JPH03213508A - Synthetic resin fiber kneaded with mineral powder and synthetic resin sheet raw material - Google Patents
Synthetic resin fiber kneaded with mineral powder and synthetic resin sheet raw materialInfo
- Publication number
- JPH03213508A JPH03213508A JP2010351A JP1035190A JPH03213508A JP H03213508 A JPH03213508 A JP H03213508A JP 2010351 A JP2010351 A JP 2010351A JP 1035190 A JP1035190 A JP 1035190A JP H03213508 A JPH03213508 A JP H03213508A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- synthetic
- fibers
- synthetic resin
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は複合繊維及びシート素材技術に係り、従来の合
成樹脂繊維又はシートになかった斬新な感触及び風合い
を備えた合成樹脂繊維及び合成樹脂シートを構成するた
めの鉱物粉体を混練した合成樹脂繊維及び合成樹脂シー
ト素材に関するものである。[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to composite fiber and sheet material technology, and relates to synthetic resin fibers and synthetic resins that have a novel feel and texture not found in conventional synthetic resin fibers or sheets. The present invention relates to synthetic resin fibers kneaded with mineral powder and synthetic resin sheet materials for forming sheets.
3−
〔従来の技術〕
従来より合成繊維材料としては、レーヨン等の再生繊維
、アセテート等の半合成繊維、ナイロン。3- [Prior Art] Conventionally, synthetic fiber materials include recycled fibers such as rayon, semi-synthetic fibers such as acetate, and nylon.
ポリエステル、アクリル、ポリエチレン及びポリプロピ
レン等の合成繊維など各種の繊維が使用されている。こ
れらの繊維材料のうち比較的透湿性及び吸湿性に優れた
合成繊維材料としてポリウレタン樹脂等があるが、天然
繊維と比較すると、般にそれらの吸湿性及び透湿性が劣
るものであると同時に、近年、風合いや感触の斬新なも
のが要求されている。Various fibers are used, including synthetic fibers such as polyester, acrylic, polyethylene, and polypropylene. Among these fiber materials, there are synthetic fiber materials such as polyurethane resin that have relatively excellent moisture permeability and moisture absorption, but when compared to natural fibers, their moisture absorption and moisture permeability are generally inferior, and at the same time, In recent years, there has been a demand for products with novel textures and textures.
また繊維として従来より知られている金糸、銀糸はそれ
ぞれ箔を糸と絡めており、使用中に金糸。In addition, gold thread and silver thread, which are conventionally known as fibers, are made by intertwining foil with thread, and the gold thread forms during use.
銀糸が簡単に抜けてしまう問題を有しており、耐久性に
乏しいものであった。The problem was that the silver thread easily came off, and the durability was poor.
本発明は上記要求に鑑み、優れた吸湿性及び高透湿性を
有すると共に、従来の繊維やシートにな4−
かった斬新な風合いや感触を有し、更に優れた耐久性を
要する複合繊維又はシート素材である鉱物粉体を混練し
た合成樹脂繊維及び合成樹脂シート素材を提供すること
を目的とするものである。In view of the above requirements, the present invention has been developed to produce composite fibers or sheets that have excellent moisture absorption and high moisture permeability, as well as a novel texture and feel not found in conventional fibers or sheets, and that require further superior durability. The object of the present invention is to provide synthetic resin fibers and synthetic resin sheet materials kneaded with mineral powder, which are sheet materials.
本発明に係る鉱物粉体を混練した合成樹脂繊維及び合成
樹脂シート素材は、超微細粉末化した鉱物材料を合成繊
維、半合成繊維又は再生繊維の線状重合体或はこれら二
種以上の線状重合体の混合からなる化学繊維素材の重合
体と混練したことを要旨とするものである。The synthetic resin fibers and synthetic resin sheet materials kneaded with mineral powder according to the present invention can be produced by mixing ultrafine powdered mineral materials with synthetic fibers, semi-synthetic fibers, linear polymers of regenerated fibers, or wires of two or more of these. The gist is that the chemical fiber material is kneaded with a polymer of a chemical fiber material consisting of a mixture of polymers.
