JP2533034B2 - Magnetic card - de - Google Patents

Magnetic card - de

Info

Publication number
JP2533034B2
JP2533034B2 JP4089828A JP8982892A JP2533034B2 JP 2533034 B2 JP2533034 B2 JP 2533034B2 JP 4089828 A JP4089828 A JP 4089828A JP 8982892 A JP8982892 A JP 8982892A JP 2533034 B2 JP2533034 B2 JP 2533034B2
Authority
JP
Japan
Prior art keywords
layer
card
magnetic
resin
magnetic card
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP4089828A
Other languages
Japanese (ja)
Other versions
JPH06130882A (en
Inventor
哲郎 入田
喜春 油井
Original Assignee
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大日本印刷株式会社 filed Critical 大日本印刷株式会社
Priority to JP4089828A priority Critical patent/JP2533034B2/en
Publication of JPH06130882A publication Critical patent/JPH06130882A/en
Application granted granted Critical
Publication of JP2533034B2 publication Critical patent/JP2533034B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Lifetime legal-status Critical

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】本発明は、磁気とホログラムの複合カードに関し、さらに詳しくは、ホログラムによる視覚効果及び磁気による機械情報処理能力を有する、磁気とホログラムが一体化した磁気カードに関する。 BACKGROUND OF THE INVENTION The present invention relates to a composite card of the magnetic and the hologram, more particularly, has a machine information processing capability visual effect and magnetic by the hologram, a magnetic card magnetic and the hologram are integrated.

【0002】 [0002]

【従来の技術】従来、クレジットカード等において、磁気層を施され、機械情報処理能力を有するもの、もくしは磁気層及びホログラムが異なる部分に施され、機械情報処理能力を有するとともに、装飾的にも優れたものが知られていた。 Conventionally, in a credit card or the like, it is subjected to a magnetic layer, having a machine information processing capability, visually applied to the portion where the magnetic layer and the hologram is different, and has a mechanical information processing capability, decorative but also excellent to have been known.

【0003】 [0003]

【発明が解決しようとする課題】これらは限られたカードスペースに於いてそれぞれの占有面積を必要としカードのデザインを施すに当たり制約をうける欠点があり、 THE INVENTION Problems to be Solved] these has the disadvantage that subject to constraints Upon applying the design of the card requires each of the occupied area at the limited card space,
又、磁気部は黒色、茶色等のため装飾的な面で美麗さに欠けるという欠点がある。 The magnetic unit is black, there is a drawback of lacking beautiful is in decorative surface for like brown.

【0004】本発明は、上記従来の欠点に鑑みなされたもので、磁気層とホログラムが一体化し、それらの占める占有面積を少なくすることができるので、カードデザイン上有利であり、着色層を設ければよりカラフルなデザインのカードを得ることができ、しかも機械情報処理を行なえる磁気カードを提供することを目的とする。 [0004] The present invention has been made in view of the above conventional drawbacks, integrated magnetic layer and the hologram, it is possible to reduce the area occupied by the they are advantageously on the card design, provided a colored layer It can be obtained from the card colorful design lever, moreover an object to provide a magnetic card can perform mechanical processing.

【0005】 [0005]

【課題を解決するための手段】即ち、本発明は、カード上に接着層、磁気記録層、ホログラム形成層が順次積層されている磁気カードであって、磁気記録層が金属の単独もしくは合金の蒸着により形成されていることを特徴とする磁気カードを要旨とするものである。 Means for Solving the Problems That is, the present invention, the adhesive layer on the card, a magnetic recording layer, a magnetic card hologram forming layer are sequentially laminated, the magnetic recording layer of a single or alloy metallic a magnetic card, characterized by being formed by vapor deposition in which the gist.

【0006】 [0006]

【実施例】以下、本発明の磁気カードの実施例に用いられる転写シートの実施例を図面に基づいて詳細に説明する。 EXAMPLES The following be described in detail with reference to the embodiment of the transfer sheet used in the embodiment of the magnetic card of the present invention with reference to the drawings. 図1は前記転写シートを示すもので、図中1は転写シートである。 Figure 1 shows the transfer sheet, reference numeral 1 is a transfer sheet. 前記転写シート1は支持体2の片面に保護層3、ホログラム形成層4、金属反射層5、磁気記録層6、接着層7を順次形成してなるものである。 The transfer sheet 1 is protective layer 3 on one surface of the support 2, the hologram forming layer 4, a metal reflective layer 5, the magnetic recording layer 6 is made by the adhesive layer 7 are sequentially formed. 尚、図中8はホログラム形成部である。 In the drawing, 8 is a hologram forming part.

