JPH0564867A - Heat-sealable polypropylene-polybutylene laminated packing film having improved optical characteristics - Google Patents
Heat-sealable polypropylene-polybutylene laminated packing film having improved optical characteristicsInfo
- Publication number
- JPH0564867A JPH0564867A JP4036913A JP3691392A JPH0564867A JP H0564867 A JPH0564867 A JP H0564867A JP 4036913 A JP4036913 A JP 4036913A JP 3691392 A JP3691392 A JP 3691392A JP H0564867 A JPH0564867 A JP H0564867A
- Authority
- JP
- Japan
- Prior art keywords
- melt index
- propylene
- weight
- homopolymer
- butene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【０００２】[0002]
【発明の分野】本発明は、慣用の熱シールできる包装用
途に適した多層の熱可塑性の熱シールできるフィルムに
関する。FIELD OF THE INVENTION The present invention relates to a multilayer thermoplastic heat sealable film suitable for conventional heat sealable packaging applications.
【０００３】[0003]
【先行技術の簡単な説明】ポリプロピレンフィルムは、
その良好な防湿性、剛性、高強度及び良好な光学特性の
ために有用で広く受け入れられる包装フィルムとなっ
た。しかしながら、ある種の用途におけるポリプロピレ
ンフィルムの光学特性はしばしばきわどくそして改善が
長らく必要とされてきた。[Brief Description of Prior Art] Polypropylene film is
Its good moisture resistance, stiffness, high strength and good optical properties have made it a useful and widely accepted packaging film. However, the optical properties of polypropylene films in certain applications have often been severe and there has long been a need for improvement.
【０００４】米国特許第４，２３０，７６７号は、ポリ
プロピレンベース層並びに、種々の他のオレフィンとの
プロピレン／エチレンコポリマー及びポリブチレンコポ
リマーを含むコポリマーとの二成分ブレンドの表面層か
ら成る熱シール包装特性を有する積層された包装材料を
開示している。第’７６７号は、ポリプロピレンコアを
有する積層されたフィルム中の高メルトインデックスポ
リブチレンの使用を開示していない。US Pat. No. 4,230,767 discloses a heat seal package comprising a polypropylene base layer and a surface layer of a binary blend with copolymers including propylene / ethylene copolymers and polybutylene copolymers with various other olefins. Disclosed are laminated packaging materials having properties. No. '767 does not disclose the use of high melt index polybutylene in laminated films having a polypropylene core.
【０００５】米国特許第４，６８１，８０４号、第４，
６７７，０２５号、第４，７６９，４２１号、第４，３
４３，８５２号及び第４，７６６，１７８号は、ポリプ
ロピレン及びポリブチレンを含む積層されたフィルムを
開示しているが、しかしながら、これらのいずれもが、
本発明において特許請求されるような高メルトインデッ
クスポリブチレンの使用を開示していない。US Pat. Nos. 4,681,804, 4,
677,025, 4,769,421, 4,3
43,852 and 4,766,178 disclose laminated films comprising polypropylene and polybutylene, however, none of these
It does not disclose the use of high melt index polybutylene as claimed in the present invention.
【０００６】１９９０年５月３１日に出願されたＵ．
Ｓ．連番第５３１，２０６号は、ポリプロピレンランダ
ムコポリマー及び高メルトインデックスポリ−１−ブテ
ンのブレンドの層によってコートされているポリプロピ
レンコアを有する積層されたフィルムを開示している。
本出願人は、ポリプロピレンコア及びポリプロピレンラ
ンダムコポリマー外側層を有する積層品が、小量の高メ
ルトインデックスポリ−１−ブテンをコアまたは外側層
のどちらかに添加する時に、驚くべきより良い光学特性
を有するフィルムを与えることを見い出した。U.S. Pat.
S. Serial No. 531,206 discloses a laminated film having a polypropylene core coated with a layer of a blend of polypropylene random copolymer and high melt index poly-1-butene.
Applicants have discovered that laminates having a polypropylene core and a polypropylene random copolymer outer layer exhibit surprisingly better optical properties when small amounts of high melt index poly-1-butene are added to either the core or the outer layer. It was found to give a film with.
【０００７】[0007]
【発明の要約】本発明は、高い引裂強さ、良好な加工性
及び改善された光学特性の予期されなかった組み合わせ
を有する新規な多層フィルム組成物である。このフィル
ムは、プロピレンホモポリマー若しくはコポリマーまた
は、プロピレンポリマーとブテン−１ホモポリマー及び
コポリマーとのブレンドの“コア”または基体を含有し
て成る。このコアの片側または両側の上に、プロピレン
／エチレンランダムコポリマー組成物または、プロピレ
ン／エチレンランダムコポリマー及び低メルトインデッ
クスブチレンホモポリマー若しくは低メルトインデック
スブチレン／エチレンコポリマーを含有して成るブレン
ドによってコートするが、この際小量の高メルトインデ
ックスブチレンホモポリマーをコアまたは外側層組成物
とブレンドする。SUMMARY OF THE INVENTION The present invention is a novel multilayer film composition having an unexpected combination of high tear strength, good processability and improved optical properties. The film comprises a "core" or substrate of propylene homopolymer or copolymer or blend of propylene polymer and butene-1 homopolymer and copolymer. The core is coated on one or both sides with a propylene / ethylene random copolymer composition or a blend comprising a propylene / ethylene random copolymer and a low melt index butylene homopolymer or a low melt index butylene / ethylene copolymer, Here, a small amount of high melt index butylene homopolymer is blended with the core or outer layer composition.
