JPH033431Y2 - - Google Patents
Info
- Publication number
- JPH033431Y2 JPH033431Y2 JP15751685U JP15751685U JPH033431Y2 JP H033431 Y2 JPH033431 Y2 JP H033431Y2 JP 15751685 U JP15751685 U JP 15751685U JP 15751685 U JP15751685 U JP 15751685U JP H033431 Y2 JPH033431 Y2 JP H033431Y2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- transfer
- foil
- base film
- release layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
〈産業上の利用分野〉
本考案は、プラスチツクス成型品・セラミツク
ス成型品・金属成型品・ガラス成型品等の表面
に、着色インキパターン等による意匠性を付与す
るための印刷や、導電性回路パターン等による機
能性を付与するための印刷等を施す際に利用され
る転写箔に関するものである。[Detailed description of the invention] <Industrial application field> This invention is used to impart design properties to the surfaces of plastic molded products, ceramic molded products, metal molded products, glass molded products, etc. using colored ink patterns, etc. The present invention relates to a transfer foil that is used when printing, printing, etc. to provide functionality with a conductive circuit pattern, etc.
さらに詳しくは、かかる転写箔を、転写印刷加
工に適切な幅となるようにスリツトする際、箔こ
ぼれを起こすことのない転写印刷加工適性に優れ
た転写箔に関するものである。 More specifically, the present invention relates to a transfer foil that does not cause foil spillage when the transfer foil is slit to a width suitable for transfer printing and has excellent suitability for transfer printing.
〈従来の技術と考案が解決しようとする問題点〉
従来、転写箔としては、ベースフイルム上に、
剥離層、柄層、接着剤層等からなる転写層が積層
されてなるものが公知である。<Problems to be solved by conventional technology and inventions> Conventionally, transfer foils are made by applying
It is known that a transfer layer consisting of a release layer, a pattern layer, an adhesive layer, etc. is laminated.
通常、このような転写箔は、転写印刷加工を行
う際の幅のもので製品を製造すると不経済である
ため、広幅のもので製品を製造しておき、これを
被転写物の大きさに合わせて適切な幅にスリツト
したのち、転写印刷加工が行われている。 Normally, it would be uneconomical to manufacture such transfer foil with the width used for transfer printing, so products are manufactured with a wide width and this is adjusted to the size of the object to be transferred. After slitting to the appropriate width, transfer printing is performed.
しかしながらこの場合、転写箔のスリツト部分
が、スリツトの際の刃が当たるシヨツクにより箔
こぼれ、すなわち転写層がベースフイルムから剥
がれる現象を起こすという欠点があつた。これは
転写箔のベースフイルムと転写層との間は、転写
印刷に供される絵柄が形成された部分のみでなく
転写印刷に供さない部分も剥離性に優れているた
めである。この欠点は、転写層として柄層が多い
場合、あるいは柄層として蒸着層を設ける必要の
ある場合、あるいは機能層が多い場合等、トータ
ルとして転写層が厚いときほど顕著であつた。 However, in this case, there was a drawback that the slit portion of the transfer foil was hit by the blade during slitting, causing the foil to spill, that is, the transfer layer to be peeled off from the base film. This is because the separation between the base film of the transfer foil and the transfer layer is excellent not only in the part where the pattern to be subjected to transfer printing is formed but also in the part not to be subjected to transfer printing. This drawback was more pronounced when the total transfer layer was thicker, such as when there were many pattern layers as the transfer layer, when it was necessary to provide a vapor-deposited layer as the pattern layer, or when there were many functional layers.
その結果、転写印刷加工時に箔こぼれした小片
が、被転写物と転写層との間にごみとして入り込
み、意匠性や機能性を損なつたりするという問題
点があつた。 As a result, there was a problem in that small pieces of foil spilled during the transfer printing process entered the space between the transferred object and the transfer layer as dust, impairing the design and functionality.
〈問題点を解決するための手段〉
本考案者らは、かかる問題点に鑑み、種々研究
考察した結果、遂に本考案を完成するに至つたも
のである。すなわち本考案は、ベースフイルム１
上に、剥離層２、柄層３、接着剤層４等からなる
転写層５が積層されてなる転写箔において；(a)該
剥離層２が、スリツト部分を除いて形成されてお
り、(b)該剥離層２が形成されたベースフイルム１
上に、ベースフイルム１、剥離層２および柄層３
と層間剥離しない箔こぼれ防止層６が、少なくと
も前記剥離層２が形成されていない部分を覆うよ
うに形成されてなることを特徴とする転写箔であ
る。<Means for Solving the Problems> In view of the above problems, the inventors of the present invention have conducted various research and considerations, and as a result, have finally completed the present invention. In other words, the present invention is based on the base film 1.
