JP7257797B2 - Concrete setting time determination device, determination method and concrete construction method - Google Patents
Concrete setting time determination device, determination method and concrete construction method Download PDFInfo
- Publication number
- JP7257797B2 JP7257797B2 JP2019010455A JP2019010455A JP7257797B2 JP 7257797 B2 JP7257797 B2 JP 7257797B2 JP 2019010455 A JP2019010455 A JP 2019010455A JP 2019010455 A JP2019010455 A JP 2019010455A JP 7257797 B2 JP7257797 B2 JP 7257797B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- setting time
- resistance value
- penetration resistance
- hardness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、打込み後のコンクリートの表面を仕上げるためのコンクリート凝結時間判定装置、判定方法およびコンクリート施工方法に関するものである。 TECHNICAL FIELD The present invention relates to a concrete setting time determination device, a determination method, and a concrete construction method for finishing the surface of concrete after placing.
従来、直押え床やスラブ状構造物のコンクリート施工において、押え作業は、（１）レベル出し（かき板均し）→（２）定規ずり→（３）アマ出し（機械コテ（円盤）使用）→（４）金ゴテ仕上げ（機械コテ（プロペラ）使用）の作業順序で概ね行われている。このうち（３）、（４）の作業は、コンクリートの凝結硬化速度と密接に関係するが（例えば、特許文献１を参照）、そのタイミングに関わる凝結時間を現場で測定することはまれであり、作業者の経験と勘によるところが大きい。 Conventionally, in the concrete construction of direct pressing floors and slab-like structures, the pressing work consists of (1) Leveling (scraping board leveling) → (2) Ruler sliding → (3) Hammering (using a machine trowel (disk)) → (4) Metal trowel finishing (using a mechanical trowel (propeller)) is generally performed in the order of work. Of these, the work of (3) and (4) is closely related to the setting and hardening speed of concrete (see, for example, Patent Document 1), but it is rare to measure the setting time related to that timing on site. , largely depends on the experience and intuition of the operator.
図３は押え着手のタイミングの説明図、図４は外気温による凝結時間の変化の一例である。図３に示すように、上記の（３）、（４）の作業の着手タイミングは一般に、凝結を示すプロクター貫入抵抗値が０．３～１．０Ｎ／ｍｍ２の時点とされている。一方、コンクリートの凝結硬化速度は、図４に示すように、外気温にも大きく左右される。こうしたことから、上記作業の着手タイミングを施工管理者が判断するためにはプロクター貫入試験などの煩雑な現場試験が必要であるため、上述したように作業者の経験と勘に委ねられていたのが現状である。 FIG. 3 is an explanatory diagram of the timing of starting pressing, and FIG. 4 is an example of a change in the condensation time depending on the outside temperature. As shown in FIG. 3, the work (3) and (4) is generally started when the proctor penetration resistance value indicating condensation is 0.3 to 1.0 N/mm 2 . On the other hand, as shown in FIG. 4, the setting and hardening speed of concrete is greatly influenced by the outside air temperature. For this reason, complicated on-site tests such as proctor penetration tests are required for construction managers to determine when to start the above work. is the current situation.
なお、本出願人は、コンクリートの表面の押え作業のタイミングに関して、特許文献２に記載の床押え施工方法を既に提案している。これは、コテ装置を使用して硬化前のコンクリート床面の押え作業を行うための方法であって、床面に打ち込まれるコンクリートに、気温に応じて凝結遅延剤または凝結促進剤を添加してコンクリートの凝結速度を調整し、打ち込んだ後のコンクリート床面の押え作業を開始するタイミングを制御するステップと、制御したタイミングでコンクリート床面の押え作業を開始するステップとを備えるものである。これにより、作業効率を向上することが可能である。
The applicant of the present application has already proposed a floor pressing construction method described in
ところで、上記の従来の特許文献２では、実際のコンクリートの凝結硬化速度は、施工条件によって異なるため、養生の開始タイミングが計画通りにいくことが難しいと考えられることから、凝結硬化の計測箇所を何箇所か設けて、代用特性（土壌硬度計やデュロメータおよび電気抵抗値などであらかじめ把握）で確認することを提案している。しかし、実際の土壌硬度計などの代用特性の使用方法は明らかではなく、現場で簡易に凝結時間を判定することのできる技術が求められていた。
By the way, in the above-mentioned
本発明は、上記に鑑みてなされたものであって、コンクリートの凝結時間を簡易に判定することのできるコンクリート凝結時間判定装置、判定方法およびコンクリート施工方法を提供することを目的とする。 SUMMARY OF THE INVENTION It is an object of the present invention to provide a concrete setting time determination apparatus, a determination method, and a concrete construction method that can easily determine the setting time of concrete.
