JPH0569490A - Inspecting method for defect of water-barrier sheet jointing section - Google Patents

Abstract

PURPOSE:To prevent the breaking of the joining section of a water-barrier sheet by accurately deciding the defect section of the joining section without interrupting a path formed to the joining section even when load is applied to the joining section of the water-barrier sheet and removing air sealed in the joining section after the completion of inspection. CONSTITUTION:A spatial path 4 is formed to a water-barrier sheet joining section 1 while interposing a cementing material 5 and an auxiliary material 6. A needle section 10 fitted to an air blower is inserted into the path 4, smoke is fed into the path 4 from the needle section 10, a position, where smoke flows out to the outside of the joining section 1, is observed. Inspection is completed, and smoke sealed into the path 4 is discharged.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for inspecting a defect of a water-impermeable sheet joint, and more specifically, forcibly sending smoke or gas to a passage previously made in the water-impermeable sheet joint, and the smoke or gas This is a method of inspecting a defect of a water-blocking sheet joint for observing a defective portion of the water-blocking sheet joint by observing how it flows out of the joint.

[0002]

2. Description of the Related Art Conventionally, proper inspection of a water-impermeable sheet joint is carried out by performing an adhesion test of the joint by a sampling test, or at the construction site, air is forced into the water-impermeable sheet joint at a non-adhered portion to maintain a constant level. After maintaining a constant pressure for a period of time, it was evaluated that the air did not flow out unless the pressure was reduced. However, this method is suitable for water-proof sheets made of synthetic resin such as vinyl chloride, but on sheets made of rubber, etc., it is in a defective state because the joints are in an adhesive state and the modulus is relatively low. Even if it is not done, the pressure may decrease, and there is a problem that the defective portion cannot be correctly determined.

As another method, there is a method in which an ultrasonic inspection machine is brought into contact with a joint portion to detect a defective portion. This method is suitable for a resin sheet, but a heterogeneous adhesive layer is interposed. There was a problem that it could not be applied in the case of a rubber sheet.

In order to improve this, the Applicant further inserts a needle portion equipped with a smoke blower into an unattached portion of the water-impermeable sheet joint portion made in advance, and sends the smoke through the through hole of the needle portion. After that, a method of observing the outflow location of the smoke to the outside of the sheet was proposed. (Disclosed in JP-A-63-182134)

[0005]

This method has some effects, but the joint is pressed down by the weight of the upper and lower water-blocking sheets and the worker's walking, and the space part of the unattached part disappears. There was a problem that the passage was blocked. That is, in the joining portion, the separated joining tapes may be deformed by pressure and adhere to each other, or the upper and lower water blocking sheets may come into contact with each other to make the passage extremely narrow.

Further, the smoke enclosed in the passage of the joint was permanently present therein, and the joint was in a swollen state.
For this reason, there is a problem that the joint portion, which is pressed down by the walking of the worker during the construction, is destroyed by the air pressure.
Further, when the joint is placed in a high temperature atmosphere, the air enclosed in the passage of the joint expands, the internal pressure increases, and the joint is easily broken.

The present invention solves the problems of the conventional inspection method as described above. Even if a load is applied to the joint portion of the water-impervious sheet, the joint can be accurately joined without blocking the passage provided in the joint portion. It is an object of the present invention to provide a method of inspecting a defect of a water-blocking sheet joint, which can judge a defective portion of the joint and prevent destruction of the joint by removing the air enclosed in the joint after the inspection.

[0008]

That is, as one of the features of the present invention, as one of them, a space-like passage is formed in a water-impervious sheet joining portion by interposing a joining material and an auxiliary material. After inserting the needle part of the blower into the passage and sending the smoke from the through hole of the needle part to the passage, the place where the smoke flows out of the joint is inspected, and the smoke enclosed in the passage after the inspection is completed. It is a method of inspecting the joint of the water-blocking sheet by discharging.

As another one, a space-like passage is formed by interposing a joining material and an auxiliary material in the water-impermeable sheet joint, and soap water is applied to the surface of the water-impermeable sheet joint. rear,
There is a method in which a needle portion equipped with a blower is inserted into this passage, gas is sealed from the needle portion, a spot where bubbles of soapy water are generated is observed, and after the inspection is completed, smoke enclosed in the passage is discharged. ..

[0010]

According to the inspection method of the present invention, even if a load is applied to the bonded portion of the water-impervious sheet, the auxiliary material intervenes together with the bonding material. Alternatively, the joining of the joining materials is prevented to maintain the space-like passage. For this reason, when a needle portion of a blower is inserted into the passage of the water-blocking sheet and a predetermined amount of smoke is sent into the space of the unattached portion, the smoke enters the passage of the sheet, and if there is a defective portion, Flows out from the defective part. This allows the smoke outflow portion to be inspected and the defective portion to be appropriately treated. Further, in this inspection method, it is not necessary to increase the air pressure because smoke is used, and thus the bonded portion of the rubber sheet is not destroyed. Of course, after applying soap water to the surface of the joint portion, gas can be sealed in this passage and the inspection can be performed by generating bubbles of water of soap water.