In a transfer foil on which a transfer layer 5 consisting of a release layer 2, a pattern layer 3, an adhesive layer 4, etc. is laminated; (a) the release layer 2 is formed excluding the slit portion; b) Base film 1 on which the release layer 2 is formed
On top, base film 1, release layer 2 and pattern layer 3
This transfer foil is characterized in that a foil spill prevention layer 6 that does not peel between the layers is formed so as to cover at least a portion where the peeling layer 2 is not formed.
以下、本考案を図面を用いて更に詳しく説明す
る。なお、図面は図示を明瞭にするために構成要
素の相対的寸法関係を無視して誇張して描いてあ
る。 Hereinafter, the present invention will be explained in more detail using the drawings. It should be noted that the drawings are drawn in an exaggerated manner, ignoring the relative dimensional relationships of the constituent elements, for clarity of illustration.
第１図は、本考案に係る転写箔の一実施例を示
す模式的な拡大断面図である。 FIG. 1 is a schematic enlarged sectional view showing an embodiment of a transfer foil according to the present invention.
１はベースフイルム、２は剥離層、３は柄層、
４は接着剤層、５は転写層、６は箔こぼれ防止層
をそれぞれ示す。 1 is a base film, 2 is a release layer, 3 is a pattern layer,
4 is an adhesive layer, 5 is a transfer layer, and 6 is a foil spill prevention layer.
本考案において特徴とする剥離層２は、転写箔
のスリツト部分を除いて形成する。つまり、転写
箔を製造した後、これを適切な幅にスリツトを行
う部分を除いて形成する。 The release layer 2, which is a feature of the present invention, is formed excluding the slit portion of the transfer foil. That is, after the transfer foil is manufactured, it is formed except for the portions to be slit to an appropriate width.
また本考案において特徴とする箔こぼれ防止層
６は、前記剥離層２が形成されたベースフイルム
１上に、少なくとも前記剥離層２が形成されてい
ない部分を覆うように形成する。 Further, the foil spill prevention layer 6, which is a feature of the present invention, is formed on the base film 1 on which the release layer 2 is formed, so as to cover at least the portion where the release layer 2 is not formed.
前記箔こぼれ防止層６は、ベースフイルム１、
剥離層２および柄層３と容易に層間剥離しないイ
ンキを用いて、0.1〜2μｍの厚みで形成するとよ
い。このインキに使用できる樹脂バインダーとし
ては、アクリル樹脂、ビニル樹脂、ウレタン樹
脂、ポリエステル樹脂等がある。 The foil spill prevention layer 6 comprises a base film 1,
It is preferable to form the layer with a thickness of 0.1 to 2 μm using an ink that does not easily separate the layers from the release layer 2 and pattern layer 3. Examples of resin binders that can be used in this ink include acrylic resin, vinyl resin, urethane resin, and polyester resin.
前記箔こぼれ防止層６は、前記剥離層２が形成
されたベースフイルム１上全面に形成してもよ
い。 The foil spill prevention layer 6 may be formed on the entire surface of the base film 1 on which the release layer 2 is formed.
前記ベースフイルム１、剥離層２、柄層３、接
着剤層４は、公知の転写箔を製造する場合と同様
な材料にて形成するとよい。 The base film 1, release layer 2, pattern layer 3, and adhesive layer 4 are preferably formed of the same materials as those used for manufacturing known transfer foils.
第２図は、本考案にかかる転写箔の一実施例を
示す斜視図である。 FIG. 2 is a perspective view showing an embodiment of the transfer foil according to the present invention.
次に実施例を挙げ説明する。 Next, examples will be given and explained.
〈実施例〉
ポリエステルフイルム上に、下記の組成１から
なるインキを用い、スリツト部分を除いて剥離層
設け、その上に組成２からなるインキを用いて箔
こぼれ防止層を全面に設け、その上に組成３から
なるインキを用いて柄層を設け、その上に組成４
からなるインキを用いて接着剤層を設けた。ここ
で「部」は全て「重量部」を示す。<Example> A release layer was provided on a polyester film except for the slit portion using an ink consisting of the following composition 1, and a foil spill prevention layer was provided on the entire surface using an ink consisting of composition 2, and then A pattern layer is provided using an ink consisting of composition 3, and on top of that a pattern layer is formed using an ink consisting of composition 3.
