JPH0223964A - 消臭剤 - Google Patents
消臭剤Info
- Publication number
- JPH0223964A JPH0223964A JP63172585A JP17258588A JPH0223964A JP H0223964 A JPH0223964 A JP H0223964A JP 63172585 A JP63172585 A JP 63172585A JP 17258588 A JP17258588 A JP 17258588A JP H0223964 A JPH0223964 A JP H0223964A
- Authority
- JP
- Japan
- Prior art keywords
- copper
- compound
- effective
- ion
- basic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は優れた消臭能を有する消臭剤に関するものであ
る。
る。
従来より脱臭剤としては活性炭がよく知られており、産
業用、家庭用として多用されている。また、活性炭以外
にも数多くの消臭能を有する物質が知られており、消臭
能を有する物質単独あるいはその数種類を組み合せてな
る消臭剤がある。更に１最近になって、有機カルボン酸
と亜鉛あるいはアルミニウムとの化合物を脱臭剤として
、これをアクリル系線維に含有させてなる脱臭性を有す
る繊維が出てきた（特開昭６３−６６３２０公報）。
業用、家庭用として多用されている。また、活性炭以外
にも数多くの消臭能を有する物質が知られており、消臭
能を有する物質単独あるいはその数種類を組み合せてな
る消臭剤がある。更に１最近になって、有機カルボン酸
と亜鉛あるいはアルミニウムとの化合物を脱臭剤として
、これをアクリル系線維に含有させてなる脱臭性を有す
る繊維が出てきた（特開昭６３−６６３２０公報）。
しかし、これらの消臭剤は、全ての種類の悪臭に対して
有効なものではない。
有効なものではない。
一方、銅イオンを結合含有する化合物はよく知られてお
り、種々の用途釦用いられている。
り、種々の用途釦用いられている。
例えば、溶液中での化学反応の触媒として用いられたり
、あるいはフタロシアニン鋼のような顔料として用いら
れたりしている。
、あるいはフタロシアニン鋼のような顔料として用いら
れたりしている。
しかし、この−銅イオンが空気中の悪臭物質（例エバア
ンモニア、硫化水素、エチルメルカプタン）Ｋ対し、優
れた消臭効果を示すことは全（知られていない。
ンモニア、硫化水素、エチルメルカプタン）Ｋ対し、優
れた消臭効果を示すことは全（知られていない。
近年、消臭剤に対するニーズは急激に増大しつつある。
上記のニーズに答えるべく、椎々の化合物を検討した結
果、銅イオンを含む化合物が各種の悪臭（例えば、アン
モニア、硫化水素、エチルメルカプタン）に対し、優れ
た消臭効果を示し、消臭剤として適していることを見い
出した。
果、銅イオンを含む化合物が各種の悪臭（例えば、アン
モニア、硫化水素、エチルメルカプタン）に対し、優れ
た消臭効果を示し、消臭剤として適していることを見い
出した。
即ち、本発明は鋼イオンを含む化合物からなる消臭剤に
関するものである。
関するものである。
以下、本発明の消臭剤について、更に詳細に説明する。
本発明の消臭剤は、鋼イオンを含む化合物である。この
銅イオンが２価であって、これを結合した陰イオン性官
能基が、カルボキシル基と７１０ゲンイオンを除く酸性
官能基である場合は、塩基性の悪臭ガス（特にアンモニ
ア）に対して有効である。これらの例としては、硫酸銅
、硝酸鋼、リン酸鋼、クロム酸銅の無機化合物を代表と
して、パラスチレンスルホン酸銅や、これを共重合成分
