CN102990536B - Knife sharpening strop - Google Patents
Knife sharpening strop Download PDFInfo
- Publication number
- CN102990536B CN102990536B CN201210573026.6A CN201210573026A CN102990536B CN 102990536 B CN102990536 B CN 102990536B CN 201210573026 A CN201210573026 A CN 201210573026A CN 102990536 B CN102990536 B CN 102990536B
- Authority
- CN
- China
- Prior art keywords
- leather
- strop
- paraffin
- knife sharpening
- green
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a knife sharpening strop and a production method thereof and belongs to the technical field of daily supplies. The knife sharpening strop comprises a leather cushion coated with hardening agents, wherein the lather cushion is further coated with knife sharpening materials to form a knife sharpening layer. The knife sharpening materials are formed by mixing paraffins, diamond powder and chromium oxide green. The knife sharpening materials of the knife sharpening materials strop are coated on the back surface of processed leather and can be coated for many times, and accordingly reutilization of the knife sharpening strop is achieved. Compared with the traditional knife sharpening stone, the knife sharpening strop is fast and convenient, the blade can be sharpened in short time, and work efficiency can be effectively improved. The knife sharpening strop is environment-friendly, sanitary, convenient to carry, strong in practicality and suitable for being comprehensively popularized and used.
Description
Technical field
The present invention relates to a kind of sharpening instrument, refer to a kind of leather strop especially.
Background technology
The knife that people use, after use is of a specified duration, all can rust, cannot be sharp as when just buying.So blade can rub back and forth by people on whetstone, make blade become sharp, use more laborsaving.Common whetstone is the stone of one piece of cuboid, carry extremely inconvenient, keep the balance of cutter during sharpening owing to pinning knife edge with hand, therefore easily hurt finger, and need watering or lubricating oil to its lubrication and cooling when sharpening, easily pollute; The density size of simultaneously traditional whetstone surface particles is uneven, and needs of whetting a knife expend larger strength.
Summary of the invention
In view of this, the present invention proposes a kind of leather strop, by leather backside coating sharpening material as sharpening layer, solve whetstone of the prior art and carry inconvenience, and use problem that is dangerous and that easily pollute.
Technical scheme of the present invention is achieved in that a kind of leather strop, it is characterized in that: comprise the leather bed course being coated with curing agent, and described leather bed course is also coated with sharpening material to form sharpening layer; Described sharpening material engraves green mixing by paraffin, bortz powder and oxidation.
In described sharpening material, paraffin is 32.5% ~ 37.5%, and bortz powder content is 57.5% ~ 62.5%, and the green content of oxidation inscription is 2.5% ~ 7.5%.
In described sharpening material, paraffin is 35%, and bortz powder is 60%, and oxidation inscription is green is 5%.
The fibre fluff thickness of described leather bed course is 1 ~ 1.5mm.
Described leather is natural leather or synthetic leather.
Described curing agent is polyurethane resin.
The manufacture method of described leather strop, is characterized in that comprising the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 32.5% ~ 37.5%, bortz powder 57.5% ~ 62.5%, the ratio mixing of oxidation inscription green 2.5% ~ 7.5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, described leather strop is made in the face being brushed with curing agent that the mixture solid of the rear formation of cooling is evenly coated in the leather in step (2).
Curing agent described in above-mentioned steps (2) is polyurethane resin.
In above-mentioned steps (3), paraffin is 35%, and bortz powder is 60%, and oxidation inscription is green is 5%.
Compared with prior art, the beneficial effect that leather strop of the present invention has is:
1) the present invention's leather replaces traditional whetstone, portably uses not only convenient but also quick, improves operating efficiency.
2) paraffin contained in leather strop of the present invention instead of in traditional whetstone use procedure needs watering or lubricating oil and prevent from bringing pollution.
3) bortz powder that contains of leather strop of the present invention and silica flour uniform particles tiny, light and respond well during sharpening, knife edge profit can be made at short notice.
4) the sharpening material solid mixture made can be convenient for carrying, and the sharpening material layer of leather strop can be smeared supplementary by it, can realize the recycling of leather strop.
Detailed description of the invention
Embodiment 1
A kind of leather strop of the present embodiment, comprises the leather bed course being coated with curing agent, and leather bed course is also coated with sharpening material to form sharpening layer; Sharpening material engraves green mixing by paraffin, bortz powder and oxidation.
In sharpening material, paraffin is 32.5%, and bortz powder is 60%, and oxidation inscription is green is 7.5%.
The fibre fluff thickness of leather bed course is 1 ~ 1.5mm.
Leather is natural leather or synthetic leather.
Curing agent is polyurethane resin.
The manufacture method of leather strop, comprises the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 32.5%, bortz powder 60%, the ratio mixing of oxidation inscription green 7.5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, described leather strop is made in the face being brushed with curing agent that the mixture solid of the rear formation of cooling is evenly coated in the leather in step (2).
Curing agent described in step (2) is polyurethane resin.
The using method of leather strop of the present invention is:
To blade bulk processing on rubble face, after the dirt above cleaning blade, blade miter angle is placed on strip leather strop, drags three to four times from front to back, then blade reverse side is done the action of above-mentioned repetition, can make the blade sharp.
Embodiment 2
A kind of leather strop of the present embodiment, comprises the leather bed course being coated with curing agent, and leather bed course is also coated with sharpening material to form sharpening layer; Sharpening material engraves green mixing by paraffin, bortz powder and oxidation.
In sharpening material, paraffin is 37.5%, and bortz powder is 60%, and oxidation inscription is green is 2.5%.
The fibre fluff thickness of leather bed course is 1 ~ 1.5mm.
Leather is natural leather or synthetic leather.
Curing agent is polyurethane resin.
