JP6738743B2 - Surface structure film manufacturing method and manufacturing apparatus - Google Patents

Description

The present invention relates to a method for manufacturing a surface structure film by transferring a surface structure to a film and a manufacturing apparatus therefor. The surface structure film obtained by the method of the present invention is an optical film having optical functions such as diffusion, light collection, reflection, and transmission, and an uneven structure film having a super liquid repellent function and cell culture suitability, such as micron size. It is used as a member that requires a nano-sized fine structure on its surface.

As a method for producing a surface structure film having a fine structure on the surface, a mold having a fine structure formed on the surface is used, and a thermosetting or radiation curable material is applied to the mold or the film before being supplied to the mold. After coating, the film is held in a heated mold to form a fine structure in the coating film and cured, and by further peeling the film from the mold, a fine structure is formed on the surface of the film. There is a method of transferring to obtain a surface structure film.

In Patent Document 1, after applying sol-gel, which is a thermosetting material, to a film mold drawn out by roll-to-roll, heat treatment is performed while pressing the mold against the substrate, thereby forming a fine structure made of the sol-gel material on the surface of the substrate. A method of transferring to a substrate is described. A fine structure is previously formed on the surface of the film mold, and a structure having substantially the same shape as this fine structure is also formed on the substrate surface. Since the sol-gel material is applied, it is possible to form an uneven structure having relatively high heat resistance.

Further, in Patent Document 2, a film having a surface coated with a radiation curable resin is irradiated while being pressed against an endless belt having a fine structure formed thereon to form a fine structure on the film surface, and then a mold is formed. And a method of producing a film having a fine structure formed on the surface thereof by peeling the film. It is described that the endless belt uses a replica made of resin, which makes it possible to reduce the molding cost.

Further, in Reference Document 3, after the raw material which is the thermoplastic resin is softened by the first heating roll to form a concavo-convex structure, the concavo-convex structure is formed while the foam material is foamed by heating on the second heating roll. There is described a method of laminating on the original fabric on which the is formed. It is described that the temperature of the first heating roll and the temperature of the second heating roll can be individually set according to the raw material and the foam material to be used, which allows the formation of the uneven structure on the raw material and the foaming of the foam material. And, it becomes possible to perform stacking in a series of operations.

Japanese Patent No. 5695804 JP, 2008-137282, A

Reference 3

JP, 2001-277354, A

However, in the method for producing a fine structure transfer film described in Patent Document 1, there is a problem that the molding cost increases because a long film roll is used as the mold. Also, although it can be applied to a sheet-shaped substrate, when applied to a roll-to-roll film, the mold and the substrate are peeled off while the thermosetting material remains uncured due to shrinkage during heating, and a predetermined surface structure cannot be formed. There was a problem. Even if it can be cured without peeling off, in the state where the film and the mold are laminated, the curing material cannot be sufficiently filled up to the inside of the pattern formed on the mold surface, and as a result, the transferred pattern shape is There was a problem of becoming defective.

In addition, in the method for manufacturing a fine structure transfer film described in Patent Document 2, when applied to a material made of a thermosetting material, the mold and the substrate are peeled off while the thermosetting material remains uncured due to shrinkage during curing. There is a problem that the surface structure cannot be formed. Moreover, since the flatness of the thermosetting material applied to the mold surface is poor, adhesion failure between the thermosetting material and the substrate occurs in the state where the thermosetting material is laminated on the substrate, and the thermosetting material is evenly distributed on the substrate. There was a problem that it was not transferred.

Further, in the method for producing a fine structure transfer film described in Reference Document 3, both the first heating roll and the second heating roll need to be at a high temperature, and it is possible to maintain the concavo-convex structure of the raw material which is a thermoplastic resin. However, in order to continuously wind the product, in addition to the two heating rolls, a cooling roll for cooling the product is required, which causes a problem that the equipment becomes large.

An object of the present invention is to solve the above problems, and to provide an apparatus and method for continuously and uniformly transferring a fine surface structure containing a thermosetting material to a film surface at a highly accurate and inexpensive molding cost. To provide.

The present invention is the following manufacturing method and manufacturing apparatus.

A manufacturing apparatus for manufacturing a surface structure film having a surface structure containing a thermosetting material on the surface of a film,
(1) An endless belt-shaped mold having a surface structure formed thereon,
(2) Mold conveying means for conveying the mold held by two or more heating rolls by rotating the heating rolls,
(3) Pressurization including at least a nip roll arranged in parallel with the first heating roll of the mold conveying means and having a surface covered with an elastic body, and a pinching means using the heating roll and the nip roll roll. Mechanism,
(4) A mold coating unit installed on the upstream side of the pressing mechanism in the transport direction of the mold and configured to coat a surface of the mold on which the surface structure is formed with a material.
(5) film supply means for supplying a film to the surface of the mold,
(6) A film coating unit, which is arranged on the upstream side of the pressing mechanism in the film transport direction, for coating a material on a surface of the film that contacts the mold,
(7) Film peeling means for peeling the film on the surface of the mold,
An apparatus for producing a surface structure film, which comprises at least:

A method of making a surface structured film comprising a thermosetting material, the method comprising:
(1) The endless belt-shaped mold having the surface structure formed thereon is held by at least two or more heated heating rolls. A step of applying the thermosetting material A,
(2) A step of applying the thermosetting material B on the surface of the film,
(3) Step of bonding the mold and the film so that the thermosetting material A and the thermosetting material B are in contact with each other (4) The film, the thermosetting material A, and the thermosetting material B And (5) pressing the mold with a nip roll in a stacked state, heating the film after pressing, the thermosetting material A, the thermosetting material B, and the mold in a stacked state While carrying,
(6) A step of peeling the surface structure film composed of the film, the thermosetting material A, and the thermosetting material B from the mold,
A method for producing a surface structure film, comprising at least:

According to the present invention, the surface structure film can be manufactured by applying an endless belt-shaped mold. The cost of the mold can be reduced because the process of manufacturing a roll film-shaped long mold for each product as in the conventional technique can be omitted. Further, even in the curing process, the laminated state can be maintained without peeling off the film and the mold, and uniform adhesion between the cured material and the film can be obtained, so that a highly accurate surface structure can be formed.

It is the schematic which saw an example of the manufacturing apparatus of the surface structure film of this invention from the cross section. It is the schematic which saw an example of the manufacturing apparatus of the surface structure film of this invention from the cross section. It is the schematic which saw an example of the manufacturing apparatus of the surface structure film of this invention from the cross section. It is the schematic which saw an example of the manufacturing apparatus of the surface structure film of this invention from the cross section. It is the schematic which saw an example of the manufacturing apparatus of the surface structure film of this invention from the cross section. It is the schematic which saw an example of the manufacturing apparatus of the surface structure film of this invention from the cross section. It is the schematic which saw an example of the apparatus which manufactures the mold applied to the surface structure film concerning this invention from the cross section. It is the perspective view which showed an example of the surface structure film manufactured by the manufacturing method of the surface structure film of this invention. 1 is a photograph of the surface of the surface structure film manufactured in Example 1 observed by an electron microscope.

