JP6658769B2 - 積層塗膜及び塗装物 - Google Patents
積層塗膜及び塗装物 Download PDFInfo
- Publication number
- JP6658769B2 JP6658769B2 JP2017553851A JP2017553851A JP6658769B2 JP 6658769 B2 JP6658769 B2 JP 6658769B2 JP 2017553851 A JP2017553851 A JP 2017553851A JP 2017553851 A JP2017553851 A JP 2017553851A JP 6658769 B2 JP6658769 B2 JP 6658769B2
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- base coating
- metallic base
- paint
- light reflectance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
上記着色ベース塗膜の着色顔料及び上記メタリックベース塗膜の着色顔料がカーボンブラック系顔料であり、
上記着色ベース塗膜は、厚さが7〜20μmであり、顔料質量濃度が5〜15質量%であり、
上記メタリックベース塗膜は、厚さが1〜5μmであり、顔料質量濃度が10%以上20%以下であり、
上記被塗装物の表面に上記着色ベース塗膜のみが形成され、上記メタリックベース塗膜が形成されていない状態で測定した、受光角(塗膜面の法線に対して45゜の角度から照明したときの、正反射方向から光源側への傾き角度のこと。以下、同じ。)15゜の光線反射率及び受光角45゜の光線反射率が波長450〜700nmにおいて共に2%以下であり、
上記メタリックベース塗膜単独で測定した、受光角15゜の光線反射率が波長450〜700nmにおいて20〜50%であり、かつ受光角45゜の光線反射率が波長450〜700nmにおいて2.5%以下であることを特徴とする。
図1に示すように本実施形態の自動車の車体(鋼板)11の表面に設けられた積層塗膜12は、着色ベース塗膜14、メタリックベース塗膜15及び透明クリヤ塗膜16を順に積層してなる。車体11の表面にはカチオン電着塗装によって電着塗膜(下塗り)13が形成され、電着塗膜13の上に上記積層塗膜12が設けられている。
上記被塗装物としては、例えば、鉄、鋼、アルミニウム、スズ、亜鉛等の金属やこれらを含む合金、および、これらの金属のメッキまたは蒸着した成型物、ならびに、ガラス、プラスチックや発泡体による成型物等を挙げることができ、具体的には、図1に示す自動車車体11や自動車部品が挙げられる。被塗装物は、図1に示す例のように、その表面に下塗り塗膜が形成されていてもよい。
着色ベース塗膜を形成するための着色ベース塗料は、硬化型塗料であることが好ましく、塗膜形成成分と、着色顔料とを含んでいる。
工程(2)で形成するメタリックベース塗膜によって、着色ベース塗膜で得られた色を微調整し、さらに濁りのない透明性と色の深み感を増すことができる。
透明クリヤ塗膜により、上記着色ベース塗膜およびメタリックベース塗膜の色落ちを防止し、さらに、得られる積層塗膜に高い透明感と色の深み感を与えることができる。
工程(4)では、上記工程(1)、(2)および(3)で得られた着色ベース塗膜、メタリックベース塗膜および透明クリヤ塗膜を加熱硬化して積層塗膜を形成する。
ステンレス容器に日本ペイント社製アクリル樹脂65.6質量部(固形分量)を入れ、これにEMPEROR 2000(キャボット社製カーボンブラック、商品名)を11.0質量部加えて粒度が0.4μm以下となるように分散させた。次いでユーバン128(三井化学社製ブチル化メラミン樹脂、商品名)15.5質量部(固形分量)を加えて卓上攪拌機で攪拌し、表1に示す着色ベース塗料1を調製した。これを塗装粘度に調整した。
リン酸亜鉛処理したダル鋼板に、パワーニクス110(日本ペイント社製カチオン電着塗料組成物)を乾燥膜厚が20μmとなるように電着塗装し、160℃で30分間加熱硬化させて電着塗膜を得た。この被塗装物上に、着色ベース塗料1を乾燥塗膜が12μmとなるようにスプレー塗装し、熱風乾燥炉にて140℃で20分間加熱硬化させて着色ベース単独塗膜を得た。この着色ベース単独塗膜の受光角15゜及び45゜の光線反射率を、U−3310型分光光度計(日立社製)を用い、波長域300〜780nm、スキャンスピード300nm/min、サンプリング間隔0.5nmの波長スキャンモードで測定した。
