JPH02116534A - Manufacture of formed item - Google Patents
Manufacture of formed itemInfo
- Publication number
- JPH02116534A JPH02116534A JP27049588A JP27049588A JPH02116534A JP H02116534 A JPH02116534 A JP H02116534A JP 27049588 A JP27049588 A JP 27049588A JP 27049588 A JP27049588 A JP 27049588A JP H02116534 A JPH02116534 A JP H02116534A
- Authority
- JP
- Japan
- Prior art keywords
- knitted fabric
- knitted
- binder fiber
- fibers
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〈産業上のl’ll用分野〉
本発明はニット地を用いた各種の成形品の製造法に関す
るしのである。DETAILED DESCRIPTION OF THE INVENTION <Industrial field> The present invention relates to a method for producing various molded articles using knitted fabrics.
〈従来の技術〉
不織布に比較的融点の低いバインダー繊維を混合し、こ
れを金型にて該繊?(1の溶融温度付近またはそれ以上
の温度で加熱成形し、種々の成形品、例えばバット芯等
を製造することはよく知られている。<Prior art> Binder fibers with a relatively low melting point are mixed with a nonwoven fabric, and the fibers are molded into a mold. (It is well known that various molded products, such as bat cores, etc., can be produced by heat molding at temperatures near or above the melting temperature of 1.
〈発明が解決しようとする課題〉
不織布を使用して金型による熱成形を行った従来の成形
品は不織布の特徴である外力に対する等方性をうまく利
用したものであるが、かかる成形品においては以下のよ
うな問題かあった。<Problems to be Solved by the Invention> Conventional molded products using nonwoven fabrics and thermoformed with a mold make good use of the isotropy with respect to external forces, which is a characteristic of nonwoven fabrics. had the following problems.
1)不織布自体の強力が不足するため強い力の加わる用
途に使用出来ない。1) Because the nonwoven fabric itself is not strong enough, it cannot be used in applications where strong force is applied.
2)不織布自体の作り方が、繊維の絡合やバインダーに
よる接着力によっている為、洗濯やその池の繰り返しの
曲げ力の作用により不織布の強力が低下したり、破壊さ
れたり4−ろ。2) Since the non-woven fabric itself is made based on the entanglement of fibers and the adhesive strength of the binder, the strength of the non-woven fabric may decrease or be destroyed by the bending force of washing or repeated washing.
3)ある程度の強力を得るため不織布がかなりの厚味の
あるものとなり、薄くて・強力のゐろ成形品を得る事が
難しい。3) In order to obtain a certain degree of strength, the nonwoven fabric must be quite thick, making it difficult to obtain a thin and strong white molded product.
本発明は上記の問題点を解決し、薄くてしかも形態安定
性及び強度的に浸れた繊維成形品を金型を用いた加熱成
形により製造することを目的とするしのである。The object of the present invention is to solve the above-mentioned problems and to produce a thin fiber molded article with excellent shape stability and strength by heat molding using a mold.
く課題を解決ずろ為の手段〉
即ち、本発明は、バインダー繊維を含何する編糸よりな
るニット地を成形用金型に供給し、該バインダーV&誰
が溶融しうる温度条件下でニット池を加熱成形すること
を特徴とする成形品の製造法である。Means for Solving the Problems> That is, the present invention supplies a knit fabric made of knitting yarn containing binder fibers to a mold for molding, and heats the knit pond under temperature conditions that can melt the binder V&. This is a method for producing a molded article characterized by heat molding.
本発明でニット地を構成する編糸には、バインダー繊維
か含まれていなければならないが、バインダー繊維と組
み合せて用いられる他の繊維は特に限定されろことはな
く、天然、半合成、合成繊維の中から任意に選ぶことが
可能である。The knitting yarn constituting the knitted fabric in the present invention must contain binder fibers, but other fibers used in combination with the binder fibers are not particularly limited and may include natural, semi-synthetic, and synthetic fibers. It is possible to arbitrarily choose from among them.
しかしながら、本発明においては、ニット地を金型へ供
給して、加熱成形する際、バインダー繊維以外の繊維が
溶融してしまったり、著しく劣化してしまう事は好まし
くないので、使用するバインダー繊維の流動開始温度又
は融点との関係て他の繊維を適切に選ぶことが望まれる
。However, in the present invention, when the knitted fabric is supplied to a mold and heat-formed, it is undesirable for fibers other than the binder fibers to melt or deteriorate significantly. It is desirable to select other fibers appropriately in relation to flow onset temperature or melting point.
本発明において使用されるバインダー繊維は、従来公知
のバインダー繊維をそのまま使用することがてき、例え
ば変成ポリエステル、変性ナイロ〉或いはポリエチレン
等のポリマー単独からなる繊−a、や、成形品の強度を
向上させるために、低融点成分を鞘部としてそれより融
点の高い成分を芯部として構成されるような芯鞘構造の
複合繊維、低融点成分と高融点成分とがサイドバイサイ
ド型こ配置された複合繊維等を使用することができる。The binder fibers used in the present invention can be conventionally known binder fibers as they are, such as fibers made of a single polymer such as modified polyester, modified nylon, or polyethylene, and fibers that improve the strength of molded products. Composite fibers have a core-sheath structure in which a low melting point component is used as a sheath and a component with a higher melting point is used as a core, and a composite fiber in which a low melting point component and a high melting point component are arranged side by side. etc. can be used.
