁体の厚さ
方向の両側面であって、前記亀裂から同一水平方向に所
定の間隔をおき且つ互いに垂直方向に所定の間隔をおい
た位置から、前記レンガ壁体の厚さ方向略中央部で前記
亀裂の断面と交差するように複数削孔される。このた
め、この方法で削孔された孔は、前記亀裂を挟んで両側
に積層されている亀裂が生じていない複数枚のレンガに
貫通された状態となる。According to the invention as set forth in claim 1, the cracks formed in the brick wall in the substantially vertical direction are cracks at a plurality of locations in the vertical direction, which are substantially central portions in the thickness direction of the brick wall. It is sewn with multiple bricks that have not occurred. That is, each hole for inserting the reinforcing bar for suturing the crack is on the same side surface in the thickness direction of the brick wall, and the crack is sandwiched between the cracks at predetermined intervals on both sides and in the mutually perpendicular direction. At a predetermined distance, or on both sides in the thickness direction of the brick wall, a predetermined distance in the same horizontal direction from the crack and a predetermined distance in the vertical direction relative to each other. From the above, a plurality of holes are drilled so as to intersect with the cross section of the crack at the substantially central portion in the thickness direction of the brick wall body. Therefore, the holes drilled by this method are in a state of being penetrated by a plurality of bricks which are laminated on both sides of the crack and have no cracks.
【００１１】従って、前記それぞれの孔に挿入される鉄
筋も、前記亀裂が生じていない複数枚のレンガに貫通さ
れた状態で配設される。さらにまた、この鉄筋は、接着
剤により前記孔内に定着され、固定される。このため、
前記亀裂は、レンガ壁体の厚さ方向略中央部であって、
垂直方向の複数の箇所で、亀裂の生じていない複数枚の
レンガと縫合され、一体化される。従って、前記亀裂が
生じたレンガ壁体は、効率よく補強される。Therefore, the reinforcing bars to be inserted into the respective holes are also arranged so as to penetrate through the plurality of bricks in which the cracks have not occurred. Furthermore, this reinforcing bar is fixed and fixed in the hole by an adhesive. For this reason,
The crack is a substantially central portion in the thickness direction of the brick wall,
It is sewn and integrated with a plurality of crack-free bricks at a plurality of vertical positions. Therefore, the brick wall body in which the crack has occurred is efficiently reinforced.
【００１２】なお、前記レンガ壁体の厚さ方向略中央部
で前記亀裂の断面と交差する孔は、特に限定するもので
はないが、水平方向に削孔することが、前記亀裂とレン
ガとを効果的に縫合するうえで望ましい。そして、請求
項２記載の発明によれば、レンガ壁体に形成された略水
平方向の亀裂は、レンガ壁体の厚さ方向略中央部であっ
て、水平方向の複数箇所で、亀裂の生じていない複数枚
のレンガと縫合される。The hole intersecting with the cross section of the crack at the substantially central portion in the thickness direction of the brick wall is not particularly limited, but it is possible to drill the hole in the horizontal direction so that the crack and the brick are cut. It is desirable for effective suturing. Further, according to the invention of claim 2, the cracks formed in the brick wall in the substantially horizontal direction are substantially central portions in the thickness direction of the brick wall, and the cracks are generated at a plurality of horizontal positions. Not sewn with multiple bricks.
【００１３】すなわち、前記亀裂の縫合を行う鉄筋を挿
入するそれぞれの孔は、レンガ壁体の厚さ方向の同一側
面であって、前記亀裂を挟んで当該亀裂と所定の間隔を
おいた両側且つ互いに水平方向に所定の間隔をおいた位
置、または、前記レンガ壁体の厚さ方向の両側面であっ
て、前記亀裂から同一垂直方向に所定の間隔をおき且つ
互いに水平方向に所定の間隔をおいた位置から、前記レ
ンガ壁体の厚さ方向略中央部で前記亀裂の断面と交差す
るように複数削孔される。このため、この方法で削孔さ
れた孔は、前記亀裂を挟んで垂直方向両側に積層されて
いる亀裂が生じていない複数枚のレンガに貫通された状
態となる。That is, the holes for inserting the reinforcing bars for stitching the cracks are located on the same side surface in the thickness direction of the brick wall body, and on both sides of the crack with a predetermined distance from the cracks. Positions at a predetermined distance from each other in the horizontal direction, or on both side surfaces in the thickness direction of the brick wall, at a predetermined distance in the same vertical direction from the crack and at a predetermined distance from each other in the horizontal direction. A plurality of holes are drilled from the set position so as to intersect with the cross section of the crack at the approximate center of the brick wall in the thickness direction. Therefore, the hole drilled by this method is in a state of being penetrated by a plurality of bricks which are laminated on both sides in the vertical direction with the crack interposed therebetween and in which no crack is generated.
【００１４】従って、前記それぞれの孔に挿入される鉄
筋も、前記亀裂が生じていない複数枚のレンガに貫通さ
れた状態で配設される。さらにまた、この鉄筋は、接着
剤により前記孔内に定着され、固定される。このため、
前記亀裂は、レンガ壁体の厚さ方向略中央部であって、
水平方向の複数の箇所で、亀裂の生じていない複数枚の
レンガと縫合され、一体化される。従って、前記亀裂が
生じたレンガ壁体は、効率よく補強される。Therefore, the reinforcing bars to be inserted into the respective holes are also arranged so as to penetrate the plurality of bricks in which the cracks have not been formed. Furthermore, this reinforcing bar is fixed and fixed in the hole by an adhesive. For this reason,
The crack is a substantially central portion in the thickness direction of the brick wall,
It is sewn and integrated with a plurality of crack-free bricks at a plurality of horizontal positions. Therefore, the brick wall body in which the crack has occurred is efficiently reinforced.
【００１５】[0015]
【実施例】次に、本発明の一実施例にかかるレンガ壁体
の補強方法について、図面を参照して説明する。 （実施例１）実施例１では、略垂直方向に亀裂が生じた
レンガ壁体を補強する方法について説明する。Next, a method of reinforcing a brick wall according to an embodiment of the present invention will be described with reference to the drawings. (Example 1) In Example 1, a method of reinforcing a brick wall body having a crack in a substantially vertical direction will be described.