ステンレス容器に日本ペイント社製アクリル樹脂33.3質量部(固形分量)を入れ、これにEMPEROR 2000(キャボット社製カーボンブラック、商品名)を16.2質量部を加えて粒度が5μm以下となるように分散させた。次いでユーバン128(三井化学社製ブチル化メラミン樹脂、商品名、固形分60%)を13.5質量部(固形分量)及びアルミペースト7640NS(東洋アルミニウム社製アルミニウム顔料、商品名)8.0質量部(固形分量)を加えて卓上攪拌機で攪拌して、表1に示すメタリックベース塗料1を調製した。これを塗装粘度に調整した。
ポリプロピレン板上に、メタリックベース塗料1を乾燥塗膜が3μmとなるようにスプレー塗装し、熱風乾燥炉にて140℃で20分間加熱硬化させた後、形成した塗膜をポリプロピレン板より剥離して単独のメタリックベース塗膜を得た。このメタリックベース塗膜単独の受光角15゜及び45゜の光線反射率を、U−3310型分光光度計(日立社製)を用い、波長域300〜780nm、スキャンスピード300nm/min、サンプリング間隔0.5nmの波長スキャンモードで測定した。
図3は着色ベース塗料1及びメタリックベース塗料1に係る着色ベース単独塗膜及びメタリックベース塗膜単独の受光角15゜の光線反射率を示し、図4は同じく受光角45゜の光線反射率を示す。
着色ベース塗料2−4を表1に記載の成分と配合によって着色ベース塗料1と同様に調製し、着色ベース塗料2−4各々に係る着色ベース単独塗膜の光線反射率を測定した。結果を表1に示す。
メタリックベース塗料2−6を表1に記載の成分と配合によってメタリックベース塗料1と同様に調製し、メタリックベース塗料2−6各々に係るメタリックベース塗膜単独の光線反射率を測定した。結果を表1に示す。
マックフローO−1600クリヤ(日本ペイント社製酸・エポキシ硬化系クリヤ塗料、商品名)を塗装粘度に調整した。
リン酸亜鉛処理したダル鋼板に、パワーニクス110(日本ペイント社製カチオン電着塗料組成物)を乾燥膜厚が20μmとなるように電着塗装し、160℃で30分間加熱硬化し電着塗膜を形成した。これを被塗装物とした。
−実施例1−
上記被塗装物に、着色ベース塗料1を乾燥膜厚が12μmとなるようにメタベル(回転霧化式静電塗装機)により塗装した。2分間のセッティングの後、メタリックベース塗料1を乾燥膜厚が5μm以下となるようにメタベルにより塗装した。4分間のセッティングの後、クリヤ塗料を乾燥塗膜が35μmとなるようにμμ(マイクロマイクロ)ベル(回転霧化式静電塗装機)により塗装した。さらに10分間のセッティングの後、140℃で20分間焼付硬化させることにより、表2に示す実施例1の積層塗膜を得た。
実施例1と同様にして、表1に示す着色ベース塗料1−4とメタリックベース塗料1−6を選択的に組み合わせて表2に示す実施例2−6及び表3に示す比較例1−10の積層塗膜を得た。
実施例1−6及び比較例1−10の透明性の高低、色の深み感の強弱及び色むらの有無を目視で評価した。結果を表2及び表3に示す。表2及び表3において、「濁りがなく透明である」、「高い深み感がある」及び「色むらを感じない」の各欄の「○」は「良好」、「△」は「普通」、「×」は「不良」をそれぞれ意味する。
12 積層塗膜
13 電着塗膜
14 着色ベース塗膜
15 メタリックベース塗膜
16 透明クリヤ塗膜
17 着色顔料
18 光輝材
Claims (5)
- 被塗装物の表面に形成された着色顔料を含有し光輝材を含有しない着色ベース塗膜と、該着色ベース塗膜の表面に形成された着色顔料および光輝材を含有するメタリックベース塗膜とを備える積層塗膜であって、
上記着色ベース塗膜の着色顔料及び上記メタリックベース塗膜の着色顔料がカーボンブラック系顔料であり、
上記着色ベース塗膜は、厚さが7〜20μmであり、顔料質量濃度が5〜15質量%であり、
上記メタリックベース塗膜は、厚さが1〜5μmであり、顔料質量濃度が10%以上20%以下であり、
上記被塗装物の表面に上記着色ベース塗膜のみが形成され、上記メタリックベース塗膜が形成されていない状態で測定した、受光角(塗膜面の法線に対して45゜の角度から照明したときの、正反射方向から光源側への傾き角度のこと。以下、同じ。)15゜の光線反射率及び受光角45゜の光線反射率が波長450〜700nmにおいて共に2%以下であり、
上記メタリックベース塗膜単独で測定した、受光角15゜の光線反射率が波長450〜700nmにおいて20〜50%であり、かつ受光角45゜の光線反射率が波長450〜700nmにおいて2.5%以下であることを特徴とする積層塗膜。 - 請求項1において、
上記メタリックベース塗膜の光輝材がアルミフレークであり、その厚さが25nm以上200nm以下であることを特徴とする積層塗膜。 - 請求項2において、
上記メタリックベース塗膜の表面に対する上記アルミフレークの配向角が3度以下であることを特徴とする積層塗膜。 - 請求項1乃至請求項3のいずれか一において、
上記メタリックベース塗膜の表面に透明クリヤ塗膜が形成されていることを特徴とする積層塗膜。 - 請求項1乃至請求項4のいずれか一に記載された積層塗膜を備えていることを特徴とする塗装物。