JPH03112637A - Decorative laminated sheet with adhesive and manufacture thereof - Google Patents
Decorative laminated sheet with adhesive and manufacture thereofInfo
- Publication number
- JPH03112637A JPH03112637A JP25144689A JP25144689A JPH03112637A JP H03112637 A JPH03112637 A JP H03112637A JP 25144689 A JP25144689 A JP 25144689A JP 25144689 A JP25144689 A JP 25144689A JP H03112637 A JPH03112637 A JP H03112637A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- adhesive
- laminated sheet
- decorative laminated
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産東土の利用分野〕
本発明は、化粧板を机，テーブル等の天板として接着す
る場合に生ずる諸問題を無《した接着剤付き化粧板に関
する。DETAILED DESCRIPTION OF THE INVENTION [Field of Application in Santo Tochi] The present invention relates to a decorative board with an adhesive that eliminates the problems that occur when a decorative board is adhered as a top plate of a desk, table, etc.
従来、机，カウンタ，テーブル等ｔＺ．＊ａ台板の上に
ＪＩＳＫ６９０３ｒ熱硬化性樹脂化粧板」に規定する化
粧板を天板として貼りつけて使用さｎる。この化粧板の
化粧樹脂層には，メラミン梢脂、エボキシ樹脂，不飽和
ポリエステル樹脂、ジアリルフタレート樹脂ｔ，裏面の
基材には２エノール樹脂を用いる。Conventionally, desks, counters, tables, etc. *a A decorative board specified in JIS K6903r Thermosetting Resin Decorative Board is pasted onto the base plate as a top plate. The decorative resin layer of this decorative board uses melamine resin, epoxy resin, unsaturated polyester resin, diallyl phthalate resin, and the back base material uses dienol resin.
上記化粧板を鋼製台板の上＃Ｊ＃′２：接層するが．そ
のためには、甘酸ゴム糸接着剤《二｝ １７ ｋ ：ｌ
’ ムＭ 。#J#'2: Layer the above decorative board on the steel base plate. For that purpose, sweet acid rubber thread adhesive《2》17k:l
'MuM.
ｐａミロプレンゴム）を各接層面に所定量スプレー塗布
し，加熱乾燥後各塗布面を憲ね甘わせ，ゴムロールで加
圧する方法が普通である０〔発明が解決しようとするｌ
ｌｊｉ！！）しかしながら、上記接着剤は有機溶剤を含
有しているため、加熱乾燥時に溶剤ガスを揮散して公害
問題をおこすから、種々の大規模な対策設備をする必要
がある。The usual method is to spray a predetermined amount of pa-miloprene rubber on each contacting surface, heat and dry it, then apply pressure to each coated surface with a rubber roll.
lji! ! ) However, since the above-mentioned adhesive contains an organic solvent, the solvent gas is volatilized during heating and drying, causing a pollution problem, so it is necessary to install various large-scale countermeasure equipment.
又、接着剤の塗布量が少ないと化粧板の剥離がおこり，
或るいを工船熱乾燥が不允分であると溶剤が残留する結
果゛として剥離しやすい。さらに、加熱乾燥温度が高き
に過ぎる時は，化粧板に反り。Also, if the amount of adhesive applied is too small, the decorative board may peel off.
Alternatively, if the thermal drying process is insufficient, the solvent may remain, resulting in easy peeling. Furthermore, if the heating drying temperature is too high, the decorative board will warp.
ねじ八等の変形が起きやすい欠点がある。It has the disadvantage that screw holes are easily deformed.
以上の諸問題は、凡て家具製作工場あるいは家具を設置
する現地での接層作条に伴って起きているものである。All of the above-mentioned problems occur in conjunction with layered cropping in furniture manufacturing factories or on-site where furniture is installed.
