JP6682714B1 - Method for producing highly basic aluminum chloride - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a method for producing highly basic aluminum chloride having a basicity of 75% to 95%.
A process for producing a high basic aluminum chloride of the present application, SO ₄ content (molar ratio) 0 to 0.1, the basicity of 40% to 65% of basic aluminum chloride first solution, and alkali solution The first step of reacting to produce an alumina gel, and the alumina gel obtained in the first step are treated with a basic aluminum chloride second with a SO ₄ content (molar ratio) of 0 to 0.1 and a basicity of 40% to 55%. The second step of adding and dissolving the solution at 40 ° C to 80 ° C, and adding the alkali carbonate to the solution obtained in the second step to obtain a basic aluminum chloride third solution having a basicity of 75% to 95%. A third step of aging the third solution obtained in the third step and the third step at 40 ° C. to 90 ° C. to obtain an aging solution, and adding a sulfate to the aging solution obtained in the fourth step, Adjust the SO ₄ content of the aging solution to (molar ratio) = 0 to 0.35 And a fifth step of manufacturing.
[Selection diagram] None

Description

  The present invention relates to a method for producing highly basic aluminum chloride.

  In recent years, the concentration of aluminum in drinking water has come to be regulated. According to the World Health Organization (WHO) guidelines for drinking water quality, 0.2 mg / L, the US Environmental Protection Agency Safe Drinking Water Act Type 2 Drinking Water Regulation 0.05 to 0.2 mg / L (provisional), the European Union drinking water quality standard defines a guide level of 0.05 mg / L and a maximum allowable concentration of 0.2 mg / L.

  On the other hand, also in Japan, Al is shown in the comfortable water quality item of the standard concerning tap water quality established by the Ministry of Health, Labor and Welfare, and its target value is set to 0.2 mg / L or less.

  To convert drinking water from river water, a coagulant for water purification using basic aluminum chloride is often used, and this basic aluminum chloride generally reacts hydrochloric acid with aluminum hydrate under pressure. Then, basic aluminum chloride is prepared, and sulfuric acid or a water-soluble sulfate is added thereto to produce a sulfate-containing basic aluminum chloride (PAC). The basicity is 40% to 60%.

  Further, as a manufacturing method for increasing basicity and improving aggregation performance, there is a method disclosed in Patent Document 1 (Patent 6186528). That is, this is a method in which an alkali (sodium carbonate, sodium aluminate, etc.) is added to basic aluminum chloride to form a gel, and then this gel is added to a basic aluminum chloride solution and dissolved to obtain highly basic aluminum chloride. In this case, it is shown that basic aluminum chloride having a high basicity of about 73% can be obtained. This method is hereinafter referred to as the gel method.

Japanese Patent No. 6186528

  The highly basic aluminum chloride flocculant with increased basicity and improved flocculation performance has the advantage of less variation in flocculation characteristics due to fluctuations in river water. It is possible to reduce residual Al etc. by maximizing the basicity. However, the invention of Patent Document 1 has a problem that when the basicity of basic aluminum chloride is increased, the basicity of the aluminum chloride rapidly increases when the basicity exceeds 75%. .

  In addition, recently, the water quality standards for drinking water have become more stringent, the content of organic components is as small as possible (evaluated by the value of E260), and biologically derived fine particles such as cryptosporidium and picoplankton (evaluated by the number of fine particles) Very low values are desired.

As a result of earnest efforts, the inventors of the present invention have studied the improvement of the alumina gel method. As a result, the content of SO ₄ in the aluminum chloride first solution as a raw material for the gelation of alumina and the aluminum chloride for dissolving the alumina gel have been investigated. The content of SO _{4 in} the second solution is set to 0 to 0.1 in terms of the molar ratio of SO ₄ / Al ₂ O ₃ , and alkali carbonate is added to the basic aluminum chloride solution after dissolution to complete the reaction. By increasing the basicity to 75% to 95% and performing dissolution aging of these under heating at 40 ° C. to 80 ° C., an extremely stable highly basic aluminum chloride solution in spite of high basicity can be obtained. The inventors have found that they can be obtained and completed the present invention.