Since the apparatus for manufacturing a surface structure film of the present invention conveys the endless belt-shaped mold having the surface structure and the mold held by two or more heating rolls by rotating the heating roll, Of the mold conveying means, a nip roll arranged in parallel with the first heating roll in the mold conveying means and having a surface covered with an elastic body, and a pinching means using the heating roll and the nip roll. A pressurizing mechanism, a mold applicator unit installed upstream of the pressurizing mechanism in the conveying direction of the mold, for applying a material to the surface of the mold on which the surface structure is formed, and the mold surface. A film supply unit for supplying a film, a film coating unit arranged on the upstream side of the pressing mechanism in the film transport direction for coating a material on a surface of the film in contact with the mold, and a surface of the mold. A film peeling means for peeling off the film, and a manufacturing device.

FIG. 1 is a schematic view of an example of an apparatus for producing a surface structure film of the present invention, as seen from a cross section. The surface structure film manufacturing apparatus 10 is an example of an apparatus for forming a surface structure film 15 in which a structure including a thermosetting material A13 and a thermosetting material B13' is formed on the surface of the film 11. Note that the thermosetting material A and the thermosetting material B are preferably the same material from the viewpoint of adhesion when they are bonded, but they are not necessarily the same material, and those that are mixed at the interface of both materials and cured A material capable of exhibiting adhesiveness at the interface at that time may be selected.

As shown in FIG. 1, an apparatus 10 for manufacturing a surface structure film according to the present invention suspends an endless belt-shaped mold 12 and a first heating roll 21 and a second heating roll 22 and conveys them in a circular manner. The mold conveying means 20, the pressure mechanism 27 for pressing the nip roll 28 arranged in parallel with the first heating roll 21 against the first heating roll 21, and the thermosetting material A13 applied to the surface of the mold 12. Mold coating unit 30, a film supply unit 23 for supplying the film 11 to the surface of the mold 12, and a film coating unit 33 for coating the surface of the film 11 on the mold 12 contact side with the thermosetting material B13′. And a film peeling means 24 for peeling the surface structure film 15 from the mold 12. The outline of each configuration is as follows.

The mold conveying unit 20 includes a first heating roll 21, a second heating roll 22, and a drive unit that rotates both rolls or the first heating roll 21. When only the first heating roll 21 is rotationally driven, the second heating roll 22 is held so as to be freely rotatable and is rotated by friction with the mold 20. Further, the first heating roll 21 and the second heating roll 22 include heating means. As the heating means, a structure of heating from the inside of the roll is preferable, but an infrared heater or an induction heating device may be installed near the outer surface of the roll to accelerate heating from the outer surface of the roll.

The pressure mechanism 27 is a mechanism that can press the nip roll 28 against the first heating roll 21 with a uniform pressure in the width direction. The nip roll 28 has a structure in which the outer surface of the core layer is covered with an elastic body. Both ends of the core layer are rotatably supported by bearings. The nip roll 28 is opened and closed by the stroke of the pressurizing mechanism 27, and the mold 12, the thermosetting material A13, the thermosetting material B13', and the film 11 are laminated or pinched or released. Further, the nip roll 28 may have a temperature control mechanism according to a desired process and film material.

As the film supply means 23, there are provided an unwinding roll 23a for unwinding the film from a rolled film, and one or a plurality of guide rolls 23b so as to match the transport route of the film 11, thereby providing the film 11 After being hugged by the nip roll, it is carried into the pressure unit 27a.

As the film peeling means 24, a peeling roll 24a for peeling the surface structure film 15 which is a laminate of the film 11, the thermosetting material A13, and the thermosetting material B13′ from the mold 12, and the peeled surface structure film. A winding roll 25a for winding the roll 15 in a roll shape, and one or a plurality of guide rolls 25b are provided so as to match the conveyance path of the surface structure film 15.

The mold coating unit 30 may be one that can discharge the thermosetting material A13, which is a coating material, continuously and uniformly in the width direction. For example, an ejector including a slit die 31 as shown in FIG. It may have a structure in which a liquid feeding mechanism capable of continuously supplying a fixed amount of coating liquid is combined. Further, in order to maintain the distance between the discharge tip surface of the slit die and the mold with high accuracy, a support roll 32 may be arranged on the side opposite to the coating surface of the mold. It is preferable to provide a position adjusting mechanism capable of adjusting the position of the applicator to the left and right with high resolution.

Although only one coating unit is shown in the figure, a plurality of mold coating units may be provided. The flatness of the coated surface may decrease due to the influence of the surface structure of the mold 12. In this case, the flatness can be improved by performing the coating process a plurality of times.

Similar to the mold coating unit, the film coating unit 33 may be one that can discharge the thermosetting material B13′ as a coating material continuously and constantly in the width direction. It may have a structure in which a discharging device including a slit die 34 and a liquid feeding mechanism capable of continuously supplying a fixed amount of coating liquid are combined. Further, in order to maintain the distance between the discharge tip surface of the slit die and the mold with high accuracy, a support roll 35 may be arranged on the opposite side of the mold application. It is preferable to provide a position adjusting mechanism capable of adjusting the position of the applicator to the left and right with high resolution.

The endless belt-shaped mold 12 is an endless belt having an uneven surface structure. A flexible one is preferable because it can be held in the roll during the transportation process. Further, in order to uniformly pressurize and heat, a material having a thin and uniform thickness is preferable. The shape is preferably a surface structure having a height difference of 1 mm or less in consideration of the deformation time and the curing time of the thermosetting material to be applied. Further, since the material is heated during transportation, a material that can withstand the heating temperature is preferable.

A series of molding operations performed by the surface structure film manufacturing apparatus 10 are as follows. The mold 12 is circulated by the first heating roll 21 and the second heating roll 22 and is heated to a predetermined temperature. Then, the thermosetting material A13 is applied to the surface of the mold 12 by the mold application unit 30. Further, the thermosetting material B13' is applied to the surface of the molding film 11 unwound from the unwinding roll 23a serving as the film supply means 23 by the film application unit 33. After the application, the pressure is applied to the surface of the mold 12 in the pressing unit 27a. The pressing mechanism 27 presses the mold 12, the thermosetting material A13, the thermosetting material B13', and the film 11 in a laminated state with the pressing unit 27a. Although the thermosetting material A13 is heated and gradually hardened immediately after being applied, it is applied to the surface of the mold 12 by being pressed by the pressurizing mechanism 27 in a state where the thermosetting material A13 is not completely hardened. At the same time when the thermosetting material A13 enters into the formed surface structure, the surface of the heating roll 21 continues to receive further thermal energy, so that the curing is accelerated. On the other hand, there is a case where unevenness is generated on the coating surface of the thermosetting material A13 due to the influence of the uneven structure provided on the surface of the mold 12, but when the mold 12 and the film 11 are bonded, the film 11 side The applied thermosetting material B13′ flows so as to fill the concave portion of the application surface of the thermosetting material A13, and as a result, the mold 12, the thermosetting material A13, the thermosetting material B13′, the film 11 In the laminated body, the layers are in close contact with each other without a gap.

