JPH0676587B2 - Lubricant for plunger tip - Google Patents
Lubricant for plunger tipInfo
- Publication number
- JPH0676587B2 JPH0676587B2 JP1036034A JP3603489A JPH0676587B2 JP H0676587 B2 JPH0676587 B2 JP H0676587B2 JP 1036034 A JP1036034 A JP 1036034A JP 3603489 A JP3603489 A JP 3603489A JP H0676587 B2 JPH0676587 B2 JP H0676587B2
- Authority
- JP
- Japan
- Prior art keywords
- lubricant
- plunger tip
- present
- graphite
- kinematic viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 産業上の利用分野 本発明はアルミニウム鋳造加工において、スリーブとプ
ランジャチップ間の摩擦低減のために用いられるプラン
ジャチップ用潤滑剤に関するものである。Description: TECHNICAL FIELD The present invention relates to a lubricant for a plunger tip used for reducing friction between a sleeve and a plunger tip in an aluminum casting process.
従来の技術 アルミニウム鋳造加工では、プランジャチップとスリー
ブ間の摩擦を低減し、アルミニウム溶湯を容易にキャビ
ティ内に送り込むため、プランジャチップに潤滑剤が用
いられる。従来からプランジャチップ用潤滑剤として
は、黒鉛粉末を鉱油などの油に分散させた黒鉛系潤滑剤
が多く使用されている。潤滑剤はプランジャチップとス
リーブ間に２ないし3ml/ショットの割合で滴下され、そ
の後にアルミニウム溶湯がキャビティ内に送り込まれる
が、その際に黒鉛系潤滑剤が垂れ落ちたり、また、プラ
ンジャ速度が速いため飛散して、機械の周辺や床に付着
して作業環境を汚染するという問題点がある。更に、潤
滑剤が機械設備本体、例えば、電動機内部に侵入して回
転子などに付着して短絡事故などが発生するような問題
点もある。2. Description of the Related Art In the aluminum casting process, a lubricant is used for the plunger tip in order to reduce friction between the plunger tip and the sleeve and to easily feed the molten aluminum into the cavity. Conventionally, as a lubricant for a plunger chip, a graphite-based lubricant in which graphite powder is dispersed in an oil such as mineral oil is often used. Lubricant is dripped between the plunger tip and the sleeve at a rate of 2 to 3 ml / shot, and then the molten aluminum is fed into the cavity. At that time, the graphite-based lubricant drops down and the plunger speed is high. Therefore, there is a problem in that it scatters and adheres to the periphery of the machine and the floor to contaminate the work environment. Further, there is a problem that the lubricant may enter the machine equipment body, for example, the inside of the electric motor and adhere to the rotor or the like to cause a short circuit accident.
発明が解決しようとする問題点 本発明は上記した従来の黒鉛系潤滑剤の欠点を解消する
ために、黒鉛を使用しない潤滑剤、すなわち、非黒鉛系
潤滑剤として、上記欠点が無く、潤滑性にも優れるプラ
ンジャチップ溶潤滑剤を提供することを目的とする。DISCLOSURE OF THE INVENTION Problems to be Solved by the Invention In order to solve the above-mentioned drawbacks of the conventional graphite-based lubricant, the present invention is a lubricant that does not use graphite, that is, as a non-graphite-based lubricant, which does not have the above-mentioned drawbacks and has a lubricity. It is also an object of the present invention to provide a plunger tip molten lubricant which is also excellent.
問題点を解決するための手段 上記の目的を達成するために、本発明者らは非黒鉛系潤
滑剤の潤滑性について鋭意研究を重ねた結果、作業環境
を悪化させず、かつ潤滑性にも優れた非黒鉛系潤滑剤を
発明するに至った。Means for Solving the Problems In order to achieve the above object, the present inventors have conducted extensive studies on the lubricity of a non-graphite lubricant, and as a result, do not deteriorate the working environment and also improve the lubricity. Invented an excellent non-graphite type lubricant.
すなわち、本発明は、鉱油を基油として、油脂または脂
肪酸エステルの１種または２種以上及び白色固体潤滑剤
を含有し、動粘度が、40℃で250ないし500mm2/sである
ことを特徴とするプランジャチップ用潤滑剤に関するも
のである。That is, the present invention is characterized by containing mineral oil as a base oil, one or more kinds of fats and oils or fatty acid esters, and a white solid lubricant, and having a kinematic viscosity of 250 to 500 mm 2 / s at 40 ° C. And a lubricant for a plunger tip.