  Then, by using the obtained highly basic aluminum chloride as a flocculant, the residual Al concentration in the purified water after the treatment, the number of microparticles derived from the microorganism, and the E260 value indicating the content of the organic matter were remarkably increased. I succeeded in lowering it.

  An object of the present invention is to provide a method for producing such highly basic aluminum chloride.

The present invention provides (1) a basic aluminum chloride first solution having a SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 65%, and A first step of reacting with the solution to produce an alumina gel,
(2) The alumina gel obtained in the first step is treated with basic aluminum chloride having a SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 55%. A second step of adding to the second solution at 40 ° C. to 80 ° C. and dissolving;
(3) A third step in which an alkali carbonate is added to the solution obtained in the second step to obtain a basic aluminum chloride third solution having a basicity of 75% to 95%,
(4) A fourth step of aging the third solution obtained in the third step at 40 ° C. to 90 ° C. to obtain an aging solution,
(5) A sulfate is added to the aging solution obtained in the fourth step to adjust the SO ₄ content in the aging solution to SO ₄ / Al ₂ O ₃ (molar ratio) = 0 to 0.35. The method for producing highly basic aluminum chloride is characterized by including five steps.

The basic aluminum chloride produced according to the present invention has a composition of M / Al ₂ O ₃ (molar ratio) = 0.8 to 2.2 (M represents the number of moles of alkali metal), E / Al ₂ O ₃ (molar ratio) = 0 to 0.3 (E indicates the number of moles of alkaline earth metal), Cl / Al ₂ O ₃ (molar ratio) = 1.0 to 3.0, SO ₄ / Al ₂ O ₃ (molar ratio) = 0 to 0.35, and basicity is 75% to 95% of highly basic aluminum chloride.

  The basic aluminum chloride produced according to the present invention can increase the basicity of basic aluminum chloride to 75% to 95%, is excellent in storage stability, and can be used as a flocculant after treatment. It is possible to significantly reduce the values of residual Al and E260 and the number of fine particles in the purified water.

The highly basic aluminum chloride of the present invention is
(1) A basic aluminum chloride first solution having a SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 65% is reacted with an alkaline solution. And a first step of forming an alumina gel,
(2) The alumina gel obtained in the first step is subjected to basic chlorination in which the SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) is 0 to 0.1 and the basicity is 40% to 55%. A second step of adding to the aluminum second solution at 40 ° C. to 80 ° C. and dissolving;
(3) A third step in which an alkali carbonate is added to the solution obtained in the second step to obtain a basic aluminum chloride third solution having a basicity of 75% to 95%,
(4) A fourth step of aging the third solution obtained in the third step at 40 ° C. to 90 ° C. to obtain an aging solution,
(5) A sulfate is added to the aging solution obtained in the fourth step to adjust the SO ₄ content in the aging solution to SO ₄ / Al ₂ O ₃ (molar ratio) = 0 to 0.35. It can be manufactured by going through five steps.

In the first step, a basic aluminum chloride first solution having an SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 65% is treated with an alkaline solution. Is reacted with to form an alumina gel.

  The first solution of basic aluminum chloride used in this first step is not particularly limited, but it is usually one having a basicity of 40% to 65%, and may be one produced by a known method, for example, in an autoclave. It can be produced by reacting hydrochloric acid with aluminum hydroxide.

  For example, 35% hydrochloric acid: 649 g, aluminum hydroxide (water content 2.6%): 325.3 g, water: 35.7 g are synthesized by reacting in an autoclave at 160 ° C. for 160 minutes. Is.

  Further, in the present invention, the alkaline solution of the raw material used in the first step may be an alkaline solution having a pH of 10 or more, and examples thereof include alkali metal hydroxides such as sodium hydroxide and potassium hydroxide, sodium aluminate, Examples include a solution containing an alkali metal aluminate such as potassium aluminate. Alkali metal carbonates such as sodium carbonate and potassium carbonate can also be used.

  Of these, when using alkali metal hydroxide or alkali metal carbonate alone, the sodium content will increase, and the basic aluminum chloride of the product will inevitably contain a large amount of sodium chloride. Therefore, it is preferable to use it in combination with an alkali metal aluminate.

