JP4478317B2 - Easy-open blister pack - Google Patents
Easy-open blister pack Download PDFInfo
- Publication number
- JP4478317B2 JP4478317B2 JP2000318855A JP2000318855A JP4478317B2 JP 4478317 B2 JP4478317 B2 JP 4478317B2 JP 2000318855 A JP2000318855 A JP 2000318855A JP 2000318855 A JP2000318855 A JP 2000318855A JP 4478317 B2 JP4478317 B2 JP 4478317B2
- Authority
- JP
- Japan
- Prior art keywords
- tray
- lid
- flange portion
- outer edge
- easy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【発明の属する技術分野】
本発明は、易開封性のブリスターに関する。
【0002】
【従来の技術】
家庭雑貨品、調理器具、小型電気製品、小型玩具、チューブ入り化粧品や接着剤、鋏、剃刀、ホッチキス等の文具等多くの商品がブリスター包装されている。例えば、図6は、従来のブリスター包装体B’の例を示す図であり、(a)斜視図、(b)および(c)は開封前、開封後のX3−X3部のそれぞれの断面図である。
このブリスター包装体B’の例は、トレー1’、蓋体10’、そして、トレーのフランジ部を蓋体10’ともに挟持する被覆材20’からなるものがある。
【0003】
【発明が解決しようとする課題】
従来のブリスター包装においては、トレーと蓋体とからなり、トレーのフランジ部と蓋体とが強固に接着されたものが多かった。このようなブリスター包装においては、包装された内容物を取出すために、蓋体をトレーから剥離するが、この際開封するときに紙層において凝集破壊したり、接着が強くて、鋏などを用いて蓋体を切断して内容物を取出すこともあった。
また、印刷が蓋体の表が主体となって必ずしも表示が見やすいとは言えなかった。つまり、内容物側と情報印刷面とが裏表となっていた。
また、前記図6(a)に示すような、蓋体10’と被覆材20’とにより、トレー1’のフランジ部3’を挟んでヒートシールする方法がある。該ヒートシールは、蓋体10’、被覆材20’にヒートシール剤を塗布し形成したヒートシール層により接着していた。この構成のブリスターを開封すると、図6(c)に示すように、蓋体10’または被覆材20’のいずれかの紙層の凝集破壊となって紙表面に印刷された絵柄や文字が判読できなくなることが多かった。
本発明の目的は、開封しやすく、印刷情報の見やすい構造を有するブリスター包装体を提供することである。
【0004】
【課題を解決するための手段】
本発明は、内容物を収納する凹部とその周縁にフランジ部を有するトレーと、トレー開口部とフランジ部を覆い、フランジ部の外縁よりも大きな外縁を有する蓋体と、外蓋体の外縁と略同じ外縁を有し、その内縁は少なくともフランジ部を被覆し得る形状を有する被覆材とからなり、内容物を凹部に収納したトレーの開口部側に蓋体を載置し、被覆材で蓋体とともにフランジ部を挟みフランジ部の外縁の外側において蓋体とヒートシールするブリスター形式の包装において、少なくとも、前記被覆材が基材層、2軸延伸ポリエステルフィルム、ポリエチレン層からなり、前記2軸延伸ポリエステルフィルムと前記ポリエチレンとの接着面の接着強度が50g/15mm巾〜500g/15mm巾である易剥離性積層体であることを特徴とする易開封ブリスター包装体であって、前記基材層が紙であることを含み、また、被覆材および蓋体が易剥離性積層体から構成されてもよい。
【0005】
【発明の実施の形態】
本発明の易開封ブリスター包装体は、トレーのフランジ部を蓋体と被覆材により挟持した状態でヒートシールして固定したブリスター容器であり、少なくとも被覆材を構成する複合フィルムの積層体に易剥離面が含まれていることを特徴とするものである。
