JPH039019B2 - - Google Patents
Info
- Publication number
- JPH039019B2 JPH039019B2 JP13743285A JP13743285A JPH039019B2 JP H039019 B2 JPH039019 B2 JP H039019B2 JP 13743285 A JP13743285 A JP 13743285A JP 13743285 A JP13743285 A JP 13743285A JP H039019 B2 JPH039019 B2 JP H039019B2
- Authority
- JP
- Japan
- Prior art keywords
- container
- adhesive
- layer
- resin layer
- easy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は易開封性包装容器に係わり、更に詳し
くは容器を破壊することなく容易に開封しうる易
開封性包装容器に関する。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to an easy-to-open packaging container, and more particularly to an easy-to-open packaging container that can be easily opened without destroying the container.
包装容器の重要な機能の一つとして製品の製造
及び流通などの過程で内容物を完全に保護するに
は充分な封着強度を有し、且つ、内容物の取り出
しに当つては基材を破壊することなくその封着部
を容易に開封し得る易開封性があげられる。
One of the important functions of packaging containers is to have sufficient sealing strength to completely protect the contents during product manufacturing and distribution processes, and to ensure that the base material is not damaged when the contents are removed. An example of this is ease of opening, in which the sealed portion can be easily opened without breaking the seal.
従来からこの要求を満足させる為に容器基材上
に基材から剥離可能であり且つ膜破断しやすい熱
接着層を設け、熱接着層の剥離及び膜破断により
ヒートシール部を開封し得るように構成する方法
が採用されている。 Conventionally, in order to satisfy this requirement, a heat-adhesive layer that can be peeled from the base material and easily breaks is provided on the container base material, and the heat-sealed part can be opened by peeling off the heat-adhesive layer and breaking the film. A method of configuring is used.
しかしながら、この方法によつて密封した易開
封性容器には、膜破断がどの方向に走つて生ずる
のか不安であり、不必要な方向に膜破断し、基材
に設けられた印刷層の一部が熱接着層と共に基材
より引剥されて容器の美感が損なわれる欠点があ
つた。 However, with easy-to-open containers sealed using this method, there is uncertainty as to which direction the film will break, and the film may break in an unnecessary direction, causing part of the printed layer on the base material to break. There was a drawback that the container was peeled off from the base material together with the thermal adhesive layer, impairing the aesthetic appearance of the container.
そこで本発明が解決しようとする問題点は開封
時に熱接着性樹脂層が不必要な方向に膜破断し、
基材に設けられた印刷層の一部が熱接着性樹脂層
と共に基材より引剥されて容器の美感が損なわれ
ることのない易開封性包装容器を提供することに
ある。
Therefore, the problem that the present invention aims to solve is that the thermally adhesive resin layer breaks in an unnecessary direction when the package is opened.
To provide an easily openable packaging container in which a part of a printed layer provided on a base material is not peeled off from the base material together with a thermoadhesive resin layer and the aesthetic appearance of the container is not impaired.
本発明者は上記の問題点を解決すべく研究の結
果、内面が熱接着性樹脂層9である1対の容器基
材3を、前記熱接着性樹脂層9を対向させて熱接
着してなる容器口部の開放部の密封のため、対向
する熱接着性樹脂層9に1対の接着部6a,6bを
有し、さらに前記1対の容器基材3の少なくとも
一方の前記接着部と同じ幅もしくは前記幅より狭
い幅の部分だけを除いて、前記容器基材3と前記
熱接着性樹脂層9との間にアンカー剤印刷層7を
設けることにより、熱接着性樹脂層の膜破断がア
ンカー剤印刷層が設けられていない領域の端縁に
沿つて生じそれ以外に破断線が走ることがないも
のを形成し得ることを見い出し、かかる知見にも
とづいて本発明を完成したものである。
As a result of research to solve the above problems, the inventor of the present invention thermally bonded a pair of container base materials 3 each having a heat-adhesive resin layer 9 on the inner surface with the heat-adhesive resin layer 9 facing each other. In order to seal the open part of the container mouth, the opposing thermoadhesive resin layer 9 has a pair of adhesive parts 6a and 6b, and the adhesive part of at least one of the pair of container base materials 3 and By providing an anchor agent printed layer 7 between the container base material 3 and the thermally adhesive resin layer 9, excluding only the portion of the same width or narrower than the width, the membrane rupture of the thermally adhesive resin layer is prevented. The inventors have discovered that it is possible to form a fracture line that occurs along the edge of the area where the anchor agent printing layer is not provided, and does not run anywhere else, and based on this knowledge, the present invention has been completed. .