【０００８】このフィルムは、実質的にエチレン／プロ
ピレンコポリマーブレンドである表皮層を実質的にポリ
プロピレンから成るコアまたはベース層に付与すること
ができる任意の慣用の技術によって製造することができ
る。このフィルムを製造するために、同時押出のまたは
押出コーティングの任意の既知の方法を使用することが
できる。The film can be made by any conventional technique which allows a skin layer, which is a substantially ethylene / propylene copolymer blend, to be applied to a core or base layer consisting essentially of polypropylene. Any known method of coextrusion or extrusion coating can be used to produce this film.
【０００９】フィルム生成組成物、またはその任意の成
分は、変更せずに使用することもできるし、または仕上
げフィルムのスリップ、粘着防止または静電特性の改善
のための添加剤によって改質することもできる。The film-forming composition, or any of its components, can be used unchanged or be modified with additives to improve the slip, detackification or electrostatic properties of the finished film. You can also
【００１０】[0010]
【好ましい実施態様の説明】本発明のコア層のために有
用な樹脂は、低メルトインデックスプロピレンホモポリ
マー及びコポリマーを含む。外側の表皮物質は、必要に
応じてブテン−１ホモポリマーまたはコポリマーと一緒
のプロピレン／エチレンランダムコポリマー及び小量の
高メルトインデックスポリ−１−ブテンホモポリマーの
ブレンドを含有して成ってよい。DESCRIPTION OF THE PREFERRED EMBODIMENTS Resins useful for the core layer of the present invention include low melt index propylene homopolymers and copolymers. The outer skin material may comprise a blend of propylene / ethylene random copolymer optionally with butene-1 homopolymer or copolymer and a small amount of high melt index poly-1-butene homopolymer.
【００１１】本発明において使用されるポリプロピレン
は、任意の結晶にすることができるポリプロピレンであ
る。前記ポリプロピレンは、結晶にすることができるポ
リプロピレンが生成される限り、使用される方法に関係
なくプロピレンを重合させることによって製造すること
ができる。好ましいポリプロピレンは、チーグラー／ナ
ッタまたはＭｇＣｌ2支持触媒重合方法によって製造さ
れた実質的にアイソタクチックなポリプロピレンであ
る。The polypropylene used in the present invention is a polypropylene which can be made into any crystal. The polypropylene can be produced by polymerizing propylene regardless of the method used, as long as a crystallizable polypropylene is produced. The preferred polypropylene is a substantially isotactic polypropylene produced by the Ziegler / Natta or MgCl 2 supported catalytic polymerization processes.
【００１２】コア層中で使用できるプロピレンポリマー
は、プロピレンホモポリマーまたはコポリマーのどちら
かでよい。プロピレンコポリマーを使用する場合には、
それらは、好ましくは１〜３０モル％のエチレン、ブテ
ン、または５〜８の炭素原子を有するα−オレフィンの
いずれかのコモノマー含量を有するランダムまたはブロ
ックコポリマーでよい。The propylene polymer that can be used in the core layer can be either a propylene homopolymer or a copolymer. When using a propylene copolymer,
They may be random or block copolymers, preferably having a comonomer content of either 1 to 30 mol% ethylene, butenes, or α-olefins with 5 to 8 carbon atoms.
【００１３】本発明におけるコア層のために有用なプロ
ピレンポリマーは、２３０℃でＡＳＴＭ Ｄ-１２３
８、条件Ｌによって測定して、好ましくは６０未満、さ
らに好ましくは約１〜１５のメルトインデックスを有す
る。特に適切なプロピレンは、２．６のメルトインデッ
クスを有しそしてＰＰ５Ａ０８としてテキサス、ヒュー
ストンのシェル ケミカル社から入手できる。The propylene polymer useful for the core layer in the present invention is ASTM D-123 at 230 ° C.
8, preferably having a melt index of less than 60, more preferably about 1-15, as measured by condition L. A particularly suitable propylene has a melt index of 2.6 and is available as PP5A08 from Shell Chemical Company of Houston, Texas.
【００１４】外側の表皮層は、プロピレン−エチレンラ
ンダムコポリマー、及び必要に応じて低メルトインデッ
クスブテン−１ポリマー及び高メルトインデックスブテ
ン−１ホモポリマーのブレンドを含有して成る。The outer skin layer comprises a propylene-ethylene random copolymer and optionally a blend of a low melt index butene-1 polymer and a high melt index butene-1 homopolymer.
【００１５】前記プロピレン−エチレンランダムコポリ
マーは、７重量％以下のエチレン含量を有しそして、１
３０℃以上または好ましくは１５０℃以上の融点及び２
３０℃でＡＳＴＭ Ｄ-１２３８、条件Ｌによって測定
して２〜２０ｇ／１０分、好ましくは４〜１５ｇ／１０
分、もっとも好ましくは６〜１０ｇ／１０分のメルトイ
ンデックスを有する。The propylene-ethylene random copolymer has an ethylene content of less than 7% by weight and
A melting point of 30 ° C or higher, or preferably 150 ° C or higher, and 2
2 to 20 g / 10 min, preferably 4 to 15 g / 10 as measured by ASTM D-1238, condition L at 30 ° C.
Min, most preferably 6-10 g / 10 min melt index.
