JPH0692552B2 - Ink composition for marking pen - Google Patents
Ink composition for marking penInfo
- Publication number
- JPH0692552B2 JPH0692552B2 JP2335032A JP33503290A JPH0692552B2 JP H0692552 B2 JPH0692552 B2 JP H0692552B2 JP 2335032 A JP2335032 A JP 2335032A JP 33503290 A JP33503290 A JP 33503290A JP H0692552 B2 JPH0692552 B2 JP H0692552B2
- Authority
- JP
- Japan
- Prior art keywords
- ink composition
- water
- resin
- marking pen
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、マーキングペン用インキ組成物に関し、詳し
くは、経時安定性にすぐれ、更に、消去性インキ組成物
の場合は、経時的な消去性にもすぐれる水性マーキング
ペン用インキ組成物に関する。TECHNICAL FIELD The present invention relates to an ink composition for a marking pen, and more specifically, it has excellent stability over time, and in the case of an erasable ink composition, it can be erased over time. It relates to an aqueous marking pen ink composition having excellent properties.
（従来の技術） 従来、多孔質樹脂や樹脂含浸した繊維束からなるペン先
を備えたマーキングペン用インキ組成物は、例えば、特
開昭49−29号公報や特公昭62−9148号公報等に記載され
ているように、一般に、着色剤、樹脂、その他の添加剤
を有機溶媒に分散又は溶解させて調製されており、上記
有機溶剤としては、通常、アルコール類、ケトン類、芳
香族炭化水素類が多用されている。しかし、これら有機
溶剤は、一般に、臭気を有するのみならず、多くは毒性
を有しているので、近年、水性のマーキングペン用イン
キ組成物が種々提案されている。(Prior Art) Conventionally, an ink composition for a marking pen provided with a pen tip composed of a porous resin or a resin-impregnated fiber bundle is disclosed in, for example, JP-A-49-29 or JP-B-62-9148. In general, the coloring agent, the resin, and other additives are dispersed or dissolved in an organic solvent, and the organic solvent is usually an alcohol, a ketone, or an aromatic carbon. Hydrogen is often used. However, since these organic solvents generally have not only odor but also toxicity, various aqueous ink compositions for marking pens have been proposed in recent years.
例えば、特開平１−174577号公報には、インキ組成物に
おける着色剤の分散性を高めると共に、筆記面上に形成
した筆跡の造膜性を高めるために、ポリビニルアルコー
ル等の水溶性の樹脂を配合してなる水性インキ組成物が
提案されている。しかし、ポリビニルアルコールは、分
子中の水酸基が分子内及び分子間で会合して、インキ組
成物の粘度を経時的に高めるので、インキ組成物は、そ
の結果として、経時的に筆記性が悪くなる。即ち、経時
の筆記安定性に劣る。例えば、インキ組成物をマーキン
グペンに充填後、長期にわたつて保存したようなとき
は、インキ組成物がペン先を浸透透過し難くなつて、筆
跡が掠れたり、或いは遂には筆記不能となつたりする。For example, in JP-A No. 1-174577, a water-soluble resin such as polyvinyl alcohol is used in order to enhance the dispersibility of the colorant in the ink composition and the film-forming property of the handwriting formed on the writing surface. A water-based ink composition prepared by blending has been proposed. However, in the case of polyvinyl alcohol, the hydroxyl groups in the molecule associate with each other within and between the molecules to increase the viscosity of the ink composition over time, and as a result, the ink composition becomes poor in writability over time. . That is, the writing stability over time is poor. For example, when the ink composition is filled in a marking pen and then stored for a long period of time, the ink composition is difficult to permeate and penetrate the pen tip, and the handwriting may be blurred, or the writing may eventually become impossible. To do.
また、ポリビニルアルコールを配合した水性インキ組成
物は高湿度下で吸湿するので、所謂剥離剤を含有する消
去性インキ組成物の場合、筆跡の筆記面への密着性が高
まり、消去性の経時的に低下する。In addition, since an aqueous ink composition containing polyvinyl alcohol absorbs moisture under high humidity, in the case of an erasable ink composition containing a so-called release agent, the adhesion to the writing surface of the handwriting is increased, and the erasability is improved with time. Fall to.