易開封包装容器は内面が熱接着性樹脂層9であ
る1対の容器基材3を、前記熱接着性樹脂層9を
対向させて熱接着してなる容器口部の開放部をも
つ包装容器において、前記容器口部の開放部は、
対向する前記熱接着性樹脂層9に1対の接着部
6a,6bを有し、さらに前記1対の容器基材3の
少なくとも一方の前記接着部と同じ幅もしくは前
記幅より狭い幅の部分だけを除いて、前記容器基
材3と前記熱接着性樹脂層9との間にアンカー剤
印刷層7を有するものである。 The easy-to-open packaging container has an opening at the mouth of the container, which is made by thermally bonding a pair of container base materials 3 each having a heat-adhesive resin layer 9 on the inner surface, with the heat-adhesive resin layers 9 facing each other. In the above, the opening part of the container mouth part is
A pair of adhesive parts on the opposing thermally adhesive resin layer 9
6a, 6b, and further excludes only a portion having the same width as or narrower than the adhesive portion of at least one of the pair of container base materials 3, and the container base material 3 and the thermal adhesive resin. An anchor agent printed layer 7 is provided between the layer 9 and the layer 9.
本発明に係る容器の形態は蓋体と容器本体とよ
りなる成形容器のみならず袋体でも良い。尚、上
記において、接着部とは例えば成形容器の場合は
フランジ面と該フランジ面と相対する蓋体下面領
域であり、袋体の場合は口部周辺において相対す
る1対の包材内面領域である。 The form of the container according to the present invention may be not only a molded container consisting of a lid and a container body, but also a bag. In addition, in the above, the adhesive part is, for example, in the case of a molded container, the flange surface and the lower surface area of the lid opposite to the flange surface, and in the case of a bag, it is the inner surface area of a pair of packaging materials facing each other around the opening. be.
以下、図面を参照しながら本発明につき説明す
る。 Hereinafter, the present invention will be explained with reference to the drawings.
第1図は本発明に係る易開封性包装容器11を
示している。 FIG. 1 shows an easy-to-open packaging container 11 according to the present invention.
容器本体1と蓋体2を構成している内面が熱接
着性樹脂層9である1対の容器基材3を、前記熱
接着性樹脂層9を対向させて熱接着してなる容器
口部の開放部の密封のため、対向する前記熱接着
性樹脂層9に1対の接着部6a,6bを有し、さら
に前記1対の容器基材3の少なくとも一方の前記
接着部と同じ幅もしくは前記幅より狭い幅の部分
だけを除いて、前記容器基材3と前記熱接着性樹
脂層9との間にイソシアネート系、イミン系、チ
タン系のアンカー剤が塗布されたアンカー剤印刷
層7が設けられている。 A container opening formed by thermally bonding a pair of container base materials 3, which constitute a container body 1 and a lid 2, and whose inner surfaces are a thermoadhesive resin layer 9, with the thermoadhesive resin layers 9 facing each other. In order to seal the open portion of the container, the thermally adhesive resin layer 9 facing each other has a pair of adhesive parts 6a and 6b, and further has a width equal to or equal to that of the adhesive part of at least one of the pair of container base materials 3. An anchor agent printed layer 7 coated with an isocyanate-based, imine-based, or titanium-based anchor agent is provided between the container base material 3 and the heat-adhesive resin layer 9, except for only the portion narrower than the width. It is provided.
第2図は第1図示の容器の開封状態を示してお
り、アンカー剤の存在しない接着領域の熱接着性
樹脂部分が蓋体2より剥離して容易に開封するこ
とができる。 FIG. 2 shows the container shown in FIG. 1 in an unsealed state, in which the heat-adhesive resin portion in the adhesive area where no anchoring agent is present is peeled off from the lid 2 and can be easily opened.