【００１６】本明細書中で述べられる低メルトインデッ
クスブテン−１ポリマーは、少なくとも９５重量％、好
ましくは９７重量％、そしてもっとも好ましくは９８重
量％のアイソタクチック部分を含む実質的にポリ−１−
ブテンホモポリマーまたはコポリマーである。適切なポ
リ−１−ブテンは０．８９５〜０．９１９の密度を有す
る。The low melt index butene-1 polymers referred to herein are substantially poly-1 containing at least 95%, preferably 97%, and most preferably 98% by weight isotactic moieties. −
Butene homopolymer or copolymer. Suitable poly-1-butenes have a density of 0.895-0.919.
【００１７】適切なポリ−１−ブテンは、例えば、ドイ
ツ公開出願第１，５７０，３５３号中に開示されたよう
なブテン−１のチーグラー - ナッタ低圧重合に従って
得ることができる。Suitable poly-1-butenes can be obtained, for example, according to the Ziegler-Natta low pressure polymerization of butene-1 as disclosed in German published application 1,570,353.
【００１８】外側層において使用できるブテン−１ポリ
マーは、ブテン−１ホモポリマーまたはコポリマーのど
ちらかである。ブテン−１コポリマーを使用する場合に
は、ブテン以外のコモノマー含量は、０．１〜２０モル
％、好ましくは０．２〜１０モル％、またはさらに好ま
しくは０．３〜６モル％のエチレン、プロピレン、また
は５〜８の炭素原子を有するα−オレフィンのいずれか
でよい。The butene-1 polymers that can be used in the outer layer are either butene-1 homopolymers or copolymers. If a butene-1 copolymer is used, the comonomer content other than butene is 0.1 to 20 mol%, preferably 0.2 to 10 mol%, or more preferably 0.3 to 6 mol% ethylene, It may be either propylene or an α-olefin having 5 to 8 carbon atoms.
【００１９】適切なポリ−１−ブテンは、例えば、ブテ
ン−１のチーグラー - ナッタ低圧重合に従って、例え
ばドイツ公開出願第１，５７０，３５３号の方法によっ
て１０〜５０℃、好ましくは２０〜４０℃の温度でＴｉ
Ｃｌ3またはＴｉＣｌ3・ＡｌＣｌ3及びＡｌ（Ｃ2Ｈ5）2
Ｃｌの触媒によってブテン−１を重合させることによっ
て得ることができる。次に高メルトインデックスはペル
オキシドクラッキングによってさらにポリマーを処理す
ることによって得られる。ポリ−１−ブテンは、例え
ば、無水マレイン酸またはその他の官能基との反応によ
って表面活性を増加させることによって改質してよい。Suitable poly-1-butenes are, for example, according to the Ziegler-Natta low pressure polymerization of butene-1, eg 10-50 ° C., preferably 20-40 ° C., by the method of German published application 1,570,353. At the temperature of Ti
Cl 3 or TiCl 3 · AlCl 3 and Al (C 2 H 5 ) 2
It can be obtained by polymerizing butene-1 with a Cl catalyst. The high melt index is then obtained by further processing the polymer by peroxide cracking. Poly-1-butene may be modified, for example, by increasing its surface activity by reaction with maleic anhydride or other functional groups.
【００２０】本明細書中で述べられる高メルトインデッ
クスポリ−１−ブテンは、少なくとも約９０重量％、好
ましくは少なくとも約９５重量％、そしてさらに好まし
くは約９７重量％のアイソタクチック部分を含むブテン
−１ポリマーである。低分子量、例えば“デカリン”
（デカヒドロノフタレン）中の溶液粘度によって測定し
て約２８０，０００未満を有するアイソタクチックポリ
−１−ブテンが、本発明において有用である。使用でき
るポリ−１−ブテンは、０．８９５〜０．９２５、好ま
しくは０．９０５〜０．９２０、そして殊に０．９１０
〜０．９１５の密度を有する。使用できるポリ−１−ブ
テンは、１９０℃で、ＡＳＴＭＤ-１２３８条件Ｅによ
って測定して、２０〜１０００、さらに好ましくは３０
〜６５０、さらに好ましくは５０〜５００、そしてもっ
とも好ましくは１００〜３００ｇ／１０分の範囲のメル
トインデックスを有する。このポリブチレンの固有粘度
は、１３０℃で約０．０３〜約０．２０好ましくは約
０．０６〜約０．１１の範囲でよい。高メルトインデッ
クスポリブチレンのブルックフィールド溶融粘度は、２
００℃で約１０，０００〜約２００，０００センチポア
ズ、好ましくは２５，０００〜１５０，０００センチポ
アズ、そしてもっとも好ましくは４０，０００〜１０
０，０００センチポアズの範囲でよい。The high melt index poly-1-butenes referred to herein include butenes containing at least about 90% by weight, preferably at least about 95% by weight, and more preferably about 97% by weight isotactic moieties. -1 polymer. Low molecular weight, eg "decalin"
Isotactic poly-1-butenes having less than about 280,000 as measured by solution viscosity in (decahydronophthalene) are useful in the present invention. Poly-1-butenes which can be used are 0.895 to 0.925, preferably 0.905 to 0.920, and especially 0.910.
It has a density of ~ 0.915. The poly-1-butenes that can be used are from 20 to 1000, more preferably 30 as measured by ASTM D-1238 condition E at 190 ° C.
~ 650, more preferably 50-500, and most preferably 100-300 g / 10 min. The intrinsic viscosity of the polybutylene may range from about 0.03 to about 0.20 at 130 ° C, preferably about 0.06 to about 0.11. The Brookfield melt viscosity of high melt index polybutylene is 2
At 00 ° C., about 10,000 to about 200,000 centipoise, preferably 25,000 to 150,000 centipoise, and most preferably 40,000-10.