ここで鉱物材料とは、アルミニウム、鉄、銅。Mineral materials here include aluminum, iron, and copper.
金、銀等の金属材料及び、石、ガラス、陶器片。Metal materials such as gold and silver, and pieces of stone, glass, and pottery.
ダイヤモンド屑、雲母等の非金属材料などをいう。Refers to non-metallic materials such as diamond scraps and mica.
また超微細粉末化した鉱物材料とは、鉱物材料の粒径が
数百ミクロンオーダより小さい動植物繊維のパウダーを
指すものである。Further, the ultrafine powdered mineral material refers to a powder of animal and vegetable fibers in which the particle size of the mineral material is smaller than on the order of several hundred microns.
前記本発明の鉱物粉体を混練した合成樹脂繊維及び合成
樹脂シート素材は、紡糸して複合合成樹脂繊維、延展し
て複合合成樹脂シートに構成することを要旨とする。The gist is that the synthetic resin fiber and synthetic resin sheet material kneaded with the mineral powder of the present invention are spun to form a composite synthetic resin fiber and spread to form a composite synthetic resin sheet.
前記本発明の鉱物粉体を混練した合成樹脂繊維は、前記
混練組成物を他の繊維の表面を被覆するような鞘状に紡
糸してなる芯鞘構造の繊維にすることもできる。The synthetic resin fiber kneaded with the mineral powder of the present invention can also be made into a fiber with a core-sheath structure by spinning the kneaded composition into a sheath shape that covers the surface of other fibers.
また本発明の鉱物粉体を混練した合成樹脂繊維は1合成
繊維、半合成繊維又は再生繊維の線状重合体或はこれら
二種以上の線状重合体の混合からなる化学繊維素材を紡
糸した素材糸の表面に超微細粉末化した鉱物材料粉を付
着し、眩光の表面を被覆することによって実現すること
ができる。In addition, the synthetic resin fiber kneaded with the mineral powder of the present invention is obtained by spinning a chemical fiber material consisting of a linear polymer of synthetic fiber, semi-synthetic fiber, or regenerated fiber, or a mixture of two or more of these linear polymers. This can be achieved by attaching ultra-fine powdered mineral material powder to the surface of the material thread to cover the dazzling surface.
更に本発明の鉱物粉体を混練した合成樹脂シートは、合
成繊維、半合成繊維又は再生繊維の線状重合体酸はこれ
ら二種以上の線状重合体の混合からなる化学繊維素材を
延展した素材フィルム表面に超微細粉末化した鉱物材料
粉を付着し、該フィルムの表面を被覆することによって
実現することができる。Furthermore, the synthetic resin sheet kneaded with the mineral powder of the present invention is made by spreading a chemical fiber material consisting of a linear polymer acid of synthetic fibers, semi-synthetic fibers or regenerated fibers, and a mixture of two or more of these linear polymers. This can be achieved by attaching ultrafine powdered mineral material powder to the surface of the material film and coating the surface of the film.
前記繊維材料としては次のものを有効に使用することか
できる。As the fiber material, the following can be effectively used.
鉱物材料 金属 金、銀、アルミニウム、亜鉛、錫、鉄、銅。mineral materials metal gold, silver, aluminum, zinc, tin, iron, copper.
鉛等。Lead etc.
非金属 石、ガラス、陶器片、ダイヤモンド屑、雲母。nonmetal Stone, glass, pottery shards, diamond scraps, mica.
等。etc.
合成樹脂繊維材料
ナイロン、ポリエステル、ポリウレタン、ビニロン、ビ
ニリデン、ポリ塩化ビニル、アクリル、ポリエチレン、
ポリプロピレン等。Synthetic resin fiber materials nylon, polyester, polyurethane, vinylon, vinylidene, polyvinyl chloride, acrylic, polyethylene,
polypropylene etc.