【００１６】図１は、レンガ造りの建物を構成するレン
ガ壁体に、略垂直方向の亀裂が生じた状態を内側（建物
の内壁側）からみた側面図であり、図２は、図１の一部
Ａ−Ａ断面図である。図１および図２に示すように、レ
ンガ壁体１の内側面であって、レンガ壁体１に生じた略
垂直方向の亀裂２Ａを挟んで、亀裂２Ａと所定の間隔を
おいた両側、且つ、互いに垂直方向に所定の間隔をおい
た位置（実施例１では、３００ｍｍピッチのちどり状
態）に、後に説明する複数の孔を削孔するためのマーキ
ングを行う。FIG. 1 is a side view of a brick wall constituting a brick building in which a crack in a substantially vertical direction is seen from the inside (inner wall side of the building), and FIG. 2 is shown in FIG. It is a partial AA sectional view. As shown in FIGS. 1 and 2, on the inner side surface of the brick wall body 1, sandwiching the crack 2A in the brick wall body 1 in a substantially vertical direction, both sides at a predetermined distance from the crack 2A, and Marking for drilling a plurality of holes, which will be described later, is performed at positions spaced by a predetermined distance in the direction perpendicular to each other (in the first embodiment, a state of 300 mm pitch trimming).
【００１７】次に、たとえば、ベビー削岩機を用いて、
孔３Ａを削孔するためのマーキング位置から、レンガ壁
体１の厚さ方向の略中央部で、亀裂２Ａの断面と交差す
る直径φ２８ｍｍの孔３Ａを、水平に削孔する。なお、
実施例１では、孔３Ａは、マーキング位置から水平に、
レンガ壁体１の内側面に対する入射角が４５〜６０度と
なるように削孔した。Next, using a baby rock drill, for example,
From the marking position for drilling the hole 3A, a hole 3A having a diameter φ28 mm that intersects the cross section of the crack 2A is horizontally drilled at a substantially central portion in the thickness direction of the brick wall body 1. In addition,
In the first embodiment, the hole 3A is horizontal from the marking position,
Drilling was performed so that the incident angle with respect to the inner surface of the brick wall body 1 was 45 to 60 degrees.
【００１８】このように削孔された孔３Ａは、特に、図
２に示すように、亀裂２Ａの両側に積層されている複数
枚のレンガを貫通した状態となる。次いで、前記と同様
に、孔３Ｂを削孔するためのマーキング位置から、レン
ガ壁体１の厚さ方向の略中央部で、亀裂２Ａの断面と交
差する直径φ２８ｍｍの孔３Ｂを、水平に削孔する。な
お、実施例１では、孔３Ｂは、マーキング位置から水平
に、レンガ壁体１の内側面に対する入射角が４５〜６０
度となるように削孔した。As shown in FIG. 2, the hole 3A thus drilled is in a state of penetrating a plurality of bricks laminated on both sides of the crack 2A. Then, similarly to the above, from the marking position for drilling the hole 3B, the hole 3B having a diameter φ28 mm that intersects the cross section of the crack 2A is horizontally drilled at the substantially central portion in the thickness direction of the brick wall body 1. Make a hole. In addition, in Example 1, the hole 3B has a horizontal incident angle of 45 to 60 from the marking position with respect to the inner surface of the brick wall 1.
Drilled to a certain degree.
【００１９】この孔３Ｂも孔３Ａと同様に、亀裂２Ａの
両側に積層されている複数枚のレンガを貫通した状態と
なる。このようにして削孔された孔３Ａおよび３Ｂは、
互いに、垂直方向にある程度の間隔をおいて、亀裂２Ａ
の断面と交差する位置で互いに上下方向に立体交差する
ように配設される。Similar to the hole 3A, the hole 3B also penetrates a plurality of bricks laminated on both sides of the crack 2A. The holes 3A and 3B thus drilled are
The cracks 2A are vertically spaced from each other to some extent.
Are arranged so as to intersect with each other in the vertical direction at a position intersecting the cross section.
【００２０】以下、図示しないが、同様に、必要な数の
孔を削孔する。ここで、孔の削孔数は、レンガ壁体１の
亀裂２Ｂの発生状態によるが、平方米当たり、４〜６箇
所程度で十分である。次に、以下に示す配合組成で混ぜ
合わせて作製したプライマー（接着剤）１４を、孔３Ａ
内に５０〜１００ｇ程度流し込み、塗布棒により孔３Ａ
の内壁に塗り付ける。 （プライマーの配合組成） 低粘度エポキシ樹脂ＣＣＲエポ４１ ２部 硬化材 １部 次いで、以下に示す配合組成で混ぜ合わせて作製した接
着材グラウド１５を、前記プライマー１４が塗布された
孔３Ａ内に、たとえば、グリスガン（注入器にロングノ
ズルを付けたもの）などを使用して、孔３Ａの奥の方か
ら注入し、充填する。 （接着材グラウドの配合組成） 低粘度エポキシ樹脂ＣＣＲエポ４１ ２部 硬化材 １部 なお、実施例１では、前記プライマー１４と接着材グラ
ウド１５が、請求項記載の『接着剤』に相当する。Although not shown, a required number of holes are similarly drilled below. Here, the number of holes to be drilled depends on the state of occurrence of the crack 2B of the brick wall body 1, but about 4 to 6 locations per square meter is sufficient. Next, the primer (adhesive) 14 prepared by mixing with the following composition is used to form the holes 3A.
Pour about 50 to 100g into the inside and use the coating stick to make a hole 3A.
Apply to the inner wall of the. (Compounding composition of primer) Low-viscosity epoxy resin CCR Epo 41 2 parts Curing material 1 part Next, an adhesive material ground 15 prepared by mixing with the following composition is prepared in the hole 3A to which the primer 14 is applied. For example, a grease gun (injector with a long nozzle) is used to inject and fill the hole 3A from the back. (Compounding composition of adhesive material grout) Low-viscosity epoxy resin CCR Epo 41 2 parts Curing material 1 part In Example 1, the primer 14 and the adhesive material grout 15 correspond to the "adhesive" in the claims.
