JP6554523B2 - Tissue paper products - Google Patents

Description

  The present invention relates to a tissue paper product in which tissue paper is stored in a storage box that can be taken out in a pop-up manner.

BACKGROUND ART Conventionally, a tissue paper product in which a laminate obtained by folding tissue paper by a so-called pop-up method is stored in a storage box (carton) and the top of the storage box is provided with a tissue paper outlet has become widespread. In addition, a film having a slit is attached inside the take-out port to prevent dust and the like from being mixed and take out easily.
When the tissue paper is taken out of this tissue paper product, the shape of the tissue paper that pops up and comes out stabilizes (it is maintained in a standing state of the tissue paper), and it looks good and comes out next It becomes easy to take out the tissue paper.
For this reason, the film is omitted to facilitate separation and disposal, and a curvilinear narrow portion is formed at the center in the longitudinal direction of the outlet so that the tissue paper that has come out from the outlet can be raised next. By doing this, a technique has been developed that holds the central portion of the tissue paper that has popped up, making it difficult for the tissue paper to drop back (a phenomenon in which the tissue paper falls into the carton) (Patent Document 1).

JP 2005-170414 A

By the way, in general, tissue paper has low strength and its shape is not stable. Therefore, the basis weight is increased to maintain the shape retaining property, and the above-described dropback is suppressed. However, when the basis weight of the tissue paper is increased, there is a problem that the strength becomes too high and the softness is reduced or the cost is increased.
Therefore, according to the present invention, even if the basis weight of the tissue paper is low, it is easy to take out, and the shape (shape retention) of the tissue paper which pops up next and is held at the outlet is stabilized, and drop back is less likely to occur. The purpose is to provide tissue paper products that ensure the softness of tissue paper.

In order to solve the above-mentioned problems, the tissue paper product of the present invention is obtained by stacking a sheet having a basis weight of 8.5 to 10.3 g / m ² and having a predetermined number of plies of one sheet or two or more sheets. A tissue paper laminate in which the tissue paper laminates are alternately stacked in a pop-up manner so as to be removable, an outlet for accommodating the tissue paper laminate, opening on its own top surface, and taking out the tissue paper; And a substantially rectangular storage box having a film formed with a slit for sticking out the tissue paper so as to cover the outlet, and having a slit for taking out the tissue paper, and the length developed in the direction for taking out the tissue paper and LA, the the ratio of the height CH of the storage box (LA / CH) is 3.0 to 7.0, a longitudinal length CL of the storage box is in 200～230Mm, the long To CL, (LB / CL) is 0.70 to 0.99 and, the direction of length LB orthogonal to the take-out direction of the tissue paper, the ratio of the longitudinal length PL of the outlet (LB / PL) is 1.05-2.2, the film thickness is 35-55 μm, the length LA is 180-210 mm, the length LB is 170-230 mm, and (LB / LA) Is 0.8 to 1.8, the length PL is 100 to 200 mm, the width PW in the short direction of the outlet is 30 to 60 mm, and the number of sets of the tissue paper laminate is 140 to 170 And the value represented by (the number of sets × the number of plies) / (the height CH) is 6.5 to 7.5, and the thickness of the sheet is 0.41 to 0.47 mm / 10 It is.

It is preferable that a ratio (TA / TB) of the strength TA in the take-out direction of the tissue paper and the strength TB in the direction orthogonal to the take-out direction of the tissue paper is 0.15 to 1.0.
To the width CW in the transverse direction before Symbol storage box, ((LA / 2) / CW) is preferably a 0.65 to 0.99.
The ply number is preferably 1 to 4.
It is preferable that (FL / PL) is 0.70 to 0.99 with respect to the slit length FL of the film.
The film is preferably polyethylene.

  According to the present invention, it is easy to take out even if the basis weight of the tissue paper is low, and the shape (shape retaining property) of the tissue paper that pops up and is held at the outlet is stabilized, and dropback hardly occurs. As a result, a tissue paper product can be obtained in which the softness of the tissue paper is ensured.

It is a perspective view of the tissue paper product concerning the embodiment of the present invention. It is a top view of the tissue paper product which concerns on embodiment of this invention. It is a figure which shows the measuring method of the length (length which expanded tissue paper) LA expand | deployed in the taking-out direction of tissue paper.