図1は、本発明の易開封ブリスター包装体の実施例を示す図で、(a)包装状態の斜視図、(b)X1−X1部断面図、(c)各部材を分離して示した図、(d)X2−X2部断面図である。図2は、被覆材の構造を示す断面図である。図3は、本発明のブリスター包装体を開封したときの剥離状態を説明するための、Y部の拡大図であり、(a)開封前、(b)開封時の状態を示す。図4は、本発明の別のブリスター包装体を開封したときの剥離状態を説明するための、Y部の拡大図であり、(a)開封前、(b)開封時の状態を示す。図5は、本発明の易開封ブリスター包装体を開封する時の各層の状態を説明する断面図である。
【0006】
本発明者は、本発明の開封しやすく、印刷情報の見やすい構造を有するブリスター包装を得るために、その包装材料と構造について鋭意研究した結果、内容物を収納する凹部とその周縁にフランジ部を有するトレーと、トレー開口部とフランジ部を覆い、フランジ部の外縁よりも大きな外縁を有する蓋体と、該蓋体の外縁と略同じ外縁を有し、その内縁は少なくともフランジ部を被覆し得る形状を有する被覆材とを用い、内容物を凹凸に収納したトレーの開口部側に蓋体を載置し、被覆材で蓋体とともにフランジ部を挟みフランジ部の外縁の外側において蓋体とヒートシールする構造のブリスター包装体において、少なくとも、前記被覆材が基材層、2軸延伸ポリエステルフィルム、ポリエチレン層からなり、前記2軸延伸ポリエステルフィルムと前記ポリエチレンとの接着面の接着強度が50g/15mm巾〜500g/15mm巾である易剥離性積層体とすることによって前記課題を解決できることを見出し本発明を完成するに到った。
【0007】
本発明の易開封ブリスター包装体Bは、図1(c)に示すように、内容物Pを収納する凹部2を形成し、かつ、周縁にフランジ部3を有するトレー1、凹部2を被覆しその外縁は、トレー1のフランジ部3の外縁4よりも大きい外縁11を有する蓋体10、そして、蓋体10の外縁11と略同じ外縁21を有し、その内縁は少なくともフランジ部3を被覆しうる形状を有する被覆材20ととする。
【0008】
そして、前記被覆材20は、図2に示すような構成の易剥離性積層体30からなり、少なくとも、基材層31、2軸延伸ポリエステルフィルム32、低密度ポリエチレン33の3層からなる。基材層31には印刷34を施してもよい。前記易剥離性積層体の易剥離は、前記2軸延伸ポリエステルフィルム32と低密度ポリエチレン33との接着界面であり、前記2軸延伸ポリエステルフィルム32と低密度ポリエチレン層33とのラミネート強度を100から200g/15mm巾とするものである。
【0009】
本発明の易開封ブリスター包装体Bは、前記トレー1に内容物Pを収納し、蓋体10でその開口部を覆い、蓋体10と被覆材20とによってトレー1のフランジ部3を挟み、蓋体10と被覆材20とを加圧加熱してヒートシールすることによって形成される。
【0010】
得られた本発明の易開封ブリスターBを開封する為に、図1(a)に示すように、ブリスターパックの周縁の一部に開封用つまみ部Tを設け開封開始部とする。該開封用つまみ部Tにおいては、図5に示すように非シール部NSを設ける。開封に際しては、前記開封用つまみ部Tの非シール部NSの蓋体10と被覆材20とを摘んで、蓋体10から被覆材20を剥離すると、被覆材20の2軸延伸ポリエステルフィルム32とポリエチレン層33との間が、容易に剥離するためトレー1がフリー状態となり内容物は容易に取出すことができる。このとき、図3(b)に示すように、被覆材20のポリエチレン層は33、前記ヒートシールの際の加熱加圧により、トレーフランジの外縁部にてフランジ部の段差によって断裂状態の損傷部6が形成され、蓋体とヒートシールされた領域は蓋体側に転移し、前記損傷部6よりも内側部分は、被覆材側に接着したままとなる。
【0011】
本発明の易開封ブリスター包装体Bにおけるトレー1の成形は、プラスチックシートを真空成形、圧空成形、真空圧空成形、インジェクション成形等の方法を用いて成形することができる。
従来のブリスター包装においては、蓋体または、蓋体に塗布されたヒートシール層に対してヒートシール性が必要であったが、本発明においては、蓋体に対するトレーとしてのヒートシール性は不要である。本発明の易開封ブリスターに用いるトレーの材質としては、ポリプロピレン、ポリスチレン、ポリ塩化ビニール、ポリエチレンテレフタレート、ポリカーボネート、ポリアクリロニトリル等が利用できる。