【００２１】次に、前記接着材グラウド１５が充填され
た孔３Ａ内に、鉄筋５Ａをゆっくり挿入する。このよう
にすることで、鉄筋５Ａは、プライマー１４と接着材グ
ラウド１５により、孔３Ａ内に定着固定され亀裂２Ａを
縫合する。このため、亀裂２Ａと、亀裂２Ａが生じてい
ない複数枚のレンガとを、強固に一体化することができ
る。なお、実施例１では、鉄筋５Ａとして、Ｄ−１０を
使用した。Next, the reinforcing bar 5A is slowly inserted into the hole 3A filled with the adhesive material grove 15. In this way, the reinforcing bar 5A is fixed and fixed in the hole 3A by the primer 14 and the adhesive material grove 15, and the crack 2A is sewn. Therefore, the crack 2A and the plurality of bricks in which the crack 2A is not generated can be firmly integrated. In addition, in Example 1, D-10 was used as the reinforcing bar 5A.
【００２２】次いで、孔３Ａの入口を、レンガ粉６Ａに
て補修する。このように、レンガ粉６Ａにて補修を行う
ため、レンガ壁体１本来の姿に支障を来すことなく、レ
ンガ壁体１の亀裂２Ａを補強できる。次に、孔３Ｂ以降
も前記と同様に、プライマー１４の塗布、接着材グラウ
ド１５の充填および鉄筋５Ｂの挿入を行った後、レンガ
粉（図１では、６Ｂ〜６Ｄ）にて孔の入口を補修する。Next, the entrance of the hole 3A is repaired with brick powder 6A. Since the repair is performed with the brick powder 6A in this way, the crack 2A of the brick wall 1 can be reinforced without affecting the original appearance of the brick wall 1. Next, after applying the primer 14, filling the adhesive material grove 15 and inserting the reinforcing bar 5B in the same manner as the above for the holes 3B and thereafter, the entrance of the holes is made with brick powder (6B to 6D in FIG. 1). Repair.
【００２３】このように、亀裂２Ａは、垂直方向の複数
の箇所で、前記縫合が行われた状態となるため、亀裂２
Ａが生じたレンガ壁体１を効果的に且つ十分に補強する
ことができる。なお、実施例１では、レンガ壁体１の内
側面１１から孔を削孔する方法について説明したが、こ
れに限らず、孔は、レンガ壁体１の外側面１２から削孔
してもよい。 （実施例２）次に、本発明の実施例２について、図面を
参照して説明する。As described above, the crack 2A is in a state in which the suturing is performed at a plurality of points in the vertical direction.
The brick wall body 1 in which A has occurred can be effectively and sufficiently reinforced. In addition, in Example 1, although the method of drilling a hole from the inner side surface 11 of the brick wall body 1 was described, it is not limited to this and a hole may be drilled from the outer side surface 12 of the brick wall body 1. . Second Embodiment Next, a second embodiment of the present invention will be described with reference to the drawings.
【００２４】実施例２では、略水平方向に亀裂が生じた
レンガ壁体を補強する方法について説明する。図３は、
レンガ造りの建物を構成するレンガ壁体に、略水平方向
の亀裂が生じた状態を内側（建物の内壁側）からみた側
面図であり、図４は、図３の一部Ｃ−Ｃ断面図である。In the second embodiment, a method of reinforcing a brick wall body having a crack in a substantially horizontal direction will be described. Figure 3
It is the side view which looked at the state where the crack of the horizontal direction was produced in the brick wall which comprises a brick building from the inside (inner wall side of a building), and FIG. 4 is a partial CC sectional view of FIG. Is.
【００２５】図３および図４に示すように、レンガ壁体
１の内側面１１であって、レンガ壁体１に生じた略水平
方向の亀裂２Ｂを挟んで、亀裂２Ｂと所定の間隔をおい
た上下両側、且つ、互いに水平方向に所定の間隔をおい
た位置（実施例２では、３００ｍｍピッチのちどり状
態）に、後に説明する複数の孔を削孔するためのマーキ
ングを行う。As shown in FIGS. 3 and 4, on the inner side surface 11 of the brick wall body 1, a substantially horizontal crack 2B generated in the brick wall body 1 is sandwiched, and a predetermined space is provided between the crack 2B. Marking for drilling a plurality of holes, which will be described later, is performed on both the upper and lower sides, and at positions at predetermined intervals in the horizontal direction (in the second embodiment, a state of a 300 mm pitch).
【００２６】次に、たとえば、ベビー削岩機を用いて、
孔３０Ａを削孔するためのマーキング位置から、レンガ
壁体１の厚さ方向の略中央部で、亀裂２Ｂの断面と交差
する直径φ２８ｍｍの孔３０Ａを、斜め下向きに削孔す
る。なお、実施例２では、孔３０Ａは、マーキング位置
からレンガ壁体１の内側面１１に対する入射角が４５〜
６０度となるように下向きに削孔した。Next, using a baby rock drill, for example,
From the marking position for drilling the hole 30A, a hole 30A having a diameter φ28 mm that intersects the cross section of the crack 2B is drilled diagonally downward at a substantially central portion in the thickness direction of the brick wall body 1. In Example 2, the hole 30A has an incident angle of 45 to the inner surface 11 of the brick wall 1 from the marking position.
The holes were drilled downward so that the angle was 60 degrees.
【００２７】このように削孔された孔３０Ａは、特に、
図４に示すように、亀裂２Ｂの上下両側に積層されてい
る複数枚のレンガを貫通した状態となる。次いで、前記
と同様に、孔３０Ｂを削孔するためのマーキング位置か
ら、レンガ壁体１の厚さ方向の略中央部で、亀裂２Ｂの
断面と交差する直径φ２８ｍｍの孔３０Ｂを、斜め上向
きに削孔する。なお、実施例２では、孔３０Ｂは、マー
キング位置からレンガ壁体１の内側面１１に対する入射
角が４５〜６０度となるように、上向きに削孔した。The hole 30A thus drilled is
As shown in FIG. 4, a plurality of bricks stacked on both upper and lower sides of the crack 2B are penetrated. Then, similarly to the above, from the marking position for drilling the hole 30B, at a substantially central portion in the thickness direction of the brick wall 1, a hole 30B having a diameter φ28 mm that intersects the cross section of the crack 2B is obliquely directed upward. Drill holes. In addition, in Example 2, the hole 30B was drilled upward so that the incident angle from the marking position to the inner surface 11 of the brick wall body 1 was 45 to 60 degrees.