上記した課題を解決し、目的を達成するために、本発明に係るコンクリート凝結時間判定装置は、コンクリートの凝結時間を判定する装置であって、コンクリートの表面の硬度を計測する硬度計測手段と、計測した硬度をコンクリートの貫入抵抗値に換算する換算手段と、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定する判定手段とを備えることを特徴とする。 In order to solve the above-described problems and achieve the object, a concrete setting time determination device according to the present invention is a device for determining the setting time of concrete, which comprises hardness measuring means for measuring the hardness of the surface of concrete; It is characterized by comprising conversion means for converting the measured hardness into a penetration resistance value of concrete, and determination means for determining the setting time of concrete based on the converted penetration resistance value.
また、本発明に係る他のコンクリート凝結時間判定装置は、上述した発明において、硬度計測手段は土壌硬度計であり、換算手段は硬度を支持強度に換算し、さらに支持強度を貫入抵抗値に換算することを特徴とする。 Further, in another concrete setting time determination device according to the present invention, in the above-described invention, the hardness measuring means is a soil hardness meter, and the converting means converts the hardness into a supporting strength and further converts the supporting strength into a penetration resistance value. characterized by
また、本発明に係るコンクリート凝結時間判定方法は、コンクリートの凝結時間を判定する方法であって、コンクリートの表面の硬度を計測するステップと、計測した硬度をコンクリートの貫入抵抗値に換算するステップと、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定するステップとを備えることを特徴とする。 Further, a concrete setting time determination method according to the present invention is a method for determining the setting time of concrete, comprising the steps of measuring the hardness of the surface of concrete, and converting the measured hardness into a penetration resistance value of concrete. and determining the setting time of concrete based on the converted penetration resistance value.
また、本発明に係る他のコンクリート凝結時間判定方法は、上述した発明において、土壌硬度計で硬度を計測した後、計測した硬度を支持強度に換算し、さらに支持強度を貫入抵抗値に換算することを特徴とする。 Another concrete setting time determination method according to the present invention is, in the above-described invention, measuring hardness with a soil hardness meter, converting the measured hardness into supporting strength, and further converting the supporting strength into a penetration resistance value. It is characterized by
また、本発明に係るコンクリート施工方法は、コンクリートを施工する方法であって、上記のコンクリート凝結時間判定装置、または、コンクリート凝結時間判定方法を用いてコンクリートの凝結時間を判定した後、判定した凝結時間に基づいて硬化前のコンクリートの表面の押え作業を行うことを特徴とする。 Further, a concrete construction method according to the present invention is a method for constructing concrete, wherein after determining the concrete setting time using the concrete setting time determination device or the concrete setting time determination method, the determined setting time is determined. It is characterized in that the surface of concrete before hardening is pressed based on time.
本発明に係るコンクリート凝結時間判定装置によれば、コンクリートの凝結時間を判定する装置であって、コンクリートの表面の硬度を計測する硬度計測手段と、計測した硬度をコンクリートの貫入抵抗値に換算する換算手段と、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定する判定手段とを備えるので、現場でプロクター貫入試験をすることなく、また試験用試料を採取することなく、極めて簡易に凝結時間を判定することができるという効果を奏する。 According to the concrete setting time determination device according to the present invention, the device is a device for determining the setting time of concrete, and includes hardness measuring means for measuring the hardness of the surface of concrete, and converting the measured hardness into a penetration resistance value of concrete. Equipped with a conversion means and a judgment means for judging the setting time of concrete based on the converted penetration resistance value, the setting can be performed very easily without conducting a proctor penetration test on site and without collecting a test sample. The effect is that the time can be determined.