【0012】
本発明の易開封ブリスター包装体Bにおける蓋体10の材質としては、紙単層であっても良いし、また、紙と他の素材との積層体であっても良い。そして、蓋体10のトレー1側の面は被覆材の低密度ポリエチレン層に対してヒートシール性を有する材質とする。また、図4(a)または図4(b)に示すように、蓋体10としても、被覆材20と同じ易剥離性積層体を用いることもできる。蓋体10としては、剛性を有し、トレーに載置する際にカールのないシートであることが好ましい。
【0013】
本発明の被覆材についてさらに詳細に説明する。被覆材は、図2に示すように、基材31と易剥離ラミネート体とを貼り合わせた易剥離性積層体である。
【0014】
前記易剥離性積層体における易剥離ラミネート体は、有極性合成樹脂基材層と無極性合成樹脂層とのラミネート体であって、前記量層のラミネート界面の接着強度が易剥離状態にコントロールしたものである。
ブリスターの端部に設けた摘み部から被覆材と蓋体とを分離しようとすると、断裂部から2軸延伸ポリエステルフィルムとポリエチレン層との間、前記易剥離面が剥離し、薄いポリエチレンの膜、2軸延伸ポリエステルフィルム面に接着した状態となるため、成形品は固定状態が完全に解除される。
【0015】
【実施例】
本発明の易開封ブリスター包装体について、実施例によりさらに具体的に説明する。
[実施例1]
被覆材に用いる易剥離性積層体は、まず、PET12μm基材(東洋紡績株式会社製 PETフィルム:E5100)に押出し機よりPE7μm(三井化学株式会社製 ポリエチレン樹脂:ミラソン11P)を押出し温度280℃にて押出しコートし、PET12μm/PE7μmの易剥離ラミネート体を作成した。
別に、基材層としてコートボール紙(坪量:400g/■)を用い、前記易剥離ラミネート体の2軸延伸ポリエステルフィルムの非ラミネート面(ポリエステル面)をコロナ処理し、該コロナ処理面に接着剤(アクリル系水性接着剤:東京インキ株式会社製;SA−T610W、接着剤の塗布量10g/■)を塗布し、前記基材層であるコートボール紙とウェットラミネートし易剥離性積層体を得た。
次に、得られた易剥離性積層体を所定の大きさに打ち抜きして被覆材とした。また、トレーとしては、無延伸ポリエステルシートを真空成形した。
蓋体としは、前記基材層と同じコートボール紙(坪量:400g/■)を用い、その内容物側にオフセット印刷方式により絵柄を設けた。
トレーに内容物である玩具を収納し、蓋体でトレーの開口部を被覆し、トレーフランジ部を蓋体と前述の打ち抜きした被覆材により挟持した状態でヒートシールして、ブリスターパック包装体の実施例1を得た。
<シール面の層構成>
(被覆材側)厚紙/PET12/・/PE7/S/厚紙(蓋体側)
(PETは2軸延伸ポリエステルフィルム、・は易剥離面を示す、Sはヒートシール面を示す、以下同じ)
<トレーフランジ部分のシール面の層構成>
(被覆材側)厚紙/PET12/・/PE7/S/トレーフランジ部/S/厚紙(蓋体側)
得られたブリスターパック実施例1のシール面を剥離したところ、シール面ではPET/PE界面(・)で剥離し、トレーフランジ部分のシール面ではPE/トレーフランジ間で剥離し、紙とプラスチックトレーを奇麗に分別することができた。また、剥離後、蓋体10に設けた絵柄も明瞭に視認できた。
[実施例2]
前記被覆材とする易剥離性積層体を作成するところまでは、同一材料、工程にて行ったが、実施例1と異なるところは、蓋体にも被覆材と同じ易剥離性積層体を使用したところである。そのため、蓋体側の易剥離性積層体を加工する際に、コートボール紙のラミネート面側に、印刷により絵柄を設けた。得られた包装体をブリスター包装体の実施例2とする。
シール面の層構成
(被覆材側)厚紙/PET12/・/PE7/S/PE7/PET12/厚紙(蓋体側)
トレーのフランジ部分のシール面の層構成
(被覆材側)厚紙/PET12/・/PE7/トレーフランジ部/PE7/PET12/厚紙(蓋体側)
