JPH0647722Y2 - Laminated sheet as a substitute for sutures - Google Patents
Laminated sheet as a substitute for suturesInfo
- Publication number
- JPH0647722Y2 JPH0647722Y2 JP1990107747U JP10774790U JPH0647722Y2 JP H0647722 Y2 JPH0647722 Y2 JP H0647722Y2 JP 1990107747 U JP1990107747 U JP 1990107747U JP 10774790 U JP10774790 U JP 10774790U JP H0647722 Y2 JPH0647722 Y2 JP H0647722Y2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- substitute
- laminated sheet
- warp
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 「産業上の利用分野」 本考案は、従来、杉や桧等の板材を紙のように薄く削る
ことによって得られる経木の代用品として使用される積
層シートに関するものである。[Detailed Description of the Invention] "Industrial application field" The present invention relates to a laminated sheet used as a substitute for a warp obtained by shaving a board material such as cedar or Japanese cypress as thin as paper. is there.
「従来の技術」 杉や桧等の板材を紙のように薄く削ることによって得ら
れる経木は、例えば、各種の餅類，串団子，赤飯，和菓
子等を折り詰め包装にして販売，流通させる際の前記内
容物のカバー材をはじめ、各種の食料品を直接包装する
際の包装用材として使用されている。"Prior art" A warp obtained by thinly cutting a board material such as cedar or Japanese cypress into a thin piece of paper is used, for example, when various rice cakes, skewer dumplings, red rice, Japanese sweets, etc. are packed and sold and distributed It is used as a packaging material for directly packaging various food products, including the cover material for the contents.
しかるに、前述の経木は、近年の傾向である省資源の意
向に沿わなく、また、高価であり、木の匂いが強く、さ
らには、木屑や虫が混入していることがある等の問題が
ある。However, the above-mentioned warp wood does not follow the tendency of resource saving which is a tendency in recent years, is also expensive, has a strong smell of wood, and further, there is a problem that wood chips and insects may be mixed. is there.
このため、最近、ポリオレフィン系合成樹脂層を中芯層
とし、その上，下両面に紙を積層させた積層シートが経
木の代用シートとして使用され始めた。For this reason, recently, a laminated sheet in which a polyolefin synthetic resin layer is used as a core layer and paper is laminated on both upper and lower surfaces thereof has begun to be used as a substitute sheet for warp wood.
「考案が解決しようとする課題」 前述のポリオレフィン系合成樹脂層を中芯層とし、その
上，下両面に紙を積層させた積層シートからなる経木の
代用シートは、シートの表，裏の両面層に紙が使用され
ているため、該積層シートの製造工程中での吸湿による
カールの発生、あるいは、蒸した後の饅頭や団子等を積
層シートの上に置いたときに、これらの食品からの水分
の吸湿によるカールの発生等があり、取り扱い上での問
題となっている。"Problems to be solved by the device" The substitute sheet made of laminated wood, which is a laminated sheet in which the above-mentioned polyolefin synthetic resin layer is used as the core layer and paper is laminated on both upper and lower sides, is used for both the front and back sides of the sheet. Since paper is used for the layer, curling due to moisture absorption in the manufacturing process of the laminated sheet, or when steamed buns or dumplings are placed on the laminated sheet Curling occurs due to the absorption of moisture of the above, which is a problem in handling.
これに対して本考案は、板材を紙のように薄く削ること
によって得られる経木と同様の外観を呈し、しかも、吸
湿によるカールの発生の問題がなく、取り扱い特性にお
いて優れた作用を有する経木の代用シートを提供する。On the other hand, the present invention has the same appearance as a warp obtained by shaving a plate material like paper, and has no problem of curling due to moisture absorption, and has an excellent action in handling characteristics. Provide a substitute sheet.
「課題を解決するための手段」 本考案の経木の代用となる積層シートは、少なくとも一
方の面に木目に類似するエンドレスの印刷模様が付され
ている耐水性を有する透明〜半透明の繊維素シートによ
る中芯層と、ポリオレフィン系樹脂による表面層と、同
じくポリオレフィン系樹脂による裏面層とを具備する積
層シートからなる。[Means for Solving the Problems] A laminated sheet which is a substitute for warp wood of the present invention is a transparent to translucent fibrous material having water resistance with an endless printed pattern similar to wood grain on at least one surface. It is composed of a laminated sheet having a core layer made of a sheet, a surface layer made of a polyolefin resin, and a back layer made of a polyolefin resin.