It may be in the range of 10,000 centipoise.
【００２１】本発明の積層組成物はまた、添加剤及び充
填剤、例えば離型剤、ＵＶ若しくは熱安定剤、スリップ
剤、粘着防止剤、成核剤、顔料、酸化防止剤、または防
炎剤を含んでもよい。The laminate compositions of the present invention also include additives and fillers such as mold release agents, UV or heat stabilizers, slip agents, antiblocking agents, nucleating agents, pigments, antioxidants, or flameproofing agents. May be included.
【００２２】これらの成分のブレンドは、数種の方法、
乾式タンブルブレンディング、マスターバッチ、または
溶融コンパウンディング技術の一つによって行うことが
できる。調合物の成分を合わせる方法は重要である。例
えば、多くの場合には、成分を合わせて効果的なブレン
ドにするための最低量のエネルギーを使用することが望
ましい。それ故、ブレンディングの好ましい方法は、粉
末の形で成分を乾式ブレンドすることである。Blends of these ingredients can be made in several ways,
It can be done by one of dry tumble blending, masterbatch, or melt compounding techniques. The manner in which the ingredients of the formulation are combined is important. For example, it is often desirable to use the lowest amount of energy to combine the components into an effective blend. Therefore, the preferred method of blending is to dry blend the ingredients in powder form.
【００２３】本発明のコートされた熱可塑性フィルム
は、多層のフィルムを製造するための任意の慣用の技
術、例えば、同時押出、予め押出されたフィルムの積
層、押出コーティング、エマルションコーティング等に
よって生成させることができる。好ましい方法は同時押
出であるが、本発明は製造の手段をいずれかの単一の技
術に限定するものではない。The coated thermoplastic film of the present invention is produced by any conventional technique for making multilayer films, such as coextrusion, laminating preextruded films, extrusion coating, emulsion coating and the like. be able to. Although the preferred method is coextrusion, the present invention does not limit the means of manufacture to any single technique.
【００２４】本明細書中で具体化された積層構造体の表
皮層は、全フィルム厚さの１ミルに対して通常は０．０
２ミル〜０．８ミルである。０．０５ミル〜０．６ミル
の表皮及び０．５ミル〜２．０ミルの全フィルム厚さが
一般的に好ましい。コーティングまたは表皮は、積層さ
れたフィルムの全厚さの３％〜３０％を構成してよい。The skin layer of the laminate structures embodied herein is typically 0.0 per mil of total film thickness.
2 mils to 0.8 mils. Skins of 0.05 mils to 0.6 mils and total film thicknesses of 0.5 mils to 2.0 mils are generally preferred. The coating or skin may make up 3% to 30% of the total thickness of the laminated film.
【００２５】[0025]
【実施例】以下の実施例は本発明を例示するが、それを
限定するとして考えてはなられない。The following examples illustrate the invention but should not be considered as limiting it.
【００２６】実施例 ポリプロピレンホモポリマーまたは、高メルトインデッ
クスポリ−１−ブテンとブレンドされたポリプロピレン
ホモポリマーのコア物質を、ポリプロピレンランダムコ
ポリマー単独（対照）または表１中に示されるその他の
成分とのブレンドを含有して成る、それの両側の上のコ
ーティングと共に同時押出することによってフィルムを
製造した。溶融したポリマーを平らな１０”のシートダ
イを通して慣用の押出機から同時押出し、溶融液流れを
ダイから押出されるのに先立ってアダプター中で合わせ
た。各々の表皮層は、フィルムの全厚さの約１／３を構
成していた。この樹脂を、表皮物質に関しては約２３０
℃そしてコア物質に関しては２２５℃そしてダイに関し
ては２３５℃で押出した。 EXAMPLE Polypropylene homopolymer or a core material of polypropylene homopolymer blended with high melt index poly-1-butene, blended with polypropylene random copolymer alone (control) or with the other ingredients shown in Table 1. A film was made by coextruding with coatings on both sides of the film. The melted polymer was coextruded from a conventional extruder through a flat 10 ″ sheet die and the melt stream was combined in an adapter prior to being extruded from the die. Each skin layer consisted of the total thickness of the film. Made up about 1/3 of this resin, about 230 for epidermal material
C. and 225.degree. C. for core material and 235.degree. C. for die.
【００２７】ダイのオリフィスを離れた後で、コートさ
れたシート（厚さが約１８ミル）を約１０℃（５０°
Ｆ）で冷却したロール上で巻いた。次にシートをトリム
しそしてコアの上に巻き取った。次に、シートを、一つ
の方向に６回そしてもう一つの方向に５回、二軸フィル
ム伸張機によって延伸した。After leaving the die orifice, the coated sheet (about 18 mils thick) is heated to about 10 ° C. (50 °).
It was wound on a roll cooled in F). The sheet was then trimmed and rolled onto the core. The sheet was then stretched in a biaxial film stretcher 6 times in one direction and 5 times in the other direction.