半合成樹脂材料 アセテート、ジアセテート、トリアセテート等。Semi-synthetic resin material Acetate, diacetate, triacetate, etc.
再生繊維材料 レーヨン等。recycled fiber material Rayon et al.
金属や非金属は、それ自体、固有の風合いや光7− 沢及び感触を持っていることは旧知である。 Metals and non-metals themselves have their own unique texture and light7- It is well known that it has a sense of flow and feeling.
上記本発明の繊維の構成は、超微細粉末化したこの鉱物
材料を化学繊維素材に混練して紡糸するか延展し、或は
紡糸又は延展した化学繊維又はシート素材の表面に超微
細粉末化したこの鉱物材料を被着した構造にして合成繊
維自体の肌触り感及び風合いを改良したものである。The composition of the fiber of the present invention is such that the ultrafine powdered mineral material is kneaded with a chemical fiber material and spun or spread, or the ultrafine powder is applied to the surface of the spun or spread chemical fiber or sheet material. This synthetic fiber has a structure coated with this mineral material to improve the feel and texture of the synthetic fiber itself.
以下、本発明に係る鉱物粉体を混練した合成樹脂繊維及
び合成樹脂シート素材の実施例を説明する。Examples of synthetic resin fibers and synthetic resin sheet materials kneaded with mineral powder according to the present invention will be described below.
ヌ】1」y
溶解したポリウレタン樹脂に2μmに粉末化した銅を3
0%重量比添加し、充分に混練して均一に分散した混練
組成物(素材)を調整する。この混練組成物をスクリュ
ー型溶融紡糸機により70デニールの糸として排出する
。] 1"y Add 3 µm powdered copper to the melted polyurethane resin.
0% weight ratio is added and sufficiently kneaded to prepare a uniformly dispersed kneaded composition (raw material). This kneaded composition is discharged as a 70-denier thread using a screw-type melt spinning machine.
遺a盗
8−
溶解したナイロン6に1μmに粉末化した金を10%重
量比添加し、充分に混練して均一に分散した混練組成物
(素材)を調整する。この混練組成物をナイロン6を5
0デニールに紡糸した芯糸の外周に対して鞘状に被着し
、70デニールの芯鞘構造繊維を紡糸する。Theft 8- Add 10% weight ratio of gold powdered to 1 μm to dissolved nylon 6 and thoroughly knead to prepare a uniformly dispersed kneaded composition (raw material). This kneaded composition was mixed with nylon 6 and 5
A core-sheath structural fiber of 70 denier is spun by adhering it in a sheath shape to the outer periphery of the core yarn spun to 0 denier.
来111支
溶解したアクリル樹脂をスクリュー型溶融紡糸機により
70デニールの糸として排出し、眩光を表面溶解温度(
約180℃)雰囲気通過中に該雰囲気内に、方解石を5
μmに粉末化したパウダーを拡散させ、該方解石パウダ
ーを眩光の表面に付着させる。The acrylic resin melted over 111 times was discharged as a 70 denier thread using a screw-type melt spinning machine, and the glare was reduced to the surface melting temperature (
Approximately 180℃) Calcite is added to the atmosphere during passage through the atmosphere.
Diffuse the micronized powder to adhere the calcite powder to the surface of the glare.
前記実施例1,2.3によって製造した鉱物粉体を混練
した合成樹脂繊維は、紡糸の過程で糸切れすることなく
、製糸性が良好であり、従来の繊維と同様に編成、織成
し、又不織布として布地を構成することができた。The synthetic resin fibers kneaded with the mineral powder produced in Examples 1 and 2.3 have good spinability without breaking during the spinning process, and can be knitted and woven in the same way as conventional fibers. The fabric could be constructed as a non-woven fabric.