Embodiments of the present invention will be described below. 1 and 2 are a perspective view and a top view of a tissue paper product 100 according to an embodiment of the present invention, respectively.
As shown in FIG. 1, the tissue paper product 100 comprises a tissue paper laminate 20 (see FIG. 2) formed by alternately laminating the tissue paper 2a, 2b,. And a substantially rectangular storage box 10 for storing the Further, an outlet 10h for taking out the tissue papers 2a, 2b,... Is opened on the top surface 10a of the storage box 10, and a plastic film 6 is stuck inside the top surface 10a so as to cover the outlet 10h. Has been. Further, a slit 6s is formed in the film 6 along the longitudinal direction of the outlet 10h, and the tissue papers 2a, 2b,... Are taken out through the slit 6s. It offers prevention and ease of removal.
In the present embodiment, each tissue paper 2a, 2b,... Is V-folded at the center and has a fold line 2af, and the respective side end portions are alternately stacked while being overlapped and can be taken out in a pop-up manner Although the tissue paper laminate is configured, other known folding methods (for example, Z-folding) may be used if it can be taken out in a pop-up manner.

The tissue papers 2a, 2b,... Have a predetermined number of plies of one or more sheets each having a basis weight of 8.5 to 10.3 g / m ² containing pulp as a main component (50% by mass or more). It becomes. By setting the basis weight per sheet to the above-mentioned range, the basis weight and hence the strength become too high to prevent the softness from being reduced, and the feeling in use is excellent. If the basis weight is less than 8.5 g / m ² , the strength may be lowered to be easily broken, or the shape retention of the tissue may be inferior. On the other hand, if the basis weight exceeds 10.3 g / m ² , the strength may be too high and the softness may be inferior. The basis weight is preferably 9.0 to 10.0 g / m ² , more preferably 9.5 to 10.0 g / m ² . The number of plies is preferably 1 to 4, and more preferably 2.
Pulp includes wood pulp, waste paper pulp, and non-wood pulp, but the pulp constituting the facial tissue may consist of 100% wood pulp, and may include waste paper pulp and non-wood pulp. Examples of components other than pulp include fillers, synthetic fibers, and natural fibers. In order to obtain target quality, it is preferable to use wood pulp of NBKP: LBKP = 10: 90 to 70:30 (mass ratio) as a raw material, and a more preferable range is NBKP: LBKP = 20: 80 to 60: 40, and a more preferable range is NBKP: LBKP = 20: 80 to 50:50.
Pulp produced from Eucalyptus eucalyptus represented by Eucalyptus genus Grandis and Eucalyptus globulus is preferred as the grade of LBKP. Moreover, up to 130 parts by mass of waste paper pulp derived from a milk pack can be included with respect to a total of 100 parts by mass of the NBKP and LBKP pulps. By mixing waste paper pulp, the strength is easily improved, and an appropriate strength can be obtained even if the basis weight is low. More preferably, the used paper pulp is blended in an amount of 1 to 120 parts by weight, more preferably 10 to 110 parts by weight, and most preferably 25 to 100 parts by weight.

In addition, in order to ensure an appropriate strength in the tissue paper, the raw materials can be blended by an ordinary means, and the strength adjustment can be performed by the beating process of the pulp fiber. As the beating for obtaining the target quality, it is preferable to be beaten so that the Canadian standard freeness (JIS P 8121) of the pulp raw material of the stock inlet (head box) is 100 to 450 ml. By setting the above-mentioned range, appropriate strength can be obtained even if the basis weight is low. The above-mentioned Canadian standard freeness is more preferably 150 to 400 ml, still more preferably 200 to 400 ml, and most preferably 250 to 350 ml. If the Canadian standard freeness exceeds 400 ml, proper strength may not be obtained. If the amount is less than 100 ml, the moisture content of the web may be increased, the load in the drying step may be increased, and the operability may be deteriorated.
A dry strength agent may be used as appropriate. In addition, it is preferable to appropriately use a wet strength agent.
In the manufacture of tissue paper, calendar processing, presence / absence of embossing, and presence / absence of printing can be selected as appropriate. Preferably, calendering is performed, and embossing and printing are not performed. Moreover, it is preferable not to apply the lotion to the tissue paper. When a lotion is applied, the tissue becomes soft and the shape retention of the tissue may be inferior.