得られたブリスターパック包装体の実施例2のシール面を剥離したところ、PET/PE界面で剥離し、トレーフランジ部分のシール面ではPE/トレーフランジで剥離し、紙とトレーとを奇麗に分別することができた。また、剥離後、蓋体に設けた絵柄も明瞭に視認できた。
[比較例]
被覆材、蓋体共に、コートボール紙(坪量:400g/■)にヒートシール剤(酢酸ビニル系水性接着剤 サイデン化学株式会社製S303、塗布量10g/■)を塗布したコートボール紙(坪量400g/■)を用い、実施例と同様の、トレー、被覆材、蓋体からなる構造のブリスターパックを作成し、ブリスター包装体の比較例1とした。
<シール面の層構成>
(被覆材側)厚紙/ヒートシール剤/S/ヒートシール剤/厚紙(蓋体紙側)
<トレーのフランジ部分のシール面の層構成>
(被覆材側)厚紙/ヒートシール剤/トレーフランジ部/ヒートシール剤/厚紙(蓋体側)
得られたブリスターパック比較例1のシール面を剥離したところ、被覆材か蓋体のいずれかが紙剥けしてしまい、更に、トレーフランジ部分のシール面ではトレーフランジに紙が付着してしまい、紙とトレーとを完全に分別することができなかった。
【0016】
【発明の効果】
フランジ部を形成したトレーに内容物を収納し、蓋体と被覆材とにより前記フランジ部を挟持した状態で、蓋体と被覆材とをヒートシールするブリスター包装において、被覆材の材質を易剥離性積層体としたことによって内容物の取出しが容易なブリスター包装体とすることができる。
また、開封が、被覆材の積層体の接着界面の剥離であるため、蓋体に設けられた印刷層が破壊されることなく印刷情報が見やすい包装体とすることができる。
【図面の簡単な説明】
【図1】本発明の易開封ブリスターの実施例を示す図で、(a)包装状態の斜視図、(b)X1−X1部断面図、(c)各部材を分離して示した図、(d)X2−X2部断面図である。
【図2】被覆材の構造を示す断面図である。
【図3】本発明のブリスターを開封したときの剥離状態を説明するための、Y部の拡大図であり、(a)開封前、(b)開封時の状態を示す。
【図4】本発明の別のブリスター包装体を開封する時の剥離状態を説明するための、Y部の拡大図であり、(a)開封前、(b)開封時の状態を示す。
【図5】本発明の易開封ブリスター包装体の開封用つまみ部を説明する断面図である。
【図6】従来のブリスターの例を示す図であり、(a)斜視図、(b)および(c)は開封前、開封後のX3−X3部のそれぞれの断面図である。
【符号の説明】
B 易開封ブリスター
P 内容物
HS ヒートシール部
T 開封用つまみ部
NS 非シール部
1、1’ トレー
2 凹部
3 フランジ部
4 フランジ部外縁
5 フランジ部内縁
6 損傷部
7 凝集破壊部
10、10’ 蓋体
11 外縁
20、20’ 被覆材
21 外縁
22 内縁
30 易剥離性積層体
31 基材層
32 有極性合成樹脂基材層
33 無極性合成樹脂層
34 印刷層
35 表面処理
36 接着剤層
37 接着樹脂層
38 剥離面
B’従来のブリスター包装体
1’トレー
3’フランジ部
7 凝集破壊部
10’ 被覆材
20 ’被覆材[0001]
BACKGROUND OF THE INVENTION
The present invention relates to an easily openable blister.
[0002]
[Prior art]
Many items such as household goods, cooking utensils, small electrical products, small toys, cosmetics and adhesives with tubes, stationery such as scissors, razors and staplers are blister packed. For example, FIG. 6 is a diagram showing an example of a conventional blister package B ', (a) a perspective view, (b) and (c) it is opened before the X 3 -X 3 parts after opening of each It is sectional drawing.