Then, the thermosetting materials A13 and B13' receive the heat energy from the mold 12 and accelerate the curing, so that the thermosetting materials A13 and B13' start to come into close contact with the film 11 and are not easily peeled off. In this state, the mold 12, the thermosetting materials A13 and B13′, and the laminated body 14 of the film 11 are conveyed to the second heating roll 22, and the thermosetting materials A13 and B13′ are further heated by the heat energy from the heated roll surface. To complete the curing reaction of the thermosetting material. When the curing of the thermosetting material is completed, the thermosetting materials A13 and B13' are firmly adhered to the mold 12 and the film 11. Next, it is divided into the mold 12 side and the surface structure film 15 side on which the film 11 and the thermosetting materials A13 and B13' are laminated by the peeling roll 24a as the film peeling means 24. The surface structure of the surface structure film 15 has an inverted shape of the mold surface structure. After peeling, the surface of the mold 12 is coated with the thermosetting material A13 again. On the other hand, the surface structure film 15 is wound by the winding roll 25a. The above operation is continuously performed.

With the above device configuration and operation, a surface structure containing a thermosetting material can be formed on the surface of the film 11. By applying the thermosetting material to both the base film 11 and the preheated mold 12, the uneven shape of the surface structure of the mold 12 is cured to some extent by heating and has an appropriate elastic modulus. By the combination of the thermosetting material A13 and the thermosetting material B13′ having a lower degree of curing and higher fluidity than the thermosetting material A13, the resin enters the concave portion of the surface structure of the mold 12 at the time of pressurization ( It is possible to obtain a fine surface structure with high accuracy by satisfying both the high filling property) and the shape (high flatness) as a film on the mold surface. Here, the high resin filling property means that the resin flows to the gap of the structure formed on the mold surface by nipping at a pressure sufficiently higher than the elastic modulus of the thermosetting material A13. .. Further, high flatness means that at the time of pressurization, the inflow into the resin in the end portion in the width direction of the nip and the conveyance direction is suppressed, and a uniform thickness is obtained in both the width direction and the conveyance direction.

Further, by applying an endless belt-shaped mold, the distance between the heating rolls can be made sufficiently long, and in some cases, a heating device can be added between the rolls to secure a sufficient resin curing time. As a result, it becomes possible to increase the speed and expand the range of application of thermosetting materials. The endless belt-shaped mold can be managed so that the mold is replaced when it deteriorates or when defects occur, and it is not a disposable one like a roll film-shaped mold, so the cost of molding can be kept low. ..

Next, the configuration of each unit will be described in detail with reference to FIG.

The first heating roll 21 constituting the mold conveying means 20 receives a load at the time of nip, so that strength and processing accuracy are required, and the first heating roll 21 further includes a heating means. Examples of the material include steel, fiber reinforced resin, ceramics, aluminum alloy and the like. Further, as a heating means, a cartridge heater or an induction heating device having a hollow interior may be installed, or a flow path may be processed inside to heat a heat medium such as oil, water or steam to heat the inside of the roll. It may have a structure. Further, an infrared heater or an induction heating device may be installed near the outer surface of the roll to heat the outer surface of the roll.

The processing accuracy of the first heating roll 21 is preferably 0.03 mm or less in the cylindricity tolerance and 0.03 mm or less in the circumferential runout tolerance defined in JIS B 0621 (revised year 1984). If these values are too large, a partial gap is created between the first heating roll 21 and the nip roll 28 during the pressing, so that the laminated body 14 cannot be pressed uniformly and the surface structure to be transferred has a shape. May cause variations. The surface roughness of the roll is preferably 0.2 μm or less in terms of arithmetic average roughness Ra defined by JIS B 0601 (revised year 2001). This is because when Ra exceeds 0.2 μm, the shape of the first heating roll 21 may be transferred to the back surface of the mold 12 and may be further transferred to the surface structure of the film 11.

The surface of the first heating roll 21 is preferably subjected to treatment for forming a high hardness coating such as hard chrome plating, ceramic spraying, diamond-like carbon coating. Since the first heating roll 21 is constantly in contact with the mold 12 and is pressed by the nip roll 28 via the laminated body 14, the surface thereof is very easily worn and the surface of the first heating roll 21 is easily damaged. This is because when the sheet is worn or scratched, problems such as variations in the shape of the surface structure and transfer of the shape of the roll surface may occur as described above.

On the other hand, the second heating roll 22 also includes heating means. The material and heating means are the same as those of the first heating roll. The processing accuracy of the second heating roll 22 is preferably 0.05 mm or less in the cylindricity tolerance defined by JIS B 0621 (Revision year 1984) and 0.05 mm or less in the circumferential runout tolerance. If these values are too large, the conveyance accuracy may be lowered, and tension unevenness in the width direction or excessive meandering may occur in the laminate 14 or the mold 12. As with the first heating roll, the surface roughness of the second heating roll 22 is preferably 0.2 μm or less in terms of arithmetic average roughness Ra defined by JIS B 0601 (revised year 2001). If Ra exceeds 0.2 μm, heat conduction to the mold may be insufficient. As for the material, similarly to the first heating roll 21, it is preferable to perform a forming treatment of a high hardness film such as hard chrome plating, ceramic spraying, diamond-like carbon coating, or the like. This is to prevent scratches and abrasion due to contact with the mold.

The end of each roll is rotatably supported by a rolling bearing or the like. The first heating roll 21 is connected to a driving means such as a motor (not shown) and is rotatable while controlling the speed. The second heating roll 22 is preferably rotated by the driving force of the first heating roll 21 through the mold 12. It is also possible to increase the productivity while conveying at a speed preferably in the range of 1 to 30 m/min while transferring the surface structure with high accuracy.

Further, it is preferable to provide a mold meandering correction mechanism in order to stably convey the mold 12. As shown in FIG. 1, a preferable form of the mold meandering suppression mechanism is an end detection sensor 36 that detects the position of the end of the mold 12 in the transport path of the mold 12, and a second detection sensor 36 based on the detected value. The controller 37 is provided for adjusting the transfer position of the mold 12 by controlling the movement of the heating roll 22.

It is preferable that the moving means of the second heating roll 22 be capable of adjusting the angle of the second heating roll 22 with respect to the conveying direction of the mold 12. A structure is preferable in which the angle of the second heating roll with respect to the mold conveying direction is adjusted based on the value from the edge detection sensor 36 so that the tension decreases in the desired direction. By providing the above-described meandering suppressing mechanism for the mold 12, it is possible to suppress meandering of the mold 12 due to thermal deformation, and to realize stable conveyance and molding operation of the mold 12. In addition, the second heating roll 22 preferably presses the non-surface structure surface of the mold 12 with a constant load by a pressing means such as an air cylinder. The above-mentioned structure is effective for maintaining a constant tension because the dimensional change of the mold is caused by the temperature change.

