JPH0121997Y2 - - Google Patents
Info
- Publication number
- JPH0121997Y2 JPH0121997Y2 JP1984195486U JP19548684U JPH0121997Y2 JP H0121997 Y2 JPH0121997 Y2 JP H0121997Y2 JP 1984195486 U JP1984195486 U JP 1984195486U JP 19548684 U JP19548684 U JP 19548684U JP H0121997 Y2 JPH0121997 Y2 JP H0121997Y2
- Authority
- JP
- Japan
- Prior art keywords
- water
- woven
- knitted fabric
- sweat
- repellent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
本考案は、スポーツ衣料をるいは作業着等の着
用時の汗のベトツキ現象を解消した織・編物に関
する。[Detailed Description of the Invention] The present invention relates to a woven or knitted fabric that eliminates the stickiness caused by sweat when wearing sports clothing or work clothes.
従来、汗のベトツキ現象を解消するための方法
として、一般的には織・編物に吸汗性を付与し、
織・編物に汗を吸収させ汗を速く乾かす方法があ
つた。しかし、この方法では激しい運動の際に出
た多量の汗を吸いとつた織・編物は汗がバインダ
ーの役割をして肌と密着し、不快な感じを与える
という欠点があつた。 Conventionally, as a method to eliminate the sticky phenomenon of sweat, the general method is to impart sweat absorption properties to woven and knitted fabrics.
There was a way to make woven and knitted fabrics absorb sweat and dry it quickly. However, this method has the disadvantage that the woven and knitted fabrics that absorb large amounts of sweat produced during intense exercise act as a binder and stick to the skin, giving an uncomfortable feeling.
又、織・編物の表全面に吸水性、裏全面に撥水
性を付与する方法がある。しかし、この方法も吸
水面が肌に触れている場合は先に述べたと同じ
で、ベトツキ感があり、逆に撥水面が肌に触れて
いる場合は、織・編物が汗を吸いとらないため、
汗が肌の上を流れ落ちなかなか乾かないという欠
点があつた。 There is also a method of imparting water absorbency to the entire surface of a woven or knitted material and water repellency to the entire back surface. However, with this method, if the water-absorbing side is in contact with the skin, it will feel sticky, as mentioned above, and conversely, if the water-repellent side is in contact with the skin, the woven or knitted fabric will not absorb the sweat. ,
The drawback was that sweat ran down the skin and did not dry easily.
本考案は上記の欠点を解消し、織・編物の裏面
に点状、線状又は格子状に撥水性を付与し、その
他の部分に吸水性を付与することによつて汗のベ
トツキ現象を克服した織・編物を提供することを
目的としている。 The present invention solves the above-mentioned drawbacks and overcomes the sticky phenomenon of sweat by imparting water repellency to the back side of woven/knitted fabrics in dots, lines, or lattice shapes, and imparting water absorbency to other parts. The aim is to provide quality woven and knitted fabrics.
本考案の織・編物の一例を添付図面を参照して
説明すると、織・編物１はその裏面に点状、線状
又は格子状に撥水剤２を付着させ、その他の部分
る吸水剤３を付着させたことを特徴としている。
この様な撥水性と吸水性とをもつ織・編物は、撥
水剤を含んだ糊剤を捺染、又はコーテイング方式
にて点状、線状又は格子状に塗布し、乾燥、熱処
理して撥水剤を織・編物に固着させ、次いで湯染
して糊剤を脱落させ、その後、この織・編物を吸
水加工剤の水溶液に含浸、浸漬し、マングルで絞
り乾燥、熱処理し吸水剤を撥水剤の付いていない
織・編物の部分に固着させることによつて作られ
る。 An example of the woven/knitted fabric of the present invention will be described with reference to the accompanying drawings.A woven/knitted fabric 1 has a water repellent 2 attached to its back surface in dots, lines, or a grid pattern, and a water absorbent 3 attached to other parts. It is characterized by having attached.
Woven and knitted fabrics with such water repellency and water absorption properties are made by applying a paste containing a water repellent agent in dots, lines, or grids using a printing or coating method, drying, and heat-treating to make them repellent. The water agent is fixed to the woven/knitted fabric, and then hot water dyed to remove the glue.Then, the woven/knitted fabric is impregnated and immersed in an aqueous solution of the water-absorbing finishing agent, squeezed dry with a mangle, and heat-treated to repel the water-absorbing agent. It is made by adhering it to parts of woven or knitted fabrics that do not have a liquid agent attached.
