JP6802361B2 - 光学フィルムならびにこれを有する画像表示装置の前面板、画像表示装置、画像表示機能付きミラ−、抵抗膜式タッチパネルおよび静電容量式タッチパネル - Google Patents
光学フィルムならびにこれを有する画像表示装置の前面板、画像表示装置、画像表示機能付きミラ−、抵抗膜式タッチパネルおよび静電容量式タッチパネル Download PDFInfo
- Publication number
- JP6802361B2 JP6802361B2 JP2019508699A JP2019508699A JP6802361B2 JP 6802361 B2 JP6802361 B2 JP 6802361B2 JP 2019508699 A JP2019508699 A JP 2019508699A JP 2019508699 A JP2019508699 A JP 2019508699A JP 6802361 B2 JP6802361 B2 JP 6802361B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin film
- group
- film
- image display
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
例えば、特許文献1には、偏光膜とこの偏光膜を挟持する一対の保護膜とを有する偏光板を有する液晶表示装置が記載されており、この保護膜にはセルロースアシレートフィルムが使用されている。特許文献1によれば、このセルロースアシレートフィルムは、正面及び膜厚方向レターデーションの発現性に優れ、製造、加工時の取り扱いが容易な薄さを有し、視野角特性変化の少ない液晶表示装置を実現できるとされる。
また、特許文献2には、色ムラの発生が抑制されたハードコートフィルムとして、基材と、基材の少なくとも一方の面に積層されたハードコート層とを備え、面内方向のレターデーションが6000nm以上40000nm以下であるハードコートフィルムが記載されている。
本発明者らが鋭意検討した結果、樹脂フィルムの膜厚を厚くすることで打鍵耐久性を改良できることが分かってきた。その一方、樹脂フィルムの膜厚が厚くなるにつれて、平滑性が低下したり、変形したり、厚膜樹脂フィルム製造の際に担体からの剥離が困難になったりする問題が生じることも分かってきた。また、膜厚の厚い樹脂フィルムを製膜するには相応の時間を要すること、特に溶液製膜の場合には、残留溶媒を除去するための乾燥工程がより長くなることから、製造効率の問題も生じてしまう。このように、樹脂フィルムの打鍵耐久性と、樹脂フィルムの外観ないし製造適性(製造効率)との間には、いわゆるトレードオフの関係が生じることが明らかとなってきた。
本発明はこれらの知見に基づきさらに検討を重ね、完成されるに至ったものである。
〔1〕
第一の樹脂フィルム(A)と、この第一の樹脂フィルム(A)の片面に配された接着層(B)と、この接着層(B)のこの第一の樹脂フィルム(A)側とは反対側に配された第二の樹脂フィルム(C)とを少なくとも有し、
上記第一の樹脂フィルム(A)の屈折率nA、上記接着層(B)の屈折率nB及び上記第二の樹脂フィルム(C)の屈折率nCが下記式(1)及び(2)を満たし、
|nA−nB|≦0.03 式(1)
|nC−nB|≦0.03 式(2)
上記第一の樹脂フィルム(A)の引張弾性率EA、上記接着層(B)の引張弾性率EB及び上記第二の樹脂フィルム(C)の引張弾性率ECが下記式(3)〜(7)を満たし、
|EA−EB|≦2.5GPa 式(3)
|EC−EB|≦2.5GPa 式(4)
2.0GPa≦EA≦12.0GPa 式(5)
2.0GPa≦EB≦12.0GPa 式(6)
2.0GPa≦EC≦12.0GPa 式(7)
上記第一の樹脂フィルム(A)と上記第二の樹脂フィルム(C)の少なくとも一方がセルロースエステルフィルムであり、
上記第一の樹脂フィルム(A)、上記接着層(B)及び上記第二の樹脂フィルム(C)の合計厚みが100μmより大きく320μm以下である、光学フィルム。
〔2〕
上記接着層(B)の厚みが10nm以上10μm以下である、〔1〕に記載の光学フィルム。
〔3〕
面内方向のレターデーションが6000nmより小さい、〔1〕又は〔2〕に記載の光学フィルム。
〔4〕
上記第一の樹脂フィルム(A)と上記第二の樹脂フィルム(C)が同一のフィルムである、〔1〕〜〔3〕のいずれか1つに記載の光学フィルム。
〔5〕
上記第一の樹脂フィルム(A)と上記第二の樹脂フィルム(C)を、80℃の環境で48時間保持した後の下記式(8)で表される収縮力Fd(単位:10N/m)が互いに異なる、〔1〕〜〔3〕のいずれか1つに記載の光学フィルム。
式(8) Fd=Ed×εd×dd
式中、Ed、εd、ddは、樹脂フィルムを80℃の環境で48時間保持した後のMD方向の弾性率、MD方向の寸法変化率の絶対値、膜厚をそれぞれ表す。
〔6〕
上記第一の樹脂フィルム(A)と上記第二の樹脂フィルム(C)を、60℃、相対湿度90%の環境で48時間保持した後の下記式(9)で表される収縮力Fw(単位:10N/m)が互いに異なる、〔1〕〜〔3〕のいずれか1つに記載の光学フィルム。
式(9) Fw=Ew×εw×dw
式中、Ew、εw、dwは、樹脂フィルムを60℃、相対湿度90%の環境で48時間保持した後のMD方向の弾性率、MD方向の湿度寸法変化率の絶対値、膜厚をそれぞれ表す。
〔7〕
上記第一の樹脂フィルム(A)及び上記第二の樹脂フィルム(C)の少なくとも一方が、上記接着層(B)と反対側の面にハードコート層を有する、〔1〕〜〔6〕のいずれか1つに記載の光学フィルム。
〔8〕
〔1〕〜〔7〕のいずれか1つに記載の光学フィルムを有する、画像表示装置の前面板。
〔9〕
〔8〕に記載の前面板と、画像表示素子とを有する画像表示装置。
〔10〕
上記画像表示素子が液晶表示素子である、〔9〕に記載の画像表示装置。
〔11〕
上記画像表示素子が有機エレクトロルミネッセンス表示素子である、〔9〕に記載の画像表示装置。
〔12〕
上記画像表示素子がインセルタッチパネル表示素子である、〔9〕〜〔11〕のいずれか1つに記載の画像表示装置。
〔13〕
上記画像表示素子がオンセルタッチパネル表示素子である、〔9〕〜〔11〕のいずれか1つに記載の画像表示装置。
〔14〕
〔8〕に記載の前面板を有する抵抗膜式タッチパネル。
〔15〕
〔8〕に記載の前面板を有する静電容量式タッチパネル。
〔16〕
〔9〕に記載の画像表示装置を用いた画像表示機能付きミラー。
本明細書において、「(メタ)アクリレート」とは、アクリレートとメタクリレートの一方または両方の意味で用いられる。また、「(メタ)アクリロイル基」は、アクリロイル基とメタクリロイル基の一方または両方の意味で用いられる。「(メタ)アクリル」は、アクリルとメタクリルの一方または両方の意味で用いられる。
本明細書に記載の各成分は、この成分を、一種のみ用いてもよく、構造の異なる二種以上を併用してもよい。また、各成分の含有量は、構造の異なる二種以上を併用する場合には、それらの合計含有量を意味する。
本明細書において、各層の厚み、屈折率及び引張弾性率は、実施例記載の方法により測定されるものである。
本発明の光学フィルムは、タッチパネルの前面板等として好適に用いることができ、また、偏光フィルム、位相差フィルム及び液晶表示用の輝度向上フィルム等の光学フィルムとしても好適に用いることができる。
[光学フィルム]
本発明の光学フィルムの好ましい実施形態を図1に示す。図1に示す光学フィルム4Aは、第一の樹脂フィルム(A)と、この第一の樹脂フィルム(A)の片面に配された接着層(B)と、この接着層(B)上に配された第二の樹脂フィルム(C)(図1においては、順に符号1A、2A、1Bで示される。)とを少なくとも有する光学フィルムである。光学フィルムにおける、上記第一の樹脂フィルム(A)の屈折率nA、上記接着層(B)の屈折率nB及び上記第二の樹脂フィルム(C)の屈折率nCは、下記式(1)及び(2)を満たす。本発明において屈折率は、波長589nmの光の25℃における屈折率を意味する。
|nA−nB|≦0.03 式(1)
|nC−nB|≦0.03 式(2)
また、上記第一の樹脂フィルム(A)の25℃における引張弾性率EA、上記接着層(B)の25℃における引張弾性率EB及び上記第二の樹脂フィルム(C)の25℃における引張弾性率ECは、下記式(3)〜(7)を満たす。本発明において引張弾性率は、25℃における引張弾性率を意味する。
|EA−EB|≦4.0GPa 式(3)
|EC−EB|≦4.0GPa 式(4)
2.0GPa≦EA 式(5)
2.0GPa≦EB 式(6)
2.0GPa≦EC 式(7)
さらに、光学フィルムの厚み、すなわち、上記第一の樹脂フィルム(A)と上記接着層(B)と上記第二の樹脂フィルム(C)の合計厚みは、100μmより大きい。
本発明の光学フィルムは上記構成を有することにより、優れた打鍵耐久性を実現することができる。これは、樹脂フィルムに打鍵を重ねると引張弾性率に大きな差がある面で歪みが発生するところ、本発明の光学フィルムでは引張弾性率が特定値以上の2層の樹脂フィルムを、これらの樹脂フィルムと引張弾性率の差が特定の値以下にある接着層を介して積層し、さらに光学フィルム全体を一定以上の厚みとすることにより、この歪みの発生を効果的に抑制できるためと推定される。また、本発明の光学フィルムは、隣接する樹脂フィルムと接着層との間の屈折率の差を特定の値以下にすることで、界面反射を効果的に抑制でき、干渉ムラも抑制できると考えられる。さらに、本発明の光学フィルムは積層体でありながらも、個々のフィルム厚を抑えることができるため、製造適性にも優れている。
樹脂フィルムの屈折率は、例えば、樹脂フィルムを構成する樹脂の種類により変えることができ、一般に、樹脂の分子量及び/又は結晶化度を高めることにより屈折率は高まる傾向がある。また、樹脂フィルムは、延伸により延伸方向の屈折率を高めることができる。樹脂フィルムが多層からなる場合にも、樹脂フィルムとしての屈折率を意味する。
第一の樹脂フィルム(A)の屈折率nA及び第二の樹脂フィルム(C)の屈折率nCは、干渉ムラをより抑制する点から、各々独立に、1.45〜1.62が好ましく、1.47〜1.60がより好ましく、1.48〜1.59がさらに好ましい。
接着層(B)(以下、単に「接着層」とも称す。)の屈折率は、例えば、接着層を構成する樹脂の種類により変えることができ、一般に、樹脂の分子量や結晶化度を高めることにより屈折率は高まる傾向がある。また、接着層の構成成分として微粒子を添加することにより、屈折率を調整することができる。
接着層(B)の屈折率nBは、干渉ムラをより抑制する点から、1.45〜1.62が好ましく、1.47〜1.60がより好ましく、1.48〜1.59がさらに好ましい。
上記式(1)で表される、第一の樹脂フィルム(A)の屈折率nAと接着層(B)の屈折率nBとの差の絶対値(|nA−nB|で記載される。以下において、絶対値と記載しない場合にも同様である。)は、干渉ムラをより抑制する点から、0.02以下が好ましく、0.01以下がより好ましい。下限値は特に制限はなく、0.00以上である。
上記式(2)で表される、第二の樹脂フィルム(C)の屈折率nCと接着層(B)の屈折率nBとの差の絶対値(|nC−nB|で記載される。以下において、絶対値と記載しない場合にも同様である。)は、干渉ムラをより抑制する点から、0.02以下が好ましく、0.01以下がより好ましい。下限値は特に制限はなく、0.00以上である。
樹脂フィルムの引張弾性率は、例えば、樹脂フィルムを構成する樹脂の種類により変えることができ、一般に、樹脂の分子量及び/又は結晶化度を高めることにより引張弾性率は高まる傾向がある。また、樹脂フィルムは、延伸により延伸方向の引張弾性率を高めることができる。樹脂フィルムが多層からなる場合にも、樹脂フィルムとしての引張弾性率を意味する。
第一の樹脂フィルム(A)の25℃における引張弾性率EA及び第二の樹脂フィルム(C)の25℃における引張弾性率ECは、打鍵耐久性をより高める点から、各々独立に、2.5GPa以上が好ましく、3.0GPa以上がより好ましく、3.5GPa以上がさらに好ましく、4.0GPa以上が最も好ましい。上限値は、特に制限はないが、12.0GPa以下が実際的である。
接着層(B)(以下、単に「接着層」とも称す。)の引張弾性率は、例えば、接着層を構成する樹脂の種類により変えることができ、一般に、樹脂の分子量や結晶化度を高めることにより引張弾性率は高まる傾向がある。また、接着層が架橋性基を持つ場合には、架橋剤などの添加によって接着層の架橋度を向上させることにより引張弾性率を高めることができる。さらに、接着層に重合性組成物が含まれる場合は、重合性基を有する化合物の重合性基当量(この化合物の分子量を、この化合物に含まれる重合性基の総数で除した値)の低減、接着層の重合率の向上、接着層への高弾性物質(例えば無機粒子等)の添加、剛直な分子構造(例えばアダマンタン骨格)を含む化合物の添加等により引張弾性率は高まる傾向がある。
接着層(B)の25℃における引張弾性率EBは、打鍵耐久性をより高める点から、2.5GPa以上が好ましく、3.0GPa以上がより好ましく、3.5GPa以上がより好ましく、4.0GPa以上がさらに好ましく、4.5GPa以上が特に好ましく、5.0GPa以上が最も好ましい。上限値は、特に制限はないが、12.0GPa以下が実際的である。
上記式(3)で表される、第一の樹脂フィルム(A)の25℃における引張弾性率EAと接着層(B)の25℃における引張弾性率EBとの差の絶対値(|EA−EB|で記載される。以下において、絶対値と記載しない場合にも同様である。)は、打鍵耐久性をより高める点から、3.4GPa以下が好ましく、3.0GPa以下がより好ましく、2.5GPa以下がより好ましく、2.0GPa以下がさらに好ましく、1.5GPa以下が特に好ましく、1.0GPa以下が最も好ましい。
上記式(4)で表される、第二の樹脂フィルム(C)の25℃における引張弾性率ECと接着層(B)の25℃における引張弾性率EBとの差の絶対値(|EC−EB|で記載される。以下において、絶対値と記載しない場合にも同様である。)は、打鍵耐久性をより高める点から、3.4GPa以下が好ましく、3.0GPa以下がより好ましく、2.5GPa以下がより好ましく、2.0GPa以下がさらに好ましく、1.5GPa以下が特に好ましく、1.0GPa以下が最も好ましい。
本発明の光学フィルムの厚みは、打鍵耐久性の点から、120μm以上が好ましく、150μm以上がより好ましく、180μm以上がさらに好ましく、200μm以上がさらに好ましい。上限値は320μm以下であることが実際的である。
樹脂フィルムの厚みは、打鍵耐久性及び製造適性の点から、各々独立に、50〜160μmが好ましく、60〜160μmがより好ましく、80〜160μmがさらに好ましく、100〜160μmが特に好ましい。
ここで、第一の樹脂フィルムと第二の樹脂フィルムの厚みの合計は、打鍵耐久性の点から、100〜320μmが好ましく、160〜320μmがより好ましく、200〜320μmがさらに好ましい。
(接着層の厚み)
接着層の厚みは、第一の樹脂フィルムと第二の樹脂フィルムを接着する点から10nm以上が好ましく、さらに干渉ムラを抑制する観点から10nm〜10μmが好ましく、10nm〜5μmがより好ましく、10nm〜1μmがさらに好ましい。
光学フィルムの波長550nmにおける面内方向のレターデーションは、干渉ムラを低減する点から、6000nmより小さいことが好ましく、1000nm以下が好ましく、500nm以下がより好ましく、50nm以下がさらに好ましい。
ここで、光学フィルムの面内方向の位相差(レターデーション)は、光学フィルムに直線偏光を入射して、光学フィルムを通過した光を、進相軸および遅相軸に沿った2つの直線偏光に分解したときに、進相軸での屈折率Nxと遅相軸での屈折率Nyおよび光学フィルムの厚さd(単位:nm)とから下記式(A)により示されるR(単位:nm)として定義される。
R=d×(Nx−Ny) (A)
(樹脂フィルムの材質)
本発明に用いられる樹脂フィルムは、光学フィルムを形成した場合に、上記屈折率の規定及び上記引張弾性率の規定を満たすものであれば、その材質は特に限定されない。
樹脂フィルムは、例えば、アクリル樹脂フィルム、ポリカーボネート(PC)樹脂フィルム、セルロースアシレート樹脂フィルム(例えば、トリアセチルセルロース(TAC)樹脂フィルム)等のセルロースエステル樹脂フィルム、ポリエチレンテレフタラート(PET)樹脂フィルム、ポリオレフィン樹脂フィルム、ポリエステル樹脂フィルム、および、アクリロニトリル−ブタジエン−スチレン共重合体フィルムを挙げることができ、アクリル樹脂フィルム、セルロースエステル樹脂フィルム、ポリエチレンテレフタラート樹脂フィルムおよびポリカーボネート樹脂フィルムから選択されるフィルムが好ましく、透湿性の点から、セルロースエステル樹脂フィルムがより好ましい。上記の各種樹脂フィルムは、誘導体及び共重合体等を含む意味で使用する。