Further, by discharging the smoke sealed in the passage of the joint after the above-mentioned inspection, the internal pressure does not rise even if a load is applied to the joint, so that the joint is not broken.

[0012]

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Specific embodiments of the present invention will be described below with reference to the accompanying drawings. FIG. 1 is a cross-sectional view of the water-impermeable sheet joint portion, and FIG. 2 is a plan view thereof. In the joint portion 1 shown here, the upper water-impervious sheet 2 and the lower water-impervious sheet 3 are overlapped at their end portions, and the joint materials 5 and 5 are used to form a space-like passage 4 therebetween. Auxiliary members 6 are provided in the passage 4 at regular intervals in the width direction. The surface of the obtained joint portion 1 has a slight step portion 7.

The joining material 5 is not particularly limited. For example, in the case of a vulcanized rubber sheet, a natural vulcanization type rubber tape or a resin film is used, and in the case of a thermoplastic resin, a thermoplastic elastomer or the like. It is joined by heat fusion. In particular, in the present invention, it is effective when joining the water-impervious sheet on site, and therefore it is preferable to use a natural vulcanization type rubber tape. The thickness of this tape is 0.5 ~
Wide one with a width of 2.0 to 60 mm and 200 to 10 mm
Two narrow 60 mm types are used.

The auxiliary material 6 used here holds the space of the passage 4, and is, for example, a rope made of a fiber material, a masking tape, a linear rubber elastic body, a non-woven fabric, a mat, a breaker or the like. The auxiliary material 6 is installed on the side of the bonding material 5 having a narrow width, and smoke or gas is caused to flow to the side of the bonding material 5 having a wide width to facilitate the inspection of the defective portion of the bonding portion 1.

As the water-blocking sheets 2 and 3, for example, ethylene-propylene terpolymer (EPT), butyl rubber (IIR) or vulcanized rubber composed of a blend of EPT and IIR, vinyl chloride, vinyl acetate, etc. It is made of a plastic resin, a thermoplastic elastomer, or rubberized asphalt.

Therefore, in the method of the present invention, the needle portion 10 attached to the blower 9 for ejecting smoke is inserted into the passage 4 provided in the joint portion 1 and the blower 9 is operated to enclose the smoke from the needle portion 10. .. As shown in FIG. 3, the blower 9 has a cylindrical needle portion 10 having a through hole, a smoke producing tube box 11 and an air injecting device 12 such as a hand pump which are connected by a pipe 13, respectively. A pressure gauge 14 is provided between the tube boxes 11. White, yellow, etc. smoke generated in the smoke tube box 11 is caused by the wind pressure of the air injecting machine 12 to cause the needle portion 1 to move.
Eject from the tip of 0.

That is, according to the inspection method of the present invention, first, after the needle portion 10 of the blower 9 is inserted into the passage 4 provided in the longitudinal direction of the prefabricated water-impermeable sheet joint, the blower 9 is operated to smoke. Is forcibly sent to the space of the passage 4. When the space portion of the passage 4 reaches a predetermined pressure due to the sent-in smoke, the smoke advances to the unattached area between the sheets and in some cases flows out to the outside of the joint portion 1, whereby the location of the defective portion becomes clear. become.

The wind pressure feed caused by the air injector 12 is sufficient at about 0.1 kg / cm ² or less, beyond which the upper, possibly adhesive portion of the lower water-impervious sheet 2 is peeled off is there. Further, although the needle portion 10 is a tubular body, it has a sharp tip and is easy to insert, and is similar to the needle shape of a syringe, for example.

When the inspection is completed, the smoke enclosed in the passage 4 of the joint 1 is operated by the manual suction pump 15 provided in the blower 9 to be discharged from the needle 10 to the outside.
The suction pump 15 is connected to a pipe 16 which communicates the needle portion 10 from the smoke tube box 11. The valve 18 is located at the connecting portion 17 and switches the circuit of the suction pump 15 and the circuit of the air injecting device 12 from each other.

The passage 4 has a width of 5 cm or less and a length of about 1-2.
It is preferable to carry out in units of 0 m, and a weight can be placed at the end of this length to close the passage 4, or the passage 4 of a predetermined length can be completely sealed by the bonding material 5. When the width of the passage 4 exceeds 5 mm, the joint portion 1 is pressed down by the weight of the upper waterproof sheet 2 and the running of the builder, and the upper and lower waterproof sheets 2 and 3 come into close contact with each other to block the passage 4. To be done. Further, the auxiliary material 6 may be pulled out from the passage 4 after the inspection is completed.