（発明が解決しようとする課題） 本発明は、従来の水性マーキングペン用インキ組成物に
おける上記した問題を解決するためになされたものであ
つて、経時の筆記性又は安定性にすぐれ、更に、消去性
インキ組成物の場合には、経時の消去性にもすぐれる水
性マーキングペン用インキ組成物を提供することを目的
とする。(Problems to be Solved by the Invention) The present invention has been made to solve the above-mentioned problems in conventional ink compositions for water-based marking pens, and is excellent in writability or stability over time, and further, In the case of an erasable ink composition, it is an object of the invention to provide an aqueous marking pen ink composition which is also excellent in erasability over time.
（課題を解決するための手段） 本発明は、水、脂肪族低級アルコール、着色剤及び樹脂
を含有するマーキングペン用インキ組成物において、上
記樹脂がポリビニルベンザールであることを特徴とす
る。また、本発明による消去性インキ組成物は、上記に
加えて、筆跡に消去性を与える剥離剤を含有する。(Means for Solving the Problems) The present invention is an ink composition for a marking pen containing water, an aliphatic lower alcohol, a colorant and a resin, wherein the resin is polyvinyl benzal. In addition to the above, the erasable ink composition according to the present invention contains a release agent that imparts erasability to handwriting.
本発明によるインキ組成物は、インキ組成物における着
色剤の分散性を高め、また、筆跡に筆記面上での付着性
や造膜性、レベリング性を与えるために、樹脂として、
ポリビニルベンザールを溶解含有している。このポリビ
ニルベンザールは、ポリビニルアルコールをベンズアル
デヒドでアセタール化してなるものであつて、本発明に
おいては、特に、重合度200〜800、ケン化度75〜99.5モ
ル％であるポリビニルアルコールを約６〜13モル％の範
囲でベンズアルデヒドでアセタール化してなるものが好
ましく用いられる。The ink composition according to the present invention enhances the dispersibility of the colorant in the ink composition, and as a resin in order to impart the adhesiveness, the film forming property, and the leveling property on the writing surface to the handwriting,
Contains polyvinyl benzal in a dissolved state. This polyvinyl benzal is obtained by acetalizing polyvinyl alcohol with benzaldehyde, and in the present invention, particularly, polyvinyl alcohol having a polymerization degree of 200 to 800 and a saponification degree of 75 to 99.5 mol% is about 6 to 13%. Those obtained by acetalizing with benzaldehyde in the range of mol% are preferably used.
このようなポリビニルベンザールは、水又は脂肪族低級
アルコールのそれぞれ単独には溶解しないが、水と脂肪
族低級アルコールとの混合溶剤にはよく溶解する。本発
明によるインキ組成物において、ポリビニルベンザール
は、通常、0.5〜15重量％、好ましくは、１〜６重量％
の範囲で配合される。配合量が余りに少ないときは、イ
ンキ組成物における着色剤の分散が不十分であり、ま
た、筆跡の造膜性を不十分であるので、筆記性に劣る。
他方、配合量が余りに多いときは、インキ組成物の粘度
が過度に高くなるので、同様に、筆記性に劣る。Such polyvinyl benzal is not soluble in water or an aliphatic lower alcohol alone, but is well soluble in a mixed solvent of water and an aliphatic lower alcohol. In the ink composition according to the present invention, polyvinyl benzal is usually contained in an amount of 0.5 to 15% by weight, preferably 1 to 6% by weight.
It is mixed in the range of. If the blending amount is too small, the dispersibility of the colorant in the ink composition will be insufficient, and the handwriting film-forming property will be insufficient, resulting in poor writing performance.
On the other hand, when the blending amount is too large, the viscosity of the ink composition becomes excessively high, and similarly, the writability is poor.
上述したように、本発明において用いるポリビニルベン
ザールは、水又は脂肪族低級アルコールのそれぞれ単独
には溶解しないが、水と脂肪族低級アルコールとの混合
溶剤にはよく溶解するので、本発明によるインキ組成物
においては、水と脂肪族低級アルコールとの混合物が溶
剤として用いられる。脂肪族低級アルコールは、水と任
意の割合で相溶するものが好ましくは、特に、エタノー
ルが好ましく用いられる。インキ組成物における溶剤量
は、通常、50〜90重量％の範囲である。As described above, the polyvinylbenzal used in the present invention does not dissolve in water or an aliphatic lower alcohol alone, but dissolves well in a mixed solvent of water and an aliphatic lower alcohol. In the composition, a mixture of water and an aliphatic lower alcohol is used as a solvent. The aliphatic lower alcohol is preferably compatible with water at an arbitrary ratio, and ethanol is particularly preferably used. The amount of solvent in the ink composition is usually in the range of 50 to 90% by weight.