尚、アクリル樹脂フィルムとは、アクリル酸エステルおよびメタクリル酸エステルからなる群から選択される1種以上の化合物から形成される重合体または共重合体の樹脂フィルムをいう。アクリル樹脂フィルムの例としては、ポリメタクリル酸メチル樹脂(PMMA)フィルムが挙げられる。
樹脂の重量平均分子量は、引張弾性率を高める点から、10,000〜1000,000が好ましく、100,000〜1000,000がより好ましい。
また、樹脂フィルムの構成も限定されず、単層でも、2層以上からなる積層フィルムであってもよいが、2層以上の積層フィルムが好ましい。積層フィルムの積層数は、2〜10層が好ましく、2〜5層がより好ましく、2層または3層がさらに好ましい。3層以上の場合、外層と外層以外の層(コア層等)とは、異なる組成のフィルムが好ましい。また、外層同士は、同じ組成のフィルムが好ましい。
具体的には、TAC−a/TAC−b/TAC−a、アクリル−a/PC/アクリル−aおよびPET−a/PET−b/PET−aの積層構造を有するフィルム、ならびに、ポリカーボネート樹脂単層のフィルムが挙げられる。ここで、同じ符号(a又はb)を付けたフィルム(例えば、Tac−a)は、同じ組成のフィルムを示す。
樹脂フィルムは、上述の樹脂の他に添加剤を含有してもよい。添加剤としては、後述のハードコート層で記載する、無機粒子、マット粒子、紫外線吸収剤、含フッ素化合物、表面調整剤、レベリング剤等が挙げられる。
後述の溶融製膜法では、上記添加剤と樹脂とを混合溶融した樹脂溶融物として、また、後述の溶液製膜法では、溶媒(後述のハードコートにおける記載を適用できる。)と樹脂と上記添加剤とを混合したドープ液として、樹脂フィルムの形成に用いることができる。
本発明の光学フィルムの作製前後で、樹脂フィルムの厚みはほとんど変化しない。
また、本発明に用いられる樹脂フィルムは、易接着層を有していてもよい。易接着層は、特開2015−224267号公報の段落0098〜0133に記載された偏光子側易接着層および偏光子側易接着層の製造方法の内容を、本発明にあわせて本明細書に組み込むことができる。
この場合、易接着層は、本発明の光学フィルムにおける樹脂フィルム(A)あるいは(C)を構成する層とし、樹脂フィルム(A)あるいは(C)の屈折率および引張弾性率は、易接着層を含む樹脂フィルム(A)あるいは(C)の屈折率および引張弾性率を意味する。
樹脂フィルムは、いずれの方法で製膜してもよく、例えば溶融製膜法および溶液製膜法が挙げられる。
樹脂フィルムを溶融製膜法で製膜する場合、樹脂を押出機で溶融する溶融工程と、溶融した樹脂をダイからシート状に押し出す工程と、フィルム状に成形する工程とを含むことが好ましい。樹脂の材質によっては、溶融工程の後に溶融樹脂のろ過工程を設けてもよく、シート状に押し出す際に冷却してもよい。
以下、具体的な溶膜製膜法を説明するが、本発明はこれに限定されるものではない。
上記樹脂フィルムの製造方法は、樹脂を押出機で溶融する溶融工程と、溶融した樹脂をフィルターが設置されたろ過装置に通してろ過するろ過工程と、ろ過した樹脂をダイからシート状に押し出し、冷却ドラムの上に密着させることにより冷却固化して未延伸の樹脂フィルムを成形するフィルム成形工程と、未延伸の樹脂フィルムを、1軸又は2軸延伸する延伸工程とを有する。
このような構成により、樹脂フィルムを製造することができる。溶融した樹脂のろ過工程で使用されるフィルターの孔径が1μm以下であると、異物を十分に取り除くことができる。その結果、得られる樹脂フィルムのフィルム幅方向の表面粗さを制御することができる。
具体的には、樹脂フィルムの形成方法は下記工程を含むことができる。
上記樹脂フィルムの製造方法は、樹脂を押出機で溶融する溶融工程を含む。
樹脂、または樹脂と添加剤の混合物を含水率200ppm以下に乾燥した後、一軸(単軸)あるいは二軸の押出機に導入し溶融させることが好ましい。この時、樹脂の分解を抑制するために、窒素中あるいは真空中で溶融することも好ましい。詳細な条件は、特許4962661号の<0051>〜<0052>(US2013/0100378号公報の<0085>〜<0086>)を援用して、これらの公報に従い実施でき、これらの公報に記載された内容は本明細書に組み込まれる。
押出機は、一軸混練押出機が好ましい。
さらに、溶融樹脂(メルト)の送り出し精度を上げるためギアポンプを使用することも好ましい。
上記樹脂フィルムの製造方法は、溶融した樹脂をフィルターが設置されたろ過装置に通してろ過するろ過工程を含み、ろ過工程で使用されるフィルターの孔径は1μm以下が好ましい。
このような孔径の範囲のフィルターを有するろ過装置は、ろ過工程において1セットのみ設置してもよく、2セット以上設置してもよい。
上記樹脂フィルムの製造方法は、ろ過した樹脂をダイからシート状に押し出し、冷却ドラムの上に密着させることにより冷却固化して未延伸の樹脂フィルムを成形するフィルム成形工程を含む。
樹脂フィルムが多層で押出されて製造されてなる場合、全層の厚みに対する得られる樹脂フィルムの内層の厚みは、50%以上99%以下が好ましく、より好ましくは60%以上97%以下、さらに好ましくは70%以上95%以下である。このような積層は、フィードブロックダイやマルチマニホールドダイを用いることで実施できる。
ダイから押し出される樹脂の温度は、放射温度計(林電工製、型番:RT61−2、放射率0.95で使用)により樹脂の表面を非接触で測定することができる。
冷却ドラムの上に密着する際の樹脂の温度は、放射温度計(林電工製、型番:RT61−2、放射率0.95で使用)により樹脂の表面を非接触で測定することができる。
上記樹脂フィルムの製造方法は、未延伸の樹脂フィルムを、1軸又は2軸延伸する延伸工程を含む。
縦延伸工程(フィルムの搬送方向と同じ方向に延伸する工程)では、樹脂フィルムが予熱された後、樹脂フィルムが加熱された状態で、周速差のある(すなわち、搬送速度の異なる)ローラー群で搬送方向に延伸される。
(ThTD−max−ThTD−min)÷ ThTD−av×100 [%]
が幅方向の厚みの変動である。
(ThMD−max−ThMD−min)÷ ThMD−av×100 [%]
が長手方向の厚みの変動である。
樹脂フィルムを溶液製膜法で製膜する場合、ドープ液を流延バンド上に流延し、流延膜を形成する工程と、流延膜に乾燥する工程と、流延膜を延伸する工程とを含むことが好ましい。具体的には、特許第4889335号に記載の方法によって製膜するのが好ましい。
本発明では、以下の方法を採用することが好ましい。
例えば、特開平11−123732号公報に記載の、流延膜の乾燥速度を乾量基準の含有溶媒量で300質量%/min(=5質量%/s)以下とし、緩やかな乾燥を行う方法が挙げられる。また、特開2003−276037号公報に記載の、中間層であるコア層の両表面にスキン層(外層)を有する多層構造の流延膜の共流延法において、コア層を形成するドープ液の粘度を高めて流延膜の強度を確保するとともに外層を形成するドープの粘度を低くする方法が挙げられる。さらに、流延膜を急乾燥して流延膜表面に膜を形成し、形成された膜のレベリング効果により面状を平滑化する方法、及び、流延膜を延伸する方法なども好ましく挙げられる。
ここで「同一のフィルム」とは、樹脂フィルムを構成する樹脂の材質が同じ(例えば、いずれもTACフィルム)であることを意味する。なかでも、樹脂の分子量が同じであることが好ましく、樹脂の分子量及び結晶化度が同じであることがより好ましく、樹脂の分子量、結晶化度及び延伸率が同じであることがさらに好ましい。また、上記に加えて、第一の樹脂フィルム(A)と第二の樹脂フィルム(C)の厚みが同じであることもより好ましい。
なお、「同じ」とは、完全同一に限定されず、実質的に同一であることを含む。具体的には、同一の製造方法(膜厚、延伸等が同じになるような条件)で作製したものであり、この条件で生じる誤差が含まれる。
また、第一の樹脂フィルム(A)の25℃における引張弾性率EAと第二の樹脂フィルム(C)の25℃における引張弾性率ECとの差(|EC−EA|)は小さいことが好ましく、具体的には、4.0GPa以下が好ましく、3.0GPa以下がより好ましく、2.0GPa以下がさらに好ましく、1.0GPa以下が特に好ましい。
詳細には、第一の樹脂フィルム(A)の熱処理後の収縮力FdAと、第二の樹脂フィルム(C)の熱処理後の収縮力FdCとの差の絶対値が20(10N/m)以上であることが好ましく、30(10N/m)以上であることがより好ましく、50(10N/m)以上であることがさらに好ましい。また、第一の樹脂フィルム(A)の湿熱処理後の収縮力FwAと、第二の樹脂フィルム(C)の湿熱処理後の収縮力FwCとの差の絶対値が20(10N/m)以上であることが好ましく、30(10N/m)以上であることがより好ましく、40(10N/m)以上であることがさらに好ましい。ここで、各差の絶対値の後ろに記載する「(10N/m)」は単位を表す。
熱処理は樹脂フィルムを80℃の環境で48時間保持する処理であり、湿熱処理はフィルムを60℃相対湿度90%の環境で48時間保持する処理を意味する。
式(8) Fd=Ed×εd×dd
[式中、Ed、εd、ddは、樹脂フィルムを80℃の環境で48時間保持した後のMD方向の弾性率、MD方向の寸法変化率の絶対値、膜厚をそれぞれ表す。]
式(9) Fw=Ew×εw×dw
[式中、Ew、εw、dwは、樹脂フィルムを60℃、相対湿度90%の環境で48時間保持した後のMD方向の弾性率、MD方向の湿度寸法変化率の絶対値、膜厚をそれぞれ表す。]
なお、「MD(Machine Direction)方向」とはフィルム搬送方向を意味し、上記のMD方向の弾性率、MD方向の湿度寸法変化率の絶対値および膜厚は、実施例記載の方法により測定されるものである。
(接着層を構成し得る成分)
接着層とは、樹脂フィルム同士を貼り合わせる役割を果たす層であり、本発明においては、第一の樹脂フィルムと第二の樹脂フィルムとを接着する。
接着層は、乾燥や反応により接着性を発現する成分(接着剤)を含む組成物を用いて形成することが好ましい。例えば、硬化反応により接着性を発現する成分を含む組成物(以下、「硬化性組成物」と称す。)を用いて形成される接着層は、かかる硬化性組成物を硬化させてなる硬化層である
ここで、セルロース誘導体とは、セルロースを変性したものを意味する。セルロース誘導体に特に制限はなく、公知のセルロース誘導体を使用することができる。例えば、HEC(ヒドロキシエチルセルロース)等を用いることができる。
樹脂の重量平均分子量は、引張弾性率を高める点から、1000以上が好ましく、10、000以上がより好ましい。上限値に特に制限はないが、1,000,000以下が実際的である。
無機微粒子の平均粒径は0.2μm以下であり、0.1μm以下が好ましく、0.06μm以下がより好ましい。下限値に特に制限はないが、例えば、0.1nm以上が好ましく、1nm以上がより好ましい。
無機微粒子の平均粒径は、透過電子顕微鏡により測定された値である。より詳細には、HR−TEM(高分解能透過型電子顕微鏡)で無作為に選択した100個の無機微粒子について、投影面積から無機微粒子の占有面積を画像処理装置によって求め、100個の無機微粒子の占有面積の合計を、選択した無機微粒子の個数(100個)で除し、得られた値に相当する円の直径の平均値(平均円相当直径)として算出した。上記平均粒径は、一次粒子が凝集してなる二次粒子の粒径は含まない。
なお、このような無機微粒子は、粒径が光の波長よりも十分小さいために散乱が生じず、接着層を構成する接着剤にこの無機微粒子が分散した分散体は光学的に均一な物質として振舞う。
ケン化の方法については、特開2007−86748号公報の段落番号<0211>及び段落番号<0212>に記載されている方法を用いることができる。
たとえば、水平方向または鉛直方向に移動する帯状の長尺の樹脂フィルム(A)あるいは(C)の一方の面に、樹脂フィルム(C)あるいは(A)を同じ移動速度で接近させ、上記樹脂フィルム(A)と樹脂フィルム(C)の間に、接着剤層(B)となる接着剤を塗布し、ピンチロールで圧力をかけて樹脂フィルム(A)と樹脂フィルム(C)を貼り合わせることができる。ここで、塗布される接着剤は、接着剤層(B)を構成する材質を塗布できるように溶媒で希釈したものであってもよい。その場合、接着剤層(B)中の溶媒を乾燥させ、樹脂フィルム(A)と樹脂フィルム(C)の接着が完了する。この際の乾燥温度は、接着剤層(B)中の溶媒種および、樹脂フィルム(A)と樹脂フィルム(C)の樹脂種および厚みによるが、例えば接着剤層(B)中の溶媒が水である場合、30〜85℃であることが好ましく、さらに好ましくは45〜80℃である。
本発明においては、表面硬度の点から、第一の樹脂フィルム(A)及び第二の樹脂フィルム(C)の少なくとも一方が、上記接着層(B)の設けられた側とは反対側の面にハードコート層を有することが好ましく、どちらか一方の樹脂フィルムが有することがより好ましい。この場合、ハードコート層は、本発明の光学フィルムにおける樹脂フィルム(A)あるいは(C)を構成する層とはみなさず、樹脂フィルム(A)あるいは(C)の引張弾性率および屈折率は、ハードコート層を含まない樹脂フィルム(A)あるいは(C)の引張弾性率および屈折率を意味する。HC層を有する光学フィルムの一態様として、図2に示すように、第一の樹脂フィルム1A、接着層2A、第二の樹脂フィルム1Bがこの順に積層され、第一の樹脂フィルム1Aの、接着層2Aを有する面とは反対側の面にハードコート層3Aを有する本発明の光学フィルム4Bが挙げられる。HC層は、光学フィルムに所望の鉛筆硬度を付与できれば、いずれの材質から構成されてもよい。
本発明の光学フィルムは、第一の樹脂フィルム(A)及び第二の樹脂フィルム(C)の少なくとも一方にHC層を有している場合にも、本発明の効果を奏する。
以下、HC層の具体的態様を説明するが、本発明は下記態様に限定されるものではない。
本発明に用いられるHC層は、HC層形成用硬化性組成物に活性エネルギー線を照射することにより硬化することで得ることができる。なお本発明および本明細書において、「活性エネルギー線」とは、電離放射線をいい、X線、紫外線、可視光、赤外線、電子線、α線、β線、γ線等が包含される。
本発明に用いられるHC層は、1層構造でも2層以上の積層構造であってもよいが、下記に詳細を記載する1層構造または2層以上の積層構造からなるHC層が好ましい。
1層構造のHC層形成用硬化性組成物の好ましい態様としては、第一の態様として、1分子中に2個以上のエチレン性不飽和基を有する重合性化合物を少なくとも一種含むHC層形成用硬化性組成物を挙げることができる。エチレン性不飽和基とは、エチレン性不飽和二重結合を含有する官能基をいう。また、第二の態様として、少なくとも一種のラジカル重合性化合物と少なくとも一種のカチオン重合性化合物を含むHC層形成用硬化性組成物を挙げることができる。
第一の態様のHC層形成用硬化性組成物に含まれる1分子中に2個以上のエチレン性不飽和基を有する重合性化合物としては、多価アルコールと(メタ)アクリル酸とのエステル〔例えば、エチレングリコールジ(メタ)アクリレート、ブタンジオールジ(メタ)アクリレート、ヘキサンジオールジ(メタ)アクリレート、1,4−シクロヘキサンジアクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート、ジペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、ペンタエリスリトールヘキサ(メタ)アクリレート、1,2,3−シクロヘキサンテトラメタクリレート、ポリウレタンポリアクリレート、ポリエステルポリアクリレート〕、上記のエステルのエチレンオキサイド変性体、ポリエチレンオキサイド変性体やカプロラクトン変性体、ビニルベンゼンおよびその誘導体〔例、1,4−ジビニルベンゼン、4−ビニル安息香酸−2−アクリロイルエチルエステル、1,4−ジビニルシクロヘキサノン〕、ビニルスルホン(例、ジビニルスルホン)、アクリルアミド(例、メチレンビスアクリルアミド)およびメタクリルアミドが挙げられる。
第二の態様のHC層形成用硬化性組成物は、少なくとも一種のラジカル重合性化合物と少なくとも一種のカチオン重合性化合物とを含む。好ましい態様としては、
アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を1分子中に2個以上含むラジカル重合性化合物と;
カチオン重合性化合物と;
を含むHC層形成用硬化性組成物を挙げることができる。
アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を1分子中に2個以上含むラジカル重合性化合物と;
カチオン重合性化合物と;
ラジカル光重合開始剤と;