これら複合成分の組み合せとしては、例えば、ポリエチ
レン/ポリプロピレン、ポリエチレン/ポリエステル、
変性ポリエステル/ポリエステル、変性ナイロン/ポリ
エステル等種々の溶融紡糸可能なポリマーの組み合什が
可能である。Examples of combinations of these composite components include polyethylene/polypropylene, polyethylene/polyester,
Various melt spinnable polymer combinations are possible, such as modified polyester/polyester, modified nylon/polyester, etc.
かかるバインダーisのニット地中における含有率は3
0重指形以上、好ましくは50〜70重量%である。3
0重量%未満ては最終成形品中の繊維間若しくは糸組織
間での融着性か不良となり、成形後の形態安定性が低下
する。The content rate of this binder is in the knit fabric is 3
It is more than 0 double fingers, preferably 50 to 70% by weight. 3
If it is less than 0% by weight, the fusion properties between fibers or yarn structures in the final molded product will be poor, and the shape stability after molding will be reduced.
本発明においてニット地を構成する編糸は、バインダー
繊維100%からなっていてもよいが、通常、バインダ
ー繊維と池の繊維との混紡糸として用いられろ。バイン
ダー繊維が、昆紡糸の外周付近により多く存在している
コアヤーン、両繊維の混繊らしくは引き揃え糸、バイン
ダー繊維以外の繊維の紡績糸又は拳フィラメントにバイ
ンダー繊維の紡績糸又はフィラメントを交撚したもの等
が使用されろ。The knitting yarn constituting the knitted fabric in the present invention may be composed of 100% binder fiber, but is usually used as a blended yarn of binder fiber and pond fiber. A core yarn in which the binder fiber is present more near the outer periphery of the kunbo yarn, a drawn yarn that seems to be a blend of both fibers, a spun yarn of a fiber other than the binder fiber, or a twisted filament with a spun yarn or filament of the binder fiber. Please use the one that was given.
本発明では、このような編糸を用いてニット地を作成す
る。この場合、ニット地の編組織等は特に限定されるこ
とはないが、金型による成形性をより良くするため、伸
度か30%以上、好ましくは50%以上のニット地であ
ることが有効であり、このようなニット地は熱可塑性樹
脂ノートの深絞り成形のように成形時に大きな変形を伴
っても比較的均一に成形でき、しかち薄手のものでも自
由に1戊形てきるという特徴を有するものである。In the present invention, a knitted fabric is created using such a knitting yarn. In this case, the knitting structure of the knit fabric is not particularly limited, but in order to improve moldability with a mold, it is effective to use a knit fabric with an elongation of 30% or more, preferably 50% or more. This type of knitted fabric can be formed relatively uniformly even if it undergoes large deformation during forming, such as deep drawing of thermoplastic resin notebooks, and even thin fabrics can be freely shaped into one shape. It has the following.
本発明において、ニット地を金型を用いて成形する方法
は従来、熱可塑性耐指等を成形する際に使用されている
加熱成形機等を利用することができる。即ち、ニット地
に含有されているバイノダ繊維の流動開始温度或いは融
点性との温度に予め設定された成形金型上に、ニット地
を供給し、次いで1〜敗分間保持することによって製造
できるものである。In the present invention, as a method for forming the knitted fabric using a mold, a thermoforming machine or the like that has been conventionally used for forming thermoplastic finger resistant materials or the like can be used. That is, it can be manufactured by feeding a knitted fabric onto a mold that is preset at a temperature that matches the flow start temperature or melting point of the Binoda fibers contained in the knitted fabric, and then holding it for a period of 1 to 30 minutes. It is.
ここで、金型の設定温度は高すぎると、バインダー繊維
以外の繊維の溶融や劣化をまねきやすいので庄キ深く設
定しなければならない。また、賦形の際の圧縮力はほと
んど必要と仕ず、得ようとする成形品のffヨ状が単純
なものであれば所定の形状の型の上にニット地を載置し
て、1方より熱風を吹きつけ゛ろノこけてら製造するこ
とかできる。Here, if the set temperature of the mold is too high, fibers other than the binder fibers tend to melt or deteriorate, so the temperature must be set deeply. In addition, almost no compression force is required during shaping, and if the shape of the molded product to be obtained is simple, the knitted fabric is placed on a mold of a predetermined shape, and then It can also be manufactured by blowing hot air from one side to the other side.