【００２８】この孔３０Ｂも孔３０Ａと同様に、亀裂２
Ｂの上下両側に積層されている複数枚のレンガを貫通し
た状態となる。このようにして削孔された孔３０Ａおよ
び３０Ｂは、互いに、水平方向にある程度の間隔をおい
て、亀裂２Ｂの断面と交差する位置で互いに水平方向に
立体交差するように配設される。Like the hole 30A, the hole 30B also has cracks 2.
A plurality of bricks stacked on both upper and lower sides of B are penetrated. The holes 30 </ b> A and 30 </ b> B thus drilled are arranged so as to horizontally intersect each other at a certain distance in the horizontal direction at a position intersecting the cross section of the crack 2 </ b> B.
【００２９】以下、図示しないが、同様に、必要な数の
孔を削孔する。ここで、孔の削孔数は、レンガ壁体１の
亀裂２Ｂの発生状態によるが、平方米当たり、４〜６箇
所程度で十分である。次に、実施例１と同様のプライマ
ー１４を、孔３０Ａ内に５０〜１００ｇ程度流し込み、
塗布棒により孔３０Ａの内壁に塗り付ける。Although not shown, a required number of holes are similarly drilled. Here, the number of holes to be drilled depends on the state of occurrence of the crack 2B of the brick wall body 1, but about 4 to 6 locations per square meter is sufficient. Next, about 50 to 100 g of the primer 14 similar to that of Example 1 is poured into the hole 30A,
The inner wall of the hole 30A is painted with a coating stick.
【００３０】次いで、以下に示す配合組成で混ぜ合わせ
て作製した接着材グラウド４５を、前記プライマー１４
が塗布された孔３０Ａ内に、たとえば、グリスガンなど
を使用して、孔３０Ａの奥の方から注入し、充填する。
（接着材グラウドの配合組成） 低粘度エポキシ樹脂ＣＣＲエポ４２ ２部 硬化材 １部 この配合組成の接着材グラウド４５は、レンガの目地か
らエポキシ樹脂が流出することを防止できる利点があ
る。また、孔３０Ｂは、上向きに削孔されているため、
開口部が下になるが、接着材グラウド４５が当該開口部
から流れ出すことがない。Next, the adhesive material grout 45 prepared by mixing the following compositional composition was used to prepare the primer 14
Into the hole 30A coated with, for example, a grease gun is used to inject and fill the hole 30A from the back.
(Composition composition of adhesive material grout) Low-viscosity epoxy resin CCR Epo 42 2 parts Curing material 1 part The adhesive material composition 45 of this composition composition has an advantage that the epoxy resin can be prevented from flowing out from the joint of the brick. Further, since the hole 30B is drilled upward,
Although the opening is on the bottom, the adhesive material grove 45 does not flow out of the opening.
【００３１】なお、実施例２では、前記プライマー１４
と接着材グラウド４５が、請求項記載の『接着剤』に相
当する。次に、前記接着材グラウド４５が充填された孔
３０Ａ内に、鉄筋５Ａをゆっくり挿入する。このように
することで、鉄筋５Ａは、プライマー１４と接着材グラ
ウド４５により、孔３０Ａ内に定着固定され亀裂２Ｂを
縫合する。このため、亀裂２Ｂと、亀裂２Ｂが生じてい
ない複数枚のレンガとを、強固に一体化することができ
る。なお、実施例２では、鉄筋５Ａとして、Ｄ−１０を
使用した。In Example 2, the primer 14 was used.
And the adhesive material grove 45 correspond to the "adhesive" in the claims. Next, the reinforcing bar 5A is slowly inserted into the hole 30A filled with the adhesive material grove 45. By doing so, the reinforcing bar 5A is fixed and fixed in the hole 30A by the primer 14 and the adhesive material grove 45, and the crack 2B is sewn. Therefore, the crack 2B and the plurality of bricks in which the crack 2B has not occurred can be firmly integrated. In addition, in Example 2, D-10 was used as the reinforcing bar 5A.
【００３２】次いで、孔３０Ａの入口を、レンガ粉６０
Ａにて補修する。このように、レンガ粉６０Ａにて補修
を行うため、レンガ壁体１本来の姿に支障を来すことな
く、レンガ壁体１の亀裂２Ｂを補強できる。次に、孔３
０Ｂ以降も前記と同様に、プライマー１４の塗布、接着
材グラウド４５の充填および鉄筋５Ｂの挿入を行った
後、レンガ粉（図３では、６０Ｂ，６０Ｃ）にて孔の入
口を補修する。Next, the entrance of the hole 30A is replaced with the brick powder 60.
Repair at A. As described above, since the brick powder 60A is repaired, the crack 2B of the brick wall body 1 can be reinforced without affecting the original appearance of the brick wall body 1. Next, hole 3
After 0B, the primer 14 is applied, the adhesive material grout 45 is filled, and the reinforcing bar 5B is inserted in the same manner as described above, and then the entrance of the hole is repaired with brick powder (60B and 60C in FIG. 3).
【００３３】このように、亀裂２Ｂは、水平方向の複数
の箇所で、前記縫合が行われた状態となるため、亀裂２
Ｂが生じたレンガ壁体１を効果的に且つ十分に補強する
ことができる。なお、実施例２では、レンガ壁体１の内
側面１１から孔を削孔する方法について説明したが、こ
れに限らず、孔は、レンガ壁体１の外側面１２から削孔
してもよい。 （実施例３）次に、本発明の実施例３について、図面を
参照して説明する。As described above, the crack 2B is in a state in which the stitching is performed at a plurality of positions in the horizontal direction.
The brick wall body 1 in which B is generated can be effectively and sufficiently reinforced. In addition, in Example 2, although the method of drilling a hole from the inner side surface 11 of the brick wall body 1 was described, it is not limited to this, and a hole may be drilled from the outer side surface 12 of the brick wall body 1. . (Third Embodiment) Next, a third embodiment of the present invention will be described with reference to the drawings.
【００３４】実施例３では、略水平方向に亀裂が生じた
レンガ壁体を補強する他の方法について説明する。図５
は、レンガ造りの建物を構成するレンガ壁体に、略水平
方向の亀裂が生じた状態を内側（建物の内壁側）からみ
た側面図であり、図６は、図５の一部Ｄ−Ｄ断面図であ
る。なお、実施例３と同一部分には、同一の記号を付し
て詳細な説明は省略する。In the third embodiment, another method for reinforcing a brick wall body in which a crack is generated in a substantially horizontal direction will be described. Figure 5
FIG. 6 is a side view of a state in which a crack in a substantially horizontal direction is generated in a brick wall body that constitutes a brick building from the inside (inner wall side of the building), and FIG. 6 is a part DD of FIG. 5. FIG. The same parts as those in the third embodiment are designated by the same reference numerals and detailed description thereof will be omitted.