また、本発明に係る他のコンクリート凝結時間判定装置によれば、硬度計測手段は土壌硬度計であり、換算手段は硬度を支持強度に換算し、さらに支持強度を貫入抵抗値に換算するので、コンクリートの品質に大きな影響を与えることなく、極めて簡易に凝結時間を判定することができるという効果を奏する。 Further, according to another concrete setting time determination device according to the present invention, the hardness measuring means is a soil hardness tester, and the converting means converts the hardness into a supporting strength, and further converts the supporting strength into a penetration resistance value. The effect is that the setting time can be determined very easily without significantly affecting the quality of concrete.
また、本発明に係るコンクリート凝結時間判定方法によれば、コンクリートの凝結時間を判定する方法であって、コンクリートの表面の硬度を計測するステップと、計測した硬度をコンクリートの貫入抵抗値に換算するステップと、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定するステップとを備えるので、現場でプロクター貫入試験をすることなく、また試験用試料を採取することなく、極めて簡易に凝結時間を判定することができるという効果を奏する。 Further, according to the concrete setting time determination method according to the present invention, the concrete setting time determination method comprises the step of measuring the hardness of the surface of the concrete, and converting the measured hardness into the penetration resistance value of the concrete. and a step of determining the setting time of concrete based on the converted penetration resistance value. There is an effect that it can be determined.
また、本発明に係る他のコンクリート凝結時間判定方法によれば、土壌硬度計で硬度を計測した後、計測した硬度を支持強度に換算し、さらに支持強度を貫入抵抗値に換算するので、コンクリートの品質に大きな影響を与えることなく、極めて簡易に凝結時間を判定することができるという効果を奏する。 Further, according to another concrete setting time determination method according to the present invention, after the hardness is measured with a soil hardness meter, the measured hardness is converted into supporting strength, and the supporting strength is converted into a penetration resistance value. There is an effect that the setting time can be determined very easily without greatly affecting the quality of the product.
また、本発明に係るコンクリート施工方法によれば、コンクリートを施工する方法であって、上記のコンクリート凝結時間判定装置、または、コンクリート凝結時間判定方法を用いてコンクリートの凝結時間を判定した後、判定した凝結時間に基づいて硬化前のコンクリートの表面の押え作業を行うので、作業者の経験と勘に頼ることなく、判定結果に基づいて押え作業を開始でき、施工管理を容易にすることができるという効果を奏する。 Further, according to the concrete construction method according to the present invention, there is provided a method for constructing concrete, in which after determining the concrete setting time using the concrete setting time determination device or the concrete setting time determination method, the determination is performed. Since the work to hold down the surface of the concrete before hardening is performed based on the set setting time, the work to hold down can be started based on the determination result without relying on the experience and intuition of the worker, and construction management can be facilitated. It has the effect of
以下に、本発明に係るコンクリート凝結時間判定装置、判定方法およびコンクリート施工方法の実施の形態を図面に基づいて詳細に説明する。なお、この実施の形態によりこの発明が限定されるものではない。 EMBODIMENT OF THE INVENTION Below, embodiment of the concrete setting time determination apparatus, determination method, and concrete construction method based on this invention is described in detail based on drawing. In addition, this invention is not limited by this embodiment.
図１に示すように、本実施の形態に係るコンクリート凝結時間判定装置１０は、硬度計測手段１２と、換算手段１４と、判定手段１６とを備える。
As shown in FIG. 1 , the concrete setting
硬度計測手段１２は、コンクリートの表面の硬度を計測するものであり、例えば土壌硬度計で構成することができる。本実施の形態では、測定原理が山中式土壌硬度計のものを想定しているが、他の方式の硬度計でもよい。また、アナログ式、デジタル式のどちらでもよい。 The hardness measuring means 12 measures the hardness of the surface of concrete, and can be composed of, for example, a soil hardness meter. In this embodiment, it is assumed that the Yamanaka soil hardness meter is used for the measurement principle, but other types of hardness meters may be used. Moreover, either an analog type or a digital type may be used.
