JPH0236393A - Method of adhering glass for timepiece - Google Patents
Method of adhering glass for timepieceInfo
- Publication number
- JPH0236393A JPH0236393A JP18636388A JP18636388A JPH0236393A JP H0236393 A JPH0236393 A JP H0236393A JP 18636388 A JP18636388 A JP 18636388A JP 18636388 A JP18636388 A JP 18636388A JP H0236393 A JPH0236393 A JP H0236393A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- case
- adhesive agent
- epoxy resin
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】 〔産業上の利用分野〕 この発明は、時計の製造方法に関する。[Detailed description of the invention] [Industrial application field] The present invention relates to a method of manufacturing a watch.
本発明は時計用ガラスの接着において、時計ケースとエ
ポキシ樹脂接着剤を塗布し、ガラスを設置した後、低粘
度の紫外線硬化型接着剤を充填し紫外線照射を行うこと
により、充填率が高く防水性の高い時計ケースを得よう
としたものである。The present invention involves applying an epoxy resin adhesive to the watch case, installing the glass, and then filling it with a low-viscosity UV-curable adhesive and irradiating it with UV rays to achieve a high filling rate and waterproofing. This was an attempt to obtain a watch case with high quality.
従来の時計用ガラス接着方法としては、エポキシ樹脂接
着剤が用いられ、ケースとガラスの接着を行った後、ガ
ラス側面とケース間に生しる隙間に再度エポキシ樹脂を
充填し硬化を行っていた。Conventional watch glass bonding methods use epoxy resin adhesives, and after bonding the case and glass, the gap between the side of the glass and the case is filled with epoxy resin again and cured. .
〔発明が解決しようとする課題)
しかし、上記のような方法においては、接着剤の硬化処
理が2回必要であること、エポキシ樹脂のボットライフ
の関係から、接着剤の調整が2度になること、さらに、
低粘度のエポキシ樹脂がないため充填作業が困難である
欠点を有していた。[Problem to be solved by the invention] However, in the above method, the adhesive needs to be cured twice, and the adhesive needs to be adjusted twice due to the bot life of the epoxy resin. In addition,
It had the disadvantage that filling work was difficult because it did not contain a low-viscosity epoxy resin.
上記問題点を解決するために、本発明においては充填剤
として低粘度の紫外線硬化型接着剤を使用することによ
り紫外線硬化時の反応熱により、エポキシ樹、指接着剤
の硬化も同時に行うようにした。In order to solve the above problems, in the present invention, by using a low viscosity ultraviolet curable adhesive as a filler, the epoxy resin and finger adhesive are cured at the same time by the reaction heat during ultraviolet curing. did.
上記の様な構成によれば、接着剤の硬化処理工程が1回
で済み作業時間の短縮が可能となる。さらに、エポキシ
樹脂接着剤では得られない低粘性により、流動性が改善
されるため接着剤の充填率が高まり接着部の防水性が向
上する。又、エポキシ樹脂が完全に硬化する前に、同し
く未硬化の紫外線硬化剤樹脂が接触するため、接着2層
の界面の強度も高めることができる。According to the above configuration, the adhesive curing process is performed only once, and the working time can be shortened. Furthermore, the low viscosity that cannot be obtained with epoxy resin adhesives improves fluidity, which increases the filling rate of the adhesive and improves the waterproofness of the bonded area. Furthermore, since the uncured ultraviolet curing resin comes into contact with the epoxy resin before it is completely cured, the strength of the interface between the two adhesive layers can also be increased.
以下に本発明の実施例を図面に基づいて説明する。第1
図において、ステンレス製時計ケース1を電解洗浄して
、表面の酸化被膜を完全に除去した後、ビスフェノール
A系エポキシ樹脂接着剤2を塗布する6次にガラス3を
設置する。さらに時計ケース1とガラス3の間に生じた
隙間部分に粘度950cpsの変性アクリル系の紫外線
硬化型接着剤をデイスペンサーで塗布し、高圧水銀ラン
プで紫外線を照射し硬化させた。Embodiments of the present invention will be described below based on the drawings. 1st
In the figure, a stainless steel watch case 1 is electrolytically cleaned to completely remove the oxide film on the surface, and then a glass 3 is installed on which a bisphenol A-based epoxy resin adhesive 2 is applied. Further, a modified acrylic ultraviolet curable adhesive with a viscosity of 950 cps was applied to the gap created between the watch case 1 and the glass 3 using a dispenser, and was cured by irradiating ultraviolet rays with a high pressure mercury lamp.
このようにして得られた時計ケースは、ガラス部の初期
接着強度が85kg/calを示し、40℃、95%R
1+の恒温恒温試験240時間後も55 kg / c
tAと高い接着強度を保持していることがわかった。さ
らに防水性を調べるためにIO気圧の加圧試験を行った
ところ、初期においても、前述の耐久性試験後も、防水
性は良好であった。The watch case thus obtained had an initial adhesive strength of 85 kg/cal at 40°C and 95% R.
55 kg/c even after 240 hours of constant temperature constant temperature test of 1+
It was found that adhesive strength as high as tA was maintained. Furthermore, in order to investigate the waterproofness, a pressurization test at IO atmospheric pressure was conducted, and the waterproofness was found to be good both at the initial stage and after the aforementioned durability test.
この他、エポキシ系接着剤としては、エポキノフェノー
ル系、エポキシナイロン系、紫外線硬化型接着剤として
は、変性ウレタン系についても同様な効果が確認された
。In addition, similar effects were confirmed for epoxy adhesives such as epoxy phenol and epoxy nylon, and for ultraviolet curing adhesives such as modified urethane.
この発明は以上説明したように、エポキシ樹脂を塗布し
た後、低粘度の紫外線硬化型接着剤を充填することによ
り、接着部の密閉性を高め、防水性の高い時計ケースの
製造を容易にする効果がある。As explained above, this invention improves the airtightness of the bonded area by filling it with a low-viscosity ultraviolet curable adhesive after applying the epoxy resin, making it easier to manufacture highly waterproof watch cases. effective.
第1図はこの発明にかかる時計ケースの断面図である。 ■・・・時計ケース 2・・・エポキシ樹脂接着剤 3・・・ガラス 4・・・紫外線硬化型接着剤 以上 出願人 セイコー電子工業株式会社 代理人 弁理士 林 敬 之 助 1時引ケース 本発明の実施例の断面図 第 ] 図 FIG. 1 is a sectional view of a watch case according to the present invention. ■・・・Watch case 2...Epoxy resin adhesive 3...Glass 4...UV curing adhesive that's all Applicant: Seiko Electronics Industries Co., Ltd. Agent: Patent Attorney Takayoshi Hayashi 1 hour discount case Cross-sectional view of an embodiment of the present invention Figure
Claims (1)
布し、ガラスを設置した後、粘度1000cps以下の
紫外線硬化型接着剤をケースとガラスの空隙に充填し、
紫外線照射で両方の接着剤を硬化させることにより、接
着することを特徴とする時計用ガラスの接着方法。After applying epoxy resin adhesive to the glass support part of the watch case and installing the glass, fill the gap between the case and the glass with an ultraviolet curing adhesive with a viscosity of 1000 cps or less.
A watch glass bonding method characterized by bonding by curing both adhesives with ultraviolet irradiation.