In alkali metal aluminate salts such as sodium aluminate and potassium aluminate, the alumina content contributes to the improvement of basicity, reducing the amount of Na necessary for achieving the desired basicity and reducing the amount of residual sodium chloride due to the reaction. It is preferable because it can be reduced. Further, the alkali metal of alkali aluminate and Al ₂ O _{3 having a} molar ratio of 1.0 to 2.0 can be used.

In this basic aluminum chloride, in addition to the alkali metal, an alkaline earth metal is contained in an amount of 0 to 0.3 mol, particularly preferably 0.02 to 0.2 mol, based on 1 mol of Al ₂ O ₃ .

Further, in this basic aluminum chloride, Cl is contained in an amount of 1.0 to 3.0 mol, particularly preferably 2.0 to 3.0 mol, per 1 mol of Al ₂ O ₃ . This Cl is the sum of Cl bound to Al and Cl bound to the alkali metal. If it is less than 1.0 mol or more than 3.0 mol, the stability of the basic aluminum chloride deteriorates, which is not preferable.

Further, in this basic aluminum chloride, SO ₄ is contained in an amount of 0 to 0.35 mol with respect to 1 mol of Al ₂ O ₃ . This SO ₄ is used as an auxiliary for cohesiveness, and may be included depending on the type of water.

  As a method of adding an alkaline earth metal such as Mg in basic aluminum chloride, a method of mixing and dissolving magnesium chloride in the first solution of basic aluminum chloride in the first step, and basic aluminum chloride as a raw material in the second step A method of mixing and dissolving in the second solution as magnesium chloride or the like can be mentioned.

SO ₄ in order to incorporate the is a method of mixing and dissolving the like SO ₄ Compound basic aluminum chloride first solution of the material in the first step, SO ₄ compound to a basic aluminum chloride the second solution of the material in the second step Examples of the method include a method of mixing and dissolving, and the SO ₄ compound may be added to the solution obtained in the second step.

Examples of the SO ₄ compound include a sulfuric acid band, an alkali metal sulfate salt, an alkaline earth metal sulfate salt, and sulfuric acid. Of these, a sulfuric acid band, sodium sulfate, and magnesium sulfate are preferable.

It must be noted here, if it contains SO ₄ basic aluminum chloride solution (first solution), the concentration of the SO ₄ is _Al 2 _{O 3} 1 mol at 0 to 0.1 mole Need to be If it exceeds 0.1 mol, the viscosity increases in the third step and thereafter, and it tends to gel and solidify, which is not preferable.

  At the time of forming the alumina gel, the first solution is added to the alkaline solution having a pH of 10 or more to react. In the initial state of alumina gel formation, the alumina gel precipitated by adding the acidic basic aluminum chloride first solution to the strong alkaline solution is rapidly dissolved in the alkaline solution.

When the reaction proceeds, the alkaline solution in which the alumina gel is dissolved becomes supersaturated and the alumina gel is precipitated, but by mixing in a reaction solution having a pH of 10 or more to prepare the alumina gel,
This precipitated alumina gel does not grow into a crystalline alumina gel that is hardly soluble in acid, but becomes an easily soluble alumina gel.

  Further, by maintaining the temperature at the time of mixing the alkaline solution and the basic aluminum chloride first solution at 0 to 40 ° C., alumina gel can be stably generated even in an alkaline environment. Further, the produced alumina gel is preferably aged before shifting to the second step.

  This aging further facilitates dissolution in the second step. The temperature during aging is also preferably 0 ° C to 40 ° C. If the temperature during mixing and aging exceeds 40 ° C., the polymerization of the alumina gel will proceed too much, and the resulting basic aluminum chloride will become translucent and white and turbid, which is not preferable. The aging time is preferably about 0 to 2 hours.

In the second step, the alumina gel obtained in the first step is treated with a base having a SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 55%. To a soluble aluminum chloride second solution at 40 ° C to 80 ° C and dissolved. In this case, the second solution may be added to the alumina gel solution.

  As the second solution, one prepared in the same manner as the basic aluminum chloride first solution used in the first step can be used.