換算手段１４は、計測した硬度をコンクリートの貫入抵抗値に換算するものである。この換算手段１４は、コンピュータなどの演算装置と、メモリやデータベースなどの記録装置と、キーボードなどの入力装置と、モニタなどの出力装置を用いて構成されているが、本発明はこれに限るものではない。換算手段１４による換算は、あらかじめ設定した換算表や換算式などを用いて行うことができる。例えば、データベースなどに換算表や換算式を登録しておき、換算手段１４がこの換算表や換算式を参照することで、計測した硬度を貫入抵抗値に換算する。換算手段１４は、計測した硬度を支持強度に一旦換算してから、この支持強度を貫入抵抗値に換算してもよい。 The conversion means 14 converts the measured hardness into a penetration resistance value of concrete. The conversion means 14 is composed of an arithmetic device such as a computer, a recording device such as a memory or a database, an input device such as a keyboard, and an output device such as a monitor, but the present invention is limited to this. isn't it. The conversion by the conversion means 14 can be performed using a preset conversion table, conversion formula, or the like. For example, a conversion table or conversion formula is registered in a database or the like, and the conversion means 14 refers to this conversion table or conversion formula to convert the measured hardness into a penetration resistance value. The conversion means 14 may convert the measured hardness into the support strength once and then convert the support strength into the penetration resistance value.
判定手段１６は、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定するものである。この判定手段１６は、コンピュータなどの演算装置と、メモリやデータベースなどの記録装置と、キーボードなどの入力装置と、モニタなどの出力装置を用いて構成されているが、本発明はこれに限るものではない。判定手段１６による判定は、あらかじめ設定した判定条件などを用いて行うことができる。例えば、データベースなどに判定条件を登録しておき、判定手段１６がこの判定条件と貫入抵抗値を比較参照することで、コンクリートの凝結時間を判定する。 The determining means 16 determines the setting time of concrete based on the converted penetration resistance value. The judging means 16 is composed of an arithmetic device such as a computer, a recording device such as a memory or a database, an input device such as a keyboard, and an output device such as a monitor, but the present invention is limited to this. isn't it. The judgment by the judging means 16 can be made using preset judging conditions or the like. For example, determination conditions are registered in a database or the like, and the determining means 16 compares and refers to the determination conditions and the penetration resistance value to determine the setting time of concrete.
上記構成の動作および作用について説明する。
まず、打込んだコンクリートの施工箇所の中から硬度の計測箇所を設定する。計測箇所とする場所は、コンクリート締固め時にφ１００～２００ｍｍ程度の囲いなどを設置して、粗骨材の影響が少なくなるように、コンクリート表層にモルタルを集めて簡単に仕上げておくことが好ましい。ただし囲いはなくてもよい。モルタルを集めた箇所を作るのは、土壌硬度計が粗骨材に接触して測定値の変動が大きくなることを避けるためである。
The operation and action of the above configuration will be described.
First, the hardness measurement points are set from among the placed concrete construction points. It is preferable to install a fence with a diameter of about 100 to 200 mm when compacting the concrete, and to collect mortar on the surface of the concrete and finish it easily so that the influence of coarse aggregate is reduced. However, there may be no enclosure. The purpose of creating a place where mortar is collected is to prevent the soil hardness meter from coming into contact with coarse aggregate and causing large fluctuations in measured values.
その箇所において、コンクリートのブリーディングがひいて水分が見えなくなった後、土壌硬度計を水平に持ち、土壌硬度計の先端の円錐部をコンクリート表面に円錐部上のつばが密着するまで確実に押し付ける。土壌硬度計の本体の指標が移動しないように静かに円錐部を引き抜き、本体の硬度目盛の値を読む。測定は、同一時間に３回以上行ってその平均を取ると精度が向上するが、モルタル面に押し付ける場合は１回でもよい。なお、デジタル式の土壌硬度計の場合は、デジタル値で表示される。 At that point, after the concrete has stopped bleeding and the water is no longer visible, hold the soil hardness tester horizontally and press the conical part at the tip of the soil hardness tester firmly against the concrete surface until the collar on the conical part comes in close contact. Gently pull out the cone part so that the indicator on the main body of the soil hardness meter does not move, and read the value on the hardness scale of the main body. If the measurement is performed three times or more at the same time and the average is taken, the accuracy will be improved. In the case of a digital soil hardness meter, the value is displayed as a digital value.