【００２８】この同じ基本的手順を使用して、以下の組
成を有するフィルムを製造した：Using this same basic procedure, a film having the following composition was produced:
【００２９】[0029]
【表１】 表１ フィルム構造体 ＃ 表皮 コア 表皮 1. PPR PP PPR 対照 2. PPR PP+3% DP0800 PPR 3. PPR+3% PB0800 PP PPR+3% DP0800 4. PPR+40% PB8340 PP PPR+40% PB8340 対照 5. PPR+40% PB8340 PP+3%DP0800 PPR+40% PB8340 6. PPR+40% PB8340+3%DP0800 PP PPR+40% PB8340+3%DP0800 実施例フィルムのために使用した種々の物質は以下の
通りであった：ＰＰＲは、ソルベイ（Ｓｏｌｖｅｙ）か
らＫＳ４０９として入手できる５重量％のエチレン含量
及び８．０のメルトインデックスを有するプロピレンラ
ンダムコポリマーである。 TABLE 1 Film structure # skin core epidermis 1. PPR PP PPR control 2. PPR PP + 3% DP0800 PPR 3. PPR + 3% PB0800 PP PPR + 3% DP0800 4. PPR + 40% PB8340 PP PPR + 40% PB8340 Control 5. PPR + 40% PB8340 PP + 3% DP0800 PPR + 40% PB8340 6. PPR + 40% PB8340 + 3% DP0800 PP PPR + 40% PB8340 + 3% DP0800 Used for example films The various materials were as follows: PPR is a propylene random copolymer with an ethylene content of 5% by weight and a melt index of 8.0, available as KS409 from Solvey.
【００３０】ＰＰは、Ｕ．Ｓ．スチール社からＦＦ０２
０Ｙとして入手できる、２３０℃で２．２ｇ／１０分の
メルトインデックス及び０．９０５の密度を有するプロ
ピレンホモポリマーである。PP is a U.S.P. S. FF02 from Steel
A propylene homopolymer having a melt index of 2.2 g / 10 min at 230 ° C. and a density of 0.905, available as OY.
【００３１】ＰＢ８３４０は、テキサス、ヒューストン
のシェル ケミカル社から入手できる、０．７５重量％
のエチレンコモノマー含量及び１９０℃で４．０ｇ／１
０分のメルトインデックス及び３２５，０００の分子量
を有するポリ−１−ブテンコポリマーである。PB8340 is 0.75% by weight, available from Shell Chemical Company, Houston, Texas.
Ethylene comonomer content of and 4.0 g / 1 at 190 ° C
It is a poly-1-butene copolymer having a melt index of 0 minutes and a molecular weight of 325,000.
【００３２】ＤＰ０８００は、テキサス、ヒューストン
のシェル ケミカル社から入手できる、１９０℃で２０
０ｇ／１０分のメルトインデックス及び１０８，０００
の分子量を有する高メルトインデックスブテン−１ホモ
ポリマーである。DP0800 is available at 20 ° C. at 190 ° C., available from Shell Chemical Company, Houston, Texas.
0 g / 10 min melt index and 108,000
It is a high melt index butene-1 homopolymer having a molecular weight of
【００３３】高メルトインデックスポリブチレン（ＤＰ
０８００）の典型的な物理的特性を表２中で以下に表示
する。High melt index polybutylene (DP
0800) typical physical properties are presented below in Table 2.
【００３４】[0034]
【表２】 表２ ＤＰ０８００ポリブチレンの典型的な物理的特性 ASTM 単位 ポリブチレン 試験方法 フートポンド法 (メートル法) DP0800 メ ルトインデックス 190℃で D1238“E" - g/10分 200 230℃で D1238“L" - g/10分 490 密度 D1505 1b/ft g/cm3 57.1(0.915) 降伏時の引張強さ D638 psi MPa 2000(13.8) 破断時の引張強さ D638 psi MPa 4200(29.0) 破断時の伸び D638 % % 350 弾性率 D638 psi MPa 35000(241) シヨア硬さ D2240 Dスケール Dスケール 55(55) 脆化温度 D746 °F ℃ 0°(-18°) 融点範囲 DSC °F ℃ 255-259° (124-126°)ビ カット軟化点 D1525 °F ℃ 241°(116°)77 °Fでの熱伝導率 C177 Btu/ft2/ Kcal/m2 1.25 hr/°F/in hr/℃/cm (16) 200℃での溶融粘度 ブルック センチポアズ - 3.9×104 フィールド 表３及び４は、６つのサンプルフィルムに関する光学的
特性を示す。表３は、６０°の角度で測定した光沢を含
む光学的特性を示す。表４は、同様にして製造したフィ
ルムの第二組の、４５°の角度で測定した光沢を含む光
学的特性を示す。小量の高メルトインデックスポリ−１
−ブテンを含む、表面層、またはコア層を有するフィル
ム、組成物２、３、５及び６は、表面が粘着性ではない
ので、非常に容易に加工できそして取り扱いの問題もな
かった。[Table 2] Table 2 Typical physical properties of DP0800 polybutylene ASTM unit Polybutylene Test method Foot pond method (Metric) DP0800 Melt index D1238 "E" at 190 ° C-g / 10 minutes 200 D 230 at 230 ° C D1238 "L"- g / 10 min 490 Density D1505 1b / ft g / cm 3 57.1 (0.915) Tensile strength at yield D638 psi MPa 2000 (13.8) Tensile strength at break D638 psi MPa 4200 (29.0) Elongation at break D638% % 350 Modulus D638 psi MPa 35000 (241) Shear hardness D2240 D scale D scale 55 (55) Embrittlement temperature D746 ° F ℃ 0 ° (-18 °) Melting point range DSC ° F ℃ 255-259 ° (124- 126 °) Vicat softening point D15 25 ° F ℃ 241 ° (116 °) Thermal conductivity at 77 ° C C177 Btu / ft 2 / Kcal / m 2 1.25 hr / ° F / in hr / ° C / cm (16) Melt Viscosity at 200 ° C. Brook Centipoise-3.9 × 10 4 fields Tables 3 and 4 show optical properties for six sample films. Table 3 shows the optical properties including gloss measured at an angle of 60 °. Table 4 shows the optical properties of a second set of similarly prepared films, including gloss measured at an angle of 45 °. Small amount of high melt index poly-1
Films with a surface layer or core layer, containing butenes, compositions 2, 3, 5 and 6 were very easy to process and had no handling problems because the surface was not tacky.
