JPH06122868A - Production of easily washable solid buff polishing agent - Google Patents
Production of easily washable solid buff polishing agentInfo
- Publication number
- JPH06122868A JPH06122868A JP4257116A JP25711692A JPH06122868A JP H06122868 A JPH06122868 A JP H06122868A JP 4257116 A JP4257116 A JP 4257116A JP 25711692 A JP25711692 A JP 25711692A JP H06122868 A JPH06122868 A JP H06122868A
- Authority
- JP
- Japan
- Prior art keywords
- polishing
- buffing
- binder
- powder
- polishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】金属加工においてバフ研磨を行う
場合に用いる研磨剤は青棒、白棒などと称される固形物
を用いるが、このものについて研磨後の製品の洗浄性の
改良に関する物である。[Industrial application] Abrasives used for buffing in metal processing are solid substances called blue rods and white rods, which are related to improving the cleanability of the product after polishing. Is.
【0002】[0002]
【従来の技術】従来の固形研磨剤は研磨粉とパラフィン
類、脂肪酸類などの油脂類をもちいていた、しかしこの
物は使用後に金属表面にバフカスと称して付着したもの
を洗浄するのに困難な場合が多かった。洗浄方法として
は界面活性剤を溶かした水溶液を高温で使用したり、有
害な有機溶剤などで洗浄しているが、非能率的である。2. Description of the Related Art Conventional solid abrasives use abrasive powder and oils and fats such as paraffins and fatty acids, but this product is difficult to clean after it is attached to a metal surface called buff residue. There were many cases. As a cleaning method, an aqueous solution in which a surfactant is dissolved is used at a high temperature or a harmful organic solvent is used for cleaning, but this is inefficient.
【0003】[0003]
【発明が解決しようとする課題】この発明は従来の洗浄
困難なバフカスを生ずる研磨剤を改良し洗浄容易なバフ
カスを生ずる固形研磨剤を得るためのものである。SUMMARY OF THE INVENTION The present invention is to improve a conventional abrasive that produces buff residue that is difficult to clean and to obtain a solid abrasive that produces buff residue that is easy to clean.
【0004】[0004]
【課題を解決する手段】従来のものは研磨剤の粘結剤と
して、水に不溶解性の油脂類を用いていたが、本発明は
水溶性で物理的性質は従来のものに類似し、安全衛生及
び公害の面でも問題のないものを発見することであっ
た。種々のものを検討した結果、界面活性剤及び其の中
間体の中から水溶性で融点30℃から160℃までのも
のを選んで使用すれば課題が解決される事を発見するに
至った。In the prior art, fats and oils insoluble in water were used as a binder for abrasives, but the present invention is water-soluble and its physical properties are similar to those of the conventional ones. It was to find something that had no problems in terms of health and safety and pollution. As a result of examining various substances, it has been found that the problem can be solved by selecting and using a water-soluble surfactant and its intermediate having a melting point of 30 ° C to 160 ° C.
【0005】[0005]
【作用】このような粘結剤を使用して製造した固形研磨
剤は研磨時の使用感は従来のものと変わらずバフカス洗
浄は常温の水に浸すだけ、ないしは振動を与えるだけで
充分な洗浄が出来る。[Function] A solid abrasive produced using such a binder has a feeling of use during polishing which is the same as that of the conventional one, and buffing residue can be sufficiently washed by simply immersing it in water at room temperature or by applying vibration. Can be done.