次に、こうして計測した硬度を換算手段１４で支持強度（Ｎ／ｍｍ２）に換算し、さらに支持強度を貫入抵抗値に換算する。 Next, the hardness thus measured is converted into supporting strength (N/mm 2 ) by the converting means 14, and the supporting strength is further converted into a penetration resistance value.
図２は、支持強度と貫入抵抗値の関係の一例を示したものである。この図には、土壌硬度計に添付の換算表から読み取った支持強度、プロクター貫入試験による実験値のプロットと、このプロットの回帰式を示している。この図によれば、貫入抵抗値（ｙ）と、土壌硬度計から得た支持強度（ｘ）との関係は、凝結の始発時間に対応する貫入抵抗値３．５Ｎ／ｍｍ２を境に異なる回帰式で表すことができる。貫入抵抗値３．５Ｎ／ｍｍ２以下の場合は、図２（１）に従い、凝結の貫入抵抗値＝１．２５×支持強度（換算値）＋０．３（Ｎ／ｍｍ２）という関係式を用いることができる。貫入抵抗値３．５Ｎ／ｍｍ２を超えた場合は、図２（２）に従い、凝結の貫入抵抗値＝１．７５×支持強度（換算値）＋０．１７（Ｎ／ｍｍ２）という関係式を用いることができる。なお、この図に示すように、実験では多少のばらつきが認められる。しかし、押え作業の着手タイミングの凝結の貫入抵抗値の数値は厳密ではないため、問題ない精度である。 FIG. 2 shows an example of the relationship between supporting strength and penetration resistance. This figure shows a plot of supporting strength read from the conversion table attached to the soil hardness meter, experimental values obtained by the Proctor Penetration Test, and a regression equation for this plot. According to this figure, the relationship between the penetration resistance value (y) and the supporting strength (x) obtained from the soil hardness tester differs at a penetration resistance value of 3.5 N/mm 2 corresponding to the first settling time. It can be expressed by a regression equation. If the penetration resistance value is 3.5 N/mm 2 or less , according to FIG. can be used. When the penetration resistance value exceeds 3.5 N/mm 2 , according to FIG. can be used. In addition, as shown in this figure, some variation is observed in the experiment. However, since the numerical value of the penetration resistance value of coagulation at the start timing of the pressing work is not exact, there is no problem in accuracy.
次に、上記の関係式に支持強度を代入することで、貫入抵抗値を求める。求めた貫入抵抗値に基づいて、判定手段１６がコンクリートの凝結時間を判定する。この判定結果に基づいて、押え作業（例えば、アマ出し（機械コテ（円盤）使用）、金ゴテ仕上げ（機械コテ（プロペラ）使用））の着手タイミングを決定する。 Next, the penetration resistance value is obtained by substituting the supporting strength into the above relational expression. Based on the determined penetration resistance value, the determining means 16 determines the setting time of concrete. Based on the result of this determination, the start timing of pressing work (for example, shoveling (using a machine iron (disk)) and metal trowel finishing (using a machine iron (propeller))) is determined.
実際のコンクリートの凝結硬化速度は、施工条件によって異なるため、押え作業の着手タイミングに関連する凝結時間を把握することは難しいと考えられる。しかしながら、本実施の形態によれば、現場でプロクター貫入試験をすることなく、また試験のために試料を別の容器に取ることなく、極めて簡易に凝結の貫入抵抗値を測定することができる。これにより、極めて簡易にコンクリートの凝結時間を判定することができる。また、施工管理者も測定値や判定結果に基づいて作業を管理することができ、作業者の経験と勘に頼らなくてよい。 Since the actual setting and hardening speed of concrete varies depending on the construction conditions, it is considered difficult to grasp the setting time related to the start timing of pressing work. However, according to the present embodiment, the penetration resistance value of condensation can be measured very easily without performing the proctor penetration test on site and without taking the sample into another container for the test. This makes it possible to determine the setting time of concrete very easily. Moreover, the construction manager can also manage the work based on the measured values and judgment results, and does not have to rely on the experience and intuition of the worker.