このような混合溶媒において、水と脂肪族低級アルコー
ルとの割合は、30:70〜70:30の範囲が好適である。ベン
ズアルデヒドのアセタール化度が高いほど、アルコール
の割合を高くすることが好ましい。In such a mixed solvent, the ratio of water to the aliphatic lower alcohol is preferably in the range of 30:70 to 70:30. The higher the degree of acetalization of benzaldehyde, the higher the proportion of alcohol.
本発明によるマーキングペンインキ用組成物において、
着色剤としては、無彩色又は有彩色の顔料が好ましく用
いられる。例えば、カーボンブラツク、フタロシアニン
ブルー、フタロシアニングリーン等、任意のものが用い
られるが、これらに限定されるものではない。In the composition for marking pen ink according to the present invention,
An achromatic or chromatic pigment is preferably used as the colorant. For example, carbon black, phthalocyanine blue, phthalocyanine green, and the like may be used, but the invention is not limited thereto.
着色剤は、インキ組成物において、通常、１〜30重量％
の範囲で配合される。着色剤を過多に含有させるとき
は、インキ組成物の粘度が高すぎるために、筆記性に劣
り、他方、着色剤の含量が少なすぎるときは、筆跡の濃
度が薄く、実用的ではない。The colorant is usually 1 to 30% by weight in the ink composition.
It is mixed in the range of. When the colorant is contained in excess, the ink composition has too high a viscosity, resulting in poor writing performance. On the other hand, when the content of the colorant is too small, the concentration of handwriting is too thin to be practical.
本発明によれば、水性インキ組成物において既に知られ
ている種々の剥離剤やその作用を助ける所謂剥離助剤を
含有させることによつて、消去性のマーキングペンイン
キ組成物とすることができる。消去性インキ組成物と
は、非吸収性乃至非透過性筆記面上に形成した筆跡を柔
らかい乾布や紙で拭き消すことができるインキ組成物を
いう。例えば、剥離剤としては、種々の微小な樹脂粒子
が用いられ、また、剥離助剤としては、例えば、常温で
液状の難揮発性水溶性物質や、或いは常温で液状の難揮
発性水不溶性物質の水性エマルジヨン等が用いられる。According to the present invention, it is possible to obtain an erasable marking pen ink composition by including various kinds of release agents already known in water-based ink compositions and so-called release aids that aid the action of the release agents. . The erasable ink composition means an ink composition capable of wiping off the handwriting formed on the non-absorbent or non-permeable writing surface with a soft dry cloth or paper. For example, various minute resin particles are used as the release agent, and as the release aid, for example, a hardly volatile water-soluble substance that is liquid at room temperature or a hardly volatile water-insoluble substance that is liquid at room temperature. Aqueous emulsion of the above is used.
上記剥離剤としての樹脂粒子としては、例えば、ポリメ
タクリル酸メチル、アクリル−スチレン共重合体、ポリ
スチレン、ポリ塩化ビニル、エポキシ樹脂、メラミン樹
脂、ベンゾグアナミン樹脂等からなる微小な粒子、ま
た、ポリ酢酸ビニル、ポリスチレン、アクリル−スチレ
ン共重合体、ポリメタクリル酸メチル等からなる樹脂エ
マルジヨンが用いられる。Examples of the resin particles as the release agent include fine particles of polymethylmethacrylate, acryl-styrene copolymer, polystyrene, polyvinyl chloride, epoxy resin, melamine resin, benzoguanamine resin, and polyvinyl acetate. Resin emulsions made of, for example, polystyrene, acrylic-styrene copolymer, and polymethylmethacrylate are used.