織・編物のこの構成によれば、肌上の汗は織・
編物の点状、線状又は格子状の撥水剤ではじかれ
て、これに隣接して位置する吸水剤で吸収され
織・編物に浸入する。従つてベトツキ感がなく、
しかも汗が織・編物を通して外部に運ばれるため
に大気空気との接触により速乾性を発揮する。 According to this structure of woven and knitted fabrics, sweat on the skin is absorbed by woven and knitted fabrics.
It is repelled by the dot-shaped, linear, or lattice-shaped water repellent on the knitted fabric, absorbed by the water-absorbing agent located adjacent to it, and penetrates into the woven/knitted fabric. Therefore, there is no sticky feeling,
Moreover, since sweat is carried to the outside through the woven or knitted fabric, it dries quickly when it comes into contact with atmospheric air.
実施例 １
フアインガムHEL10％液（第一工業製薬(株)プ
リント糊） 72％
アサヒガードAG710（旭硝子(株)撥水剤） ５％
水 23％
上記の撥水剤を含んだプリント糊をポリエステ
ル織物に125メツシユロータリースクリーンで点
状にプリントし120℃×２分乾燥を行つた。次に
170℃×１分熱処理を行い固着させ、次いで70℃
×10分湯洗を行つた。120℃×２分乾燥後、下記
の吸水剤溶液で浸漬しマングルで絞り、乾燥、熱
処理を行つた。Example 1 Faingum HEL 10% liquid (Daiichi Kogyo Seiyaku Co., Ltd. print glue) 72% Asahi Guard AG710 (Asahi Glass Co., Ltd. water repellent) 5% Water 23% Print glue containing the above water repellent was applied to polyester fabric Dots were printed using a 125 mesh rotary screen and dried at 120°C for 2 minutes. next
Heat treated at 170℃ for 1 minute to solidify, then heated to 70℃
I washed it with hot water for 10 minutes. After drying at 120°C for 2 minutes, it was immersed in the following water-absorbing agent solution, squeezed with a mangle, dried, and heat-treated.
SR1000（高松油脂(株)吸水剤） ５％
水 95％
出来あがつた織物は、撥水プリントした面に水
滴を落すと１〜２秒のうちになくなり、撥水面は
ほとんどぬれた状態とならず、反対側の面に水滴
の輪が拡がつたものとなつた。 SR1000 (Takamatsu Yushi Co., Ltd. Water Absorbing Agent) 5% Water 95% If you drop a drop of water on the water-repellent printed surface of the finished fabric, it will disappear within 1-2 seconds, leaving the water-repellent surface almost wet. Then, a ring of water droplets spread out on the opposite surface.
実施例 ２
ミネラルターベン（三菱油化(株)プリント糊）
60％
K380（酒伊エンジニヤリング(株)界面活性剤）
30％
アサヒガードAG730（旭硝子(株)撥水剤） 10％
上記の撥水剤を含んだプリント糊をナイロン
100％織物に100メツシユロータリースクリーンで
点状にプリントし、以下実施例１と同様な処理を
施したところ、実施例１と同様な効果が得られ
た。Example 2 Mineral turbine (Mitsubishi Yuka Co., Ltd. print glue)
60% K380 (Sakai Engineering Co., Ltd. surfactant)
30% Asahi Guard AG730 (Asahi Glass Co., Ltd. water repellent) 10% Print glue containing the above water repellent on nylon
When dots were printed on a 100% fabric using a 100 mesh rotary screen and the same treatment as in Example 1 was performed, the same effects as in Example 1 were obtained.
添付図面は本考案による織・編物の概略断面図
である。
１……織・編物、２……撥水剤、３……吸水
剤。
The accompanying drawing is a schematic cross-sectional view of a woven or knitted fabric according to the present invention. 1...Woven/knitted fabric, 2...Water repellent, 3...Water absorbing agent.
Claims (1)
子状に付着させ、その他の部分に吸水剤を付着さ
せたことを特徴とする撥水性および吸水性を付与
した織・編物。 A woven or knitted fabric imparted with water repellency and water absorption, characterized in that a water repellent agent is attached to the back side of the woven or knitted fabric in dots, lines or grids, and a water absorbing agent is attached to the other parts.