また、現場のコンクリートでモルタルとする部分は全体のごく一部であり、コンクリートの品質に影響を及ぼすほどの面積ではなく、かつ仕上げの作業で土壌硬度計の刺し穴も消すことが可能である。さらに、現場でコンクリートと同一箇所で計測するため、温度履歴などが同一の条件で実施でき、信頼性が高い。 In addition, the concrete mortar at the site is only a small part of the whole, and the area is not large enough to affect the quality of the concrete. . Furthermore, since measurements are taken at the same location as the concrete on site, the temperature history can be measured under the same conditions, resulting in high reliability.
また、本実施の形態に係るコンクリート施工方法は、上記のコンクリート凝結時間判定装置１０または判定方法を用いてコンクリートの凝結時間を判定した後、判定した凝結時間に基づいて硬化前のコンクリートの表面の押え作業を行うものである。これによれば、作業者の経験と勘に頼ることなく、判定結果に基づいて押え作業を開始でき、施工管理を容易にすることができる。
Further, in the concrete construction method according to the present embodiment, after determining the concrete setting time using the above-described concrete setting
以上説明したように、本発明に係るコンクリート凝結時間判定装置によれば、コンクリートの凝結時間を判定する装置であって、コンクリートの表面の硬度を計測する硬度計測手段と、計測した硬度をコンクリートの貫入抵抗値に換算する換算手段と、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定する判定手段とを備えるので、現場でプロクター貫入試験をすることなく、また試験用試料を採取することなく、極めて簡易に凝結時間を判定することができる。 INDUSTRIAL APPLICABILITY As described above, according to the concrete setting time determination device according to the present invention, the device determines the setting time of concrete, and includes hardness measuring means for measuring the hardness of the surface of the concrete, and measurement of the measured hardness of the concrete. Since it is equipped with conversion means for converting into a penetration resistance value and judgment means for judging the setting time of concrete based on the converted penetration resistance value, it is possible to collect a test sample without conducting a proctor penetration test on site. Therefore, the setting time can be determined very easily.
また、本発明に係る他のコンクリート凝結時間判定装置によれば、硬度計測手段は土壌硬度計であり、換算手段は硬度を支持強度に換算し、さらに支持強度を貫入抵抗値に換算するので、コンクリートの品質に大きな影響を与えることなく、極めて簡易に凝結時間を判定することができる。 Further, according to another concrete setting time determination device according to the present invention, the hardness measuring means is a soil hardness tester, and the converting means converts the hardness into a supporting strength, and further converts the supporting strength into a penetration resistance value. The setting time can be determined very easily without significantly affecting the quality of concrete.
また、本発明に係るコンクリート凝結時間判定方法によれば、コンクリートの凝結時間を判定する方法であって、コンクリートの表面の硬度を計測するステップと、計測した硬度をコンクリートの貫入抵抗値に換算するステップと、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定するステップとを備えるので、現場でプロクター貫入試験をすることなく、また試験用試料を採取することなく、極めて簡易に凝結時間を判定することができる。 Further, according to the concrete setting time determination method according to the present invention, the concrete setting time determination method comprises the step of measuring the hardness of the surface of the concrete, and converting the measured hardness into the penetration resistance value of the concrete. and a step of determining the setting time of concrete based on the converted penetration resistance value. can judge.
また、本発明に係る他のコンクリート凝結時間判定方法によれば、土壌硬度計で硬度を計測した後、計測した硬度を支持強度に換算し、さらに支持強度を貫入抵抗値に換算するので、コンクリートの品質に大きな影響を与えることなく、極めて簡易に凝結時間を判定することができる。 Further, according to another concrete setting time determination method according to the present invention, after the hardness is measured with a soil hardness meter, the measured hardness is converted into supporting strength, and the supporting strength is converted into a penetration resistance value. The setting time can be determined very easily without significantly affecting the quality of the product.
また、本発明に係るコンクリート施工方法によれば、コンクリートを施工する方法であって、上記のコンクリート凝結時間判定装置、または、コンクリート凝結時間判定方法を用いてコンクリートの凝結時間を判定した後、判定した凝結時間に基づいて硬化前のコンクリートの表面の押え作業を行うので、作業者の経験と勘に頼ることなく、判定結果に基づいて押え作業を開始でき、施工管理を容易にすることができる。 Further, according to the concrete construction method according to the present invention, there is provided a method for constructing concrete, in which after determining the concrete setting time using the concrete setting time determination device or the concrete setting time determination method, the determination is performed. Since the work to hold down the surface of the concrete before hardening is performed based on the set setting time, the work to hold down can be started based on the determination result without relying on the experience and intuition of the worker, and construction management can be facilitated. .
以上のように、本発明に係るコンクリート凝結時間判定装置、判定方法およびコンクリート施工方法は、打込み後のコンクリートの表面を仕上げる作業の着手タイミングを判断するのに有用であり、特に、作業者の経験と勘に頼ることなく簡易に判断するのに適している。 INDUSTRIAL APPLICABILITY As described above, the concrete setting time determination apparatus, determination method, and concrete construction method according to the present invention are useful for determining the start timing of finishing the surface of concrete after pouring. It is suitable for making a simple judgment without relying on intuition.
１０ コンクリート凝結時間判定装置
１２ 硬度計測手段
１４ 換算手段
１６ 判定手段
10 concrete setting
Claims (3)
コンクリートの表面の硬度を計測する土壌硬度計である硬度計測手段と、計測した硬度を支持強度に換算し、さらにこの支持強度をコンクリートの貫入抵抗値に換算する換算手段と、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定する判定手段とを備え、
支持強度と貫入抵抗値の関係を示す回帰式として、コンクリートの凝結の始発時間に対応する貫入抵抗値を境に異なる回帰直線式をあらかじめ設定しておき、
前記換算手段は、前記回帰直線式に、換算した支持強度を代入することで、換算した支持強度に対応する貫入抵抗値を求めることを特徴とするコンクリート凝結時間判定装置。 An apparatus for determining the setting time of concrete, comprising:
A hardness measuring means, which is a soil hardness tester for measuring the hardness of the surface of concrete, a conversion means for converting the measured hardness into supporting strength, further converting this supporting strength into a penetration resistance value of concrete, and a converted penetration resistance value. and determining means for determining the setting time of concrete based on
As a regression equation showing the relationship between the bearing strength and the penetration resistance value, different regression linear equations are set in advance with the penetration resistance value corresponding to the initial setting time of concrete as a boundary,
The concrete setting time determination device, wherein the conversion means obtains a penetration resistance value corresponding to the converted support strength by substituting the converted support strength into the regression line equation.
コンクリートの表面の硬度を土壌硬度計で計測する計測ステップと、計測した硬度を支持強度に換算し、さらにこの支持強度をコンクリートの貫入抵抗値に換算する換算ステップと、換算した貫入抵抗値に基づいてコンクリートの凝結時間を判定する判定ステップとを備え、
支持強度と貫入抵抗値の関係を示す回帰式として、コンクリートの凝結の始発時間に対応する貫入抵抗値を境に異なる回帰直線式をあらかじめ設定しておき、
前記換算ステップは、前記回帰直線式に、換算した支持強度を代入することで、換算した支持強度に対応する貫入抵抗値を求めることを特徴とするコンクリート凝結時間判定方法。 A method for determining the setting time of concrete, comprising:
A measurement step of measuring the hardness of the concrete surface with a soil hardness meter , a conversion step of converting the measured hardness into a supporting strength, and further converting this supporting strength into a penetration resistance value of concrete, and a conversion step based on the converted penetration resistance value a determination step of determining the setting time of concrete by
As a regression equation showing the relationship between the bearing strength and the penetration resistance value, different regression linear equations are set in advance with the penetration resistance value corresponding to the initial setting time of concrete as a boundary,
The concrete setting time determination method, wherein the conversion step is to obtain a penetration resistance value corresponding to the converted support strength by substituting the converted support strength into the regression line equation.
請求項１に記載のコンクリート凝結時間判定装置、または、請求項２に記載のコンクリート凝結時間判定方法を用いてコンクリートの凝結時間を判定した後、判定した凝結時間に基づいて硬化前のコンクリートの表面の押え作業を行うことを特徴とするコンクリート施工方法。 A method of constructing concrete, comprising:
After determining the setting time of concrete using the concrete setting time determination device according to claim 1 or the concrete setting time determination method according to claim 2 , the surface of the concrete before hardening based on the determined setting time A concrete construction method characterized by performing a pressing work of.