本発明に係る易開封性包装容器においては、熱
接着性樹脂層の破断がアンカー剤印刷層が設けら
れていない領域の端縁に沿つて生じそれ以外に破
断線が走ることがないので熱接着性樹脂層の破断
もしくは剥離が印刷模様が施こされている領域に
迄及んで容器壁の美感が損なわれることはない。 In the easy-open packaging container according to the present invention, the thermal adhesive resin layer breaks along the edge of the area where the anchor agent printing layer is not provided, and there is no other break line. The aesthetic appearance of the container wall will not be impaired due to breakage or peeling of the adhesive resin layer extending to the area where the printed pattern is applied.
而して、本発明に係る易開封性包装容器におい
て、容器基材3としてはポリエチレン、ポリプロ
ピレン、ポリアミド、ポリエステル、ポリ塩化ビ
ニル、ポリスチレン、アクリル樹脂、ポリビニル
アルコール、ポリ塩化ピニリデン、ポリカーポネ
ート、セルロースプラスチツク等のプラスチツク
フイルム、セロハン、アルミ箔の単体もしくはそ
れらの積層フイルムを使用することができる。 In the easy-to-open packaging container according to the present invention, the container base material 3 may be polyethylene, polypropylene, polyamide, polyester, polyvinyl chloride, polystyrene, acrylic resin, polyvinyl alcohol, polypinylidene chloride, polycarbonate, or cellulose. A single plastic film such as plastic, cellophane, or aluminum foil, or a laminated film thereof can be used.
次に本発明に係る易開封性包装容器において、
熱接着性樹脂層としてはポリエチレン、ポリプロ
ピレン、ポリアミド、アイオノマー、エチレン−
酢酸ビニル共重合体等を使用することができる。 Next, in the easy-to-open packaging container according to the present invention,
The thermoadhesive resin layer can be made of polyethylene, polypropylene, polyamide, ionomer, ethylene-
Vinyl acetate copolymers and the like can be used.
尚、熱接着性樹脂層の厚さは膜破断可能な10μ
ないし30μ程度であるのが望ましい。 In addition, the thickness of the thermal adhesive resin layer is 10μ, which allows the film to break.
It is desirable that the thickness be about 30 μm to 30 μm.
本発明に係る易開封性包装容器において、開封
容易性の点から、容器口部の開放部の外方に非接
着部を設けるのが望ましい。 In the easy-open packaging container according to the present invention, from the viewpoint of ease of opening, it is desirable to provide a non-adhesive portion outside the opening of the container mouth.
尚、本発明に係る易開封性包装容器において、
ヒートシール巾とアンカー剤を施塗しない領域の
巾とが全く同一であると極めて剥離しやすくなる
のでヒートシール巾の方をアンカー剤を塗工しな
い領域の巾よりも若干広くするのが望ましい。 In addition, in the easy-to-open packaging container according to the present invention,
If the heat seal width and the width of the area to which no anchor agent is applied are exactly the same, peeling will occur extremely easily, so it is desirable that the heat seal width is slightly wider than the width of the area to which no anchor agent is applied.
本発明において、接着部に相当する領域の少な
くとも一方の領域内を除いて設けられたアンカー
剤印刷層は開封容易な構造を形成すると共にアン
カー剤印刷層が設けられていない領域の端縁に沿
つて生ぜしめ、それ以外に熱接着性樹脂層の破断
線を走らせない作用をするものである。
In the present invention, the anchor agent printed layer provided except in at least one region corresponding to the adhesive part forms a structure that is easy to open, and the anchor agent printed layer is provided along the edge of the region where the anchor agent printed layer is not provided. In addition to this, it also acts to prevent the break line of the heat-adhesive resin layer from running.
実施例 1
ポリエステル#12にビニル樹脂系インキ(大日
本インキ(株)製、CVL)を使用して美麗な絵柄を
印刷すると同時にシール部に相当する領域を除い
た領域全面にイソシアネート系アンカー剤をパー
トコートした。その後に押出しラミネート法によ
りポリエチレン樹脂(MI=40、SP=0.918)を
30μ押出しラミネートしてポリエステル#12/絵
柄印刷層/アンカー剤パートコート層/ポリエチ
レン30μの層構成の積層包材を製造した。次いで
この包材を用いて包装袋を作成した。
Example 1 Beautiful designs were printed on polyester #12 using vinyl resin ink (Dainippon Ink Co., Ltd., CVL), and at the same time an isocyanate anchoring agent was applied to the entire area except for the area corresponding to the seal area. Part coated. After that, polyethylene resin (MI=40, SP=0.918) was applied using the extrusion lamination method.
A 30μ extrusion lamination was performed to produce a laminated packaging material having a layer structure of polyester #12/design printing layer/anchor agent part coat layer/polyethylene 30μ. Next, a packaging bag was created using this packaging material.
得られた包装袋につき開封試験を行なつた結果
包装袋の印刷が施こされた部分を損壊することな
く容易に開封することができた。又、アンカー剤
のない部分のポリエステルとポリエチレンの層間
の剥離強度は40〜60gr/15mm巾、アンカー剤の
ある部分のポリエステルとポリエチレンの層間の
剥離強度は200gr/mm巾以上、ポリエチレン層
相互間のヒートシール強度は800〜1000gr/15
mm巾であつた。 An opening test was conducted on the resulting packaging bag, and the result was that it could be easily opened without damaging the printed portion of the packaging bag. In addition, the peel strength between the polyester and polyethylene layers in the area without the anchor agent is 40 to 60 gr/15 mm width, the peel strength between the polyester and polyethylene layers in the area with the anchor agent is 200 gr/mm width or more, and the peel strength between the polyethylene layers is 40 to 60 gr/15 mm width. Heat seal strength is 800~1000gr/15
It was mm wide.
実施例 2
ポリエステル#300の片面にニトロセルロース
−ポリアミド系インキ(東洋インキ(株)製、GNC
−X)を使用して美麗な絵柄の印刷を施し、イン
ラインで上記ポリエステルの他面にシール部に相
当する領域を除いて上記絵柄に見当を合わせてイ
ミン系アンカー剤をパートコートした。その後に
上記ポリエステルの印刷を施こした側にポリ塩化
ビニリデン樹脂コート延伸ポリプロピレン#20
(ダイセル(株)製、KOP#20)をドライラミネート
し、その後に上記ポリエステルのアンカー剤をパ
ートコートした側に押出しラミネート法によりポ
リエチレン(MI=4、SP=0.918)を20μコート
してポリ塩化ビニリデン樹脂コート延伸ポリプロ
ピレン#20/接着層/絵柄印刷層/ポリエステル
#300/アンカー剤パートコート層/ポリエステ
ル20μの層構成の積層包材を製造した。次いで、
この包材を用いて包装袋を作成した。Example 2 Nitrocellulose-polyamide ink (manufactured by Toyo Ink Co., Ltd., GNC) was applied to one side of polyester #300.
-X) was used to print a beautiful pattern, and an imine-based anchor agent was part-coated in-line on the other side of the polyester in register with the pattern except for the area corresponding to the seal portion. Then, the side printed with the above polyester is coated with polyvinylidene chloride resin and stretched polypropylene #20.
(manufactured by Daicel Corporation, KOP #20), and then coated with 20μ of polyethylene (MI = 4, SP = 0.918) by extrusion lamination method on the side that was part-coated with the above polyester anchor agent, and then polychlorinated. A laminated packaging material having a layer structure of vinylidene resin coated stretched polypropylene #20/adhesive layer/design printing layer/polyester #300/anchor agent part coat layer/polyester 20μ was produced. Then,
A packaging bag was created using this packaging material.
得られた包装袋につき開封試験を行なつた結
果、包装袋の印刷が施こされた部分を損壊するこ
となく容易に開封することができた。又、アンカ
ー剤のない領域のポリエステル/ポリエチレン間
の層間の剥離強度は40〜50gr/15mm巾、アンカ
ー剤を設けた領域のポリエステル/ポリエチレン
間の層間の剥離強度は150gr/15mm巾、ポリエ
チレン層相互間のヒートシール強度は500〜600g
r/15mm巾であつた。 An opening test was conducted on the resulting packaging bag, and as a result, it was found that the packaging bag could be easily opened without damaging the printed portion. In addition, the interlayer peel strength between polyester/polyethylene in the area without anchoring agent is 40 to 50gr/15mm width, and the interlayer peeling strength between polyester/polyethylene in the area with anchoring agent is 150gr/15mm width, between polyethylene layers. The heat seal strength between is 500~600g
It was r/15mm wide.
以上、詳記した通り、本発明に係る易開封性包
装容器は、容易に開封できると共に熱接着性樹脂
層9の膜破断がアンカー剤印刷層が設けられてい
ない領域の両方の端縁に沿つてのみ生ぜしめ、そ
れ以外に破断線が走ることがないので、熱接着性
樹脂層9の破断もしくは剥離がアンカー剤を印刷
していない部分だけで、それ以外の不必要な部
分、方向に及ぶことはないので、容器を開封する
とき剥がれて汚くなり容器の美感が損なわれるこ
とはないという利点を有するものである。
As described above in detail, the easy-open packaging container according to the present invention can be easily opened, and the film rupture of the thermoadhesive resin layer 9 occurs along both edges of the area where the anchor agent printing layer is not provided. Since the thermal adhesive resin layer 9 only breaks or peels off in the area where the anchor agent is not printed, it extends to other unnecessary areas and directions. Therefore, it has the advantage that when the container is opened, it will not peel off and become dirty, which will impair the aesthetic appearance of the container.
第1図は本発明の易開封性包装容器の断面図、
第2図は第1図示の容器の開封状態を示す断面図
である。
1……容器本体、2……蓋体、3……容器基
材、6a,6b……接着部、7……アンカー剤印
刷層、8……印刷模様層、9……熱接着性樹脂
層、10a,10b……非接着部、11……易開
封性包装容器。
FIG. 1 is a sectional view of an easy-to-open packaging container of the present invention;
FIG. 2 is a sectional view showing the container shown in FIG. 1 in an unsealed state. DESCRIPTION OF SYMBOLS 1... Container body, 2... Lid, 3... Container base material, 6a, 6b... Adhesive part, 7... Anchor agent printed layer, 8... Printed pattern layer, 9... Heat adhesive resin layer , 10a, 10b...non-adhesive portion, 11...easy-open packaging container.
Claims (1)
材3を、前記熱接着性樹脂層9を対向させて熱接
着してなる容器口部の開放部をもつ包装容器にお
いて、前記容器口部の開放部は、対向する前記熱
接着性樹脂層9に1対の接着部6a,6bを有し、
さらに前記1対の容器基材3の少なくとも一方の
前記接着部と同じ幅もしくは前記幅より狭い幅の
部分だけを除いて、前記容器基材3と前記熱接着
性樹脂層9との間にアンカー剤印刷層7を有する
易開封性包装容器。 2 前記容器口部の開放部の外方に非接着部10
a,10bが設けられていることを特徴とする特
許請求の範囲第1項記載の易開封性包装容器。 3 前記容器基材3面に前記アンカー剤印刷層7
と絵柄を整合させて印刷模様を施こしたことを特
徴とする特許請求の範囲第1項又は第2項記載の
易開封性包装容器。[Scope of Claims] 1. A container having an opening at the mouth formed by thermally bonding a pair of container base materials 3 whose inner surfaces are a thermoadhesive resin layer 9 with the thermoadhesive resin layers 9 facing each other. In the packaging container, the open part of the container opening has a pair of adhesive parts 6a and 6b on the opposing heat-adhesive resin layer 9,
Further, an anchor is provided between the container base material 3 and the thermally adhesive resin layer 9, excluding only a portion of at least one of the pair of container base materials 3 having the same width as or narrower than the adhesive portion. An easy-to-open packaging container having an agent-printed layer 7. 2. A non-adhesive part 10 is provided outside the open part of the container mouth part.
The easy-open packaging container according to claim 1, further comprising: a and 10b. 3 The anchor agent printed layer 7 on the 3 sides of the container base material
3. The easy-open packaging container according to claim 1 or 2, characterized in that a printed pattern is applied by matching the pattern.