JPH0428758Y2 - - Google Patents
Info
- Publication number
- JPH0428758Y2 JPH0428758Y2 JP1984008690U JP869084U JPH0428758Y2 JP H0428758 Y2 JPH0428758 Y2 JP H0428758Y2 JP 1984008690 U JP1984008690 U JP 1984008690U JP 869084 U JP869084 U JP 869084U JP H0428758 Y2 JPH0428758 Y2 JP H0428758Y2
- Authority
- JP
- Japan
- Prior art keywords
- printing ink
- transparent
- metal foil
- synthetic resin
- decorative sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
本考案は別製の木質板、繊維板、プラスチツク
板等に貼着されてテーブルトツプ、キヤビネツ
ト、間仕切板、壁装材等に加工される化粧シート
に関するものであり、深みのある金属調を具備
し、しかも堅牢性及び加工特性に富み、かつ比較
的廉価に得ることの出来る化粧シートを提供する
ものである。[Detailed description of the invention] The present invention relates to a decorative sheet that is attached to a separate wood board, fiberboard, plastic board, etc. and processed into table tops, cabinets, partition boards, wall coverings, etc. To provide a decorative sheet that has a deep metallic tone, is rich in fastness and processability, and can be obtained at a relatively low price.
金属調を呈する化粧シートには、絵柄入り鏡
板、ステンレス、銅・アルミ、スチール等の金属
板の表面にシルク刷り印刷層を形成したもの、あ
るいはアルミホイル表面にグラビア印刷による印
刷層を形成したもの等があるが、例えば絵柄入り
鏡板は高価であるうえに割れ易く、また金属板の
表面にシルク刷り印刷層を形成したものは、深み
のある金属調を呈するものが得難く、しかも高価
であり、更にアルミホイル表面にグラビア印刷層
を形成したものは、深みのある金属調を呈するも
のが得られないうえに表面の耐久性が乏しい等の
欠点がある。 Decorative sheets with a metallic look include mirror plates with patterns, those with a silk-screen printing layer formed on the surface of metal plates such as stainless steel, copper/aluminum, and steel, or those with a printing layer formed by gravure printing on the surface of aluminum foil. For example, mirror plates with patterns are expensive and break easily, and metal plates with a silk-printed layer formed on the surface have a deep metallic tone that is difficult to obtain and is also expensive. Furthermore, those in which a gravure printing layer is formed on the surface of aluminum foil have drawbacks such as not being able to obtain a deep metallic tone and having poor surface durability.
本考案は、透明もしくは半透明の合成樹脂製フ
イルムと、該フイルムの裏面に接着剤層を介して
貼着されている金属箔と、前記金属箔の裏面に接
着剤層を介して貼着されている硬化性合成樹脂含
浸紙もしくは合成ゴムラテツクス含浸紙とで構成
されている積層シートからなる化粧シートで、し
かも、前記透明もしくは半透明の合成樹脂製フイ
ルムの裏面と金属箔の表面とのうちの少なくとも
いずれか一方の面には、印刷用インキによる透明
もしくは半透明の全面あるいは部分的な印刷イン
キ層か、あるいは不透明な部分的印刷インキ層の
うちの少なくともいずれか１種類の印刷インキ層
が形成されており、透明もしくは半透明の合成樹
脂製フイルムの裏面と金属箔の表面との間に介在
されている前記接着剤層が、透明もしくは半透明
な接着剤で構成されている化粧シートとすること
により、深みのある金属色調を呈し、かつ堅牢性
及び加工性に富み、しかも比較的廉価に得ること
が出来、極めて優れた意匠性を有する化粧シート
を提供し得たものである。 The present invention consists of a transparent or translucent synthetic resin film, a metal foil attached to the back side of the film via an adhesive layer, and a metal foil attached to the back side of the metal foil via an adhesive layer. A decorative sheet consisting of a laminated sheet composed of curable synthetic resin-impregnated paper or synthetic rubber latex-impregnated paper, the back side of the transparent or translucent synthetic resin film and the front side of the metal foil. At least one of the following types of printing ink layer is formed on at least one of the surfaces: a transparent or translucent entire or partial printing ink layer made of printing ink, or an opaque partial printing ink layer. and the adhesive layer interposed between the back surface of the transparent or translucent synthetic resin film and the surface of the metal foil is composed of a transparent or translucent adhesive. As a result, it is possible to provide a decorative sheet that exhibits a deep metallic color tone, has excellent fastness and workability, can be obtained at a relatively low cost, and has an extremely excellent design.
また、特に、前記構成の化粧シートにおいて、
金属箔を、少なくともその表面にエンボス模様を
有する金属箔で構成することにより、該金属箔表
面が光の散乱作用を呈するので、化粧シートの表
面が平滑面であるにも拘らず具現される金属調の
深みが一層優れた化粧シートとすることが出来
る。 In particular, in the decorative sheet having the above configuration,
By composing the metal foil with a metal foil having an embossed pattern on at least its surface, the surface of the metal foil exhibits a light scattering effect, so that even though the surface of the decorative sheet is a smooth surface, the metal foil that can be realized is A decorative sheet with even better depth of tone can be obtained.
更に、透明もしくは半透明の合成樹脂製フイル
ムの裏面と金属箔の表面との間の接着剤層を、ウ
レタン樹脂による透明な接着剤層で構成すること
により、特に耐熱性に優れた性質を有する化粧シ
ートとなし得るばかりか、プレス成形で本考案の
化粧シートを得る際のプレス加工性に優れたもの
となし得るものである。 Furthermore, by constructing the adhesive layer between the back side of the transparent or translucent synthetic resin film and the front side of the metal foil with a transparent adhesive layer made of urethane resin, it has particularly excellent heat resistance properties. Not only can it be used as a decorative sheet, but it can also be made into a sheet with excellent press workability when the decorative sheet of the present invention is obtained by press molding.
また、透明もしくは半透明の合成樹脂製フイル
ムの裏面と金属箔の表面とのうちの少なくともい
ずれか一方の面に形成されている印刷インキ層
が、不透明な印刷用インキによる部分的な印刷イ
ンキ層で構成されるか、あるいは、不透明な印刷
用インキによる部分的な印刷インキ層と透明もし
くは半透明をなす印刷用インキによる印刷インキ
層との組み合わせで構成される場合には、金属光
沢が発現される部分と、金属光沢が隠蔽される部
分とが共に存在するため、極めて斬新な意匠特性
を具現する化粧シートとなし得るものである。 In addition, the printing ink layer formed on at least one of the back side of the transparent or translucent synthetic resin film and the front side of the metal foil is a partial printing ink layer made of opaque printing ink. or a combination of a partial printing ink layer made of opaque printing ink and a printing ink layer made of transparent or translucent printing ink, metallic luster is developed. Since there are both parts where the metallic luster is hidden and parts where the metallic luster is concealed, it can be made into a decorative sheet that embodies extremely innovative design characteristics.
次に、本考案の金属調を呈する化粧シートにつ
いて、その代表的な構成の具体例を図面実施例で
説明する。 Next, a specific example of a typical configuration of the metallic-looking decorative sheet of the present invention will be described with reference to drawings and examples.
第１図に符号１で表示される本考案の実施例品
たる金属調を呈する化粧シートは、ウレタン樹脂
をベヒクルとする印刷用インキによる不透明な印
刷インキ層m1が裏面に形成されている厚さ25μの
ポリエステル製フイルム（フイルム部分の商品
名：東レルミラー）２の前記印刷インキ層m1面
と、厚さ30μのアルミニウム箔３の表面とが、ウ
レタン系接着剤（商品名：セイカボンドE295）
30ｇ／m2からなる透明な接着剤層４を介して貼着
されており、かつ、前記アルミニウム箔３の裏面
には、ウレタン系接着剤（商品名：セイカボンド
E295）15ｇ／m2からなる接着剤層５を介して、
245ｇ／m2のパルプ抄造紙に含浸率30％にSBRラ
テツクスを含浸、固化せしめた厚さ400μ、350
ｇ／m2のSBRラテツクス含浸紙６が貼着、積層
された積層シートによつて構成されているもので
ある。 A decorative sheet with a metallic appearance, which is an example product of the present invention and is denoted by reference numeral 1 in FIG. One side of the printing ink layer m of the 25μ thick polyester film (product name of the film part: Torel Mirror) 2 and the surface of the 30μ thick aluminum foil 3 are bonded with a urethane adhesive (product name: Seikabond E295).
It is attached via a transparent adhesive layer 4 of 30 g/m 2 , and the back side of the aluminum foil 3 is coated with a urethane adhesive (trade name: Seikabond).
E295) Through an adhesive layer 5 consisting of 15 g/ m2 ,
245g/ m2 pulp paper impregnated with SBR latex at an impregnation rate of 30% and solidified to a thickness of 400μ, 350
It is composed of a laminated sheet on which SBR latex impregnated paper 6 of g/m 2 is adhered and laminated.
尚、前記化粧シート１は、印刷インキ層m1が
印刷されているポリエステル製フイルム２とアル
ミニウム箔３とを接着剤層４をなす接着剤でドラ
イラミネートし、得られた積層体のアルミニウム
箔３面に、更に別製の固化処理済みのSBRラテ
ツクス含浸紙６を、接着剤層５をなす接着剤でド
ライラミネートし、養生、硬化させた後、続いて
鏡面盤を前記得られた積層シートのポリエステル
製フイルム２面に乗せ、熱圧プレスすることによ
つて成形されたものであり、得られた化粧シート
は、表面が保護層たるポリエステル樹脂層で被覆
され、しかもアルミニウム鏡面に部分的な絵柄が
形成された斬新な意匠間隔の金属調を呈するもの
である。 The decorative sheet 1 is made by dry laminating the polyester film 2 on which the printing ink layer m 1 is printed and the aluminum foil 3 with an adhesive forming the adhesive layer 4, and the aluminum foil 3 of the resulting laminate. Further, a separately made hardened SBR latex impregnated paper 6 is dry-laminated on the surface with an adhesive forming the adhesive layer 5, and after curing and curing, a mirror surface plate is then applied to the obtained laminated sheet. It is molded by placing it on two sides of a polyester film and pressing under hot pressure.The surface of the obtained decorative sheet is covered with a polyester resin layer that serves as a protective layer, and it also has a partial pattern on the aluminum mirror surface. It has a novel design with a metallic look.
第２図に符号７で表示される本考案の別の実施
例品たる金属調を呈する化粧シートは、ウレタン
樹脂をベヒクルとする印刷用インキによる不透明
な印刷インキ層m2が裏面に形成されている厚さ
25μのポリエステル製フイルム（フイルム部分の
商品名：東レルミラー）８の前記印刷インキ層
m2面と、厚さ30μのアルミニウム箔に微細な絹目
のエンボス加工を全体に施すことによつて得られ
たエンボス模様を有するアルミニウム箔９の表面
とが、ウレタン系接着剤（商品名：セイカボンド
E295）８ｇ／m2からなる透明な接着剤層１０を
介して貼着されており、かつ、前記アルミニウム
箔９の裏面には、ウレタン系接着剤（商品名：セ
イカボンドE295）15ｇ／m2からなる接着剤層１
１を介して、245ｇ／m2のパルプ抄造紙に含浸率
30％にSBRラテツクスを含浸、固化せしめた厚
さ400μ、350ｇ／m2のSBRラテツクス含浸紙１２
が貼着、積層された積層シートによつて構成され
ているものである。 Another embodiment of the present invention, designated by reference numeral 7 in FIG. 2, is a decorative sheet exhibiting a metallic appearance. An opaque printing ink layer m 2 of printing ink using a urethane resin as a vehicle is formed on the back surface. thickness
The printing ink layer of 25μ polyester film (product name of film part: Torel Mirror) 8
m 2 side and the surface of the aluminum foil 9, which has an embossed pattern obtained by applying a fine texture embossing process to the entire aluminum foil with a thickness of 30 μm, are bonded with urethane adhesive (product name: Seikabond
E295) 8 g/m 2 of a transparent adhesive layer 10, and the back side of the aluminum foil 9 is coated with a urethane adhesive (trade name: Seikabond E295) of 15 g/m 2 Adhesive layer 1
1, impregnation rate into pulp paper making of 245g/ m2
SBR latex-impregnated paper 12 with a thickness of 400 μ and 350 g/m 2 which is 30% SBR latex impregnated and solidified.
It is composed of laminated sheets that are adhered and laminated.
尚、前記化粧シート７は、前述の化粧シート１
と同様の成形手順に従つて得られたものである
が、表面の保護層たるポリエステル樹脂層表面は
平滑面であり、しかも前記ポリエステル樹脂層を
通して透視されるアルミニウム箔９の表面にはエ
ンボス加工による光の散乱作用が呈せられ、深み
のあるトーンが現出されており、かつ、この光の
散乱作用は印刷インキ層m2で隠蔽される部分も
存在するため、これらの条件が相伴つて、極めて
斬新な意匠を発現する金属調を呈するものであ
る。 Note that the decorative sheet 7 is similar to the decorative sheet 1 described above.
This was obtained by following the same molding procedure as above, but the surface of the polyester resin layer serving as the surface protective layer was smooth, and the surface of the aluminum foil 9 that could be seen through the polyester resin layer was embossed. A light scattering effect is exhibited, creating a deep tone, and there are also areas where this light scattering effect is hidden by the printing ink layer m2 , so these conditions are combined, It has a metallic appearance that gives it an extremely innovative design.
また、図示実施例においては印刷インキ層m1
及びm2として、いずれもポリエステル製フイル
ムの裏面に不透明な印刷インキによつて部分的に
形成されている印刷インキ層の例を示したが、印
刷インキによる印刷インキ層は、透明もしくは半
透明の合成樹脂製フイルムの裏面と金属箔の表面
との少なくともいずれか一方に形成されていれば
良く、またこの印刷インキ層が透明もしくは半透
明をなすものであれば必ずしも部分的に形成され
ている印刷インキ層である必要はなく、その全面
に形成されていても良く、勿論、透明な印刷イン
キ層と不透明な部分的に設けられている印刷イン
キ層との組み合わせであつても良い。 In addition, in the illustrated embodiment, the printing ink layer m 1
and m 2 are examples of printing ink layers partially formed with opaque printing ink on the back side of polyester films. It is sufficient that the printing ink layer is formed on at least one of the back side of the synthetic resin film and the front side of the metal foil, and is not necessarily formed partially if the printing ink layer is transparent or translucent. It does not have to be an ink layer, and may be formed on the entire surface, or of course may be a combination of a transparent printing ink layer and an opaque printing ink layer provided partially.
本考案の金属調を呈する化粧シートは叙上の通
りの構成からなるものであり、透明または半透明
の合成樹脂製フイルムとしては、ポリエステルフ
イルム、ボリ塩化ビニルフイルム、アクリルニト
リルフイルム、ポリカーボネートフイルム、ポリ
エチレンやポリプロピレン等のポリオレフイン系
樹脂フイルム等が好ましいが、この合成樹脂製フ
イルムは化粧シートの表面保護層たる合成樹脂層
となるものであるので、耐薬品性、耐光性、耐擦
傷性、耐溶剤性等の面から、及び汎用性の面から
ポリエステルフイルムが最も好ましい。 The metallic-looking decorative sheet of the present invention is constructed as described above, and transparent or translucent synthetic resin films include polyester film, polyvinyl chloride film, acrylonitrile film, polycarbonate film, and polyethylene film. A polyolefin resin film such as or polypropylene is preferable, but since this synthetic resin film serves as a synthetic resin layer that serves as a surface protection layer of the decorative sheet, it has good chemical resistance, light resistance, scratch resistance, and solvent resistance. Polyester film is most preferable from the viewpoint of versatility and the like.
また金属箔としては、アルミニウム、ステンレ
ススチール、銅、亜鉛等の金属光沢を有する通常
30μ程度の厚みのものが利用される。 In addition, as metal foil, ordinary materials with metallic luster such as aluminum, stainless steel, copper, and zinc are used.
A material with a thickness of about 30μ is used.
印刷インキ層は、これが透明もしくは半透明の
印刷インキ層の場合は、染料や超微細粒子顔料を
色剤とする印刷用インキで形成され得るものであ
る。 When the printing ink layer is a transparent or translucent printing ink layer, it can be formed from a printing ink containing a dye or an ultrafine particle pigment as a coloring agent.
透明もしくは半透明の合成樹脂製フイルムと金
属箔との接着剤としては、これが硬化された場合
に透明もしくは半透明の接着剤層となるものであ
れば如何なるものでも利用し得るが、その成形工
程中にプレス工程が含まれるので、ウレタン樹脂
が良く、なかでも耐熱性や加工特性の点からポリ
エステルポリオールからなる主剤にイソシアネー
ト硬化剤を利用した接着剤を利用するのが最も好
ましい。 As the adhesive between the transparent or translucent synthetic resin film and the metal foil, any adhesive can be used as long as it forms a transparent or translucent adhesive layer when cured, but the forming process Since it involves a pressing process, urethane resins are preferable, and from the viewpoint of heat resistance and processability, it is most preferable to use adhesives that use an isocyanate curing agent as a main ingredient made of polyester polyol.
また、固化されている合成樹脂含浸紙あるいは
同じく固化されている合成ゴムラテツクス含浸紙
は、本考案の化粧シートに厚みを具備せしめるも
のであり、別製の木質板、繊維板、プラスチツク
板等に貼着される際のそれらの板の表面の凹凸を
吸収する作用を奏し、かつ化粧シートの補強をな
すもので、化粧シートの表面から仮令傷が入るよ
うなことがあつても、その傷が、得られた化粧板
の内部にまで侵入してゆくという不測の事態を阻
止するものであり、例えば、パルプ紙に不飽和ポ
リエステル樹脂、ジアリルフタレート樹脂、エポ
キシ樹脂、フエノール樹脂、ウレタン樹脂、メラ
ミン樹脂、あるいはこれらの樹脂の混合樹脂等か
らなる硬化性合成樹脂、またはSBR，CR，BR，
NR，NBR等のラテツクスを含浸率20〜50％程
度に含浸せしめ、これを固化させて得られた80〜
400ｇ／m3、好ましくは200〜350ｇ／m3程度のも
のが使用される。 In addition, the hardened synthetic resin-impregnated paper or the similarly hardened synthetic rubber latex-impregnated paper gives thickness to the decorative sheet of the present invention, and can be applied to a separate wooden board, fiberboard, plastic board, etc. It has the effect of absorbing the unevenness of the surface of these boards when worn, and also reinforces the decorative sheet, so even if scratches occur from the surface of the decorative sheet, the scratches will be removed. This prevents the unexpected situation of intrusion into the interior of the obtained decorative board. For example, unsaturated polyester resin, diallyl phthalate resin, epoxy resin, phenol resin, urethane resin, melamine resin, etc. Alternatively, curable synthetic resins made of mixed resins of these resins, or SBR, CR, BR, etc.
80~ obtained by impregnating latex such as NR, NBR to an impregnation rate of about 20~50% and solidifying it.
About 400 g/m 3 , preferably 200 to 350 g/m 3 is used.
尚、合成樹脂含浸率（％）は、
含浸紙全体の重量−原紙の重量／含浸紙全体の重量×
100
に従つて計算した値である。 The synthetic resin impregnation rate (%) is calculated as follows: weight of the entire impregnated paper - weight of the base paper / weight of the entire impregnated paper x
100.
金属箔と、固化されている熱硬化性合成樹脂含
浸紙あるいは同じく固化されている合成ゴムラテ
ツクス含浸紙との接着剤は、金属箔と合成樹脂含
浸紙との積層体が高温圧着に耐え得るように、主
剤がポリエステルポリオールで構成されこれにイ
ソシアネート系硬化剤が添加されているウレタン
系接着剤が最も好適である。 The adhesive between the metal foil and the hardened thermosetting synthetic resin-impregnated paper or the hardened synthetic rubber latex-impregnated paper is such that the laminate of the metal foil and the synthetic resin-impregnated paper can withstand high-temperature pressure bonding. The most suitable adhesive is a urethane adhesive whose main ingredient is a polyester polyol to which an isocyanate curing agent is added.
金属箔に所望により施されるエンボス加工は、
ヘアーライン加工やサンドブラスト加工等の深さ
数μ程度のものから、金属箔と合成樹脂含浸紙と
の積層体にエンボス加工を施すことによつて形成
された深さ数mmもに達するエンボス模様まで含ま
れるが、金属箔と合成樹脂含浸紙との積層体を得
る際の接着工程で、合成樹脂含浸紙の表面の凹凸
が金属箔表面に到達することによつて金属箔の表
面に形成されるエンボス模様の場合もある。 The embossing process applied to metal foil as desired is
This includes embossed patterns that are several microns deep, such as hairline processing and sandblasting, to embossed patterns that are several millimeters deep, formed by embossing a laminate of metal foil and synthetic resin-impregnated paper. Emboss is formed on the surface of the metal foil when the irregularities on the surface of the synthetic resin-impregnated paper reach the surface of the metal foil during the adhesion process when obtaining a laminate of metal foil and synthetic resin-impregnated paper. Sometimes it is a pattern.
本考案の金属調を呈する化粧シートは以上の通
りの構成からなるもので、別製の木質板、繊維
板、プラスチツク板等に貼着されてテーブルトツ
プ、キヤビネツト、間仕切板、壁装材等に加工さ
れるものであるが、その表面が透明ないし半透明
の合成樹脂製フイルムで被覆され、該合成樹脂製
フイルムによつて構成されている合成樹脂層を通
して金属箔表面の印刷模様が視認されるので、深
みのある意匠性に富む金属調が表現され、しかも
堅牢性に富み、かつ金属性を表現する部分が厚み
の小さい箔で構成されているので、化粧シートの
取扱い工程中にワレやカケの発生が無く、曲げ加
工時の賦形特性にも優れ、加工後に形状が復元し
てしまうというようなことも無く、更には従来の
この種の化粧シートはエンドレス状に巻き取り保
管すると巻き癖が付くことによる取扱い性が悪い
ことが欠点であつたが、本考案の化粧シートは圧
着、押し曲げ等の操作でこの巻き癖を容易に直す
ことが出来るので、取扱い性が優れている等の作
用、効果をも奏するものである。 The metallic-looking decorative sheet of the present invention has the above-mentioned structure, and can be attached to a separate wooden board, fiberboard, plastic board, etc. to be used as a table top, cabinet, partition board, wall covering material, etc. The surface of the metal foil is covered with a transparent or translucent synthetic resin film, and the printed pattern on the surface of the metal foil is visible through the synthetic resin layer made of the synthetic resin film. As a result, a metallic tone with a deep and rich design is expressed, and it is also highly durable, and since the part expressing the metallicity is made of thin foil, there is no possibility of cracking or chipping during the handling process of the decorative sheet. There is no occurrence of this kind of decorative sheet, it has excellent shaping properties during bending, and there is no possibility that the shape will be restored after processing.Furthermore, conventional decorative sheets of this type tend to curl if they are rolled up endlessly and stored. However, the decorative sheet of the present invention has excellent handling properties because it can easily correct the curling tendency by pressing, pressing, bending, etc. It also has functions and effects.
第１図、第２図は本考案の金属調を呈する化粧
シートのそれぞれ別の実施例品を示す模型的断面
図である。
１……金属調を呈する化粧シート、２……透明
な合成樹脂製フイルムたるポリエステル製フイル
ム、３……金属箔たるアルミニウム箔、４……接
着剤層、５……接着剤層、６……固化されている
硬化性合成樹脂もしくは合成ゴムラテツクス含浸
紙、m1……印刷インキ層。
FIGS. 1 and 2 are schematic cross-sectional views showing different examples of decorative sheets exhibiting a metallic appearance according to the present invention. DESCRIPTION OF SYMBOLS 1... Decorative sheet exhibiting a metallic tone, 2... Polyester film which is a transparent synthetic resin film, 3... Aluminum foil which is a metal foil, 4... Adhesive layer, 5... Adhesive layer, 6... Paper impregnated with hardened curable synthetic resin or synthetic rubber latex, m 1 ...Printing ink layer.
Claims (1)
裏面と金属箔の表面とが透明もしくは半透明の
ウレタン系の接着剤層を介して貼着されてお
り、かつ前記金属箔の裏面には、固化されてい
る硬化性合成樹脂含浸紙あるいは同じく固化さ
れている合成ゴムラテツクス含浸紙がウレタン
系の接着剤により貼着、積層されている積層シ
ートからなり、しかも前記透明もしくは半透明
の合成樹脂製フイルムの裏面と金属箔の表面と
のうちの少なくともいずれか一方の面には、透
明もしくは半透明をなす印刷インキによる全面
もしくは部分的な印刷インキ層か、あるいは不
透明をなす印刷用インキによる部分的な印刷イ
ンキ層のうちの少なくともいずれか１種類の印
刷インキ層が形成されていることを特徴とする
金属調を呈する化粧シート。 (2) 金属箔が、少なくともその表面にエンボス模
様をする金属箔である実用新案登録請求の範囲
第１項記載の金属調を呈する化粧シート。[Claims for Utility Model Registration] (1) The back side of a transparent or semi-transparent synthetic resin film and the front side of a metal foil are attached via a transparent or semi-transparent urethane adhesive layer, and The back side of the metal foil is made of a laminated sheet in which hardened curable synthetic resin-impregnated paper or hardened synthetic rubber latex-impregnated paper is adhered and laminated with a urethane adhesive, and the transparent Alternatively, at least one of the back side of the translucent synthetic resin film and the front side of the metal foil is coated with a full or partial printing ink layer of transparent or translucent printing ink, or an opaque printing ink layer. 1. A decorative sheet exhibiting a metallic appearance, characterized in that a printing ink layer of at least one type of partial printing ink layers made of eggplant printing ink is formed. (2) A decorative sheet exhibiting a metallic tone according to claim 1, wherein the metal foil is a metal foil having an embossed pattern on at least its surface.