In addition, after the thermosetting material A13 is applied in the mold conveying process, it may be heated by another heating unit until it is pressed to accelerate the hardening of the thermosetting material A13. FIG. 2 shows an example of an apparatus to which a heating unit is added, and is a schematic view of a surface structure film manufacturing apparatus 40 as seen from a cross section. By setting the heating unit 41 at the position immediately after application, the thermosetting material A13 immediately after application is started to be cured, and in a state of being cured to some extent, the pressure mechanism 27 presses the film 11 in a laminated state. .. It is possible to suppress the widthwise end portion of the material from spreading during pressing and make the thickness of the thermosetting material film after pressing uniform in the width direction. The heating unit 41 may be any as long as it can heat the thermosetting material A13, and the heating unit 41 such as an infrared heater is installed separately from the heating unit 41, or the heating roll is brought into contact with a heating roll from the non-application side of the mold 12. It may be configured to heat by conduction.

In addition, a flattening unit may be provided to flatten the application surface of the thermosetting material A between the application of the thermosetting material A13 and the pressurization in the mold conveying process. FIG. 3 shows an example of an apparatus in which a flattening means 46 is added, and is a schematic view of a surface structure film manufacturing apparatus 45 as seen from a cross section. The flattening means 46 is a structure for flattening a coated surface having irregularities, and is preferably a structure having an edge that contacts the coated surface. Furthermore, it is preferable to have a mechanism or structure that allows the edge portion to come into contact with the coating surface while maintaining a uniform pressure in the width direction of the mold 12 or a uniform distance from the surface of the mold 12.

In addition, a pressing mechanism may be provided to bring the film 11 into close contact with the thermosetting material while heating after heating the thermosetting materials A13 and B13' in the mold conveying process. FIG. 4 shows an example of an apparatus to which a pressing mechanism is added, and is a schematic view of a surface structure film manufacturing apparatus 50 as seen from a cross section. The pressing mechanism 51 is an example of a mechanism that presses the laminated body 14 pressed by the pressing mechanism 27 on the surface of the first heating roll 21 by the endless belt 54. The endless belt 54 is suspended by the rolls 52 and 53, and follows the conveyance of the laminated body 14, and the endless belt 54 circulates due to friction with the film 11. The rolls 52 and 53 are rotatably held. The endless belt 54 is preferably heated, and the rolls 52 and 53 are also preferably provided with a temperature control mechanism. The material of the endless belt 54 is preferably resin so as not to scratch the film 11, but may be a metal belt such as stainless steel. With the above configuration, the laminated body 14 after being pressed is pressed against the thermosetting materials A13 and B13′ while the film 11 is being heated, thereby promoting the curing of the thermosetting materials A13 and B13′. The filling of the thermosetting material A13 into the surface structure of the mold 12 and the close contact between the film 11 and the thermosetting material B13' can be promoted.

In addition, a heating roll may be added to the mold conveying means in order to accelerate the curing of the thermosetting materials A13 and B13' after pressing during the mold conveying process. FIG. 5 shows an example of an apparatus in which three or more heating rolls are added to the mold conveying means, and is a schematic view of a cross-section of the surface structure film manufacturing apparatus 60. The heating rolls 66a, 66b, 66c, and 66d are provided as a conveyance means, and the pressing mechanism 51 for pressing the first heating roll 21 and the laminated body 14 is further provided as in FIG. With the configuration in which the heating rolls 66a to 66d and the pressing mechanism 51 are added, it is possible to promote the curing while maintaining the close contact between the film 11 and the thermosetting material B13', and therefore, as shown in FIGS. It is effective for materials whose curing is insufficient by the mold conveying means illustrated in FIG.

Here, the pressurizing mechanism 27 will be described with reference to FIG. The pressurizing mechanism 27 is composed of a nip roll 28 and a mechanism for pressing the nip roll 28 against the first heating roll 21 arranged in parallel with and facing the nip roll 28. The nip roll 28 has a structure in which the outer surface of the core layer is covered with an elastic body. The core layer is required to have strength and processing accuracy, and for example, steel, fiber reinforced resin, ceramics, aluminum alloy or the like is applied. The elastic body is a layer that is deformed by a pressing force, and a resin layer typified by rubber or an elastomer material is preferably applied. The core layer is rotatably supported by bearings at both ends thereof, and the bearings are connected to pressing means 29 such as a cylinder. The nip roll 28 is opened and closed by the stroke of the pressing means 29 to pinch or release the laminated body 14.

Further, the nip roll 28 may have a temperature control mechanism according to a desired process and film material. As the temperature control mechanism, the inside of the roll can be heated by making the inside of the roll hollow and embedding a cartridge heater or an induction heating device, or by processing a flow path inside to flow a heat medium such as oil, water, or steam. It may have a structure. Further, an infrared heater may be installed near the outer surface of the roll to heat from the outer surface of the roll.

The processing accuracy of the nip roll 28 is preferably 0.03 mm or less in the cylindricity tolerance defined by JIS B 0621 (revised year 1984) and 0.03 mm or less in the circumferential runout tolerance. If these values are too large, a partial gap is created between the first heating roll 21 and the nip roll 28 during the pressing, so that the laminated body 14 cannot be pressed with a uniform force in the width direction. In some cases, the laminate 14 cannot be pressed uniformly, which causes variations in the shape of the transferred surface structure. The surface roughness of the elastic body is preferably one having an arithmetic mean roughness Ra of 1.6 μm or less, which is defined by JIS B 0601 (Revision year 2001). This is because when Ra exceeds 1.6 μm, the surface shape of the elastic body may be transferred to the back surface of the film 11 when pressed.

The heat resistance of the elastic body of the nip roll 28 preferably has a heat resistant temperature of 160° C. or higher, and more preferably has a heat resistant temperature of 180° C. or higher. Here, the heat resistant temperature is determined by the temperature at which the rate of change in tensile strength when left at that temperature for 24 hours exceeds 10%.

As the material of the elastic body, for example, when rubber is used, silicone rubber, EPDM (ethylene propylene diene rubber), neoprene, CSM (chlorosulfonated polyethylene rubber), urethane rubber, NBR (nitrile rubber), ebonite, etc. Can be used. When a higher elastic modulus and hardness are required, a hard pressure-resistant resin having improved toughness (eg, polyester resin) can be used. The rubber hardness of the elastic body is preferably in the range of 70 to 97° according to the ASTM D2240:2005 (Shore D) standard. If the hardness is less than 70°, the amount of deformation of the elastic body becomes large and the pressure contact width with the film 11 becomes too large, so that the pressure necessary for forming the structure may not be secured, and the hardness Is more than 97°, on the contrary, the amount of deformation of the layer becomes small, and the pressure contact width becomes too small, so that the pressing time necessary for transferring the surface structure may not be secured in some cases.