以下に本発明を詳説する。The present invention will be described in detail below.
（鉱 油） 本発明において使用される鉱油は、たとえば日本工業規
格K2213に記載されたタービン油全般、日本工業規格K22
38に記載されたマシンン油全般などである。(Mineral oil) The mineral oil used in the present invention includes, for example, all turbine oils described in Japanese Industrial Standard K2213 and Japanese Industrial Standard K22.
This includes all the machine oils listed in 38.
（油 脂） 本発明において使用される油脂としては、ナタネ油、大
豆油、豚脂、牛脂などの動植物油脂がある。(Fats and Oils) As the fats and oils used in the present invention, there are animal and vegetable fats and oils such as rapeseed oil, soybean oil, lard and beef tallow.
（脂肪酸エステル） 本発明において使用される脂肪酸エステルとしては、炭
素原子数が10ないし18の脂肪酸と１価または多価のアル
コールのエステルが使用できるが、好ましくは耐熱性、
溶解性に優れているヒンダードエステルが良い。これら
のエステルの具体例としては、トリメチロールプロパ
ン、ネオペンチルグリコールまたはペンタエリスリトー
ルとオレイン酸のエステルが挙げられる。(Fatty Acid Ester) As the fatty acid ester used in the present invention, an ester of a fatty acid having 10 to 18 carbon atoms and a monovalent or polyvalent alcohol can be used, preferably heat resistance,
Hindered ester, which has excellent solubility, is preferable. Specific examples of these esters include esters of trimethylolpropane, neopentyl glycol or pentaerythritol with oleic acid.
本発明の潤滑剤の中に含有される油脂または脂肪酸エス
テルの１種または２種以上の割合は、５ないし10重量％
が適当である。この含有量が５重量％未満では、白色固
体潤滑剤の分散安定性が悪くなり、含有量が10重量％を
越えると、耐熱性が低下するからである。The proportion of one or more oils or fatty acid esters contained in the lubricant of the present invention is 5 to 10% by weight.
Is appropriate. This is because if the content is less than 5% by weight, the dispersion stability of the white solid lubricant becomes poor, and if the content exceeds 10% by weight, the heat resistance is lowered.
（白色固体潤滑剤） 本発明に使用される白色固体潤滑剤としては、タルク、
ふっ化黒鉛、雲母、窒化ほう素、ポリフッ化エチレン及
びポリエチレンを使用することができる。また、白色固
体潤滑剤の含有量は２ないし30重量％が好ましい。この
含有量が２重量％未満では、潤滑性が劣り、含有量が30
重量％を越えても、潤滑性向上効果に変化がなく、分散
安定性が悪くなるからである。(White solid lubricant) As the white solid lubricant used in the present invention, talc,
Graphite fluoride, mica, boron nitride, polyfluorinated ethylene and polyethylene can be used. The content of the white solid lubricant is preferably 2 to 30% by weight. If this content is less than 2% by weight, the lubricity is poor and the content is 30%.
This is because even if it exceeds the weight percentage, there is no change in the effect of improving the lubricity and the dispersion stability deteriorates.
（任意成分） 本発明の潤滑剤は基本的には上記成分から構成される
が、それらの成分のほかに増粘剤、防食剤、酸化防止剤
等を必要に応じて、適宜、添加することができる。本発
明における増粘剤としては、モンモリロナイト、ポリイ
ソブテン、アルキルメタクリレートの重合体、ポリスチ
レン等を使用することができる。(Arbitrary Components) The lubricant of the present invention is basically composed of the above components, but in addition to these components, a thickener, an anticorrosive agent, an antioxidant, etc. may be appropriately added if necessary. You can As the thickener in the present invention, montmorillonite, polyisobutene, a polymer of alkyl methacrylate, polystyrene and the like can be used.
（動粘度） 本発明の潤滑剤の動粘度は、40℃で250ないし500mm2/s
の範囲であることが必要である。すなわち、動粘度が25
0mm2/s未満では潤滑性が不足し、プランジャチップとス
リーブ間で焼付きが生じる。一方、動粘度が500mm2/sを
越えると、潤滑剤供給時のポンプアップや滴下が困難と
なり、潤滑剤供給が不十分となって、プランジャチップ
とスリーブ間で焼付きが生じることがある。(Kinematic viscosity) The lubricant of the present invention has a kinematic viscosity of 250 to 500 mm 2 / s at 40 ° C.
