JPH068362A - Production of laminated sheet molded article - Google Patents
Production of laminated sheet molded articleInfo
- Publication number
- JPH068362A JPH068362A JP5017293A JP5017293A JPH068362A JP H068362 A JPH068362 A JP H068362A JP 5017293 A JP5017293 A JP 5017293A JP 5017293 A JP5017293 A JP 5017293A JP H068362 A JPH068362 A JP H068362A
- Authority
- JP
- Japan
- Prior art keywords
- phenol resin
- cardboard
- molded article
- foam
- laminated sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は主として自動車の成形天
井基材、ドアトリム基材等の内装基材に用いられる積層
材成形物の製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a laminated material molded product which is mainly used as an interior base material such as a molded ceiling base material and a door trim base material for automobiles.
【０００２】[0002]
【従来の技術】従来、この種の内装基材としては、ダン
ボール成形物が用いられていた。2. Description of the Related Art Conventionally, cardboard moldings have been used as this type of interior base material.
【０００３】[0003]
【発明が解決しようとする課題】ダンボール成形物は軽
量かつ安価であり、この面からは自動車の内装基材とし
て適しているが、耐熱性、耐湿性や吸音性に劣りまた易
燃性である。更にダンボール成形物は伸びに乏しく深絞
り成形部分に亀裂、しわ等を生じこれらが内装材の表面
に凹凸となって現われ、内装材の外観を著るしく損な
う。Cardboard moldings are lightweight and inexpensive, and from this point of view, they are suitable as interior base materials for automobiles, but they are inferior in heat resistance, moisture resistance and sound absorption, and are easily flammable. . Furthermore, the corrugated cardboard product has poor elongation and cracks, wrinkles, and the like appear in the deep-drawn part, and these appear as irregularities on the surface of the interior material, which significantly impairs the appearance of the interior material.
【０００４】[0004]
【課題を解決するための手段】本発明は上記従来の課題
を解決するための手段として、ダンボール(1) 表面に粉
状もしくは液状の発泡性フェノール樹脂初期縮合物を塗
布し、ホットプレスすることによって該ダンボール(1)
を所定形状に成形するとともに該発泡性フェノール樹脂
初期縮合物を発泡硬化せしめてフェノール樹脂発泡体
(2) とする積層材成形物(10)の製造方法を提供するもの
である。Means for Solving the Problems As a means for solving the above-mentioned conventional problems, the present invention comprises applying a powdery or liquid foamable phenol resin initial condensate to the surface of a cardboard (1) and hot pressing. By the cardboard (1)
Is molded into a predetermined shape, and the foamable phenol resin initial condensate is foam-cured to obtain a phenol resin foam.
(2) A method for producing a laminated material molded product (10) is provided.
【０００５】[0005]
【作用】ダンボール表面に粉状もしくは液状の発泡性フ
ェノール樹脂初期縮合物を塗布し、ホットプレスして該
ダンボールを所定形状に成形すると、該発泡性フェノー
ル樹脂初期縮合物は発泡しかつ樹脂化して硬化し、フェ
ノール樹脂発泡体となるが、上記成形過程においてダン
ボール表面に亀裂やしわ等が生じても、該フェノール樹
脂発泡体の形成過程において発泡かつ樹脂化しつゝある
フェノール樹脂初期縮合物によって該亀裂は充填されか
つしわは吸収される。そして該ダンボール表面に形成さ
れるフエノール樹脂発泡体は難燃性かつ耐熱性を有し、
また内部に空気を含有するから断熱性および吸音性に富
む。When the powdery or liquid foamable phenol resin initial condensate is applied to the surface of the cardboard and hot pressed to form the cardboard into a predetermined shape, the foamable phenolic resin precondensate foams and becomes a resin. Although it hardens to form a phenol resin foam, even if cracks, wrinkles, etc. occur on the cardboard surface during the above-mentioned molding process, the phenol resin initial condensation product that foams and becomes a resin during the formation process of the phenol resin foam Cracks fill and wrinkles are absorbed. And the phenol resin foam formed on the cardboard surface has flame resistance and heat resistance,
In addition, since it contains air inside, it is rich in heat insulation and sound absorption.
【０００６】[0006]
【発明の効果】したがって本発明においては、難燃性、
耐熱性、断熱性、および吸音性に富み、しかも成形して
も表面の平滑性を維持する積層材成形物が得られ、該積
層材成形物は自動車の内装基材等として有用である。Therefore, in the present invention, flame retardance,
A laminated material molded article that is excellent in heat resistance, heat insulation, and sound absorption and maintains the surface smoothness even when molded is obtained, and the laminated material molded article is useful as an interior base material for automobiles and the like.
