JPH0638656A - Production of fishing bait - Google Patents
Production of fishing baitInfo
- Publication number
- JPH0638656A JPH0638656A JP4128306A JP12830692A JPH0638656A JP H0638656 A JPH0638656 A JP H0638656A JP 4128306 A JP4128306 A JP 4128306A JP 12830692 A JP12830692 A JP 12830692A JP H0638656 A JPH0638656 A JP H0638656A
- Authority
- JP
- Japan
- Prior art keywords
- bait
- neri
- fishing
- gelling agent
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はミンチ状のネリ餌を原料
とした釣り餌の製造方法に係るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing fishing baits using minced Neri baits as a raw material.
【０００２】[0002]
【従来の技術】従来より、活エサに代わる釣り餌とし
て、ネリ餌が知られている。このネリ餌は、成形が比較
的容易で、任意の大きさや形状に成形できるばかりでな
く、種々の原料を配合調整する事により、対象魚に応じ
た集魚効果を得られる利点を有している。2. Description of the Related Art Neri bait has been known as a bait to replace live food. This Neri bait is relatively easy to mold and can be molded into any size and shape, and it has the advantage that the fish collecting effect according to the target fish can be obtained by blending and adjusting various raw materials. .
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、従来の
ネリ餌は柔らかく、ハリ掛けしても餌持ちが悪い。また
ネリ餌を凍結していても、水中に投入すると溶け易い。
そのため、ネリ餌を食わせ餌として用いると、ネリ餌は
上層で溶けだし、中層や海底に達する前にバラケるた
め、石鯛、黒鯛のごとき根魚を対象とした釣りには用い
る事ができないものであった。However, the conventional Neri bait is soft and has poor bait retention even if it is hung. Even if the Neri bait is frozen, it is easily melted when put in water.
For this reason, when used as bait to feed on Neri bait, it melts in the upper layer and disperses before reaching the middle layer or the sea floor, so it cannot be used for fishing for root fish such as stone bream and black bream. It was
【０００４】また、ネリ餌を投げ釣りに用いようとする
と、ネリ餌は投げた直後に、ハリから離脱し易いため、
従来は殆ど投げ釣りに使用される事はなかった。Further, when the Neri bait is used for throwing fishing, the Neri bait is easily separated from the strain immediately after throwing,
In the past, it was rarely used for pitch fishing.
【０００５】本発明は上述のごとき課題を解決しようと
するものであって、ネリ餌を用いた食わせ用の釣り餌に
於て、釣り餌を水中に投入しても、上層でバラケる事が
なく、餌持ちを良好とし、中層、海底に確実に到達し、
中層魚、根魚を対象とした釣りを可能にするとともに投
げ釣り等に於ても、餌の離脱を生じる事がないようにし
ようとするものである。The present invention is intended to solve the above-described problems, and in the case of a bait for feeding using Neri bait, even if the bait is put into water, the bait may disperse in the upper layer. It has a good feeding ability and reliably reaches the middle layer and the seabed.
It is intended to enable mid-layer fish and root fish to be fished and to prevent bait from being detached even in throwing fishing and the like.
【０００６】[0006]
【課題を解決するための手段】本発明は上述のごとき課
題を解決するため、原料餌にアルギン酸ナトリウムから
成る増粘剤を１wt％〜20wt％混合してネリ餌を形成し、
このネリ餌を加圧成形した後、ゲル化剤溶液中に浸漬
し、ネリ餌をゲル化して製造する事を特徴とする。[Means for Solving the Problems] In order to solve the above-mentioned problems, the present invention forms a Neri bait by mixing a raw material bait with a thickener composed of sodium alginate at 1 wt% to 20 wt%.
This neri bait is pressure-molded and then immersed in a gelling agent solution to gel the neri bait for production.