カチオン光重合開始剤と;
を含むHC層形成用硬化性組成物を挙げることができる。以下において、本態様を、第二の態様(1)と記載する。
a)脂環式エポキシ基およびエチレン性不飽和基を含み、1分子中に含まれる脂環式エポキシ基の数が1個であり、かつ1分子中に含まれるエチレン性不飽和基の数が1個であり、分子量が300以下であるカチオン重合性化合物と;
b)1分子中に3個以上のエチレン性不飽和基を含むラジカル重合性化合物と;
c)ラジカル重合開始剤と;
d)カチオン重合開始剤と;
を含むHC層形成用硬化性組成物を挙げることができる。以下において、本態様を、第二の態様(2)と記載する。第二の態様(2)のHC層形成用硬化性組成物を硬化したHC層は、好ましくは、HC層の全固形分を100質量%とした場合に、上記a)由来の構造を15〜70質量%、上記b)由来の構造を25〜80質量%、上記c)を0.1〜10質量%、上記d)を0.1〜10質量%含むことができる。また、一態様では、第二の態様(2)のHC層形成用硬化性組成物は、このHC層形成用硬化性組成物の全固形分を100質量%とした場合に、上記a)を15〜70質量%含むことが好ましい。なお、「脂環式エポキシ基」とは、エポキシ環と飽和炭化水素環とが縮合した環状構造を有する1価の官能基をいうものとする。
第二の態様のHC層形成用硬化性組成物は、少なくとも一種のラジカル重合性化合物と少なくとも一種のカチオン重合性化合物とを含む。第二の態様(1)におけるラジカル重合性化合物は、アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を1分子中に2個以上含む。上記ラジカル重合性化合物は、アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を、1分子中に、好ましくは例えば2〜10個含むことができ、より好ましくは2〜6個含むことができる。
GPC装置:HLC−8120(東ソー製)
カラム:TSK gel Multipore HXL−M(東ソー製、内径7.8mm×カラム長30.0cm)
溶離液:テトラヒドロフラン
また、第二の態様(1)のHC層形成用硬化性組成物の第一のラジカル重合性化合物の含有量は、組成物全量100質量%に対して、好ましくは30質量%以上であり、より好ましくは50質量%以上であり、更に好ましくは70質量%以上である。一方、第一のラジカル重合性化合物の含有量は、組成物全量100質量%に対して、98質量%以下であることが好ましく、95質量%以下であることがより好ましく、90質量%以下であることが更に好ましい。
第二のラジカル重合性化合物の1分子中に含まれるラジカル重合性基の数は、好ましくは、少なくとも2個であり、より好ましくは3個以上であり、更に好ましくは4個以上である。また、第二のラジカル重合性化合物の1分子中に含まれるラジカル重合性基の数は、一態様では、例えば10個以下であるが、10個超であってもよい。また、第二のラジカル重合性化合物としては、分子量が200以上1000未満のラジカル重合性化合物が好ましい。
第二のラジカル重合性化合物は2種以上併用してもよい。この場合、ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物“DPHA”(日本化薬製)などを好ましく用いることができる。
b)成分としては、多価アルコールと(メタ)アクリル酸とのエステル、ビニルベンゼンおよびその誘導体、ビニルスルホン、(メタ)アクリルアミド等が挙げられる。中でも、アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を1分子中に3個以上含むラジカル重合性化合物が好ましい。具体例としては、多価アルコールと(メタ)アクリル酸とのエステルであって、1分子中に3個以上のエチレン性不飽和基を有する化合物を挙げることができる。より詳しくは、例えば、(ジ)ペンタエリスリトールテトラ(メタ)アクリレート、(ジ)ペンタエリスリトールトリ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、EO変性トリメチロールプロパントリ(メタ)アクリレート、PO変性トリメチロールプロパントリ(メタ)アクリレート、EO変性リン酸トリ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート、ジトリメチロールプロパンテトラ(メタ)アクリレート、ジペンタエリスリトールテトラ(メタ)アクリレート、(ジ)ペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、ペンタエリスリトールヘキサ(メタ)アクリレート、1,2,3−シクロヘキサンテトラメタクリレート、ポリウレタンポリアクリレート、ポリエステルポリアクリレート、カプロラクトン変性トリス(アクリロキシエチル)イソシアヌレート、トリペンタエリスリトールトリアクリレート、トリペンタエリスリトールヘキサトリアクリレート、1,2,4−シクロヘキサンテトラ(メタ)アクリレート、ペンタグリセロールトリアクリレート、等が挙げられる。なお上記の「(ジ)ペンタエリスリトール」とは、ペンタエリスリトールとジペンタエリスリトールの一方または両方の意味で用いられる。
アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を1分子中に3個以上含む樹脂としては、例えば、ポリエステル系樹脂、ポリエーテル系樹脂、アクリル系樹脂、エポキシ系樹脂、ウレタン系樹脂、アルキド系樹脂、スピロアセタール系樹脂、ポリブタジエン系樹脂、ポリチオールポリエン系樹脂、多価アルコール等の多官能化合物等の重合体等も挙げられる。
更に、アクリロイル基およびメタクリロイル基からなる群から選ばれるラジカル重合性基を1分子中に3個以上含むラジカル重合性化合物の具体例としては、日本化薬製KAYARAD DPHA、同DPHA−2C、同PET−30、同TMPTA、同TPA−320、同TPA−330、同RP−1040、同T−1420、同D−310、同DPCA−20、同DPCA−30、同DPCA−60、同GPO−303、大阪有機化学工業製V#400、V#36095D等のポリオールと(メタ)アクリル酸のエステル化物を挙げることができる。また紫光UV−1400B、同UV−1700B、同UV−6300B、同UV−7550B、同UV−7600B、同UV−7605B、同UV−7610B、同UV−7620EA、同UV−7630B、同UV−7640B、同UV−6630B、同UV−7000B、同UV−7510B、同UV−7461TE、同UV−3000B、同UV−3200B、同UV−3210EA、同UV−3310EA、同UV−3310B、同UV−3500BA、同UV−3520TL、同UV−3700B、同UV−6100B、同UV−6640B、同UV−2000B、同UV−2010B、同UV−2250EA、同UV−2750B(日本合成化学製)、UL−503LN(共栄社化学製)、ユニディック17−806、同17−813、同V−4030、同V−4000BA(大日本インキ化学工業製)、EB−1290K、EB−220、EB−5129、EB−1830,EB−4358(ダイセルUCB製)、ハイコープAU−2010、同AU−2020((株)トクシキ製)、アロニックスM−1960(東亜合成製)、アートレジンUN−3320HA、UN−3320HC、UN−3320HS、UN−904、HDP−4T等の3官能以上のウレタンアクリレート化合物、アロニックスM−8100、M−8030、M−9050(東亜合成製)、KBM−8307(ダイセルサイテック製)の3官能以上のポリエステル化合物なども好適に使用することができる。
また、b)成分としては、一種のみ用いてもよく、構造の異なる二種胃需要を併用してもよい。
第二の態様のHC層形成用硬化性組成物は、少なくとも一種のラジカル重合性化合物と少なくとも一種のカチオン重合性化合物とを含む。カチオン重合性化合物としては、カチオン重合可能な重合性基(カチオン重合性基)を有するものであれば、何ら制限なく用いることができる。また、1分子中に含まれるカチオン重合性基の数は、少なくとも1個である。カチオン重合性化合物は、カチオン重合性基を1分子中に1個含む単官能化合物であっても、2個以上含む多官能化合物であってもよい。多官能化合物に含まれるカチオン重合性基の数は、特に限定されるものではないが、例えば1分子中に2〜6個である。また、多官能化合物の1分子中に2個以上含まれるカチオン重合性基は、同一あってもよく、構造が異なる二種以上であってもよい。
(1)カチオン重合性化合物として、含窒素複素環含有化合物を含む。好ましくは、含窒素複素環含有化合物が有する含窒素複素環は、イソシアヌレート環およびグリコールウリル環からなる群から選択される。含窒素複素環含有化合物は、より好ましくは、イソシアヌレート環含有化合物である。更に好ましくは、イソシアヌレート環含有化合物は、1分子中に1つ以上のエポキシ環を含むエポキシ環含有化合物である。
(2)カチオン重合性化合物として、カチオン重合性基当量が150未満のカチオン重合性化合物を含む。好ましくは、エポキシ基当量が150未満のエポキシ基含有化合物を含む。
(3)カチオン重合性化合物が、エチレン性不飽和基を含む。
(4)カチオン重合性化合物として、1分子中に1個以上のオキセタン環を含むオキセタン環含有化合物を、他のカチオン重合性化合物とともに含む。好ましくは、オキセタン環含有化合物は、含窒素複素環を含まない化合物である。
また、上記HC層形成用硬化性組成物のカチオン重合性化合物の含有量は、第一のラジカル重合性化合物の含有量とカチオン重合性化合物との合計含有量100質量部に対して、好ましくは0.05質量部以上であり、より好ましくは0.1質量部以上であり、更に好ましくは1質量部以上である。一方、カチオン重合性化合物の含有量は、第一のラジカル重合性化合物の含有量とカチオン重合性化合物との合計含有量100質量部に対して、50質量部以下であることが好ましく、40質量部以下であることがより好ましい。
なお本発明および本明細書において、カチオン重合性基とラジカル重合性基をともに有する化合物は、カチオン重合性化合物に分類し、HC層形成用硬化性組成物における含有量を規定するものとする。
HC層形成用硬化性組成物は重合開始剤を含むことが好ましく、光重合開始剤を含むことがより好ましい。ラジカル重合性化合物を含むHC層形成用硬化性組成物は、ラジカル光重合開始剤を含むことが好ましく、カチオン重合性化合物を含むHC層形成用硬化性組成物は、カチオン光重合開始剤を含むことが好ましい。なおラジカル光重合開始剤は一種のみ用いてもよく、構造の異なる二種以上を併用してもよい。この点は、カチオン光重合開始剤についても同様である。
以下、各光重合開始剤について、順次説明する。
ラジカル光重合開始剤としては、光照射により活性種としてラジカルを発生することができるものであればよく、公知のラジカル光重合開始剤を、何ら制限なく用いることができる。具体例としては、例えば、ジエトキシアセトフェノン、2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン、ベンジルジメチルケタール、4−(2−ヒドロキシエトキシ)フェニル−(2−ヒドロキシ−2−プロピル)ケトン、1−ヒドロキシシクロヘキシルフェニルケトン、2−メチル−2−モルホリノ(4−チオメチルフェニル)プロパン−1−オン、2−ベンジル−2−ジメチルアミノ−1−(4−モルホリノフェニル)ブタノン、2−ヒドロキシ−2−メチル−1−[4−(1−メチルビニル)フェニル]プロパノンオリゴマー、2−ヒドロキシ−1−{4−[4−(2−ヒドロキシ−2−メチル−プロピオニル)−ベンジル]フェニル}−2−メチル−プロパン−1−オン等のアセトフェノン類;1,2−オクタンジオン、1−[4−(フェニルチオ)−,2−(O−ベンゾイルオキシム)]、エタノン,1−[9−エチル−6−(2−メチルベンゾイル)−9H−カルバゾール−3−イル]−,1−(0−アセチルオキシム)等のオキシムエステル類;ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンゾインイソブチルエーテル等のベンゾイン類;ベンゾフェノン、オルト−ベンゾイル安息香酸メチル、4−フェニルベンゾフェノン、4−ベンゾイル−4’−メチル−ジフェニルサルファイド、3,3’,4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン、2,4,6−トリメチルベンゾフェノン、4−ベンゾイル−N,N−ジメチル−N−[2−(1−オキソ−2−プロペニルオキシ)エチル]ベンゼンメタナミニウムブロミド、(4−ベンゾイルベンジル)トリメチルアンモニウムクロリド等のベンゾフェノン類;2−イソプロピルチオキサントン、4−イソプロピルチオキサントン、2,4−ジエチルチオキサントン、2,4−ジクロロチオキサントン、1−クロロ−4−プロポキシチオキサントン、2−(3−ジメチルアミノ−2−ヒドロキシ)−3,4−ジメチル−9H−チオキサントン−9−オンメソクロリド等のチオキサントン類;2,4,6−トリメチルベンゾイル−ジフェニルフォスフィンオキサイド、ビス(2,6−ジメトキシベンゾイル)−2,4,4−トリメチル−ペンチルフォスフィンオキサイド、ビス(2,4,6−トリメチルベンゾイル)−フェニルフォスフィンオキサイド等のアシルフォスフィンオキサイド類;等が挙げられる。また、ラジカル光重合開始剤の助剤として、トリエタノールアミン、トリイソプロパノールアミン、4,4’−ジメチルアミノベンゾフェノン(ミヒラーケトン)、4,4’−ジエチルアミノベンゾフェノン、2−ジメチルアミノエチル安息香酸、4−ジメチルアミノ安息香酸エチル、4−ジメチルアミノ安息香酸(n−ブトキシ)エチル、4−ジメチルアミノ安息香酸イソアミル、4−ジメチルアミノ安息香酸2−エチルヘキシル、2,4−ジエチルチオキサンソン、2,4−ジイソプロピルチオキサンソン等を併用してもよい。
以上のラジカル光重合開始剤および助剤は、公知の方法で合成可能であり、市販品として入手も可能である。市販のラジカル光重合開始剤としては、BASF製のイルガキュア(127,651,184,819,907,1870(CGI−403/Irg184=7/3混合開始剤、500,369,1173,2959,4265,4263など)、OXE01)等、日本化薬製のKAYACURE(DETX−S,BP−100,BDMK,CTX,BMS,2−EAQ,ABQ,CPTX,EPD,ITX,QTX,BTC,MCAなど)、サートマー製のEsacure(KIP100F,KB1,EB3,BP,X33,KT046,KT37,KIP150,TZT)等を好ましい例として挙げられる。
カチオン光重合開始剤としては、光照射により活性種としてカチオンを発生することができるものであればよく、公知のカチオン光重合開始剤を、何ら制限なく用いることができる。具体例としては、公知のスルホニウム塩、アンモニウム塩、ヨードニウム塩(例えばジアリールヨードニウム塩)、トリアリールスルホニウム塩、ジアゾニウム塩、イミニウム塩などが挙げられる。より具体的には、例えば、特開平8−143806号公報段落0050〜0053に示されている式(25)〜(28)で表されるカチオン光重合開始剤、特開平8−283320号公報段落0020にカチオン重合触媒として例示されているもの等を挙げることができる。また、カチオン光重合開始剤は、公知の方法で合成可能であり、市販品としても入手可能である。市販品としては、例えば、日本曹達製CI−1370、CI−2064、CI−2397、CI−2624、CI−2639、CI−2734、CI−2758、CI−2823、CI−2855およびCI−5102等、ローディア製PHOTOINITIATOR2047等、ユニオンカーバイト製UVI−6974、UVI−6990、サンアプロ製CPI−10Pを用いることができる。
HC層形成用硬化性組成物は、活性エネルギー線の照射により硬化する性質を有する少なくとも一種の成分を含み、任意に少なくとも一種の重合開始剤を含むことができ、含むことが好ましい。それらの詳細は、先に記載した通りである。
次に、HC層形成用硬化性組成物に任意に含まれ得る各種成分について説明する。
HC層形成用硬化性組成物は、平均一次粒径が2μm未満の無機粒子を含むことができる。HC層形成用硬化性組成物を硬化したHC層を有する前面板の硬度向上(更にはこの前面板を有する液晶パネルの硬度向上)の観点からは、HC層形成用硬化性組成物およびこの組成物を硬化したHC層は、平均一次粒径が2μm未満の無機粒子を含むことが好ましい。無機粒子の平均一次粒径は、10nm〜1μmの範囲であることが好ましく、10nm〜100nmの範囲であることがより好ましく、10nm〜50nmの範囲であることが更に好ましい。