The manufacture method of leather strop, comprises the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 37.5%, bortz powder 60%, the ratio mixing of oxidation inscription green 2.5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, described leather strop is made in the face being brushed with curing agent that the mixture solid of the rear formation of cooling is evenly coated in the leather in step (2).
Curing agent described in step (2) is polyurethane resin.
The using method of leather strop of the present invention is:
To blade bulk processing on rubble face, after the dirt above cleaning blade, blade miter angle is placed on strip leather strop, drags three to four times from front to back, then blade reverse side is done the action of above-mentioned repetition, can make the blade sharp.
Embodiment 3
A kind of leather strop of the present embodiment, comprises the leather bed course being coated with curing agent, and leather bed course is also coated with sharpening material to form sharpening layer; Sharpening material engraves green mixing by paraffin, bortz powder and oxidation.
In sharpening material, paraffin is 35. 5%, and bortz powder is 57.5%, and oxidation inscription is green is 7.5%
The fibre fluff thickness of leather bed course is 1 ~ 1.5mm.
Leather is natural leather or synthetic leather.
Curing agent is polyurethane resin.
The manufacture method of leather strop, comprises the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 35.5%, bortz powder 57.5%, the ratio mixing of oxidation inscription green 7.5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, described leather strop is made in the face being brushed with curing agent that the mixture solid of the rear formation of cooling is evenly coated in the leather in step (2).
Curing agent described in step (2) is polyurethane resin.
The using method of leather strop of the present invention is:
To blade bulk processing on rubble face, after the dirt above cleaning blade, blade miter angle is placed on strip leather strop, drags three to four times from front to back, then blade reverse side is done the action of above-mentioned repetition, can make the blade sharp.
Embodiment 4
A kind of leather strop of the present embodiment, comprises the leather bed course being coated with curing agent, and leather bed course is also coated with sharpening material to form sharpening layer; Sharpening material engraves green mixing by paraffin, bortz powder and oxidation.
In sharpening material, paraffin is 32.5%, and bortz powder is 62.5%, and oxidation inscription is green is 5%
The fibre fluff thickness of leather bed course is 1 ~ 1.5mm.
Leather is natural leather or synthetic leather.
Curing agent is polyurethane resin.
The manufacture method of leather strop, comprises the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 32.5%, bortz powder 62.5%, the ratio mixing of oxidation inscription green 5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, described leather strop is made in the face being brushed with curing agent that the mixture solid of the rear formation of cooling is evenly coated in the leather in step (2).
Curing agent described in step (2) is polyurethane resin.
The using method of leather strop of the present invention is:
To blade bulk processing on rubble face, after the dirt above cleaning blade, blade miter angle is placed on strip leather strop, drags three to four times from front to back, then blade reverse side is done the action of above-mentioned repetition, can make the blade sharp.
Embodiment 5
A kind of leather strop of the present embodiment, comprises the leather bed course being coated with curing agent, and leather bed course is also coated with sharpening material to form sharpening layer; Sharpening material engraves green mixing by paraffin, bortz powder and oxidation.
In sharpening material, paraffin is 35%, and bortz powder is 60%, and oxidation inscription is green is 5%
The fibre fluff thickness of leather bed course is 1 ~ 1.5mm.
Leather is natural leather or synthetic leather.
Curing agent is polyurethane resin.
The manufacture method of leather strop, comprises the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 35%, bortz powder 60%, the ratio mixing of oxidation inscription green 5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, described leather strop is made in the face being brushed with curing agent that the mixture solid of the rear formation of cooling is evenly coated in the leather in step (2).
Curing agent described in step (2) is polyurethane resin.
The using method of leather strop of the present invention is:
To blade bulk processing on rubble face, after the dirt above cleaning blade, blade miter angle is placed on strip leather strop, drags three to four times from front to back, then blade reverse side is done the action of above-mentioned repetition, can make the blade sharp.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (6)
1. a leather strop, is characterized in that: comprise the leather bed course being coated with curing agent, and described leather bed course is also coated with sharpening material to form sharpening layer; Described sharpening material engraves green mixing by paraffin, bortz powder and oxidation, and wherein, paraffin content is 32.5% ~ 37.5%, and bortz powder content is 57.5% ~ 62.5%, and the green content of oxidation inscription is 2.5% ~ 7.5%;
The manufacture method of described leather strop, comprises the following steps:
(1) getting fibre fluff thickness is that the leather of 1 ~ 1.5mm is placed in 100 ~ 120 DEG C, baking oven drying process, and the time is 5 ~ 7 minutes;
(2) rear stand-by by being again placed in baking oven drying process after the slurry brush curing agent of the cooled leather back side;
(3) by paraffin 32.5% ~ 37.5%, bortz powder 57.5% ~ 62.5%, the ratio mixing of oxidation inscription green 2.5% ~ 7.5% is inserted in baking oven and is heated, after paraffin dissolves, engrave green mixing with bortz powder and be oxidized, the mixture solid of the rear formation of cooling be evenly coated in the leather in step (2) is brushed with curing agent face on make described leather strop.
2. leather strop as claimed in claim 1, it is characterized in that: in described sharpening material, paraffin is 35%, bortz powder is 60%, and oxidation inscription is green is 5%.
3. leather strop as claimed in claim 2, is characterized in that: the fibre fluff thickness of described leather bed course is 1 ~ 1.5mm.
4. leather strop as claimed in claim 3, is characterized in that: described leather is natural leather or synthetic leather.
5. leather strop as claimed in claim 4, is characterized in that: described curing agent is polyurethane resin.
6. the preparation method of the leather strop as described in claim 1, is characterized in that: in above-mentioned steps (3), paraffin is 35%, and bortz powder is 60%, and oxidation inscription is green is 5%.