去m乞
溶解したポリウレタン樹脂に2μmに粉末化したメノウ
を20%重量比添加し、充分に混練して均一に分散した
混練組成物(素材)を調整する。Agate powdered to a size of 2 μm is added at a weight ratio of 20% to the dissolved polyurethane resin, and thoroughly kneaded to prepare a uniformly dispersed kneaded composition (raw material).
この混練組成物をフィルム抽出機により厚さ150μm
のシートとして排出する。This kneaded composition was processed into a film extractor to a thickness of 150 μm.
It is discharged as a sheet.
矢】1」i
溶解したアクリル樹脂をフィルム抽出機により厚さ15
0μmの合成樹脂フィルムを抽出し、該フィルムを表面
溶解温度(約180℃)雰囲気通過中に該雰囲気内に、
絹糸を3μmに粉末化した雲母のパウダーを拡散させ、
該パウダーを該シートの表面に付着させる。Arrow] 1"i Melted acrylic resin is made into a film extractor to a thickness of 15
A 0 μm synthetic resin film was extracted, and the film was placed in the atmosphere at a surface melting temperature (approximately 180°C) while passing through the atmosphere.
Diffuse mica powder made by powdering silk thread to 3 μm,
The powder is attached to the surface of the sheet.
前記実施例4,5によって製造した鉱物粉体を混練した
合成樹脂シートは、従来の合成樹脂シートと全く異なっ
た感触や風合い及び色合いを持たせることができた。The synthetic resin sheets kneaded with the mineral powder produced in Examples 4 and 5 were able to have a feel, texture, and color that were completely different from conventional synthetic resin sheets.
そして、上記鉱物粉体を混練した合成樹脂繊維及び合成
樹脂シート素材から構成した合成樹脂繊維による布地又
はシートは、
(1)斬新な風合いと感触及び色合いを持つ。A fabric or sheet made of synthetic resin fibers made of synthetic resin fibers kneaded with the mineral powder and synthetic resin sheet material (1) has an innovative texture, feel, and color.
たけでなく、従来の布地又はシートにはなかった(2)
優れた耐熱性、吸熱性を有する。Not only that, but it is not found in conventional fabrics or sheets (2)
Has excellent heat resistance and endothermic properties.
(3)優れた耐久性を有する。(3) Has excellent durability.
等の特徴を備える。It has the following characteristics.
以上述べたように本発明に係る鉱物粉体を混練した合成
樹脂繊維及び合成樹脂シート素材は、優れた耐久性を有
するだけでなく天然素材の持つ斬新な風合いや感触及び
色合いを有するものであり、iam維によって編成又は
織成したシートは、通常の服飾素材としてだけでなく、
各種日用品や生活用品の素材として極めて有用である等
、本発明実施後の効果は極めて大きい。As described above, the synthetic resin fibers and synthetic resin sheet materials kneaded with mineral powder according to the present invention not only have excellent durability but also have the novel texture, feel, and color of natural materials. Sheets knitted or woven with iam fibers are used not only as ordinary clothing materials, but also as
The effects of implementing the present invention are extremely large, such as being extremely useful as a material for various daily necessities and daily necessities.