無機粒子および後述のマット粒子の平均一次粒径については、透過型電子顕微鏡(倍率50万〜200万倍)で粒子の観察を行い、無作為に選択した粒子(一次粒子)100個を観察し、それらの粒径の平均値をもって平均一次粒径とする。
S−1 H2C=C(X)COOC3H6Si(OCH3)3
S−2 H2C=C(X)COOC2H4OTi(OC2H5)3
S−3 H2C=C(X)COOC2H4OCOC5H10OPO(OH)2
S−4 (H2C=C(X)COOC2H4OCOC5H10O)2POOH
S−5 H2C=C(X)COOC2H4OSO3H
S−6 H2C=C(X)COO(C5H10COO)2H
S−7 H2C=C(X)COOC5H10COOH
S−8 CH2CH(O)CH2OC3H6Si(OCH3)3
(Xは、水素原子またはメチル基を表す)
HC層形成用硬化性組成物は、マット粒子を含むこともできる。マット粒子とは、平均一次粒径が2μm以上の粒子をいうものとし、無機粒子であっても有機粒子であってもよく、または無機・有機の複合材料の粒子であってもよい。マット粒子の形状は、球形、非球形を問わない。マット粒子の平均一次粒径は、2〜20μmの範囲であることが好ましく、4〜14μmの範囲であることがより好ましく、6〜10μmの範囲であることが更に好ましい。
HC層形成用硬化性組成物は、紫外線吸収剤を含有することも好ましい。紫外線吸収剤としては、例えば、ベンゾトリアゾール化合物、トリアジン化合物を挙げることができる。ここでベンゾトリアゾール化合物とは、ベンゾトリアゾール環を有する化合物であり、具体例としては、例えば特開2013−111835号公報段落0033に記載されている各種ベンゾトリアゾール系紫外線吸収剤を挙げることができる。トリアジン化合物とは、トリアジン環を有する化合物であり、具体例としては、例えば特開2013−111835号公報段落0033に記載されている各種トリアジン系紫外線吸収剤を挙げることができる。樹脂フィルム中の紫外線吸収剤の含有量は、例えばフィルムに含まれる樹脂100質量部に対して0.1〜10質量部程度であるが、特に限定されるものではない。また、紫外線吸収剤については、特開2013−111835号公報段落0032も参照できる。なお本発明および本明細書における紫外線とは200〜380nmの波長帯域に発光中心波長を有する光をいうものとする。
HC層形成用硬化性組成物は、レベリング剤および防汚剤等の含フッ素化合物を含有することも好ましい。
レベリング剤としては、含フッ素ポリマーが好ましく用いられる。例えば、特許5175831号に記載されているフルオロ脂肪族基含有ポリマーが挙げられる。またフルオロ脂肪族基含有ポリマーを構成する、一般式(1)で表されるフルオロ脂肪族基含有モノマーの含有量が全重合単位の50質量%以下のフルオロ脂肪族基含有ポリマーをレベリング剤として用いることもできる。
HC層が防汚剤を含むと、指紋や汚れの付着を低減し、また、付着した汚れの拭き取りを容易にすることができる。また、表面のすべり性を向上させる事により耐擦性をより向上させることも可能になる。
HC層形成用硬化性組成物は、防汚剤を、1種のみ含んでいても良いし、2種以上含んでいても良い。2種以上含まれている場合、その合計量が上記範囲となることが好ましい。
また、HC層形成用硬化性組成物は、防汚剤を実質的に含まない構成とすることもできる。
防汚剤は、含フッ素化合物を含有することが好ましい。含フッ素化合物は、モノマー、オリゴマー、ポリマーいずれでもよい。防汚剤としての含フッ素化合物(含フッ素防汚剤)は、HC層中でその他の成分(例えば、後述する含ポリシロキサン化合物、樹脂の構成成分である重合性モノマー、樹脂)との結合形成あるいは相溶性に寄与する置換基を有していることが好ましい。この置換基は同一であっても異なっていてもよく、複数個あることが好ましい。
この置換基は重合性基が好ましく、ラジカル重合性、カチオン重合性、アニオン重合性、縮重合性及び付加重合性のうちいずれかを示す重合性反応基であればよく、好ましい置換基の例としては、アクリロイル基、メタクリロイル基、ビニル基、アリル基、シンナモイル基、エポキシ基、オキセタニル基、水酸基、ポリオキシアルキレン基、カルボキシル基、アミノ基が挙げられる。その中でもラジカル重合性基が好ましく、中でもアクリロイル基、メタクリロイル基が特に好ましい。
含フッ素化合物はフッ素原子を含まない化合物とのポリマーであってもオリゴマーであってもよい。
一般式(F): (Rf)−[(W)−(RA)n]m
(式中、Rfは(パー)フルオロアルキル基又は(パー)フルオロポリエーテル基、Wは単結合又は連結基、RAは重合性不飽和基を表す。nは1〜3の整数を表す。mは1〜3の整数を表す。)
ここで、「(パー)フルオロアルキル基」は、フルオロアルキル基及びパーフルオロアルキル基のうち少なくとも1種を表し、「(パー)フルオロポリエーテル基」は、フルオロポリエーテル基及びパーフルオロポリエーテル基のうち少なくとも1種を表す。耐擦性の観点では、Rf中のフッ素含有率は高いほうが好ましい。
(パー)フルオロアルキル基は、直鎖構造(例えば−CF2CF3、−CH2(CF2)4H、−CH2(CF2)8CF3、−CH2CH2(CF2)4H)であっても、分岐構造(例えば−CH(CF3)2、−CH2CF(CF3)2、−CH(CH3)CF 2CF3、−CH(CH3)(CF2)5CF2H)であっても、脂環式構造(好ましくは5員環又は6員環で、例えばパーフルオロシクロへキシル基及びパーフルオロシクロペンチル基並びにこれらの基で置換されたアルキル基)であってもよい。
上記p及びqはそれぞれ独立に0〜20の整数を表す。ただしp+qは1以上の整数である。
p及びqの総計は1〜83が好ましく、1〜43がより好ましく、5〜23がさらに好ましい。
上記含フッ素防汚剤は、耐擦性に優れるという観点から−(CF2O)p−(CF2CF2O)q−で表されるパーフルオロポリエーテル基を有することが特に好ましい。
Wとして、好ましくは、エチレン基、より好ましくは、カルボニルイミノ基と結合したエチレン基である。
Rf2(CF2CF2)pR22CH2CH2R21OCOCR11=CH2
F(CF2)q−CH2−CHX−CH2Y(式中、qは1〜20の整数、X及びYは(メタ)アクリロイルオキシ基又は水酸基を示し、X及びYの少なくとも一方は(メタ)アクリロイルオキシ基である。)
F(CF2)rO(CF2CF2O)sCF2CH2OCOCR3=CH2(式中R3は水素原子又はメチル基であり、sは1〜20の整数であり、rは1〜4の整数を表す。)
F(CF2)rO(CF2CF2O)sCF2CH2OH(一般式(FG−3)中、sは1〜20の整数の整数であり、rは1〜4の整数を表す。)
これらは市場で入手でき、その具体例としては例えば、1H,1H−ペルフルオロ−3,6−ジオキサヘプタン−1−オール(商品名「C5GOL」、エクスフロアー社製)、1H,1H−ペルフルオロ−3,6,9−トリオキサデカン−1−オール(商品名「C7GOL」、エクスフロアー社製)、1H,1H−ペルフルオロ−3,6−ジオキサデカン−1−オール(商品名「C8GOL」、エクスフロアー社製)、1H,1H−ペルフルオロ−3,6,9−トリオキサトリデカン−1−オール(商品名「C10GOL」、エクスフロアー社製)、1H,1H−ペルフルオロ−3,6,9,12−テトラオキサヘキサデカン−1−オール(商品名「C12GOL」、エクスフロアー社製)等が挙げられる。
本発明においては、1H,1H−ペルフルオロ−3,6,9,12−テトラオキサトリデカン−1−オールを用いることが好ましい。
(b−2):F9C4O2F4OC2F4OCF2CH2OCOC(CH3)=CH2
Rf3−[(O)c(O=C)b(CX4X5)a−CX3=CX1X2]
(式中、X1及びX2は、H又はFを表し、X3はH、F、CH3又はCF3を表し、X4及びX5は、H、F、又はCF3を表し、a、b、及びcは0又は1を表し、Rf3は炭素数18〜200のエーテル結合を含む含フッ素アルキル基を表す)
上記一般式(F−3)’で表される化合物は、Rf3基中に、一般式(FG−3)’:−(CX6 2CF2CF2O)− (式中、X6はF又はH)で示される繰り返し単位を6個以上有する、含フッ素不飽和化合物である。
(c−1) Rf3−[(O)(O=C)b−CX3=CX1X2]
(c−2) Rf3−[(O)(O=C)−CX3=CX1X2]
(c−3) Rf3−[(O)c(O=C)−CF=CH2]
などを挙げることができる((c−1)〜(c−3)における各記号の定義は一般式(FG−3)’と同義である。)。
上記含フッ素ポリエーテル化合物の重合性不飽和基としては、以下の構造を含むものを好ましく用いることができる。
本発明においては、−O(C=O)CF=CH2の構造を有する化合物が重合(硬化)反応性が特に高く、効率よく硬化物を得ることができる点で好ましい。
また更に詳しくは、含フッ素ポリエーテル鎖の繰り返し単位が6個以上のものを含んでいる混合物でもよいが、混合物の形で使用する場合、上記繰り返し単位が6個未満の含フッ素不飽和化合物と6個以上の含フッ素不飽和化合物との分布において、ポリエーテル鎖の繰り返し単位が6個以上の含フッ素不飽和化合物の存在比率が最も高い混合物とすることが好ましい。
一般式(FG−3)’で表される含フッ素ポリエーテル鎖の繰り返し単位は6個以上が好ましく、10個以上がより好ましく、18個以上が更に好ましく、20個以上が特に好ましい。これによって、動摩擦係数を低減し、耐擦性を向上することができる。また、含フッ素ポリエーテル鎖はRf3基の末端にあっても、鎖中に存在していてもよい。
一般式(c−4):
R4−(CX6 2CF2CF2O)t−(R5)e−(式中、X6は式(FG−3)’で表される含フッ素ポリエーテル鎖、R4は水素原子、ハロゲン原子、アルキル基、含フッ素アルキル基、エーテル結合を含むアルキル基又はエーテル結合を含む含フッ素アルキル基、R5は二価以上の有機基、tは6〜66の整数、eは0又は1を表す。)で表される基が好ましい。
つまり、Rf3基は、二価以上の有機基R5を介して、反応性の炭素−炭素二重結合と結合し、更に末端にR4を有する含フッ素有機基である。
R5は一般式(FG−3)’で表される含フッ素ポリエーテル鎖を反応性の炭素−炭素二重結合に結合させることができる有機基であれば、如何なるものでもよい。例えば、アルキレン基、含フッ素アルキレン基、エーテル結合を含むアルキレン基及びエーテル結合を含む含フッ素アルキレン基が挙げられる。中でも含フッ素アルキレン基及びエーテル結合を含む含フッ素アルキレン基が、透明性、低屈折率性の点で好ましい。
(一般式(F−4)中、Rf1は(パー)フルオロアルキル基又は(パー)フルオロポリエーテル基、Wは連結基、RAは重合性不飽和基を表す。nは1〜3の整数、mは1〜3の整数を表し、nとmは同時に1であることはない。)
撥水撥油性に優れると共に撥水撥油性の持続(防汚耐久性)に優れるという観点からnが2〜3、mが1〜3であることが好ましく、nが2〜3、mが2〜3であることがより好ましく、nが3、mが2〜3であることがさらに好ましい。
一般式(F−4)で表される化合物の好ましい具体例や合成方法は国際公開第2005/113690号に記載されている。
(d−2):HFPO−CONH−C−(CH2OCOCH=CH2)2H
(d−3):HFPO−CONH−C3H6NHCH3とトリメチロールプロパントリアクリレートの1:1マイケル付加重合物
(d−4):(CH2=CHCOOCH2)2H−C−CONH−HFPO−CONH−(CH2OCOCH=CH2)2H
(d−5):(CH2=CHCOOCH2)3−C−CONH−HFPO−CONH−C−(CH2OCOCH=CH2)3
CH2=CX1−COO−CHY−CH2−OCO−CX2=CH2
(式中X1及びX2は、水素原子又はメチル基を示し、Yは、フッ素原子を3個以上有する炭素数2〜20のフルオロアルキル基又はフッ素原子を4個以上有する炭素数4〜20のフルオロシクロアルキル基を示す。)
重合性不飽和基を有する含フッ素化合物の重量平均分子量(Mw)は、分子排斥クロマトグラフィー、例えばゲル浸透クロマトグラフィー(GPC)などを用いて測定できる。
本発明で用いられる含フッ素化合物のMwは400以上50000未満が好ましく、400以上30000未満がより好ましく、400以上25000未満が更に好ましい。上記下限値以上であると、防汚剤のHC層中での表面移行性が高くなるため好ましい。また、上記上限値未満であると、HC層形成用硬化性組成物を塗布してから硬化する工程の間に、含フッ素化合物の表面移行性が妨げられず、HC層表面への偏在がより均一に起こりやすくなり、耐擦性及び膜硬度が向上するため好ましい。また、含フッ素化合物は重量平均分子量に関して多峰性であってもよい。
含フッ素化合物の添加量は、HC層形成用硬化性組成物中の全固形分に対して、0.01〜5質量%が好ましく、0.1〜5質量%がより好ましく、0.5〜5質量%が更に好ましく、0.5〜2質量%が特に好ましい。添加量が上記上限値以上であると、スチールウールに対する摩擦係数を低減でき、耐擦性がより向上される。また、添加量が上記下限値以下であると、HC層形成用硬化性組成物中の重合性化合物(HC層を形成する際の樹脂成分)との混合が不十分な含フッ素化合物が表面に析出することがなく、HC層が白化したり表面に白粉を生じたりすることが抑制されるため好ましい。
HC層が後述する2層以上の積層構造である場合には、含フッ素化合物を含有するHC層を形成する、HC層形成用硬化性組成物中での添加量を意味する。
尚、本明細書では、防汚剤が、重合性基を有する場合であっても、上記重合性化合物1〜3および上記他の重合性化合物には該当しないものとして扱う。
また、後述の(vi)その他の成分に記載するレベリング剤および防汚剤も、上記に加えて含有することができる。
含ポリシロキサン化合物は、特に制限されることなく、分子中にポリシロキサン構造を有する化合物を用いることができる。
含ポリシロキサン化合物が有するポリシロキサン構造としては、直鎖状、分岐状及び環状のいずれでもよい。
RaRA bSiO(4−a−b)/2
(式中、Rは水素原子、メチル基、エチル基、プロピル基又はフェニル基であり、RAは重合性不飽和基を含有する有機基であり、0<a、0<b、a+b<4である。)
ポリシロキサン防汚剤においても、膜強度の観点から一分子中に重合性不飽和基を複数有することが好ましく、一分子中に重合性不飽和基を複数有するポリジメチルシロキサンであることがより好ましい。
この置換基は重合性基が好ましく、ラジカル重合性、カチオン重合性、アニオン重合性、縮重合性及び付加重合性のうちいずれかを示す重合性基記基であればよい。好ましい置換基の例としては(メタ)アクリロイル基、((メタ)アクリロイルオキシ)基、ビニル基、アリル基、シンナモイル基、エポキシ基、オキセタニル基、水酸基、フルオロアルキル基、ポリオキシアルキレン基、カルボキシル基、アミノ基などを含む基が挙げられる。なかでも、ラジカル重合性基が好ましく、特に(メタ)アクリロイルオキシ基が膜硬度を向上する観点で好ましい。
また、化合物中の上記置換基数は、官能基等量として100〜10000g/molが膜強度の観点から好ましく、100〜3000g/molがより好ましく、100〜2000g/molが更に好ましく、100〜1000g/molが特に好ましい。官能基当量を上記下限値以上にすることで、HC層形成用硬化性組成物中の重合性化合物(HC層を形成する際の樹脂成分)と必要以上に相溶することがなく、防汚剤のHC層中での表面移行性が高くなるため好ましい。官能基当量を上記上限値以下にすることで、膜硬度を向上させることができるため好ましい。
ポリシロキサン構造を有する添加剤としては、ポリシロキサン{例えば“KF−96−10CS” ,“KF−100T”,“X−22−169AS”,“KF−102”,“X−22−3701IE”, “X−22−164” ,“X−22−164A” ,“X−22−164AS” ,“X−22−164B” ,“X−22−164C”,“X−22−5002”,“X−22−173B”,“X−22−174D”,“X−22−167B”,“X−22−161AS”(商品名)、以上、信越化学工業(株)製;“AK−5”,“AK−30”,“AK−32”(商品名)、以上東亜合成(株)製;、「サイラプレーンFM0725」,「サイラプレーンFM0721」(商品名)、以上チッソ(株)製;、“DMS−U22”、“RMS−033”、“UMS−182”(商品名)、以上Gelest製;、「アクリット8SS−723」(商品名)、以上大成ファインケミカル(株)製等}を添加するのも好ましい。また、特開2003−112383号公報の表2、表3に記載のポリシロキサン系化合物も好ましく使用できる。
含ポリシロキサン化合物の重量平均分子量は、300以上が好ましく、300以上100000以下がより好ましく、300以上30000以下がさらに好ましい。含ポリシロキサン化合物の重量平均分子量が300以上であると、含ポリシロキサン化合物のHC層表面への偏在化が促進され、耐擦性及び硬度がより向上される。