The driving means of the nip roll 28 is connected to the end portion of the first heating roll 21 by a chain or a belt so that it can rotate in conjunction with the first heating roll 21, or it can be connected to the first heating roll 21. It is preferable to rotate independently by using a motor or the like that can synchronize speeds, but it may have a rotatable structure so that it is rotated by friction with the film 11.

The film supply means 23 is composed of an unwinding roll 23a and one or a plurality of guide rolls 23b installed so as to match the transport path of the film 11. The guide roll 23b includes a tension detecting mechanism. It is preferable to control the rotation torque of the guide roll 23a so that the tension is constant. The film 11 is conveyed to the pressure unit 27a after being held by the nip roll 28, but a wrinkle-rolling roll may be installed immediately before the film is held.

The film peeling means 24 is composed of a winding roll 25a for peeling the surface structure film 15 from the mold 12 by a peeling roll 24a, and then winding the roll in a roll shape, and one or a plurality of guide rolls 25b. It is preferable that the guide roll 25b is provided with a tension detecting mechanism to control the rotation torque of the winding roll 25a so that the tension is constant. Further, the surface structure film 15 does not necessarily have to be wound into a roll shape, and may be provided with a mechanism for gripping the widthwise end portion and cutting into a sheet shape during the conveying process and collecting into a sheet shape. Further, a cooling mechanism may be provided on the inner surface of the peeling roll 24a. The heated surface structure film 15 may be cooled before being wound. In addition, a cooling device such as an air blower may be provided to cool the surface structure film 15 during the transportation process from the peeling roll to before winding. By cooling to room temperature before winding, it is possible to suppress wrinkles, poor planarity, and the like that may occur due to temperature changes in the surface structure film 15 after winding.

The mold coating unit 30 includes a slit die 31 and a coating material supply mechanism connected to the slit die 31 on the upstream side of the pressing unit 27a in the process of conveying the mold 12. The slit die 31 faces the surface of the mold 12 on which the surface structure is formed so that the thermosetting material A13 can be applied. In order to form a uniform coating film, it is preferable that the gap between the slit die 31 and the mold 12 is maintained with high precision and evenly, and as shown in the figure, the support roll 32 is opposite to the surface on which the surface structure is formed. It is preferable to arrange so as to support the mold from the side surface. Further, it is preferable that the support roll 32 be provided with a temperature adjusting mechanism inside so that the mold temperature can be controlled to a predetermined temperature when the mold is brought into contact with the mold. Here, with respect to the distance between the slit die 31 and the mold 12, it is preferable that the distance between the ejection surface of the slit die 31 and the surface of the mold 12 can be controlled at an interval of 10 μm to 500 μm. The accuracy of the widthwise spacing is preferably 10 μm or less, more preferably 3 μm or less. Further, in order to realize the accuracy in the present invention, the straightness and rotational runout of the support roll 32 are preferably 5 μm or less, and more preferably 1 μm or less. Although the coating method using the slit die is illustrated here, another coating method may be used.

The film coating unit 33 includes an applicator and a coating material supply mechanism connected to the applicator on the upstream side of the pressurizing unit 27a in the process of transporting the film 11, and the film applicator serves as the above-mentioned mold applicator. A slit die or the like may be used as in the coating unit. In this case, it is preferable that the gap between the slit die 34 and the film 11 is maintained with high accuracy and uniformly in the width direction, and it is preferable to dispose the support roll 35 as shown in the drawing. Here, with respect to the distance between the slit die 34 and the film 11, it is preferable that the distance between the discharge surface of the slit die 34 and the surface of the film 11 can be controlled at an interval of 10 μm to 500 μm. The accuracy of the widthwise spacing is preferably 10 μm or less, more preferably 3 μm or less. Further, in order to realize the accuracy in the present invention, the straightness and the rotational runout of the support roll 35 are preferably 5 μm or less, and more preferably 1 μm or less. Although the coating method using the slit die is illustrated here, another coating method may be used.

A transfer unit and a coating unit for molding thermosetting material may be further added so that a layer of thermosetting material can be formed on both surfaces of the film 11. FIG. 6 shows an example of an apparatus for forming a layer containing a thermosetting material on both sides, and is a schematic view of a cross-section of an apparatus 70 for manufacturing a surface structure film. The second mold carrying means 71 constituting the transfer unit is provided in parallel with the mold carrying means 20. The surface structure of the second mold 80 constituting the second mold conveying means 71 may or may not be provided on the surface. In the absence of surface structures, a flat surface of thermosetting material is obtained. The second mold conveying means 71 arranges the heating rolls 72 and 73 so that the second mold 80 comes into contact with the film 11 in the vicinity where the mold 12 is separated from the first heating roll 21. The second mold 80 is suspended. The slit die 74 constituting the second mold coating unit is provided on the upstream side of the film transfer point 77 in the mold transfer step in the transfer process of the second mold. Further, the heating unit 75 is provided between the slit die 74 and the film contact point 77. In addition, after passing through the first heating roll 21, the heating rolls 78 and 79 may be squeezed multiple times to promote curing of the thermosetting material and adhesion of the film 11 and the thermosetting material. You can The heating roll 73 is provided at a position opposed to the second heating roll 22 with the film to be conveyed interposed therebetween. The surface structure film 81 is peeled off from the mold 12 by the heating roll 72 and wound on the winding roll. Since the surface structure film 81 has layers of thermosetting material formed on both sides thereof, it is possible to suppress warp deformation of the film due to shrinkage of the thermosetting material and improve flatness.

The endless belt-shaped mold 12 is an endless belt having a surface structure processed. The material may be a metal such as nickel, steel, stainless steel, or copper in consideration of high strength and thermal conductivity, but a resin is preferable in consideration of releasability from the thermosetting material. In the case of resin, a thermoplastic material having a surface energy of 25 mN/m or less is preferable so that higher peelability can be obtained. As the material, a polyolefin-based material is preferably exemplified. It may be laminated with a biaxially stretched polyethylene terephthalate film (PET) in order to enhance the flatness as a mold.

As a method of producing the mold 12 having a surface structure, a method of pressing a die against the surface of the thermoplastic resin film to form a shape may be applied. In the method of molding the shape by pressing the mold on the surface of the thermoplastic resin film, the thermoplastic resin film is pressed against the mold in a heated state, and the structure of the reverse of the structure formed on the surface of the mold is thermoplastic. It is formed on the surface of the resin film. For example, it can be manufactured by a process through a mold manufacturing apparatus as shown in FIG. FIG. 7 is a cross-sectional view showing an example of an apparatus for manufacturing the mold 12 using the endless belt-shaped mold 101.