On the other hand, when the basis weight is in the above range, the shape retention of the tissue paper held up in the vicinity of the outlet 10h pops up from the outlet 10h is degraded or drop back (the tissue paper falls into the carton without standing Phenomenon). Therefore, in the present embodiment, the following provisions have been made. First, let D be the direction in which the tissue paper 2a, 2b... Is taken out from the outlet 10h (slit 6s). In the case of FIG. 1, the vertical direction is the takeout direction D.
In the present embodiment, the ratio (LA / CH) of the length LA (the length in which the tissue paper is unfolded) LA developed in the take-out direction D of the tissue paper 2a and the height CH of the storage box 10 is 3.0. To 7.0, and the ratio (LB / PL) of the length LB of the tissue paper 2a in the direction orthogonal to the takeout direction D to the length PL of the takeout port 10h in the longitudinal direction is 1.05 to 2 2 and the thickness of the film 6 is 20 to 80 μm. Here, the longitudinal direction of the take-out port 10h is along the direction orthogonal to the take-out direction D of the tissue paper 2a.

By defining as described above, even if the basis weight of the tissue paper is low, it is easy to take out, and the shape retention property of the tissue paper that pops up next can be improved, and the drop back can be suppressed.
In addition, as shown in FIG. 3, the length LA develops the popped up tissue paper 2a in the taking-out direction D and places it on the flat plate 200, and one side 2a1 in the direction orthogonal to the taking-out direction D Secure with. Then, the opposite side 2a2 is slightly pulled to set a length when the convex portion of the fold 2af of the tissue paper 2a is crushed and almost flattened.

When (LA / CH) is less than 3.0, the upper and lower lengths of tissue paper held at the outlet 10h are shortened, making it difficult to take out tissue paper (second and subsequent sheets) to be used next. On the other hand, if (LA / CH) exceeds 7.0, the upper and lower lengths of the tissue paper held in the outlet 10h become too long, and the shape retention property is reduced. (LA / CH) is preferably 3.0 to 6.0, more preferably 3.5 to 5.5.
When (LB / PL) is less than 1.05, the length in the planar direction of the tissue paper held at the outlet 10h becomes too short, and dropback occurs. On the other hand, if (LB / PL) exceeds 2.2, the length in the planar direction of the tissue paper held by the take-out port 10h becomes too long, and the resistance of the take-out port 10h increases when taking out the tissue paper, There are cases where the first and second and subsequent sheets can not be easily removed. (LB / PL) is preferably 1.05 to 2.0, more preferably 1.1 to 1.6.
If the thickness of the film 6 is less than 20 μm, the strength of the film may be weakened to cause dropback, or the shape retention may be reduced. On the other hand, when the thickness of the film 6 exceeds 80 μm, the resistance to the film increases when the tissue paper is taken out, and the takeout properties of the first and second sheets may be inferior. The thickness of the film 6 is preferably 20 to 60, more preferably 35 to 55 μm.

It is preferable that length LA is 150-230 mm, length LB is 150-240 mm, and (LB / LA) is 0.8-1.8.
If the length LA or LB is less than 150 mm, the tissue paper may be too small to be used. When the length LA exceeds 230 mm or the length LB exceeds 240 mm, the tissue paper may be too large to be used. In addition, if LB / LA exceeds 1.8 or is less than 0.8, the balance of the size of the tissue paper in the vertical and horizontal directions may be poor and it may be difficult to use.
The length LA is preferably 170 to 220 mm, more preferably 180 to 210 mm. Moreover, length LB becomes like this. Preferably it is 170-230 mm, More preferably, it is 190-220 mm. Further, (LB / LA) is preferably 0.8 to 1.5, more preferably 1.0 to 1.3.

It is preferable that the length PL is 100 to 200 mm and the width PW in the short direction of the outlet 10 h is 20 to 60 mm.
If the length PL is less than 100 mm, the resistance may increase when the tissue is taken out, and the takeability of the first and second and subsequent sheets may be inferior. On the other hand, when PL exceeds 200 mm, the length in the planar direction of the tissue paper held in the outlet 10 h may become relatively short, and drop back may be apt to occur. The length PL is preferably 135 to 200 mm, 145 to 180 mm.
When the width PW is less than 20 mm, it is difficult for a finger to enter the outlet 10h, and the first tissue may be unsatisfactory. On the other hand, if PW exceeds 60 mm, the area of the film becomes large, so when taking out the tissue, the film may be stretched, resulting in poor shape retention and drop back may occur. The width PW is preferably 30 to 60 mm, more preferably 38 to 52 mm.

It is preferable that the ratio (TA / TB) of the strength TA in the tissue paper take-out direction D and the strength TB in the direction perpendicular to the take-out direction of the tissue paper is 0.15 to 1.0.
When (TA / TB) is less than 0.15, the strength in the take-out direction D is weak, the tissue paper falls down, and the shape retention may be inferior. On the other hand, if (TA / TB) exceeds 1.0, the strength in the take-out direction D becomes too strong, and the end of the tissue paper after drawing out may be rounded, resulting in poor shape retention. (TA / TB) is preferably 0.20 to 1.0, more preferably 0.20 to 0.40.
The strength TA in the take-out direction D is preferably 0.75 to 1.9 N / 25 mm, more preferably 0.85 to 1.9 N / 25 mm, and 1.1 to 1.5 N / 25 mm. More preferably. The strength TB in the direction orthogonal to the take-out direction is preferably 2.5 to 5.2 N / 25 mm, more preferably 3.0 to 5.2 N / 25 mm, and 3.7 to 4. More preferably, it is 5 N / 25 mm.
Further, it is preferable that √ (TA × TB), which is the square root of the product of the strength TA in the removal direction D and the strength TB in the direction orthogonal to the removal direction, is 1.4 to 3.1 N / 25 mm. If √ (TA × TB) is less than 1.3 N / 25 mm, the tissue paper may be easily broken. On the other hand, when √ (TA × TB) exceeds 3.1 N / 25 mm, the tissue paper may have poor softness. √ (TA × TB) is preferably 1.6 to 3.1 N / 25 mm, more preferably 2.0 to 2.6 N / 25 mm.
The strengths TA and TB of the tissue paper are the strength of the entire tissue paper formed by stacking one or two or more sheets.

The thickness of the sheet is preferably 0.35 to 0.70 mm / 10.
If the thickness of the sheet is less than 0.35 mm / 10, the shape retention of the tissue may be inferior. On the other hand, if the thickness of the sheet exceeds 0.70 mm / 10, it may be necessary to increase (increase) the height CH of the storage box in order to ensure the insertability of the tissue paper laminate into the storage box. is there. Further, when the height CH of the storage box is increased, (LA / CH) becomes less than 3.0, and the vertical length of the tissue paper held at the outlet 10h is shortened. It may be inferior in the taking out property of the sheet. The thickness of the sheet is preferably 0.41 to 0.60 mm / 10, and more preferably 0.43 to 0.55 mm / 10.

The number of tissue paper laminates is preferably 100 to 200, and the value represented by (number of pairs × number of plies) / (height CH) is preferably 5.5 to 10.0.
If the above value is less than 5.5, the number of sets is too small with respect to the height CH of the storage box, and the upper space in the storage box becomes large (the tissue paper laminate is unevenly distributed in the lower portion of the storage box, The upper part becomes empty, and it may be difficult to take out the first tissue paper. On the other hand, when the above value exceeds 10.0, the number of sets increases with respect to the height CH, and the tissue paper laminate is tightly packed in the storage box, and the first tissue paper is taken out. May be inferior. The value represented by (number of sets × number of plies) / (height CH) is preferably 5.5 to 9.0, and more preferably 6.5 to 7.5. The number of sets is preferably 140 to 170 sets, and more preferably 150 to 160 sets.

(LB / CL) is 0.70 to 0.99 with respect to the length CL in the longitudinal direction of the storage box 10, and ((LA / 2) / CW) with respect to the width CW in the short direction of the storage box 10 Is preferably 0.65 to 0.99.
If (LB / CL) is less than 0.70, the size balance between the storage box and the laminate is not good, and the laminate may be biased or bent in the storage box, and the first sheet can be taken out. It may be inferior. On the other hand, when (LB / CL) exceeds 0.99, it is difficult to insert the tissue paper laminate into the storage box at the time of manufacture, and the insertability may be deteriorated. (LB / CL) is preferably 0.80 to 0.99, more preferably 0.85 to 0.99. The length CL in the longitudinal direction of the storage box 10 is preferably 150 to 250 mm, more preferably 170 to 250 mm, and still more preferably 200 to 230 mm.
If ((LA / 2) / CW) is less than 0.65, the size balance between the storage box and the laminate is not good, and the laminate may be biased or bent in the storage box, and the first sheet In some cases, the extractability of the On the other hand, when ((LA / 2) / CW) exceeds 0.99, it becomes difficult to insert the tissue paper laminate into the storage box at the time of manufacture, and the insertability may deteriorate. ((LA / 2) / CW) is preferably 0.70 to 0.99, more preferably 0.75 to 0.95. The width CW in the short direction of the storage box 10 is preferably 90 to 140 mm, more preferably 100 to 140, and still more preferably 105 to 120 mm.

It is preferable that (FL / PL) is 0.70 to 0.99 with respect to the length FL in the longitudinal direction of the slit 6s of the film 6.
When (FL / PL) is less than 0.70, the resistance of the film may increase when the tissue paper is removed, and the removal performance of the first and second sheets may be inferior. On the other hand, if (FL / PL) exceeds 0.99, the left and right ends of the tissue paper may rub against the outlet 10h, and the tissue paper may be torn. (FL / PL) is preferably 0.70 to 0.99, more preferably 0.80 to 0.99, and still more preferably 0.90 to 0.99.
Note that the length FL is equal to or shorter than the length PL, and normally FL <PL <LB.
In addition, it is preferable that the film 6 is polyethylene because the film is easily stretched and hardly broken.

  It goes without saying that the present invention is not limited to the above-described embodiments, and extends to various modifications and equivalents included in the spirit and scope of the present invention.

A pulp composition (mass%) is NBKP 35%, LBKP 65%, 40 mass parts of waste paper raw material derived from a milk pack is blended with 100 mass parts of this raw material, and one sheet of sheets having the characteristics shown in Table 1 and Table 2 Then, a double-layered tissue paper was made and V-folded in a known manner to produce a pop-up removable tissue paper laminate. The tissue paper laminate was stored in a storage box (predetermined paperboard) having the characteristics shown in Table 1 and Table 2 to produce a tissue paper product. The following evaluation was performed.
Sheet basis weight: Measured based on JIS P8124 and converted per sheet.
Sheet thickness: Measured using a thickness gauge (dial thickness gauge "PEACOCK" manufactured by Ozaki Mfg. Co., Ltd.). The measurement conditions were a measurement load of 250 gf and a probe diameter of 30 mm. A sample was placed between the probe and the measurement table, and the gauge was read when the probe was lowered at a speed of 1 mm or less per second. One measurement was performed by stacking 10 samples, and the measurement was repeated 10 times and the measurement results were averaged.
TA, TB: Tensile strength at drying (unit: N / 25 mm) based on JIS-P8113 was measured. Film thickness: Measured in accordance with JIS P 8118. In addition, the thickness of the film was measured as pressure 50 kPa of a pressurization surface using the measuring machine (product name TM600) made from Kumagaya Riki Kogyo Co., Ltd. product.
The measurements of the basis weight, TA, TB, sheet and film thickness were carried out after maintaining the state of equilibrium under the temperature and humidity conditions (23 ± 1 ° C., 50 ± 2% RH) defined in JIS-P8111.

The following sensory evaluation was performed by 20 monitors.
Shape retention of tissue paper (shape retention after sheet withdrawal): The shape of the tissue paper held in the outlet when popped up (whether or not the tissue paper is kept standing) was evaluated.
Drop back: When popping up, the likelihood of drop back (a phenomenon in which tissue paper falls into a carton) was evaluated.
Ease of taking out first tissue paper: Ease of taking out the first tissue paper after opening the outlet and taking out the first tissue paper from the outlet was evaluated.
Take-out property of the second and subsequent tissue papers: The ease of taking-out when the take-out port was opened and the second and subsequent tissue papers were taken out from the exit port was evaluated.
Tissue paper size (ease of use): The tissue paper taken out was evaluated for the balance between size and length and width when held in hand.
Tissue paper softness: The softness of the extracted tissue paper when it was unfolded and held in the hand was evaluated.
The tear resistance of the tissue paper: The tear resistance when the tissue paper taken out was unfolded and pulled with both hands was evaluated.
As the evaluation criteria, the relative evaluation of each sample was performed based on the following criteria, with a full score of 6 points.
6 points: Very good 5 points: Excellent 4 points: Somewhat excellent 3 points: No problem in practical use 2 points: Inferior 1 point: Notably inferior

Operability: Insertability when inserting the tissue paper laminate into the storage box was evaluated according to the following criteria.
6 points: Very good 5 points: Excellent 4 points: Somewhat excellent 3 points: No problem in practical use 2 points: Inferior 1 point: Notably inferior

  The obtained results are shown in Tables 1 and 2.

As is apparent from Tables 1 and 2, the basis weight per sheet is 8.5 to 10.3 g / m ² , (LA / CH) is 3.0 to 7.0, and (LB / PL) is In the case of each example having a thickness of 1.05 to 2.2 and a film thickness of 20 to 80 μm, the tissue paper has excellent shape retention, dropback, take-out property, size, softness, and resistance to tearing. The property was also excellent.

On the other hand, in the case of Comparative Example 1 in which the basis weight per sheet was less than 8.5 g / m ² , the tissue shape of the tissue paper was inferior and the resistance to tearing was inferior.
In the case of Comparative Example 2 in which (LA / CH) is less than 3.0 and (LB / PL) is less than 1.05, dropback occurs and shape retention is inferior, and the first and second tissue papers are prepared. The ease of taking out after the first piece was inferior.
In the case of Comparative Example 3 in which (LA / CH) is less than 3.0 and (LB / PL) exceeds 2.2, drop back is generated and the paper sheet first and second sheets after the removal property Was inferior. In Comparative Example 3, it is considered that dropback occurred because the PW exceeded 60 mm.
In the case of Comparative Example 2, (LA / 2) / CW) exceeded 0.99 and the operability was inferior.
Moreover, in the case of the comparative example 3, (LB / CL) exceeded 0.99 and the operativity was also inferior.

  In the case of Comparative Example 4 in which (LA / CH) exceeded 7.0, the shape retaining property was lowered and the takeout property of the first tissue paper was inferior.

In the case of Comparative Example 5 where the thickness of the film was 20 μm, the shape retaining property was lowered and dropback occurred.
In the case of Comparative Example 6 in which the thickness of the film exceeded 80 μm, the takeout properties of the first and second sheets of tissue paper were inferior.
In the case of Comparative Example 7 in which (LB / PL) exceeded 2.2, the takeout properties of the first and the second paper sheets were inferior. Further, in Comparative Example 7, the softness of the tissue paper was also inferior because the basis weight per sheet exceeded 10.3 g / m ² .

In the case of Comparative Example 8 which is a commercially available product, (LA / CH) was less than 3.0, the shape retention property was inferior, and the takeout properties for the first and second tissue papers were inferior. Although the basis weight per sheet of Comparative Example 8 exceeded 10.3 g / m ² , the softness of the tissue paper was good because it was a lotion tissue coated with a drug solution.
In the case of Comparative Example 9 which is a commercial product having a basis weight per sheet exceeding 10.3 g / m ² , the softness of the tissue paper was inferior.

2a, 2b tissue paper 6 film 6s slit 10 storage box 10a top surface of storage box 10h outlet 20 tissue paper laminate 100 tissue paper product

Claims (6)

Tissue paper made up of a predetermined number of plies of one sheet or two or more sheets with a basis weight of 8.5 to 10.3 g / m ² mainly composed of pulp is alternately stacked so that it can be taken out in a pop-up manner. Tissue paper laminate,
The tissue paper laminate is accommodated, an outlet opening on its own top surface to take out the tissue paper, and a slit formed on the inside of the top surface to cover the outlet, and a slit to take out the tissue paper formed A substantially rectangular storage box having the film
A tissue paper product with
The ratio (LA / CH), which is the ratio of the length LA expanded in the removal direction of the tissue paper to the height CH of the storage box, is 3.0 to 7.0,
The longitudinal length CL of the storage box is 200 to 230 mm, and (LB / CL) is 0.70 to 0.99 with respect to the length CL.
And, a ratio (LB / PL) of a length LB in a direction orthogonal to the taking-out direction of the tissue paper and a length PL in the longitudinal direction of the taking-out port is 1.05 to 2.2,
The thickness of the film is 35 to 55 μm,
The length LA is 180 to 210 mm, the length LB is 170 to 230 mm, and (LB / LA) is 0.8 to 1.8,
The length PL is 100 to 200 mm, the width PW in the short direction of the outlet is 30 to 60 mm,
The number of sets of the tissue paper laminate is 140 to 170, and the value represented by (the number of sets × the number of plies) / (the height CH) is 6.5 to 7.5,
A tissue paper product having a thickness of 0.41 to 0.47 mm / 10 sheets.   The ratio (TA / TB) of the strength TA in the take-out direction of the tissue paper and the strength TB in the direction perpendicular to the take-out direction of the tissue paper is 0.15 to 1.0. Described tissue paper products. To the width CW in the transverse direction before Symbol storage box, ((LA / 2) / CW) is tissue paper product according to claim 1 or 2 is 0.65 to 0.99. The tissue paper product according to any one of claims 1 to 3, wherein the ply number is 1 to 4. The tissue paper product according to any one of claims 1 to 4, wherein (FL / PL) is 0.70 to 0.99 with respect to a length FL of the slit of the film. The tissue paper product according to any one of claims 1 to 5, wherein the film is polyethylene.