【0007】前記転写シートに於ける支持体2としては、種々のプラスチックフィルムが使用可能であるが、 [0007] As in the support 2 to the transfer sheet, various plastic films can be used,
抗張力、耐熱性を兼ね備えたポリエステルフィルムが好ましい。 Tensile strength, a polyester film is preferable that combines heat resistance.

【0008】前記転写シートに於ける保護層3としてはポリメチルメタクリレート樹脂と他の熱可塑性樹脂、例えば塩化ビニル/酢酸ビニル共重合体もしくはニトロセルロース樹脂との混合物、又はポリメチルメタクリレート樹脂とポリエチレンワックスとの混合物等が挙げられ、又、酢酸セルロース樹脂と熱硬化性樹脂、例えばエポキシ樹脂、フェノール樹脂、熱硬化型アクリル樹脂もしくはメラミン樹脂との混合物が好ましい例として挙げられる。 [0008] The transfer As in the protective layer 3 on the sheet polymethyl methacrylate resin and another thermoplastic resin, for example mixtures of vinyl chloride / vinyl acetate copolymer or nitrocellulose resin, or polymethyl methacrylate resin and polyethylene wax mixture and the like with, also, cellulose acetate resin and thermosetting resin such as epoxy resin, phenol resin, mixture of a thermosetting acrylic resin or melamine resin can be cited as preferred examples.

【0009】前記転写シートに於いて、ホログラム形成層4の材質として、ポリ塩化ビニル、アクリル(例、M [0009] In the transfer sheet, as the material of the hologram forming layer 4, a polyvinyl chloride, acrylic (eg, M
MA)、ポリスチレン、ポリカーボネート等の熱可塑性樹脂、不飽和ポリエステル、メラミン、エポキシ、ポリエステル(メタ)アクリレート、ウレタン(メタ)アクリレート、エポキシ(メタ)アクリレート、ポリエーテル(メタ)アクリレート、ポリオール(メタ)アクリレート、メラミン(メタ)アクリレート、トリアジン系アクリレート等の熱硬化性樹脂を硬化させたもの、或いは、上記熱可塑性樹脂と熱硬化性樹脂の混合物が使用可能である。 MA), polystyrene, thermoplastic resins such as polycarbonate, unsaturated polyester, melamine, epoxy, polyester (meth) acrylate, urethane (meth) acrylate, epoxy (meth) acrylates, polyether (meth) acrylate, polyol (meth) acrylates , melamine (meth) acrylate, those obtained by curing a thermosetting resin such as triazine-based acrylate, or a mixture of the thermoplastic resin and a thermosetting resin can be used.

【0010】前記転写シートに於いて、金属反射層5の材質として、アルミニウム、銀、ニッケル、金、銅、 [0010] In the transfer sheet, as the material of the metal reflecting layer 5, aluminum, silver, nickel, gold, copper,
錫、インジウム、コバルトの箔もしくは蒸着層が挙げられ、特にアルミニウムの箔もしくは蒸着層が好適である。 Tin, indium, foil or vapor-deposited layer of cobalt and the like, particularly suitable foil or deposited layer of aluminum.

【0011】前記転写シートに於いて、磁気記録層6は例えば公知の磁気塗料を用いて印刷もしくは塗布方法により形成したものである。 [0011] The In the transfer sheet, the magnetic recording layer 6 are those formed by printing or coating method using, for example, known magnetic paint. 磁気塗料としては例えば、ブチラール樹脂、塩化ビニル/酢酸ビニル共重合体、ウレタン樹脂、ポリエステル樹脂、セルロース系樹脂、アクリル樹脂、スチレン/マレイン酸共重合樹脂等の合成樹脂をバインダー樹脂とし、必要に応じ、ニトリルゴム等のゴム系樹脂、ウレタンエラストマーを添加し、磁性体としてはγ−Fe 23 、Co含有Fe 23 、Fe 3 The magnetic coating material for example, a butyral resin, a vinyl chloride / vinyl acetate copolymer, urethane resin, polyester resin, cellulose resin, an acrylic resin, a synthetic resin such as styrene / maleic acid copolymer resin as a binder resin, if necessary , rubber-based resins such as nitrile rubber, the addition of urethane elastomers, as the magnetic γ-Fe 2 O 3, Co-containing Fe 2 O 3, Fe 3
4 、バリウムフエライト、ストロンチウムフエライト、Co・Ni・Fe・Crの単独もしくは合金、希土類Co磁性体の他、界面活性剤、シランカップリング剤、可塑剤、ワックス、シリコーンオイル、カーボンその他の顔料を必要に応じて添加し、3本ロール、サンドミル、ボールミル等により混練して作成したものを用いることができる。 O 4, barium ferrite, strontium ferrite, alone or an alloy of Co · Ni · Fe · Cr, other rare earth Co magnetic, surface active agents, silane coupling agents, plasticizers, waxes, silicone oils, carbon and other pigments added as needed, it can be used those prepared by kneading by a three-roll mill, a ball mill or the like.