含ポリシロキサン化合物の添加量は、HC層形成用硬化性組成物中の全固形分に対して、0.01〜5質量%が好ましく、0.1〜5質量%がより好ましく、0.5〜5質量%が更に好ましく、0.5〜2質量%が特に好ましい。添加量が上記下限値以上であると、打鍵後の耐付着性をより向上することができる。また、添加量が上記上限値以下であると、HC層形成用硬化性組成物中の重合性化合物(HC層を形成する際の樹脂成分)との混合が不十分な含ポリシロキサン化合物が表面に析出することがなく、HC層が白化したり表面に白粉を生じたりすることが抑制されるため好ましい。
なお、HC層が後述する2層以上の積層構造である場合には、含ポリシロキサン化合物を含有するHC層を形成する、HC層形成用硬化性組成物中での添加量を意味する。
HC層形成用硬化性組成物は、溶媒を含むことも好ましい。溶媒としては、有機溶媒が好ましく、有機溶媒の1種または2種以上を任意の割合で混合して用いることができる。有機溶媒の具体例としては、例えば、メタノール、エタノール、プロパノール、n−ブタノール、i−ブタノール等のアルコール類;アセトン、メチルイソブチルケトン、メチルエチルケトン、シクロヘキサノン等のケトン類;エチルセロソルブ等のセロソルブ類;トルエン、キシレン等の芳香族類;プロピレングリコールモノメチルエーテル等のグリコールエーテル類;酢酸メチル、酢酸エチル、酢酸ブチル等の酢酸エステル類;ジアセトンアルコール等が挙げられる。これらの中でも、シクロヘキサノン、メチルエチルケトン、メチルイソブチルケトンおよび酢酸メチルが好ましく、シクロヘキサノン、メチルエチルケトン、メチルイソブチルケトンおよび酢酸メチルを任意の割合で混合して用いることがより好ましい。このような構成とすることにより、耐擦性、打抜き性および密着性により優れた光学フィルムが得られる。
また、HC形成用硬化性組成物の固形分は、10〜90質量%であることが好ましく、50〜80質量%であることがより好ましく、65〜75質量%であることが特に好ましい。
HC層形成用硬化性組成物は、上記成分に加えて、公知の添加剤の一種以上を任意の量で含むことができる。添加剤としては、表面調整剤、レベリング剤、重合禁止剤、ポリロタキサン等を挙げることができる。それらの詳細については、例えば特開2012−229412号公報の段落0032〜0034を参照できる。また、市販の防汚剤または公知の方法で調製可能な防汚剤を含むこともできる。ただし添加剤はこれらに限らず、HC層形成用硬化性組成物に一般に添加され得る各種添加剤を用いることができる。また、HC層形成用硬化性組成物は、公知の溶媒を任意の量で含むこともできる。
本発明の光学フィルムは、図2におけるHC層3Aが、少なくとも、第1のHC層、および第2のHC層を樹脂フィルム1A側から順に有する態様も好ましい。
樹脂フィルム1Aの表面に、第1のHC層が位置していても、間に他の層を有していてもよい。同様に、第1のHC層の表面に、第2のHC層が位置していても、間に他の層を有していても良い。第1のHC層と第2のHC層の密着性を高める観点からは、第1のHC層の表面に第2のHC層が位置する、すなわち、両層は、膜面の少なくとも一部において接している方が好ましい。
本発明に用いられる第1のHC層は、第1のHC層形成用硬化性組成物から形成される。
第1のHC層形成用硬化性組成物は、ラジカル重合性基を有する重合性化合物1と、同一分子内にカチオン重合性基とラジカル重合性基を有し、かつ重合性化合物1とは異なる重合性化合物2とを含有し、第1のHC層形成用硬化性組成物に含まれる重合性化合物中、重合性化合物2の含有量が51質量%以上である。
重合性化合物1としては、前述のラジカル重合性化合物の記載が好ましく適用され、重合性化合物2としては、前述のカチオン重合性化合物におけるa)成分の記載が好ましく適用される。
また、第1のHC層形成用硬化性組成物は、重合性化合物1とも重合性化合物2とも異なる他の重合性化合物を有していてもよい。
上記他の重合性化合物は、カチオン重合性基を有する重合性化合物であることが好ましい。上記カチオン重合性基としては、重合性化合物2で述べたカチオン重合性基と同義であり、好ましい範囲も同様である。特に、本発明では、他の重合性化合物として、カチオン重合性基を含む、含窒素複素環含有化合物が好ましい。このような化合物を用いることにより、樹脂フィルムと第1のHC層の密着性をより効果的に向上させることができる。
含窒素複素環としては、イソシアヌレート環(後述の例示化合物B−1〜B−3に含まれる含窒素複素環)およびグリコールウリル環(後述の例示化合物B−10に含まれる含窒素複素環)からなる群から選ばれる含窒素複素環が例示され、イソシアヌレート環がより好ましい。他の重合性化合物が有するカチオン性基の数は、1〜10が好ましく、2〜5がより好ましい。また、他の重合性化合物として、カチオン重合性基と含窒素複素環構造を有する重合性化合物を用いる場合、樹脂フィルムは、アクリル系樹脂フィルムを含む樹脂フィルムが好ましい。このような構成とすることにより、樹脂フィルムと第1のHC層の密着性がより向上する傾向にある。
他の重合性化合物の具体例としては、前述の例示化合物B−1〜B−14が挙げられるが、本発明は前述の具体例に限定されるものではない。
その他、前述の、重合開始剤、無機粒子、マット粒子、紫外線吸収剤、含フッ素化合物、溶媒およびその他の成分の記載を好ましく適用することができる。
特に第1のHC層形成用硬化性組成物は、溶媒を含むことが好ましく、第2のHC層形成用硬化性組成物は、防汚剤を含むことが好ましい。
HC層の厚みは、3μm以上100μm以下が好ましく、5μm以上70μm以下がより好ましく、10μm以上50μm以下がさらに好ましい。
(HC層の鉛筆硬度)
HC層の鉛筆硬度は、硬いほどよく、具体的には3H以上が好ましく、5H以上がより好ましく、7H以上がさらに好ましい。
HC層形成用硬化性組成物を、樹脂フィルム上に直接、または易接着層等の他の層を介して、塗布し、活性エネルギー線を照射することにより、HC層を形成することができる。塗布は、ディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ダイコート法、ワイヤーバーコート法、グラビアコート法等の公知の塗布方法により行うことができる。なおHC層は、二種以上の異なる組成の組成物を同時または逐次塗布することにより二層以上(例えば二層〜五層程度)の積層構造のHC層として形成することもできる。
本発明の光学フィルムは、樹脂フィルムのHC層を有する面とは反対側の面に、衝撃吸収層を有してもよい。衝撃吸収層は、HC層側から受けた衝撃を吸収することで、例えば、本発明の光学フィルムを画像表示装置の前面板として使用する場合に、HC層側とは反対側に配置される画像表示素子の破損を防ぐことができる。
衝撃吸収層は、本発明の光学フィルムを画像表示装置の前面板として用いた際に、表示内容の視認性を確保できる透明性を有し、かつ前面板への押さえ付け及び衝突等に由来する画像表示素子の破損を防ぐことができるものであれば、樹脂から構成されていてもよいし、エラストマー(油展ゴムを含む)から構成されていてもよい。
上記樹脂としては、1,2−ポリブタジエン樹脂、エチレン−酢酸ビニル共重合体(「EVA」と略す。通常3質量%以上の酢酸ビニル単位を含有する。)及びポリエチレン等のポリオレフィン樹脂、ポリ塩化ビニル樹脂、ポリスチレン樹脂、ビニルエステル樹脂(EVAを除く)、飽和ポリエステル樹脂、ポリアミド樹脂、フッ素樹脂(ポリフッ化ビニリデン等)、ポリカーボネート樹脂、ポリアセタール樹脂、ウレタン樹脂、エポキシ樹脂、(メタ)アクリル樹脂、不飽和ポリエステル樹脂及びケイ素樹脂、並びにこれらの樹脂の変性樹脂等が挙げられる。これらの樹脂のうち、ウレタン変性ポリエステル樹脂、ウレタン樹脂、(メタ)アクリル樹脂等が好ましい。
衝撃吸収層の形成方法には特に限定はなく、たとえば、コーティング法、キャスト法(無溶剤キャスト法及び溶剤キャスト法)、プレス法、押出法、射出成形法、注型法及びインフレーション法等が挙げられる。詳細には、上記衝撃吸収材料を溶媒に溶解もしくは分散させた液状物、又は上記衝撃吸収材料を構成する成分の溶融液を調製し、次いで、この液状物又は溶融液を樹脂フィルムに塗布し、その後、必要により溶媒の除去等をすることにより、衝撃吸収層が積層された光学フィルムを作製することができる。
本発明の光学フィルムが衝撃吸収層を有する場合、衝撃吸収層の樹脂フィルムとは反対側の面に、保護層を設けることが好ましい。かかる保護層を有することにより、使用前の光学フィルムが有する衝撃吸収層の破損および埃、汚れ等の付着を防ぐことができる。
本発明の光学フィルムを含む物品としては、家電業界、電気電子業界、自動車業界、住宅業界をはじめとする様々な産業界において、干渉ムラの抑制ならびに打鍵耐久性および製造適性の向上が求められる各種物品を挙げることができる。具体例としては、タッチセンサ、タッチパネル、液晶表示装置等の画像表示装置、自動車の窓ガラス、住居の窓ガラス、等を挙げることができる。これら物品に、好ましくは表面保護フィルムとして本発明の光学フィルムを設けることにより、干渉ムラが十分に抑制され、優れた打鍵耐久性を示す物品を優れた製造適性で提供することが可能となる。本発明の光学フィルムは、画像表示装置用の前面板に用いられる光学フィルムとして好ましく用いられ、タッチパネルの画像表示素子の前面板に用いられる光学フィルムであることがより好ましい。
本発明の光学フィルムを用いることができるタッチパネルは特に制限はなく、目的に応じて適宜選択することができ、例えば、表面型静電容量式タッチパネル、投影型静電容量式タッチパネル、抵抗膜式タッチパネルなどが挙げられる。詳細については、後述する。
なお、タッチパネルとは、いわゆるタッチセンサを含むものとする。タッチパネルにおけるタッチパネルセンサー電極部の層構成が、2枚の透明電極を貼合する貼合方式、1枚の基板の両面に透明電極を具備する方式、片面ジャンパーあるいはスルーホール方式あるいは片面積層方式のいずれでもよい。
本発明の光学フィルムを有する画像表示装置は、本発明の光学フィルムを有する前面板と、画像表示素子とを有する画像表示装置である。
画像表示装置としては、液晶表示装置(Liquid Crystal Display;LCD)、プラズマディスプレイパネル、エレクトロルミネッセンスディスプレイ、陰極管表示装置およびタッチパネルのような画像表示装置に用いることができる。
液晶表示装置としては、TN(Twisted Nematic)型、STN(Super−Twisted Nematic)型、TSTN(Triple Super Twisted Nematic)型、マルチドメイン型、VA(Vertical Alignment)型、IPS(In Plane Switching)型、OCB(Optically CompensatedBend)型等が挙げられる。
画像表示装置は、脆性が改良されハンドリング性に優れ、表面平滑性やシワによる表示品位を損なう事が無く、湿熱試験時の光漏れを低減できることが好ましい。
すなわち、本発明の光学フィルムを有する画像表示装置は、画像表示素子が液晶表示素子であることが好ましい。液晶表示素子を有する画像表示装置としては、ソニーエリクソン社製、エクスペリアPなどを挙げることができる。
有機エレクトロルミネッセンス表示素子は、公知技術を、何ら制限なく適用することができる。有機エレクトロルミネッセンス表示素子を有する画像表示装置としては、SAMSUNG社製、GALAXY SIIなどを挙げることができる。
インセルタッチパネル表示素子は、例えば、特開2011−76602号公報、特開2011−222009号公報等の公知技術を、何ら制限なく適用することができる。インセルタッチパネル表示素子を有する画像表示装置としては、ソニーエリクソン社製、エクスペリアPなどを挙げることができる。
オンセルタッチパネル表示素子は、例えば、特開2012−88683号公報等の公知技術を、何ら制限なく適用することができる。オンセルタッチパネル表示素子を有する画像表示装置としては、SAMSUNG社製、GALAXY SIIなどを挙げることができる。
本発明の光学フィルムを有するタッチパネルは、例えば、本発明の光学フィルムにタッチセンサーフィルムを貼り合わせてタッチセンサを含むタッチパネルである。本発明の光学フィルムがHC層を有する場合には、HC層が配置された面とは反対側の樹脂フィルム面にタッチセンサーフィルムを貼り合わせることが好ましい。
タッチセンサーフィルムとしては特に制限はないが、導電層が形成された導電性フィルムであることが好ましい。
導電性フィルムは、任意の支持体の上に導電層が形成された導電性フィルムであることが好ましい。
導電層は、電極パターンであることが好ましい。また、透明電極パターンであることも好ましい。電極パターンは透明導電材料層をパターニングしたものでもよく、不透明な導電材料の層をパターン形成したものでもよい。
金属細線が銀または銀を含む合金からなることが好ましい。金属細線が銀または銀を含む合金からなる導電層としては特に制限は無く、公知の導電層を用いることができる。例えば、特開2014−168886号公報の段落0040〜0041に記載の導電層を用いることが好ましく、この公報の内容は本明細書に組み込まれる。
金属細線が銅または銅を含む合金からなることも好ましい。上記合金は、特に制限は無く、公知の導電層を用いることができる。例えば、特開2015−49852号公報の段落0038〜0059に記載の導電層を用いることが好ましく、この公報の内容は本明細書に組み込まれる。
タッチセンサーフィルムは、両面に導電層を有することも好ましい。
本発明の光学フィルムを有する抵抗膜式タッチパネルは、本発明の光学フィルムを有する前面板を有する抵抗膜式タッチパネルである。
抵抗膜式タッチパネルは、導電性膜を有する上下1対の基板の導電性膜同士が対向するようにスペーサーを介して配置された基本構成からなるものである。なお抵抗膜式タッチパネルの構成は公知であり、本発明では公知技術を何ら制限なく適用することができる。
本発明の光学フィルムを有する静電容量式タッチパネルは、本発明の光学フィルムを有する前面板を有する静電容量式タッチパネルである。
静電容量式タッチパネルの方式としては、表面型静電容量式、投影型静電容量式等が挙げられる。投影型の静電容量式タッチパネルは、X軸電極と、X電極と直交するY軸電極とを絶縁体を介して配置した基本構成からなる。具体的態様としては、X電極およびY電極が、1枚の基板上の別々の面に形成される態様、1枚の基板上にX電極、絶縁体層、Y電極を上記順で形成する態様、1枚の基板上にX電極を形成し、別の基板上にY電極を形成する態様(この態様では、2枚の基板を貼り合わせた構成が上記基本構成となる)等が挙げられる。なお静電容量式タッチパネルの構成は公知であり、本発明では公知技術を何ら制限なく適用することができる。
また、図3に示すように、平坦化または、導電部材6Aおよび6Bを保護する目的で、導電部材6Aおよび導電部材6Bを覆うように透明な保護層7Aおよび保護層7Bが配置されていてもよい。
光学フィルム4Cには、後述する周辺領域S2を遮光する加飾層を形成してもよい。
透明絶縁基板5の材質としては、例えば、ガラス、PET(ポリエチレンテレフタレート)、PEN(ポリエチレンナフタレート)、COP(シクロオレフィンポリマー)、COC(シクロオレフィンポリマー)、PC(ポリカーボネート)等が使用できる。また、透明絶縁基板5の厚さは20〜200μmが好ましい。
光学フィルム4Cとタッチパネル用導電フィルム1との間には、粘着層(図中で図示しない)を設けてもよく、粘着層としては、光学透明粘着シート(Optical Clear Adhesive)または光学透明粘着樹脂(Optical Clear Resin)が使用できる。粘着層の好ましい厚みは10〜100μmである。光学透明粘着シートとしては、一般的には、例えば3M社製の8146シリーズが好ましく使用できる。粘着層の比誘電率の好ましい値は4.0〜6.0であり、より好ましくは5.0〜6.0である。
保護層7Aおよび保護層7Bとしては、例えば、ゼラチン、アクリル樹脂、ウレタン樹脂等の有機膜、および、二酸化シリコン等の無機膜を使用できる。厚みは、10nm以上100nm以下が好ましい。比誘電率は、2.5〜4.5が好ましい。
保護層7Aおよび保護層7B中のハロゲン不純物の濃度は、50ppm以下であることが好ましく、ハロゲン不純物は含有しないことがより好ましい。この態様によれば、導電部材6Aおよび導電部材6Bの腐食を抑制できる。
アクティブエリアS1内には、透明絶縁基板5の表面(第1面)上に形成された第1導電層8と透明絶縁基板5の裏面(第2面)上に形成された第2導電層9とが互いに重なるように配置されている。なお、第1導電層8および第2導電層9は、透明絶縁基板5を介して、互いに絶縁された状態で配置されている。