このような剥離剤は、通常１〜50重量％好ましくは１〜
40重量％の範囲で含有される。インキ組成物において、
剥離剤の配合量が１重量％よりも少ないときは十分な筆
跡の消去性を得ることができず、他方、50重量％を越え
て過多に配合したときは、筆跡の色調を変化させること
があるので好ましくない。Such a release agent is usually 1 to 50% by weight, preferably 1 to
It is contained in the range of 40% by weight. In the ink composition,
When the content of the release agent is less than 1% by weight, sufficient erasability of handwriting cannot be obtained. On the other hand, when the content of the release agent exceeds 50% by weight, the color tone of the handwriting may be changed. It is not preferable because it exists.
また、上記剥離助剤としての水溶性物質としては、例え
ば、グリセリン、エチレングリコール、プロピレングリ
コール等のグリコール類、ジエチレングリコール、トリ
エチレングリコール、ポリエチレングリコール、ジプロ
ピレングリコール、トリプロピレングリコール、ポリプ
ロピレングリコール等のポリアルキレングリコールを挙
げることができる。Examples of the water-soluble substance as the release aid include glycols such as glycerin, ethylene glycol and propylene glycol, polyethylene glycol such as diethylene glycol, triethylene glycol, polyethylene glycol, dipropylene glycol, tripropylene glycol and polypropylene glycol. Mention may be made of alkylene glycols.
常温で液状の難揮発性水不溶性物質の水性エマルジヨン
としては、例えば、脂肪族カルボン酸エステル、グリセ
リド、高級炭化水素等の水性エマルジヨンを挙げること
ができる。Examples of the aqueous emulsion of the hardly volatile water-insoluble substance that is liquid at room temperature include aqueous emulsions such as aliphatic carboxylic acid esters, glycerides, and higher hydrocarbons.
このような剥離助剤は、通常、インキ組成物において20
重量％以下、好ましくは10重量％以下の範囲で用いられ
る。インキ組成物において、剥離助剤の配合量が20重量
％を越えるときは、剥離助剤の分散性が悪く、得られる
インキ組成物は、却つて消去性が阻害される。Such a peeling aid is usually used in the ink composition.
It is used in a range of not more than 10% by weight, preferably not more than 10% by weight. In the ink composition, when the amount of the peeling aid compounded is more than 20% by weight, the dispersibility of the peeling aid is poor, and the ink composition obtained is rather impaired in erasability.
剥離剤や剥離助剤は、既に消去性インキ組成物の分野に
おいてよく知られており、本発明においても、前記例示
に限定されるものではない。Release agents and release aids are already well known in the field of erasable ink compositions, and the present invention is not limited to the above examples.
更に、本発明によるインキ組成物は、上記以外に、必要
に応じて、通常、水性インキ組成物に配合される任意の
pH調整剤や防腐剤を含有していてもよい。In addition to the above, the ink composition according to the present invention may optionally be added to an aqueous ink composition, if desired.
It may contain a pH adjuster or a preservative.
（実施例） 以下に実施例を挙げて本発明を説明するが、本発明はこ
れら実施例により何ら限定されるものではない。(Examples) Hereinafter, the present invention will be described with reference to examples, but the present invention is not limited to these examples.
実施例１ 重合度500、ケン化度88モル％のポリビニルアルコール1
80gを水1750gに加え、90℃で約２時間攪拌して溶解させ
た。この後、45℃に冷却し、これに35重量％濃度の塩酸
55gを加え、更に20℃まで冷却した。Example 1 Polyvinyl alcohol 1 having a polymerization degree of 500 and a saponification degree of 88 mol% 1
80 g was added to 1750 g of water and dissolved by stirring at 90 ° C. for about 2 hours. After that, it was cooled to 45 ° C and 35% by weight hydrochloric acid was added to this.
55 g was added and further cooled to 20 ° C.
次いで、これに純度99％のベンズアルデヒド25gを加
え、20℃で４時間反応させて、白濁した反応混合物を得
た。Next, 25 g of benzaldehyde having a purity of 99% was added thereto, and the mixture was reacted at 20 ° C. for 4 hours to obtain a cloudy reaction mixture.