【0012】磁気記録層6は上記の塗布型以外にも、近年高密度記録の可能な点で注目されている蒸着、特に斜方蒸着によって形成された金属薄膜型のものでもよい。 [0012] The magnetic recording layer 6 The above coating type, in recent years deposition is noted possible points of high density recording, it may be of particular metal thin film type formed by oblique deposition.
例えばニッケルやコバルトの単独もしくは合金の斜方蒸着膜がその具体例である。 For example obliquely evaporated film of nickel or cobalt alone or alloy is a specific example.

【0013】前記転写シートに於ける接着層7としては、ヒートシール性の良好な塩酢ビ共重合体等の合成樹脂が使用可能である。 [0013] As the transfer sheet in the adhesive layer 7, the heat-sealing of good VCVAC copolymer synthetic resin can be used.

【0014】前記転写シートに於いて、保護層3から金属反射層5までの総厚みは2〜10μであり、好ましくは2〜6μである。 [0014] In the transfer sheet, the total thickness of the protective layer 3 to the metal reflective layer 5 is 2~10Myu, preferably 2~6Myu. 上記厚みを2〜10μの範囲にすることにより、機械情報処理に支障なく磁気カードに使用することができる。 By the thickness in the range of 2~10Myu, it can be used without hindrance magnetic card into the machine processing.

【0015】上記のように構成される転写シート1を形成するに当たっては種々の方法があるが、例えば、支持体2片面に保護層3を従来公知の方法で塗布した後、ホログラム形成層4を形成する樹脂組成物を塗布し、従来公知の方法でホログラム形成部8を形成する。 [0015] While in forming a transfer sheet 1 constructed as described above there are various methods, for example, the protective layer 3 on the support 2 sided after applying a conventionally known method, a hologram forming layer 4 forming a resin composition is coated to form a hologram forming unit 8 by a known method. 次に、金属反射層5を真空蒸着法により形成した後、磁気記録層6、接着層7を順次塗布して転写シート1を形成する。 After forming by vacuum deposition a metal reflective layer 5, the magnetic recording layer 6, and an adhesive layer 7 successively coated to form a transfer sheet 1.

【0016】上記の様に構成される転写シート1を使用するに際しては、例えば、図2、図3に示す如く、転写シート1を所要の大きさ、形状に切断し、カード9に例えば加熱融着する等により貼着した後、支持体2を剥離してホログラム形成部8及び磁気記録層6を有するカード9を形成することで本発明の磁気カードがえられる。 [0016] In using the transfer sheet 1 constructed as described above, for example, FIG. 2, as shown in FIG. 3, the transfer sheet 1 the desired size, cut into shape, for example, heat fusion to the card 9 after adhered such as by wear, the magnetic card of the present invention will be obtained by forming the card 9 having a hologram forming part 8 and the magnetic recording layer 6 is peeled off the support 2.
形成された本発明の磁気カードはカード9にホログラム形成部8及び磁気記録層6が一体に形成されており、必要に応じてカード表面の占有面積を小さくすることが出来、その結果カードの装飾性を与える部分が大きくなり、装飾性大なるカードが得られる。 Magnetic card of the present invention formed is a hologram forming unit 8 and the magnetic recording layer 6 in the card 9 is formed integrally, it is possible to reduce the area occupied by the card surface as required, decoration resulting card the part that gives the sex becomes large, decorative large become card is obtained. 又、磁気記録層6 The magnetic recording layer 6
上面にホログラム形成部8が形成されているため、磁気記録層6の黒色、茶色等の色が隠れて美麗なカード9が得られる。 Since the hologram forming part 8 on the top surface is formed, the black magnetic recording layer 6, is beautiful card 9 Obscured color such as brown obtained.

【0017】図4は、前記転写シート1の他の実施例を示すもので、保護層3とホログラム形成層4との間に着色層10を設けたものである。 [0017] Figure 4 shows another embodiment of the transfer sheet 1, in which the colored layer 10 is provided between the protective layer 3 and the hologram forming layer 4. 着色層10としては、合成樹脂が使用可能であり、樹脂中に顔料を添加して着色した樹脂組成物を塗布して形成してもよく、合成樹脂のフィルム上に印刷を施したものを貼着して形成してもよい。 The coloring layer 10, the synthetic resin can be used, and may form a resin composition colored by adding a pigment in the resin is coated, bonded those subjected to printing on a film of synthetic resin it may be formed by wearing. 着色層10が形成された転写シート1はカード等に使用した際、カラフルなデザインのカードを得ることが出来る。 Transfer sheet 1 on which the colored layer 10 is formed when using the card, it is possible to obtain a card colorful design. 以下具体的実施例を挙げて本発明を更に詳細に説明する。 Hereinafter by way of specific examples to illustrate the invention in more detail.

【0018】実施例1 基材として厚み25μのポリエステルフィルムを用い、 [0018] Using a polyester film having a thickness of 25μ as Example 1 substrate,
このフィルムの片面に下記(1)、(2)、(3)、 Following on one surface of the film (1), (2), (3),
(4)、(5)の各組成物を用い、剥離保護層(厚さ0.5μ)、ホログラム形成層(厚さ2.5μ)、金属反射層(500〜1000μ)、磁気記録層(15 (4), (5) using the composition of the peeling protective layer (thickness 0.5 [mu]), a hologram forming layer (thickness 2.5 [mu]), a metal reflective layer (500~1000Myu), magnetic recording layer (15
μ)、ヒートシール層(5μ)を順次塗布形成して転写シートを作成した。 mu), creating the transfer sheet heat seal layer (5 [mu]) are sequentially applied and formed. 尚、金属反射層は塗布ではなく真空蒸着法を用いて積層した。 The metal reflective layer was laminated by a vacuum evaporation method instead of the coating.

【0019】上記積層した転写シートを0.1ミリの透明硬質塩化ビニルフィルムに熱転写し、支持体を取り除いた後、乳白及び透明硬質塩化ビニルフィルムを0.7 [0019] The transfer sheet as described above laminated thermal transfer to the transparent hard vinyl chloride film of 0.1 mm after removal of the support, opacifying and transparent hard vinyl chloride film 0.7
〜0.8ミリの厚さになるように積層し、加熱,加圧により一枚の板にし、打ち抜きによりカードサイズ(54 0.8 laminated to a thickness of a millimeter, heating, and in one plate by pressure, card size by punching (54
ミリ×86ミリ)に打ち抜くことにより、ホログラム、 By punching in mm × 86 mm), hologram,
磁気入りのプラスチックカードを作成した。 We have created a plastic card of the magnetic-filled. 得られたカードは美麗な外観を呈し、機械情報処理能力も優れたものであった。 The resulting card exhibits a beautiful appearance, were excellent also mechanical information processing capability.

【0020】(1)剥離性保護層組成物 酢酸セルロース樹脂・・・・・・・・・5重量部 メタノール・・・・・・・・・・・・25重量部 MEK・・・・・・・・・・・・・・45重量部 トルエン・・・・・・・・・・・・・25重量部 メチロール化メラミン樹脂・・・・0.5重量部 パラトルエンスルフォン酸・・・0.05重量部 (2)ホログラム形成層組成物 アクリル樹脂・・・・・・・・・・・40重量部 メラミン樹脂・・・・・・・・・・・10重量部 アノン・・・・・・・・・・・・・・50重量部 MEK・・・・・・・・・・・・・・50重量部 (3)反射層 アルミ (4)磁気記録層組成物 γ−Fe 23・・・・・・・・・・30重量部 塩酢ビ共重合体・・・・・・・・・・・3重量部 ポリウレタンエラストマー [0020] (1) peelable protective layer composition cellulose acetate resin ......... 5 parts by weight of methanol ............ 25 parts by weight of MEK · · · · · · ........ 45 parts by weight toluene ............. 25 parts by weight of methylol melamine resin .... 0.5 part by weight paratoluene sulfonic acid. 0. 05 parts by weight (2) hologram forming layer composition acrylic resin ........... 40 parts by weight melamine resin ........... 10 parts by Anon ...... ........ 50 parts by weight of MEK .............. 50 parts by weight (3) a reflective layer of aluminum (4) the magnetic recording layer composition γ-Fe 2 O 3 · ......... 30 parts by weight of vinyl chloride acetate copolymer ........... 3 parts by weight polyurethane elastomer ・・・・20重量部 トルエン・・・・・・・・・・・・・15重量部 MEK・・・・・・・・・・・・・・15重量部 IPA・・・・・・・・・・・・・・16重量部 (5)接着層組成物 塩酢ビ共重合体・・・・・・・・・・20重量部 アクリル樹脂・・・・・・・・・・・10重量部 酢酸エチル・・・・・・・・・・・・20重量部 トルエン・・・・・・・・・・・・・50重量部 .... 20 parts by weight of toluene ............. 15 parts by weight MEK .............. 15 parts by weight IPA · · · · · · · ....... 16 parts by weight (5) adhesive layer composition vinyl chloride acetate copolymer .......... 20 parts by weight of acrylic resin ........... 10 parts by weight of ethyl acetate .................. 20 parts by weight toluene ............. 50 parts by weight