【００３５】図５および図６に示すように、レンガ壁体
１の内側面１１および外側面１２の所定位置に、マーキ
ングを行う。実施例３では、孔３０Ａを削孔するための
マーキング位置は、実施例３と同様の位置に行う。ま
た、孔３０Ｘを削孔するためのマーキング位置は、外側
面１２であって、亀裂２Ｂに対して孔３０Ａと同一垂直
方向（図５では上方向）に同一間隔をあけた位置且つ孔
３０Ａから左方へ所定の間隔をおいた位置にマーキング
を行う。さらに、孔３０Ｙを削孔するためのマーキング
位置は、外側面１２であって、亀裂２Ｂに対して孔３０
Ａと同一垂直方向（図５では上方向）に同一間隔をあけ
た位置且つ孔３０Ａから右方へ所定の間隔をおいた位置
にマーキングを行う。As shown in FIGS. 5 and 6, marking is performed at predetermined positions on the inner side surface 11 and the outer side surface 12 of the brick wall body 1. In the third embodiment, the marking position for drilling the hole 30A is the same as in the third embodiment. In addition, the marking position for drilling the hole 30X is the outer surface 12, and is located at the same distance from the hole 30A in the same vertical direction (upward in FIG. 5) as the hole 30A with respect to the crack 2B. Mark on the left side at a predetermined interval. Further, the marking position for drilling the hole 30Y is the outer surface 12, and the hole 30Y with respect to the crack 2B.
Marking is performed at a position with the same spacing in the same vertical direction as A (upward in FIG. 5) and with a predetermined spacing from the hole 30A to the right.
【００３６】さらに、必要に応じて、内側面１１と外側
面１２に、交互に前記と同様のマーキングを行う。次
に、たとえば、実施例３と同様の方法で、孔３０Ａ、孔
３０Ｙを斜め下向きに削孔する。なお、実施例３では、
孔３０Ａおよび孔３０Ｙは、マーキング位置からレンガ
壁体１の内側面１１に対する入射角が４５〜６０度とな
るように下向きに削孔した。Further, if necessary, the inner surface 11 and the outer surface 12 are alternately marked with the same marking as described above. Next, for example, the hole 30A and the hole 30Y are drilled obliquely downward in the same manner as in Example 3. In the third embodiment,
The holes 30A and 30Y were drilled downward from the marking position so that the incident angle with respect to the inner surface 11 of the brick wall 1 was 45 to 60 degrees.
【００３７】このように削孔された孔３０Ａおよび３０
Ｙは、特に、図６に示すように、亀裂２Ｂの上下両側に
積層されている複数枚のレンガを貫通した状態となる。
このようにして削孔された孔３０Ａおよび３０Ｙは、互
いに、水平方向にある程度の間隔をおいて、亀裂２Ｂの
断面と交差する位置で互いに水平方向に立体交差するよ
うに配設される。Holes 30A and 30 thus drilled
In particular, Y is in a state of penetrating a plurality of bricks laminated on both upper and lower sides of the crack 2B, as shown in FIG.
The holes 30 </ b> A and 30 </ b> Y thus drilled are arranged so as to horizontally intersect each other at a certain distance in the horizontal direction at a position intersecting the cross section of the crack 2 </ b> B.
【００３８】以下、図示しないが、同様に、必要な数の
孔を削孔する。ここで、孔の削孔数は、レンガ壁体１の
亀裂２Ｂの発生状態によるが、平方米当たり、４〜６箇
所程度で十分である。次に、実施例１と同様のプライマ
ー１４を、孔３０Ａ内に５０〜１００ｇ程度流し込み、
塗布棒により孔３０Ａの内壁に塗り付ける。Although not shown, a required number of holes are similarly drilled below. Here, the number of holes to be drilled depends on the state of occurrence of the crack 2B of the brick wall body 1, but about 4 to 6 locations per square meter is sufficient. Next, about 50 to 100 g of the primer 14 similar to that of Example 1 is poured into the hole 30A,
The inner wall of the hole 30A is painted with a coating stick.
【００３９】次いで、実施例２と同様の接着材グラウド
４５を、前記プライマー１４が塗布された孔３０Ａ内
に、たとえば、グリスガンなどを使用して、孔３０Ａの
奥の方から注入し、充填する。なお、実施例３では、前
記プライマー１４と接着材グラウド４５が、請求項記載
の『エポキシ樹脂』に相当する。Then, the same adhesive grout 45 as that of the second embodiment is injected into the hole 30A coated with the primer 14 from the inner side of the hole 30A by using, for example, a grease gun to fill the hole. . In addition, in Example 3, the primer 14 and the adhesive material grove 45 correspond to the "epoxy resin" in the claims.
【００４０】次に、前記接着材グラウド４５が充填され
た孔３０Ａ内に、鉄筋５Ａをゆっくり挿入する。このよ
うにすることで、鉄筋５Ａは、プライマー１４と接着材
グラウド４５により、孔３０Ａ内に定着固定され亀裂２
Ｂを縫合する。このため、亀裂２Ｂと、亀裂２Ｂが生じ
ていない複数枚のレンガとを、強固に一体化することが
できる。なお、実施例３では、鉄筋５Ａとして、Ｄ−１
０を使用した。Next, the reinforcing bar 5A is slowly inserted into the hole 30A filled with the adhesive material grove 45. By doing so, the reinforcing bar 5A is fixed and fixed in the hole 30A by the primer 14 and the adhesive material grove 45, and the crack 2
Suture B. Therefore, the crack 2B and the plurality of bricks in which the crack 2B has not occurred can be firmly integrated. In addition, in Example 3, as rebar 5A, D-1
0 was used.