として含有するポリマーなと有機金属化合物である。
銅イオンが２価であって、これを結合した陰イオン性官
能基が、カルボキシル基と７１０ゲンイオンを除く酸性
官能基である場合は、塩基性の悪臭ガス（特にアンモニ
ア）に対して有効である。これらの例としては、硫酸銅
、硝酸鋼、リン酸鋼、クロム酸銅の無機化合物を代表と
して、パラスチレンスルホン酸銅や、これを共重合成分
として含有するポリマーなと有機金属化合物である。
銅イオンが２価であって、陰イオン性官能基が塩基性で
ある場合は、酸性もしくは中性の悪臭ガス（特に硫化水
素、エチルメルカプタン）に対し有効である。これらの
例としては水酸化銅や塩基性炭酸銅が挙げられる。
ある場合は、酸性もしくは中性の悪臭ガス（特に硫化水
素、エチルメルカプタン）に対し有効である。これらの
例としては水酸化銅や塩基性炭酸銅が挙げられる。
銅イオンが１価もしくは２価であって、陰イオン性官能
基がノ・ログンイオンである場合は、塩基性、中性、酸
性の悪臭ガス（特Ｋ、アンモニア、エチルメルカプタン
、硫化水素）のいずれに対しても有効であり、非常に有
用である。これらの例としては、フッ化第１銅、フッ化
第２銅、塩化第１銅、塩化第２銅、臭化第１銅、臭化第
２銅、ヨウ化第１鋼、ヨウ化第２銅がある。
基がノ・ログンイオンである場合は、塩基性、中性、酸
性の悪臭ガス（特Ｋ、アンモニア、エチルメルカプタン
、硫化水素）のいずれに対しても有効であり、非常に有
用である。これらの例としては、フッ化第１銅、フッ化
第２銅、塩化第１銅、塩化第２銅、臭化第１銅、臭化第
２銅、ヨウ化第１鋼、ヨウ化第２銅がある。
銅イオンが２価であって、陰イオン性官能基が、カルボ
キシル基である場合も、塩基性、中性酸性の悪臭ガス（
特にアンモニア、エチルメルカプタン、硫化水素）のい
ずれに対しても有効であり、非常に有用である。これは
、（Ｒ−Ｃｏｏ＋２Ｃｕ： （Ｒ：Ｈもしくは有機残基
）で代表される有機カルボン酸銅のいずれでもよい。そ
の例は、ギ酸銅、酢酸銅、硝酸鋼、イタコン酸銅、コノ
・り酸銅、マレイン酸銅、ポリアクリル酸鋼等があげら
れる。
キシル基である場合も、塩基性、中性酸性の悪臭ガス（
特にアンモニア、エチルメルカプタン、硫化水素）のい
ずれに対しても有効であり、非常に有用である。これは
、（Ｒ−Ｃｏｏ＋２Ｃｕ： （Ｒ：Ｈもしくは有機残基
）で代表される有機カルボン酸銅のいずれでもよい。そ
の例は、ギ酸銅、酢酸銅、硝酸鋼、イタコン酸銅、コノ
・り酸銅、マレイン酸銅、ポリアクリル酸鋼等があげら
れる。
これらの化合物を使用するにあたっては、和紙のような
通気性の良い紙で包んだり、あらい結晶のものを、その
ままカラムに充填したり、あるいは、増粒剤とともに増
粒し、粒度を上げてからカラムにつめ込んだりして用い
ることができる。
通気性の良い紙で包んだり、あらい結晶のものを、その
ままカラムに充填したり、あるいは、増粒剤とともに増
粒し、粒度を上げてからカラムにつめ込んだりして用い
ることができる。
また粒体のまま、直接悪臭源に添加することもできる。
また、これらの化合物は、各種の悪臭成分と反応するこ
とＫよって色の変化を伴なう場合が多く、各種の悪臭に
対するインジケーターとしても使用できる場合もある。
とＫよって色の変化を伴なう場合が多く、各種の悪臭に
対するインジケーターとしても使用できる場合もある。
以下、本発明を実施例によって更に詳１１１ＩＩＫ説明
する。
する。
なお、測定法は次のとおりである。
（硫化水素に対する消臭能の測定法）
試料を０．５９秤取し、これを通気性の良い和紙で包み
３００ｍ／三角フラスコ内につるし、ここに、純度６６
％硫化鉄４１ｎ９と９％硫酸２１を入れ２３℃下で２時
間放置した後、内部のガス濃度をガス検知管にて測定し
た。
３００ｍ／三角フラスコ内につるし、ここに、純度６６