【００３５】[0035]
【表３】 表３ 光学的特性 厚さ 曇り度 光沢 フィルム組成物 ミクロン ％ (６０°で) 1. 対照 13 0.4 113.1 2. 27.5 0.2 127.1 3. 15.5 0.2 130.0 4. 対照 15.5 0.4 111.3 5. 24.5 0.3 136.5 6. 15.5 0.4 131.1 Table 3 Optical Properties Thickness Haze Haze Gloss Film Composition Micron % (at 60 °) 1. Control 13 0.4 113.1 2. 27.5 0.2 127.1 3. 15.5 0.2 130.0 4. Control 15.5 0.4 111.3 5. 24.5 0.3 136.5 6. 15.5 0.4 131.1
【００３６】[0036]
【表４】 表４ 光学的特性 厚さ 曇り度 光沢 フィルム組成物 ミクロン ％ (４５°で) 1. 対照 13 0.5 80.0 2. 27.5 0.39 81.0 3. 15.5 0.43 81.5 4. 対照 15.5 1.87 69.5 5. 24.5 0.55 77.0 6. 15.5 0.88 81.0 このデータから明らかであるように、本発明の積層さ
れたフィルム、即ちフィルム２、３、５及び６は、対照
フィルム１及び４よりも顕著に優れた光学的特性を有し
そして粘着性表面に伴う何らの問題も持たない。 Table 4 Optical Properties Thickness Haze Haze Gloss Film Composition Micron % (at 45 °) 1. Control 13 0.5 80.0 2. 27.5 0.39 81.0 3. 15.5 0.43 81.5 4. Control 15.5 1.87 69.5 5. 24.5 0.55 77.0 6. 15.5 0.88 81.0 As is evident from this data, the laminated films of the present invention, namely Films 2, 3, 5 and 6, have significantly better optical properties than Control Films 1 and 4. And does not have any problems with sticky surfaces.
【００３７】ポリマーブレンド及びフィルムを製造する
ことの上の説明におけるある種の変更は、本発明の範囲
から逸脱すること無く行うことができ、そしてこの説明
中に含まれるすべての事項は、例示的として解釈されそ
して限定的な意味では解釈されないことが意図されてい
る。Certain modifications in the above description of making polymer blends and films can be made without departing from the scope of the invention, and all matter contained in this description is exemplary. Is intended to be and is not to be construed in a limiting sense.
【００３８】本発明の主なる特徴及び態様は以下の通り
である。The main features and aspects of the present invention are as follows.
【００３９】１）（Ｉ）プロピレンホモポリマー及び、
プロピレンと１〜約３０重量％の２または４〜８の炭素
原子を有するα−オレフィンとのコポリマーを含有して
成るコア層、 （ＩＩ）該コアの少なくとも一つの側の上の、７重量％
以下のエチレン含量を有するプロピレン−エチレンラン
ダムコポリマーを含有して成る外側層 を含有して成り、そして該コアの少なくとも一つまたは
該外側層が、１９０℃で約２０〜約１０００ｇ／１０分
のメルトインデックスを有する、約０．２〜約１０重量
％の高メルトインデックスブテン−１ホモポリマーを含
む、多層の熱シールできる積層されたフィルム。1) (I) propylene homopolymer, and
A core layer comprising a copolymer of propylene and 1 to about 30% by weight of an α-olefin having 2 or 4 to 8 carbon atoms, (II) 7% by weight, on at least one side of the core
An outer layer comprising a propylene-ethylene random copolymer having the following ethylene content, and at least one of said cores or said outer layer has a melt at 190 ° C. of from about 20 to about 1000 g / 10 minutes. A multi-layer heat sealable laminated film comprising about 0.2 to about 10 wt% high melt index butene-1 homopolymer having an index.
【００４０】２）（Ｉ）プロピレンホモポリマー及び、
プロピレンと１〜約３０重量％の２または４〜８の炭素
原子を有するα−オレフィンとのコポリマーを含有して
成るコア層、 （ＩＩ）該コアの少なくとも一つの側の上の、 （ａ）４０〜８０重量％の、７重量％以下のエチレン含
量を有するプロピレン−エチレンランダムコポリマー （ｂ）２０〜６０重量％の、１９０℃で１．０〜１５ｇ
／１０分のメルトインデックスを有する低メルトインデ
ックスブテン−１ポリマー のブレンドを含有して成る外側層 を含有して成り、そして該コアの少なくとも一つまたは
該外側層が、１９０℃で約２０〜約１０００ｇ／１０分
のメルトインデックスを有する、約０．２〜約１０重量
％の高メルトインデックスブテン−１ホモポリマーを含
む、多層の熱シールできる積層されたフィルム。2) (I) propylene homopolymer and
A core layer comprising a copolymer of propylene and 1 to about 30% by weight of an α-olefin having 2 or 4 to 8 carbon atoms, (II) on at least one side of the core, (a) 40-80% by weight, propylene-ethylene random copolymer having an ethylene content of 7% by weight or less (b) 20-60% by weight, 1.0-15 g at 190 ° C
An outer layer comprising a blend of a low melt index butene-1 polymer having a melt index of / 10 min, and at least one of the cores or the outer layer comprises from about 20 to about 20 at 190 ° C. A multi-layer heat sealable laminated film comprising from about 0.2 to about 10% by weight of high melt index butene-1 homopolymer having a melt index of 1000 g / 10 minutes.
【００４１】３）該高メルトインデックスブチレンホモ
ポリマーが、１９０℃で３０〜６５０ｇ／１０分のメル
トインデックスを有する、上記１に記載のフィルム。3) The film as described in 1 above, wherein the high melt index butylene homopolymer has a melt index at 190 ° C. of 30 to 650 g / 10 minutes.
【００４２】４）該高メルトインデックスブチレンホモ
ポリマーが、１９０℃で５０〜３００ｇ／１０分のメル
トインデックスを有する、上記１に記載のフィルム。4) The film as described in 1 above, wherein the high melt index butylene homopolymer has a melt index at 190 ° C. of 50 to 300 g / 10 minutes.
【００４３】５）該高メルトインデックスブチレンホモ
ポリマーが、１９０℃で１００〜２００ｇ／１０分のメ
ルトインデックスを有する、上記１に記載のフィルム。5) The film as described in 1 above, wherein the high melt index butylene homopolymer has a melt index at 190 ° C. of 100 to 200 g / 10 minutes.
【００４４】６）該高メルトインデックスブチレンホモ
ポリマーが、２００℃で１０，０００〜約２００，００
０センチポアズの溶融粘度を有する、上記１に記載のフ
ィルム。6) The high melt index butylene homopolymer is 10,000 to about 200,000 at 200 ° C.
The film of claim 1 having a melt viscosity of 0 centipoise.
【００４５】７）該高メルトインデックスブチレンホモ
ポリマーが、２００℃で４０，０００〜１００，０００
センチポアズの溶融粘度を有する、上記１に記載のフィ
ルム。7) The high melt index butylene homopolymer is 40,000-100,000 at 200 ° C.
The film of claim 1 having a melt viscosity of centipoise.
【００４６】８）該表面層が、５０〜７０重量％の該プ
ロピレンエチレンランダムコポリマー、３０〜５０重量
％の該低メルトインデックスポリブチレン、及び０．５
〜約５．０重量％の該高メルトインデックスブチレンホ
モポリマーを含有して成る、上記１に記載のフィルム。8) The surface layer comprises 50-70% by weight of the propylene ethylene random copolymer, 30-50% by weight of the low melt index polybutylene, and 0.5.
The film of claim 1 comprising about 5.0 wt% of the high melt index butylene homopolymer.
【００４７】９）該表面層が、５５〜６５重量％の該プ
ロピレンエチレンランダムコポリマー、３５〜４５重量
％の該低メルトインデックスポリブチレンポリマー、及
び２．０〜約４．０重量％の該高メルトインデックスブ
チレンホモポリマーを含有して成る、上記７に記載のフ
ィルム。9) The surface layer comprises 55-65% by weight of the propylene ethylene random copolymer, 35-45% by weight of the low melt index polybutylene polymer, and 2.0 to about 4.0% by weight of the high layer. 8. The film according to 7 above, which comprises a melt index butylene homopolymer.
【００４８】１０）該外側層が約０．０２ミル〜約０．
６ミルの厚さであり、そして全フィルム厚さが０．５〜
２．０ミルである、上記１に記載の積層されたフィル
ム。10) The outer layer is about 0.02 mils to about 0.
6 mils thick and the total film thickness is 0.5 ~
The laminated film of 1 above, which is 2.0 mils.
【００４９】１１）フィルムが同時押出によって生成さ
れる、上記１に記載の積層されたフィルム。11) The laminated film as described in 1 above, wherein the film is produced by coextrusion.
【００５０】１２）（Ｉ）プロピレンホモポリマー及
び、プロピレンと１〜約３０重量％の２または４〜８の
炭素原子を有するα−オレフィンとのコポリマーを含有
して成るコア層、 （ＩＩ）該コアの少なくとも一つの側の上の、 （ａ）５５〜６５重量％の、７重量％以下のエチレン含
量及び２３０℃で６〜１０ｇ／１０分のメルトインデッ
クスを有するプロピレン−エチレンランダムコポリマー （ｂ）３５〜４５重量％の、０．３〜２０．０モル％の
エチレン含量及び１９０℃で１．０〜１５ｇ／１０分の
メルトインデックスを有する低メルトインデックスブテ
ン−１エチレンランダムコポリマー のブレンドを含有して成る外側層 を含有して成り、そして該コアの少なくとも一つまたは
該外側層が、１９０℃で１００〜約３００ｇ／１０分の
メルトインデックス及び２００℃で４０，０００〜１０
０，０００センチポアズの溶融粘度を有する、約２〜約
４重量％の高メルトインデックスブテン−１ホモポリマ
ーを含む、多層の熱シールできる積層されたフィルム。12) A core layer comprising (I) a propylene homopolymer and 1 to about 30% by weight of a copolymer of propylene and an α-olefin having 2 or 4 to 8 carbon atoms, (II) On at least one side of the core: (a) 55-65% by weight of a propylene-ethylene random copolymer having an ethylene content of 7% by weight or less and a melt index of 6-10 g / 10 min at 230 ° C. (b) 35 to 45% by weight of a blend of low melt index butene-1 ethylene random copolymer having an ethylene content of 0.3 to 20.0 mol% and a melt index at 190 ° C. of 1.0 to 15 g / 10 min. And at least one of the cores or the outer layer comprises 100 to about 300 g / 10 at 190 ° C. Minute melt index and 40,000-10 at 200 ° C
A multi-layer heat sealable laminated film comprising from about 2 to about 4 weight percent high melt index butene-1 homopolymer having a melt viscosity of 10,000 centipoise.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ２９Ｌ 7:00 4Ｆ 9:00 4Ｆ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Office reference number FI Technical display area B29L 7:00 4F 9:00 4F
Claims (4)
ロピレンと１〜約３０重量％の２または４〜８の炭素原
子を有するα−オレフィンとのコポリマーを含有して成
るコア層、 （ＩＩ）該コアの少なくとも一つの側の上の、７重量％
以下のエチレン含量を有するプロピレン−エチレンラン
ダムコポリマーを含有して成る外側層 を含有して成り、そして該コアの少なくとも一つまたは
該外側層が、１９０℃で約２０〜約１０００ｇ／１０分
のメルトインデックスを有する、約０．２〜約１０重量
％の高メルトインデックスブテン−１ホモポリマーを含
む、多層の熱シールできる積層されたフィルム。1. A core layer comprising (I) a propylene homopolymer and a copolymer of propylene and 1 to about 30% by weight of an α-olefin having 2 or 4 to 8 carbon atoms, (II) 7% by weight, on at least one side of the core
An outer layer comprising a propylene-ethylene random copolymer having the following ethylene content, and at least one of said cores or said outer layer has a melt at 190 ° C. of from about 20 to about 1000 g / 10 minutes. A multi-layer heat sealable laminated film comprising about 0.2 to about 10 wt% high melt index butene-1 homopolymer having an index.