【００４１】次いで、孔３０Ａの入口を、レンガ粉６０
Ａにて補修する。このように、レンガ粉６０Ａにて補修
を行うため、レンガ壁体１本来の姿に支障を来すことな
く、レンガ壁体１の亀裂２Ｂを補強できる。次に、孔３
０Ｙ以降も前記と同様に、プライマー１４の塗布、接着
材グラウド４５の充填および鉄筋５Ｂの挿入を行った
後、レンガ粉（図５では、６０Ｘ，６０Ｙ）にて孔の入
口を補修する。Next, the entrance of the hole 30A is filled with the brick powder 60.
Repair at A. As described above, since the brick powder 60A is repaired, the crack 2B of the brick wall body 1 can be reinforced without affecting the original appearance of the brick wall body 1. Next, hole 3
After 0Y, the primer 14 is applied, the adhesive material grove 45 is filled and the reinforcing bar 5B is inserted in the same manner as described above, and then the entrance of the hole is repaired with brick powder (60X, 60Y in FIG. 5).
【００４２】このように、亀裂２Ｂは、水平方向の複数
の箇所で、前記縫合が行われた状態となるため、亀裂２
Ｂが生じたレンガ壁体１を効果的に且つ十分に補強する
ことができる。なお、実施例３では、図６に示すよう
に、亀裂２Ｂの上側から孔３０Ａおよび３０Ｙを削孔し
たが、これに限らず、前記孔は、亀裂２Ｂの下側から削
孔してもよいことは勿論である。 （実施例４）次に、本発明の実施例４について説明す
る。As described above, the crack 2B is in a state in which the suturing is performed at a plurality of positions in the horizontal direction.
The brick wall body 1 in which B is generated can be effectively and sufficiently reinforced. In Example 3, as shown in FIG. 6, the holes 30A and 30Y were drilled from the upper side of the crack 2B, but the present invention is not limited to this, and the holes may be drilled from the lower side of the crack 2B. Of course. (Fourth Embodiment) Next, a fourth embodiment of the present invention will be described.
【００４３】実施例４では、本発明にかかるレンガ壁体
の補強方法を採用した試験用レンガ壁体（発明品）と、
本発明にかかるレンガ壁体の補強方法を採用しない試験
用レンガ壁体（従来品）との比較を行う。表１に示す条
件で、各々の試験用レンガ壁体（Ｎｏ．１〜Ｎｏ．６）
について、せん断強度（Ｋｇ／ｃｍ2 ）の測定を行っ
た。なお、各試験用レンガ壁体のサイズ、厚さ、素材な
どは、同一とし、発明品と従来品との違いは、アンカー
（鉄筋）の有無のみとし、試験条件も同一とした。そし
て、発明品のアンカーの本数は、平方米当たりの本数と
した。In Example 4, a test brick wall body (invention product) adopting the method for reinforcing a brick wall body according to the present invention,
A comparison is made with a test brick wall body (conventional product) that does not employ the method for reinforcing a brick wall body according to the present invention. Under the conditions shown in Table 1, each test brick wall (No. 1 to No. 6)
The shear strength (Kg / cm 2 ) was measured. The size, thickness, material, etc. of each test brick wall were the same, and the difference between the invention product and the conventional product was only the presence or absence of an anchor (rebar) and the test conditions were also the same. The number of the anchors of the invention product was the number per square rice.
【００４４】この結果を表１に示す。The results are shown in Table 1.
【００４５】[0045]
【表１】 [Table 1]
【００４６】表１から、従来品（無補強のレンガ壁体）
の破壊荷重の平均値＝１１６．９トンであり、せん断強
度の平均値＝１２．８０Ｋｇｆ／ｃｍ2 、せん断強度の
標準偏差＝４．８０Ｋｇｆ／ｃｍ2 であることがわか
る。一方、発明品（補強したレンガ壁体）の破壊荷重の
平均値＝１２２．８トンであり、せん断強度の平均値＝
２０．４６Ｋｇｆ／ｃｍ2 、せん断強度の標準偏差＝
２．７１Ｋｇｆ／ｃｍ2 であることがわかる。また、ア
ンカーの本数により大差は見られなかったことがわか
る。From Table 1, the conventional product (unreinforced brick wall)
It can be seen that the average value of the fracture load is 116.9 tons, the average value of the shear strength is 12.80 Kgf / cm 2 , and the standard deviation of the shear strength is 4.80 Kgf / cm 2 . On the other hand, the average value of the breaking load of the invention product (reinforced brick wall) = 122.8 tons, and the average value of the shear strength =
20.46 Kgf / cm 2 , standard deviation of shear strength =
It can be seen that it is 2.71 Kgf / cm 2 . Also, it can be seen that no great difference was found depending on the number of anchors.
【００４７】これより、発明品は、従来品に比べ、破壊
荷重およびせん断強度共に向上したことが確認され、本
発明は、レンガ壁体を効果的に補強することができこと
が立証された。ここで、発明品のせん断強度のはらつき
分布を正規分布とみなし、９５％信頼確率によるせん断
強度の下限値を、式１から求める。From this, it was confirmed that the invented product had improved breaking load and shear strength as compared with the conventional product, and it was verified that the present invention can effectively reinforce the brick wall. Here, the fluctuation distribution of the shear strength of the invention product is regarded as a normal distribution, and the lower limit value of the shear strength based on the 95% confidence probability is obtained from Expression 1.
【００４８】せん断強度（σOK）＝平均値−ｔ分布値×
｛標準偏差値／（ｎ−１）0.5 ｝----- 式１ なお、本実施例の場合、ｎ＝３、ｔ分布値＝４．３０３
であり、表１および式１から、 σOK＝２０．４６−４．３０３×（２．７１／２0.5 ）
＝１２．２１ が得られる。Shear strength (σ OK ) = average value−t distribution value ×
{Standard deviation value / (n-1) 0.5 } ----- Equation 1 In the case of the present embodiment, n = 3, t distribution value = 4.303.
From Table 1 and Equation 1, σ OK = 20.46-4.303 × (2.71 / 2 0.5 )
= 12.21 is obtained.
【００４９】これは、片側検定であるため、せん断強度
１２．２１Ｋｇｆ／ｃｍ2 を下回るのは、２．５％以下
の確率であり、発明品のせん断強度は、１２．２１Ｋｇ
ｆ／ｃｍ2 以上と考えて差し支えない。なお、実施例１
ないし実施例３では、直径φ２８ｍｍの孔を削孔した場
合について説明したが、これに限らず、本発明にかかる
レンガ壁体の補強方法で削孔する孔の径は、所望により
決定してよい。Since this is a one-sided test, the probability that the shear strength is less than 12.21 Kgf / cm 2 is 2.5% or less, and the shear strength of the invention product is 12.21 Kg.