前記構成からなる本考案の経木の代用となる積層シート
における中芯層として使用される透明〜半透明の繊維素
シートは、繊維素を利用して得られる耐水性シート、例
えば、グラシン紙（坪量40g/m2以下）、パーチメント紙
（坪量40g/m2以下）、さらには、坪量12g/m2以下のセル
ロース系不織布等である。The transparent to translucent fibrin sheet used as the core layer in the laminated sheet as a substitute of the warp of the present invention having the above-mentioned structure is a water-resistant sheet obtained by using fibrin, for example, glassine paper (tsubo). An amount of 40 g / m 2 or less), parchment paper (basis weight of 40 g / m 2 or less), and a cellulosic nonwoven fabric having a basis weight of 12 g / m 2 or less.
また、前記積層シートにおける表，裏両面層をなすポリ
オレフィン系樹脂層の厚さは、積層シートが経木の代用
品として使用されるものであることから、積層シート全
体の厚さが経木の通常の厚さである0.02〜0.8mm程度と
なるように、通常10〜100μ程度に形成されている。Further, the thickness of the polyolefin-based resin layers forming the front and back double-sided layers in the above-mentioned laminated sheet is the same as that of the ordinary laminated tree because the laminated sheet is used as a substitute for the wooden tree. It is usually formed to have a thickness of about 0.02 to 0.8 mm and a thickness of about 10 to 100 μ.
前記構成からなる本考案の経木の代用となる積層シート
は、表，裏面層となるポリオレフィン系樹脂層を、中芯
層たる繊維素シートの上，下両面に対して押し出しコー
トすることによって容易に得られるものであり、中芯層
をなす繊維素シートにおけるポリオレフィン系樹脂層と
の接着面をあらかじめコロナ放電処理等の接着性改良処
理に付しておくことによって、中芯層をなす繊維素シー
トの接着性を改良し、積層シートの接着強度を向上させ
るようにしておくことが好ましい。The laminated sheet as a substitute of the warp of the present invention having the above-mentioned structure can be easily prepared by extrusion-coating the front and back layers of the polyolefin resin layer on the upper and lower surfaces of the fibrous sheet as the core layer. A fibrin sheet forming a core layer is obtained by subjecting the adhesive surface of the fibrin sheet forming the core layer to the polyolefin resin layer to an adhesion improving treatment such as a corona discharge treatment in advance. It is preferable to improve the adhesiveness of (1) to improve the adhesive strength of the laminated sheet.
また、耐水性を有する透明〜半透明の繊維素シートによ
る中芯層を、２枚以上の透明〜半透明の繊維素シートを
利用して形成した場合には、腰のある積層シートが得ら
れる。In addition, when a core layer made of a transparent to translucent fibrous sheet having water resistance is formed by using two or more transparent to translucent fibrous sheets, a flexible laminated sheet can be obtained. .
なお、中芯層が２枚以上の透明〜半透明の繊維素シート
によって構成される場合には、利用される透明〜半透明
の繊維素シートの中の１枚に対して、木目に類似するエ
ンドレスの印刷模様が付されていれば十分である。When the core layer is composed of two or more transparent to translucent fibrin sheets, one of the transparent to translucent fibrin sheets used is similar to the grain. An endless print pattern is sufficient.
「実施例」 以下本考案の経木の代用となる積層シートの具体的な構
成を、図面に基づいて、製造実施例をもって説明する。[Examples] Hereinafter, a specific structure of a laminated sheet which is a substitute of the warp of the present invention will be described with reference to the drawings with reference to manufacturing examples.