Must be within the range. That is, the kinematic viscosity is 25
If it is less than 0 mm 2 / s, lubricity is insufficient and seizure occurs between the plunger tip and the sleeve. On the other hand, if the kinematic viscosity exceeds 500 mm 2 / s, pumping up or dropping at the time of supplying the lubricant becomes difficult, the supply of the lubricant becomes insufficient, and seizure may occur between the plunger tip and the sleeve.
動粘度を所定の値に調整するには、本発明の基本成分と
任意成分を混合した後に、動粘度の値が所定の値になる
まで増粘剤を添加すれば良い。In order to adjust the kinematic viscosity to a predetermined value, it is sufficient to add the thickener until the value of the kinematic viscosity reaches a predetermined value after mixing the basic component of the present invention and the optional component.
（発明の作用） ところで、アルミニウム鋳造加工においては、アルミニ
ウム溶湯の温度が600ないし700℃であり、プランジャチ
ップもその温度の影響を受けることになる。そのためプ
ランジャチップには内部冷却が施されており、60ないし
70℃以下の温度に制御されている。(Operation of the Invention) In the aluminum casting process, the temperature of the molten aluminum is 600 to 700 ° C, and the plunger tip is also affected by the temperature. For this reason, the plunger tip is internally cooled, 60 or
The temperature is controlled below 70 ℃.
本発明の潤滑剤が上記加工条件下で優れた潤滑効果を発
揮するのは、潤滑剤組成物中の油脂または脂肪酸エステ
ルの粘性及び吸着効果により、均一で強い油膜を形成す
ること、及び、白色固体潤滑剤の優れた耐熱性、潤滑性
によるものと考えられる。The lubricant of the present invention exerts an excellent lubricating effect under the above-mentioned processing conditions is that a uniform and strong oil film is formed by viscous and adsorption effects of fats and oils or fatty acid esters in the lubricant composition, and white. This is considered to be due to the excellent heat resistance and lubricity of the solid lubricant.
また本発明の潤滑剤は黒鉛のような黒色成分を含有して
いないので、作業環境を汚染することがない。Further, since the lubricant of the present invention does not contain a black component such as graphite, it does not pollute the working environment.
実施例 以下に本発明の実施例を比較例とともに説明するが、本
発明はこれら実施例に限定されるものではない。Examples Hereinafter, examples of the present invention will be described together with comparative examples, but the present invention is not limited to these examples.
実施例１ないし９ 基油としての鉱油を用い、第１表に示した成分を配合し
て本発明のプランジャチップ用潤滑剤を得た。なお、モ
ンモリロナイトは鉱油に徐々に添加後、60℃に加熱し、
その後にホモジナイザー処理をした。第１表中の数値の
単位は重量％である。Examples 1 to 9 Mineral oil was used as a base oil, and the components shown in Table 1 were blended to obtain a lubricant for plunger tips of the present invention. In addition, montmorillonite was gradually added to mineral oil and then heated to 60 ° C,
After that, a homogenizer treatment was performed. The unit of numerical values in Table 1 is% by weight.
これらの潤滑剤と比較例の潤滑剤について、第２表の摩
擦試験機と条件で潤滑性を評価した。 The lubricity of these lubricants and the lubricants of Comparative Examples were evaluated under the friction tester and conditions shown in Table 2.
この試験では第１図に示される摩擦試験機を用いて行っ
た。この摩擦試験機は潤滑剤を一定の厚さで回転体１に
被覆し、この回転体１を回転させながら所定温度に加熱
された加熱体２を押し付けて回転体１と加熱体２との間
の摩擦係数を測定して潤滑性能を評価するものである。
加熱体２には変圧器３が接続されており、この変圧器３
の出力を変えることにより加熱体２の温度を変化させる
ことができる。 This test was conducted using the friction tester shown in FIG. In this friction tester, the rotor 1 is coated with a lubricant with a constant thickness, and the rotating body 1 is rotated to press the heating body 2 heated to a predetermined temperature to press the rotating body 1 between the rotating body 1 and the heating body 2. The lubrication performance is evaluated by measuring the friction coefficient of.