この反応混合物を攪拌下に20重量％濃度の水酸化ナトリ
ウム水溶液に105gを加えて中和し、脱水することによつ
て、スラリー状の含水樹脂を得た。この含水樹脂に水と
エタノールとを加えて樹脂を溶解させ、水／エタノール
（1/1）を溶媒とする10重量％のポリビニルベンザール
溶液を得た。This reaction mixture was neutralized by adding 105 g to a 20% by weight aqueous sodium hydroxide solution under stirring, and dehydrated to obtain a water-containing resin in a slurry form. Water and ethanol were added to this water-containing resin to dissolve the resin, and a 10% by weight polyvinylbenzal solution using water / ethanol (1/1) as a solvent was obtained.
この溶液をポリエチレンフイルム上に流延し、乾燥させ
て透明なフイルムを得た。このフイルムをDMSO−d6溶液
に溶解し、1H−NMRによつて測定したベンザール化度は
８モル％であつた。This solution was cast on a polyethylene film and dried to obtain a transparent film. The film was dissolved in DMSO-d 6 solution, benzal degree that have been conducted under the measured 1 H-NMR was found to be 8 mol%.
このようにして得られた10重量％のポリビニルベンザー
ル溶液30g、カーボンブラツク5g、アクリル−スチレン
共重合体樹脂（昭和高分子（株）製ポリゾールAT−201
1）6g及びポリエチレングリコール（平均分子量200）2g
を水／エタノール混合溶液（1/1）65g中に溶解分散させ
て、黒色インキ組成物を得た。30 g of a 10% by weight polyvinyl benzal solution thus obtained, 5 g of carbon black, acrylic-styrene copolymer resin (Polysol AT-201 manufactured by Showa Highpolymer Co., Ltd.)
1) 6g and polyethylene glycol (average molecular weight 200) 2g
Was dissolved and dispersed in 65 g of a water / ethanol mixed solution (1/1) to obtain a black ink composition.
実施例２ 重合度500、ケン化度98モル％のポリビニルアルコール1
80gとベンズアルデヒド28gを用いた以外は、実施例１と
同様にして、水／エタノール（6/4）を溶媒とするベン
ザール化度９モル％のポリビニルベンザールの10重量％
溶液を得た。Example 2 Polyvinyl alcohol 1 having a degree of polymerization of 500 and a degree of saponification of 98 mol% 1
10% by weight of polyvinylbenzal having a benzalation degree of 9 mol% and using water / ethanol (6/4) as a solvent in the same manner as in Example 1 except that 80 g and benzaldehyde 28 g were used.
A solution was obtained.
このようにして得られた10重量％のポリビニルベンザー
ル溶液50g、カーボンブラツク4g、アクリル−スチレン
共重合体樹脂（昭和高分子（株）製ポリゾールAT−201
1）4g及びポリエチレングリコール（平均分子量200）2g
を水／エタノール混合溶液（6/4）45g中に溶解分散させ
て、黒色インキ組成物を得た。50 g of a 10% by weight polyvinyl benzal solution thus obtained, 4 g of carbon black, acrylic-styrene copolymer resin (Polysol AT-201 manufactured by Showa Highpolymer Co., Ltd.)
1) 4g and polyethylene glycol (average molecular weight 200) 2g
Was dissolved and dispersed in 45 g of a water / ethanol mixed solution (6/4) to obtain a black ink composition.
実施例３ 重合度300、ケン化度80モル％のポリビニルアルコール1
80gとベンズアルデヒド20gを用いた以外は、実施例１と
同様にして、水／エタノール（7/3）を溶媒とするベン
ザール化度６モル％のポリビニルベンザールの15重量％
溶液を得た。Example 3 Polyvinyl alcohol 1 having a degree of polymerization of 300 and a degree of saponification of 80 mol% 1
15% by weight of polyvinylbenzal having a benzalization degree of 6 mol% and using water / ethanol (7/3) as a solvent in the same manner as in Example 1 except that 80 g and benzaldehyde 20 g were used.
A solution was obtained.
このようにして得られた15重量％のポリビニルベンザー
ル溶液30g、カーボンブラツク6g、ポリスチレン樹脂
（旭化成工業（株）製ラテツクスSBL8801）15g及びジエ
チレングリコール3gを水／エタノール混合溶液（7/3）4
5g中に溶解分散させて、黒色インキ組成物を得た。30 g of the 15 wt% polyvinylbenzal solution thus obtained, 6 g of carbon black, 15 g of polystyrene resin (Latex SBL8801 manufactured by Asahi Kasei Kogyo Co., Ltd.) and 3 g of diethylene glycol were mixed with water / ethanol (7/3) 4
It was dissolved and dispersed in 5 g to obtain a black ink composition.