【０００７】また、第２の発明は、原料餌にアルギン酸
ナトリウムから成る増粘剤を１wt％〜20wt％混合してネ
リ餌を形成し、このネリ餌にゲル化剤を混合して加圧成
形し、ネリ餌をゲル化して製造する事を特徴とする。A second aspect of the invention is that a raw material feed is mixed with a thickener composed of sodium alginate in an amount of 1 wt% to 20 wt% to form a Neri bait, and the Neri bait is mixed with a gelling agent to be pressure-molded. However, it is characterized by gelling Neri bait and manufacturing.
【０００８】また、第３の発明は、原料餌にアルギン酸
ナトリウムから成る増粘剤を１wt％〜20wt％混合してネ
リ餌を形成し、このネリ餌にゲル化剤を混合して、加圧
成形した後、ゲル化剤溶液中に浸漬し、ネリ餌をゲル化
して製造する事を特徴とする。In a third aspect of the invention, a raw material feed is mixed with a thickener consisting of sodium alginate in an amount of 1 to 20% by weight to form a Neri feed, and the Neri feed is mixed with a gelling agent to pressurize. It is characterized in that after molding, it is immersed in a gelling agent solution to gelate the Neri bait to produce it.
【０００９】また、増粘剤は、アルギン酸ナトリウムに
加えてカルボキシメチルセルロース、ポリアクリル酸ナ
トリウム、カラギーナン、グァーガム、糖分、α−デン
プンの内から選択した一種または二種以上を添加しても
良い。As the thickener, one or more selected from carboxymethylcellulose, sodium polyacrylate, carrageenan, guar gum, sugar and α-starch may be added in addition to sodium alginate.
【００１０】また、ゲル化剤は、乳酸カルシウム、塩化
カルシウムの内から選択した一種または二種であっても
良い。The gelling agent may be one or two selected from calcium lactate and calcium chloride.
【００１１】また、ネリ餌は、ゲル化した後、加熱し、
冷却しても良い。The Neri food is heated after gelling.
It may be cooled.
【００１２】[0012]
【作用】本発明は上述の如く、釣り餌の成形を行うに
は、まず、オキアミ、イワシ、サナギ、ウニ、トコブシ
等の原料餌をミンチ状に粉砕する。この原料餌の選定
は、釣りの対象魚に応じて、単品または複数種を用いる
事ができる。また、アミ等の小型の原料餌を用いる場合
には、必ずしも粉砕を必要としない。As described above, according to the present invention, in order to form the fishing bait, first, the raw material bait such as krill, sardines, pupa, sea urchin, and beetle is ground into mince form. The raw material bait can be selected from a single item or a plurality of types depending on the target fish for fishing. In addition, crushing is not always necessary when using a small raw material feed such as a net.
【００１３】次に、ミンチ状の原料餌に、アルギン酸ナ
トリウムから成る増粘剤を１wt％〜20wt％混合して練り
込み、原料餌に粘りを生じさせる。この原料餌の練り込
みには、適宜の水分が必要であるが、この水分が不足し
ている場合には、水を加えて水分を補給する。また、こ
の水の補給には、海水を用いても良い。Next, 1 wt% to 20 wt% of a thickening agent consisting of sodium alginate is mixed with the minced raw material feed and kneaded to make the raw material sticky. A proper amount of water is required for kneading the raw material feed, and when the water content is insufficient, water is added to replenish the water content. In addition, seawater may be used to replenish this water.
【００１４】また、上記では増粘剤を１wt％〜20wt％混
合したが、１wt％未満の混合では、柔らか過ぎてハリ掛
けが困難となる。また、20wt％を超えて増粘剤を混合す
ると、増粘剤が溶けきれず、水の補給が必要となる。そ
のため、原料餌に対する水の比率が多くなり、魚類の捕
食欲を低下するものとなり、好ましくない。Further, in the above description, the thickener is mixed in an amount of 1 wt% to 20 wt%, but if it is less than 1 wt%, it will be too soft and it will be difficult to apply tension. Also, if the thickener is mixed in an amount exceeding 20 wt%, the thickener cannot be completely dissolved, and it becomes necessary to replenish the water. Therefore, the ratio of water to the raw material feed is increased, and the desire to eat fish is reduced, which is not preferable.
【００１５】また、アルギン酸ナトリウムから成る増粘
剤の混合だけでは、固すぎたり、伸びが不足している場
合には、この増粘剤に、カルボキシメチルセルロース、
ポリアクリル酸ナトリウム、カラギーナン、グァーガ
ム、糖分、α−デンプンの内から選択した一種または二
種以上を添加すれば、柔軟で伸びのあるネリ餌(１)が得
られる。また、増粘剤に、カラギーナン、グァーガム、
糖分、α−デンプン等を添加すれば、ネリ餌(１)は保水
性を有し、水分の蒸発を防止できる。また、ネリ餌(１)
は、最終工程で冷凍し、使用時に解凍するものである
が、この解凍時に於ても、保水性を有するため、原料餌
の成分や水分が溶けて抜け出るような事がない。また、
増粘剤にブドウ糖、蜂蜜等の糖分を添加すれば、クロダ
イ等の甘味を好む魚類の集魚効果が向上する。If the thickening agent consisting of sodium alginate alone is too hard or the elongation is insufficient, the thickening agent may be mixed with carboxymethyl cellulose,
By adding one or more selected from sodium polyacrylate, carrageenan, guar gum, sugar, and α-starch, a soft and stretchable Neri bait (1) can be obtained. In addition, as a thickener, carrageenan, guar gum,
If sugar, α-starch, etc. are added, the Neri bait (1) has water retention and can prevent evaporation of water. Also, Neri bait (1)
, Which is frozen in the final step and thawed at the time of use, has a water-retaining property even at the time of thawing so that the ingredients and water of the raw material feed do not melt and escape. Also,
When sugars such as glucose and honey are added to the thickener, the effect of collecting fish such as black sea bream that likes sweetness is improved.
【００１６】次に、増粘剤の混合後、ネリ餌(１)を加圧
成形して任意の形状に形成する。この加圧手段には、射
出成形機、パスタマシン、型枠等を使用する事が可能で
ある。そして射出成形機を使用すると、ネリ餌(１)は、
図１に示す如くウドン状や、図２に示す如くマカロニ状
に成形する事が可能となる。Next, after mixing the thickening agent, the Neri bait (1) is pressure-molded to form an arbitrary shape. An injection molding machine, a pasta machine, a mold, or the like can be used as the pressurizing means. And using an injection molding machine, Neri bait (1)
It is possible to mold it into a Udon shape as shown in FIG. 1 or a macaroni shape as shown in FIG.
【００１７】また、パスタマシンを使用するとネリ餌
(１)を平板状に成形でき、このネリ餌(１)を、図３に示
す如く幅３mm〜４mmに短冊状に切断する。また、この短
冊状のネリ餌(１)を、図４に示す如くねじったり、ま
た、図５に示す如く曲げて成形する事も可能である。Moreover, when pasta machine is used, it is possible to feed
(1) can be formed into a flat plate shape, and this Neri bait (1) is cut into strips with a width of 3 mm to 4 mm as shown in FIG. It is also possible to twist the strip-shaped bait (1) as shown in FIG. 4 or bend it as shown in FIG.
【００１８】また、型枠を用いると、ネリ餌(１)を、図
６に示す如くダンゴ状、また図７に示す如く釣糸(２)の
挿通穴(３)を設けたダンゴ状に成形する事ができる。こ
のようにしてネリ餌(１)をハリ掛けし易い形状に形成す
る。Further, by using a mold, the Neri bait (1) is molded into a dango shape as shown in FIG. 6 and a dango shape with an insertion hole (3) for the fishing line (2) as shown in FIG. I can do things. In this way, the Neri bait (1) is formed into a shape that can be easily tensioned.
【００１９】そして、成形したネリ餌(１)をゲル化剤溶
液中に浸漬し、釣り餌を形成する。この場合、ゲル化剤
溶液の濃度を３％〜５％にすれば、浸漬時間は10分〜15
分と短く、ゲル化剤の使用量も少なくコストが割安とな
る。Then, the molded Neri bait (1) is dipped in the gelling agent solution to form a fishing bait. In this case, if the concentration of the gelling agent solution is 3% to 5%, the immersion time is 10 minutes to 15 minutes.
It is short, the amount of gelling agent used is small, and the cost is low.
【００２０】また、このゲル化剤溶液に用いるゲル化剤
には、乳酸カルシウム、塩化カルシウムの内から選択し
た一種または二種を用いる事ができる。この場合、乳酸
カルシウムを用いると、ゲル化した被膜は柔らかく、ま
た比重が軽いものとなる。また塩化カルシウムを用いる
と、ゲル化した被膜は固く、比重は重くなる。このよう
に浸漬して表面をゲル化したネリ餌(１)は、ハリ掛け、
餌持ち等が向上し、良好な釣りが可能となる。また、簡
易な方法で製造を行うため、廉価な製造が可能となる。As the gelling agent used in this gelling agent solution, one or two selected from calcium lactate and calcium chloride can be used. In this case, when calcium lactate is used, the gelled film becomes soft and has a low specific gravity. When calcium chloride is used, the gelled film becomes hard and the specific gravity becomes heavy. The Neri bait (1) whose surface has been gelled by soaking is hung on
Bait retention is improved and good fishing becomes possible. In addition, since the manufacturing is performed by a simple method, the manufacturing cost can be reduced.
【００２１】また、上記第１の発明では、原料餌の練り
込み後、ネリ餌(１)を、加圧成形し、ゲル化剤溶液中に
浸漬した。しかし、第２の発明に於ては、原料餌の練り
込み後、ネリ餌(１)にゲル化剤を混合する。また、この
ゲル化剤として、乳酸カルシウム、塩化カルシウムの内
から選択した一種または二種を用いる事ができる。In the first aspect of the invention, after kneading the raw material feed, the Neri feed (1) is pressure-molded and immersed in the gelling agent solution. However, in the second invention, the gelling agent is mixed with the Neri bait (1) after kneading the raw material bait. As the gelling agent, one or two selected from calcium lactate and calcium chloride can be used.
【００２２】このゲル化剤の混合方法には、ゲル化剤を
粉末等の状態で直接混合する方法と、ゲル化剤溶液とし
て混合する方法とがある。そして、ゲル化剤を直接混合
する場合、0.1wt％〜1.5wt％を混合する。また、ゲル化
剤溶液として混合する場合、0.1％〜1.5％濃度のゲル剤
溶液を５wt％〜15wt％混合する。そして、最後に、ネリ
餌(１)を、上記第１の発明と同様に種々の形状に加圧成
形して、釣り餌を形成する。As a method for mixing the gelling agent, there are a method of directly mixing the gelling agent in a powder state or a method of mixing as a gelling agent solution. When the gelling agent is directly mixed, 0.1 wt% to 1.5 wt% is mixed. When mixed as a gelling agent solution, a gelling agent solution having a concentration of 0.1% to 1.5% is mixed at 5% by weight to 15% by weight. Then, finally, the Neri bait (1) is pressure-molded into various shapes in the same manner as the above-mentioned first invention to form a fishing bait.
【００２３】このようにゲル化剤をネリ餌(１)に混合す
ると、ネリ餌(１)は、内部でゲル化被膜を形成し、ハリ
持ちが向上する。また、このネリ餌(１)は、ゲル化剤溶
液に浸漬する場合に比し加工がし易く、手指等で任意の
形状、大きさ等に変形させる事が可能となる。When the gelling agent is mixed with the Neri bait (1) in this way, the Neri bait (1) forms a gelled film inside, and the firmness is improved. In addition, this Neri bait (1) is easier to process as compared with the case where it is immersed in the gelling agent solution, and it can be deformed into an arbitrary shape, size, etc. by fingers or the like.
【００２４】また、上記のゲル化剤の混合比率は、原料
餌の種類、水分の量等により必ずしも、限定されるもの
ではない。また、原料餌として、オキアミ等の既にゲル
化剤が含まれている餌を使用する場合には、ゲル化剤の
混合比率を少なめにして調整する必要がある。また、混
合するゲル化剤の量が少ないと、ネリ餌(１)は保形性が
低下し、ハリ持ちが悪くなる。また、ゲル化剤の混合量
が多いと、ダンゴ状のダマとなるだけで、成形が困難と
なる。The mixing ratio of the above gelling agent is not necessarily limited depending on the kind of raw material feed, the amount of water and the like. Further, when using a feed such as krill which already contains a gelling agent, it is necessary to adjust the mixing ratio of the gelling agent to be small. Further, when the amount of the gelling agent mixed is small, the shape retention of the Neri bait (1) is lowered and the firmness thereof is deteriorated. Further, if the amount of the gelling agent mixed is large, only dango-like lumps are formed, which makes molding difficult.
【００２５】また、上記第２の発明では、加圧成形を最
終工程とした。しかし、第３の発明に於ては、加圧成形
後、成形したネリ餌(１)を、３％〜５％濃度のゲル化剤
溶液中に10分〜15分間浸漬し、釣り餌を形成する。この
場合に於ても、ゲル化剤溶液に用いるゲル化剤は、上記
第１の発明と同様に、乳酸カルシウム、塩化カルシウム
の内から選択した一種または二種を用いる事ができる。
このように形成すると、ネリ餌(１)は、内部と表面とが
迅速にゲル化し、太めのネリ餌(１)を成形する場合に、
好適なものとなる。Further, in the second invention, pressure molding is the final step. However, in the third invention, after pressure molding, the molded Neri bait (1) is immersed in a gelling agent solution having a concentration of 3% to 5% for 10 to 15 minutes to form a fishing bait. To do. Also in this case, the gelling agent used in the gelling agent solution may be one or two selected from calcium lactate and calcium chloride, as in the first invention.
When formed in this way, the Neri bait (1) rapidly gels inside and on the surface, and when forming a thick Neri bait (1),
It will be suitable.
【００２６】また、上記では、釣り餌は生餌状態とし
た。しかしながら、釣り餌は最終工程に於て温水等で加
熱した後、冷却して形成する事も可能である。このよう
に形成すると、釣り餌は、弾力性が得られ、海中での餌
持ちが良くなるとともに保存性も向上できるものとな
る。Further, in the above, the fishing bait is in a raw bait state. However, it is also possible to form the fishing bait by heating it with warm water in the final step and then cooling it. When formed in this manner, the fishing bait can have elasticity, have better bait retention in the sea, and can be more storable.
【００２７】[0027]
【実施例】以下本発明の第１実施例を説明する。まず、
冷凍状態のオキアミを解凍し、このオキアミを細かく粉
砕して、原料餌を形成する。そしてこの１kgの原料餌に
250ｇの水を加えてネリ餌を形成する。また、このネリ
餌に３wt％のアルギン酸ナトリウムを混合して練り込
み、ネリ餌に粘りを生じさせる。EXAMPLE A first example of the present invention will be described below. First,
Frozen krill is thawed and this krill is finely crushed to form a raw material feed. And to this 1kg raw material feed
Add 250 g of water to form a Neri bait. In addition, 3 wt% of sodium alginate is mixed and kneaded into the Neri bait to make the Neri bait sticky.
【００２８】次に、このネリ餌を注出器に導入し、この
注出器のネリ餌を棒状に加圧成形した後、３％濃度の塩
化カルシウム溶液中に15分間浸漬してゲル化させる。そ
して、このゲル化したネリ餌を、釣りの対象魚に対応し
て適宜な長さに切断し、冷凍する。Next, this Neri bait is introduced into a pouring device, the Neri bait of this pouring device is pressure-molded into a rod shape, and then immersed in a 3% concentration calcium chloride solution for 15 minutes to cause gelation. . Then, the gelled Neri bait is cut into a suitable length corresponding to the fish to be fished and frozen.
【００２９】また、第２実施例に於ては、粉砕した原料
餌に水を加えてネリ餌を形成するまでは第１実施例と同
様である。そして、このネリ餌に４wt％のアルギン酸ナ
トリウムを混合して練り込み、ネリ餌に粘りを生じさせ
る。Further, the second embodiment is the same as the first embodiment until water is added to the crushed raw material feed to form the Neri feed. Then, 4 wt% of sodium alginate is mixed and kneaded into the Neri bait so that the Neri bait becomes sticky.
【００３０】次に、このネリ餌に0.5％濃度の乳酸化カ
ルシウム溶液を10wt％加え、さらに練り込み、ダンゴ状
に成形する。そして、このダンゴ状のネリ餌を冷凍す
る。Next, 10 wt% of calcium lactate solution having a concentration of 0.5% is added to the Neri bait and further kneaded to form a dango-like shape. Then, this dango-like feed is frozen.
【００３１】また、第３実施例に於ては、ネリ餌をダン
ゴ状に成形するまでは、第２実施例と同様である。そし
て、このダンゴ状のネリ餌を、３％濃度の塩化カルシウ
ム溶液中に15分間浸漬してゲル化した後、ネリ餌を冷凍
する。The third embodiment is the same as the second embodiment until the duck-shaped bait is formed. Then, this dango-like Neri food is immersed in a 3% calcium chloride solution for 15 minutes for gelation, and then the Neri food is frozen.
【００３２】[0032]
【発明の効果】本発明はネリ餌を用いた食わせ用の釣り
餌に於て、釣り餌は、ゲル化しているため、水中に投入
されても、上層でバラケる事がなく、餌持ちが良好とな
って、中層、海底に確実に到達し、中層魚、根魚を対象
とした釣りが可能となる。INDUSTRIAL APPLICABILITY The present invention relates to a fishing bait for feeding using a Neri bait, and since the fishing bait is gelled, it does not disperse in the upper layer even if it is put into water, and the bait is retained. It will be good, and it will reach the middle layer and the seabed reliably, and it will be possible to fish for middle-class fish and root fish.
【００３３】また、投げ釣りに用いても、ネリ餌はハリ
から離脱するような事がなく、釣りの広範囲な使用が可
能となるものである。Also, when used for throwing fishing, the Neri bait does not come off from the firmness, and the fishing can be widely used.
【００３４】また、第１の発明に於ては、ネリ餌は、ハ
リ掛け、餌持ち等が向上し、良好な釣りが可能となる。
また、簡易な方法で製造を行うため、廉価な製造が可能
となる。Further, in the first aspect of the present invention, the hooked bait improves the hooking and holding of the bait and enables good fishing.
In addition, since the manufacturing is performed by a simple method, the manufacturing cost can be reduced.
【００３５】また、第２の発明に於ては、ネリ餌は、ネ
リ餌は、内部でゲル化被膜を形成し、ハリ持ちが向上す
る。また、ゲル化剤溶液に浸漬する場合に比し加工がし
易く、手指等で任意の形状、大きさ等に変形させる事が
可能となる。Further, in the second aspect of the invention, the Neri bait has a gelling film formed inside, and the firmness is improved. Further, it is easier to process as compared with the case where it is immersed in the gelling agent solution, and it is possible to deform it into an arbitrary shape, size, etc., with fingers or the like.
【００３６】また、第３の発明に於ては、ネリ餌は、内
部と表面とが迅速にゲル化し、太めのネリ餌を成形する
場合に、好適なものとなる。According to the third aspect of the invention, the Neri bait is suitable for forming a thick Neri bait by rapidly gelling the inside and the surface.
【図１】ウドン状の釣り餌を示す斜視図。FIG. 1 is a perspective view showing a fishing bait in an udon shape.
【図２】マカロニ状の釣り餌を示す斜視図。FIG. 2 is a perspective view showing a macaroni-shaped fishing bait.
【図３】短冊状の釣り餌を示す斜視図。FIG. 3 is a perspective view showing a strip of fishing bait.
【図４】短冊状にねじりを加えた状態の釣り餌を示す斜
視図。FIG. 4 is a perspective view showing a fishing bait in a state in which a strip is twisted.
【図５】短冊状に曲げを加えた状態の釣り餌を示す斜視
図。FIG. 5 is a perspective view showing the fishing bait in a state of being bent in a strip shape.
【図６】ダンゴ状の釣り餌を示す斜視図。FIG. 6 is a perspective view showing a dango-shaped fishing bait.
【図７】挿通穴を設けてダンゴ状とした釣り餌を示す斜
視図。FIG. 7 is a perspective view showing a fishing bait having an insertion hole and a dango shape.
１ ネリ餌 1 Neri bait
Claims (6)
増粘剤を１wt％〜20wt％混合してネリ餌を形成し、この
ネリ餌を加圧成形した後、ゲル化剤溶液中に浸漬し、ネ
リ餌をゲル化して製造する事を特徴とする釣り餌の製造
方法。1. A Neri bait is formed by mixing a raw material bait with a thickener composed of sodium alginate in an amount of 1 wt% to 20 wt%, and the Neri bait is pressure-molded and then immersed in a gelling agent solution. A method for producing a fishing bait, which comprises producing a bait by gelling it.
増粘剤を１wt％〜20wt％混合してネリ餌を形成し、この
ネリ餌にゲル化剤を混合して加圧成形し、ネリ餌をゲル
化して製造する事を特徴とする釣り餌の製造方法。2. A Neri bait is formed by mixing 1 wt% to 20 wt% of a thickening agent composed of sodium alginate with a raw material bait, and a gelling agent is mixed with the Neri bait and pressure-molded to gel the Neri bait. A method for producing a fishing bait, which comprises producing the fishing bait.
増粘剤を１wt％〜20wt％混合してネリ餌を形成し、この
ネリ餌にゲル化剤を混合して、加圧成形した後、ゲル化
剤溶液中に浸漬し、ネリ餌をゲル化して製造する事を特
徴とする釣り餌の製造方法。3. A raw material feed is mixed with a thickening agent consisting of sodium alginate in an amount of 1 wt% to 20 wt% to form a Neri feed, and this Neri feed is mixed with a gelling agent and pressure-molded, followed by gelation. A method for producing a fishing bait, which is characterized in that it is immersed in an agent solution and gelled from the neri bait.
てカルボキシメチルセルロース、ポリアクリル酸ナトリ
ウム、カラギーナン、グァーガム、糖分、α−デンプン
の内から選択した一種または二種以上を添加する事を特
徴とする請求項１、２、３の釣り餌の製造方法。4. The thickener is characterized by adding one or more selected from carboxymethyl cellulose, sodium polyacrylate, carrageenan, guar gum, sugar and α-starch in addition to sodium alginate. The method for manufacturing the fishing bait according to claim 1, 2, or 3.
シウムの内から選択した一種または二種である事を特徴
とする請求項１、２、３の釣り餌の製造方法。5. The method for producing a fishing bait according to claim 1, 2 or 3, wherein the gelling agent is one or two selected from calcium lactate and calcium chloride.
する事を特徴とする請求項１、２、３の釣り餌の製造方
法。6. The method for producing a fishing bait according to claim 1, 2, 3 or 4, wherein the Neri bait is heated and cooled after gelling.