A transformer 3 is connected to the heating element 2, and this transformer 3
The temperature of the heating element 2 can be changed by changing the output of the heating element 2.
比較例は以下に示す組成の潤滑剤を用いた。In the comparative example, a lubricant having the following composition was used.
比較例 １ 基油:40℃で動粘度が263mm2/sの鉱油 90重量％ 添加剤：平均粒径が７μｍの鱗状黒鉛 10重量％ 40℃の動粘度は350mm2/sであった。Comparative Example 1 Base oil: kinematic viscosity at 40 ° C. is 263 mm 2 / s of the mineral oil 90 wt% Additives: kinematic viscosity vein graphite 10 wt% 40 ° C. of the average particle size of 7μm was 350 mm 2 / s.
比較例 ２ 基油:40℃で動粘度が263mm2/sの鉱油 85重量％ 添加剤：ナタネ油 15重量％ 40℃の動粘度は205mm2/sであった。Comparative Example 2 Base oil: kinematic viscosity at 40 ° C. is 263 mm 2 / s of the mineral oil 85 wt% Additives: kinematic viscosity of rapeseed oil 15% by weight 40 ° C. was 205 mm 2 / s.
摩擦試験の結果を第３表に示す。The results of the friction test are shown in Table 3.
第３表の結果から明らかなように、本発明のプランジャ
チップ用潤滑剤は、従来技術の黒鉛系潤滑剤と同等もし
くはそれ以上の潤滑性能を示す。 As is clear from the results shown in Table 3, the plunger tip lubricant of the present invention exhibits a lubricating performance equal to or higher than that of the graphite lubricant of the prior art.
発明の効果 以上説明したように、基油として鉱油を用い、油脂また
は脂肪酸エステルの１種または２種以上及び白色固体潤
滑剤を２ないし30重量％含有して、40℃での動粘度が25
0ないし500mm2/sである潤滑剤（すなわち本発明の潤滑
剤）は、潤滑性に優れているため、高速あるいは高型締
力のアルミニウム鋳造加工におけるプランジャチップ用
潤滑剤として使用することができる。更に本発明の潤滑
剤は、黒鉛のような作業環境を汚染する成分を含有しな
いので、作業環境の良化が可能となる。As described above, mineral oil is used as a base oil, and one or more kinds of fats or oils or fatty acid esters and 2 to 30% by weight of a white solid lubricant are contained, and the kinematic viscosity at 40 ° C. is 25
The lubricant of 0 to 500 mm 2 / s (that is, the lubricant of the present invention) has excellent lubricity and therefore can be used as a plunger tip lubricant in aluminum casting with high speed or high mold clamping force. . Furthermore, since the lubricant of the present invention does not contain a component such as graphite that contaminates the work environment, the work environment can be improved.
第１図は、本発明の潤滑剤の性能を試験するために使用
した摩擦試験機を示す概念図である。 図面において１は回転体、２は加熱体、３は変圧器を示
す。FIG. 1 is a conceptual diagram showing a friction tester used to test the performance of the lubricant of the present invention. In the drawings, 1 is a rotating body, 2 is a heating body, and 3 is a transformer.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ１０Ｍ 101:04 105:32） Ｃ１０Ｎ 20:02 40:24 Ｚ 8217−4Ｈ ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 5 Identification number Office reference number FI technical display location C10M 101: 04 105: 32) C10N 20:02 40:24 Z 8217-4H
Claims (3)
剤において、油脂または脂肪酸エステルの１種または２
種以上及び白色固体潤滑剤を含有し、動粘度が40℃で25
0ないし500mm2/sであることを特徴とするプランジャチ
ップ用潤滑剤。1. A lubricant for plunger chips comprising a mineral oil as a base oil, wherein one or two of fats and oils or fatty acid esters is used.
Contains more than one kind and white solid lubricant, kinematic viscosity of 25 at 40 ℃
Lubricant for plunger tip, characterized by 0 to 500 mm 2 / s.
からなる群から選択される請求項１に記載のプランジャ
チップ用潤滑剤。2. The lubricant for a plunger tip according to claim 1, wherein the white solid lubricant is selected from the group consisting of talc and fluorinated graphite.
剤全体の２ないし30重量％含有される請求項１または２
に記載のプランジャチップ用潤滑剤。3. The white solid lubricant is contained in an amount of 2 to 30% by weight based on the whole lubricant for the plunger tip.
Lubricant for plunger tip described in.