実施例１ 第１図において、片面に杉板の正目に酷似する色彩およ
び輪郭形状の木目模様m,m,……が印刷されているパーチ
メント紙（坪量34.9g/m2）２に対して、該パーチメント
紙２の上，下両面にコロナ放電処理を施した後、続い
て、前記パーチメント紙２における木目模様m,m,……の
印刷面に、厚さ15μのポリエチレン樹脂を溶融，押し出
しコートすることによって、符号３で表示される表面層
を形成した。Example 1 In FIG. 1, to parchment paper (basis weight 34.9 g / m 2 ) 2 on one side of which is printed a color and contour wood pattern m, m, ... Then, corona discharge treatment is applied to both upper and lower surfaces of the parchment paper 2, and then a polyethylene resin having a thickness of 15 μ is melted on the printed surface of the parchment paper 2 having a wood grain pattern m, m ,. A surface layer indicated by reference numeral 3 was formed by extrusion coating.
次いで、パーチメント紙２の非印刷面に対して、厚さ15
μのポリエチレン樹脂を溶融，押し出しコートすること
によって、符号４で表示される表面層を形成し、本考案
の１実施例品たる経木の代用となる積層シート１を得
た。Then, with respect to the non-printed surface of the parchment paper 2, the thickness 15
By melting and extruding a polyethylene resin of μ to form a surface layer indicated by reference numeral 4, a laminated sheet 1 which is a substitute of a warp as an example of the present invention was obtained.
実施例２ 第１図において、片面に杉板の正目に酷似する色彩およ
び輪郭形状の木目模様m,m,……が印刷されているパーチ
メント紙（坪量34.9g/m2）６に対して、該パーチメント
紙６の上，下両面にコロナ放電処理を施した後、パーチ
メント紙６の非印刷面に厚さ15μのポリエチレン樹脂を
溶融，押し出しコートすることによって、符号７で表示
される表面層を形成した。Example 2 In FIG. 1, for parchment paper (grammage 34.9 g / m 2 ) 6 on one side of which is printed a wood grain pattern m, m, ... Then, after subjecting the parchment paper 6 to corona discharge treatment on both upper and lower surfaces, a non-printed surface of the parchment paper 6 is melted and extrusion coated with a 15 μm-thick polyethylene resin to form a surface indicated by reference numeral 7. Layers were formed.
続いて、符号８で表示されるパーチメント紙（坪量34.9
g/m2）の上，下両面にコロナ放電処理を施した後、パー
チメント紙８と先の表面層７を有するパーチメント紙６
の木目模様m,m,……の印刷面とを、両者の間に、厚さ15
μのポリエチレン樹脂の溶融，押し出し層９を介在させ
て接着，積層し、さらに、パーチメント紙８面に対し
て、厚さ15μのポリエチレン樹脂を溶融，押し出しコー
トすることによって、符号10で表示される表面層を形成
し、本考案の別の実施例品たる経木の代用となる積層シ
ート５を得た。Next, parchment paper (reference weight 34.9
g / m 2 ) Parchment paper 6 having parchment paper 8 and the above surface layer 7 after corona discharge treatment on both upper and lower surfaces
Between the printed surface of the wood grain pattern m, m, ...
A polyethylene resin having a thickness of 15 μm is adhered and laminated with an extrusion layer 9 interposed therebetween, and further, a polyethylene resin having a thickness of 15 μm is melted and extrusion-coated on the parchment paper 8 surface, which is indicated by reference numeral 10. A surface layer was formed to obtain a laminated sheet 5 as a substitute for warp, which is another embodiment of the present invention.
「考案の作用，効果」 本考案の経木の代用となる積層シートは、耐水性を有す
る透明〜半透明の繊維素シートによる中芯層と、ポリオ
レフィン系樹脂による表面層と、同じくポリオレフィン
系樹脂による裏面層とを具備し、中芯層をなす繊維素シ
ートの少なくとも一方の面に、木目に類似するエンドレ
スの印刷模様が付されているものであり、従来の経木の
欠点、すなわち、高価，木の匂い，木屑の落下，虫の混
入等の欠点を悉く解消するものである。"Function and effect of the device" The laminated sheet which is a substitute of the warp of the present invention is made of a transparent to semitransparent fibrous sheet having water resistance, a core layer, a surface layer made of a polyolefin resin, and a polyolefin resin. An endless printed pattern similar to wood grain is provided on at least one surface of a fibrous sheet forming a core layer, which has a back surface layer. It eliminates the drawbacks such as the smell of wood, the fall of wood chips, and the mixture of insects.
