JPH05186730A - Water-base pigment ink composition for ball-point pen - Google Patents

Water-base pigment ink composition for ball-point pen

Info

Publication number
JPH05186730A
JPH05186730A JP21568492A JP21568492A JPH05186730A JP H05186730 A JPH05186730 A JP H05186730A JP 21568492 A JP21568492 A JP 21568492A JP 21568492 A JP21568492 A JP 21568492A JP H05186730 A JPH05186730 A JP H05186730A
Authority
JP
Japan
Prior art keywords
water
alkylene oxide
weight
pigment
ink composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP21568492A
Other languages
Japanese (ja)
Other versions
JP2999632B2 (en
Inventor
Mizue Saito
瑞恵 斎藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Pencil Co Ltd
Original Assignee
Mitsubishi Pencil Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Pencil Co Ltd filed Critical Mitsubishi Pencil Co Ltd
Priority to JP21568492A priority Critical patent/JP2999632B2/en
Priority to CA 2075730 priority patent/CA2075730C/en
Priority to IT92MI1997 priority patent/IT1256404B/en
Priority to FR9210152A priority patent/FR2680513B1/en
Priority to DE4227600A priority patent/DE4227600C2/en
Priority to AU21145/92A priority patent/AU2114592A/en
Publication of JPH05186730A publication Critical patent/JPH05186730A/en
Application granted granted Critical
Publication of JP2999632B2 publication Critical patent/JP2999632B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

PURPOSE:To provide an ink which scarcely causes blotting of a writing, has sufficient lubricity and gives good touch in writing. CONSTITUTION:The title composition contains at least one polyhydric alcohol/ alkylene oxide adduct selected among a polyglycerin/alkylene oxide adduct, a glycerin/alkylene oxide (1-150mol) adduct, and a trimethylolpropane/alkylene oxide adduct and their mixture, a pigment, a dispersant and water.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は水性ボールペン用顔料イ
ンキ組成物に関する。
FIELD OF THE INVENTION The present invention relates to a pigment ink composition for water-based ballpoint pens.

【0002】[0002]

【従来の技術】従来のボールペン用水性顔料インキは、
着色剤として顔料を分散し、またペン先でのインキ乾燥
抑制(ノンドライ性)のため主成分の溶剤として水の他
に、グリコールやグリセリンのような水溶性溶剤が用い
られている。しかし、このままでは潤滑性に乏しくて、
筆記時ボールが回転する際にボールとボール受座との摩
擦抵抗が大きくなるため、つぎのような欠点がある。す
なわち、ボール受座が摩耗してボールが沈んだり、ボー
ルにガタツキが生じたり、或いはインキの流出が不均一
になるなど、筆記性が著しく低下する。この様な欠点を
改良する目的で、例えば不飽和脂肪酸やオレイン酸カリ
ウムなどの潤滑性向上剤を添加することが試みられてい
る。
2. Description of the Related Art Conventional aqueous pigment inks for ballpoint pens are
In addition to water, a water-soluble solvent such as glycol or glycerin is used as a main component solvent in which a pigment is dispersed as a colorant and ink is suppressed from drying with a pen tip (non-drying property). However, as it is, the lubricity is poor,
Since the frictional resistance between the ball and the ball seat increases when the ball rotates during writing, there are the following drawbacks. That is, the writability of the ball is remarkably deteriorated because the ball seat is worn and the ball is sunk, the ball is loose, or the ink flows out unevenly. For the purpose of improving such drawbacks, it has been attempted to add a lubricity improver such as unsaturated fatty acid or potassium oleate.

【0003】一方、特開昭63−234073には、染
料を用いてポリグリセリンエチレンオキサイド付加物を
添加したボールペン用インキが開示され、また特開昭5
5−106273には染料を用いてソルビトール、グリ
セリンなどのポリオキシアルキレン付加物、およびフッ
素界面活性剤を含むボールペン用水性インキ組成物が開
示されている。いずれも潤滑性にすぐれた書き味の滑ら
かなボールペン用インキであることを示している。しか
し染料ではアルキレンオキサイド付加物を用いれば、潤
滑性に優れるが、滲み易くなる欠点がある。
On the other hand, Japanese Patent Laid-Open No. 63-234073 discloses a ball-point pen ink in which a polyglycerin ethylene oxide adduct is added by using a dye, and Japanese Patent Laid-Open No. Sho.
5-106273 discloses a water-based ink composition for a ballpoint pen containing a sorbitol, a polyoxyalkylene adduct such as glycerin, and a fluorosurfactant using a dye. All of these are inks for ball-point pens that have excellent lubricity and smooth writing. However, when an alkylene oxide adduct is used as a dye, it has excellent lubricity but has a drawback that it easily bleeds.

【0004】また、特公昭62−10547には、グリ
セリンのアルキレンオキサイド付加物を含むインクジェ
ット記録方式に適した記録液について開示されている。
しかし、ボールペンに用いた場合、潤滑性が必ずしも満
足すべきものでなく、顔料の分散が良くないなどの欠点
がある。
Further, Japanese Examined Patent Publication No. 62-10547 discloses a recording liquid containing an alkylene oxide adduct of glycerin and suitable for an ink jet recording system.
However, when it is used for a ballpoint pen, there are drawbacks such that the lubricity is not always satisfactory and the pigment is not well dispersed.

【0005】[0005]

【発明が解決しようとする課題】このように前記した従
来の方法では、充分な潤滑性が得られず、ボール受座の
摩耗による筆記不能現象が発生したり、また、たとえ充
分な潤滑性が得られても、一方でインキの表面張力を著
しく低下させて、筆跡が滲み易くなるなどの実用上の問
題があった。
As described above, in the above-mentioned conventional method, sufficient lubricity cannot be obtained, and an unreadable phenomenon occurs due to wear of the ball seat, and even if sufficient lubricity is not obtained. Even if it is obtained, on the other hand, there is a problem in practical use that the surface tension of the ink is remarkably lowered and the handwriting is easily blurred.

【0006】本発明の目的は、表面張力が極端に低下せ
ず、従って筆跡が滲みにくく、しかも充分な潤滑性を有
することにより、円滑なボール回転によりボール受座の
摩耗を少なくし筆記性能を顕著に向上させると共に、快
適な筆記感を与え、更にノンドライ性の優れた水性ボー
ルペン用顔料インキを提供しようとするものである。
An object of the present invention is that the surface tension does not drop extremely, and therefore the handwriting is less likely to bleed and has sufficient lubricity, so that smooth ball rotation reduces wear on the ball seat and improves writing performance. It is an object of the present invention to provide a pigment ink for a water-based ballpoint pen, which is remarkably improved and gives a comfortable writing feeling and is also excellent in non-drying property.

【0007】[0007]

【課題を解決するための手段】本発明者は、前記課題を
解決するため鋭意研究を行なった結果、顔料インキ組成
物に特定の多価アルコールのアルキレンオキサイド付加
物を含有させることにより、前記目的を達成しうること
を見いだし、この知見に基づいて本発明を完成した。
Means for Solving the Problems As a result of intensive studies to solve the above-mentioned problems, the present inventors have found that the pigment ink composition contains an alkylene oxide adduct of a specific polyhydric alcohol to achieve the above-mentioned object. The present invention has been completed based on this finding.

【0008】本発明の水性ボールペン用顔料インキ組成
物は、ポリグリセリンのアルキレンオキサイド付加物、
グリセリンにアルキレンオキサイドが1〜150モル付
加したグリセリンのアルキレンオキサイド付加物、およ
びトリメチロールプロパンのアルキレンオキサイド付加
物からなる群およびこれらの混合物から選ばれた少なく
とも一種の多価アルコールのアルキレンオキサイド付加
物、顔料、分散剤および水を含有することを特徴とす
る。
The aqueous pigment ink composition for a ballpoint pen of the present invention comprises a polyglycerin alkylene oxide adduct,
Alkylene oxide adduct of at least one polyhydric alcohol selected from the group consisting of alkylene oxide adduct of glycerin in which alkylene oxide is added to glycerin in an amount of 1 to 150 mol, and alkylene oxide adduct of trimethylolpropane, and a mixture thereof, It is characterized by containing a pigment, a dispersant and water.

【0009】本発明の第一の水性ボールペン用顔料イン
キ組成物は、顔料、分散剤、水およびポリグリセリンの
アルキレンオキサイド付加物を含有することを特徴とす
る。好ましくは、重合度2〜4のポリグリセリンにアル
キレンオキサイドが1〜60モル付加したポリグリセリ
ンのアルキレンオキサイド付加物を全組成物の0.5〜
40重量%、顔料が全組成物の2〜30重量%、分散剤
が全組成物の0.1〜10重量%、および水が40〜9
0重量%含有してなる水性ボールペン用顔料インキ組成
物である。
The first aqueous pigment ink composition for a ball-point pen of the present invention is characterized by containing a pigment, a dispersant, water and an alkylene oxide adduct of polyglycerin. Preferably, an alkylene oxide adduct of polyglycerin obtained by adding 1 to 60 mol of alkylene oxide to polyglycerin having a degree of polymerization of 2 to 4 is added to 0.5 to 10% of the total composition.
40% by weight, pigment 2-30% by weight of the total composition, dispersant 0.1-10% by weight of the total composition, and water 40-9.
The pigment ink composition for water-based ballpoint pens contains 0% by weight.

【0010】本発明の第二の水性ボールペン用顔料イン
キ組成物は、顔料、分散剤、水およびグリセリンにアル
キレンオキサイドが1〜150モル付加したグリセリン
のアルキレンオキサイド付加物を含有することを特徴と
する。好ましくは、グリセリンのアルキレンオキサイド
付加物を全組成物の0.5〜40重量%、顔料2〜30
重量%、分散剤0.1〜10重量%、および水40〜9
0重量%含有してなる水性ボールペン用顔料インキ組成
物である。
The second aqueous pigment ink composition for a ball-point pen of the present invention is characterized by containing a pigment, a dispersant, water, and an alkylene oxide adduct of glycerin obtained by adding 1 to 150 mol of alkylene oxide to glycerin. .. Preferably, the alkylene oxide adduct of glycerin is 0.5 to 40% by weight of the total composition, and the pigment is 2 to 30%.
Wt%, dispersant 0.1-10 wt%, and water 40-9
The pigment ink composition for water-based ballpoint pens contains 0% by weight.

【0011】本発明の第三の水性ボールペン用顔料イン
キ組成物は、顔料、分散剤、水溶性溶剤および水を主成
分とする水性顔料インキにおいて、トリメチロールプロ
パンのアルキレンオキサイド付加物を添加することを特
徴とする。好ましくは、トリメチロールプロパンのアル
キレンオキサイドが1〜60モル付加したトリメチロー
ルプロパンのアルキレンオキサイド付加物を全組成物の
0.5〜40重量%、顔料2〜30重量%、分散剤0.
1〜10重量%および水40〜90重量%含有してなる
水性ボールペン用顔料インキ組成物である。
The third aqueous pigment ink composition for a ball-point pen of the present invention comprises adding an alkylene oxide adduct of trimethylolpropane to an aqueous pigment ink containing a pigment, a dispersant, a water-soluble solvent and water as main components. Is characterized by. Preferably, the alkylene oxide adduct of trimethylolpropane in which 1 to 60 mol of alkylene oxide of trimethylolpropane is added is 0.5 to 40% by weight of the total composition, the pigment is 2 to 30% by weight, and the dispersant is 0.1.
An aqueous pigment ink composition for a ball-point pen, containing 1 to 10% by weight and 40 to 90% by weight of water.

【0012】本発明の組成物に用いるポリグリセリンの
アルキレンオキサイド付加物とは、重合度2〜4のポリ
グリセリンにアルキレンオキサイドが1〜60モル付加
したものであり、たとえば、ジグリセリン、トリグリセ
リンなどのグリセリン2〜4モルの重合物にエチレンオ
キサイドもしくはプロピレンオキサイド、またはそれら
の混合物を1〜60モル付加したものの一種である。ポ
リグリセリンのアルキレンオキサイド付加物の含有量と
しては、全組成物の0.5〜40重量が好ましいが、更
に好ましくは、1〜30重量%である。0.5重量%以
下では充分な潤滑性が得られず筆記性の向上を期待する
ことができず、また、40重量%以上ではインキの粘度
を高くし、流出が悪くなり不適である。
The alkylene oxide adduct of polyglycerin used in the composition of the present invention is obtained by adding 1 to 60 mol of alkylene oxide to polyglycerin having a polymerization degree of 2 to 4, and examples thereof include diglycerin and triglycerin. 1 to 60 mol of ethylene oxide or propylene oxide, or a mixture thereof is added to 2 to 4 mol of glycerin. The content of the alkylene oxide adduct of polyglycerin is preferably 0.5 to 40% by weight of the total composition, more preferably 1 to 30% by weight. If it is less than 0.5% by weight, sufficient lubricity cannot be obtained and improvement in writing performance cannot be expected, and if it is more than 40% by weight, the viscosity of the ink becomes high and the outflow becomes worse, which is not suitable.

【0013】本発明のインキ組成物に用いるグリセリン
のアルキレンオキサイド付加物とは、グリセリンにアル
キレンオキサイドが1〜150モル付加したものであ
り、好ましくは11〜60モル付加したものである。た
とえば、グリセリンにエチレンオキサイドもしくはプロ
ピレンオキサイド、またはそれらの混合物を1〜150
モル付加したもの、好ましくは11〜60モル付加した
ものの一種である。グリセリンのアルキレンオキサイド
付加物の含有量としては、組成物に対して0.5〜40
重量%が好ましい。更に好ましくは、1〜30重量%で
ある。0.5重量%以下では、充分な潤滑性を得て、筆
記性が向上する効果を期待することができず、また、4
0重量%以上ではインキの粘度を高くし、流出が悪くな
り不適である。
The alkylene oxide adduct of glycerin used in the ink composition of the present invention is 1 to 150 mol of alkylene oxide added to glycerin, preferably 11 to 60 mol. For example, glycerin may be mixed with ethylene oxide or propylene oxide, or a mixture thereof in an amount of 1 to 150.
It is one of those added by moles, preferably 11-60 moles. The content of the alkylene oxide adduct of glycerin is 0.5 to 40 with respect to the composition.
Weight percent is preferred. More preferably, it is 1 to 30% by weight. If it is less than 0.5% by weight, sufficient lubricity cannot be obtained and the effect of improving the writability cannot be expected.
When the content is 0% by weight or more, the viscosity of the ink is increased and the outflow is deteriorated, which is not suitable.

【0014】本発明のインキ組成物に用いるトリメチロ
ールプロパンのアルキレンオキサイド付加物とは、トリ
メチロールプロパンにアルキレンオキサイドが1〜60
モル付加したものであり、たとえば、トリメチロールプ
ロパンにエチレンオキサイドもしくはプロピレンオキサ
イド、またはそれらの混合物を1〜60モル付加したも
のの一種である。トリメチロールプロパンのアルキレン
オキサイド付加物の含有量としては、組成物に対して
0.5〜40重量%が好ましい。更に久野ましくは、1
〜30重量%である。含有量としては、0.5〜40重
量%が好ましい。0.5重量%以下では、充分な潤滑
性、筆記性の向上の効果を期待することができず、ま
た、40重量%以上ではインキの粘度を高くし、流出が
悪くなり不適である。
The alkylene oxide adduct of trimethylolpropane used in the ink composition of the present invention is trimethylolpropane having 1 to 60 alkylene oxides.
For example, it is one of those obtained by adding 1 to 60 mol of ethylene oxide or propylene oxide or a mixture thereof to trimethylolpropane. The content of the alkylene oxide adduct of trimethylolpropane is preferably 0.5 to 40% by weight based on the composition. More Kuno, 1
~ 30% by weight. The content is preferably 0.5 to 40% by weight. If it is 0.5% by weight or less, the effect of sufficiently improving lubricity and writability cannot be expected. On the other hand, if it is 40% by weight or more, the viscosity of the ink becomes high and the outflow becomes worse, which is not suitable.

【0015】本発明のインキ組成物において、特定の多
価アルコールアルキレンオキサイド付加物は、水溶性有
機溶剤と混合して用いてもよい。その溶剤としては、エ
チレングリコール、プロピレングリコールグリコール、
グリセリンなどの水溶性多価アルコール類、エチレング
リコールモノメチルエーテル(メチルセルソルブ)、エ
チレングリコールモノエチルエーテル(エチルセルソル
ブ)などのセルソルブ類、ジエチレングリコールモノメ
チルエーテル(メチルカルビトール)、ジエチレングリ
コールモノエチルエーテル(エチルカルビトール)など
のカルビトール類、エチレングリコールモノエチルエー
テルアセテートのようなグリコールエーテルエステル類
などが挙げられる。これらはノンドライ性を向上する。
また、その配合量は、全組成物に対して、通常40重量
%以下好ましくは5〜40重量%で選ばれる。
In the ink composition of the present invention, the specific polyhydric alcohol alkylene oxide adduct may be used as a mixture with a water-soluble organic solvent. As the solvent, ethylene glycol, propylene glycol glycol,
Water-soluble polyhydric alcohols such as glycerin, ethylene glycol monomethyl ether (methyl cellsolve), cellosolves such as ethylene glycol monoethyl ether (ethyl cellsolve), diethylene glycol monomethyl ether (methyl carbitol), diethylene glycol monoethyl ether (ethyl) Carbitols) such as carbitol) and glycol ether esters such as ethylene glycol monoethyl ether acetate. These improve the non-drying property.
Moreover, the compounding amount is usually 40% by weight or less, preferably 5 to 40% by weight, based on the entire composition.

【0016】本発明のインキ組成物に用いられる顔料の
種類は特に制限はなく、従来、水性顔料インキ組成物に
慣用されている無機系及び有機系顔料の中から任意のも
のを使用することができる。無機系顔料としては、例え
ば酸化チタン、カーボンブラック、金属粉などが挙げら
れ、また有機系顔料としては、例えばアゾレーキ、不溶
性アゾ顔料、キレートアゾ顔料、フタロシアニン顔料、
ペリレン及びペリノン顔料、アントラキノン顔料、キナ
クリドン顔料、染料レーキ、ニトロ顔料、ニトロソ顔料
などが挙げられる。
The type of pigment used in the ink composition of the present invention is not particularly limited, and any of inorganic and organic pigments conventionally used in water-based pigment ink compositions can be used. it can. Examples of the inorganic pigment include titanium oxide, carbon black, metal powder, and the like, and examples of the organic pigment include azo lake, insoluble azo pigment, chelate azo pigment, phthalocyanine pigment, and the like.
Perylene and perinone pigments, anthraquinone pigments, quinacridone pigments, dye lakes, nitro pigments, nitroso pigments and the like.

【0017】具体的には、フタロシアニンブルー(C.
I.74160)、フタロシアニングリーン(C.I.
74260)、ハンザイエロー3G(C.I.1167
0)ジスアゾエローGR(C.I.21100)、パー
マネントレッド4R(C.I.12335)、ブリリア
ントカーミン6B(C.I.15850)キナクリドン
レッド(C.I.46500)が使用できる。これらの
顔料はそれぞれ単独で用いてもよいし、2種類以上を組
み合わせて用いてもよく、その配合量は、全組成物の重
量に基づき、通常2〜30重量%、好ましくは5〜15
重量%の範囲で選ばれる。
Specifically, phthalocyanine blue (C.
I. 74160), phthalocyanine green (C.I.
74260), Hansa Yellow 3G (C.I. 1167)
0) Disazo yellow GR (CI. 21100), permanent red 4R (CI. 12335), brilliant carmine 6B (CI. 15850) quinacridone red (CI. 46500) can be used. These pigments may be used alone or in combination of two or more, and the compounding amount thereof is usually 2 to 30% by weight, preferably 5 to 15% based on the weight of the entire composition.
It is selected in the range of weight%.

【0018】本発明の組成物における分散剤とは、顔料
粒子表面に吸着して、水中に顔料を分散するために用い
るものであり、ノニオン、アニオン系界面活性剤や水溶
性高分子が用いられる。好ましくは水溶性高分子が用い
られる。ノニオン系界面活性剤としては、ポリオキシア
ルキレン高級脂肪酸エステル、多価アルコールの高級脂
肪酸部分エステル、糖の高級脂肪酸エステルなどがあ
り、具体的にはグリセリンの脂肪酸エステル、ポリグリ
セリン脂肪酸エステル、プロピレングリコール脂肪酸エ
ステル、ペンタエリスリトール脂肪酸エステル、ポリオ
キシエチレンソルビタン脂肪酸エステル、ポリオキシエ
チレンソルビット脂肪酸エステル、ポリオキシエチレン
グリセリン脂肪酸エステル、ポリエチレングリコール脂
肪酸エステル、ポリオキシエチレンアルキレルエーテ
ル、ポリオキシエチレンフィトステロール、ポリオキシ
エチレンポリオキシプロピレンアルキルエーテル、ポリ
オキシエチレンアルキルフェニルエーテル、ポリオキシ
エチレンヒマシ油、ポリオキシエチレンラノリン、ポリ
オキシエチレンラノリンアルコール、ポリオキシエチレ
ンアルキルアミン、ポリオキシエチレン脂肪酸アミド、
ポリオキシエチレンアルキルフェニルホルムアルデヒド
縮合物などがある。
The dispersant in the composition of the present invention is used to disperse the pigment in water by adsorbing it on the surface of the pigment particles, and nonionic, anionic surfactant or water-soluble polymer is used. .. A water-soluble polymer is preferably used. Nonionic surfactants include polyoxyalkylene higher fatty acid esters, higher fatty acid partial esters of polyhydric alcohols, higher fatty acid esters of sugars, and the like. Specifically, fatty acid esters of glycerin, polyglycerin fatty acid esters, propylene glycol fatty acid Ester, pentaerythritol fatty acid ester, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene sorbitol fatty acid ester, polyoxyethylene glycerin fatty acid ester, polyethylene glycol fatty acid ester, polyoxyethylene alkyl ether, polyoxyethylene phytosterol, polyoxyethylene polyoxy Propylene alkyl ether, polyoxyethylene alkylphenyl ether, polyoxyethylene castor oil, polyoxy Chirenranorin, polyoxyethylene lanolin alcohols, polyoxyethylene alkyl amines, polyoxyethylene fatty acid amides,
Examples include polyoxyethylene alkylphenyl formaldehyde condensates.

【0019】アニオン系界面活性剤としては、高級脂肪
酸アミドのアルキル化スルフォン酸塩、アルキルアリル
スルフォン酸塩などがあり、具体的には、アルキル硫酸
塩、ポリオキシエチレンアルキルエーテル硫酸塩、N‐
アシルアミノ酸塩、N‐アシルメチルタウリン塩、ポリ
オキシエチレンアルキルエーテル酢酸塩、アルキルリン
酸塩、ポリオキシエチレンアルキルエーテルリン酸塩な
どがある。水溶性高分子としては、ポリアクリル酸、ア
クリル酸共重合体、マレイン酸樹脂などがある。
Examples of the anionic surfactant include alkylated sulfonates of higher fatty acid amides and alkylallyl sulfonates, and specifically, alkyl sulfates, polyoxyethylene alkyl ether sulfates, N-
Acyl amino acid salts, N-acyl methyl taurine salts, polyoxyethylene alkyl ether acetate salts, alkyl phosphate salts, polyoxyethylene alkyl ether phosphate salts, and the like. Examples of the water-soluble polymer include polyacrylic acid, acrylic acid copolymer, and maleic acid resin.

【0020】具体的には、アクリル樹脂、スチレンアク
リル樹脂、スチレンマレイン酸樹脂などの樹脂を塩の形
にして水溶性にしたものを用いる。塩を形成するアルカ
リ金属としては、ナトリウム、カリウムが代表的であ
り、アミンとしてはモノー、ジー又はトリーメチルアミ
ンなどの脂肪族第1から第3級アミン、モノー、ジ又は
トリープロパノールアミン、メチルエタノールアミン、
メチルプロパノールアミンジメチルエタノールアミンな
どのアルコールアミンその他アンモニア、モルホリン及
びN‐メチルホリン等が代表的である。その配合量は組
成物中0.1〜10重量%である。
Specifically, a resin such as an acrylic resin, a styrene acrylic resin, or a styrene maleic acid resin which is made water-soluble in the form of a salt is used. As the alkali metal forming a salt, sodium and potassium are typical, and as the amine, aliphatic primary to tertiary amines such as mono-, di- or tri-methyl amine, mono-, di- or tri-propanol amine, methyl ethanol. Amine,
Typical examples are alcohol amines such as methyl propanol amine dimethyl ethanol amine, ammonia, morpholine and N-methyl pholine. The compounding amount is 0.1 to 10% by weight in the composition.

【0021】本発明の組成物に用いる水は特に限定しな
いが40〜90%が望ましい。
The water used in the composition of the present invention is not particularly limited, but is preferably 40 to 90%.

【0022】以上の他、必要に応じて、潤滑剤としてリ
ノール酸カリウム、リシノール酸ナトリウム、オレイン
酸カリウム、オレイン酸ナトリウムなど、防腐剤として
フェノール、安息香酸ナトリウムなど、防錆剤としてベ
ンゾトリゾール、ジシクロヘキシルアンモニウム・ナイ
トライト、ジイソプロピルアンモニウム・ナイトライト
など、pH調節剤としてトリエタノールアミン、モノエ
タノールアミン、ジエタノールアミン、アンモニアなど
を配合することができる。
In addition to the above, if necessary, potassium linoleate, sodium ricinoleate, potassium oleate, sodium oleate and the like as lubricants, phenol and sodium benzoate as preservatives, and benzotrizole as rust preventives, Triethanolamine, monoethanolamine, diethanolamine, ammonia and the like can be blended as a pH adjusting agent such as dicyclohexylammonium nitrite and diisopropylammonium nitrite.

【0023】[0023]

【作用】本発明の水性インキ組成物は潤滑性に優れ、筆
記性能を向上させる。その詳細な作用機構は明らかでは
ないが、本発明に使用の特定の多価アルコールのアルキ
レンオキサイド付加物の構造中の水酸基およびエーテル
結合部の酸素が、金属表面に吸着作用を示し、金属表面
との反対側には炭化水素鎖がならぶ。そこで、特定の多
価アルコールのアルキレンオキサイド付加物自身の粘性
により、ボールとボールの受座の間に潤滑皮膜が形成さ
れることによって潤滑性を付与されるものと推察され
る。
The water-based ink composition of the present invention has excellent lubricity and improves writing performance. Although its detailed mechanism of action is not clear, oxygen of the hydroxyl group and the ether bond in the structure of the alkylene oxide adduct of the specific polyhydric alcohol used in the present invention shows an adsorption action on the metal surface, A hydrocarbon chain is lined up on the opposite side of. Therefore, it is assumed that the viscosity of the alkylene oxide adduct of a specific polyhydric alcohol itself gives a lubricity by forming a lubricating film between the ball and the seat of the ball.

【0024】本発明の組成物は、特定の多価アルコール
のアルキレンオキサイド付加物のグリセリンもしくはエ
チレンオキサイドの高分子連鎖の影響による適度の粘
性、および分散剤の影響により、ボールペンに使用した
場合に滲みがすくなく良好な潤滑性を得られるものと考
えられる。また、特定の多価アルコールのアルキレンオ
キサイド付加物を用いたインキにおいて、染料では、滲
み易く、顔料では、滲みにくいのかは、明らかではない
が、染料と顔料との溶剤に対する溶解性の違いによるも
のと思われる。
The composition of the present invention has a moderate viscosity due to the influence of the polymer chain of glycerin or ethylene oxide which is an alkylene oxide adduct of a specific polyhydric alcohol, and the influence of a dispersant. It is considered that good lubricity can be obtained with little scrap. Further, in an ink using an alkylene oxide adduct of a specific polyhydric alcohol, it is not clear whether the dye easily bleeds and the pigment hardly bleeds, but it is due to the difference in the solubility between the dye and the pigment in the solvent. I think that the.

【0025】[0025]

【実施例】次に実施例により本発明をさらに詳細に説明
するが、本発明はこれらの例によってなんら限定される
ものではない。実施例1〜8、比較例1〜6のインキ
は、各成分を撹拌機にて3時間の撹拌・混合したのち、
サンドミルにて5時間分散し、更に、粗大粒子を遠心分
離機により除去することにより得た。比較例7および8
の染料インキは、各成分を40〜60℃で1時間撹拌し
た後に冷却し、更にろ過して得た。各実施例、比較例で
得られたインキの評価はつぎの筆記試験の判定で行っ
た。結果を表1に示した。
The present invention will be described in more detail by way of examples, which should not be construed as limiting the invention thereto. In the inks of Examples 1 to 8 and Comparative Examples 1 to 6, after the components were stirred and mixed for 3 hours with a stirrer,
It was obtained by dispersing in a sand mill for 5 hours and further removing coarse particles with a centrifuge. Comparative Examples 7 and 8
The dye ink of (1) was obtained by stirring each component at 40 to 60 ° C. for 1 hour, cooling, and further filtering. The inks obtained in the respective examples and comparative examples were evaluated by the following writing test. The results are shown in Table 1.

【0026】筆記試験におけるボール沈み測定法と筆
感、筆跡の滲み状態の判定は次のとおりである。 ボール沈み:螺旋筆記試験機にて筆記角度60度、筆記
速度5.5m/min 、荷重100gの条件で500m筆
記後のボールの座の摩耗した深さ、すなわちホルダーよ
り突出したボールの突出長さの減少した長さを測定し
た。 筆感: ○ 滑らかで安定した書味 △ ゴツゴツした硬い書味 × ゴツゴツした硬い書味でかつ線切れ、方向性があ
る。 筆跡滲み: ○ 滲みなく鮮明な筆跡 △ 滲みがあり不鮮明な筆跡 × 滲みが著しく非常に不鮮明な筆跡
The ball sinking measuring method, the writing feeling, and the blurring state of the handwriting in the writing test are determined as follows. Ball sinking: With a spiral writing tester at a writing angle of 60 degrees, a writing speed of 5.5 m / min, and a load of 100 g, the worn depth of the ball seat after 500 m writing, that is, the protruding length of the ball protruding from the holder. The reduced length of was measured. Writing feel: ○ Smooth and stable writing quality △ Rugged and hard writing quality × Rugged and hard writing quality, with line breaks and directionality. Handwriting blur: ○ Clear handwriting without bleeding △ Bleeding and unclear writing × Extremely unclear writing with remarkable bleeding

【0027】実施例1 下記の配合で黒色水性ボールペン用顔料インキを調製し
た。 カーボンブラックMA100 (三菱化成(株)製) 8.0重量% エチレングリコール 10.0 〃 ジグリセリンのエチレンオキサイド30モル付加物 5.0 〃 スチレンアクリル酸樹脂アンモニウム塩 3.0 〃 リノール酸カリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 73.0 〃 合計 100.0 〃
Example 1 A black aqueous pigment ink for a ballpoint pen was prepared with the following composition. Carbon black MA100 (manufactured by Mitsubishi Kasei Co., Ltd.) 8.0% by weight Ethylene glycol 10.0 〃 Diglycerin ethylene oxide 30 mol adduct 5.0 〃 Styrene acrylate resin ammonium salt 3.0 〃 Potassium linoleate 0.3 〃 Triethanolamine 0.5 〃 Phenol 0.1 〃 Benzotriazole 0.1 〃 Purified water 73.0 〃 Total 100.0 〃

【0028】実施例2 下記の配合で青色水性ボールペン用顔料インキを調製し
た。 フタロシアニンブルー(大日精化(株)製Chromofine Blue 4965) 8.0重量% グリセリン 5.0 〃 トリグリセリンのプロピレンオキサイド20モル付加物 10.0 〃 スチレンマレイン酸樹脂アンモニウム塩 3.0 〃 リシノール酸ナトリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 73.0 〃 合計 100.0 〃
Example 2 A blue water-based ballpoint pen pigment ink was prepared with the following formulation. Phthalocyanine blue (Chromofine Blue 4965 manufactured by Dainichiseika Co., Ltd.) 8.0% by weight glycerin 5.0 〃 Triglycerin propylene oxide 20 mol adduct 10.0 〃 Styrene maleic acid resin ammonium salt 3.0 〃 Sodium ricinoleate 0.3 〃 Triethanolamine 0.5 〃 Phenol 0.1 〃 Benzotriazole 0.1 〃 Purified water 73.0 〃 Total 100.0 〃

【0029】比較例1 ジグリセリンのエチレンオキサイド30モル付加物を使
用せずエチレングリコール15%にした以外は、実施例
1と同様にして調製し、黒色水性顔料インキを得た。
Comparative Example 1 A black water-based pigment ink was obtained in the same manner as in Example 1 except that 30 mol of an ethylene oxide adduct of diglycerin was not used and ethylene glycol was changed to 15%.

【0030】比較例2 トリグリセリンのプロピレンオキサイド20モル付加物
を使用せず、グリセリン15%にし、リシノール酸ナト
リウムを0.5%にし、精製水を72.8%にした以外
は、実施例2と同様にして調製し、青色水性顔料インキ
を得た。
Comparative Example 2 Example 2 was repeated, except that 20 mol of a propylene oxide adduct of triglycerin was not used, but glycerin was 15%, sodium ricinoleate was 0.5%, and purified water was 72.8%. A blue water-based pigment ink was obtained in the same manner as in.

【0031】実施例3 つぎの配合にて、青色水性ボールペン用顔料インキを得
た。筆記試験の結果を表1に示す。 フタロシアニンブルー(大日精化(株)製Chromofine Blue4965 ) 7.0重量% エチレングリコール 17.0 〃 グリセリンのエチレンオキサイド40モル付加物 3.0 〃 スチレンアクリル酸樹脂アンモニウム塩 3.0 〃 リノール酸カリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 69.0 〃 合計 100.0 〃
Example 3 A blue water-based ballpoint pen pigment ink was obtained with the following formulation. The results of the written test are shown in Table 1. Phthalocyanine Blue (Chromofine Blue4965 manufactured by Dainichiseika Co., Ltd.) 7.0% by weight Ethylene glycol 17.0 〃 Ethylene oxide 40 mol adduct of glycerin 3.0 〃 Styrene acrylate resin ammonium salt 3.0 〃 Potassium linoleate 0.3 〃 Triethanolamine 0.5 〃 Phenol 0.1 〃 Benzotriazole 0.1 〃 Purified water 69.0 〃 Total 100.0 〃

【0032】実施例4 つぎの配合にて、黒色水性ボールペン用顔料インキを調
製した。筆記試験の結果を表1に示す。 カーボンブラックMA100 (三菱化成(株)製) 8.0重量% グリセリン 5.0 〃 グリセリンのエチレンオキサイド20モル付加物 5.0 〃 スチレンマレイン酸樹脂アンモニウム塩 3.0 〃 リシノール酸ナトリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 78.0 〃 合計 100.0 〃
Example 4 A black water-based ballpoint pen pigment ink was prepared with the following formulation. The results of the written test are shown in Table 1. Carbon black MA100 (manufactured by Mitsubishi Kasei Co., Ltd.) 8.0% by weight glycerin 5.0 〃 ethylene oxide 20 mol adduct of glycerin 5.0 〃 styrene maleic acid resin ammonium salt 3.0 〃 sodium ricinoleate 0.3 〃 triethanolamine 0.5 〃 phenol 0.1 〃 benzotriazole 0.1 〃 Purified water 78.0 〃 Total 100.0 〃

【0033】比較例3 グリセリンのエチレンオキサイド40モル付加物を用い
ず、エチレングリコール20重量%とした以外は、実施
例3と同様にして青色水性顔料インキを得た。筆記試験
の結果を表1に示す。
Comparative Example 3 A blue water-based pigment ink was obtained in the same manner as in Example 3 except that 20% by weight of ethylene glycol was used without using 40 mol of ethylene oxide adduct of glycerin. The results of the written test are shown in Table 1.

【0034】比較例4 グリセリンのエチレンオキサイド20モル付加物を用い
ず、グリセリン10重量%にし、リシノール酸ナトリウ
ムを0.5%にし、精製水を77.8%にした以外は、
実施例4と同様にして黒色水性顔料インキを得た。筆記
試験の結果を表1に示す。
Comparative Example 4 Except that 20 mol of ethylene oxide adduct of glycerin was not used, glycerin was 10% by weight, sodium ricinoleate was 0.5%, and purified water was 77.8%.
A black aqueous pigment ink was obtained in the same manner as in Example 4. The results of the written test are shown in Table 1.

【0035】実施例5 つぎの配合にて青色水性ボールペン用顔料インキを調製
した。筆記試験の結果を表1に示す。 フタロシアニンブルー(大日精化(株)製Chromofine Blue4965 ) 7.0重量% エチレングリコール 17.0 〃 グリセリンのエチレンオキサイド40モル付加物 3.0 〃 ニッコールNP‐10(ポリオキシエチレンノニルフェニルエーテル) (日光ケミカルズ(株)製) 3.0 〃 リノール酸カリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 69.0 〃 合計 100.0 〃
Example 5 A blue water-based ballpoint pen pigment ink was prepared with the following formulation. The results of the written test are shown in Table 1. Phthalocyanine Blue (Chromofine Blue4965 manufactured by Dainichiseika Co., Ltd.) 7.0% by weight Ethylene glycol 17.0 〃 Addition of 40 mol of ethylene oxide to glycerin 3.0 〃 Nikkor NP-10 (polyoxyethylene nonylphenyl ether) (manufactured by Nikko Chemicals Co., Ltd.) 3.0 potassium linoleate 0.3 〃 triethanolamine 0.5 〃 phenol 0.1 〃 benzotriazole 0.1 〃 purified water 69.0 〃 total 100.0 〃

【0036】実施例6 つぎの配合にて、赤色水性ボールペン用顔料インキを調
製した。筆記試験の結果を表1に示す。 赤色顔料(RED K 富士色素(株)製) 8.0重量% エチレングリコール 30.0 〃 スチレンアクリル酸樹脂アンモニウム塩 3.0 〃 リノール酸カリウム 0.3 〃 トリメチロールプロパンのエチレンオキサイド5モル付加物 2.0 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 56.0 〃 合計 100.0 〃
Example 6 A red pigment ink for water-based ballpoint pens was prepared with the following composition. The results of the written test are shown in Table 1. Red pigment (RED K, manufactured by Fuji Dye Co., Ltd.) 8.0% by weight Ethylene glycol 30.0 〃 Styrene acrylic acid resin ammonium salt 3.0 〃 Potassium linoleate 0.3 〃 Ethylene oxide 5 mol adduct of trimethylolpropane 2.0 〃 Triethanolamine 0.5 〃 Phenol 0.1 〃 Benzotriazole 0.1 〃 Purified water 56.0 〃 Total 100.0 〃

【0037】実施例7 つぎの配合にて、黒色水性顔料インキを調製した。筆記
試験の結果を表1に示す。 カーボンブラックMA100 (三菱化成(株)製) 8.0重量% グリセリン 10.0 〃 スチレンマレイン酸アンモニウム塩 3.0 〃 トリメチロールプロパンのプロピレンオキサイド10モル付加物 1.5 〃 トリエタノールアミン 0.5 〃 リシノール酸ナトリウム 0.3 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 76.5 〃 合計 100.0 〃
Example 7 A black aqueous pigment ink was prepared with the following formulation. The results of the written test are shown in Table 1. Carbon black MA100 (manufactured by Mitsubishi Kasei Co., Ltd.) 8.0 wt% Glycerin 10.0 〃 Styrene maleic acid ammonium salt 3.0 〃 Propylene oxide 10 mol adduct of trimethylolpropane 1.5 〃 Triethanolamine 0.5 〃 Sodium ricinoleate 0.3 〃 Phenol 0.1 〃 Benzo Triazole 0.1 〃 Purified water 76.5 〃 Total 100.0 〃

【0038】比較例5 トリメチロールプロパンのエチレンオキサイド5モル付
加物を除き、精製水を58%にした以外は、実施例6と
同様にして調製し赤色水性顔料インキを得た。
Comparative Example 5 A red aqueous pigment ink was prepared in the same manner as in Example 6 except that 5 mol of ethylene oxide of trimethylolpropane was added and purified water was changed to 58%.

【0039】比較例6 トリメチロールプロパンのプロピレンオキサイド10モ
ル付加物を除き、リシノール酸ナトリウムを0.5%に
し、精製水を77.8%とした以外は、実施例7と同様
に調製し、黒色水性顔料インキを得た。
Comparative Example 6 Preparation was carried out in the same manner as in Example 7 except that trimethylolpropane 10 mol adduct of propylene oxide was removed, sodium ricinoleate was 0.5%, and purified water was 77.8%. A black aqueous pigment ink was obtained.

【0040】比較例7 つぎの配合にて、黒色水性ボールペン用染料インキ調製
した。筆記試験の結果を表1に示す。 C.I.ダイレクトブラック#19 5.0重量% エチレングリコール 10.0 〃 ジグリセリンのエチレンオキサイド30モル付加物 5.0 〃 リノール酸カリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 精製水 79.0 〃 合計 100.0 〃
Comparative Example 7 A black ink dye ink for ballpoint pens was prepared with the following composition. The results of the written test are shown in Table 1. C. I. Direct Black # 19 5.0 wt% Ethylene glycol 10.0 〃 Addition of 30 mol of ethylene oxide to diglycerin 5.0 〃 Potassium linoleate 0.3 〃 Triethanolamine 0.5 〃 Phenol 0.1 〃 Benzotriazole 0.1 〃 Purified water 79.0 〃 Total 100.0 〃

【0041】比較例8 つぎの配合にて、青色水性ボールペン用染料インキ調製
した。筆記試験の結果を表1に示す。 食用青1号 6.0重量% エチレングリコール 17.0 〃 グリセリンのエチレンオキサイド40モル付加物 3.0 〃 リノール酸カリウム 0.3 〃 トリエタノールアミン 0.5 〃 フェノール 0.1 〃 ベンゾトリアゾール 0.1 〃 アニオン性フッ素系界面活性剤 0.01 〃 精製水 72.99 〃 合計 100.0 〃
Comparative Example 8 A blue water-based ballpoint pen dye ink was prepared according to the following formulation. The results of the written test are shown in Table 1. Food Blue No. 1 6.0% by weight Ethylene glycol 17.0 〃 Glycerin ethylene oxide 40 mol adduct 3.0 〃 Potassium linoleate 0.3 〃 Triethanolamine 0.5 〃 Phenol 0.1 〃 Benzotriazole 0.1 〃 Anionic fluorosurfactant 0.01 〃 Purified water 72.99 〃 Total 100.0 〃

【0042】以上、実施例1〜7、比較例1〜8で得ら
れたインキを用いたボールペンによって、筆記試験でボ
ール沈み、筆感、筆跡の滲み状態を調べた結果を表1に
示す。
Table 1 shows the results of examining the ball sinking, the writing feeling, and the bleeding state of the handwriting in the writing test with the ballpoint pens using the inks obtained in Examples 1 to 7 and Comparative Examples 1 to 8.

【0043】[0043]

【表1】 このように、本発明の水性顔料インキは、ボール沈みが
極めて少なく、筆感も滑らかであり、更に筆跡が滲みに
くい。
[Table 1] As described above, the aqueous pigment ink of the present invention has very little ball sinking, has a smooth writing feel, and is less likely to cause handwriting to bleed.

【0044】[0044]

【発明の効果】本発明の水性ボールペン用顔料インキ組
成物は、ボールペンに使用した場合、筆跡の滲みが少な
く、良好な潤滑性を与え、ボールの回転によるボール受
座の摩耗が少なく、適正なインキ流出性を保持すると共
に滑らかな筆感を与える。また、ペン先でのインキの乾
燥が抑制されるので、カスレにくいという効果を奏す
る。更に、ペン先やオリフィス先端部でのドライアップ
を抑制し、目詰りを防ぎ、印字部の滲みが少ないのでイ
ンクジェット用インキとしても極めて好適である。
INDUSTRIAL APPLICABILITY The aqueous pigment ink composition for a ball-point pen of the present invention, when used in a ball-point pen, has less blurring of handwriting, provides good lubricity, has less abrasion of the ball seat due to rotation of the ball, and is suitable for use in a ball-point pen. Maintains ink outflow and gives a smooth writing feel. Further, since the ink is suppressed from being dried by the pen tip, it is possible to prevent the ink from being easily scraped. Furthermore, it is extremely suitable as an ink jet ink because it suppresses dry-up at the tip of the pen or the orifice, prevents clogging, and causes less bleeding in the printed portion.

Claims (11)

【特許請求の範囲】[Claims] 【請求項1】 ポリグリセリンのアルキレンオキサイド
付加物、グリセリンにアルキレンオキサイドが1〜15
0モル付加したグリセリンのアルキレンオキサイド付加
物およびトリメチロールプロパンのアルキレンオキサイ
ド付加物からなる群およびこれらの混合物から選ばれた
少なくとも一種の多価アルコールのアルキレンオキサイ
ド付加物、顔料、分散剤および水を含有することを特徴
とする水性ボールペン用顔料インキ組成物。
1. An alkylene oxide adduct of polyglycerin, wherein glycerin has 1 to 15 alkylene oxides.
Containing at least one polyhydric alcohol alkylene oxide adduct, a pigment, a dispersant, and water selected from the group consisting of alkylene oxide adducts of glycerin and alkylene oxide adducts of trimethylolpropane added with 0 mol and mixtures thereof. A pigment ink composition for water-based ballpoint pens, characterized in that
【請求項2】 前記の多価アルコールのアルキレンオキ
サイド付加物を全組成物の0.5〜40重量%含有して
なる請求項1記載の水性ボールペン用顔料インキ組成
物。
2. The pigment ink composition for water-based ballpoint pens according to claim 1, wherein the alkylene oxide adduct of the polyhydric alcohol is contained in an amount of 0.5 to 40% by weight of the total composition.
【請求項3】 顔料分散剤、水およびポリグリセリンの
アルキレンオキサイド付加物を含有することを特徴とす
る水性ボールペン用顔料インキ組成物。
3. An aqueous pigment ink composition for a ballpoint pen, which comprises a pigment dispersant, water and an alkylene oxide adduct of polyglycerin.
【請求項4】 重合度2〜4のポリグリセリンにアルキ
レンオキサイドが1〜60モル付加したポリグリセリン
のアルキレンオキサイド付加物を全組成物の0.5〜4
0重量%、顔料が組成物の2〜30重量%、分散剤が組
成物の0.1〜10重量%、および水が40〜90重量
%含有してなる請求項3記載の水性ボールペン用顔料イ
ンキ組成物。
4. An alkylene oxide adduct of polyglycerin obtained by adding 1 to 60 mol of alkylene oxide to polyglycerin having a degree of polymerization of 2 to 4 is added to 0.5 to 4 of the total composition.
The pigment for water-based ballpoint pens according to claim 3, wherein 0% by weight, 2 to 30% by weight of the pigment, 0.1 to 10% by weight of the dispersant and 40 to 90% by weight of water are contained. Ink composition.
【請求項5】 分散剤が水溶性高分子である請求項4記
載の水性ボールペン用顔料インキ組成物。
5. The aqueous pigment ink composition for a ballpoint pen according to claim 4, wherein the dispersant is a water-soluble polymer.
【請求項6】 顔料、分散剤、水、およびグリセリンに
アルキレンオキサイドが1〜150モル付加したグリセ
リンのアルキレンオキサイド付加物を含有することを特
徴とする水性ボールペン用顔料インキ組成物。
6. A pigment ink composition for a water-based ballpoint pen, which comprises a pigment, a dispersant, water, and an alkylene oxide adduct of glycerin in which 1 to 150 mol of alkylene oxide is added to glycerin.
【請求項7】 グリセリンのアルキレンオキサイド付加
物を全組成物の0.5〜40重量%、顔料2〜30重量
%、分散剤0.1〜10重量%、および水40〜90重
量%含有してなる請求項6記載の水性ボールペン用顔料
インキ組成物。
7. An alkylene oxide adduct of glycerin is contained in an amount of 0.5 to 40% by weight of the total composition, 2 to 30% by weight of a pigment, 0.1 to 10% by weight of a dispersant, and 40 to 90% by weight of water. The pigment ink composition for water-based ballpoint pens according to claim 6.
【請求項8】 分散剤が水溶性高分子である請求項7記
載の水性ボールペン用顔料インキ組成物。
8. The aqueous pigment ink composition for a ballpoint pen according to claim 7, wherein the dispersant is a water-soluble polymer.
【請求項9】 トリメチロールプロパンのアルキレンオ
キサイド付加物、顔料分散剤、水溶性溶剤および水を含
有することを特徴とする水性ボールペン用顔料インキ組
成物。
9. An aqueous pigment ink composition for a ball-point pen, which comprises an alkylene oxide adduct of trimethylolpropane, a pigment dispersant, a water-soluble solvent and water.
【請求項10】 トリメチロールプロパンのアルキレン
オキサイドが1〜60モル付加したトリメチロールプロ
パンのアルキレンオキサイド付加物を全組成物の0.5
〜40重量%、顔料2〜30重量%、分散剤0.1〜1
0重量%および水40〜90重量%含有してなる請求項
9記載の水性ボールペン用顔料インキ組成物。
10. An alkylene oxide adduct of trimethylolpropane in which 1 to 60 mol of alkylene oxide of trimethylolpropane is added is added to 0.5% of the total composition.
-40% by weight, pigment 2-30% by weight, dispersant 0.1-1
The aqueous pigment ink composition for a ball-point pen according to claim 9, which comprises 0% by weight and 40 to 90% by weight of water.
【請求項11】 分散剤が水溶性高分子である請求項1
0記載の水性ボールペン用顔料インキ組成物。
11. The dispersant is a water-soluble polymer.
The pigment ink composition for water-based ballpoint pens according to 0.
JP21568492A 1991-08-21 1992-07-22 Pigment ink composition for aqueous ballpoint pens Expired - Fee Related JP2999632B2 (en)