It can be considered as f / cm 2 or more. In addition, Example 1
In the third embodiment, the case where a hole having a diameter of 28 mm is drilled has been described, but the present invention is not limited to this, and the diameter of the hole drilled by the method for reinforcing a brick wall according to the present invention may be determined as desired. .
【００５０】また、実施例１ないし実施例３では、レン
ガ壁体１の内側面１１あるいは外側面１２に対して、入
射角が４５〜６０度となるように、孔を削孔したが、こ
れに限らず、前記孔の角度は、所望により決定してよ
い。そして、実施例１ないし実施例３では、低粘度エポ
キシ樹脂ＣＣＲエポ４１と硬化材とからなるプライマー
１４を使用したが、これに限らず、プライマー１４は、
主成分がエポキシ樹脂からなれば、他の組成を有しても
よい。In the first to third embodiments, the inner wall surface 11 or the outer wall surface 12 of the brick wall 1 is drilled so that the incident angle is 45 to 60 degrees. However, the angle of the holes may be determined as desired. And in Example 1 thru | or Example 3, although the primer 14 which consists of the low-viscosity epoxy resin CCR Epo 41 and the hardening | curing material was used, it is not restricted to this, The primer 14 is as follows.
If the main component is an epoxy resin, it may have another composition.
【００５１】また、実施例１では、プライマー１４と同
一組成の接着材グラウド１５を使用し、実施例２および
実施例３では、低粘度エポキシ樹脂ＣＣＲエポ４２と硬
化材とからなる接着材グラウド４５を使用したが、これ
に限らず、接着材グラウドは、主成分がエポキシ樹脂か
らなれば、他の組成を有してもよい。そして、実施例１
ないし実施例３では、削孔した孔の内壁に、プライマー
を塗布した後、接着材グラウドを充填する方法について
説明したが、これに限らず、前記孔内には、エポキシ樹
脂を一度に充填してもよい。Further, in Example 1, an adhesive material grove 15 having the same composition as that of the primer 14 was used, and in Examples 2 and 3, an adhesive material grout 45 composed of a low-viscosity epoxy resin CCR Epo 42 and a curing material was used. However, not limited to this, the adhesive material ground may have another composition as long as the main component is an epoxy resin. And Example 1
In Example 3, the method of filling the inner wall of the drilled hole with the primer and then filling the adhesive material with the primer was described, but the method is not limited to this, and the hole is filled with the epoxy resin at one time. May be.
【００５２】そしてまた、実施例１ないし実施例３で
は、孔に挿入する鉄筋として、Ｄ−１０を使用したが、
これに限らず、鉄筋の種類は、削孔した孔のサイズや、
レンガ壁体に生じた亀裂などに応じて、任意に決定して
よい。さらにまた、実施例１ないし実施例３では、ベビ
ー削岩機を用いて削孔を行ったが、これに限らず、削孔
は、削孔する孔のサイズや、レンガ壁体に生じた亀裂な
どに応じて、たとえば、ハンマードリルなど、他の装置
を使用して行ってもよい。Further, in Examples 1 to 3, D-10 was used as the reinforcing bar to be inserted into the hole.
Not limited to this, the type of rebar, the size of the drilled holes,
It may be arbitrarily determined according to a crack or the like generated in the brick wall body. Furthermore, in Example 1 to Example 3, the baby rock drill was used to perform the drilling, but the drilling is not limited to this, and the drilling is performed by the size of the hole to be drilled or a crack generated in the brick wall body. For example, other devices such as a hammer drill may be used.
【００５３】[0053]
【発明の効果】以上説明してきたように、請求項１記載
のレンガ壁体の補強方法によれば、前記レンガ壁体に略
垂直方向の亀裂が生じた場合、前記レンガ壁体の厚さ方
向に、前記亀裂を挟んで該亀裂と壁体内外両表面に所定
の間隔をおいて互いに垂直方向に所定の間隔をおいた位
置から、前記レンガ壁体の厚さ方向略中央部で前記亀裂
の断面と交差する孔を複数削孔するため、当該孔を前記
亀裂を挟んで両側に積層されている亀裂が生じていない
複数枚のレンガに貫通された孔を削孔することができ
る。また、前記孔内に接着剤を充填した後、当該孔内に
鉄筋を挿入するため、前記亀裂と、亀裂の生じていない
複数枚のレンガとを、レンガ壁体の厚さ方向略中央部で
あって、垂直方向の複数の箇所で縫合することができ
る。この結果、前記両者を一体化することができ、前記
亀裂が生じたレンガ壁体を、効率よく補強することがで
きる。As described above, according to the method for reinforcing a brick wall body according to the first aspect, when a crack in a substantially vertical direction occurs in the brick wall body, the brick wall body has a thickness direction. In, from the position with a predetermined interval in the vertical direction with respect to the crack and both surfaces inside and outside the wall and the crack across the crack, in the thickness direction substantially central portion of the brick wall of the crack Since a plurality of holes intersecting the cross section are drilled, it is possible to drill holes penetrated by a plurality of bricks which are laminated on both sides of the crack and have no cracks. In addition, after filling the hole with an adhesive, in order to insert a reinforcing bar in the hole, the crack, and a plurality of bricks without cracks, in the thickness direction substantially central portion of the brick wall body. Therefore, it can be sewn at multiple points in the vertical direction. As a result, the both can be integrated, and the brick wall body having the crack can be efficiently reinforced.