ロピレンと１〜約３０重量％の２または４〜８の炭素原
子を有するα−オレフィンとのコポリマーを含有して成
るコア層、 （ＩＩ）該コアの少なくとも一つの側の上の、 （ａ）４０〜８０重量％の、７重量％以下のエチレン含
量を有するプロピレン−エチレンランダムコポリマー （ｂ）２０〜６０重量％の、１９０℃で１．０〜１５ｇ
／１０分のメルトインデックスを有する低メルトインデ
ックスブテン−１ポリマー のブレンドを含有して成る外側層 を含有して成り、そして該コアの少なくとも一つまたは
該外側層が、１９０℃で約２０〜約１０００ｇ／１０分
のメルトインデックスを有する、約０．２〜約１０重量
％の高メルトインデックスブテン−１ホモポリマーを含
む、多層の熱シールできる積層されたフィルム。2. A core layer comprising (I) a propylene homopolymer and a copolymer of propylene and 1 to about 30% by weight of an α-olefin having 2 or 4 to 8 carbon atoms, (II) On at least one side of the core: (a) 40-80 wt% propylene-ethylene random copolymer with an ethylene content of 7 wt% or less (b) 20-60 wt% 1.0 at 190 ° C. ~ 15g
An outer layer comprising a blend of a low melt index butene-1 polymer having a melt index of / 10 min, and at least one of the cores or the outer layer comprises from about 20 to about 20 at 190 ° C. A multi-layer heat sealable laminated film comprising from about 0.2 to about 10% by weight of high melt index butene-1 homopolymer having a melt index of 1000 g / 10 minutes.
ルの厚さであり、そして全フィルム厚さが０．５〜２．
０ミルである、請求項１記載の積層されたフィルム。3. The outer layer is about 0.02 mils to about 0.6 mils thick and the total film thickness is 0.5-2.
The laminated film of claim 1, which is 0 mil.
ロピレンと１〜約３０重量％の２または４〜８の炭素原
子を有するα−オレフィンとのコポリマーを含有して成
るコア層、 （ＩＩ）該コアの少なくとも一つの側の上の、 （ａ）５５〜６５重量％の、７重量％以下のエチレン含
量及び２３０℃で６〜１０ｇ／１０分のメルトインデッ
クスを有するプロピレン−エチレンランダムコポリマー （ｂ）３５〜４５重量％の、０．３〜２０．０モル％の
エチレン含量及び１９０℃で１．０〜１５ｇ／１０分の
メルトインデックスを有する低メルトインデックスブテ
ン−１エチレンランダムコポリマー のブレンドを含有して成る外側層 を含有して成り、そして該コアの少なくとも一つまたは
該外側層が、１９０℃で１００〜約３００ｇ／１０分の
メルトインデックス及び２００℃で４０，０００〜１０
０，０００センチポアズの溶融粘度を有する、約２〜約
４重量％の高メルトインデックスブテン−１ホモポリマ
ーを含む、多層の熱シールできる積層されたフィルム。4. A core layer comprising (I) a propylene homopolymer and a copolymer of propylene and 1 to about 30% by weight of an α-olefin having 2 or 4 to 8 carbon atoms, (II) On at least one side of the core: (a) 55-65% by weight of a propylene-ethylene random copolymer having an ethylene content of 7% by weight or less and a melt index of 6-10 g / 10 min at 230 ° C. (b) 35 to 45% by weight of a blend of low melt index butene-1 ethylene random copolymer having an ethylene content of 0.3 to 20.0 mol% and a melt index at 190 ° C. of 1.0 to 15 g / 10 min. And at least one of the cores or the outer layer comprises 100 to about 300 g / 10 min at 190 ° C. In the belt index and 200 ℃ 40,000~10
A multi-layer heat sealable laminated film comprising from about 2 to about 4 weight percent high melt index butene-1 homopolymer having a melt viscosity of 10,000 centipoise.