Further, as another method, as shown in FIG. 5, soap water 20 is applied to the surface of the joint portion 1, and then the needle portion 10 is inserted into the passage 4 of the joint portion 1 as described above. Blower 9
Then, a gas such as air is sealed in and the location of bubbles in the soap water 20 is observed. In this case, it is not necessary to use smoke as gas.

Next, a specific example of the inspection method of the present invention will be described. 1.0 to 1.5 m in thickness at the joint part (width 150 mm) of the water-blocking sheet mainly composed of EPT having a thickness of 1.5 mm.
m, 100 mm wide natural vulcanization type adhesive tape and 30 mm wide natural vulcanization type adhesive tape are installed at a width of 30 mm, and diameter of polyester fiber is about 1.5 mm The rope was inserted close to the end face of the narrow adhesive tape to form a space-like passage. Then, the joined portion was pressure-bonded by a roller (rolling pressure 0.5 kg / cm) to obtain a joined portion having a length of 10 m. Both ends in the lengthwise direction of the passage were sealed with the above-mentioned adhesive tape, and at the same time, a defective portion for communicating the outside of the sheet with the passage was intentionally provided.

When the pressure-sensitive adhesive tape is naturally vulcanized to bond the water-impermeable sheets, about 10 parts from one end of the bonding part to the other end are bonded.
After being walked by the worker for m, a blower was brought in, the needle part of the blower was inserted into the passage of the water-blocking sheet, and the blower was operated to send the smoke generated in the smoke pipe into the passage from the needle part. When a predetermined amount of smoke was sent in, it was observed that the smoke in the passage moved and flowed out from the defective portion to the outside, and the defective portion was clarified.

Subsequently, after sealing the defective portion, the valve was switched to operate the suction pump to discharge the smoke enclosed in the passage of the joint portion. When the worker walked on the joint, the joint was not destroyed.

As another method, a joining portion using a masking tape having a width of 6 mm instead of the rope as an auxiliary material is prepared, and a worker is made to walk along the length direction of the joining portion. Apply soapy water to the step area of the joint,
Air was enclosed in the passage by a blower as described above. As a result, generation of bubbles was observed from the defective part, and it was revealed that the passage was not blocked even when a load was applied. Subsequently, after sealing the defective portion, the valve was switched and the suction pump was operated to discharge the air enclosed in the passage of the joint portion. Walking on the joint did not destroy the joint.

[0026]

As described above, according to the inspection method of the present invention, since the auxiliary material is interposed in the passage of the prefabricated water-impermeable sheet joint, the passage is opened even if a load is applied to the joint. Since there is no interruption, it is possible to accurately inspect the defective portion of the joint. Moreover, by discharging the air sealed in the passage of the joint after the above-mentioned inspection, it is possible to prevent the internal pressure of the joint from rising and prevent the joint from being broken.

[Brief description of drawings]

FIG. 1 is a cross-sectional view of a waterproof sheet joining portion.

FIG. 2 is a plan view of the water-impermeable sheet joint portion of FIG.

FIG. 3 is a perspective view of a blower used in the method of the present invention.

FIG. 4 is a cross-sectional view of a water-impermeable sheet joint portion showing the method of the present invention.

FIG. 5 is a cross-sectional view of a water-impermeable sheet joining portion showing another method of the present invention.

[Explanation of symbols]

 1 Joining part 2 Upper side water blocking sheet 3 Lower side water blocking sheet 4 Passage 5 Joining material 6 Auxiliary material 7 Stepped portion 9 Blower 10 Needle portion 11 Smoke tube box 12 Air injector 15 Suction pump

 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Etsuji Uenoyama 4-1-21, Hamazoe-dori, Nagata-ku, Kobe Mitsuboshi Belt Co., Ltd.

Claims (3)

[Claims] 1. A space-like passage is formed in a water-impervious sheet joint by interposing a joining material and an auxiliary material, and a needle portion provided in a blower is inserted into the passage, and smoke is emitted from the needle portion to the passage. A method for inspecting a defect of a water-impermeable sheet joint, comprising observing a portion where the smoke flows out of the joint after being sent, and discharging the smoke enclosed in the passage after the inspection is completed. 2. A space-like passage is formed in the water-impervious sheet joint by interposing a joint material and an auxiliary material, and soap water is applied to the surface of the joint portion, and the passage is equipped with a blower. A water-impervious sheet joint characterized by inserting a needle portion, enclosing gas from the needle portion into a passage, observing a location where bubbles of soapy water are generated, and discharging smoke enclosed in the passage after the inspection is completed. Defect inspection method. 3. A joint material having a large width and a joint material having a narrow width are arranged at an interval at a joint portion of a water-impervious sheet to form a space-like passage, and an auxiliary material is used on the joint material side having a narrow width. The method for inspecting a defect of a water-impermeable sheet joint portion according to claim 1 or 2, which is located close to the water-impermeable sheet.