【0021】 [0021]

【発明の効果】以上説明したように、本発明の磁気カードは、カード上に接着層、磁気記録層、ホログラム形成層が順次積層されている磁気カードであって、磁気記録層が金属の単独もしくは合金の蒸着により形成されているものであるから、金属の蒸着からなる磁気記録層が磁気記録可能であるためホログラム形成層と磁気記録層を積層してなるものであり、カードの表面に美麗なホログラムを有し、ホログラムによる視覚効果が得られ、しかも機械的情報処理を行うことができるものである。 As described above, according to the present invention, a magnetic card of the present invention, the adhesive layer on the card, a magnetic recording layer, a magnetic card hologram forming layer are sequentially laminated, alone magnetic recording layer is a metal or from those which are formed by vapor deposition of alloys are those formed by laminating a hologram forming layer and the magnetic recording layer for the magnetic recording layer formed from the deposition of metals can be magnetically recorded, beautiful on the surface of the card has a hologram, a visual effect by the hologram can be obtained. Moreover is capable of performing mechanical processing.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明の磁気カードの実施例に用いられる転写シートを示す縦断面図である。 1 is a longitudinal sectional view showing a transfer sheet used in an embodiment of the magnetic card of the present invention.

【図2】転写シートをカードに装着し支持体を剥離して本発明の磁気カードを製造している状態を示す斜示図である。 2 is a perspective 示図 showing a state of manufacturing the magnetic card of the release to the present invention was mounted transfer sheet to the card support.

【図3】図2の縦断面図である。 3 is a longitudinal sectional view of FIG.

【図4】本発明の磁気カードの他の実施例に用いられる転写シートを示す縦断面図である。 It is a longitudinal sectional view showing a transfer sheet used in another embodiment of the magnetic card of the present invention; FIG.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 転写シート 2 支持体 3 保護層 4 ホログラム形成層 5 金属反射層 6 磁気記録層 7 接着層 8 ホログラム形成部 9 カード 1 transfer sheet 2 support 3 protective layer 4 hologram forming layer 5 metal reflective layer 6 a magnetic recording layer 7 adhesive layer 8 hologram forming unit 9 Card

Claims (5)

    (57)【特許請求の範囲】 (57) [the claims]
  1. 【請求項1】 カード上に接着層、磁気記録層、ホログラム形成層が順次積層されている磁気カードであって、 1. A bonding layer on the card, a magnetic recording layer, a magnetic card hologram forming layer are sequentially laminated,
    磁気記録層が金属の単独もしくは合金の蒸着により形成されていることを特徴とする磁気カード。 Magnetic card, characterized in that the magnetic recording layer is formed by vapor deposition of metal alone or an alloy.
  2. 【請求項2】 前記磁気記録層が、斜方蒸着膜であることを特徴とする請求項1記載の磁気カード。 Wherein said magnetic recording layer is a magnetic card according to claim 1, characterized in that the oblique deposition film.
  3. 【請求項3】 前記金属が、ニッケルまたはコバルトであることを特徴とする請求項1又は2記載の磁気カード。 Wherein the metal is, according to claim 1 or 2 magnetic card, wherein the nickel or cobalt.
  4. 【請求項4】 保護層が、ホログラム形成層の磁気記録層と反対側に形成されていることを特徴とする請求項1 4. A protective layer according to claim 1, characterized in that it is formed on the side opposite to the magnetic recording layer of the hologram forming layer
    から3のいずれか1項記載の磁気カード。 3 any one magnetic card as claimed in.
  5. 【請求項5】 着色層が、保護層とホログラム形成層の間に形成されていることを特徴とする請求項1から4のいずれか1項記載の磁気カード。 5. A colored layer, the protective layer and the magnetic card according to any one of claims 1 4, characterized in that formed between the hologram forming layer.
JP4089828A 1992-03-13 1992-03-13 Magnetic card - de Expired - Lifetime JP2533034B2 (en)