従って、本発明は、発想？１１−笈えて、予め化粧板の
製造工場において接着剤を付け、接層削材き化粧板とし
て供給することとし、かつ上ＨＣ問題点を解決するため
、熱活性型接着剤層を基材面に形成した桜清剤付き化粧
板及びその製造方法を提供することを目的としている０
〔昧題を解決するための手攻〕
上記目的を達成するために、本発明は、化粧板の基材面
に熱活性型接着剤層を形成してなる接庸剤付き化粧板で
ある。Therefore, the present invention is an idea? 11-In order to solve the above HC problem, we decided to apply adhesive in advance at a decorative board manufacturing factory and supply it as a decorative board with laminated material. It is an object of the present invention to provide a decorative board with a cherry blossom detergent formed thereon and a method for manufacturing the same. This is a decorative board with an adhesive formed by forming a heat-activated adhesive layer on the surface.
用いる化粧板は、フェノール＠脂の基伺層にメラミン樹
脂、エポキシ梱脂、不飽和ポリエステル樹脂、ジアリル
フタレートａ′ｌ脂等の熱硬化性樹脂層を重ね接着した
ものとする０この化粧板を、机。The decorative board used is a base layer of phenol@fat and a layer of thermosetting resin such as melamine resin, epoxy resin, unsaturated polyester resin, diallyl phthalate a'l resin, etc. ,desk.
カウンタ、テーブル等の天板として用いるが、そのため
Ｋは上記机等の鋼製台板に接層する０本発明に用いる接
着剤を熱活性型接層剤とし、フィルム状または液状の何
れでも良い。フィルム状の熱活性型接着剤は、エチレン
酢酸ビニル共憲曾樹脂（ＥＶＡ）、ポリアミド、ポリエ
ステル。It is used as a top plate for counters, tables, etc. Therefore, K is in contact with the steel base plate of the above-mentioned desk, etc. The adhesive used in the present invention is a heat-activated adhesive, and it may be in either film form or liquid form. . The film-like heat-activated adhesive is made of ethylene vinyl acetate resin (EVA), polyamide, and polyester.
ボリウＶタン等である。この接層剤を化粧板の基材面に
融層する方法は、ａ−ルラミネータを用い。Boliu Vtan etc. This adhesive is applied to the base material surface of the decorative board using an a-lu laminator.
温度１００〜１５０℃、圧力０．５〜２０ｋｇ／ＣＨＩ
で加熱圧着する。Temperature 100-150℃, pressure 0.5-20kg/CHI
Heat and press.
液状の熱活性型接着剤は、上記フィルム状のものと同じ
樹脂を溶剤に溶かした溶液を用いて、基材面に対してロ
ールコーティング方式、フローコーティング方式、櫛々
の印刷方式等によりて所定量を塗布し、塗布面を８０〜
１２０℃で加熱乾燥して樹脂ｍＭＨｔ形成する。Liquid heat-activated adhesives are applied to the substrate surface using a roll coating method, flow coating method, comb printing method, etc. using a solution of the same resin as the film-form adhesive dissolved in a solvent. Apply a fixed amount and apply 80~
Heat and dry at 120°C to form resin mMHt.
さらに、基材面に熱活性型接層剤付き化粧板の接着剤面
を裸状態にして相互に又を１他の物とＮねろとブロッキ
ングをおこす。こｎｉ防ぐために。Further, the adhesive side of the decorative board with a heat-activated adhesive is left exposed on the base material surface, and blocking is caused between each other and another object. To prevent this.
接着剤面に粘Ｎフィルムを貼り甘わせる０〔作用〕
本発明の熱活性型接層剤付き化粧板は、フィルム状及び
液状の何ｎも、テーブル、カウンタ等の鋼製台板に対し
て簡単にｍ度良く熱圧層することができる。Adhering a viscous N film to the adhesive surface to make it sweet 0 [Function] The decorative board with a heat-activated adhesive of the present invention can be applied to steel base plates of tables, counters, etc. in both film and liquid form. It can be easily layered under heat and pressure.