実施例４ 重合度700、ケン化度99.5モル％のポリビニルアルコー
ル180gとベンズアルデヒド33gを用いた以外は、実施例
１と同様にして、水／エタノール（1/1）を溶媒とする
ベンザール化度12モル％のポリビニルベンザールの10重
量％溶液を得た。Example 4 A benzalization degree of 12 using water / ethanol (1/1) as a solvent was used in the same manner as in Example 1 except that 180 g of polyvinyl alcohol having a polymerization degree of 700 and a saponification degree of 99.5 mol% and 33 g of benzaldehyde were used. A 10% by weight solution of mol% polyvinylbenzal was obtained.
このようにして得られた10重量％のポリビニルベンザー
ル溶液15g、カーボンブラツク3g、アクリル−スチレン
共重合体樹脂（昭和高分子（株）製ポリゾールAT−201
1）10g及びグリセリン2gを水／エタノール混合溶液（1/
1）80g中に溶解分散させて、黒色インキ組成物を得た。15 g of a 10% by weight polyvinyl benzal solution thus obtained, 3 g of carbon black, acrylic-styrene copolymer resin (Polysol AT-201 manufactured by Showa Highpolymer Co., Ltd.)
1) 10g and glycerin 2g water / ethanol mixed solution (1 /
1) Dissolved in 80 g to obtain a black ink composition.
比較例１ 重合度500、ケン化度88モル％のポリビニルアルコール5
g、カーボンブラツク4g、アクリル−スチレン共重合体
樹脂（昭和高分子（株）製ポリゾールAT−2011）6g及び
ポリエチレングリコール（平均分子量200）2gを水／エ
タノール混合溶液（9/1）90g中に溶解分散させて、黒色
インキ組成物を得た。Comparative Example 1 Polyvinyl alcohol 5 having a degree of polymerization of 500 and a degree of saponification of 88 mol% 5
g, carbon black 4 g, acrylic-styrene copolymer resin (Polysol AT-2011 manufactured by Showa Highpolymer Co., Ltd.) 6 g and polyethylene glycol (average molecular weight 200) 2 g in water / ethanol mixed solution (9/1) 90 g It was dissolved and dispersed to obtain a black ink composition.
比較例２ 重合度300、ケン化度98モル％のポリビニルアルコール8
g、カーボンブラツク6g、ポリスチレン樹脂（旭化成工
業（株）製ラテツクスSBL8801）15g及びジエチレングリ
コール3gを水／エタノール混合溶液（9/1）90g中に溶解
分散させて、黒色インキ組成物を得た。Comparative Example 2 Polyvinyl alcohol 8 having a degree of polymerization of 300 and a degree of saponification of 98 mol% 8
g, carbon black 6 g, polystyrene resin (Latex SBL8801 manufactured by Asahi Chemical Industry Co., Ltd.) 15 g and diethylene glycol 3 g were dissolved and dispersed in 90 g of a water / ethanol mixed solution (9/1) to obtain a black ink composition.
以上のようにして得たそれぞれのインキ組成物をほうろ
うからなる非吸収性筆記面に筆記し、５分間放置して乾
燥させ、この筆跡を乾布で軽く擦過したときの筆跡の消
去性（筆記後初期消去性）と、温度25度、湿度60％RHで
１か月間放置した後の同様の消去性（筆記後経時消去
性）を調べた。Each of the ink compositions obtained as described above is written on a non-absorbent writing surface made of enamel, left standing for 5 minutes to dry, and the handwriting is erased when lightly rubbed with a dry cloth (after writing). The initial erasability) and the same erasability (erasability after writing with time) after being left for 1 month at a temperature of 25 ° C. and a humidity of 60% RH were examined.
結果を第１表に示す。評価は、◎が極めて良好、○が良
好、×が悪いの３段階（目視）とした。The results are shown in Table 1. The evaluation was made into three grades (visual inspection): ⊚ is extremely good, ◯ is good, and x is bad.