【０００７】[0007]
【実施例】本発明を図１〜図４に示す一実施例によって
説明すれば、積層材成形物(10)はダンボール(1) と、該
ダンボール(1) の表面に形成されているフエノール樹脂
発泡体(2) とからなる。該積層材成形物(10)は例えば図
２に示すように天井形に成形されており、自動車の成形
天井の基材(11)として使用される。この場合には更に図
３に示すように繊維不織物、繊維編織物、人工レザー等
からなる表装材(3) をフエノール樹脂発泡体(2) 表面に
貼着する。EXAMPLES The present invention will be described with reference to one example shown in FIGS. 1 to 4. The laminated material molded product (10) comprises a cardboard (1) and a phenol resin formed on the surface of the cardboard (1). It consists of a foam (2). The laminated material molded product (10) is molded into a ceiling shape as shown in FIG. 2, for example, and is used as a base material (11) for a molded ceiling of an automobile. In this case, as shown in FIG. 3, a surface covering material (3) made of a fiber non-woven fabric, a fiber knitted fabric, artificial leather or the like is further attached to the surface of the phenol resin foam (2).
【０００８】本発明の積層材成形物(10)を製造するには
ダンボール(1) の表面に発泡性フエノール樹脂初期縮合
物の粉末または液体を塗布し、ホットプレスによって該
ダンボール(1) を所定形状に成形する。この際発泡性フ
ェノール樹脂初期縮合物は発泡しかつ樹脂化して硬化す
る。上記ホットプレスの前段階において該ダンボール
(1) の表面に塗布した発泡性フェノール樹脂初期縮合物
を前段キュアーしてシート化しておいてもよい。In order to produce the laminated material molded product (10) of the present invention, the surface of the cardboard (1) is coated with the powder or liquid of the foamable phenol resin initial condensate, and the cardboard (1) is predetermined by hot pressing. Shape to shape. At this time, the foamable phenol resin initial condensate foams and becomes a resin to be cured. The corrugated cardboard before the hot pressing
The expandable phenol resin initial condensate applied to the surface of (1) may be cured in the previous stage to form a sheet.
【０００９】上記成形過程において、ダンボール(1) 表
面に亀裂やしわ等が生じた場合、発泡かつ樹脂化しつゝ
あるフェノール樹脂初期縮合物が該亀裂を充填しかつし
わを吸収し、結果として得られるフエノール樹脂発泡体
の表面は平滑になる。例えば図４に示すようにダンボー
ル(1) 表面にしわ(1A)が生じたとしても、該しわ(1A)は
フエノール樹脂発泡体(2) の層の厚みにより吸収され表
面には発現しない。When cracks, wrinkles, etc. occur on the surface of the cardboard (1) in the above-mentioned molding process, the phenol resin precondensate, which is foamed and resinified, fills the cracks and absorbs wrinkles. The surface of the obtained phenol resin foam becomes smooth. For example, as shown in FIG. 4, even if wrinkles (1A) are generated on the surface of the cardboard (1), the wrinkles (1A) are absorbed by the layer thickness of the phenol resin foam (2) and do not appear on the surface.
【００１０】ホットプレス条件はフエノール樹脂がノボ
ラック型の場合には１５０〜１７０℃で１分、レゾール
型の場合には酸硬化触媒を用いて６０〜７０℃で１分行
なう。そしてホットプレス圧は当然フエノール樹脂の発
泡を阻害しない程度の圧力を適用する。The hot pressing conditions are 150 to 170 ° C. for 1 minute when the phenol resin is a novolac type resin, and 60 to 70 ° C. for 1 minute when an acid curing catalyst is used when the phenol resin is a resol type resin. The hot pressing pressure is of course a pressure that does not hinder the foaming of the phenol resin.
図１〜図４は本発明の一実施例を示すものである。 1 to 4 show an embodiment of the present invention.
【図１】側断面図1] Side sectional view
【図２】成形天井基材としての斜視図FIG. 2 is a perspective view of a molded ceiling base material.
【図３】表装材を貼着した状態の側断面図FIG. 3 is a side sectional view showing a state in which a covering material is attached.
【図４】成形部分側断面図FIG. 4 is a sectional side view of a molding portion.
1 ダンボール 2 フエノール樹脂発泡体 10 積層材成形物 1 cardboard 2 phenolic resin foam 10 laminated material molded product
Claims (2)
性フェノール樹脂初期縮合物を塗布し、ホットプレスす
ることによって該ダンボールを所定形状に成形するとと
もに該発泡性フェノール樹脂初期縮合物を発泡硬化せし
めてフェノール樹脂発泡体とすることを特徴とする積層
材成形物の製造方法1. A powdery or liquid foamable phenolic resin initial condensate is applied to the surface of a cardboard and hot pressed to form the cardboard into a predetermined shape, and the foamable phenolic resin initial condensate is foamed and cured. To produce a phenolic resin foam
性フェノール樹脂初期縮合物を塗布し、前段キュアーす
ることによって該発泡性フェノール樹脂初期縮合物をシ
ート化し、次いでホットプレスすることによって該ダン
ボールを所定形状に成形するとともに該発泡性フェノー
ル樹脂初期縮合物を発泡硬化せしめてフェノール樹脂発
泡体とする請求項１に記載の積層材成形物の製造方法2. A powdery or liquid foamable phenol resin initial condensate is applied to the surface of the cardboard, and the foamable phenol resin precondensate is sheeted by pre-curing, and then hot pressed to form the cardboard. The method for producing a laminated material molded product according to claim 1, wherein the product is molded into a predetermined shape and the foamable phenol resin initial condensate is foam-cured to form a phenol resin foam.