本発明の製造C去によって得られる成形品は、qパット
広、ブランヤー芯等の立体的な構造が要求されろ衣料用
芯地、家兜小物用芯地に利用でき、更には、ツユリンク
包装的な包装用素材に応用でき、種々の用途に展開でき
る乙のである。The molded product obtained by the production method of the present invention can be used as interlining for clothing, interlining for household helmets, etc. that require a three-dimensional structure such as Q-pat wide, branyard interlining, etc. It can be applied to various packaging materials and can be used for various purposes.
〈実施例〉
以下、実意例によって本発明を説明するが、本発明は何
らこれに限定されろものではない。<Example> The present invention will be described below with reference to practical examples, but the present invention is not limited thereto in any way.
実施例1及び比較例1
通常のポリエステル繊u(1,5デニール、51m1T
I長)を300≦及び芯部がポリエステル鞘部が変成ポ
リエステル(融点110℃)からなる芯鞘型複合繊維(
2デニール、51mm長)を70%含む、昆紡糸を作成
した(棉番手:20番手)。この紡績糸を使用し、20
ゲーノのノングルノヤーノイ編機で天竺組織のニット地
を作り、これを非イオン系洗浄剤の入った温浴(1g/
Q、50°C)中で20分間撹陣洗浄し、脱水後70°
Cで乾燥した。Example 1 and Comparative Example 1 Ordinary polyester fiber u (1.5 denier, 51m1T
I length) is 300≦ and the core is made of polyester and the sheath part is made of modified polyester (melting point 110°C).
2 denier, 51 mm length) was produced (cotton count: 20 count). Using this spun yarn, 20
A knit fabric with a jersey texture is made using Geno's non-grey knitting machine, and it is soaked in a hot bath containing a non-ionic detergent (1 g/
Q, 50°C) for 20 minutes, then dehydrated and then washed at 70°C.
It was dried at C.
得らnた編地の伸度(JISL1068、グラブ法)は
経方向40%、緯方向60%であり、目付は150g/
m’であった。このニット地を成形金型上に供給し、1
50°Cx1分間加鳩成形し、カップ状の成形品を得た
。The elongation (JISL1068, Grab method) of the obtained knitted fabric was 40% in the warp direction and 60% in the weft direction, and the basis weight was 150 g/
It was m'. This knitted fabric is supplied onto a molding die, and 1
The molded product was molded at 50°C for 1 minute to obtain a cup-shaped molded product.
また、比較例として上記と同じポリエステル繊維30%
とバインダー繊維准70%とを、昆綿し、メタリックカ
ードでウェッブを作成した後、ニードルパンチ機にて不
織布を作成した(目付145g/m’ )。In addition, as a comparative example, 30% of the same polyester fiber as above
and 70% binder fiber were kombinized and a web was created using a metallic card, and then a nonwoven fabric was created using a needle punch machine (fabric weight: 145 g/m').
そして、この不織布を実施例1と同様にしてカップ状成
形品とした。Then, this nonwoven fabric was made into a cup-shaped molded product in the same manner as in Example 1.
それぞれの成形品の性能を第1表に示した。Table 1 shows the performance of each molded product.
以下余白
第
表
第1表からもわかるように、本発明の成形品は繰り返し
洗濯後においても、破裂強さが十分保持されており、こ
れに比べ不織布からなる成形品は、成形時に引伸ばされ
薄くなった部分より破れ、洗濯後においても破裂強さは
著しく悪く実用性のないもので、あった。As can be seen from Table 1 of the margin table below, the molded product of the present invention retains sufficient bursting strength even after repeated washing, and in comparison, molded products made of nonwoven fabric are not stretched during molding. It tore at the thinner part, and its burst strength was extremely poor even after washing, making it impractical.
〈発明の効果〉
本発明においては、成形品の素材ンートとしてニット地
を使用するため、その伸び変形が大きく、金型に沿って
深絞り的な成彩や複雑な影状の成形ら可能となり、しか
も、成形により最終製品の厚さの均一性が損われること
がない。また、成形時に軟化溶融したニット構成糸中の
バインダー繊維は、成形後に繊維間および糸間さらには
組織そのものを強固に接着固定するため、成形品の伸度
が抑えられある作文のソフトさを有しながらも形態安定
性か向上する。<Effects of the Invention> In the present invention, since knitted fabric is used as the raw material for the molded product, its elongation deformation is large, and it is possible to perform deep drawing-like coloring along the mold and molding into complex shadow shapes. Moreover, the uniformity of the thickness of the final product is not impaired by the molding. In addition, the binder fibers in the knit constituent yarns that are softened and melted during molding firmly adhere and fix the fibers and threads as well as the structure itself after molding, which suppresses the elongation of the molded product and gives it a certain softness. However, the morphological stability is improved.
Claims (1)
を成形用金型に供給し、該バインダー繊維が溶融しうる
温度条件下でニット地を加熱成形することを特徴とする
成形品の製造法。(1) A method for producing a molded article, which comprises supplying a knitted fabric made of knitting yarn containing binder fibers to a molding die, and heating and forming the knitted fabric under temperature conditions that allow the binder fibers to melt. .