更に、インキ組成物の調製直後に筆記した筆跡の消去性
（調製後初期消去性）と、インキ組成物の調製後、温度
40℃、湿度60％RHで１か月間放置した後に筆記した筆跡
の同様の消去性（調製後経時消去性）を前記同様にして
調べた。結果を第１表に示す。Furthermore, the erasability of the handwriting written immediately after the ink composition was prepared (the initial erasability after preparation) and the temperature after the ink composition was prepared.
The same erasability (erasability after preparation) of the handwriting written after leaving at 40 ° C and humidity 60% RH for 1 month was examined in the same manner as above. The results are shown in Table 1.
また、インキ組成物の調整直後に筆記した筆記性（調整
後初期筆記性）とインキ組成物の調整後、温度40℃、湿
度60％RHで１か月放置した後に筆記した筆記性（調整後
経時筆記性）を調べた。結果を第１表に示す。評価は上
記同様の３段階（目視）とした。In addition, the writability written immediately after preparation of the ink composition (initial writability after adjustment) and the writability written after leaving the ink composition for 1 month at a temperature of 40 ° C. and a humidity of 60% RH (after adjustment) (Writability over time) was examined. The results are shown in Table 1. The evaluation was made in the same three stages (visual inspection) as above.
筆記面がメラミン樹脂又はフツ素樹脂からなるときも、
上記とほぼ同様の結果を得た。Even when the writing surface is made of melamine resin or fluorine resin,
Results similar to the above were obtained.
（発明の効果） 本発明によるマーキングペン用インキ組成物は、水と脂
肪族低級アルコールとの混合溶剤からなる水性溶剤を用
い、着色剤と共にポリビニルベンザールを溶解させてな
るものである。 (Effect of the Invention) The ink composition for a marking pen according to the present invention comprises an aqueous solvent composed of a mixed solvent of water and an aliphatic lower alcohol, and a polyvinyl benzal dissolved with a colorant.
このポリビニルベンザールは、水性溶剤中での着色剤の
分散性を高めると共に、筆跡の造膜性を高める一方、ポ
リビニルアルコールを異なつて、分子中の水酸基が分子
内及び分子間で会合することがない。従つて、本発明に
よるインキ組成物は、経時的に粘度が増加することがな
く、マーキングペンを長期間にわたつて保存しても、常
にすぐれた筆記性を有する。This polyvinyl benzal enhances the dispersibility of the colorant in an aqueous solvent and enhances the film-forming property of the handwriting, while different polyvinyl alcohols allow the hydroxyl groups in the molecules to associate intramolecularly and intermolecularly. Absent. Therefore, the ink composition according to the present invention does not increase in viscosity with time and always has excellent writability even when the marking pen is stored for a long period of time.
更に、剥離剤及び剥離助剤を含有させてなる消去性イン
キ組成物の場合も、ポリビニルアルコールと異なり、ポ
リビニルベンザールは、高湿度条件下でも吸湿しないの
で、筆跡は、長期間にわたつて放置しても、すぐれた消
去性を保持している。Further, also in the case of an erasable ink composition containing a release agent and a release aid, unlike polyvinyl alcohol, polyvinyl benzal does not absorb moisture even under high humidity conditions, so handwriting should be left for a long period of time. However, it retains excellent erasability.
勿論、本発明によるマーキングペンインキ用組成物が、
溶剤が上記したように、脂肪族低級アルコールを含む水
性溶剤であるので、臭気も殆どないうえに、安全性にも
すぐれている。Of course, the composition for marking pen ink according to the present invention,
Since the solvent is an aqueous solvent containing an aliphatic lower alcohol as described above, it has almost no odor and is excellent in safety.
Claims (2)
脂を含有するマーキングペン用インキ組成物において、
上記樹脂がポリビニルベンザールであることを特徴とす
るマーキングペン用インキ組成物。1. A marking pen ink composition comprising water, an aliphatic lower alcohol, a colorant and a resin,
An ink composition for a marking pen, wherein the resin is polyvinyl benzal.
剤及び樹脂を含有するマーキングペン用消去性インキ組
成物において、上記樹脂がポリビニルベンザールである
ことを特徴とするマーキングペン用インキ組成物。2. An erasable ink composition for a marking pen containing water, an aliphatic lower alcohol, a colorant, a release agent and a resin, wherein the resin is polyvinylbenzal. object.