％硫化鉄４１ｎ９と９％硫酸２１を入れ２３℃下で２時
間放置した後、内部のガス濃度をガス検知管にて測定し
た。
（エチルメルカプタンに対する消臭能の測定法）試料ｏ
、ｓｙを秤取し、これを通気性の良い和紙で包み３ｏ
ｏｗｌ三角フラスコ内につるし、これに、エチルメルカ
プタン溶液を２μｌ注入し、２３℃下で２時間放置した
後、内部のガス濃度をガス検知管にて測定した。
、ｓｙを秤取し、これを通気性の良い和紙で包み３ｏ
ｏｗｌ三角フラスコ内につるし、これに、エチルメルカ
プタン溶液を２μｌ注入し、２３℃下で２時間放置した
後、内部のガス濃度をガス検知管にて測定した。
実施例１
代表的な酸性官能基を有する２価の銅イオン化合物とし
て硫酸鋼と硝酸銅を用い、比較例としてヤシガラ活性炭
を用いそれぞれ０．５．９秤取し通気性の良い和紙で包
み、３００ｍ三角フラスコ中につるし、ここに１％アン
モニア水を注入し、２３℃下で２時間放置した後、フラ
スコ内のガス濃度を測定した結果を表１に示した。
て硫酸鋼と硝酸銅を用い、比較例としてヤシガラ活性炭
を用いそれぞれ０．５．９秤取し通気性の良い和紙で包
み、３００ｍ三角フラスコ中につるし、ここに１％アン
モニア水を注入し、２３℃下で２時間放置した後、フラ
スコ内のガス濃度を測定した結果を表１に示した。
表 １
以上のように酸性官能基と結合した２価の銅イオンはア
ンモニアに対し、きわめて有効な消臭剤であることがわ
かる。
ンモニアに対し、きわめて有効な消臭剤であることがわ
かる。
実施例２
代表的な塩基性官能基を有する２価の銅イオン化合物と
して、水酸化鋼と塩基性炭酸鋼を用いて、硫化水素及び
エチルメルカプタンに対する消臭能を調べた結果を表２
に示した。
して、水酸化鋼と塩基性炭酸鋼を用いて、硫化水素及び
エチルメルカプタンに対する消臭能を調べた結果を表２
に示した。
表 ２
また、２価の銅イオンと結合した陰イオン性官能基がカ
ルボキシル基である化合物の例とし【、酢酸鋼とポリア
クリル酸銅な用い、また比較例として、ヤシガラ活性炭
を用いてアンモニア、エチルメルカプタン、硫化水素の
３１！１の悪臭ガスについて実施例１と２で示した方法
にのっとって、その消臭効果を調べた結果を表３に示し
た。
ルボキシル基である化合物の例とし【、酢酸鋼とポリア
クリル酸銅な用い、また比較例として、ヤシガラ活性炭
を用いてアンモニア、エチルメルカプタン、硫化水素の
３１！１の悪臭ガスについて実施例１と２で示した方法
にのっとって、その消臭効果を調べた結果を表３に示し
た。
表 ３
以上のよ５Ｋ、塩基性官能基と結合した２価の銅イオン
は硫化水素、エチルメルカプタンに対し有効な消臭剤で
あることがわかる。
は硫化水素、エチルメルカプタンに対し有効な消臭剤で
あることがわかる。
実施例３
銅イオンが１価もしくは２価であって、これと結合した
陰イオン性官能基がハロゲンである化合物の例として、
塩化第１銅及び塩化第２銅を用い、以上のように、ここ
で示したタイプの銅イオンを含む化合物は活性炭に比べ
。３種のガス全てに対して有効であるという、きわめて
有用な消臭剤であることがわかる。
陰イオン性官能基がハロゲンである化合物の例として、
塩化第１銅及び塩化第２銅を用い、以上のように、ここ
で示したタイプの銅イオンを含む化合物は活性炭に比べ
。３種のガス全てに対して有効であるという、きわめて
有用な消臭剤であることがわかる。
以上のように本発明の銅イオンを含む化合物を有効成分
とする消臭剤は、気相中の悪臭成分に対し、きわめて有
効な消臭効果をもたらすものである。
とする消臭剤は、気相中の悪臭成分に対し、きわめて有
効な消臭効果をもたらすものである。
捕出臥 旭化成工業株式会社
Claims (1)
- １．銅イオンを結合含有する化合物を有効成分とする消
臭剤