透明絶縁基板5の表面上の第1導電層8により、それぞれ第1の方向D1に沿って延び且つ第1の方向D1に直交する第2の方向D2に並列配置された複数の第1電極11が形成され、透明絶縁基板5の裏面上の第2導電層9により、それぞれ第2の方向D2に沿って延び且つ第1の方向D1に並列配置された複数の第2電極21が形成されている。
これら複数の第1電極11および複数の第2電極21は、タッチパネル2の検出電極を構成するものである。第1電極11および第2電極21の電極幅は1〜5mmが好ましく、電極間ピッチは3〜6mmであることが好ましい。
同様に、周辺領域S2における透明絶縁基板5の裏面上に、複数の第2電極21に接続された複数の第2周辺配線22が形成され、透明絶縁基板5の縁部に複数の第2外部接続端子23が配列形成されると共に、それぞれの第2電極21の両端に第2コネクタ部24が形成されている。第2コネクタ部24に、対応する第2周辺配線22の一端部が接続され、第2周辺配線22の他端部は、対応する第2外部接続端子23に接続されている。
タッチパネル用導電フィルム1は、透明絶縁基板5の表面上に第1電極11、第1周辺配線12、第1外部接続端子13および第1コネクタ部14を含む導電部材6Aを有すると共に、透明絶縁基板5の裏面上に第2電極21、第2周辺配線22、第2外部接続端子23および第2コネクタ部24を含む導電部材6Bを有する。
第1コネクタ部14および第2コネクタ部24を設けることで、電極と周辺配線との接続箇所での電気的導通を良くすることができる効果がある。特に、電極と周辺配線の材料が異なる場合は、第1コネクタ部14および第2コネクタ部24を設けることが好ましい。第1コネクタ部14および第2コネクタ部24の幅は、それぞれ接続される電極の幅の1/3以上、電極の幅以下であることが好ましい。第1コネクタ部14および第2コネクタ部24の形状はベタ膜形状でもよいし、国際公開WO2013/089085号公報に示されているような枠形状、またはメッシュ形状でもよい。
第1周辺配線12および第2周辺配線22の配線幅は10μm以上200μm以下であり、最小配線間隔(最小配線間距離)は20μm以上100μm以下であることが好ましい。
各周辺配線は、ウレタン樹脂、アクリル樹脂、エポキシ樹脂等からなる保護絶縁膜で覆ってもよい。保護絶縁膜を設けることにより、周辺配線のマイグレーション、錆び等を防止できる。なお、周辺配線の腐食を引きこす可能性があるので、絶縁膜中にはハロゲン不純物を含有しないことが好ましい。保護絶縁膜の厚みは1〜20μmが好ましい。
タッチパネル用導電フィルム1をタッチパネルとして使用する場合、第1外部接続端子13と第2外部接続端子23とは異方性導電フィルム(Anisotropic Conductive Film)を介してフレキブル配線基板(Flexible Printed Circuits)と電気的に接続される。フレキシブル配線基板は、駆動機能と位置検出機能とを有するタッチパネル制御基板に接続される。
第1外部接続端子13と第2外部接続端子23はフレキシブル配線基板との電気接続性を良くする目的で、第1周辺配線12および第2周辺配線22の配線幅より大きい端子幅で形成される。具体的には、第1外部接続端子13と第2外部接続端子23の端子幅は0.1mm以上0.6mm以下が好ましく、端子長さは0.5mm以上2.0mm以下が好ましい。
メッシュパターンの形状としては、図5のような同一のメッシュ(定形セル)が繰り返し配置されたパターンが好ましく、メッシュの形状はひし形が特に好ましいが、平行四辺形、正方形、長方形等の四角形でも良く、正六角形や他の多角形であっても良い。ひし形の場合、そのひし形の狭角角度は20°以上70°以下であることが表示装置の画素とのモアレ低減の観点から好ましい。メッシュの中心間距離(メッシュピッチ)は100〜600μmであることが視認性の観点から好ましい。第1金属細線15からなるメッシュパターンM1と第2金属細線25からなるメッシュパターンM2が同一形状であることが好ましい。さらに、図5のように、第1金属細線15からなるメッシュパターンM1と第2金属細線25からなるメッシュパターンM2とを、メッシュピッチ半分相当の距離だけずらして配置し、視認側からはメッシュピッチが半分になるメッシュパターンを形成するように配置することが、視認性の観点から好ましい。別の形態としては、メッシュの形状はランダムなパターン、または特開2013−214545号公報に示されているようなひし形の定形セルのピッチに10%程度のランダム性を付与するような、定形セル形状にある一定のランダム性を付与したセミランダム形状であっても良い。
また、互いに隣り合う第1電極11の間、互いに隣り合う第2電極21の間に、それぞれ第1金属細線15、第2金属細線25で形成された電極と絶縁されたダミーメッシュパターンを有していてもよい。ダミーメッシュパターンは、電極を形成するメッシュパターンと同一のメッシュ形状で形成することが好ましい。
ダイレクトボンディング方式に使用される透明な粘着剤は前述の透明な粘着層と同じく、光学透明粘着シート(Optical Clear Adhesive)または光学透明粘着樹脂(Optical Clear Resin)が使用でき、好ましい厚みは10μm以上100μm以下である。光学透明粘着シートとしては、例えば同じく3M社製の8146シリーズが好ましく使用できる。ダイレクトボンディング方式に使用される透明な粘着剤の比誘電率は、前述の透明な粘着層の比誘電率より小さいものを使用することがタッチパネル2の検出感度を向上させる点で好ましい。ダイレクトボンディング方式に使用される透明な粘着剤の比誘電率の好ましい値は、2.0〜3.0である。
上記可視光反射率の測定方法としては、以下のようにして測定する。先ず、日本分光社製紫外可視分光光度計V660(1回反射測定ユニットSLM−721)を使用し、測定波長350nmから800nm、入射角5度で反射スペクトルを測定する。なお、アルミ蒸着平面鏡の正反射光をベースラインとする。得られた反射スペクトルからXYZ表色系D65光源2度視野のY値(等色関数JIS Z9701−1999)を、日本分光社製色彩計算プログラムを用いて計算し、可視光反射率とする。
第1金属細線15を構成する材料で、第1電極11、第1周辺配線12、第1外部接続端子13および第1コネクタ部14を含む導電部材6Aを形成することができる。よって、第1電極11、第1周辺配線12、第1外部接続端子13および第1コネクタ部14を含む導電部材6Aはすべて同じ金属で同じ厚みで形成され、同時形成することができる。
第2電極21、第2周辺配線22、第2外部接続端子23および第2コネクタ部24を含む導電部材6Bに関しても同様である。
なお、第1電極11と隣接する第1ダミー電極11Aとは、連続的な第1メッシュパターンM1に沿って配置された金属細線に幅5μm以上30μm以下の断線を設けることにより、電気的に絶縁している。図6は、第1電極11と隣接する第1ダミー電極11Aとの境界線のみに断線を形成した形状であるが、第1ダミー電極11A内の第1セルC1の辺の全てに、または部分的に断線を形成してもよい。
また、図示しないが、アクティブエリアS1内における透明絶縁基板5の裏面上に配置されている第2導電層9は、複数の第2電極21の間にそれぞれ配置された複数の第2ダミー電極を有していてもよい。これらの第2ダミー電極は、複数の第2電極21から絶縁されており、第2電極21と同様に、多数の第2セルC2で構成された第2メッシュパターンM2を有している。
なお、第2電極21と隣接する第2ダミー電極とは、連続的な第2メッシュパターンM2に沿って配置された金属細線に幅5μm以上30μm以下の断線を設けることにより、電気的に絶縁している。第2電極21と隣接する第1ダミー電極との境界線のみに断線を形成した形状でもよいが、第2ダミー電極内の第2セルC2の辺の全てに、または部分的に断線を形成してもよい。
このとき、第1電極11は、第1メッシュパターンM1に沿って第1金属細線15が配置された第1導電層8からなり、第2電極21は、第2メッシュパターンM2に沿って第2金属細線25が配置された第2導電層9からなり、第1導電層8と第2導電層9とが透明絶縁基板5を挟んで図4のようにアクティブエリアS1内で互いに重なるように配置されるものとする。
これら導電部材6Aおよび導電部材6Bの形成方法は、特に限定されるものではない。例えば、特開2012−185813号公報の<0067>〜<0083>、特開2014−209332号公報の<0115>〜<0126>、または、特開2015−5495号公報の<0216>〜<0215>に記載されているように感光性ハロゲン化銀塩を含有する乳剤層を有する感光材料を露光し、現像処理を施すことによって、導電部材6Aおよび6Bを形成することができる。
例えば、透明絶縁基板5の一方の面側に、導電部材6Aと導電部材6Bが層間絶縁膜を介して配置される構成とすることもできる。
さらに、2枚基板の構成とすることもできる。すなわち、第1透明絶縁基板の表面上に導電部材6Aを配置し、第2透明絶縁基板の表面上に導電部材6Bを配置し、これら第1透明絶縁基板および第2透明絶縁基板を、光学透明粘着シート(Optical Clear Adhesive)を用いて貼り合わせて使用することもできる。
さらに、透明絶縁基板5を用いずに、図3に示した光学フィルム4Cの表面上に導電部材6Aと導電部材6Bが層間絶縁膜を介して配置される構成としてもよい。
また、US2012/0262414号公報等に開示されている交差部がない電極構成のように検出電極が基板の片側にしかない構成のタッチパネルにも適用できる。
さらに、タッチパネルは他の機能フィルムとの組合せとの使用も可能である、特開2014−13264号公報に開示されている高レタレーション値を有する基板を用いたニジムラを防止する画像品位向上用機能フィルム、特開2014−142462号公報に開示されているタッチパネルの電極の視認性改善の為の円偏光板との組合せ等も可能である。
本発明の光学フィルムは、一方の樹脂フィルムの、接着層を有する面とは反対側の面に、反射層(直線偏光反射層または円偏光反射層)を有してもよい。かかる光学フィルムは、画像表示素子と組み合わせることにより、画像表示機能付きミラーの前面板に用いられる光学フィルムとして好ましく用いられる。本発明の光学フィルムと反射層との間には、粘着層を設けてもよく、粘着層としては、光学透明粘着シート(Optical Clear Adhesive)または光学透明粘着樹脂(Optical Clear Resin)が使用できる。
本明細書において、画像表示機能付きミラーの前面板に用いられる、直線偏光反射層または円偏光反射層を有する光学フィルムを「ハーフミラー」と称することがある。
湾曲は、上下方向、左右方向、または上下方向および左右方向にあればよい。また、湾曲は、曲率半径が500〜3000mmであればよく、1000〜2500mmであることがより好ましい。曲率半径は、断面で湾曲部分の外接円を仮定した場合の、この外接円の半径である。
反射層としては、半透過半反射層として機能できる反射層を用いればよい。すなわち、反射層は、画像表示時には、画像表示素子が備える光源からの出射光を透過させることにより、画像表示機能付きミラーの前面に画像が表示されるように機能し、一方で、画像非表示時には、反射層は、前面方向からの入射光の少なくとも一部を反射するとともに、画像表示素子からの反射光を透過させ、画像表示機能付きミラーの前面がミラーとなるように機能するものであればよい。
反射層としては、偏光反射層が用いられる。偏光反射層は、直線偏光反射層または円偏光反射層であればよい。
直線偏光反射層としては、例えば、(i)多層構造の直線偏光反射板、(ii)複屈折の異なる薄膜を積層してなる偏光子、(iii)ワイヤーグリッド型偏光子、(iv)偏光プリズムおよび(v)散乱異方性型偏光板が挙げられる。
誘電体薄膜の成膜方法としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、イオンプレーティングおよびイオンビーム等の真空蒸着法、スパッタリング等の物理的気相成長法(PVD法)ならびに化学的気相成長法(CVD法)が挙げられる。これらの中でも、真空蒸着法またはスパッタリング法が好ましく、スパッタリング法が特に好ましい。
複屈折の異なる薄膜を積層した偏光子としては、市販品を用いることができ、市販品としては、例えば、DBEF(登録商標)(3M社製)が挙げられる。
ワイヤーグリッド偏光子は、金属ワイヤーを周期的に配列したもので、テラヘルツ波帯域で主に偏光子として用いられる。ワイヤーグリッドが偏光子として機能するためには、ワイヤー間隔が入射電磁波の波長よりも十分小さいことが必要となる。
ワイヤーグリッド偏光子では、金属ワイヤーが等間隔に配列されている。金属ワイヤーの長手方向と平行な偏光方向の偏光成分はワイヤーグリッド偏光子において反射され、垂直な偏光方向の偏光成分はワイヤーグリッド偏光子を透過する。
ハーフミラーに円偏光反射層を用いることにより、前面側からの入射光を円偏光として反射させ、画像表示素子からの入射光を円偏光として透過させることができる。そのため、円偏光反射層を用いた画像表示機能付きミラーでは、偏光サングラスを介しても、画像表示機能付きミラーの方向に依存せずに、表示画像およびミラー反射像の観察を行うことができる。
Polλ/4円偏光反射層において、直線偏光反射板と1/4波長板とは直線偏光反射板の偏光反射軸に対しλ/4波長板の遅相軸が45°となるように配置されていればよい。また、1/4波長板と直線偏光反射板とは、例えば、接着層により接着されていればよい。
Polλ/4円偏光反射層において、直線偏光反射板が画像表示素子に近い面となるように配置して使用する、つまり、光学フィルムに対し1/4波長板および直線偏光反射板をこの順に配置して使用することで、画像表示素子からの画像表示のための光を効率よく円偏光に変換して、画像表示機能付きミラー前面から出射させることができる。画像表示素子からの画像表示のための光が直線偏光であるとき、この直線偏光を透過するように直線偏光反射板の偏光反射軸を調整すればよい。
Polλ/4円偏光反射層の厚みは2.0μm〜300μmの範囲が好ましく、8.0μm〜200μmの範囲がより好ましい。
直線偏光反射板としては、上記で直線偏光反射層として説明したものを用いることができる。
1/4波長板としては、後述する1/4波長板を用いることができる。
コレステリック円偏光反射層は、コレステリック液晶層を少なくとも1層含む。コレステリック円偏光反射層に含まれるコレステリック液晶層は可視光領域で選択反射を示すものであればよい。
円偏光反射層は2層以上のコレステリック液晶層を含んでいてもよく、配向層などの他の層を含んでいてもよい。円偏光反射層はコレステリック液晶層のみからなることが好ましい。また、円偏光反射層が複数のコレステリック液晶層を含むときは、それらは隣接するコレステリック液晶層と直接接していることが好ましい。円偏光反射層は、3層および4層など、3層以上のコレステリック液晶層を含んでいることが好ましい。
コレステリック円偏光反射層の厚みは、2.0μm〜300μmの範囲が好ましく、8.0〜200μmの範囲がより好ましい。
コレステリック液晶相は、特定の波長域において右円偏光または左円偏光のいずれか一方のセンスの円偏光を選択的に反射させるとともに他方のセンスの円偏光を選択的に透過する円偏光選択反射を示すことが知られている。本明細書において、円偏光選択反射を単に選択反射ということもある。
分光光度計UV3150(島津製作所社製、商品名)を用いて反射層の透過スペクトル(コレステリック液晶層の法線方向から測定したもの)を測定すると、選択反射領域に透過率の低下ピークがみられる。この最も大きいピーク高さの1/2の高さの透過率となる2つの波長のうち、短波長側の波長の値をλ1(nm)、長波長側の波長の値をλ2(nm)とすると、選択反射の中心波長と半値幅は下記式で表すことができる。
選択反射の中心波長=(λ1+λ2)/2
半値幅=(λ2−λ1)
上記のように求められる、コレステリック液晶層が有する選択反射の中心波長λは、コレステリック液晶層の法線方向から測定した円偏光反射スペクトルの反射ピークの重心位置にある波長と通常一致する。なお、本明細書において、「選択反射の中心波長」はコレステリック液晶層の法線方向から測定した時の中心波長を意味する。
上記式から分かるように、螺旋構造のピッチを調節することによって、選択反射の中心波長を調整できる。n値とP値を調節することにより、所望の波長の光に対して右円偏光または左円偏光のいずれか一方を選択的に反射させるための、中心波長λを調節することができる。
λd=n2×P×cosθ2
赤外光領域に選択反射の中心波長を有するコレステリック液晶層を設ける場合は、可視光領域に選択反射の中心波長をそれぞれ有するコレステリック液晶層すべてに対し、最も画像表示素子側にあることが好ましい。
選択反射の中心波長が同一の1種のコレステリック液晶層の形成のために、周期Pが同じで、同じ螺旋のセンスのコレステリック液晶層を複数積層してもよい。周期Pが同じで、同じ螺旋のセンスのコレステリック液晶層を積層することによっては、特定の波長での円偏光選択性を高くすることができる。
コレステリック円偏光反射層を用いた画像表示機能付きミラーにおいて、ハーフミラーはさらに1/4波長板を含んでいてもよく、高Re(面内レターデーション)位相差膜と、コレステリック円偏光反射層と、1/4波長板とをこの順に含むことが好ましい。
画像表示素子とコレステリック円偏光反射層との間に1/4波長板を含むことによって、特に、直線偏光により画像表示している画像表示素子からの光を円偏光に変換してコレステリック円偏光反射層に入射させることが可能となる。そのため、円偏光反射層において反射されて画像表示素子側に戻る光を大幅に減らすことができ、明るい画像の表示が可能となる。また、1/4波長板の利用によりコレステリック円偏光反射層において画像表示素子側に反射するセンスの円偏光を生じさせない構成が可能であるため、画像表示素子およびハーフミラーの間の多重反射による画像表示品質の低下が生じにくい。
すなわち、例えば、コレステリック円偏光反射層に含まれるコレステリック液晶層の選択反射の中心波長が、画像表示素子の白表示時の発光スペクトルにおける青色光の発光ピーク波長と略同一(例えば差異が5nm未満)であったとしても、円偏光反射層において画像表示側に反射するセンスの円偏光を生じさせることなく、画像表示素子の出射光を前面側に透過させることができる。
前者の1/4波長板の正面位相差は、画像表示素子の発光波長の1/4の長さであればよい。それゆえ、例えば画像表示素子の発光波長が450nm、530nmおよび640nmの場合は、450nmの波長で112.5nm±10nm、好ましくは112.5nm±5nm、より好ましくは112.5nm、530nmの波長で132.5nm±10nm、好ましくは132.5nm±5nm、より好ましくは132.5nm、640nmの波長で160nm±10nm、好ましくは160nm±5nm、より好ましくは160nmの位相差であるような逆分散性の位相差層が、1/4波長板として最も好ましいが、位相差の波長分散性の小さい位相差板や順分散性の位相差板も用いることができる。なお、「逆分散性」とは長波長になるほど位相差の絶対値が大きくなる性質を意味し、「順分散性」とは短波長になるほど位相差の絶対値が大きくなる性質を意味する。
λ/4波長板としては、市販品を用いることもでき、市販品としては、例えば、ピュアエース(登録商標) WR(帝人株式会社製ポリカーボネートフィルム)が挙げられる。
λ/4波長板はコレステリック円偏光反射層と、直接接していてもよく、接着層により接着されていてもよく、直接接していることが好ましい。
以下、コレステリック液晶層および液晶組成物から形成される1/4波長板の作製材料および作製方法について説明する。
上記1/4波長板の形成に用いる材料としては、重合性液晶化合物を含む液晶組成物などが挙げられる。上記コレステリック液晶層の形成に用いる材料としては、重合性液晶化合物と、さらにキラル剤(光学活性化合物)とを含む液晶組成物などが挙げられる。必要に応じてさらに界面活性剤や重合開始剤などと混合して溶媒などに溶解した上記液晶組成物を、仮支持体、支持体、配向膜、高Re位相差膜、下層となるコレステリック液晶層、または1/4波長板などに塗布し、配向熟成後、液晶組成物の硬化により固定化してコレステリック液晶層および/または1/4波長板を形成することができる。
重合性液晶化合物としては、重合性の棒状液晶化合物を用いればよい。
重合性の棒状液晶化合物の例としては、棒状ネマチック液晶化合物が挙げられる。棒状ネマチック液晶化合物としては、アゾメチン類、アゾキシ類、シアノビフェニル類、シアノフェニルエステル類、安息香酸エステル類、シクロヘキサンカルボン酸フェニルエステル類、シアノフェニルシクロヘキサン類、シアノ置換フェニルピリミジン類、アルコキシ置換フェニルピリミジン類、フェニルジオキサン類、トラン類およびアルケニルシクロヘキシルベンゾニトリル類が好ましく用いられる。低分子液晶化合物だけではなく、高分子液晶化合物も用いることができる。
コレステリック液晶層の形成に用いる材料はキラル剤を含んでいることが好ましい。キラル剤はコレステリック液晶相の螺旋構造を誘起する機能を有する。キラル剤は、化合物によって誘起する螺旋のセンスまたは螺旋ピッチが異なるため、目的に応じて選択すればよい。
キラル剤としては、特に制限はなく、通常用いられる化合物(例えば、液晶デバイスハンドブック、第3章4−3項、TN、STN用カイラル剤、199頁、日本学術振興会第142委員会編、1989に記載)、イソソルビドおよびイソマンニド誘導体を用いることができる。
キラル剤は、一般に不斉炭素原子を含むが、不斉炭素原子を含まない軸性不斉化合物あるいは面性不斉化合物もキラル剤として用いることができる。軸性不斉化合物または面性不斉化合物の例には、ビナフチル、ヘリセン、パラシクロファンおよびこれらの誘導体が含まれる。キラル剤は、重合性基を有していてもよい。キラル剤と液晶化合物とがいずれも重合性基を有する場合は、重合性キラル剤と重合性液晶化合物との重合反応により、重合性液晶化合物から誘導される繰り返し単位と、キラル剤から誘導される繰り返し単位とを有するポリマーを形成することができる。この態様では、重合性キラル剤が有する重合性基は、重合性液晶化合物が有する重合性基と、同種の基であることが好ましい。従って、キラル剤の重合性基も、不飽和重合性基、エポキシ基またはアジリジニル基であることが好ましく、不飽和重合性基であることがさらに好ましく、エチレン性不飽和重合性基であることが特に好ましい。
また、キラル剤は、液晶化合物であってもよい。
本発明に用いられる液晶組成物は、重合開始剤を含有していることが好ましい。紫外線照射により重合反応を進行させる態様では、使用する重合開始剤は、紫外線照射によって重合反応を開始可能な光重合開始剤であることが好ましい。光重合開始剤の例には、α−カルボニル化合物(米国特許第2367661号、米国特許第2367670号の各明細書記載)、アシロインエーテル(米国特許第2448828号明細書記載)、α−炭化水素置換芳香族アシロイン化合物(米国特許第2722512号明細書記載)、多核キノン化合物(米国特許第3046127号、米国特許第2951758号の各明細書記載)、トリアリールイミダゾールダイマーとp−アミノフェニルケトンとの組み合わせ(米国特許第3549367号明細書記載)、アクリジンおよびフェナジン化合物(特開昭60−105667号公報、米国特許第4239850号明細書記載)、アシルフォスフィンオキシド化合物(特公昭63−40799号公報、特公平5−29234号公報、特開平10−95788号公報、特開平10−29997号公報記載)、オキシム化合物(特開2000−66385号公報、日本特許第4454067号明細書記載)、ならびにオキサジアゾール化合物(米国特許第4212970号明細書記載)等が挙げられる。
液晶組成物中の光重合開始剤の含有量は、重合性液晶化合物量に対して0.1〜20質量%であることが好ましく、0.5質量%〜5質量%であることがさらに好ましい。
液晶組成物は、硬化後の膜強度向上、耐久性向上のため、任意に架橋剤を含有していてもよい。架橋剤としては、紫外線、熱、湿気等で硬化するものが好適に使用できる。
架橋剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えばトリメチロールプロパントリ(メタ)アクリレートおよびペンタエリスリトールトリ(メタ)アクリレート等の多官能アクリレート化合物;グリシジル(メタ)アクリレートおよびエチレングリコールジグリシジルエーテル等のエポキシ化合物;2,2−ビスヒドロキシメチルブタノール−トリス[3−(1−アジリジニル)プロピオネート]および4,4−ビス(エチレンイミノカルボニルアミノ)ジフェニルメタン等のアジリジン化合物;ヘキサメチレンジイソシアネートおよびビウレット型イソシアネート等のイソシアネート化合物;オキサゾリン基を側鎖に有するポリオキサゾリン化合物;ならびにビニルトリメトキシシランおよびN−(2−アミノエチル)3−アミノプロピルトリメトキシシラン等のアルコキシシラン化合物が挙げられる。また、架橋剤の反応性に応じて通常用いられる触媒を用いることができ、膜強度および耐久性向上に加えて生産性を向上させることができる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
液晶組成物における架橋剤の含有量は3質量%〜20質量%が好ましく、5質量%〜15質量%がより好ましい。架橋剤の含有量が、上記下限値以上であることにより、架橋密度向上の効果を得ることができる。また、上記上限値以下とすることにより、形成される層の安定性を維持することができる。
液晶組成物中には、安定的にまたは迅速にプレーナー配向とするために寄与する配向制御剤を添加してもよい。配向制御剤の例としては特開2007−272185号公報の段落〔0018〕〜〔0043〕等に記載のフッ素(メタ)アクリレート系ポリマーならびに特開2012−203237号公報の段落〔0031〕〜〔0034〕等に記載の式(I)〜(IV)で表される化合物などが挙げられる。
なお、配向制御剤としては1種を単独で用いてもよいし、2種以上を併用してもよい。
その他、液晶組成物は、塗膜の表面張力を調整し厚みを均一にするための界面活性剤、および重合性モノマー等の種々の添加剤から選ばれる少なくとも1種を含有していてもよい。また、液晶組成物中には、必要に応じて、さらに重合禁止剤、酸化防止剤、紫外線吸収剤、光安定化剤、色材、金属酸化物微粒子等を、光学的性能を低下させない範囲で添加することができる。
液晶組成物の調製に使用する溶媒としては、特に制限はなく、目的に応じて適宜選択することができるが、有機溶媒が好ましく用いられる。
有機溶媒としては、特に制限はなく、目的に応じて適宜選択することができ、例えばケトン類、アルキルハライド類、アミド類、スルホキシド類、ヘテロ環化合物、炭化水素類、エステル類およびエーテル類が挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。これらの中でも、環境への負荷を考慮した場合にはケトン類が特に好ましい。
仮支持体、配向膜、高Re位相差膜、1/4波長板、及び/又は下層となるコレステリック液晶層などへの液晶組成物の塗布方法は、特に制限はなく、目的に応じて適宜選択することができ、例えば、ワイヤーバーコーティング法、カーテンコーティング法、押し出しコーティング法、ダイレクトグラビアコーティング法、リバースグラビアコーティング法、ダイコーティング法、スピンコーティング法、ディップコーティング法、スプレーコーティング法およびスライドコーティング法などが挙げられる。また、別途支持体上に塗設した液晶組成物を転写することによっても実施できる。塗布した液晶組成物を加熱することにより、液晶分子を配向させる。コレステリック液晶層形成の際はコレステリック配向させればよく、1/4波長板形成の際は、ネマチック配向させることが好ましい。コレステリック配向の際、加熱温度は、200℃以下が好ましく、130℃以下がより好ましい。この配向処理により、重合性液晶化合物が、フィルム面に対して実質的に垂直な方向に螺旋軸を有するように捩れ配向している光学薄膜が得られる。ネマチック配向の際、加熱温度は、25℃〜120℃が好ましく、30℃〜100℃がより好ましい。
[実施例1]
<1.樹脂フィルムの作製>
(1)コア層セルロースアシレートドープ液の調製
下記の組成物をミキシングタンクに投入して撹拌し、コア層セルロースアシレートドープ溶液を調製した。
−−−−−−−−−−−−−−−−−−−−−−−
コア層セルロースアシレートドープ液
−−−−−−−−−−−−−−−−−−−−−−−
・アセチル置換度2.88、重量平均分子量260,000のセルロースアセテート 100質量部
・下記構造のフタル酸エステルオリゴマーA 10質量部
・下記式Iで表される化合物(A−1) 4質量部
・下記式IIで表される紫外線吸収剤(BASF社製) 2.7質量部
・光安定剤(BASF社製、商品名:TINUVIN123) 0.18質量部
・N−アルケニルプロピレンジアミン3酢酸(ナガセケムテックス社製、商品名:テークランDO) 0.02質量部
・メチレンクロライド(第1溶媒) 430質量部
・メタノール(第2溶媒) 64質量部
−−−−−−−−−−−−−−−−−−−−−−−
フタル酸エステルオリゴマーA(重量平均分子量:750)
式I:
上記のコア層セルロースアシレートドープ液90質量部に下記の無機粒子含有組成物を10質量部加え、外層セルロースアシレートドープ液を調製した。
−−−−−−−−−−−−−−−−−−−−−−−
無機粒子含有組成物
−−−−−−−−−−−−−−−−−−−−−−−
平均一次粒径20nmのシリカ粒子(日本アエロジル社製、商品名:AEROSIL R972) 2質量部
メチレンクロライド(第1溶媒) 76質量部
メタノール(第2溶媒) 11質量部
コア層セルロースアシレートドープ液 1質量部
−−−−−−−−−−−−−−−−−−−−−−−
外層セルロースアシレートドープ液がコア層セルロースアシレートドープ液の両側に配されるように、外層セルロースアシレートドープ液、コア層セルロースアシレートドープ液、および外層セルロースアシレートドープ液の3種を、流延口から表面温度20℃の流延バンド上に同時に流延した。
流延バンドとして幅2.1mで長さが70mのステンレス製のエンドレスバンドを利用した。流延バンドは、厚みが1.5mm、表面粗さが0.05μm以下になるように研磨した。その材質はSUS316製であり、十分な耐腐食性と強度を有する流延バンドを用いた。流延バンドの全体の厚みムラは0.5%以下であった。
得られた流延膜に、風速が8m/s、ガス濃度が16%、温度が60℃の急速乾燥風を流延膜表面に当てて初期膜を形成した。その後、流延バンド上部の上流側からは140℃の乾燥風を送風した。また下流側からは120℃の乾燥風および60℃の乾燥風を送風した。
残留溶媒量を約33質量%にした後、バンドから剥ぎ取った。次いで、得られたフィルムの幅方向の両端をテンタークリップで固定し、溶媒残留量が3〜15質量%のフィルムを、横方向に1.06倍延伸しつつ乾燥した。その後、熱処理装置のロール間を搬送することにより、更に乾燥し、厚みが100μm(外層/コア層/外層=3μm/94μm/3μm)である第一の樹脂フィルム(A)を作製した。
第一の樹脂フィルム(A)と同様の作製方法で、厚みが100μmである第二の樹脂フィルム(C)を作製した。
作製した樹脂フィルム(A)および(C)を、液温55℃に保った1.5mol/LのNaOH水溶液(ケン化液)に2分間浸漬した後、フィルムを水洗し、その後、液温25℃の0.05mol/Lの硫酸水溶液に30秒浸漬した後、更に30秒流水下に通して水洗し、フィルムを中性の状態にした。そして、エアナイフによる水切りを3回繰り返し、水を落とした後に雰囲気温度70℃の乾燥ゾーンに15秒間滞留させて乾燥し、ケン化処理した樹脂フィルム(A)および(C)を作製した。
以降、光学フィルムの作製においては、ケン化処理した樹脂フィルム(A)および(C)を単に樹脂フィルム(A)および(C)と称す。
下記表1に示す配合で各成分を混合し、孔径10μmのポリプロピレン製フィルターでろ過して、接着層(B)形成用液A−1〜A−9を調製した。
表1に記載した各化合物の詳細を以下に示す。
エポクロス WS300:商品名(日本触媒社製)、オキサゾリン基含有ポリマー
HEC:ヒドロキシエチルセルロース、重量平均分子量74,000
ゴーセネックス Z410:商品名(日本合成化学社製)、アセトアセチル変性ポリビニルアルコール
PVA−117H:クラレポバールPVA−117H(商品名、クラレ社製)、ポリビニルアルコール
セロキサイド2021P:商品名(ダイセル社製)、以下に示すエポキシ基含有化合物
CPI100P:商品名(サンアプロ社製)、以下に示すトリアリールスルホニウム塩系の光酸発生剤
スルーリア2320:商品名(日輝触媒社製)、中空シリカ、平均粒径50nm、固形分濃度20.5質量%。表中では固形分量での配合質量比を示す。
ZrO2:酸化ジルコニウム、平均粒径4nm
上記で作製した膜厚100μmの樹脂フィルム(A)のバンド側と接していた面に、上記で作製した接着層形成用液A−1を乾燥後の接着層(B)の厚みが0.5μmとなるように塗布した。次いで、樹脂フィルム(C)のバンド側と接していた面と上述の接着層(B)とを、ロール機で圧力3MPa、速度900rpmの条件で貼り合わせ、雰囲気温度70℃で10分以上乾燥して、樹脂フィルム(A)および(C)が接着層(B)で貼り合わされた積層体を作製した。
下記表2に示す配合で各成分を混合し、孔径10μmのポリプロピレン製フィルターでろ過して、ハードコート層(HC層)形成用硬化性組成物HC−1およびHC−2を調製した。
表2に記載した各化合物の詳細を以下に示す。
DPHA:ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物(日本化薬社製、商品名:KAYARAD DPHA)
サイクロマーM100:3,4−エポキシシクロヘキシルメチルメタクリレート(ダイセル社製、商品名)
Irg184:1−ヒドロキシ−シクロヘキシル−フェニル−ケトン(α−ヒドロキシアルキルフェノン系のラジカル光重合開始剤、BASF社製、商品名:IRGACURE184)
PAG−1:以下に示すヨードニウム塩化合物であるカチオン光重合開始剤
RS−90:防汚剤、商品名(DIC社製)、ラジカル重合性基を有する含フッ素オリゴマー
P−112:レベリング剤、特許5175831号の段落0053に記載の化合物P−112
MEK:メチルエチルケトン
MIBK:メチルイソブチルケトン
上記で作製した積層体の、接着層(B)とは逆側の樹脂フィルム(A)の表面上に、HC層形成用硬化性組成物HC−1を塗布し、硬化させてハードコート層を形成した。
塗布および硬化の方法は、具体的には、次の通りとした。特開2006−122889号公報の実施例1記載のスロットダイを用いたダイコート法で、搬送速度30m/分の条件でHC層形成用硬化性組成物を塗布し、雰囲気温度60℃で150秒間乾燥した。その後、更に窒素パージ下、酸素濃度約0.1体積%で160W/cmの空冷メタルハライドランプ(アイグラフィックス社製)を用いて、照度20mW/cm2、照射量30mJ/cm2の紫外線を照射して、塗布したHC層形成用硬化性組成物を硬化させてハードコート層HC−1を形成した後、巻き取りを行った。
接着層形成用液A−1に代えて接着層形成用液A−2、A−5又はA−6をそれぞれ使用した以外は実施例1と同様にして、実施例2〜4の光学フィルムを作製した。
樹脂フィルム(A)および(C)として、特許第3325560号公報[実施例3]を参考に作製した、厚み100μmのポリカーボネートフィルム(550nmにおける面内方向のレターデーションは140nmだった。)を使用し、接着層形成用液A−1に代えて接着層形成用液A−8を使用した以外、実施例1と同様の方法で、実施例7の光学フィルムを作製した。下記表3において、ポリカーボネートフィルムをPCと記載した。
樹脂フィルム(C)として、上記で作製したアクリル樹脂フィルム(PMMA)を使用し、接着層形成用液A−1に代えて接着層形成用液A−9を使用した以外は実施例1と同様にして、実施例8の光学フィルムを作製した。
接着層(B)の厚みを下記表3に記載の厚みに変更した以外は、実施例2と同様にして、実施例9〜12の光学フィルムを作製した。
[比較例1及び2]
接着層形成用液A−1に代えて接着層形成用液A−4又はA−3をそれぞれ使用した以外は実施例1と同様にして、比較例1及び2の光学フィルムを作製した。
[比較例4]
樹脂フィルム(C)として、上記で作製したポリカーボネート樹脂フィルム(PC)を使用し、接着層形成用液A−1に代えて接着層形成用液A−3を使用した以外は実施例1と同様にして、比較例4の光学フィルムを作製した。
上記で作製した光学フィルムについて、以下の試験を行った。試験結果を下記表3にまとめて記載する。なお、表3中、引張弾性率は、弾性率と略して記載する。
ガラス板(Corning社製、商品名:イーグル XG、厚み1mm)と、上記で作製した光学フィルム(HC層付き積層体)とを、ガラス板と樹脂フィルム(C)側が向かい合うようにして、厚み20μmの粘着剤(綜研化学社製、商品名:SK−2057)を介して、ゴムローラーで2kgの荷重を掛けながら貼り合わせて、温度25℃、相対湿度60%で2時間調湿した。作製した試験片を、打鍵試験機(株式会社YSC製)を用いて、HC層の上方から入力ペン(ペン先材料はポリアセタール、半径R=0.8mm、ワコム株式会社製)を押し当て(打鍵速度:2回/分、荷重:250g)、光学フィルムの正面から三波長蛍光灯(ナショナルパルック蛍光灯FL20SS・EX−D/18)で照らしながら目視で観察し、以下の基準で「打鍵耐久性」を評価した。
<評価基準>
A:50000回打鍵しても凹みが発生しなかった。
B:10001回〜50000回打鍵する間に凹みが発生した。
C:1001回〜10000回打鍵する間に凹みが発生した。
D:101回〜1000回打鍵する間に凹みが発生した。
上記で作製した積層体(HC層付与前の積層体)を、第一の樹脂フィルム(A)を上にしてブラックボードの上に置き、積層体の正面50cm手前から三波長蛍光灯(パナソニック社製、ナショナルパルック蛍光灯FL20SS・EX−D/18)でサンプルを照らしながら目視で干渉ムラを観察し、以下の基準で評価した。
<評価基準>
A:干渉ムラが全く見えない。
B:干渉ムラがほとんど見えない。
C:干渉ムラが弱く見えるところがある。
D:干渉ムラが全体に弱く見えるが、問題ないレベルであった。
E:干渉ムラが全体に強く見え、問題があるレベルであった。
各樹脂フィルムの「引張弾性率」は、JIS K7127に記載の方法に従って、以下の方法により試験し、算出した。
上記で作製した樹脂フィルムについて、測定方向に15cmの長さで、幅1cm、の樹脂フィルムを測定用試料として切り出した。切り出した測定用試料を、引張試験機(東洋精機社製、商品名「ストログラフ−R2」)に、測定方向のチャック間隔が10cmとなるように設置し、測定温度25℃の条件下、延伸速度10mm/分でチャック間隔が広がるように延伸し、応力−ひずみ曲線を得た。規定された2点のひずみε1=0.0005及びε2=0.0025の間の曲線の線形回帰により、25℃における引張弾性率を算出した。
なお、樹脂フィルムが異方性を有する場合は、樹脂フィルムの厚み方向に垂直な面において、配向度の最も大きい配向方向を長辺とする測定用試料の引張弾性率と、この配向方向と直行する方向を長辺とする測定用試料の引張弾性率との平均を、樹脂フィルムの引張弾性率とした。
接着層の「弾性率」については、上記で使用した各接着層形成用液について、ガラス板(厚み1mm)上にアプリケーターを用いて乾燥後の膜厚が20μmとなるように流延し、雰囲気温度80℃で10分以上乾燥したのち、ガラス板から剥離した。得られた接着層の試料を用いて、上記樹脂フィルムの引張弾性率と同様の方法により試験し、算出した。
各樹脂フィルムの「屈折率」は、JIS K7142に記載の方法に従って、アッベ屈折率計(アタゴ社製)を用い、25℃の温度条件下、光源にナトリウムD線(589nm)を用い、測定した。
なお、樹脂フィルムが異方性を有する場合は、樹脂フィルムの厚み方向に垂直な面において、配向度の最も大きい配向方向の屈折率と、この配向方向と直行する方向の屈折率との平均を、樹脂フィルムの屈折率とした。
接着層の「屈折率」については、樹脂フィルム(A)上に接着層形成用液を塗布し、乾燥処理を施して溶媒を除去し、厚み1μmの接着層を形成した。得られた接着層の表面屈折率を、上記樹脂フィルムの屈折率と同様の方法により測定した。
「厚み」は、以下の方法により、走査型電子顕微鏡(Scanning Electron microscope;SEM)により観察して測定した。
各構成部材(樹脂フィルム、接着層及びHC層)または各構成部材を含む部材(例えば液晶パネルやその一部)の断面を、イオンビーム、ミクロトーム等の常法により露出させた後、露出した断面においてSEMによる断面観察を行った。断面観察において、部材の幅方向を4等分した際の、両端を除く3つの等分点における厚みの算術平均として、各種厚みを求めた。
<表の注>
接着層(B)の粒子(含有量%):接着層(B)に含まれる粒子の種類、および、接着層(B)を構成する固形分中の粒子の含有質量%を意味し、「−」は粒子を含まないことを意味する。
光学フィルムの厚み:樹脂フィルム(A)と接着層(B)と樹脂フィルム(C)の合計厚みを意味する。
これに対して、樹脂フィルム(A)、接着層(B)及び樹脂フィルム(C)の屈折率が式(1)及び(2)を満たし、樹脂フィルム(A)、接着層(B)及び樹脂フィルム(C)の引張弾性率が式(3)〜(7)を満たし、光学フィルムの厚みが100μmより大きい実施例1〜4及び7〜12の本発明の光学フィルムは、いずれも、干渉ムラが十分に抑制され、また、打鍵耐久性に優れていた。
樹脂フィルム(C)として、フジタックTDP40UT(商品名、富士フイルム社製、屈折率:1.48、引張弾性率:5.4MPa)を使用した以外は実施例3と同様にして、実施例13の光学フィルムを作製した。
樹脂フィルム(A)として、フジタックTG40UL(商品名、富士フイルム社製、屈折率:1.48、引張弾性率:4.8MPa)を使用した以外は実施例3と同様にして、実施例14の光学フィルムを作製した。
(偏光板の作製)
(1)光学フィルムの鹸化
実施例で作製した各光学フィルム及びフジタックZRD40、TJ40(いずれも商品名、富士フイルム社製)を37℃に調温した4.5mol/Lの水酸化ナトリウム水溶液(けん化液)に1分間浸漬した後、フィルムを水洗し、その後、0.05mol/Lの硫酸水溶液に30秒浸漬した後、更に水洗浴を通した。そして、エアナイフによる水切りを3回繰り返し、水を落とした後に70℃の乾燥ゾーンに15秒間滞留させて乾燥し、鹸化処理した光学フィルムを作製した。
特開2001−141926号公報の実施例1に従い、2対のニップロール間に周速差を与え、長手方向に延伸し、厚み20μmの偏光膜を調製した。
このようにして得た偏光膜の両面に、鹸化処理した光学フィルムを、表4に記載の組み合わせで、PVA(クラレ社製、商品名:PVA−117H)3%水溶液を接着剤として用いて、偏光軸と光学フィルムのMD方向とが平行となるようにロールツーロールで貼り合わせて、光学フィルム1/偏光膜/光学フィルム2の構成からなる偏光板101〜104を作製した。
作製した偏光板101〜103から、偏光板の吸収軸と平行する方向が長辺となるように、サイズ250mm×140mmの試験片101〜103を切り出した。また、作製した偏光板104から、偏光板の吸収軸と直交する方向が長辺となるように、サイズ250mm×140mmの試験片104を切り出した。
得られた試験片101〜103のZRD40側の表面に、アクリル系粘着剤(20μm)を介してサイズ255mm×150mmのガラス板(0.3mm厚)をそれぞれ貼り合わせた。得られた偏光板付きガラス板における、試験片101〜103と反対側のガラス板表面に、試験片104を粘着剤を介して貼り合わせた。このとき、試験片101〜103の吸収軸と試験片104の吸収軸が直交するように、かつ、試験片104のZRD40側がガラス板と対向するように貼り合わせた。
得られた偏光板付きガラス板に対して、60℃相対湿度90%で48時間保持する処理(以下、「湿熱処理」とも称す。)をした後にガラス板の4角の反り量を測定し、その平均値を求め、湿熱処理後の反り量とした。また、80℃で48時間保持する処理(以下、「熱処理」とも称す。)をした後にガラス板の4角の反り量を測定し、その平均値を求め、熱処理後の反り量とした。
第一の樹脂フィルム(A)と第二の樹脂フィルム(C)の、下記式(9)で表される湿熱処理後の収縮力Fw(単位:10N/m)および下記式(8)で表される熱処理後の収縮力Fd(単位:10N/m)を算出した。
式(9) Fw=Ew×εw×dw
[式中、Ew、εw、dwは、樹脂フィルムを60℃、相対湿度90%の環境で48時間保持した後のMD方向の弾性率、MD方向の湿度寸法変化率の絶対値、膜厚をそれぞれ表す。]
式(8) Fd=Ed×εd×dd
[式中、Ed、εd、ddは、樹脂フィルムを80℃の環境で48時間保持した後のMD方向の弾性率、MD方向の寸法変化率の絶対値、膜厚をそれぞれ表す。]
ここで、MD方向の弾性率は試験例3に記載の方法に従って求めた。
MD方向の寸法変化率の絶対値は、第一の樹脂フィルム(A)と第二の樹脂フィルム(C)から、MD方向を長手方向として切り出した長さ12cm(測定方向)、幅3cmのフィルム試料をそれぞれ用意し、この試料に10cmの間隔でピン孔を空け、25℃相対湿度60%にて24時間調湿後、ピン孔の間隔L0をピンゲージで測長した。続いてこの試料を60℃、相対湿度90%の環境で48時間、もしくは80℃の環境で48時間保持した後、25℃、相対湿度80%(湿熱処理後)もしくは25℃、相対湿度10%(熱処理後)にてそれぞれ48時間調湿後、ピン孔の間隔L1をピンゲージで測長した。これらの測定値L0及びL1を用いて下記式により寸法変化率の絶対値を算出した。
寸法変化率[%]=|L0−L1|
膜厚は試験例5に記載の方法に従って求めた。
1B:第二の樹脂フィルム
2A:接着層
3A:ハードコート層(HC層)
4A、4B:光学フィルム
1:タッチパネル用導電フィルム
2:タッチパネル
4C:光学フィルム
5:透明絶縁基板
6A、6B:導電部材
7A、7B:保護層
8:第1導電層
9:第2導電層
11A:第1ダミー電極
11:第1電極
12:第1周辺配線
13:第1外部接続端子
14:第1コネクタ部
15:第1金属細線
21:第2電極
22:第2周辺配線
23:第2外部接続端子
24:第2コネクタ部
25:第2金属細線
C1:第1セル
C2:第2セル
D1:第1の方向
D2:第2の方向
M1:第1メッシュパターン
M2:第2メッシュパターン
S1:アクティブエリア
S2:周辺領域
Claims (16)
- 第一の樹脂フィルム(A)と、該第一の樹脂フィルム(A)の片面に配された接着層(B)と、該接着層(B)の該第一の樹脂フィルム(A)側とは反対側に配された第二の樹脂フィルム(C)とを少なくとも有し、
前記第一の樹脂フィルム(A)の屈折率nA、前記接着層(B)の屈折率nB及び前記第二の樹脂フィルム(C)の屈折率nCが下記式(1)及び(2)を満たし、
|nA−nB|≦0.03 式(1)
|nC−nB|≦0.03 式(2)
前記第一の樹脂フィルム(A)の引張弾性率EA、前記接着層(B)の引張弾性率EB及び前記第二の樹脂フィルム(C)の引張弾性率ECが下記式(3)〜(7)を満たし、
|EA−EB|≦2.5GPa 式(3)
|EC−EB|≦2.5GPa 式(4)
2.0GPa≦EA≦12.0GPa 式(5)
2.0GPa≦EB≦12.0GPa 式(6)
2.0GPa≦EC≦12.0GPa 式(7)
前記第一の樹脂フィルム(A)と前記第二の樹脂フィルム(C)の少なくとも一方がセルロースエステルフィルムであり、
前記第一の樹脂フィルム(A)、前記接着層(B)及び前記第二の樹脂フィルム(C)の合計厚みが100μmより大きく320μm以下である、光学フィルム。 - 前記接着層(B)の厚みが10nm以上10μm以下である、請求項1に記載の光学フィルム。
- 面内方向のレターデーションが6000nmより小さい、請求項1又は2に記載の光学フィルム。
- 前記第一の樹脂フィルム(A)と前記第二の樹脂フィルム(C)が同一のフィルムである、請求項1〜3のいずれか1項に記載の光学フィルム。
- 前記第一の樹脂フィルム(A)と前記第二の樹脂フィルム(C)を、80℃の環境で48時間保持した後の下記式(8)で表される収縮力Fdが互いに異なる請求項1〜3のいずれか1項に記載の光学フィルム。
式(8) Fd=Ed×εd×dd
式中、Ed、εd、ddは、樹脂フィルムを80℃の環境で48時間保持した後のMD方向の弾性率、MD方向の寸法変化率の絶対値、膜厚をそれぞれ表す。 - 前記第一の樹脂フィルム(A)と前記第二の樹脂フィルム(C)を、60℃、相対湿度90%の環境で48時間保持した後の下記式(9)で表される収縮力Fwが互いに異なる請求項1〜3のいずれか1項に記載の光学フィルム。
式(9) Fw=Ew×εw×dw
式中、Ew、εw、dwは、樹脂フィルムを60℃、相対湿度90%の環境で48時間保持した後のMD方向の弾性率、MD方向の湿度寸法変化率の絶対値、膜厚をそれぞれ表す。 - 前記第一の樹脂フィルム(A)及び前記第二の樹脂フィルム(C)の少なくとも一方が、前記接着層(B)と反対側の面にハードコート層を有する、請求項1〜6のいずれか1項に記載の光学フィルム。
- 請求項1〜7のいずれか1項に記載の光学フィルムを有する、画像表示装置の前面板。
- 請求項8に記載の前面板と、画像表示素子とを有する画像表示装置。
- 前記画像表示素子が液晶表示素子である、請求項9に記載の画像表示装置。
- 前記画像表示素子が有機エレクトロルミネッセンス表示素子である、請求項9に記載の画像表示装置。
- 前記画像表示素子がインセルタッチパネル表示素子である、請求項9〜11のいずれか1項に記載の画像表示装置。
- 前記画像表示素子がオンセルタッチパネル表示素子である、請求項9〜11のいずれか1項に記載の画像表示装置。
- 請求項8に記載の前面板を有する抵抗膜式タッチパネル。
- 請求項8に記載の前面板を有する静電容量式タッチパネル。
- 請求項9に記載の画像表示装置を用いた画像表示機能付きミラー。