Examples of the blister package B ′ include a
[0003]
[Problems to be solved by the invention]
In conventional blister packaging, a tray and a lid are often used, and the flange portion of the tray and the lid are often firmly bonded. In such blister packaging, the lid is peeled off from the tray in order to take out the packaged contents. At this time, when opening, the paper layer is agglomerated and broken, or the adhesion is strong. In some cases, the lid was cut to remove the contents.
In addition, it cannot be said that printing is easy to see because printing is mainly performed on the front of the lid. In other words, the contents side and the information printing surface are the front and back.
Further, as shown in FIG. 6 (a), there is a method of heat sealing by sandwiching the
The objective of this invention is providing the blister package which has a structure which is easy to open and it is easy to see printing information.
[0004]
[Means for Solving the Problems]
The present invention includes a concave portion for storing contents, a tray having a flange portion at the periphery thereof, a lid body that covers the tray opening portion and the flange portion, and has an outer edge larger than the outer edge of the flange portion, and an outer edge of the outer cover body. The outer edge has substantially the same outer edge, and the inner edge is made of a covering material having a shape capable of covering at least the flange portion. The lid is placed on the opening side of the tray in which the contents are stored in the concave portion, and the cover is covered with the covering material. In a blister-type packaging in which a flange portion is sandwiched with a body and heat-sealed with a lid outside the outer edge of the flange portion, at least the covering material comprises a base material layer, a biaxially stretched polyester film, and a polyethylene layer, and the biaxially stretched It is an easily peelable laminate having an adhesive strength between the polyester film and the polyethylene of 50 g / 15 mm to 500 g / 15 mm. A open blister package, said method comprising the substrate layer is paper, or may be composed of dressing and the lid is easily peelable laminate.
[0005]
DETAILED DESCRIPTION OF THE INVENTION
The easy-open blister package of the present invention is a blister container that is heat-sealed and fixed in a state where the flange portion of the tray is sandwiched between the lid and the covering material, and is easily peeled off at least to a composite film laminate constituting the covering material A surface is included.
FIG. 1 is a view showing an embodiment of the easy-open blister package of the present invention, in which (a) a perspective view of a packaged state, (b) a cross-sectional view of X 1 -X 1 part, and (c) each member is separated. indicated figure, a (d) X 2 -X 2 parts cross section. FIG. 2 is a cross-sectional view showing the structure of the covering material. FIG. 3 is an enlarged view of a Y portion for explaining a peeled state when the blister package of the present invention is opened, and shows a state before (a) opening and (b) opening. FIG. 4 is an enlarged view of a Y portion for explaining a peeled state when another blister package of the present invention is opened, and shows a state before (a) opening and (b) opening. FIG. 5 is a cross-sectional view illustrating the state of each layer when the easy-open blister package of the present invention is opened.
[0006]
As a result of earnest research on the packaging material and structure in order to obtain a blister package having a structure that allows easy opening and easy-to-read printing information of the present invention, the inventor of the present invention has a concave portion for storing contents and a flange portion on the periphery thereof. A tray that covers the tray opening and the flange portion, has a lid body that has an outer edge larger than the outer edge of the flange portion, and has an outer edge substantially the same as the outer edge of the lid body, and the inner edge can cover at least the flange portion The cover is placed on the opening side of the tray that contains the contents in irregularities, and the cover is sandwiched between the cover and the flange with the cover. In the blister package having a structure to be sealed, at least the covering material comprises a base material layer, a biaxially stretched polyester film, and a polyethylene layer. Adhesive strength of the adhesive surface of the arm and said polyethylene has completed the present invention can solve the above problems by the easy peelable laminate is 50 g / 15 mm width to 500 g / 15 mm width.
[0007]
As shown in FIG. 1 (c), the easy-open blister package B of the present invention forms a
[0008]
The covering
[0009]
The easy-open blister package B of the present invention contains the contents P in the
[0010]
In order to open the obtained easy-opening blister B of the present invention, as shown in FIG. 1 (a), an opening knob T is provided on a part of the peripheral edge of the blister pack to form an opening start portion. The unsealing knob portion T is provided with a non-sealing portion NS as shown in FIG. At the time of opening, when the
[0011]
The
In conventional blister packaging, heat sealing is required for the lid or the heat seal layer applied to the lid, but in the present invention, heat sealing as a tray for the lid is not required. is there. As a material for the tray used in the easy-open blister of the present invention, polypropylene, polystyrene, polyvinyl chloride, polyethylene terephthalate, polycarbonate, polyacrylonitrile, or the like can be used.