In the example shown in FIG. 7, the film 102 is drawn out from the unwinding roll 110, and is supplied to the surface of the endless belt-shaped mold 101 having a heated surface structure by the heating roll 120. The surface structure of the mold 101 is formed to have substantially the same shape as the surface structure of the surface structure film 15 to be finally obtained. The mold 101 is heated by the heating roll 120 immediately before coming into contact with the film. The surface structure of the mold 101 is pressed against the continuously supplied film 102 by the nip roll 121, and a structure in which the surface structure of the mold 101 is reversed is formed on the film 102.

After that, the film 102 is conveyed to the outer surface position of the cooling roll 130 while being in close contact with the mold 101. The film 102 is cooled by heat conduction through the mold 101 by the cooling roll 130, and then peeled from the mold 101 by the peeling roll 140, and the film is wound up by the winding roll 150. By such a process, a roll film-shaped mold is obtained. The mold 12 shown in FIG. 1 is cut into an appropriate length according to the device to which it is applied, and is processed into an endless belt by fixing the ends from the inner surface side with tape.

As a processing method applied to the surface of the mold 101, a method of directly cutting or laser processing the surface of the metal belt, a method of directly cutting or laser processing the plating film formed on the surface of the metal belt, Examples thereof include a method of subjecting a cylindrical original plate having a structure on the inner surface to electroforming, and a method of continuously laminating a thin plate having a finely structured surface on the surface of a metal belt. Further, a method of butting and welding ends of metal plates having a predetermined thickness and length may be mentioned.

Further, as the surface structure of the mold 12, it is suitable that the concave shapes are discretely arranged. This is because it is possible to receive pressure on the flat surface of the mold at the time of pressurization, so that the pressure is concentrated on the tip of the shape and is unlikely to cause deformation at the tip. As the recessed shape, a cylindrical recess having a diameter of 10 nm to 1 mm and a height of 10 nm to 0.5 mm is preferably arranged at a pitch of 100 nm to 1 mm, more preferably a height of 1 μm to 500 μm. However, the shape is not limited to this, and may be a conical or pyramidal recess. Further, for example, a plurality of grooves may be arranged in stripes, or convex shapes may be discretely arranged.

The second mold 80 used when forming the thermosetting material on both surfaces shown in FIG. 6 may have the same configuration, material, and manufacturing method as the mold 12. It may be flat without a surface structure.

Next, a method for producing the surface structure film of the present invention will be described. The method for producing a surface structure film according to the present invention is a mold transfer in which an endless belt-shaped mold having a surface structure formed thereon is held by at least two heated heating rolls so that the mold is circulated while being heated. Part, the step of applying the thermosetting material A to the surface of the mold, the step of applying the thermosetting material B to the surface of the film, the mold and the film, the thermosetting material A and the thermosetting material. A step of adhering so that the material B is in contact, a step of pressing the film, the thermosetting material A, the thermosetting material B, and the mold with a nip roll in a laminated state, the film after pressing, A step of transporting the thermosetting material A, the thermosetting material B, and the mold while heating them in a laminated state, and comprising the film, the thermosetting material A, and the thermosetting material B. A surface structure film is manufactured by including at least a step of peeling the surface structure film from the mold.

Next, the manufacturing method will be described with reference to FIGS.

As a preparatory step, the film 11 is pulled out from the unwinding roll 23a, placed along the mold 12, passed through the peeling roll 24a, and then wound up by the winding roll 25a.

Subsequently, while the film 11 is being conveyed by the driving means, the first heating roll 21 and the second heating roll 22 are operated, and the temperature is controlled until the surface temperature of both heating rolls reaches a predetermined temperature. The condition of the surface temperature of both heating rolls depends on the materials of the thermosetting materials A13 and B13′ to be applied, the heat resistance of the film 11, the shape of the surface structure of the mold 12, the aspect ratio, etc., but is usually 80° C. to 200° C. Set between °C. When the mold is resin, the surface temperature of the heating roll is preferably 20° C. or more lower than the glass transition temperature of the resin forming the mold. This is because the shape of the surface structure of the mold can be suppressed from being deformed. Further, as shown in FIG. 2, a heating unit 41 may be installed between the mold coating unit 30 and the pressurizing section 27a to heat the mold. At this time, the set temperature of the heating unit 41 is preferably set so that the thermosetting material A13 is in an appropriate cured state in the pressurizing section 27a. By setting an appropriate cured state, it is possible to suppress the widthwise end portion of the material from spreading at the time of pressing, and to make the thickness of the thermosetting material film after pressing uniform in the width direction.

When the surface temperatures of the first heating roll 21 and the second heating roll 22 reach the set values, the film 11 is conveyed at the molding speed, and at the same time, the mold coating unit 30 and the film coating unit 33 are operated to move the mold. At the same time when the application of the thermosetting material A13 to 12 and the application of the thermosetting material B13′ to the film 11 are started, the nip roll 28 is closed, and the film 11 and the mold 12 are applied by the first heating roll 21 and the nip roll 28. By pressing, an inverted shape of the surface structure of the mold 12 is formed in the thermosetting material A13. Further, when the thermosetting material A13 and the thermosetting material B13′ are brought into contact with each other and pressed, the unevenness of the coating surface of the thermosetting material A13 generated by the influence of the surface structure of the mold is thermally cured. The conductive material B13' is filled. The conditions at this time depend on the mechanical properties of the thermosetting materials A and B to be applied, the shape of the surface structure of the mold 12, the aspect ratio, etc., but the film forming speed is 1 to 30 m/min, and the nip pressure is It is preferable to set in the range of 10 MPa or more and 100 MPa or less. Further, as shown in FIG. 3, a flattening means 46 is installed between the mold coating unit 30 and the pressing portion 27a to flatten the coated surface immediately after the thermosetting material A is coated. You may stay. Complete flattening is difficult, but by reducing the size of the unevenness on the coated surface, the subsequent thermosetting material B13' is likely to fill the uneven surface.

The thermosetting materials A and B to be applied may be either inorganic materials or organic materials, but considering the heat resistance of the film 11, an organic material having a relatively low curing temperature is suitable. For example, phenol resin, urea resin (urea resin), melamine resin, epoxy resin, unsaturated polyester, silicone resin, polyurethane and the like are preferably used. Further, a two-component curing type silicone rubber, which can be widely selected in viscosity at the time of application and hardness at the time of curing, is preferably used.

When the nip pressure is less than 10 MPa, when the fine structure is transferred, the resin may not be sufficiently deformed and molding may be defective. Further, if it exceeds 100 MPa, the shape of the mold may be deformed, and the size of the device may be large due to the strength design, which may cause a problem of cost.

The thermosetting material A13 is heated by heat conduction from the mold 12, and is pressed by the first heating roll 21 and the nip roll 28 to be filled in the surface structure of the mold 12. Then, the laminated body 14 in which the film 11, the thermosetting material, and the mold 12 that have passed through the pressing unit 27a are laminated is conveyed to the second heating roll 22 while maintaining the temperature substantially. Here again, the mold 12 is further heated, and the thermosetting materials A13 and B13' are also heated by heat conduction from the mold 12, and the curing progresses. Then, the film is peeled off by a peeling roll 24a which is a film peeling means. Further, as shown in FIG. 4, the laminated body 14 may be pressed from the film 11 side using the endless belt 54 on the surface of the first heating roll 21. It is possible to promote the curing of the thermosetting materials A13 and B13' and the close contact with the film 11.

