JPH06263509A - Packed mortar - Google Patents
Packed mortarInfo
- Publication number
- JPH06263509A JPH06263509A JP7610293A JP7610293A JPH06263509A JP H06263509 A JPH06263509 A JP H06263509A JP 7610293 A JP7610293 A JP 7610293A JP 7610293 A JP7610293 A JP 7610293A JP H06263509 A JPH06263509 A JP H06263509A
- Authority
- JP
- Japan
- Prior art keywords
- mortar
- weight
- parts
- pts
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】この発明は、壁下地用モルタル又
は目地用モルタルを目的とした包装モルタルに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a packaging mortar intended for wall mortar or joint mortar.
【0002】[0002]
【従来の技術】従来瓦下地のモルタルとして遅延剤を含
む包装セメントモルタルが知られていた(特願昭62−
312585号)。2. Description of the Related Art Conventionally, packaging cement mortar containing a retarder has been known as a mortar for roof tiles (Japanese Patent Application No. 62-
312585).
【0003】[0003]
【発明により解決すべき課題】前記従来の包装セメント
モルタルは炭酸カルシウムを混入してないので、壁下地
用その他のモルタルとしては粘度および強度上不十分で
あった。Since the conventional packaging cement mortar described above does not contain calcium carbonate, it is insufficient in viscosity and strength as other mortar for wall foundation.
【0004】また通常の壁下地用又は目地用モルタルは
現場で必要材料を混合し、水を入れて練り上げているの
で、過大に作ると使い終るまでに硬化が始る問題点があ
り、過小に作ると、混練時間が塗着の作業時間に比し多
くなって、効率低下のおそれがあった。Ordinary wall base or joint mortar mixes the necessary materials on site and kneads with water, so if it is made too large, there is the problem that hardening will start before the end of use, and it will be too small. When it was made, the kneading time was longer than the coating work time, and there was a risk of a drop in efficiency.
【0005】[0005]
【課題を解決するための手段】然るにこの発明は、包装
モルタルとしたので、必要量宛袋を開けばよく、現場混
練作業を皆無とし、前記従来の問題点を解決したのであ
る。However, since the present invention uses the packaging mortar, it is only necessary to open the bag for the required amount, eliminating the on-site kneading work, and solving the above-mentioned conventional problems.
【0006】即ちこの発明は石灰1〜6重量部、炭化カ
ルシウム1〜15重量部、砂35〜45重量部、セメン
ト0.1〜0.5重量部、硬化遅延剤0.1〜0.3重
量部および適量の水を加えて混練し、これを袋詰めした
ことを特徴とした包装モルタルである。また他の発明は
石灰5重量部、炭化カルシウム10重量部、砂40重量
部、セメント0.3重量部、糖蜜0.2重量部、つなぎ
材0.08重量部および水3.5重量部を混練し、これ
を包装したことを特徴とする包装モルタルである。前記
における硬化遅延剤としては、例えば糖蜜を使用する
が、一般に空気に触れることによって硬化遅延の効果を
失う薬剤(例えばポリオール複合体を含むもの)ならば
使用することができる。That is, the present invention comprises 1 to 6 parts by weight of lime, 1 to 15 parts by weight of calcium carbide, 35 to 45 parts by weight of sand, 0.1 to 0.5 parts by weight of cement, and a retarder of 0.1 to 0.3. A packaging mortar characterized by adding parts by weight and an appropriate amount of water, kneading, and bagging the mixture. In another invention, 5 parts by weight of lime, 10 parts by weight of calcium carbide, 40 parts by weight of sand, 0.3 part by weight of cement, 0.2 part by weight of molasses, 0.08 part by weight of binder and 3.5 parts by weight of water are added. A packaging mortar characterized by being kneaded and packaged. As the setting retarder in the above, for example, molasses is used, but in general, any agent that loses the setting retarding effect by contact with air (for example, one containing a polyol complex) can be used.
【0007】前記におけるモルタルには、つなぎ材(ツ
タ、繊維など)を入れる場合と、入れない場合とがあ
る。The mortar described above may or may not contain a binder (such as ivy or fiber).
【0008】この発明は、必要とする材料に所定量の硬
化遅延剤を混入し、水を加えて混練した後、合成樹脂袋
(通気性のない合成樹脂フィルム製)に密封している。According to the present invention, a predetermined amount of a curing retarder is mixed in a required material, water is added and the mixture is kneaded, and then sealed in a synthetic resin bag (made of a non-breathable synthetic resin film).
【0009】この発明のモルタルは、ラスボードなどに
塗着するモルタル、目地モルタルその他一般建築に用い
るセメントモルタルの代りに使用することができる。The mortar of the present invention can be used in place of mortar applied to a lath board or the like, joint mortar and cement mortar used for general construction.