  Furthermore, the dissolution liquid obtained in the second step is preferably subjected to a heating treatment at 50 ° C. to 90 ° C. during and / or after the dissolution. The processing time is 1 to 3 hours. By this treatment, undissolved alumina gel can be reduced and basic aluminum chloride can be stabilized to prevent precipitation and settling during storage.

Also in this basic aluminum chloride solution (second solution), when SO ₄ is contained, the concentration of this SO ₄ is 0 to 0.1 mol relative to 1 mol of Al ₂ O ₃ as in the first solution. Must be If it exceeds 0.1 mol, the alumina gel after dissolution tends to gel again and solidify easily, which is not preferable. Especially when the basicity is high, this tendency is remarkable.

  In the third step, an alkali carbonate such as sodium carbonate or potassium carbonate is added to the solution obtained in the second step to obtain a basic aluminum chloride third solution having a basicity of 75% to 95%.

  In the fourth step, the basic aluminum chloride third solution is aged for about 2 hours while maintaining the temperature of 50 ° C to 80 ° C. This makes it possible to obtain a stabilized aged solution of highly basic aluminum chloride having a basicity of 75% to 95%.

Then, the highly basic aluminum chloride of the present invention can be produced by adding a sulfate to the aged solution to adjust the SO ₄ content to 0 to 0.35.
In addition, when the SO ₄ content is not within the above range, the required amount (when the first and second solutions partially contain SO ₄ is subtracted from the required amount) Add to make highly basic aluminum chloride. When magnesium is included, it is preferably added in the form of magnesium chloride in any step as described above.

  As the sulfate, a sulfate band, sodium sulfate, magnesium sulfate or the like can be used.

The highly basic aluminum chloride produced by the production method of the present invention has a composition of M / Al ₂ O ₃ (molar ratio) = 0.8 to 2.2 (M represents the number of moles of the alkali metal), E / Al ₂ O ₃ (molar ratio) = 0 to 0.3 (E represents the number of moles of the alkaline earth metal), Cl / Al ₂ O ₃ (molar ratio) = 1.0 to 3.0, SO ₄ / Al ₂ O ₃ (molar ratio) = 0 to 0.35, and it is highly basic aluminum chloride having a basicity of 75% to 95%.

In the high basic aluminum chloride, alkali metal overbased chloride in aluminum, to _Al 2 _{O 3} 1 mol, 0.8 to 2.2 mol, preferably included 1.3 to 1.9 moles. If the amount of the alkali metal is less than 0.8 mol with respect to 1 mol of Al ₂ O ₃ , the effect of reducing the residual Al, E260 and the number of fine particles cannot be sufficiently obtained, and if it exceeds 2.2 mol, the viscosity increases. Manufacturing becomes difficult.

  In the highly basic aluminum chloride, examples of the alkali metal represented by M include lithium, potassium, sodium and rubidium, with potassium and sodium being preferred.

The alkaline earth metal in highly basic aluminum chloride is contained in an amount of 0 to 0.3 mol, preferably 0.02 to 0.2 mol, per 1 mol of Al ₂ O ₃ . Alkaline earth metal has an effect of further enhancing cohesiveness due to a synergistic effect with the silicon compound with respect to 1 mol of Al ₂ O ₃ . The effect is saturated when the alkaline earth metal exceeds 0.3 mol with respect to 1 mol of Al ₂ O ₃ .

  In the highly basic aluminum chloride, examples of the alkaline earth metal represented by E include beryllium, magnesium, calcium and barium, and magnesium and calcium are preferable.

In the highly basic aluminum chloride, Cl in the highly basic aluminum chloride is contained in an amount of 1.0 to 3.0 mol, preferably 2.0 to 3.0 mol, based on 1 mol of Al ₂ O _3. . This Cl is the sum of Cl bound to Al and Cl bound to the alkali metal. The higher the basicity, the less Cl is bound to Al and the more Cl is bound to the alkali metal.

In the highly basic aluminum chloride, SO ₄ in the highly basic aluminum chloride contains 0 to 0.35 mol, preferably 0.05 to 0.25 mol of SO ₄ with respect to 1 mol of Al ₂ O _3. Be done.