Next, on the surface of the second heating roll 22, the surface structure film 15 in which the film 11 and the thermosetting materials A13 and B13' are adhered and laminated on the surface of the second heating roll 22 is peeled from the mold 12 by the peeling roll 24a. The peeled surface structure film 15 is wound by the winding roll 25a.

Further, as shown in FIG. 6, a transfer unit and a thermosetting material mold coating unit may be further added to transfer a layer of the thermosetting material to both surfaces of the film 11. The material and thickness of the thermosetting material to be applied are preferably set to be equal to those of the thermosetting material A13 formed on the opposite surface. Further, the set temperatures of the heating rolls 72 and 73 and other heating rolls to be added are also preferably set to be equal to the heating setting on the side of the thermosetting material A13. This is because in the surface structure film 81, the amount of heat shrinkage on both sides of the film is made equal to suppress the warpage of the film and improve the flatness.

The film 11 preferably has strength and heat resistance so as not to be deformed even during transportation or curing shrinkage of the thermosetting material, and specifically, preferably polyethylene terephthalate, polyethylene-2,6-naphthalate, polypropylene terephthalate. Polyester resin such as polybutylene terephthalate, polyolefin resin such as polyethylene, polystyrene, polypropylene, polyisobutylene, polybutene and polymethylpentene, polyamide resin, polyimide resin, polyether resin, polyesteramide resin, polyether Some are made of ester resin, acrylic resin, polyurethane resin, polycarbonate resin, polyvinyl chloride resin, or the like.

An example of the form of the manufactured surface structure film is shown in FIG. FIG. 8 is a perspective view in which a region of the surface structure film 15 is cut out. In the surface structure film 15, the pattern layer 13a containing a thermosetting material is coated on the surface of the film 11, and the structure is formed on the surface layer. As a preferable structure to which the manufacturing method of the present invention is suitably applied, protrusions having a pillar shape or a cone shape, a cone shape, a pyramid shape in a discrete manner, a stripe shape, or a recess shape is discretely arranged. However, the present invention is not limited thereto. The pattern pitch is preferably 100 nm to 1 mm and the height is preferably 100 nm to 500 μm.

[Example 1]
As the film 11, a 100 μm thick film (trade name “Lumirror” (registered trademark), S10, manufactured by Toray Industries, Inc.) made of biaxially stretched polyethylene terephthalate was used. The width was 300 mm.

A film (Opulan, manufactured by Mitsui Chemicals, Inc.) having a thickness of 100 μm, a length of 3 m, and a width of 320 mm made of methylpentene polymer is applied to the mold 12, and the surface of the thermoplastic resin film shown in FIG. 7 is used to form the surface structure. An apparatus was used to press the mold onto the and mold the shape. The surface structure is a striped pattern having a cross section of an isosceles triangle, which is a wavy shape in which the height of the isosceles triangle is 12.5 μm, the apex angle is 90 degrees, and the pitch is 25 μm.

As the thermosetting materials A13 and B13′, a two-component curing type silicone rubber (trade name 7-6830, manufactured by Toray Dow Corning Co., Ltd.) was used, and two components were mixed, stirred and defoamed. ..

The apparatus shown in FIG. 1 is used as an apparatus for producing a surface structure film. The first and second heating rolls 21 and 22 have a cylindrical heater made of carbon steel and a cartridge heater incorporated therein, and a hard chrome plating on the surface. What was done was used. The outer diameter of the central portion supporting the mold 12 was 400 mm, and the length in the width direction was 340 mm. The surface temperature of the first heating roll 21 was heated to 120°C, and the surface temperature of the second heating roll 22 was heated to 160°C.

A thermosetting material A13 was applied to the surface of the mold 12 using a slit die 31 having a discharge width of 290 mm and a slit width of 100 μm so that the applied thickness would be 10 μm when applied on a flat surface.

The thermosetting material B13' was applied to the surface of the film 11 using a slit die 34 having a discharge width of 290 mm and a slit width of 200 μm so as to have a thickness of 20 μm.

The peeling roll 24a, which is a film peeling means, has an outer diameter of 400 mm and a widthwise length of 340 mm, and has a structure in which cooling water can flow inside a hollow core material made of carbon steel. The temperature of the cooling water was 30°C.

The film 11 was supplied to the mold 12 from the film wound in a roll shape, and the unwinding tension was set to 30N.

The film of the surface structure film 15 was peeled from the mold 12 with a winding tension of 30 N and wound as a film roll.

The mold 12 was circulated at a speed of 2 m/min. The mold 12 held the first and second heating rolls so that a tension of 30 N was applied.

The nip roll 28 has an outer diameter of 160 mm and a cylindrical core made of carbon steel, and a polyester resin (hardness: Shore D80°) as an elastic body is coated on the surface so that the pressing width is 290 mm. I was there. A pressing force of 100 kN was applied to the nip roll 28 by using a hydraulic cylinder as the pressing means. At this time, the contact width B between the nip roll 28 and the film 11 was confirmed using a pressure measurement film (Prescale, manufactured by Fuji Film Co., Ltd.), and the total width was 6 mm, and the pressure applied to the molding film was about It was 50 MPa, which was uniform in the width direction.

As a result of continuously performing the molding operation, the thermosetting material B13′ on the film 11 is bonded to the thermosetting material A13 on the mold 12, and the thermosetting material A13 on the mold 12 is provided with the surface shape of the mold 12. It was possible to transfer almost 100%. FIG. 9 shows the result of observing the surface of the surface structure film with a scanning electron microscope.

[Example 2]
The same films and molds as those described in Example 1 were used.

As the thermosetting materials A13 and B13′, a two-part curable silicone rubber (trade name RBL-9101-05, manufactured by Toray Dow Corning Co., Ltd.) was used, and the two parts were mixed, stirred, and defoamed. Using.

The apparatus shown in FIG. 3 is used as an apparatus for producing a surface structure film. The first and second heating rolls 21 and 22 have a cylindrical heater made of carbon steel and a cartridge heater incorporated therein, and hard chromium plating is applied to the surface thereof. What was done was used. The outer diameter of the central portion supporting the mold 12 was 400 mm, and the length in the width direction was 340 mm. The surface temperature of the first heating roll 21 was heated to 70° C., and the surface temperature of the second heating roll 22 was heated to 150° C.

The slit die 31 has a discharge width of 290 mm and a slit width of 100 μm, and the thermosetting material A13 was applied so that the application thickness was 25 μm when applied on a flat surface. The thermosetting material B13' was applied to the surface of the film 11 using a slit die 34 having a discharge width of 290 mm and a slit width of 200 μm so as to have a thickness of 10 μm.