液状の熱活性型接着剤は、溶剤を揮散させる問題がある
にしても化粧板の製造工場で処理するものであって、化
粧板基材に樹脂塗膜として形成した後はフィルム状熱活
注型接層剤と全く同じである０
〔実施例〕
厚さ１．６ＩＩＩＩ１１のメラミン樹脂化粧板の裏面す
なわち基材面に厚さ１５０μのポリアミド樹脂フィルム
を、ａ−ルラミネータを用いて、温度１２０℃圧力３ｋ
ｇ／ａＩｌｌで熱圧層し、さらにブロッキング防止透明
粘Ｎフィルム（日π化成Ａ−１３５５Ｌａ：貼り合わせ
、熱活性型接着剤付き化粧板を得た０こｎを図によりて
説明すると、第１図において。Liquid heat-activated adhesives are processed at decorative laminate manufacturing plants, even though they have the problem of evaporating the solvent, and after being formed as a resin coating on a decorative laminate substrate, they are processed into a film-like heat-activated adhesive. [Example] A polyamide resin film with a thickness of 150μ was placed on the back side of a melamine resin decorative board with a thickness of 1.6III11, that is, on the base material surface, using an a-L laminator at a temperature of 120℃. °C pressure 3k
The process of forming a heat-pressure layer with g/aIll and further laminating an anti-blocking transparent viscous N film (Nippon Kasei A-1355La) to obtain a decorative board with a heat-activated adhesive is as follows. In fig.
化粧樹脂層１と基羽２からなる化粧板の基材面にポリア
ミド樹脂フィルム３を１ね熱圧層する０図はさらに粘着
２イルム４を貼り甘わせた状態を示すＯ
得た熱活性型接層剤付き化粧板と鋼製台板とを温度１０
０℃圧力５ ｋｇ／ａｌＩ’１’熱圧漕した場合、表１
の接ｙＩＩ特性を得た。A heat-pressing layer of a polyamide resin film 3 is applied to the base material surface of a decorative board consisting of a decorative resin layer 1 and a base plate 2. Figure 0 shows a state in which an adhesive film 4 is further pasted and softened. The decorative board with adhesive and the steel base plate are heated to a temperature of 10
Table 1 when heated at 0°C pressure 5 kg/alI'1'
We obtained the tangent yII characteristics.
表 １
〔発明の効果〕
本発明の熱活性型接層剤付き化粧板ｔ−使用することに
よって、机、テーブル等の天板として接層する工程を著
しく全理化省力化することができたが、しかも表１に示
す優ｎた＃＃％性値を確実に得ることが可能となった。Table 1 [Effects of the Invention] By using the decorative board with heat-activated adhesive of the present invention, it was possible to greatly reduce labor and labor in the process of attaching it as a top plate for desks, tables, etc. Moreover, it became possible to reliably obtain the excellent ##% property values shown in Table 1.
第１図は本発明の熱活性型接層剤付き化粧板の態様説明
［Ｆ］である。
１・・・・・・化粧樹脂層、 ２・・・・・・基材
。
３・・・・・・ポリアミド樹脂フィルム、４・・・・・
・粘着フィルム０FIG. 1 is an explanation [F] of a decorative board with a heat-activated adhesive according to the present invention. 1... Decorative resin layer, 2... Base material. 3...Polyamide resin film, 4...
・Adhesive film 0
Claims (1)
接着剤付き化粧板。 ２、化粧板の基材面にフィルム状の熱活性型接着剤層を
加熱加圧により融着形成することを特徴とする請求項１
記載の接着剤付き化粧板の製造方法。 ３、化粧板の基材面に液状の熱活性型接着剤を塗布し塗
膜を形成することを特徴とする請求項１記載の接着剤付
き化粧板の製造方法。[Scope of Claims] 1. A decorative board with an adhesive, which is formed by forming a heat-activated adhesive layer on the base material surface of the decorative board. 2. Claim 1, characterized in that a film-like heat-activated adhesive layer is fused and formed on the base material surface of the decorative board by heating and pressing.
The method for manufacturing the adhesive-backed decorative board described above. 3. The method for manufacturing an adhesive-backed decorative board according to claim 1, wherein a liquid heat-activated adhesive is applied to the base material surface of the decorative board to form a coating film.