In the highly basic aluminum chloride, SO ₄ (sulfate) may be included depending on the type of river. SO ₄ has an effect of increasing the cohesiveness, but has a negative effect of reducing the residual Al, and it is better to reduce the residual Al as much as possible in order to reduce the residual Al.

In the highly basic aluminum chloride, as described above, the alkaline earth metal can further enhance the cohesiveness due to the synergistic effect with the silicon compound, and particularly for river water that requires cohesiveness due to SO _4. Since it is possible to reduce the content of SO ₄ by combining magnesium, magnesium and silicon, it is preferable to use an alkaline earth metal and a silicon compound in combination.

The silicon compound is contained in highly basic aluminum chloride as silicon in an amount of 0.001 to 0.1 mol, preferably 0.01 to 0.05 mol, based on 1 mol of Al ₂ O ₃ .

  Silicon enhances cohesiveness and is particularly effective for treated water with high turbidity. If it is less than 0.001 mol, no improvement in cohesiveness is observed, and if it exceeds 0.1 mol, the effect is saturated, which is not preferable.

  The basicity of the highly basic aluminum chloride is 75% to 95%, preferably 80% to 90%. In the present invention, highly basic aluminum chloride is possible.

The highly basic aluminum chloride may be contained in water in an amount of 8% by weight to 12% by weight in terms of Al ₂ O _{3 to} prepare a flocculant composition for water treatment.

The water treatment flocculant composition, the high basic aluminum chloride in terms of Al ₂ O ₃ in water 8% to 12% by weight, preferably comprises 10 wt% to 11 wt%, river water used and other The concentration can be appropriately changed depending on the water quality of the sampled water.

  Further, the flocculant composition for water treatment can also use various additives, as long as it does not inhibit the flocculating action as an additive and does not hinder the drinking of treated water subjected to the flocculation treatment. However, it is not particularly limited.

  Specific additives include, for example, polymer flocculants, sodium citrate, sodium gluconate and the like.

  The coagulant composition for water treatment of the present invention can be used by adding and mixing highly basic aluminum chloride to water so as to have a predetermined concentration.

  When the coagulant composition for water treatment of the present invention is used as a coagulant, the residual Al, E260 and the number of fine particles in the treated water after the treatment are remarkably reduced.

Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to the examples.

Example 1
Sodium aluminate solution (Al ₂ O ₃ conversion 19.7%, Na ₂ O conversion 20.2%) 109.0 g and sodium silicate solution (SiO ₂ conversion 28%, Na ₂ O conversion 10%) 7.0 g. Were mixed.

126.7 g of a basic aluminum chloride solution (basicity 49.7%, Al ₂ O ₃ concentration 19.1%, SO ₄ concentration 0%) was mixed to produce an alumina gel. Thereafter, this alumina gel was aged at room temperature for 0.25 to 2 hours, and 281.1 g of a basic aluminum chloride solution (basicity 49.7%, Al ₂ O ₃ concentration 19.1%, SO ₄ concentration 0%). Was added and dissolved.

  This solution was aged at 40 ° C. to 80 ° C. for 60 to 180 minutes, and 28.4 g of sodium carbonate was added to increase the basicity. Further, this basic aluminum chloride solution was aged at 40 ° C to 90 ° C for 60 to 240 minutes.

After that, 30.8 g of liquid sulfuric acid band (Al ₂ O ₃ 8.0%, SO ₄ 22.3%) and 12 g of magnesium chloride hexahydrate were added, and finally, highly basic with a basicity of 80.5%. An aluminum chloride solution (Al ₂ O ₃ 10.3%) was obtained.

The composition of the obtained highly basic aluminum chloride was as follows: Si / Al ₂ O ₃ (molar ratio) = 0.03, Na / Al ₂ O ₃ (molar ratio) = 1.3, Mg / Al ₂ O ₃ (molar ratio) Ratio) = 0.06, Cl / Al ₂ O ₃ (molar ratio) = 2.7, SO ₄ / Al ₂ O ₃ (molar ratio) = 0.07, and the obtained highly basic aluminum chloride is The viscosity was hardly increased and the storage stability was very good.