An adhesive layer was provided using an ink consisting of: All "parts" here indicate "parts by weight."
組成１：アクリル樹脂 10部
トルエン 45部
メチルエチルケトン 45部
組成２：アクリル・ポリエステル樹脂 10部
トルエン 45部
メチルエチルケトン 45部
組成３：アクリル・ビニル樹脂 15部
顔料 30部
トルエン 35部
メチルエチルケトン 20部
組成４：アクリル樹脂 15部
トルエン 40部
酢酸エチル 45部
次に、剥離層が設けられていない部分をスリツ
トしたところ、箔こぼれは全く発生しなかつた。 Composition 1: Acrylic resin 10 parts Toluene 45 parts Methyl ethyl ketone 45 parts Composition 2: Acrylic/polyester resin 10 parts Toluene 45 parts Methyl ethyl ketone 45 parts Composition 3: Acrylic/vinyl resin 15 parts Pigment 30 parts Toluene 35 parts Methyl ethyl ketone 20 parts Composition 4: Acrylic Resin 15 parts Toluene 40 parts Ethyl acetate 45 parts Next, when the part where the release layer was not provided was slit, no foil spillage occurred.
〈考案の効果〉
本考案は、以上のような構成からなるものであ
るから、次のような効果を有する。即ち、本考案
に係る転写箔は、製造した後、適切な幅にスリツ
トを行う際、ベースフイルムと転写層との間で層
間剥離を起こさないため箔こぼれを起こすことは
なく、その結果、転写印刷加工時に転写層と被転
写物との間に箔こぼれした小片がごみとして入り
込まず、意匠性・機能性を損なうことなく転写印
刷加工を行うことができる。しかも、箔こぼれ防
止層が形成された部分は、他の部分より膜層が大
きくなり、転写箔を製造した後に巻き取る際、柄
層に付加がかかりにくいためブロツキングをも起
こし難いものである。<Effects of the invention> Since the present invention is constructed as described above, it has the following effects. That is, when the transfer foil according to the present invention is slit to an appropriate width after being manufactured, there is no delamination between the base film and the transfer layer, so there is no foil spillage, and as a result, the transfer Transfer printing processing can be performed without impairing design and functionality, since small pieces of foil do not enter as dust between the transfer layer and the transferred object during printing processing. In addition, the portion where the foil spill prevention layer is formed has a larger film layer than other portions, and when the transfer foil is manufactured and then rolled up, the pattern layer is less likely to be added to the transfer foil, so blocking is less likely to occur.
従つて、本考案は実用上極めて利用価値が高い
考案である。 Therefore, the present invention is of extremely high practical value.
第１図は、本考案に係る転写箔の一実施例を示
す模式的な拡大断面図である。第２図は、本考案
に係る転写箔の一実施例を示す斜視図である。
図中、１……ベースフイルム、２……剥離層、
３……柄層、４……接着剤層、５……転写層、６
……箔こぼれ防止層。
FIG. 1 is a schematic enlarged sectional view showing one embodiment of a transfer foil according to the present invention. FIG. 2 is a perspective view showing an embodiment of the transfer foil according to the present invention. In the figure, 1...Base film, 2...Peeling layer,
3... Pattern layer, 4... Adhesive layer, 5... Transfer layer, 6
...Foil spill prevention layer.
Claims (1)
着剤層４等からなる転写層５が積層されてなる転
写箔において； (a) 該剥離層２が、スリツト部分を除いて形成さ
れており、 (b) 該剥離層２が形成されたベースフイルム１上
に、ベースフイルム１、剥離層２および柄層３
と層間剥離しない箔こぼれ防止層が、少なくと
も前記剥離層２が形成されていない部分を覆う
ように形成されてなることを特徴とする転写
箔。[Claims for Utility Model Registration] In a transfer foil in which a transfer layer 5 consisting of a release layer 2, a pattern layer 3, an adhesive layer 4, etc. is laminated on a base film 1; (a) the release layer 2 is (b) The base film 1, the release layer 2 and the handle layer 3 are formed on the base film 1 on which the release layer 2 is formed.
A transfer foil characterized in that a foil spill prevention layer that does not peel between the layers is formed so as to cover at least a portion where the peeling layer 2 is not formed.