【0006】[0006]
(1)ステンレス製ビーカーに研磨用酸化クローム粉8
00グラム、ポリエチレングリコール200グラムを入
れ撹拌しながら加熱すると全体がペースト状態となる、
これをアルミニウムで作った容器に流し込んで冷却した
後取り出すと固形研磨剤が得られた。これを使用してス
テンレス材の研磨を行い、その後洗浄を行ったが、研磨
具合は従来品と変わらず、洗浄性は常温水で簡単に行え
た。 (2)ステンレス製ビーカーに研磨用酸化アルミニウム
粉700グラム、ポリオキシエチレンポリオキシプロピ
レングリコールエーテル300グラムをいれ撹拌しなが
ら加熱するとぜんたいがペースト状態となる、これをア
ルミニウムで作った容器に流し込んで冷却した後取り出
したものについて試験を行った。研磨具合は従来品と変
わらず、洗浄性は常温水で簡単に行えた。 (3)ステンレス製ビーカーに研磨用酸化クローム粉8
00グラム、ポリオキシエチレン脂肪酸エステル100
グラム、ポリエチレングリコール100グラムをいれ撹
拌しながら加熱すると全体がペースト状態となる、これ
をアルミ製の容器に流し込んで冷却した後取り出した物
について試験を行った。研磨具合は従来と変わらず、洗
浄性は常温水で簡単に行えた。 (4)ステンレス製ビーカーに研磨用酸化アルミニウム
粉700グラム、ポリオキシエチレンアルキルエーテル
りん酸塩300グラムをいれ撹拌しながら加熱を行うと
全体がペースト状態となる、これをアルミ製容器に流し
込み、冷却した後取り出し、試験を行った。研磨具合は
従来と変わらず、洗浄性は常温水で簡単に行えた。 (5)ステンレス製ビーカーに研磨用酸化クローム粉8
00グラム、ポリオキシエチレンアルキルフエノールエ
ーテル200グラムを入れ、撹拌しながら加熱を行うと
全体がペースト状態となる、これをアルミ製容器に流し
込み、冷却した後取り出し、試験を行った。研磨具合は
従来と変わらず、洗浄性は常温水で簡単に行えた。 (6)ステンレス製ビーカーに研磨用酸化アルミニウム
粉700グラム、ポリオキシエチレンポリオキシプロピ
レンブロックポリマー300グラムを入れ、撹拌しなが
ら加熱を行うと全体がペースト状態となる、これをアル
ミ製容器に流し込み、冷却した後取り出し、試験を行っ
た。研磨具合は従来と変わらず、洗浄性は常温水で簡単
に行えた。(1) Oxidized chrome powder 8 in a stainless steel beaker
Add 00g and polyethylene glycol 200g and heat it with stirring to make the whole paste.
This was poured into a container made of aluminum, cooled, and taken out to obtain a solid abrasive. Using this, the stainless steel material was polished and then washed, but the polishing condition was the same as that of the conventional product, and the cleanability was easily performed with normal temperature water. (2) Add 700 g of aluminum oxide powder for polishing and 300 g of polyoxyethylene polyoxypropylene glycol ether to a beaker made of stainless steel, and heat it with stirring to turn it into a paste. Cool it by pouring it into a container made of aluminum. After that, the test was conducted on the one taken out. The polishing condition was the same as the conventional product, and the cleanability was easily performed with normal temperature water. (3) Oxide chromium powder 8 for polishing in a stainless steel beaker
00 grams, polyoxyethylene fatty acid ester 100
Grams and 100 grams of polyethylene glycol were put in and heated with stirring to make a whole paste state. This was poured into an aluminum container, cooled, and then taken out and tested. The polishing condition was the same as before, and the cleanability was easily achieved with room temperature water. (4) Put 700 g of aluminum oxide powder for polishing and 300 g of polyoxyethylene alkyl ether phosphate in a stainless steel beaker and heat with stirring to make the whole paste state. Pour this into an aluminum container and cool. After that, it was taken out and tested. The polishing condition was the same as before, and the cleanability was easily achieved with room temperature water. (5) Oxidized chrome powder 8 for polishing in a stainless steel beaker
00 grams and 200 grams of polyoxyethylene alkylphenol ether were added, and the whole was in a paste state when heated with stirring. This was poured into an aluminum container, cooled, taken out, and tested. The polishing condition was the same as before, and the cleanability was easily achieved with room temperature water. (6) Put 700 g of aluminum oxide powder for polishing and 300 g of polyoxyethylene polyoxypropylene block polymer in a beaker made of stainless steel, and heat while stirring to make the whole paste state. Pour this into an aluminum container, After cooling, it was taken out and tested. The polishing condition was the same as before, and the cleanability was easily achieved with room temperature water.
【0007】[0007]
【発明の効果】本発明によれば今まで固形研磨剤を使用
するバフ研磨において難点とされていた研磨後のバフカ
ス洗浄が安全、衛生的、公害性が低い、作業が能率的で
ある等の点で優れている。EFFECTS OF THE INVENTION According to the present invention, cleaning after buffing, which has been a problem in buffing using solid abrasives, is safe, hygienic, low in pollution, and efficient in work. Excellent in terms.
Claims (1)
ールの中より水溶性で融点30℃より160℃までのも
のを研磨粉と練り合わせて固形の研磨剤を製造する。What is claimed is: 1. A solid abrasive is produced by kneading a water-soluble surfactant having a melting point of 30 ° C. to 160 ° C. with a polishing powder.