さらに、本考案の経木の代用となる積層シートは、中芯
層をなす繊維素シートに付されている木目模様の印刷
が、該積層シートの表，裏両面から視認し得る程度の半
透明性を有しているので、天然木を利用して得られる経
木にきわめて酷似する外観を呈するものであって、良好
な意匠性を発揮する。Further, the laminated sheet which is a substitute of the warp of the present invention has a semi-transparency such that the wood grain pattern printed on the fibrous sheet forming the core layer can be visually recognized from both front and back surfaces of the laminated sheet. Therefore, it has an appearance very similar to warp wood obtained by using natural wood, and exhibits good designability.
また、本考案の経木の代用となる積層シートは、表，裏
両面層がポリオレフィン系樹脂層で形成されているの
で、蒸した後の饅頭や団子等を積層シートの上に置いた
ときに、これらの食品からの水分の吸湿が殆どないた
め、吸湿によるカールの発生がなく、取り扱い性におい
て優れた作用を奏する。Further, since the front and back double-sided layers of the laminated sheet which is a substitute of the warp of the present invention are formed of polyolefin resin layers, when steamed buns or dumplings are placed on the laminated sheet, Since there is almost no moisture absorption from these foods, curling due to moisture absorption does not occur and excellent handling properties are exhibited.
さらに本考案の経木の代用となる積層シートは、表，裏
両面層がポリオレフィン系樹脂層で形成されているもの
であるから、表，裏面層の中のいずれの面が被包装物と
接する側となるようにして利用されても、被包装物であ
る食品等に対する衛生性が良好であり、主として食料品
の包装に利用される経木の代用品をなす積層シートとし
て、優れた作用，効果を奏する。Further, since the laminated sheet which is a substitute of the warp of the present invention has the front and back double-sided layers formed of the polyolefin resin layer, whichever of the front and back layers is in contact with the object to be packaged. Even if it is used in such a way, it has good hygiene properties for foods to be packaged, and has excellent action and effect as a laminated sheet which is a substitute of warp wood mainly used for packaging foods. Play.
第１図〜第２図は、本考案の経木の代用となる積層シー
トのそれぞれの別の実施例品を示す模型断面図である。 １……経木の代用となる積層シート、 ２……繊維素シートによる中芯層、 ３……ポリオレフィン系樹脂による表面層、 ４……ポリオレフィン系樹脂による裏面層、 m,m……繊維素シート２に付されている木目模様の印刷
模様。1 and 2 are model cross-sectional views showing other examples of laminated sheets which are substitutes for the warp of the present invention. 1 ... Laminated sheet as a substitute for warp, 2 ... Core layer made of fibrin sheet, 3 ... Surface layer made of polyolefin resin, 4 ... Back layer made of polyolefin resin, m, m …… Fibrous sheet Printed wood grain pattern attached to 2.
Claims (2)
トによる中芯層と、ポリオレフィン系樹脂による表面層
と、同じくポリオレフィン系樹脂による裏面層とを具備
し、前記中芯層をなす繊維素シートの少なくとも一方の
面には、木目に類似するエンドレスの印刷模様が付され
ていることを特徴とする経木の代用となる積層シート。1. A fiber comprising a core layer made of a transparent to translucent fibrin sheet having water resistance, a surface layer made of a polyolefin resin, and a back layer made of a polyolefin resin, the fiber constituting the core layer. A laminated sheet which is a substitute for a warp tree, wherein an endless printed pattern similar to wood grain is provided on at least one surface of the bare sheet.
トによる中芯層が、２枚の耐水性を有する透明〜半透明
の繊維素シートと、該繊維素シート同士の間に介装され
ているポリオレフィン系樹脂層との積層構成からなる実
用新案登録請求の範囲第１項記載の経木の代用となる積
層シート。2. A water-resistant transparent to semi-transparent fibrous sheet core layer is interposed between two water-resistant transparent to semi-transparent fibrous sheets. A laminated sheet as a substitute for a warp according to claim 1, which has a laminated constitution with a polyolefin resin layer as described above.