【0010】[0010]
【作用】この発明によれば、石灰、炭化カルシウムなど
よりなるモルタルに硬化遅延剤を入れて密封したので、
必要な際に必要な量のみを開封して使用し得ると共に、
粘着性と強度の優れたモルタルを提供することができ
る。According to the present invention, since the hardening retarder is put in the mortar composed of lime, calcium carbide, etc. and sealed,
You can open and use only the necessary amount when needed,
It is possible to provide a mortar having excellent adhesiveness and strength.
【0011】[0011]
【実施例】石灰6kg、炭化カルシウム10kg、砂40k
g、セメント0.3kg、糖蜜200ccおよびつなぎ材
0.05kgに水3.0リットルを入れて均一に混練し、
60kgの混練物を得た。これを厚手(厚さ0.2mm)の
塩化ビニール袋に20kg宛包装して製品とした。Example: 6 kg of lime, 10 kg of calcium carbide, 40 k of sand
g, 0.3 kg of cement, 200 cc of molasses, and 0.05 kg of binder, add 3.0 liters of water and knead uniformly,
60 kg of kneaded material was obtained. 20 kg of this was packed in a thick (0.2 mm thick) vinyl chloride bag to give a product.
【0012】前記包装モルタルは、180日経過後も混
練直後と同一の性能が認められた。また使用残のモルタ
ルは密封保存することにより24時間経過後の使用に耐
えることが認められた。更に塗着後の硬化速度は、硬化
遅延剤の入らないモルタルと大差はない。The above-mentioned packaging mortar was found to have the same performance as that immediately after kneading even after 180 days had passed. Further, it was confirmed that the mortar remaining after use could be used after 24 hours by keeping it sealed. Further, the curing speed after coating is not much different from that of the mortar containing no curing retardant.
【0013】従来壁下地として、石灰、砂、少量のセメ
ント及びつなぎ材の混合物が現場で配合混練され、使用
されているが、現場混練のモルタルより均一混合できる
のみならず、強度および粘度を安定させることができ
る。Conventionally, a mixture of lime, sand, a small amount of cement and a binder is mixed and kneaded on-site as a wall base, and it is used, but not only it can be mixed more uniformly than on-site kneading mortar, but also the strength and viscosity are stable. Can be made.
【0014】[0014]
【発明の効果】この発明によれば、従来知られている壁
下地用、目地などのモルタルに炭化カルシウムを添加す
ると共に、硬化遅延剤を添加しこれを密封袋により包装
したので、壁下地モルタル等の必要時に、包装を開き必
要量だけ取出して使用し、残部を再び密封すれば、後日
使用することができる効果がある。According to the present invention, since calcium carbide is added to a conventionally known mortar for wall foundations, joints, etc., a hardening retarder is added and the mortar is packaged in a sealed bag. When necessary, if the package is opened and only the required amount is taken out and used, and the rest is sealed again, there is an effect that it can be used at a later date.
【0015】また炭化カルシウムを添加したので、モル
タルの粘性を増加すると共に強度を増強する効果があ
る。Since calcium carbide is added, it has the effects of increasing the viscosity of the mortar and enhancing its strength.
【0016】この発明のモルタルは従来使用のモルタル
に比し強度が大きい(図1参照)。The mortar of the present invention has a higher strength than the mortar used conventionally (see FIG. 1).
【図1】この発明のモルタルと従来使用のモルタルとの
強度−日数グラフ。FIG. 1 is a graph of strength-days of a mortar of the present invention and a mortar of conventional use.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 FI 技術表示箇所 C04B 14:32 2102−4G 24:10) 2102−4G ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 5 Identification code Office reference number FI technical display location C04B 14:32 2102-4G 24:10) 2102-4G
Claims (3)
15重量部、砂35〜45重量部、セメント0.1〜
0.5重量部、硬化遅延剤0.1〜0.3重量部および
適量の水を加えて混練し、これを袋詰めしたことを特徴
とした包装モルタル。1. 1-6 parts by weight of lime, 1-calcium carbide
15 parts by weight, sand 35-45 parts by weight, cement 0.1-
A packaging mortar characterized by adding 0.5 parts by weight, 0.1 to 0.3 parts by weight of a setting retarder and an appropriate amount of water, kneading, and bagging this.
包装モルタル。2. The packaging mortar according to claim 1, wherein the setting retarder is molasses.
部、砂40重量部、セメント0.3重量部、糖蜜0.2
重量部、つなぎ材0.08重量部および水3.5重量部
を混練し、これを包装したことを特徴とする包装モルタ
ル。3. Lime 5 parts by weight, calcium carbide 10 parts by weight, sand 40 parts by weight, cement 0.3 parts by weight, molasses 0.2.
A packaging mortar characterized by kneading parts by weight, 0.08 parts by weight of a binder and 3.5 parts by weight of water, and packaging the mixture.