11−11-
Claims (1)
維又は再生繊維の線状重合体或はこれら二種以上の線状
重合体の混合からなる化学繊維素材の重合体と混練して
なる鉱物粉体を混練した合成樹脂繊維及び合成樹脂シー
ト素材。 (2)超微細粉末化した鉱物材料を合成繊維、半合成繊
維又は再生繊維の線状重合体或はこれら二種以上の線状
重合体の混合からなる化学繊維素材の重合体と混練した
後、該混練組成物を紡糸してなる繊維。 (3)超微細粉末化した鉱物材料を合成繊維、半合成繊
維又は再生繊維の線状重合体或はこれら二種以上の線状
重合体の混合からなる化学繊維素材の重合体と混練した
後、該混練組成物を、他の繊維の表面を被覆するような
鞘状に紡糸してなる芯鞘構造繊維。 (4)合成繊維、半合成繊維又は再生繊維の線状重合体
或はこれら二種以上の線状重合体の混合からなる化学繊
維素材の重合体の混練組成物を紡糸する際、繊維の半硬
化時に超微細粉末化した鉱物材料を繊維表面に付着せし
めてなる繊維。(5)前記請求項2、3又は4記載の繊
維によって織成又は編成した布地、或は不織布地を合成
樹脂シートの表面に溶着又は接着によって被着したシー
ト状繊維シート。 (6)前記請求項2、3又は4記載の繊維によって織成
又は編成した布地、或は不織布地を多孔質性合成樹脂シ
ートの多重積層間に存在せしめたシート状繊維シート。 (7)前記請求項2、3又は4記載の繊維によって織成
又は編成した布地、或は不織布地を多孔質性の合成樹脂
シート間に存在させた湿度調整シート。 (8)超微細粉末化した鉱物材料を合成繊維、半合成繊
維又は再生繊維の線状重合体或はこれら二種以上の線状
重合体の混合からなる化学繊維素材の重合体と混練した
後、該混練組成物をフィルム状に延展してなるシート。 (9)合成繊維、半合成繊維又は再生繊維の線状重合体
或はこれら二種以上の線状重合体の混合からなる化学繊
維素材の重合体の混練組成物をフィルム状に延展する際
、フィルムの半硬化時に超微細粉末化した鉱物材料を表
面に付着せしめてなるシート。[Scope of Claims] (1) A chemical fiber material made of a linear polymer of synthetic fiber, semi-synthetic fiber, or regenerated fiber, or a mixture of two or more of these linear polymers, using an ultrafine powdered mineral material. Synthetic resin fibers and synthetic resin sheet materials made by kneading mineral powder kneaded with polymers. (2) After kneading the ultra-fine powdered mineral material with a linear polymer of synthetic fiber, semi-synthetic fiber, or recycled fiber, or a chemical fiber material polymer consisting of a mixture of two or more of these linear polymers. , a fiber obtained by spinning the kneaded composition. (3) After kneading the ultra-fine powdered mineral material with a linear polymer of synthetic fiber, semi-synthetic fiber, or recycled fiber, or a polymer of chemical fiber material consisting of a mixture of two or more of these linear polymers. A core-sheath structure fiber obtained by spinning the kneaded composition into a sheath shape that covers the surface of another fiber. (4) When spinning a polymer kneading composition of a chemical fiber material consisting of a linear polymer of synthetic fibers, semi-synthetic fibers, or regenerated fibers, or a mixture of two or more of these linear polymers, half of the fibers A fiber made by attaching mineral materials that are turned into ultra-fine powder to the fiber surface during hardening. (5) A sheet-like fiber sheet in which a fabric woven or knitted with the fibers according to claim 2, 3 or 4 or a non-woven fabric is adhered to the surface of a synthetic resin sheet by welding or adhesion. (6) A sheet-like fiber sheet in which a fabric woven or knitted with the fibers according to claim 2, 3 or 4 or a non-woven fabric is present between multiple laminations of porous synthetic resin sheets. (7) A humidity control sheet in which a fabric woven or knitted with the fibers according to claim 2, 3 or 4 or a non-woven fabric is present between porous synthetic resin sheets. (8) After kneading the ultra-fine powdered mineral material with a linear polymer of synthetic fiber, semi-synthetic fiber, or recycled fiber, or a chemical fiber material polymer consisting of a mixture of two or more of these linear polymers. , a sheet formed by spreading the kneaded composition into a film. (9) When spreading into a film a kneaded composition of a chemical fiber material polymer consisting of a linear polymer of synthetic fibers, semi-synthetic fibers, or regenerated fibers, or a mixture of two or more of these linear polymers, A sheet made by attaching ultra-fine powdered mineral material to the surface of the film during semi-curing.