A scraping blade made of stainless steel and having a scraping width of 320 mm was used as the flattening means 46, and held so that the shortest distance between the surface of the mold 12 and the scraping blade was 20 μm.

The excess liquid scraped by the scraping blade was collected by a suction nozzle having a suction width of 320 mm and a slit width of 200 μm, which was arranged above the scraping blade and connected to a vacuum pump. The suction pressure of the suction nozzle was set to -10 kPa by the pressure regulator.

The peeling roll 24a, which is a film peeling means, has an outer diameter of 400 mm and a widthwise length of 340 mm, and has a structure that allows cooling water to flow inside a hollow core material made of carbon steel. The temperature of the cooling water was 30°C.

The film 11 was supplied to the mold 12 from the film wound in a roll shape, and the unwinding tension was set to 30N.

The film of the surface structure film 15 was peeled from the mold 12 with a winding tension of 30 N and wound as a film roll.

The mold 12 was circulated at a speed of 2 m/min. The mold 12 held the first and second heating rolls so that a tension of 30 N was applied.

As the nip roll 28, a cylindrical core material made of carbon steel having an outer diameter of 160 mm and a polyester resin (hardness: Shore D80°) as an elastic body having a pressure width of 290 mm was coated on the surface. A pressing force of 100 kN was applied to the nip roll 28 by using a hydraulic cylinder as the pressing means.

As a result of continuously performing the molding operation, the thermosetting material B13′ on the film 11 is bonded to the thermosetting material A13 on the mold 12, and the thermosetting material A13 on the mold 12 is provided with the surface shape of the mold 12. It was possible to transfer almost 100%.

10: Manufacturing apparatus for surface structure film of the present invention 11: Film 12: Mold 13: Thermosetting material A
13': Thermosetting material B
13a: pattern layer 14: laminated body 15: surface structure film 20: mold conveying means 21: first heating roll 22: second heating roll 23: film supply means 23a: unwinding roll 23b: guide roll 24: film peeling Means 24a: Peeling roll 25a: Winding roll 25b: Guide roll 27: Pressing mechanism 27a: Pressing unit 28: Nip roll 29: Pressing means 30: Mold coating unit 31: Slit die 32: Support roll 33: Film coating Unit 34: Slit die 35: Support roll 36: Edge detection sensor 37: Controller 40: Manufacturing device for surface structure film of the present invention 41: Heating unit 45: Manufacturing device for surface structure film of the present invention 46: Flattening means 50 : Surface structure film production apparatus 51 of the present invention: Pressing mechanism 52, 53: Roll 54: Endless belt 60: Surface structure film production apparatus 66a to 66d of the present invention: Heating roll 70: Surface structure film production of the present invention Device 71: Second mold conveying means 72, 73: Heating roll 74: Slit die 75: Heating unit 77: Film contact points 78, 79: Heating roll 80: Mold 81: Surface structure film 100: Surface structure film of the present invention Mold manufacturing apparatus applied to the manufacturing apparatus 101: Mold 102: Film 110: Unwinding roll 120: Heating roll 121: Nip roll 130: Cooling roll 140: Peeling roll 150: Winding roll

Claims (14)

A manufacturing apparatus for manufacturing a surface structure film having a surface structure containing a thermosetting material on the surface of a film,
(1) An endless belt-shaped mold having a surface structure formed thereon,
(2) Mold conveying means for conveying the mold held by two or more heating rolls by rotating the heating rolls,
(3) A pressure mechanism including at least a nip roll arranged in parallel with the first heating roll of the mold conveying means and having a surface covered with an elastic body, and a pressing means using the heating roll and the nip roll. When,
(4) A mold coating unit installed on the upstream side of the pressing mechanism in the transport direction of the mold and configured to coat a surface of the mold on which the surface structure is formed with a material.
(5) film supply means for supplying a film to the surface of the mold,
(6) A film coating unit, which is arranged on the upstream side of the pressing mechanism in the film transport direction, for coating a material on a surface of the film that contacts the mold,
(7) Film peeling means for peeling the film on the surface of the mold,
An apparatus for producing a surface structure film, which comprises at least: The surface structure film manufacturing apparatus according to claim 1, further comprising: a heating unit configured to heat the mold between the mold coating unit and the first heating roll. The surface structure film according to claim 1 or 2, further comprising: a flattening unit for flattening the material applied to the mold surface, between the mold coating unit and the pressure mechanism. Manufacturing equipment. 4. The apparatus for manufacturing a surface structure film according to claim 1, further comprising a pressing mechanism that can press the first heating roll on the outer peripheral surface of the first heating roll. The surface structure film manufacturing apparatus according to claim 1, wherein the endless belt-shaped mold is made of resin. The surface according to any one of claims 1 to 5, further comprising a transfer unit for transferring a layer of a thermosetting material to the surface of the film opposite to the surface having the surface structure. Structural film manufacturing equipment. A method of making a surface structured film comprising a thermosetting material, the method comprising:
(1) The endless belt-shaped mold having the surface structure formed thereon is held by at least two or more heated heating rolls. A step of applying the thermosetting material A,
(2) A step of applying the thermosetting material B on the surface of the film,
(3) bonding the mold and the film so that the thermosetting material A and the thermosetting material B are in contact with each other,
(4) A step of pressing the film, the thermosetting material A, the thermosetting material B, and the mold in a laminated state by a nip roll,
(5) A step of transporting the film, the thermosetting material A, the thermosetting material B, and the mold after being pressed in a stacked state while heating,
(6) A step of peeling the surface structure film composed of the film, the thermosetting material A, and the thermosetting material B from the mold,
A method for producing a surface structure film, comprising at least: The mold is heated after the step of applying the thermosetting material A to the surface of the mold and before the step of laminating a film from the side of the thermosetting material A. Method for manufacturing surface structure film. After the step of applying the thermosetting material A to the surface of the mold, and before the step of attaching the film from the side of the thermosetting material A, the application surface of the thermosetting material A is flattened. The method for producing a surface structure film according to claim 7 or 8. After the step of pressurizing the film, the thermosetting material A, the thermosetting material B, and the mold in a laminated state with a nip roll, the film side is held in a state in which the mold is held in the heating roll. The method for producing a surface structure film according to claim 7, wherein the heating structure is pressed against the heating roll. The method for producing a surface structure film according to claim 7, wherein the endless belt-shaped mold is made of resin. The method for producing a surface structure film according to claim 11, wherein the endless belt-shaped mold is a thermoplastic resin film produced by a method of molding a shape by pressing a mold on the surface of the thermoplastic resin film. .. The method for producing a surface structure film according to claim 11 or 12, wherein the surface temperature of the heating roll during heating is lower than the glass transition temperature of the resin constituting the mold by 20°C or more. The surface of any one of claims 7 to 13, wherein a layer of a thermosetting material is transferred to the surface of the surface structure film on the opposite side where the surface structure is formed, in the process of the circular transport of the mold. Method of manufacturing structural film.