[0012]
The material of the
[0013]
The coating material of the present invention will be described in further detail. As shown in FIG. 2, the covering material is an easily peelable laminate in which a
[0014]
The easily peelable laminate in the easily peelable laminate is a laminate of a polar synthetic resin base material layer and a nonpolar synthetic resin layer, and the adhesive strength at the laminate interface of the quantity layer was controlled to an easily peelable state. Is.
When the covering material and the lid are separated from the knob provided at the end of the blister, the easily peelable surface is peeled between the biaxially stretched polyester film and the polyethylene layer from the tearing portion, and a thin polyethylene film, Since the biaxially stretched polyester film surface is adhered, the molded product is completely released from the fixed state.
[0015]
【Example】
The easy-open blister package of the present invention will be described more specifically with reference to examples.
[Example 1]
The easy-peelable laminate used for the covering material was first extruded into a PET 12 μm base material (PET film: Toyobo Co., Ltd., PET film: E5100), PE7 μm (Mitsui Chemicals Co., Ltd., polyethylene resin: Mirason 11P) was extruded at a temperature of 280 ° C. Extrusion-coating was carried out to prepare an easily peelable laminate of PET 12 μm /
Separately, using coated cardboard (basis weight: 400 g / ■) as the base material layer, the non-laminated surface (polyester surface) of the biaxially stretched polyester film of the easily peelable laminate was subjected to corona treatment and adhered to the corona-treated surface. A coating agent (acrylic water-based adhesive: manufactured by Tokyo Ink Co., Ltd .; SA-T610W, adhesive application amount 10 g / ■) is applied and wet-laminated with the coated cardboard as the base material layer to form an easily peelable laminate. Obtained.
Next, the obtained easily peelable laminate was punched into a predetermined size to obtain a coating material. Moreover, as a tray, the unstretched polyester sheet was vacuum-formed.
As the lid, the same coated cardboard (basis weight: 400 g / ■) as that of the base material layer was used, and a pattern was provided on the content side by an offset printing method.
Store the toy as the contents in the tray, cover the opening of the tray with the lid, heat seal with the tray flange sandwiched between the lid and the above-mentioned punched coating material, Example 1 was obtained.
<Layer structure of sealing surface>
(Coating material side) Cardboard / PET12 /./ PE7 / S / Cardboard (lid side)
(PET is a biaxially stretched polyester film,... Indicates an easily peelable surface, S indicates a heat seal surface, and the same applies hereinafter)
<Layer structure of the sealing surface of the tray flange>
(Coating material side) Cardboard / PET12 /./ PE7 / S / Tray flange / S / Cardboard (lid side)
When the sealing surface of the obtained blister pack Example 1 was peeled off, the sealing surface peeled off at the PET / PE interface (•), and the sealing surface of the tray flange peeled off between the PE / tray flange, and the paper and plastic tray Could be sorted neatly. In addition, the pattern provided on the
[Example 2]
The same material and process were used until the preparation of the easily peelable laminate as the covering material. However, the difference from Example 1 was that the same easily peelable laminate as the covering material was used for the lid. I have just done it. Therefore, when processing the easily peelable laminate on the lid side, a pattern was provided by printing on the laminate surface side of the coated cardboard. Let the obtained package be Example 2 of a blister package.
Layer structure of the sealing surface (coating material side) cardboard / PET12 /./ PE7 / S / PE7 / PET12 / cardboard (lid side)
Layer structure of the sealing surface of the flange part of the tray (coating material side) cardboard / PET12 /./ PE7 / tray flange part / PE7 / PET12 / cardboard (lid side)
When the sealing surface of Example 2 of the resulting blister pack package was peeled off, it was peeled off at the PET / PE interface, and the sealing surface of the tray flange was peeled off at the PE / tray flange, thus neatly separating the paper and the tray. We were able to. Moreover, after peeling, the pattern provided on the lid was also clearly visible.
[Comparative example]
Coated cardboard (basis weight) coated with a heat sealant (vinyl acetate aqueous adhesive S303, coated amount 10 g / square) on coated cardboard (basis weight: 400 g / ■) for both the covering material and the lid A blister pack having a structure composed of a tray, a covering material, and a lid, similar to the example, was prepared using a quantity of 400 g / ■), and used as a blister package comparative example 1.
<Layer structure of sealing surface>
(Coating material side) Cardboard / heat sealant / S / heat sealant / cardboard (lid paper side)
<Layer structure of the sealing surface of the flange part of the tray>
(Coating material side) Cardboard / heat sealant / tray flange / heat sealant / cardboard (lid side)
When the sealing surface of the obtained blister pack comparative example 1 was peeled off, either the covering material or the lid peeled off the paper, and further, paper adhered to the tray flange at the sealing surface of the tray flange portion, The paper and tray could not be completely separated.
[0016]
【The invention's effect】
The blister packaging that heat-seals the lid and the covering material in a state where the contents are stored in the tray having the flange portion and the flange portion is sandwiched between the lid and the covering material, and the material of the covering material is easily peeled off. By using a conductive laminate, it is possible to obtain a blister package that allows easy removal of the contents.
In addition, since the unsealing is peeling of the adhesive interface of the laminate of the covering material, the printed layer provided on the lid can be easily broken without breaking the printed layer.
[Brief description of the drawings]
FIG. 1 is a view showing an embodiment of an easy-open blister of the present invention, in which (a) a perspective view of a packaged state, (b) a cross-sectional view of X 1 -X 1 part, and (c) each member is shown separately. Figure a (d) X 2 -X 2 parts cross section.
FIG. 2 is a cross-sectional view showing the structure of a covering material.
FIG. 3 is an enlarged view of a Y portion for explaining a peeled state when the blister of the present invention is opened, and shows a state before (a) opening and (b) opening.
FIGS. 4A and 4B are enlarged views of a Y portion for explaining a peeled state when another blister package of the present invention is opened, showing (a) before opening and (b) a state when opening. FIG.
FIG. 5 is a cross-sectional view illustrating an opening knob portion of the easy-open blister package of the present invention.
6A and 6B are diagrams showing an example of a conventional blister, wherein FIG. 6A is a perspective view, and FIGS. 6B and 6C are cross-sectional views of X 3 -X 3 part before opening and after opening, respectively.
[Explanation of symbols]
B Easy-opening blister P Contents HS Heat-sealing part T Unsealing knob part NS
Claims (3)
少なくとも、前記被覆材が、少なくとも、基材層と、2軸延伸ポリエステルフィルムと、ポリエチレン層との積層体からなり、
更に、前記2軸延伸ポリエステルフィルムと前記ポリエチレン層との接着面の接着強度が50g/15mm巾〜500g/15mm巾である易剥離性積層体からなり、
そして、前記被覆材を、そのポリエチレン層の面を上記蓋体側に位置させて、そのポリエチレン層を介して、蓋体とともにトレ−のフランジ部を挟み、そのフランジ部の外縁の外側において蓋体とヒートシールするブリスター形式の包装体を構成すること
を特徴とする易開封ブリスター包装体。A concave portion for storing contents, a tray having a flange portion on the periphery thereof, a lid body that covers the tray opening portion and the flange portion and has an outer edge larger than the outer edge of the flange portion, and an outer edge substantially the same as the outer edge of the lid body And the inner edge is formed of a covering material having a shape capable of covering at least the flange portion, the lid body is placed on the opening side of the tray in which the contents are stored in the recess, and the flange portion together with the lid body is covered with the covering material. In the blister-type package that heat seals with the lid on the outside of the outer edge of the flange part,
At least, the coating material is at least a base layer, and a biaxially oriented polyester film, a laminated body of the polyethylene layer,
Furthermore, the adhesive strength of the adhesive surface between the biaxially stretched polyester film and the polyethylene layer is an easily peelable laminate having a width of 50 g / 15 mm to 500 g / 15 mm ,
Then, the covering material is positioned with the polyethylene layer side facing the lid body, the flange portion of the tray is sandwiched with the lid body through the polyethylene layer, and the lid body is formed outside the outer edge of the flange portion. An easy-open blister package characterized by comprising a blister-type package for heat sealing .