【００５４】そして、請求項２記載のレンガ壁体の補強
方法によれば、前記レンガ壁体に略水平方向の亀裂が生
じた場合、前記レンガ壁体の厚さ方向同一側面であっ
て、前記亀裂を挟んで該亀裂と所定の間隔をおいた両側
且つ互いに水平方向に所定の間隔をおいた位置、また
は、前記レンガ壁体の厚さ方向の両側面であって、前記
亀裂から同一垂直方向に所定の間隔をおき且つ互いに水
平方向に所定の間隔をおいた位置から、前記レンガ壁体
の厚さ方向略中央部で前記亀裂の断面と交差する孔を複
数削孔するため、当該孔を前記亀裂を挟んで上下両側に
積層されている亀裂が生じていない複数枚のレンガに貫
通された孔を削孔することができる。また、前記孔内に
接着材を充填した後、当該孔内に鉄筋を挿入するため、
前記亀裂と、亀裂の生じていない複数枚のレンガとを、
レンガ壁体の厚さ方向略中央部であって、垂直方向の複
数の箇所で縫合することができる。この結果、前記両者
を一体化することができ、前記亀裂が生じたレンガ壁体
を、効率よく補強することができる。According to the brick wall reinforcing method of the second aspect, when a crack in a substantially horizontal direction occurs in the brick wall, the brick wall has the same side in the thickness direction, and Positions on both sides of the crack with a predetermined distance and a predetermined distance in the horizontal direction from each other, or on both sides in the thickness direction of the brick wall, the same vertical direction from the crack In order to drill a plurality of holes intersecting the cross section of the crack in the thickness direction substantially central portion of the brick wall body, from the positions with a predetermined interval in the horizontal direction and a predetermined distance from each other in the horizontal direction. It is possible to drill holes penetrating a plurality of bricks which are laminated on the upper and lower sides with the crack interposed therebetween and in which no crack has occurred. Also, after filling the hole with an adhesive, to insert the reinforcing bar in the hole,
The crack and a plurality of bricks without cracks,
The brick wall can be sewn at a plurality of locations in the vertical direction, which is substantially the center in the thickness direction. As a result, the both can be integrated, and the brick wall body having the crack can be efficiently reinforced.
【図１】本発明の実施例１にかかるレンガ造りの建物を
構成するレンガ壁体に、略垂直方向の亀裂が生じた状態
を内側からみた側面図である。FIG. 1 is a side view of a brick wall constituting a brick building according to a first embodiment of the present invention, in which a crack in a substantially vertical direction is viewed from the inside.
【図２】図１の一部Ａ−Ａ断面図である。FIG. 2 is a partial AA sectional view of FIG.
【図３】本発明の実施例２にかかるレンガ造りの建物を
構成するレンガ壁体に、略垂直方向の亀裂が生じた状態
を内側からみた側面図である。FIG. 3 is a side view of a brick wall constituting a brick building according to a second embodiment of the present invention, in which a crack in a substantially vertical direction is viewed from the inside.
【図４】図３の一部Ｃ−Ｃ断面図である。4 is a sectional view taken along the line CC of FIG.
【図５】本発明の実施例３にかかるレンガ造りの建物を
構成するレンガ壁体に、略垂直方向の亀裂が生じた状態
を内側からみた側面図である。[Fig. 5] Fig. 5 is a side view of a brick wall constituting a brick building according to a third embodiment of the present invention, in which a crack in a substantially vertical direction is seen from the inside.
【図６】図５の一部Ｄ−Ｄ断面図である。6 is a partial DD cross-sectional view of FIG.
【図７】従来例にかかる一部断面図である。FIG. 7 is a partial cross-sectional view of a conventional example.
【図８】従来例にかかる一部断面図である。FIG. 8 is a partial cross-sectional view of a conventional example.
１ レンガ壁体 ２Ａ 亀裂 ２Ｂ 亀裂 ３Ａ 孔 ５Ａ 鉄筋 ６Ａ レンガ粉 １１ 内側面 １２ 外側面 １４ プライマー １５ 接着材グラウド 1 Brick Wall 2A Crack 2B Crack 3A Hole 5A Reinforcing Bar 6A Brick Powder 11 Inner Side 12 Outer Side 14 Primer 15 Adhesive Grout
Claims (2)
補強方法において、前記レンガ壁体の厚さ方向に、前記
亀裂を挟んで該亀裂と壁体内外両表面に所定の間隔をお
いて互いに垂直方向に所定の間隔をおいた位置から、前
記レンガ壁体の厚さ方向略中央部で前記亀裂の断面と交
差する孔を複数削孔する工程と、前記孔内に接着材を充
填する工程と、前記接着剤が充填された孔内に鉄筋を挿
入して前記接着剤で埋め込む工程と、前記亀裂に接着材
を充填する工程と、を含んでなることを特徴とするレン
ガ壁体の補強方法。1. A method of reinforcing a brick wall in which a crack is generated in a substantially vertical direction, wherein a predetermined space is provided between the crack and both the inside and outside surfaces of the wall in the thickness direction of the brick wall with the crack interposed. And from a position with a predetermined interval in the direction perpendicular to each other, a step of drilling a plurality of holes intersecting the cross section of the crack at the substantially central portion in the thickness direction of the brick wall, and filling the hole with an adhesive. Brick wall body, comprising: a step of, a step of inserting a reinforcing bar into the hole filled with the adhesive and embedding it with the adhesive, and a step of filling the crack with the adhesive. Reinforcement method.
補強方法において、前記レンガ壁体の厚さ方向同一側面
であって、前記亀裂を挟んで該亀裂と所定の間隔をおい
た両側且つ互いに水平方向に所定の間隔をおいた位置、
または、前記レンガ壁体の厚さ方向の両側面であって、
前記亀裂から同一垂直方向に所定の間隔をおき且つ互い
に水平方向に所定の間隔をおいた位置から、前記レンガ
壁体の厚さ方向略中央部で前記亀裂の断面と交差する孔
を複数削孔する工程と、前記孔内に接着剤を充填する工
程と、前記接着剤が充填された孔内に鉄筋を挿入して前
記接着剤で埋め込む工程と、前記亀裂に接着材を充填す
る工程と、を含んでなることを特徴とするレンガ壁体の
補強方法。2. A method of reinforcing a brick wall body in which a crack is generated in a substantially horizontal direction, wherein both sides of the brick wall body on the same side in the thickness direction are spaced apart from the crack by a predetermined distance. And positions that are horizontally spaced from each other,
Or, on both side surfaces in the thickness direction of the brick wall,
A plurality of holes that intersect with the cross section of the crack at substantially the center in the thickness direction of the brick wall are drilled from positions that have a predetermined distance in the same vertical direction from the crack and are spaced from each other by a predetermined distance in the horizontal direction. A step of filling the hole with an adhesive, a step of inserting a reinforcing bar into the hole filled with the adhesive and embedding it with the adhesive, and a step of filling the crack with the adhesive, A method for reinforcing a brick wall, which comprises: