JPH06327856A - Wadding for futon - Google Patents
Wadding for futonInfo
- Publication number
- JPH06327856A JPH06327856A JP14686393A JP14686393A JPH06327856A JP H06327856 A JPH06327856 A JP H06327856A JP 14686393 A JP14686393 A JP 14686393A JP 14686393 A JP14686393 A JP 14686393A JP H06327856 A JPH06327856 A JP H06327856A
- Authority
- JP
- Japan
- Prior art keywords
- fibers
- fiber
- futon
- cotton
- crimped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は天然繊維と潜在捲縮又は
高収縮性を有する合成繊維とが混合されたふとん用詰綿
材料に関し、従来のふとん用詰綿材料と比較して繰り返
し圧縮による嵩保持率が高く、へたり難く、所謂床つき
感の少ない、例えば敷ふとん用としては極めて優れた性
能を有するふとん用詰綿材料を提供するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cotton stuffing material for futon, which is a mixture of natural fibers and synthetic fibers having latent crimp or high shrinkability, and is obtained by repeated compression as compared with a conventional cotton stuffing material for futon. It is intended to provide a stuffed cotton material for a futon, which has a high bulk retention rate, is hard to settle down, and has a so-called floor feeling, and has extremely excellent performance for, for example, a futon.
【０００２】[0002]
【従来の技術】従来からふとん用詰綿材料として天然繊
維特に綿のみ又は合成繊維のみ又は天然繊維と合成繊維
とを混合し、それぞれカ−デイングしてウエツブを積層
したものがある。また本出願人の発明になる天然繊維の
わたの中に少なくとも一部がコイル状の合成繊維よりな
り、かつ天然繊維わた中に絡合混在せしめたふとん綿に
関する発明がある。（特開昭63−222792号）2. Description of the Related Art Conventionally, as a cotton stuffing material for futon, there has been a natural fiber, particularly cotton alone or synthetic fiber alone, or a mixture of natural fiber and synthetic fiber, each of which is carded and laminated with a web. Further, there is an invention relating to a futon cotton which is made of a synthetic fiber having a coil shape at least partially in a natural fiber cotton which is invented by the present applicant and which is entangled and mixed in the natural fiber cotton. (JP-A-63-222792)
【０００３】[0003]
【発明が解決しようとする課題】天然繊維、例えば綿や
羊毛のふとん用詰綿材料は使用繊維によつて程度の差は
あるが吸湿性、吸水性などに優れた性能を有しているも
のの、嵩高性に乏しいためにふとん用詰綿材料としては
その重量を増加させる必要があり、天然繊維に合成繊維
を混合したふとん用詰綿材料はわたのへたりが大きいた
め、所謂せんべいふとんになりやすいという問題点があ
る。更に上記本出願人の特開昭63−222792号発明は通常
の顕在化した捲縮繊維を使用しているので、混綿工程で
既に天然繊維と部分的に絡合して均一なウエブができ
ず、そのためふとん綿が均一な嵩高性を発揮できない問
題点があつた。そのためふとんの圧縮抵抗のバラツキが
大であつた。Natural fibers, such as cotton and wool stuffing materials for futons of wool, have excellent hygroscopicity and water-absorbing properties, although they differ to some extent depending on the fibers used. However, because of its low bulkiness, it is necessary to increase its weight as a futon stuffing material, and because the futon stuffing material that mixes natural fibers with synthetic fibers has a large cotton slip, it becomes a so-called senbei futon. There is a problem that it is easy. Further, since the above-mentioned Japanese Patent Application Laid-Open No. 63-222792 of the present applicant uses ordinary crimped fibers, it cannot be uniformly entangled with natural fibers in the blending step to form a uniform web. However, there is a problem in that the futon cotton cannot exhibit uniform bulkiness. Therefore, there was a large variation in the compression resistance of the futon.
【０００４】上記の問題点を解決するために、本発明は
上記本発明者の先願発明を改良して、充分満足すべきふ
とんの詰綿材料として嵩高でかつ床つき感がなく、しか
も嵩高性が低下することのない所謂へたりの少ないふと
ん用詰綿材料を提供することを目的とするものである。In order to solve the above-mentioned problems, the present invention is an improvement on the above-mentioned prior invention of the present inventor, and is a bulky cotton material for futon which is sufficiently satisfactory and has no feeling of flooring and is bulky. The purpose of the present invention is to provide a so-called futon-filled cotton material with less sagging, which does not deteriorate its properties.
【０００５】[0005]
【課題を解決するための手段】本発明の第１は天然繊維
と２種類以上のポリエステル系繊維とが均一に混綿さ
れ、該２種類以上のポリエステル系繊維の少なくとも１
種類が３デニ−ル以上、１５デニ−ル以下の潜在捲縮繊
維及び／又は高収縮性繊維と顕在化した立体捲縮中空繊
維で構成され、該捲縮繊維に混綿後熱処理が施されるこ
とによつて捲縮の発現した該潜在捲縮繊維及び／又は高
収縮性繊維が他の繊維に絡み合つてなることを特徴とす
るふとん用詰綿材料であり、The first aspect of the present invention is to uniformly mix natural fibers and two or more kinds of polyester fibers, and at least one of the two or more kinds of polyester fibers.
It is composed of latent crimp fibers and / or highly shrinkable fibers of 3 denier or more and 15 denier or less and three-dimensionally crimped hollow fibers that are exposed, and the crimped fibers are heat treated after being mixed. A latent stuffing material for a futon, characterized in that the latently crimped fibers and / or the highly shrinkable fibers in which crimps are expressed thereby are entangled with other fibers,
【０００６】その第２は第１発明において天然繊維が羊
毛及び／又は木綿であり、その第３は第１発明において
潜在捲縮繊維が２種類のポリエステル系繊維の貼り合わ
せ構造又は潜在捲縮繊維偏芯型芯鞘構造であり、その第
４は第１発明において高収縮性繊維がその乾熱収縮率
（ＳＨＤ）≧２０％であり、かつ繊維断面形態が中空状
であり、更にその第５は前記第１、第２、第３、第４発
明において、天然繊維とポリエステル系繊維との混合割
合が重量比で３：７〜７：３であり、かつ全構成繊維に
占める潜在捲縮繊維及び／又は高収縮性繊維と顕在化し
た立体捲縮中空維繊との比率が少なくとも２０重量％以
上である、ふとん用詰綿材料に関するものである。In the second aspect, the natural fiber in the first invention is wool and / or cotton, and in the third aspect, in the first invention, the latent crimp fiber is a laminated structure of two types of polyester fibers or the latent crimp fiber. An eccentric core-sheath structure, the fourth of which is that in the first invention, the highly shrinkable fiber has a dry heat shrinkage (SHD) ≧ 20%, and the fiber cross-sectional shape is hollow. In the above first, second, third, and fourth inventions, the mixing ratio of the natural fiber and the polyester fiber is 3: 7 to 7: 3 by weight, and the latent crimped fiber accounts for all the constituent fibers. And / or a stuffed cotton material for futon, in which the ratio of the highly shrinkable fibers and the three-dimensionally crimped hollow fibers that have become apparent is at least 20% by weight or more.
【０００７】本発明の天然繊維は羊毛、木綿、麻、絹な
ど特に限定されるものではないが、汎用性の面で羊毛又
は木綿が好ましく、特に混綿工程で均一に混綿されカ−
デイング後均一なウエツブが形成され潜在捲縮繊維の捲
縮が発現した場合、潜在捲縮繊維との絡み合いが著しく
強くなる捲縮を有する羊毛が特に好ましい。また本発明
の潜在捲縮繊維は２種類のポリエステル系繊維を貼り合
わせた構造又は偏芯型芯鞘構造又は高収縮性繊維にして
カ−デイング処理後に熱処理することにより捲縮数が２
倍以上になる繊維が好適に使用され、３デニ−ル以上、
１５デニ−ル以下の繊度が必要である。繊度が３デニ−
ル未満であると熱処理により捲縮が発現しても数が少な
く、必要な絡み合い性が得られないし、また１５デニ−
ルを超過すると、熱処理によつて硬くなりすぎて嵩不足
となる欠点がある。The natural fiber of the present invention is not particularly limited to wool, cotton, hemp, silk, etc., but wool or cotton is preferable from the viewpoint of versatility, and particularly, the cotton which is uniformly mixed in the cotton mixing process is used.
Wool having crimps in which the entanglement with the latently crimped fibers is remarkably strong when a uniform web is formed after the dening and the crimps of the latently crimped fibers are expressed, are particularly preferable. The latent crimped fiber of the present invention is made into a structure in which two types of polyester fibers are bonded together, an eccentric core-sheath structure or a highly shrinkable fiber, and the number of crimps is 2 by heat treatment after the carding treatment.
Fibers that are more than doubled are preferably used, and 3 denier or more,
A fineness of 15 denier or less is required. Fineness is 3 deniers
If it is less than 1, the number of crimps generated by heat treatment is small and the required entanglement property cannot be obtained.
If it exceeds the range, there is a drawback that it becomes too hard due to heat treatment and becomes insufficient in bulk.
【０００８】また高収縮性繊維はその乾熱収縮率（ＳＨ
Ｄ）≧２０％であり、中空繊維であることが好ましい。
ＳＨＤ＜２０％では収縮による充分満足すべき捲縮が発
現しないため、本発明のふとん用詰綿材料としては不適
当である。顕在化した立体捲縮性繊維は５デニ−ル以上
の中空又は異形断面形状であることが嵩高性、保温性、
弾力性から特に望ましい。潜在捲縮繊維は捲縮の発現性
能の面よりすると望ましくは繊度が５デニ−ル以上であ
る。断面形状については丸、中空、異形など特に限定は
ない。全構成繊維に占めるポリエステル系繊維の比率は
３０〜７０重量％であり、また全構成繊維に占める潜在
捲縮繊維又は高収縮性繊維の比重は少なくとも２０重量
％以上が必要である。Further, the highly shrinkable fiber has a dry heat shrinkage (SH
D) ≧ 20%, preferably hollow fibers.
When SHD <20%, a sufficient crimp due to shrinkage does not appear, so that it is unsuitable as the futon material of the present invention. The revealed three-dimensional crimpable fiber has a hollow or irregular cross-sectional shape of 5 denier or more, and is bulky, heat-retaining, and
Especially desirable due to its elasticity. The latent crimped fiber preferably has a fineness of 5 denier or more in view of the crimp development performance. The cross-sectional shape is not particularly limited, such as round, hollow, or irregular shape. The proportion of polyester fibers in all the constituent fibers is 30 to 70% by weight, and the specific gravity of latently crimped fibers or highly shrinkable fibers in all the constituent fibers must be at least 20% by weight or more.
【０００９】上記ポリエステル系繊維の比率が３０重量
％未満では嵩高性が著しく減少して本発明の目的を達成
することができず、また７０重量％を超過すると天然繊
維の含有比率が低くなるため吸湿性など天然繊維の優れ
た性能が減殺される。また更に全構成繊維に対する潜在
捲縮繊維又は高収縮性繊維の比率が２０重量％未満では
繊維間の絡み合いが弱くふとんとしての床つき感が生
じ、また嵩の回復性も悪くなる。また潜在捲縮繊維又は
高収縮性繊維の比率が５０重量％を越えると嵩不足にな
る。特に望ましくはポリエステル系繊維の比率が４０〜
６０重量％、潜在捲縮、高収縮性繊維の比率が３０〜５
０重量％の範囲であることが本発明者の研究の結果判明
した。If the proportion of the polyester fiber is less than 30% by weight, the bulkiness is remarkably reduced and the object of the present invention cannot be achieved, and if it exceeds 70% by weight, the content ratio of the natural fiber becomes low. The excellent properties of natural fibers such as hygroscopicity are diminished. Further, if the ratio of the latently crimped fibers or the highly shrinkable fibers to all the constituent fibers is less than 20% by weight, the entanglement between the fibers is weak and a flooring feeling as a futon occurs, and the bulk recovery property is deteriorated. If the ratio of latently crimped fibers or highly shrinkable fibers exceeds 50% by weight, the bulk becomes insufficient. Particularly preferably, the ratio of polyester fiber is 40 to
60% by weight, the ratio of latent crimp and highly shrinkable fiber is 30 to 5
It was found as a result of the study by the present inventor that the range was 0% by weight.
【００１０】本発明のふとん用詰綿材料は通常羊毛のふ
とん製造設備であるスチ−ムアンドドライ（Steam and
Dry ）加工機で容易に製造することができる。即ち所定
の割合で天然繊維とポリエステル系繊維とを混綿し、カ
−デイングをしてウエツブとし、所定の厚さまで積層し
た後、該積層されたウエツブを熱処理するか或はエアレ
イ方式でウエツブを製造することも可能である。天然繊
維が羊毛の場合は熱処理前にスチ−ミングを施すと羊毛
の捲縮の発現がより強固になり、従つて繊維間の絡み合
いがより強固になり好適である。また加熱処理前に軽度
のニ−ドルパンチング又は接着剤の付与をすることも可
能である。熱処理条件は潜在捲縮繊維の捲縮が発現する
条件を選定すればよく、通常は150 〜170 ℃で３〜１０
分間の熱処理で充分である。The cotton stuffing material for futon of the present invention is usually steam and dry (Steam and Dry)
Dry) Can be easily manufactured with a processing machine. That is, natural fibers and polyester fibers are mixed at a predetermined ratio, carded into a web, laminated to a predetermined thickness, and then the laminated web is heat-treated or manufactured by an air-laid method. It is also possible to do so. When the natural fibers are wool, it is preferable to perform steaming before the heat treatment so that the crimps of the wool are more strongly developed, and accordingly the entanglement between the fibers is stronger. It is also possible to apply mild needle punching or apply an adhesive agent before the heat treatment. The heat treatment conditions may be selected so that the crimp of the latently crimped fiber is developed. Usually, the heat treatment is carried out at 150 to 170 ° C. for 3 to 10
A heat treatment of minutes is sufficient.
【００１１】[0011]
【実施例】以下に本発明を実施例によつて説明するが、
本発明は実施例のみに限定されるものではない。本発明
の評価に使用した物性値の測定方法を次に示す。 (イ) 繰り返し圧縮嵩保持率 詰綿材料を３０×３０cmで６０g となるように調整し、
0.6g／cm2 の荷重をのせて初期厚さ（Ｈ０）を測定す
る。次にＨ０の１／５の厚さまで圧縮することを１ＨＺ
の周期で２万回繰り返した後、0.2g／cm2 の荷重をのせ
て繰り返し圧縮後の厚さ（Ｈ１）を測定する。嵩保持率
を次式で計算する。 嵩保持率％＝（Ｈ１／Ｈ０）×１００ 数字が大きいほど嵩の保持性能が良い。嵩保持率≧８０
％が望ましい。 (ロ) 圧縮係数 上記と同様に調整した詰綿材料に2.6g／cm2 の荷重をの
せて厚さ（Ｈ２）を測定する。次に25.6g ／cm2 の荷重
をのせて厚さ（Ｈ３）を測定し、圧縮係数を次式で計算
する。 圧縮係数＝Ｈ２／Ｈ３ 圧縮係数が４以上の場合寝た時に床つき感を感じる。圧
縮係数≦４が望ましい。 (ハ) ウエツブ強力詰綿材料を５×２５cmで約２g となる
ように調整し、定速引張試験機で幅５cm、間隔２０cmに
保持し引張強力（Ｔ）を測定し、次式を使用して計算す
る。 ウエブ強力（ｇ／ｇ）＝Ｔ／詰綿材料重量 ウエブ強力が大きいほどウ−ルと合成繊維の絡み合いが
強く、嵩保持率の向上、ウ−ルのフエルト化を防止する
と同時に適度の弾力性を付与する。ウエブ強力≧2.5g/g
が望ましい。EXAMPLES The present invention will be described below with reference to examples.
The invention is not limited to the examples. The methods for measuring physical property values used in the evaluation of the present invention are shown below. (B) Repeated compression bulk retention ratio Adjust the stuffing material to 30 g by 30 cm and 60 g,
The initial thickness (H0) is measured under a load of 0.6 g / cm 2 . Then compressing to a thickness of 1/5 of H0 is 1HZ
After repeating 20,000 times in the above cycle, a load of 0.2 g / cm 2 is applied and the thickness (H1) after repeated compression is measured. The bulk retention rate is calculated by the following formula. Bulk retention rate = (H1 / H0) x 100 The larger the number, the better the bulk retention performance. Bulk retention ≧ 80
% Is desirable. (B) Compression coefficient A thickness of (H2) is measured by applying a load of 2.6 g / cm 2 to the wadding material prepared as described above. Next, the thickness (H3) is measured by applying a load of 25.6 g / cm 2 , and the compression coefficient is calculated by the following formula. Compression coefficient = H2 / H3 When the compression coefficient is 4 or more, a feeling of flooring is felt when sleeping. It is desirable that the compression coefficient ≦ 4. (C) Adjust the tensile strength (T) of the wet strong cotton stuffing by adjusting the width to 5g and the width to 20g with a constant speed tensile tester and measure the tensile strength (T) using the following formula. Calculate. Web strength (g / g) = T / weight of stuffed material The higher the web strength, the stronger the entanglement between the wool and the synthetic fiber, which improves the bulk retention rate and prevents the felt from becoming a felt, while also having a moderate elasticity. Is given. Web strength ≧ 2.5g / g
Is desirable.
【００１２】[0012]
【実施例１，２】繊度５デニ−ルのポリエステル系潜在
捲縮綿（Ａ）、フランスウ−ル（Ｂ）及び繊度１３デニ
−ルの中空ポリエステル綿（Ｃ）を〔表１〕に示す重量
比２：４：４（実施例１）及び３：５：２（実施例２）
の割合で混合し、オ−プナ−、ロ−ラ−カ−ド、クロス
レイヤ−で処理し、160 ℃セツタ−で熱処理して詰綿材
料を製造した。得られた詰綿材料の物性を〔表２〕に示
す。また熱処理前後の繊維形態の一実施例を〔図１〕、
〔図２〕に示した。〔図１〕、〔図２〕において(1)は
羊毛、(2) は潜在捲縮ポリエステル繊維、(3) は捲縮発
現のポリエステル系繊維である。Examples 1 and 2 [Table 1] shows a polyester latent crimped cotton (A) having a fineness of 5 denier, a French wool (B) and a hollow polyester cotton (C) having a fineness of 13 denier. Weight ratios 2: 4: 4 (Example 1) and 3: 5: 2 (Example 2)
The mixture was mixed in the following proportions, treated with an opener, a roller card and a cross layer, and heat-treated in a 160 ° C. setter to produce a cotton material. The physical properties of the obtained wadding material are shown in [Table 2]. In addition, one example of fiber morphology before and after heat treatment [Fig. 1],
It is shown in [Fig. 2]. In FIGS. 1 and 2, (1) is wool, (2) is latently crimped polyester fiber, and (3) is crimped polyester fiber.
【００１３】[0013]
【表１】 [Table 1]
【００１４】[0014]
【表２】 [Table 2]
【００１５】[0015]
【図１】[Figure 1]
【００１６】[0016]
【図２】[Fig. 2]
【００１７】[0017]
【実施例３，４】実施例１の原料（Ａ）と（Ｂ）を重量
比３：７及び５：５の割合で混合し、実施例１と同じ方
法で詰綿材料を製造した。得られた詰綿材料の特性を
〔表２〕に示した。Examples 3 and 4 The raw materials (A) and (B) of Example 1 were mixed in a weight ratio of 3: 7 and 5: 5, and a wadding material was produced in the same manner as in Example 1. The characteristics of the obtained cotton material are shown in [Table 2].
【００１８】[0018]
【比較例１】実施例２のポリエステル系潜在捲縮綿の繊
度を2.5 デニ−ルに変えて、実施例１と同じ方法で詰綿
材料を製造した。得られた詰綿材料の物性を〔表２〕に
示す。Comparative Example 1 A wadding material was produced in the same manner as in Example 1 except that the polyester latent crimped cotton of Example 2 had a fineness of 2.5 denier. The physical properties of the obtained wadding material are shown in [Table 2].
【００１９】[0019]
【比較例２】実施例４の原料（Ａ）を（Ｃ）に代えた以
外は同一方法で詰綿材料を製造した。得られた詰綿材料
の特性を〔表２〕に示す。Comparative Example 2 A cotton material was manufactured by the same method except that the raw material (A) of Example 4 was replaced with (C). The characteristics of the obtained wadding material are shown in [Table 2].
【００２０】[0020]
【比較例３】実施例１の原料（Ａ），（Ｂ），（Ｃ）の
混合割合を１：５：４とした以外は同一方法で詰綿材料
を製造した。得られた詰綿材料の特性を〔表２〕に示
す。〔表１〕，〔表２〕に示すように本発明のふとん用
詰綿材料は比較例として採用した従来の詰綿材料よりも
顕在化し優れた特性を有している。Comparative Example 3 A wadding material was produced by the same method except that the mixing ratio of the raw materials (A), (B) and (C) of Example 1 was changed to 1: 5: 4. The characteristics of the obtained wadding material are shown in [Table 2]. As shown in [Table 1] and [Table 2], the cotton stuffing material for futon of the present invention has properties which are apparent and superior to the conventional cotton stuffing material used as a comparative example.
【００２１】[0021]
【発明の効果】本発明は従来の天然繊維と合成繊維とが
混合されたふとん用詰綿材料と比較した場合、潜在捲縮
が均一に形成されているため、繰り返し圧縮による嵩保
持率が高く、へたり難く、また圧縮係数が低く、床つき
感が少なく、かつウエツブ強力が大であるため使用中の
羊毛のフエルト化がしにくく、また天然繊維と捲縮繊維
とが均一に絡合しているため洗濯した時の綿切れの発生
が少ないなど優れた特性を有する新規なふとん用詰綿材
料を提供するものである。INDUSTRIAL APPLICABILITY According to the present invention, when compared with the conventional cotton stuffing material for a futon, which is a mixture of natural fibers and synthetic fibers, the latent crimps are formed uniformly, so that the bulk retention rate by repeated compression is high. It is hard to settle down, has a low compression coefficient, has a low feeling of flooring, and has a high wetting strength, so it is difficult to make the felt wool felt during use, and the natural fibers and crimped fibers are evenly entangled. Therefore, the present invention provides a novel stuffed cotton material for futon, which has excellent properties such as less occurrence of cotton breakage when washed.
【図１】本発明の羊毛とポリエステル潜在捲縮繊維を使
用したふとん用詰綿材料の熱セツト前の状態を示す斜視
図の一実施例。FIG. 1 is an embodiment of a perspective view showing a state before heat setting of a cotton stuffing material for a futon using wool and polyester latently crimped fiber of the present invention.
【図２】〔図１〕のふとん用詰綿材料の熱セツト後、ポ
リエステル潜在捲縮繊維が均一に混合され、捲縮が発現
した状態を示す斜視図。FIG. 2 is a perspective view showing a state in which the latent polyester crimped fibers are uniformly mixed and crimps are developed after the heat setting of the cotton stuffing material for futon of FIG.
【符号の説明】 １．羊毛繊維 ２．熱処理前の潜在捲縮を有するポリエステル繊維 ３．熱処理後の捲縮を発現せしめたポリエステル繊維[Explanation of symbols] 1. Wool fiber 2. 2. Polyester fiber having latent crimp before heat treatment Polyester fiber with crimp after heat treatment
Claims (5)
繊維とが混綿されたふとん用詰綿材料において、該２種
類以上のポリエステル系繊維の少なくとも１種類が３デ
ニ−ル以上、１５デニ−ル以下の潜在捲縮繊維及び／又
は高収縮性繊維と顕在化した立体捲縮中空繊維で構成さ
れ、該捲縮繊維に混綿後熱処理が施されることによつて
捲縮の発現した該潜在捲縮繊維および／又は高収縮繊維
が他の繊維に、絡み合つてなることを特徴とするふとん
用詰綿材料。1. A stuffing material for futon, which is a mixture of natural fibers and two or more types of polyester fibers, wherein at least one of the two or more types of polyester fibers is 3 denier or more, 15 denier. The latent crimp fiber and / or the highly shrinkable fiber and the three-dimensional crimped hollow fiber which have been revealed, and the latent crimp in which the crimp has been developed by subjecting the crimped fiber to heat treatment after mixing. A stuffed cotton material for a futon, characterized in that crimped fibers and / or highly shrinkable fibers are intertwined with other fibers.
求項１記載のふとん用詰綿材料。2. The futon material for futon according to claim 1, wherein the natural fiber is wool and / or cotton.
維の貼り合わせ構造又は偏芯型芯鞘構造である請求項１
記載のふとん用詰綿材料。3. The latent crimped fiber has a laminated structure of two kinds of polyester fibers or an eccentric core-sheath structure.
Futon material for the futon described.
Ｄ）≧２０％であり、繊維断面が中空状である請求項１
記載のふとん用詰綿材料。4. The highly shrinkable fiber has a dry heat shrinkage (SH
D) ≧ 20% and the fiber cross section is hollow.
Futon material for the futon described.
割合が重量比で３：７〜７：３であり、かつ全構成繊維
に占める潜在捲縮繊維及び／又は高収縮性繊維と顕在化
した立体捲縮中空繊維との比率が少なくとも２０重量％
以上である請求項１又は２又は３又は４記載のふとん用
詰綿材料。5. The mixing ratio of the natural fiber and the polyester fiber is 3: 7 to 7: 3 by weight, and the latent crimped fiber and / or the highly shrinkable fiber accounted for in all the constituent fibers. At least 20% by weight with three-dimensional crimped hollow fibers
The stuffed cotton material for futon according to claim 1 or 2 or 3 or 4 which is the above.