  The performance of the highly basic aluminum chloride as a flocculant was evaluated using river water under the following test conditions. The composition is shown in Table 1 and the results are shown in Table 2.

<Test conditions>
Place 1 liter of river water in a beaker, add highly basic aluminum chloride while rapid stirring (100 rpm: 64 cm / sec), and then continue rapid stirring for 1 minute and slow stirring (60 rpm; 38 cm / sec) as in the above conditions. After 10 minutes, the mixture was allowed to stand for 10 minutes, and the supernatant was collected with a siphon to determine the turbidity, residual aluminum concentration, E260 (ultraviolet absorbance: trihalomethane removal rate), and the number of fine particles.

  Further, the highly basic aluminum chloride was stored in a water bath at 50 ° C., and the storage stability was visually confirmed.

<Measurement method>
Turbidity: Measured using a turbidimeter (WA-6000, manufactured by Nippon Denshoku Industries Co., Ltd.) using the supernatant as a sample.

Residual aluminum concentration: Using the supernatant as a sample, the filtrate filtered through 0.5 μm filter paper (GC-90 manufactured by Advantech Toyo Co., Ltd.) was measured by ICP emission spectroscopy. As the ICP emission spectroscopic analyzer, VARIAN ICP-OES, SPS5000 was used.

E260: The supernatant was filtered using 0.5 μm filter paper (GC-90 manufactured by Advantech Toyo Co., Ltd.) as a sample, and the filtrate was analyzed using a spectrophotometer (Shimadzu Co., Ltd.) using a quartz glass cell with an optical path length of 1 cm. Absorbance at a wavelength of 260 nm was measured with a manufacturing company UV-2400PC).

  Number of fine particles: Measured using a high sensitivity turbidimeter (NP-6000T manufactured by Nippon Denshoku Industries Co., Ltd.).

<Evaluation>
Turbidity was evaluated by the measured value. The storage stability was visually evaluated by storing in a water bath at 50 ° C. The residual aluminum concentration, E260 and the number of fine particles were evaluated by the measured values.

Example 2
A highly basic aluminum chloride was obtained in the same manner as in Example 1 except that the sodium silicate solution, magnesium chloride hexahydrate and liquid sulfuric acid band of Example 1 were not added. The composition is shown in Table 1. Further, the same tests as in Example 1 were conducted and evaluated. Table 2 shows the results.

Example 3
A highly basic aluminum chloride having a basicity of 90% was obtained in the same manner as in Example 1 except that 60.6 g of sodium carbonate in Example 1 was added. The composition is shown in Table 1. Further, the same tests as in Example 1 were conducted and evaluated. Table 2 shows the results.

Example 4
In the fifth step of Example 3, a highly basic aluminum chloride was obtained in the same manner as in Example 3 except that 26.6 g of sodium sulfate was added to add the insufficient amount of SO ₄ . The composition is shown in Table 1. Further, the same tests as in Example 1 were conducted and evaluated. Table 2 shows the results.

Example 5
A highly basic aluminum chloride having a basicity of 75.5% was obtained in the same manner as in Example 1 except that 14.5 g of sodium carbonate of Example 1 was added. The composition is shown in Table 1. Further, the same tests as in Example 1 were conducted and evaluated. Table 2 shows the results.

Example 6
Sodium aluminate solution _(Al 2 _{O 3} in terms of 19.7%, Na ₂ O in terms of 20.2%) 110.7 g and, based on aluminum chloride solution (basicity 49.7%, _Al 2 _{O 3} concentration 19.1 %, SO ₄ concentration 0%) 128.7 g were mixed to form an alumina gel. Thereafter, this alumina gel was aged at room temperature for 0.25 to 2 hours, and 273.8 g of a basic aluminum chloride solution (basicity 49.7%, Al ₂ O ₃ concentration 19.1%, SO ₄ concentration 0%). Was added and dissolved. The solution was aged at 40 ° C to 80 ° C for 60 to 180 minutes, and 14.5 g of sodium carbonate was added to increase the basicity.

Further, this basic aluminum chloride solution was aged at 40 ° C to 90 ° C for 60 to 240 minutes. Then, 39.7 g of a liquid sulfuric acid band (Al ₂ O ₃ 8.0%, SO ₄ 22.3%) was added, and finally a highly basic aluminum chloride solution (Al ₂ O _{3 having a} basicity of 75.5%) was added. 10.2%) was obtained. Further, the same tests as in Example 1 were conducted and evaluated. Table 2 shows the results.

Comparative Example 1
Instead of the highly basic aluminum chloride of Example 1, commercially available (made by Asahi Chemical Industry Co., Ltd.) PAC (Al ₂ O ₃ : 10.3%, basicity: 52%, SO ₄ : 2.6% (SO ₄ / Al ₂ O ₃ (molar ratio) = 0.27) was evaluated in the same manner as in Example 1. The results are shown in Table 2.

Comparative Example 2
Sodium aluminate solution (Al ₂ O ₃ conversion 19.7%, Na ₂ O conversion 20.2%) 109.0 g and sodium silicate solution (SiO ₂ conversion 28%, Na ₂ O conversion 10%) 7.0 g. Were mixed.

231.4 g of a basic aluminum chloride solution (basic aluminum chloride, basicity 52%, Al ₂ O ₃ 10.3%, SO ₄ 2.6%, Cl 11.4%) was mixed with this to form an alumina gel. did.

Then, this alumina gel was aged at room temperature for 0.25 to 2 hours, and 290.9 g of a basic aluminum chloride solution (basicity 49.7%, Al ₂ O ₃ 19.1%) and a liquid sulfuric acid band (Al ₂ O ₃ 8.0%, SO ₄ 22.3%) 5.3 g and magnesium chloride hexahydrate 12 g were added and dissolved.

This solution was aged at 30 ° C to 50 ° C for 90 minutes, and a highly basic aluminum chloride solution (Al ₂ O ₃ 10.3%) having a basicity of 71% was evaluated in the same manner as in Example 1. Table 2 shows the results.

Comparative Example 3
45.5 g of metal aluminum pieces were dissolved with 94.6 g of hydrochloric acid (35.6%) to obtain 402.4 g of a basic aluminum chloride solution (basicity 83.3%, Al ₂ O ₃ 23.1%). .

  To this, 112.1 g of liquid sulfuric acid band was added and mixed. Thereafter, 13.0 g of sodium carbonate was added, and the mixture was dissolved and aged at 80 ° C. for 120 minutes to obtain a basic aluminum chloride solution.

The composition of the obtained highly basic aluminum chloride was as follows: Na / Al ₂ O ₃ (molar ratio) = 0.3, Cl / Al ₂ O ₃ (molar ratio) = 0.9, SO ₄ / Al ₂ O ₃ ( The molar ratio was 0.26. The composition is shown in Table 1, but the stability at 50 ° C was poor, and the turbidity in the evaluation was 1 or more, so that it was not usable.

Comparative Example 4
Highly basic aluminum chloride having a basicity of 73.5% was prepared in the same manner as in Example 2 except that 7 g of sodium carbonate was added before the addition of the liquid sulfuric acid band of Comparative Example 2 and the aging temperature was set to 65 ° C. Obtained. This solution was evaluated in the same manner as in Example 1. Table 2 shows the results.

Claims (1)

(1) A basic aluminum chloride first solution having a SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 65% is reacted with an alkaline solution. A first step of producing an alumina gel,
(2) The alumina gel obtained in the first step is treated with basic aluminum chloride having a SO ₄ content (SO ₄ / Al ₂ O ₃ (molar ratio)) of 0 to 0.1 and a basicity of 40% to 55%. A second step of adding to the second solution at 40 ° C. to 80 ° C. and dissolving;
(3) A third step in which an alkali carbonate is added to the solution obtained in the second step to obtain a basic aluminum chloride third solution having a basicity of 75% to 95%,
(4) A fourth step of aging the third solution obtained in the third step at 40 ° C. to 90 ° C. to obtain an aging solution,
(5) A fifth step of adding sulfate to the aging solution obtained in the fourth step to adjust the SO ₄ content of the aging solution to SO ₄ / Al 2 O 3 (molar ratio) = 0 to 0.35,
A process for producing highly basic aluminum chloride, which comprises: