  The present invention relates to a method for producing a structure including a phase separation structure and a structure including a phase separation structure.

  In recent years, with the further miniaturization of large-scale integrated circuits (LSIs), a technique for processing more delicate structures is required. In response to such a demand, attempts have been made to form a finer pattern using a phase separation structure formed by self-assembly of block copolymers in which incompatible blocks are bonded to each other. (For example, refer to Patent Document 1).

  In order to use the phase separation of the block copolymer, it is essential to form the self-assembled nanostructure formed by the microphase separation only in a specific region and arrange it in a desired direction. In order to realize these position control and orientation control, methods such as grapho epitaxy for controlling the phase separation pattern by the guide pattern and chemical epitaxy for controlling the phase separation pattern by the difference in the chemical state of the substrate have been proposed. (For example, refer nonpatent literature 1).

  In order to realize the position control and the orientation control, a resist material containing a base material component such as a resin is used for forming the guide pattern. For example, Patent Document 2 discloses a method of forming a phase separation structure by forming a guide pattern on a substrate using a resist composition and applying a block copolymer to a recess of the guide pattern.

JP 2008-36491 A JP 2012-61531 A

Proceedings of SPIE, Volume 7637, 76370G-1 (2010).

  However, the graphoepitaxy that controls the phase separation pattern by a physical guide can form a phase separation structure between the guides, but forms a phase separation structure in the portion where the guide pattern is formed. It was difficult to form a desired phase separation structure. In addition, conventional chemical epitaxy has a problem in that the process is complicated, for example, in order to form a desired phase separation structure, it is necessary to arrange a thin film made of a surface treatment agent in accordance with the period of the block copolymer. It was.

  The present invention has been made in view of the above circumstances, and provides a method for manufacturing a structure including a phase separation structure, which can manufacture a structure including a phase separation structure without going through complicated steps. The task is to do.

The present invention includes a step of forming a neutralized film containing a surface treatment agent having an affinity with any polymer constituting a block copolymer on a substrate, and generating an acid on the neutralized film by exposure. Forming a photosensitive resin film by using a photosensitive resin composition whose solubility in a developing solution is changed by the action of an acid, exposing, developing, and forming the photosensitive resin pattern; Forming a layer including a block copolymer in which a plurality of types of polymers are bonded so as to cover the photosensitive resin pattern and the neutralized film on the pattern; and on the photosensitive resin pattern and the neutralized film. , the layers were phase separation containing the block copolymer, possess the steps of forming a phase separation structure in the photosensitive on the resin pattern and neutralization film, wherein the photosensitive resin pattern is high from the substrate surface Saga It is a manufacturing method of a structure including a phase separated structure and less than 2 nm.

In the present invention, in the step of forming the photosensitive resin pattern, baking after development is preferably performed at 180 ° C. or higher .

In the present specification and claims, “aliphatic” is a relative concept with respect to aromatics, and is defined to mean groups, compounds, etc. that do not have aromaticity.
The “alkyl group” includes linear, branched and cyclic monovalent saturated hydrocarbon groups unless otherwise specified.
The “alkylene group” includes linear, branched, and cyclic divalent saturated hydrocarbon groups unless otherwise specified. The same applies to the alkyl group in the alkoxy group.
The “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of the alkyl group are substituted with a halogen atom, and examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
“Fluorinated alkyl group” or “fluorinated alkylene group” refers to a group in which part or all of the hydrogen atoms of an alkyl group or alkylene group are substituted with fluorine atoms.
“Structural unit” means a monomer unit (monomer unit) constituting a polymer compound (resin, polymer, copolymer).
“A structural unit derived from an acrylate ester” means a structural unit formed by cleavage of an ethylenic double bond of an acrylate ester.
“Acrylic acid ester” is a compound in which the hydrogen atom at the carboxy group terminal of acrylic acid (CH ₂ ═CH—COOH) is substituted with an organic group.
In the acrylate ester, the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent. The substituent that replaces the hydrogen atom bonded to the α-position carbon atom is an atom or group other than a hydrogen atom, such as an alkyl group having 1 to 5 carbon atoms, a halogenated alkyl group having 1 to 5 carbon atoms, hydroxy An alkyl group etc. are mentioned. The α-position carbon atom of the acrylate ester is a carbon atom to which a carbonyl group is bonded unless otherwise specified.
Hereinafter, an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position is substituted with a substituent may be referred to as an α-substituted acrylate ester. Further, the acrylate ester and the α-substituted acrylate ester may be collectively referred to as “(α-substituted) acrylate ester”.
“A structural unit derived from hydroxystyrene or a hydroxystyrene derivative” means a structural unit formed by cleavage of an ethylenic double bond of hydroxystyrene or a hydroxystyrene derivative.
“Hydroxystyrene derivative” is a concept including those in which the hydrogen atom at the α-position of hydroxystyrene is substituted with another substituent such as an alkyl group or an alkyl halide group, and derivatives thereof. The derivatives include those in which the hydrogen atom at the α-position may be substituted with a substituent, the hydrogen atom of the hydroxyl group of hydroxystyrene substituted with an organic group, and the hydrogen atom at the α-position substituted with a substituent. Examples include those in which a substituent other than a hydroxyl group is bonded to a good benzene ring of hydroxystyrene. The α-position (α-position carbon atom) means a carbon atom to which a benzene ring is bonded unless otherwise specified.
Examples of the substituent for substituting the hydrogen atom at the α-position of hydroxystyrene include the same substituents as those mentioned as the substituent at the α-position in the α-substituted acrylic ester.
The “structural unit derived from vinyl benzoic acid or a vinyl benzoic acid derivative” means a structural unit configured by cleavage of an ethylenic double bond of vinyl benzoic acid or a vinyl benzoic acid derivative.
The “vinyl benzoic acid derivative” is a concept including a compound in which the hydrogen atom at the α-position of vinyl benzoic acid is substituted with another substituent such as an alkyl group or an alkyl halide group, and derivatives thereof. These derivatives include those obtained by substituting the hydrogen atom of the carboxy group of vinyl benzoic acid with an organic group, which may be substituted with a hydrogen atom at the α-position, and the hydrogen atom at the α-position with a substituent. Examples thereof include those in which a substituent other than a hydroxyl group and a carboxy group is bonded to the benzene ring of vinyl benzoic acid. The α-position (α-position carbon atom) means a carbon atom to which a benzene ring is bonded unless otherwise specified.
“Styrene” is a concept including styrene and those in which the α-position hydrogen atom of styrene is substituted with another substituent such as an alkyl group or a halogenated alkyl group.
“Structural unit derived from styrene” and “structural unit derived from styrene derivative” mean a structural unit formed by cleavage of an ethylenic double bond of styrene or a styrene derivative.
The alkyl group as the substituent at the α-position is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group) and the like.
Specific examples of the halogenated alkyl group as the substituent at the α-position include groups in which part or all of the hydrogen atoms of the above-mentioned “alkyl group as the substituent at the α-position” are substituted with a halogen atom. It is done. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
Specific examples of the hydroxyalkyl group as the substituent at the α-position include a group in which part or all of the hydrogen atoms of the “alkyl group as the substituent at the α-position” are substituted with a hydroxyl group. 1-5 are preferable and, as for the number of the hydroxyl groups in this hydroxyalkyl group, 1 is the most preferable.
“Exposure” is a concept including general irradiation of radiation.

  The present invention can provide a method for producing a structure including a phase separation structure without a complicated process by forming an ultrathin photosensitive resin pattern on a substrate.

It is a schematic process drawing explaining the embodiment of the manufacturing method of the structure containing the phase-separation structure of this invention. It is a schematic process drawing explaining the method of manufacturing the structure containing a phase-separation structure by grapho epitaxy.

≪Method for producing structure including phase separation structure≫
The method for producing a structure including a phase separation structure according to the present invention includes a step of forming a neutralized film containing a surface treatment agent on a substrate, and forming a photosensitive resin film on the neutralized film. Exposing and developing to form a pattern, and forming a layer containing a block copolymer in which a plurality of types of polymers are bonded on the pattern so as to cover the pattern and the neutralized film; Separating the layer containing the block copolymer on the pattern and the neutralized film.
A method for producing a structure including the phase separation structure of the present invention will be specifically described with reference to the drawings. However, the present invention is not limited to this.

[Step of forming neutralized film containing surface treatment agent on substrate]
First, a neutralized film containing a surface treatment agent is formed on a substrate. In the present invention, for example, as shown in FIG. 1, a neutralization film 2 containing a surface treatment agent is formed on a substrate 1.

<Board>
If the board | substrate 1 can apply | coat the solution containing a block copolymer on the surface, the kind will not be specifically limited. For example, metals such as silicon, copper, chromium, iron, and aluminum, substrates made of inorganic materials such as glass, titanium oxide, silica, and mica, substrates made of organic compounds such as acrylic plates, polystyrene, cellulose, cellulose acetate, and phenol resins Is mentioned.
Moreover, the magnitude | size and shape of the board | substrate 1 used in this invention are not specifically limited. The substrate 1 does not necessarily have a smooth surface, and substrates of various materials and shapes can be appropriately selected. For example, a substrate having a curved surface, a flat plate having an uneven surface, and a substrate having various shapes such as a flake shape can be used.

  In addition, an inorganic and / or organic film may be provided on the surface of the substrate 1. An inorganic antireflection film (inorganic BARC) is an example of the inorganic film. Examples of the organic film include an organic antireflection film (organic BARC).

Before forming the neutralization film on the substrate, the surface of the substrate 1 may be cleaned. By cleaning the surface of the substrate 1, the subsequent neutralization film forming step may be performed satisfactorily.
As the cleaning treatment, conventionally known methods can be used, and examples thereof include oxygen plasma treatment, hydrogen plasma treatment, ozone oxidation treatment, acid-alkali treatment, and chemical modification treatment. For example, the substrate is immersed in an acid solution such as sulfuric acid / hydrogen peroxide solution, washed with water, and dried. Thereafter, a layer containing a block copolymer can be formed on the surface of the substrate.

<Neutralized film forming step including surface treatment agent>
In the present invention, first, the substrate is neutralized. The neutralization treatment refers to a treatment for modifying the substrate surface so as to have affinity with any polymer constituting the block copolymer. By performing the neutralization treatment, it is possible to suppress only the phase made of a specific polymer from coming into contact with the substrate surface by phase separation. For this reason, in order to form a lamellar structure oriented in a direction perpendicular to the substrate surface by phase separation, before forming the layer containing the block copolymer, the substrate surface is subjected to a medium depending on the type of block copolymer used. An oxidizing film is formed.

Specifically, a thin film (neutralized film 2) containing a surface treatment agent having affinity with any polymer constituting the block copolymer is formed on the substrate surface.
As such a neutralization film 2, a film made of a resin composition can be used. The resin composition used as the surface treatment agent can be appropriately selected from conventionally known resin compositions used for thin film formation according to the type of polymer constituting the block copolymer. The resin composition used as the surface treatment agent may be a heat-polymerizable resin composition or a photosensitive resin composition such as a positive resist composition or a negative resist composition.
In addition, a non-polymerizable film formed by applying a compound as a surface treatment agent and applying the compound may be used as a neutralized film. For example, a siloxane organic monomolecular film formed using phenethyltrichlorosilane, octadecyltrichlorosilane, hexamethyldisilazane, or the like as a surface treatment agent can also be suitably used as the neutralization film.
The neutralization film 2 made of these surface treatment agents can be formed by a conventional method.

As such a surface treatment agent, for example, a resin composition containing all of the constituent units of each polymer constituting the block copolymer, a resin containing all of the constituent units having high affinity with each polymer constituting the block copolymer, etc. Is mentioned.
For example, in the case of using a PS-PMMA block copolymer, which will be described later, as a surface treatment agent, a substance resin composition containing both PS and PMMA as structural units, a site having high affinity with PS such as an aromatic ring, It is preferable to use a compound or composition containing both PMMA such as a highly polar functional group and a portion having high affinity.
Examples of the resin composition containing both PS and PMMA as structural units include a random copolymer of PS and PMMA, an alternating polymer of PS and PMMA (in which each monomer is alternately copolymerized), and the like.

In addition, as a composition including both a part having high affinity with PS and a part having high affinity with PMMA, for example, as a monomer, at least a monomer having an aromatic ring and a monomer having a polar substituent are polymerized. The resin composition obtained by making it contain is mentioned. As a monomer having an aromatic ring, one hydrogen atom is removed from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, or a phenanthryl group. And monomers having a heteroaryl group in which some of the carbon atoms constituting the ring of these groups are substituted with a heteroatom such as an oxygen atom, a sulfur atom or a nitrogen atom. Examples of the monomer having a highly polar substituent include a trimethoxysilyl group, a trichlorosilyl group, a carboxy group, a hydroxyl group, a cyano group, and a hydroxyalkyl group in which a part of hydrogen atoms of the alkyl group is substituted with a fluorine atom. The monomer which has is mentioned.
In addition, as a compound containing both a site having high affinity with PS and a site having high affinity with PMMA, a compound containing both an aryl group such as phenethyltrichlorosilane and a highly polar substituent, an alkylsilane compound, etc. Examples include compounds containing both an alkyl group and a highly polar substituent.
In the present invention, as will be described later, a pattern made of a photosensitive resin is formed on the neutralization film. Therefore, it is more preferable that the neutralization film has a polarity close to that of the photosensitive resin composition from the viewpoint of pattern adhesion.

[Step of forming a photosensitive resin film on the neutralized film, exposing and developing the pattern]
In the present invention, after performing the above-described step (a step of forming a neutralized film containing a surface treatment agent on the substrate), a photosensitive resin film is formed on the surface of the layer made of the neutralized film, and exposure is performed. And developing to form a pattern.

Specifically, first, a photosensitive resin composition described later is applied onto a neutralized film containing a surface treatment agent with a spinner or the like, and baking (post-apply bake (PAB)) treatment is performed at a temperature of 80 to 150 ° C., for example. A photosensitive resin film is formed by applying for 40 to 120 seconds, preferably 60 to 90 seconds under the conditions.
Next, the photosensitive resin film is exposed through a mask (mask pattern) in which a predetermined pattern is formed using an exposure apparatus such as an ArF exposure apparatus, an electron beam drawing apparatus, or an EUV exposure apparatus, or After performing selective exposure by drawing or the like by direct irradiation of an electron beam without passing through a mask pattern, baking (post-exposure baking (PEB)) treatment is preferably performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds. Is applied for 60-90 seconds.
Next, the photosensitive resin film is developed.

The development treatment is performed using an alkaline developer in the case of an alkali development process, and using a developer (organic developer) containing an organic solvent in the case of a solvent development process.
A rinsing treatment is preferably performed after the development treatment. The rinse treatment is preferably a water rinse using pure water in the case of an alkali development process, and is preferably a rinse solution containing an organic solvent in the case of a solvent development process.
In the case of a solvent development process, after the development process or the rinse process, a process of removing the developer or rinse liquid adhering to the pattern with a supercritical fluid may be performed.

  Drying is performed after development or rinsing. In the present invention, it is preferable to perform a baking process (post baking) after the development process. In this way, a photosensitive resin pattern can be obtained. In the present invention, the baking treatment after development is preferably performed at 180 ° C. or higher, more preferably performed at 190 ° C. or higher, and particularly preferably performed at 200 ° C. or higher.

In the present invention, a layer containing a block copolymer in which a plurality of types of polymers are bonded so as to cover a pattern and a neutralized film, which will be described later, by performing baking after development at a high temperature of, for example, 180 ° C. or higher. In the step of forming, it is considered that the photosensitive resin pattern can be given resistance to the solvent of the layer containing the block copolymer.
By imparting resistance to the solvent of the layer containing the block copolymer to the photosensitive resin pattern, it becomes possible to apply the block copolymer to the upper part of the photosensitive resin pattern. Further, the block copolymer can be applied to the photosensitive resin pattern. It is considered that phase separation is possible.
Moreover, the photosensitive resin pattern flows moderately by this high temperature baking process. As a result, the height and shape of the photosensitive resin pattern 3 to be described later from the substrate surface (or neutralized film surface) are optimized, and a block copolymer phase separation structure is formed on the photosensitive resin pattern 3. I think it can be done.

The wavelength used for exposure is not particularly limited, and ArF excimer laser, KrF excimer laser, F ₂ excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-ray, soft X-ray, etc. Can be done using radiation. The photosensitive resin composition is highly useful for KrF excimer laser, ArF excimer laser, EB or EUV.

The exposure method of the photosensitive resin film may be normal exposure (dry exposure) performed in an inert gas such as air or nitrogen, or may be immersion exposure (Liquid Immersion Lithography).
In immersion exposure, the space between the photosensitive resin film and the lowermost lens of the exposure apparatus is previously filled with a solvent (immersion medium) having a refractive index larger than that of air, and exposure is performed in this state (immersion exposure). It is the exposure method which performs.
As the immersion medium, a solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the exposed photosensitive resin film is preferable. The refractive index of such a solvent is not particularly limited as long as it is within the above range.
Examples of the solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the photosensitive resin film include water, a fluorine-based inert liquid, a silicon-based solvent, and a hydrocarbon-based solvent. .
Specific examples of the fluorine-based inert liquid include a fluorine-based compound such as C ₃ HCl ₂ F ₅ , C ₄ F ₉ OCH ₃ , C ₄ F ₉ OC ₂ H ₅ , and C ₅ H ₃ F ₇ as a main component. Examples thereof include liquids, and those having a boiling point of 70 to 180 ° C are preferable, and those having a boiling point of 80 to 160 ° C are more preferable. It is preferable that the fluorine-based inert liquid has a boiling point in the above range since the medium used for immersion can be removed by a simple method after the exposure is completed.
As the fluorine-based inert liquid, a perfluoroalkyl compound in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly preferable. Specific examples of the perfluoroalkyl compound include a perfluoroalkyl ether compound and a perfluoroalkylamine compound.
More specifically, examples of the perfluoroalkyl ether compound include perfluoro (2-butyl-tetrahydrofuran) (boiling point: 102 ° C.). Examples of the perfluoroalkylamine compound include perfluorotributylamine ( Boiling point of 174 ° C.).
As the immersion medium, water is preferably used from the viewpoints of cost, safety, environmental problems, versatility, and the like.

Examples of the alkali developer used for the development treatment in the alkali development process include a 0.1 to 10% by mass tetramethylammonium hydroxide (TMAH) aqueous solution.
The organic solvent contained in the organic developer used in the development process in the solvent development process is not particularly limited as long as it can dissolve the component (A) (component (A) before exposure). It can be selected as appropriate. Specifically, polar solvents such as ketone solvents, ester solvents, alcohol solvents, amide solvents, ether solvents, and hydrocarbon solvents can be used.
A known additive can be blended in the organic developer as required. Examples of the additive include a surfactant. The surfactant is not particularly limited. For example, ionic or nonionic fluorine-based and / or silicon-based surfactants can be used.
When the surfactant is blended, the blending amount is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and 0.01 to 0. 5 mass% is more preferable.

  The development process can be performed by a known development method. For example, a method in which a support is immersed in a developer for a certain period of time (dip method), a developer is raised on the surface of the support by surface tension, and is left for a certain period of time. (Paddle method), spraying developer on the surface of the support (spray method), coating the developer while scanning the developer coating nozzle at a constant speed on the support rotating at a constant speed The method to continue (dynamic dispensing method) etc. are mentioned.

  The rinse treatment (washing treatment) using the rinse liquid can be performed by a known rinse method. Examples of the method include a method of continuously applying a rinsing liquid on a support rotating at a constant speed (rotary coating method), a method of immersing the support in a rinsing liquid for a predetermined time (dip method), and the surface of the support. And a method of spraying a rinse liquid (spray method).

The height of the photosensitive resin pattern 3 from the substrate surface (or neutralized film surface) is appropriately determined depending on the film thickness of the photosensitive resin film formed by applying the photosensitive resin composition for forming the photosensitive resin pattern. It is preferable to adjust.
In the present invention, the height of the photosensitive resin pattern 3 from the substrate surface (or neutralized film surface) is preferably less than 22 nm, more preferably 20 nm or less, and 15 nm or less. Particularly preferred.
In the present invention, by setting the height of the photosensitive resin pattern 3 in the above range, the photosensitive resin pattern 3 can be completely covered with a layer 4 containing a block copolymer described later, and the layer 4 containing a block copolymer. Since the thickness of the film becomes suitable for forming a desired phase separation structure on the neutralized film 2 and the photosensitive resin pattern 3, not only the neutralized film but also the photosensitive resin It is considered that a phase-separated structure of the block copolymer can be formed on the pattern 3 as well.

  The photosensitive resin composition for forming the photosensitive resin pattern 3 is a photosensitive resin composition generally used for forming a photosensitive resin pattern or a modification thereof, and any polymer constituting a block copolymer. Those having affinity can be appropriately selected and used. Examples of the photosensitive resin composition include a photosensitive resin composition that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid. Details of the photosensitive resin composition will be described later.

[Step of forming a layer containing a block copolymer in which a plurality of types of polymers are bonded so as to cover the pattern and the neutralized film on the pattern]
In the present invention, after performing the above-described steps (a step of forming a photosensitive resin film on the neutralized film, exposing and developing the pattern to form a pattern), the pattern 3 and the medium are formed on the pattern 3. A layer 4 including a block copolymer to which a plurality of types of polymers are bonded is formed so as to cover the activated film 2.

Specifically, a block copolymer dissolved in a suitable organic solvent is applied so as to cover the photosensitive resin pattern 3 and the neutralized film 2 using a spinner or the like.
The organic solvent for dissolving the block copolymer will be described later.

The thickness of the layer 4 containing the block copolymer formed on the substrate surface depends on the molecular weight (polymer period) of the block copolymer and is generally applied in the range of 0.5 to 4.0 times the polymer period.
In the present invention, the thickness of the layer 4 containing the block copolymer may be sufficient to cover the photosensitive resin pattern 3 and cause phase separation, and the lower limit of the thickness is not particularly limited. However, in consideration of the strength of the nanostructure, the uniformity of the substrate on which the nanostructure is formed, etc., it is preferably 3 nm or more, and more preferably 5 nm or more.
Further, the upper limit is not particularly limited, but is preferably in a range where the effect of the neutralized film can be obtained.

<Block copolymer>
Block copolymer In the present invention, the block copolymer is a polymer in which a plurality of partial constituent components (blocks) in which only structural units of the same kind are bonded. There may be two types of blocks constituting the block copolymer, or three or more types. In the present invention, the plural types of blocks constituting the block copolymer are not particularly limited as long as they are combinations in which phase separation occurs, but are preferably combinations of blocks that are incompatible with each other. Moreover, it is preferable that the phase which consists of at least 1 type block in the multiple types of block which comprises a block copolymer is a combination which can be selectively removed easily rather than the phase which consists of other types of block.

Examples of block copolymers include:
A block copolymer in which a block of structural units derived from styrene or a derivative thereof and a block of structural units derived from an (α-substituted) acrylate ester are combined;
A block copolymer obtained by combining a block of a structural unit derived from styrene or a derivative thereof and a block of a structural unit derived from siloxane or a derivative thereof;
-A block copolymer in which a block of a structural unit derived from an alkylene oxide and a block of a structural unit derived from an (α-substituted) acrylate ester are combined.

The structural unit derived from styrene or a derivative thereof and the structural unit derived from an (α-substituted) acrylate ester are the same as described above.
Examples of the siloxane derivative include dimethylsiloxane, diethylsiloxane, diphenylsiloxane, methylphenylsiloxane, and the like.
Examples of the alkylene oxide include ethylene oxide, propylene oxide, isopropylene oxide, and butylene oxide.

Among these, as the block copolymer, it is preferable to use a block copolymer obtained by bonding a block of a structural unit derived from styrene or a derivative thereof and a block of a structural unit derived from (meth) acrylate.
Specifically, polystyrene-polymethyl methacrylate (PS-PMMA) block copolymer, polystyrene-polyethyl methacrylate block copolymer, polystyrene- (poly-t-butyl methacrylate) block copolymer, polystyrene-polymethacrylic acid block copolymer, polystyrene-poly. Examples thereof include a methyl acrylate block copolymer, a polystyrene-polyethyl acrylate block copolymer, a polystyrene- (poly-t-butyl acrylate) block copolymer, a polystyrene-polyacrylic acid block copolymer, and it is particularly preferable to use a PS-PMMA block copolymer. .

The mass average molecular weight (Mw) (polystyrene conversion standard by gel permeation chromatography) of each polymer constituting the block copolymer is not particularly limited as long as it is a size capable of causing phase separation. To 50,000,000 are preferable, 5,000 to 400,000 are more preferable, and 5,000 to 300,000 are more preferable.
Further, the dispersity (Mw / Mn) of the block copolymer is preferably 1.0 to 3.0, more preferably 1.0 to 1.5, and still more preferably 1.0 to 1.2. In addition, Mn shows a number average molecular weight.

  In addition to the block copolymer described above, the composition containing the block copolymer may further contain, if desired, miscible additives, for example, an additional resin for improving the performance of the layer made of the neutralized film, and coatability. A surfactant, a dissolution inhibitor, a plasticizer, a stabilizer, a colorant, an antihalation agent, a dye, a sensitizer, a base proliferating agent, a basic compound, and the like can be added and contained as appropriate.

-Organic solvent The composition containing a block copolymer can be prepared by dissolving the block copolymer in an organic solvent. Any organic solvent may be used as long as it can dissolve each component to be used to form a uniform solution. Conventionally, an arbitrary solvent can be selected from among known solvents for resin-based film compositions. One or more types can be appropriately selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone, cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, and 2-heptanone; Monohydric alcohols; compounds having an ester bond, such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, dipropylene glycol monoacetate, monomethyl ether, monoethyl of the polyhydric alcohols or compound having the ester bond Ether alkyl such as ether, monopropyl ether, monobutyl ether or monophenyl ether Derivatives of polyhydric alcohols such as compounds having a propylene glycol monomethyl ether acetate (PGMEA) or propylene glycol monomethyl ether (PGME) among these]; cyclic ethers such as dioxane, methyl lactate, Esters such as ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate; anisole, ethyl benzyl ether, cresyl methyl ether, diphenyl ether, Aromatic organics such as dibenzyl ether, phenetol, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene, mesitylene A solvent etc. can be mentioned.
These organic solvents may be used independently and may be used as 2 or more types of mixed solvents.
Among these, propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), cyclohexanone, and EL are preferable.
Moreover, the mixed solvent which mixed PGMEA and the polar solvent is also preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA and the polar solvent, preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. It is preferable to be within the range. For example, when EL is blended as a polar solvent, the mass ratio of PGMEA: EL is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3. Further, when PGME and cyclohexanone are blended as polar solvents, the mass ratio of PGMEA: (PGME + cyclohexanone) is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2, and even more preferably 3. : 7 to 7: 3.

In addition, as the organic solvent in the composition containing the block copolymer, PGMEA, EL, or a mixed solvent of PGMEA and a polar solvent and a mixed solvent of γ-butyrolactone are also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
The amount of the organic solvent used in the composition containing the block copolymer is not particularly limited, and can be appropriately set according to the coating film thickness at a coatable concentration. Is used in such a manner that the solid content concentration is 0.2 to 70% by mass, preferably 0.2 to 50% by mass.

In the following, among the blocks constituting the block copolymer, after the blocks that are not selectively removed in optional step P _A block, the block to be selectively removed as P _B block. For example, after phase-separating a layer containing PS-PMMA block copolymer, a phase composed of PMMA is selectively removed by performing oxygen plasma treatment, hydrogen plasma treatment, or the like on the layer. In this case, PS is a block _{P A,} PMMA is _{P B} block.

In the present invention, phase is selectively removed (i.e., P _B of blocks phase 4a) shape and size of the component ratio or the blocks constituting the block copolymer is defined by the molecular weight of the block copolymer. For example, by a relatively small component ratio per volume of the block P _B occupied in the block copolymer, forming a cylindrical structure phase 4a made of block P _B into phase 13b consisting of P _A block is present in the cylindrical Can be made. On the other hand, by the component ratio per volume of the block P _B and P _A block occupied in the block copolymer to the same extent, and the phase 4a of phase 4b and P _B block consisting of block P _A stacked alternately A lamellar structure can be formed. In addition, the size of each phase can be increased by increasing the molecular weight of the block copolymer.

[Step of phase-separating the layer containing the block copolymer on the pattern and the neutralized film]
In the present invention, after the above step (a step of forming a layer containing a block copolymer in which a plurality of types of polymers are bonded so as to cover the pattern and the neutralized film on the pattern), the pattern 3 and the neutralized film 2, the layer 4 containing the block copolymer is phase separated.

The phase separation of the layer 4 containing the block copolymer is performed after the layer 4 containing the block copolymer is formed, thereby forming a phase separation structure. The temperature of the heat treatment is preferably higher than the glass transition temperature of the layer containing the block copolymer to be used and lower than the thermal decomposition temperature. For example, when the block copolymer is PS-PMMA (Mw: 18k-18k), heat treatment is preferably performed at 160 to 270 ° C. for 30 to 3600 seconds.
The heat treatment is preferably performed in a gas having low reactivity such as nitrogen.

In the present invention, a structure including a phase separation structure in which the layer 4 containing a block copolymer is phase-separated into a phase 4a and a phase 4b as shown in FIG. 1 can be obtained by the heat treatment.
In the present invention, a phase separation structure can be formed on the photosensitive resin pattern 3 and the neutralization film 2 as shown in FIG.

In the present invention, a structure including a phase separation structure along the direction of the photosensitive resin pattern can be obtained through the above-described steps. That is, it is considered that the orientation of the phase separation structure can be controlled by the present invention.
In graphoepitaxy in which the orientation of the phase separation pattern is controlled by a physical guide, the phase separation structure is formed between the guides as shown in FIG. Although it cannot be formed, in the present invention, since a phase separation structure can be formed also on the photosensitive resin pattern, a desired phase separation structure can be obtained.

<Optional process>
In the present invention, a plurality of types of blocks constituting the block copolymer among the layers containing the block copolymer after the step (step of phase-separating the layer containing the block copolymer on the pattern and the neutralized film) A pattern may be formed by selectively removing the phase 4a composed of at least one of the blocks.
Specifically, the phase of the layer containing the block copolymer on a substrate after the separation structure was formed, selectively removing at least a portion of the block phase in consisting of block P _B (low molecular weight) to Thus, a method of forming a pattern can be mentioned. By pre selectively removing portions of the block P _B, results enhanced dissolution in a developer, tends to selectively remove than the phase 4b the phase 4a made of block P _B is formed of a block P _A .

Such selective removal process does not affect relative block P _A, if a process capable of decomposing and removing the block P _B, is not particularly limited, the technique used for the removal of the resin film from within, according to the type of block P _a and P _B block can be performed appropriately selected. Also, when the pre-neutralization film is formed on the substrate surface, the neutralization film is also removed as well as phase consisting block P _B. Examples of such removal treatment include oxygen plasma treatment, ozone treatment, UV irradiation treatment, thermal decomposition treatment, and chemical decomposition treatment.

  The substrate on which the pattern 4b is formed by phase separation of the block copolymer layer as described above can be used as it is, but the shape of the polymer nanostructure on the substrate is changed by further heat treatment. You can also The temperature of the heat treatment is preferably higher than the glass transition temperature of the block copolymer used and lower than the thermal decomposition temperature. The heat treatment is preferably performed in a gas having low reactivity such as nitrogen.

<Photosensitive resin composition>
In the present invention, the photosensitive resin composition is a photosensitive resin composition that generates an acid upon exposure and changes its solubility in the developer by the action of the acid, and its solubility in the developer changes by the action of the acid. The base material component (A) (hereinafter also referred to as “component (A)”) is preferably contained.
When a photosensitive resin film is formed using such a photosensitive resin composition and selective exposure is performed on the photosensitive resin film, an acid is generated in the exposed portion, and the action of the acid causes the component (A). While the solubility in the developer changes, the solubility of the component (A) in the developer does not change in the unexposed area, so a difference in solubility in the developer occurs between the exposed area and the unexposed area. Therefore, when the photosensitive resin film is developed, when the photosensitive resin composition is positive, the exposed portion is dissolved and removed to form a positive photosensitive resin pattern, and the photosensitive resin composition is negative. In this case, the unexposed portion is dissolved and removed to form a negative photosensitive resin pattern.
In the present specification, a photosensitive resin composition in which an exposed portion is dissolved and removed to form a positive photosensitive resin pattern is referred to as a positive photosensitive resin composition, and a negative photosensitive resin in which an unexposed portion is dissolved and removed. The photosensitive resin composition that forms the resin pattern is referred to as a negative photosensitive resin composition.
In the present invention, the photosensitive resin composition may be a positive photosensitive resin composition or a negative photosensitive resin composition.
In the present invention, the photosensitive resin composition may be used for an alkali development process using an alkali developer for the development processing at the time of forming the photosensitive resin pattern. May be used for a solvent developing process using a system developing solution).

In the present invention, the photosensitive resin composition has an acid generating ability to generate an acid upon exposure. The component (A) may generate an acid upon exposure, and is blended separately from the component (A). The additive component may generate an acid upon exposure.
Specifically, in the present invention, the photosensitive resin composition is
(1) It may contain an acid generator component (B) that generates an acid upon exposure (hereinafter referred to as “component (B)”);
(2) The component (A) may be a component that generates an acid upon exposure;
(3) The component (A) is a component that generates an acid upon exposure, and may further contain a component (B).
That is, in the case of the above (2) and (3), the component (A) is a “base material component that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid”. When the component (A) is a base material component that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid, the component (A1) described later generates an acid upon exposure, and A polymer compound whose solubility in a developing solution is changed by the action of an acid is preferable. As such a polymer compound, a resin having a structural unit that generates an acid upon exposure can be used. A well-known thing can be used as a structural unit which generate | occur | produces an acid by exposure.
In the present invention, the photosensitive resin composition is particularly preferably the case (1).

<(A) component>
In the present invention, the “base component” is an organic compound having a film forming ability, and preferably an organic compound having a molecular weight of 500 or more is used. When the molecular weight of the organic compound is 500 or more, the film forming ability is improved, and in addition, a nano-level photosensitive resin pattern is easily formed.
Organic compounds used as the base material component are roughly classified into non-polymers and polymers.
As the non-polymer, those having a molecular weight of 500 or more and less than 4000 are usually used. Hereinafter, the “low molecular compound” refers to a non-polymer having a molecular weight of 500 or more and less than 4000.
As the polymer, those having a molecular weight of 1000 or more are usually used. Hereinafter, the term “resin” refers to a polymer having a molecular weight of 1000 or more.
As the molecular weight of the polymer, a polystyrene-reduced weight average molecular weight by GPC (gel permeation chromatography) is used.
As the component (A), a resin may be used, a low molecular compound may be used, or these may be used in combination.
Component (A) may have increased solubility in a developer due to the action of an acid, or may decrease solubility in a developer due to the action of an acid.
In the present invention, the component (A) may generate an acid upon exposure.

In the present invention, the component (A) is a structural unit containing an acid-decomposable group whose polarity is increased by the action of an acid (hereinafter sometimes referred to as “structural unit (a1)”), a —SO ₂ -containing cyclic group. A structural unit derived from an acrylate ester containing a group (hereinafter sometimes referred to as “structural unit (a2)”), a structural unit containing a polar group-containing aliphatic hydrocarbon group (hereinafter referred to as “structural unit (a3)”) ), A structural unit containing a non-acid-dissociable cyclic group (hereinafter sometimes referred to as “structural unit (a4)”) and a lactone-containing cyclic group or a carbonate-containing cyclic group The polymer compound (A1) having a unit (hereinafter sometimes referred to as “structural unit (a5)”) is preferably included.

(Structural unit (a1))
The structural unit (a1) is a structural unit containing an acid-decomposable group whose polarity is increased by the action of an acid.
The “acid-decomposable group” is an acid-decomposable group that can cleave at least part of bonds in the structure of the acid-decomposable group by the action of an acid.
Examples of the acid-decomposable group whose polarity increases by the action of an acid include a group that decomposes by the action of an acid to generate a polar group.
Examples of the polar group include a carboxy group, a hydroxyl group, an amino group, a sulfo group (—SO ₃ H), and the like. Among these, a polar group containing —OH in the structure (hereinafter sometimes referred to as “OH-containing polar group”) is preferable, a carboxy group or a hydroxyl group is preferable, and a carboxy group is particularly preferable.
More specifically, examples of the acid-decomposable group include groups in which the polar group is protected with an acid-dissociable group (for example, a group in which a hydrogen atom of an OH-containing polar group is protected with an acid-dissociable group).
Here, “acid-dissociable group” means
(I) an acid-dissociable group capable of cleaving a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group by the action of an acid, or
(Ii) a group capable of cleaving a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group by further decarboxylation reaction after partial bond cleavage by the action of an acid ,
Both.
The acid-dissociable group constituting the acid-decomposable group must be a group having a lower polarity than the polar group generated by dissociation of the acid-dissociable group. Is dissociated, a polar group having a polarity higher than that of the acid dissociable group is generated to increase the polarity. As a result, the polarity of the entire component (A1) increases. As the polarity increases, the solubility in the developer changes relatively, and when the developer is an organic developer, the solubility decreases.

The acid-dissociable group is not particularly limited, and those that have been proposed as acid-dissociable groups for base resins for chemically amplified resists can be used.
Among the polar groups, examples of the acid dissociable group that protects a carboxy group or a hydroxyl group include an acid dissociable group represented by the following general formula (a1-r-1) (hereinafter referred to as “acetal acid dissociable for convenience”). Group ”).

［式中、Ｒａ’^１、Ｒａ’^２は水素原子またはアルキル基、Ｒａ’^３は炭化水素基、Ｒａ’^３は、Ｒａ’^１、Ｒａ’^２のいずれかと結合して環を形成してもよい。］

[Wherein, Ra ′ ¹ and Ra ′ ² are hydrogen atoms or alkyl groups, Ra ′ ³ is a hydrocarbon group, and Ra ′ ³ may be bonded to either Ra ′ ¹ or Ra ′ ² to form a ring. Good. ]

In formula (a1-r-1), Ra ′ ¹ and Ra ′ ² are exemplified as substituents that may be bonded to the α-position carbon atom in the description of the α-substituted acrylate ester described above. Examples thereof include the same as the alkyl group, preferably a methyl group or an ethyl group, and most preferably a methyl group.

The hydrocarbon group for Ra ′ ³ is preferably an alkyl group having 1 to 20 carbon atoms, more preferably an alkyl group having 1 to 10 carbon atoms; a linear or branched alkyl group is preferable, specifically , Methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group, 1,1-dimethylethyl group, 1,1-diethylpropyl group 2,2-dimethylpropyl group, 2,2, -dimethylbutyl group and the like can be mentioned.

When Ra ′ ³ is a cyclic hydrocarbon group, it may be aliphatic or aromatic, may be polycyclic, or may be monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group obtained by removing one hydrogen atom from a monocycloalkane. The monocycloalkane preferably has 3 to 8 carbon atoms, and specific examples include cyclopentane, cyclohexane and cyclooctane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing one hydrogen atom from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

In the case of an aromatic hydrocarbon group, specific examples of the aromatic ring contained include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, phenanthrene; carbon atoms constituting the aromatic hydrocarbon ring An aromatic heterocycle partially substituted with a heteroatom; and the like. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group is a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring (aryl group); a group in which one of the hydrogen atoms of the aryl group is substituted with an alkylene group (for example, Benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, arylalkyl group such as 2-naphthylethyl group); and the like. The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

When Ra ′ ³ is bonded to either Ra ′ ¹ or Ra ′ ² to form a ring, the cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

  Among the polar groups, examples of the acid dissociable group that protects the carboxy group include an acid dissociable group represented by the following general formula (a1-r-2) (the following formula (a1-r-2) Among the acid dissociable groups represented by), those composed of an alkyl group may hereinafter be referred to as “tertiary alkyl ester type acid dissociable groups” for convenience).

［式中、Ｒａ’^４〜Ｒａ’^６は炭化水素基であり、Ｒａ’^５、Ｒａ’^６は互いに結合して環を形成してもよい。］

[Wherein, Ra ′ ^{4 to} Ra ′ ⁶ are hydrocarbon groups, and Ra ′ ⁵ and Ra ′ ⁶ may be bonded to each other to form a ring. ]

As the hydrocarbon group for Ra ′ ^{4 to} Ra ′ ^6, the same groups as those described above for Ra ′ ³ can be mentioned. Ra ′ ⁴ is preferably an alkyl group having 1 to 5 carbon atoms. In the case where Ra ′ ⁵ and Ra ′ ⁶ are bonded to each other to form a ring, a group represented by general formula (a1-r2-1) shown below can be given.
On the other hand, when Ra ′ ^{4 to} Ra ′ ⁶ are not bonded to each other and are independent hydrocarbon groups, groups represented by the following general formula (a1-r2-2) are exemplified.

［式中、Ｒａ’^１０は炭素数１〜１０のアルキル基、Ｒａ’^１１はＲａ’^１０が結合した炭素原子と共に脂肪族環式基を形成する基、Ｒａ’^１２〜Ｒａ’^１４は、それぞれ独立に炭化水素基を示す。］

[Wherein, Ra ′ ¹⁰ is an alkyl group having 1 to ¹⁰ carbon atoms, Ra ′ ¹¹ is a group that forms an aliphatic cyclic group together with a carbon atom to which Ra ′ ¹⁰ is bonded, and Ra ′ ^{12 to} Ra ′ ¹⁴ are Independently represents a hydrocarbon group. ]

In formula (a1-r2-1), the alkyl group of the alkyl group having 1 to ¹⁰ carbon atoms of Ra ′ ¹⁰ is a linear or branched alkyl group of Ra ′ ³ in formula (a1-r-1) The groups mentioned as are preferred. Wherein (a1-r2-1), Ra 'aliphatic cyclic ^{group 11} is configured, Ra in formula (a1-r-1)' group listed as a cyclic alkyl group of ³ is preferred.

In formula (a1-r2-2), Ra ′ ¹² and Ra ′ ¹⁴ are preferably each independently an alkyl group having 1 to 10 carbon atoms, and the alkyl group is represented by Ra in formula (a1-r-1). 'The group mentioned as a linear or branched alkyl group of ³ is more preferable, It is more preferable that it is a C1-C5 linear alkyl group, It is especially preferable that it is a methyl group or an ethyl group .
In formula (a1-r2-2), Ra ′ ¹³ is a linear, branched or cyclic alkyl group exemplified as the hydrocarbon group for Ra ′ ³ in formula (a1-r-1). Is preferred. Among these, a group exemplified as the cyclic alkyl group for Ra ′ ³ is more preferable.

  Specific examples of the formula (a1-r2-1) are given below. In the following formula, “*” indicates a bond.

  Specific examples of the formula (a1-r2-2) are given below.

  Examples of the acid dissociable group for protecting the hydroxyl group among the polar groups include, for example, an acid dissociable group represented by the following general formula (a1-r-3) (hereinafter referred to as “tertiary alkyloxycarbonyl acid for convenience”). Sometimes referred to as a “dissociable group”).

［式中、Ｒａ’^７〜Ｒａ’^９はアルキル基を示す。］

[Wherein, Ra ′ ^{7 to} Ra ′ ⁹ represent an alkyl group. ]

In formula (a1-r-3), Ra ′ ^{7 to} Ra ′ ⁹ are preferably an alkyl group having 1 to 5 carbon atoms, and more preferably 1 to 3 groups.
Moreover, it is preferable that the total carbon number of each alkyl group is 3-7, it is more preferable that it is 3-5, and it is most preferable that it is 3-4.

  The structural unit (a1) is a structural unit derived from an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position may be substituted with a substituent, and an acid whose polarity is increased by the action of an acid. A structural unit containing a decomposable group; a structural unit in which at least a part of hydrogen atoms in the hydroxyl group of a structural unit derived from hydroxystyrene or a hydroxystyrene derivative is protected by a substituent containing the acid-decomposable group; vinylbenzoic acid or Examples include a structural unit in which at least a part of hydrogen atoms in —C (═O) —OH of a structural unit derived from a vinylbenzoic acid derivative is protected by a substituent containing the acid-decomposable group.

Among the above, the structural unit (a1) is preferably a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent.
As the structural unit (a1), structural units represented by general formula (a1-1) or (a1-2) shown below are preferred.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基である。Ｖａ^１はエーテル結合、ウレタン結合、又はアミド結合を有していてもよい２価の炭化水素基であり、ｎ_ａ１は０〜２であり、
Ｒａ^１は上記式（ａ１−ｒ−１）〜（ａ１−ｒ−２）で表される酸解離性基である。
Ｗａ^１はｎ_ａ２＋１価の炭化水素基であり、ｎ_ａ２は１〜３であり、
Ｒａ^２は上記式（ａ１−ｒ−１）または（ａ１−ｒ−３）で表される酸解離性基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. Va ¹ is a divalent hydrocarbon group which may have an ether bond, a urethane bond, or an amide bond, _na1 is 0 to 2,
Ra ¹ is an acid dissociable group represented by the above formulas (a1-r-1) to (a1-r-2).
Wa ¹ is n _a2 +1 valent hydrocarbon group, n _a2 is 1 to 3,
Ra ² is an acid dissociable group represented by the above formula (a1-r-1) or (a1-r-3). ]

In the general formula (a1-1), the alkyl group having 1 to 5 carbon atoms is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, specifically, a methyl group, an ethyl group, Examples include propyl group, isopropyl group, n-butyl group, isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like. The halogenated alkyl group having 1 to 5 carbon atoms is a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and is most preferably a hydrogen atom or a methyl group in terms of industrial availability.
The hydrocarbon group for Va ¹ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity. The aliphatic hydrocarbon group as a divalent hydrocarbon group in Va ¹ may be saturated or unsaturated, and is usually preferably saturated.
More specific examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like.
Examples of Va ¹ include those in which the divalent hydrocarbon group is bonded through an ether bond, a urethane bond, or an amide bond.

The linear or branched aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, more preferably 1 to 4, and most preferably 1 to 3.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

Examples of the aliphatic hydrocarbon group containing a ring in the structure include an alicyclic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and an alicyclic hydrocarbon group that is linear or branched. Examples thereof include a group bonded to the end of a chain aliphatic hydrocarbon group and a group in which an alicyclic hydrocarbon group is interposed in the middle of a linear or branched aliphatic hydrocarbon group. Examples of the linear or branched aliphatic hydrocarbon group include those described above.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a polycycloalkane, and the polycycloalkane preferably has 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring.
The aromatic hydrocarbon group as the divalent hydrocarbon group in Va ¹ preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, still more preferably 5 to 20 carbon atoms, and 6 to 6 carbon atoms. 15 is particularly preferable, and 6 to 10 is most preferable. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic ring possessed by the aromatic hydrocarbon group include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene; some of the carbon atoms constituting the aromatic hydrocarbon ring are heterogeneous. Aromatic heterocycles substituted with atoms; and the like. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group is a group obtained by removing two hydrogen atoms from the aromatic hydrocarbon ring (arylene group); a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring (aryl group) ) In which one of the hydrogen atoms is substituted with an alkylene group (for example, arylalkyl such as benzyl, phenethyl, 1-naphthylmethyl, 2-naphthylmethyl, 1-naphthylethyl, 2-naphthylethyl, etc.) Group in which one hydrogen atom is further removed from the aryl group in the group); and the like. The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

In the formula (a1-2), the n _a2 +1 valent hydrocarbon group in Wa ¹ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. The aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity, may be saturated or unsaturated, and is usually preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group including a ring in the structure, or a linear or branched aliphatic hydrocarbon group. It includes a group formed by combining an aliphatic hydrocarbon group in the structure containing a ring, and specific examples thereof include the same groups as Va ¹ of the aforementioned formula (a1-1).
The n _a2 +1 valence is preferably 2 to 4, and more preferably 2 or 3.

  As the formula (a1-2), a structural unit represented by general formula (a1-2-01) shown below is particularly desirable.

In formula (a1-2-01), Ra ² is an acid dissociable group represented by the above formula (a1-r-1) or (a1-r-3). n _a2 is an integer of 1 to 3, preferably 1 or 2, and more preferably 1. c is an integer of 0 to 3, preferably 0 or 1, and more preferably 1. R is the same as described above.
Specific examples of the above formulas (a1-1) and (a1-2) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

  The proportion of the structural unit (a1) in the component (A) is preferably from 20 to 80 mol%, more preferably from 20 to 75 mol%, more preferably from 25 to 70 mol%, based on all structural units constituting the component (A). Is more preferable. By setting the lower limit value or more, lithography properties such as sensitivity, resolution, and LWR are also improved. Moreover, the balance with another structural unit can be taken by making it below an upper limit.

(Structural unit (a2))
The structural unit (a2) is a structural unit containing a —SO ₂ — containing cyclic group.
The —SO ₂ — containing cyclic group of the structural unit (a2) is effective for enhancing the adhesion of the photosensitive resin film to the substrate when the component (A1) is used for forming the photosensitive resin film. It is.
In the present invention, the component (A1) preferably has the structural unit (a2).
In addition, when the structural unit (a1) includes a —SO ₂ — containing cyclic group in the structure, the structural unit also corresponds to the structural unit (a2). It corresponds to a1) and does not correspond to the structural unit (a2).

  The structural unit (a2) is preferably a structural unit represented by the following general formula (a2-1).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基であり、Ｙａ^２１は単結合または２価の連結基であり、Ｌａ^２１は−Ｏ−、−ＣＯＯ−、−ＣＯＮ（Ｒ’）−、−ＯＣＯ−、−ＣＯＮＨＣＯ−又は−ＣＯＮＨＣＳ−であり、Ｒ’は水素原子またはメチル基を示す。ただしＬａ^２１が−Ｏ−の場合、Ｙａ^２１は−ＣＯ−にはならない。Ｒａ^２１は−ＳＯ_２−含有環式基である。］

[Wherein, R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, Ya ²¹ is a single bond or a divalent linking group, and La ²¹ is —O -, -COO-, -CON (R ')-, -OCO-, -CONHCO- or -CONHCS-, wherein R' represents a hydrogen atom or a methyl group. However, when La ²¹ is —O—, Ya ²¹ is not —CO—. Ra ²¹ is a —SO ₂ — containing cyclic group. ]

The divalent linking group of Ya ²¹ is not particularly limited, and preferred examples thereof include a divalent hydrocarbon group which may have a substituent and a divalent linking group containing a hetero atom.

(Divalent hydrocarbon group which may have a substituent)
The hydrocarbon group as the divalent linking group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.
An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated.
Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like. Specifically, the above-described formula (a1- The group illustrated by Va ¹ in 1) is mentioned.

  The linear or branched aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and a carbonyl group.

As the aliphatic hydrocarbon group containing a ring in the structure, a cyclic aliphatic hydrocarbon group which may contain a substituent containing a hetero atom in the ring structure (excluding two hydrogen atoms from the aliphatic hydrocarbon ring) Group), a group in which the cyclic aliphatic hydrocarbon group is bonded to the end of a linear or branched aliphatic hydrocarbon group, and the cyclic aliphatic hydrocarbon group is a linear or branched chain fatty acid. Group intervening in the middle of the group hydrocarbon group. Examples of the linear or branched aliphatic hydrocarbon group include those described above.
The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
Specific examples of the cyclic aliphatic hydrocarbon group include the groups exemplified for Va ¹ in the above formula (a1-1).
The cyclic aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and a carbonyl group.
The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as the substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.
In the cyclic aliphatic hydrocarbon group, a part of carbon atoms constituting the ring structure may be substituted with a substituent containing a hetero atom. As the substituent containing the hetero atom, —O—, —C (═O) —O—, —S—, —S (═O) ₂ —, and —S (═O) ₂ —O— are preferable.

Specific examples of the aromatic hydrocarbon group as the divalent hydrocarbon group include groups exemplified by Va ¹ in the above formula (a1-1).
In the aromatic hydrocarbon group, a hydrogen atom of the aromatic hydrocarbon group may be substituted with a substituent. For example, a hydrogen atom bonded to an aromatic ring in the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxyl group.
The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
Examples of the alkoxy group, the halogen atom and the halogenated alkyl group as the substituent include those exemplified as the substituent for substituting the hydrogen atom of the cyclic aliphatic hydrocarbon group.

(Divalent linking group containing a hetero atom)
The hetero atom in the divalent linking group containing a hetero atom is an atom other than a carbon atom and a hydrogen atom, and examples thereof include an oxygen atom, a nitrogen atom, a sulfur atom, and a halogen atom.

When Ya ²¹ is a divalent linking group containing a hetero atom, preferred examples of the linking group include —O—, —C (═O) —O—, —C (═O) —, and —O—C. (═O) —O—, —C (═O) —NH—, —NH—, —NH—C (═NH) — (H may be substituted with a substituent such as an alkyl group or an acyl group). _{.), - S -, -} S (= O) 2 -, - S (= O) 2 -O-, the formula ^{-Y 21 -O-Y 22 -,} - Y 21 -O -, - Y 21 - C (═O) —O—, —C (═O) —O—Y ²¹ , [Y ²¹ —C (═O) —O] _{m ′} —Y ²² — or —Y ²¹ —O—C (= O) a group represented by —Y ²² —, wherein Y ²¹ and Y ²² are each independently a divalent hydrocarbon group which may have a substituent, O is an oxygen atom, m 'is an integer of 0-3. ] Etc. are mentioned.
When the divalent linking group containing a hetero atom is —C (═O) —NH—, —NH—, —NH—C (═NH) —, H is a substituent such as an alkyl group or acyl. May be substituted. The substituent (alkyl group, acyl group, etc.) preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and particularly preferably 1 to 5 carbon atoms.
Formula ^{-Y 21 -O-Y 22 -,} - Y 21 -O -, - Y 21 -C (= O) -O -, - C (= O) -O-Y 21, - [Y 21 -C ( ═O) —O] _{m ′} —Y ²² — or —Y ²¹ —O—C (═O) —Y ²² —, wherein Y ²¹ and Y ²² each independently have a substituent. It is a good divalent hydrocarbon group. Examples of the divalent hydrocarbon group include those similar to the “divalent hydrocarbon group optionally having substituent (s)” mentioned in the description of the divalent linking group.
Y ²¹ is preferably a linear aliphatic hydrocarbon group, more preferably a linear alkylene group, still more preferably a linear alkylene group having 1 to 5 carbon atoms, and particularly preferably a methylene group or an ethylene group. preferable.
Y ²² is preferably a linear or branched aliphatic hydrocarbon group, and more preferably a methylene group, an ethylene group or an alkylmethylene group. The alkyl group in the alkylmethylene group is preferably a linear alkyl group having 1 to 5 carbon atoms, more preferably a linear alkyl group having 1 to 3 carbon atoms, and most preferably a methyl group.
In the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² —, m ′ is an integer of 0 to 3, preferably an integer of 0 to 2, Or 1 is more preferable, and 1 is particularly preferable. That is, the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² — is represented by the formula —Y ²¹ —C (═O) —O—Y ²² —. The group is particularly preferred. Among these, a group represented by the formula — (CH ₂ ) _{a ′} —C (═O) —O— (CH ₂ ) _{b ′} — is preferable. In the formula, a ′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, further preferably 1 or 2, and most preferably 1. b ′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, more preferably 1 or 2, and most preferably 1.

In the present invention, Ya ²¹ is a single bond, an ester bond [—C (═O) —O—], an ether bond (—O—), a linear or branched alkylene group, or a combination thereof. Preferably there is.

In the formula (a2-1), Ra ²¹ is a —SO ₂ — containing cyclic group.

The “—SO ₂ -containing cyclic group” refers to a cyclic group containing a ring containing —SO ₂ — in the ring skeleton, specifically, the sulfur atom (S) in —SO ₂ — is It is a cyclic group that forms part of the ring skeleton of the cyclic group. The ring containing —SO ₂ — in the ring skeleton is counted as the first ring, and when it is only the ring, it is a monocyclic group, and when it has another ring structure, it is a polycyclic group regardless of the structure. Called. The —SO ₂ — containing cyclic group may be monocyclic or polycyclic.
The —SO ₂ — containing cyclic group as the cyclic hydrocarbon group in R ¹ is particularly a cyclic group containing —O—SO ₂ — in its ring skeleton, that is, —O— in —O—SO ₂ —. -S- is preferably a cyclic group containing a sultone ring that forms part of the ring skeleton. More specifically, examples of the —SO ₂ -containing cyclic group include groups represented by the following general formulas (a5-r-1) to (a5-r-4).

［式中、Ｒａ’^５１はそれぞれ独立に水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり；Ｒ”は水素原子またはアルキル基であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり、ｎ’は０〜２の整数である。］

[Wherein, Ra ′ ⁵¹ independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group. Yes; R ″ is a hydrogen atom or an alkyl group; A ″ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, and n ′ is 0 to 2 Is an integer. ]

In the general formulas (a5-r-1) to (a5-r-4), A ″ is the same as A ″ in the general formulas (a2-r-1) to (a2-r-7). As the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in Ra ′ ⁵¹ , the above general formulas (a2-r-1) to (a2 The same as Ra ′ ²¹ in −r-7).

  Specific examples of groups represented by general formulas (a5-r-1) to (a5-r-4) are given below. “Ac” in the formula represents an acetyl group.

As the —SO ₂ — containing cyclic group, among the above, a group represented by the general formula (a5-r-1) is preferable, and the chemical formulas (r-sl-1-1) and (r-sl— It is more preferable to use at least one selected from the group consisting of groups represented by any one of 1-18), (r-sl-3-1) and (r-sl-4-1), The group represented by (r-sl-1-1) is most preferable.

The structural unit (a2) contained in the component (A1) may be one type or two or more types.
When the component (A1) has the structural unit (a2), the proportion of the structural unit (a2) is preferably 1 to 80 mol% with respect to the total of all the structural units constituting the component (A1). It is more preferably 5 to 70 mol%, further preferably 10 to 65 mol%, and particularly preferably 10 to 60 mol%. By making it the lower limit value or more, the effect of containing the structural unit (a2) can be sufficiently obtained, and by making it the upper limit value or less, it is possible to balance with other structural units, and various lithography characteristics and patterns Good shape.

(Structural unit (a3))
The structural unit (a3) is a structural unit containing a polar group-containing aliphatic hydrocarbon group (except for those corresponding to the structural units (a1) and (a2) described above).
It is considered that when the component (A1) has the structural unit (a3), the hydrophilicity of the component (A) is increased and the resolution is improved.
Examples of the polar group include a hydroxyl group, a cyano group, a carboxy group, and a hydroxyalkyl group in which a part of hydrogen atoms of an alkyl group is substituted with a fluorine atom. A hydroxyl group is particularly preferable.
Examples of the aliphatic hydrocarbon group include a linear or branched hydrocarbon group having 1 to 10 carbon atoms (preferably an alkylene group) and a cyclic aliphatic hydrocarbon group (cyclic group). The cyclic group may be a monocyclic group or a polycyclic group. For example, a resin for a resist composition for an ArF excimer laser can be appropriately selected from those proposed. The cyclic group is preferably a polycyclic group, and more preferably 7 to 30 carbon atoms.
Among them, a structural unit derived from an acrylate ester containing an aliphatic polycyclic group containing a hydroxyalkyl group in which a part of hydrogen atoms of a hydroxyl group, a cyano group, a carboxy group, or an alkyl group is substituted with a fluorine atom Is more preferable. Examples of the polycyclic group include groups in which two or more hydrogen atoms have been removed from bicycloalkane, tricycloalkane, tetracycloalkane and the like. Specific examples include groups in which two or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among these polycyclic groups, there are groups in which two or more hydrogen atoms have been removed from adamantane, groups in which two or more hydrogen atoms have been removed from norbornane, and groups in which two or more hydrogen atoms have been removed from tetracyclododecane. Industrially preferable.

The structural unit (a3) is not particularly limited as long as it contains a polar group-containing aliphatic hydrocarbon group, and any structural unit can be used.
The structural unit (a3) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, and includes a polar group-containing aliphatic hydrocarbon group A structural unit is preferred.
The structural unit (a3) is derived from a hydroxyethyl ester of acrylic acid when the hydrocarbon group in the polar group-containing aliphatic hydrocarbon group is a linear or branched hydrocarbon group having 1 to 10 carbon atoms. When the hydrocarbon group is a polycyclic group, the structural unit represented by the following formula (a3-1), the structural unit represented by the formula (a3-2), the formula ( The structural unit represented by a3-3) is preferred.

［式中、Ｒは前記と同じであり、ｊは１〜３の整数であり、ｋは１〜３の整数であり、ｔ’は１〜３の整数であり、ｌは１〜５の整数であり、ｓは１〜３の整数である。］

[Wherein, R is as defined above, j is an integer of 1 to 3, k is an integer of 1 to 3, t ′ is an integer of 1 to 3, and l is an integer of 1 to 5] And s is an integer of 1 to 3. ]

In formula (a3-1), j is preferably 1 or 2, and more preferably 1. When j is 2, it is preferable that the hydroxyl group is bonded to the 3rd and 5th positions of the adamantyl group. When j is 1, it is preferable that the hydroxyl group is bonded to the 3-position of the adamantyl group.
j is preferably 1, and it is particularly preferred that the hydroxyl group is bonded to the 3-position of the adamantyl group.

In formula (a3-2), k is preferably 1. The cyano group is preferably bonded to the 5th or 6th position of the norbornyl group.
In formula (a3-3), t ′ is preferably 1. l is preferably 1. s is preferably 1. In these, a 2-norbornyl group or a 3-norbornyl group is preferably bonded to the terminal of the carboxy group of acrylic acid. The fluorinated alkyl alcohol is preferably bonded to the 5th or 6th position of the norbornyl group.

As the structural unit (a3) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
In the component (A1), the proportion of the structural unit (a3) is preferably 5 to 50 mol%, more preferably 5 to 40 mol%, based on the total of all structural units constituting the resin component (A1). Preferably, 5 to 25 mol% is more preferable.
By setting the proportion of the structural unit (a3) to the lower limit value or more, the effect of including the structural unit (a3) can be sufficiently obtained, and by setting the proportion of the structural unit (a3) to the upper limit value or less, balance with other structural units can be obtained. It becomes easy.

(Structural unit (a4))
The structural unit (a4) is a structural unit containing an acid non-dissociable cyclic group. When the component (A1) has the structural unit (a4), the dry etching resistance of the formed photosensitive resin pattern is improved. Moreover, the hydrophobicity of (A1) component increases. The improvement in hydrophobicity is thought to contribute to the improvement in resolution, photosensitive resin pattern shape, etc., particularly in the case of organic solvent development.
The “acid non-dissociable cyclic group” in the structural unit (a4) means that when an acid is generated from the later-described component (B) by exposure, it is not dissociated even if the acid acts on the structural unit. The remaining cyclic group.
As the structural unit (a4), for example, a structural unit derived from an acrylate ester containing a non-acid-dissociable aliphatic cyclic group is preferable. Examples of the cyclic group include those similar to those exemplified for the structural unit (a1), for ArF excimer laser, for KrF excimer laser (preferably for ArF excimer laser), etc. A number of hitherto known materials can be used as the resin component of the resist composition.
In particular, at least one selected from a tricyclodecyl group, an adamantyl group, a tetracyclododecyl group, an isobornyl group, and a norbornyl group is preferable in terms of industrial availability. These polycyclic groups may have a linear or branched alkyl group having 1 to 5 carbon atoms as a substituent.
Specific examples of the structural unit (a4) include those having the structures of the following general formulas (a4-1) to (a4-7).

［式中、Ｒ^αは、水素原子、メチル基またはトリフルオロメチル基を示す。］

[Wherein, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group. ]

As the structural unit (a4) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
When the structural unit (a4) is contained in the component (A1), the proportion of the structural unit (a4) is preferably 1 to 30 mol% with respect to the total of all the structural units constituting the component (A1). More preferably, it is 10-20 mol%.

(Structural unit (a5))
The structural unit (a5) is a structural unit containing a lactone-containing cyclic group or a carbonate-containing cyclic group.
The lactone-containing cyclic group or carbonate-containing cyclic group of the structural unit (a5) is used to enhance the adhesion of the photosensitive resin film to the substrate when the component (A1) is used for forming the photosensitive resin film. It is effective.
In addition, when the structural unit (a1) includes a lactone-containing cyclic group or a carbonate-containing cyclic group in the structure, the structural unit also corresponds to the structural unit (a5). It corresponds to the structural unit (a1) and does not correspond to the structural unit (a5).

The structural unit (a5) is preferably a structural unit in which Ra ²¹ in the formula (a2-1) is a lactone-containing cyclic group or a carbonate-containing cyclic group.

The “lactone-containing cyclic group” refers to a cyclic group containing a ring (lactone ring) containing —O—C (═O) — in the ring skeleton. The lactone ring is counted as the first ring. When only the lactone ring is present, it is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The lactone-containing cyclic group may be a monocyclic group or a polycyclic group.
The lactone-containing cyclic group as the cyclic hydrocarbon group for R ¹ is not particularly limited, and any one can be used. Specific examples include groups represented by the following general formulas (a2-r-1) to (a2-r-7). Hereinafter, “*” represents a bond.

［式中、Ｒａ’^２１はそれぞれ独立に水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり；Ｒ”は水素原子またはアルキル基であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり、ｎ’は０〜２の整数であり、ｍ’は０または１である。］

[Wherein, Ra ′ ²¹ each independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group. Yes; R ″ is a hydrogen atom or an alkyl group; A ″ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, and n ′ is 0 to 2 And m ′ is 0 or 1. ]

In general formulas (a2-r-1) to (a2-r-7), A ″ represents an oxygen atom (—O—) or a sulfur atom (—S—), and may have 1 to 5 carbon atoms. The alkylene group having 1 to 5 carbon atoms in A ″ is preferably a linear or branched alkylene group, a methylene group, an ethylene group, an n-propylene group, An isopropylene group etc. are mentioned. When the alkylene group contains an oxygen atom or a sulfur atom, specific examples thereof include a group in which —O— or —S— is interposed between the terminal or carbon atoms of the alkylene group, such as —O—CH _{2. -, - CH 2 -O-CH} 2 -, - S-CH 2 -, - CH 2 -S-CH 2 - , and the like. A ″ is preferably an alkylene group having 1 to 5 carbon atoms or —O—, more preferably an alkylene group having 1 to 5 carbon atoms, and most preferably a methylene group. Ra ′ ²¹ independently represents an alkyl group or an alkoxy group. A group, a halogen atom, a halogenated alkyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group.
The alkyl group in ra ^'21, preferably an alkyl group having 1 to 5 carbon atoms.
The alkoxy group in the ra ^'21, preferably an alkoxy group having 1 to 6 carbon atoms.
The alkoxy group is preferably linear or branched. Specifically, groups of the the Ra 'group and an oxygen atom mentioned as the alkyl group in ²¹ (-O-) are linked and the like.
Examples of the halogen atom in Ra ′ ²¹ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
'Examples of the halogenated alkyl group for ^21, the Ra' Ra part or all of the hydrogen atoms of the alkyl group in ²¹ can be mentioned it has been substituted with the aforementioned halogen atoms. As the halogenated alkyl group, a fluorinated alkyl group is preferable, and a perfluoroalkyl group is particularly preferable.

  Specific examples of groups represented by general formulas (a2-r-1) to (a2-r-7) are given below.

The “carbonate-containing cyclic group” refers to a cyclic group containing a ring (carbonate ring) containing —O—C (═O) —O— in the ring skeleton. When the carbonate ring is counted as the first ring, the carbonate ring alone is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The carbonate-containing cyclic group may be a monocyclic group or a polycyclic group.
The carbonate ring-containing cyclic group as the cyclic hydrocarbon group for R ¹ is not particularly limited, and any one can be used. Specific examples include groups represented by the following general formulas (ax3-r-1) to (ax3-r-3).

［式中、Ｒａ’^ｘ３１はそれぞれ独立に水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり；Ｒ”は水素原子またはアルキル基であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子でありｑ’は０または１である。］

[ ^Wherein , Ra ′ ^x31 each independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group. Yes; R ″ is a hydrogen atom or an alkyl group; A ″ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, and q ′ is 0 or 1. is there. ]

In the general formulas (ax3-r-1) to (ax3-r-3), A ″ is the same as A ″ in the general formula (a2-r-1).
As the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in Ra ′ ³¹ , the above general formulas (a2-r-1) to ( a2-r-7) as in the same as those exemplified in the description of the Ra ^'21 of the like.

  Specific examples of groups represented by general formulas (ax3-r-1) to (ax3-r-3) are given below.

  Among them, the lactone-containing cyclic group is preferably a group represented by the general formula (a2-r-1) or (a2-r-2), and represented by the chemical formula (r-lc-1-1). Groups are more preferred.

The structural unit (a5) contained in the component (A1) may be one type or two or more types.
When the component (A1) has the structural unit (a5), the proportion of the structural unit (a5) is preferably 1 to 80 mol% with respect to the total of all the structural units constituting the component (A1). It is more preferably 5 to 70 mol%, further preferably 10 to 65 mol%, and particularly preferably 10 to 60 mol%. The effect by containing the structural unit (a5) can be sufficiently obtained by setting it to the lower limit value or more, and it can be balanced with other structural units by setting it to the upper limit value or less, and various kinds of DOF, CDU, etc. The lithography characteristics and pattern shape of the film are improved.

  The component (A1) is preferably a copolymer having any one of (a1), (a2), (a3), (a4) or (a5), the structural units (a1) and (a2), A copolymer having units (a1), (a2) and (a5) or structural units (a1), (a2), (a3) and (a5) is more preferred.

  In the present invention, the weight average molecular weight (Mw) of the component (A1) (polystyrene conversion standard by gel permeation chromatography) is not particularly limited, preferably 1000 to 50000, more preferably 1500 to 30000, 2000 ˜20,000 is most preferred. If it is below the upper limit of this range, it has sufficient solubility in a photosensitive resin solvent to be used as the photosensitive resin, and if it is above the lower limit of this range, it is resistant to dry etching and the cross section of the photosensitive resin pattern. Good shape.

As the component (A1), one type may be used alone, or two or more types may be used in combination.
The proportion of the component (A1) in the substrate component (A) is preferably 25% by mass or more, more preferably 50% by mass, further preferably 75% by mass, based on the total mass of the substrate component (A). It may be mass%. When the proportion is 25% by mass or more, the lithography properties are further improved.

In the photosensitive resin composition of the present invention, as the component (A), one type may be used alone, or two or more types may be used in combination.
In the photosensitive resin composition of the present invention, the content of the component (A) may be adjusted according to the thickness of the photosensitive resin film to be formed.

<Acid generator component; (B) component>
The photosensitive resin composition of this invention may contain the acid generator component (B) (henceforth (B) component) which generate | occur | produces an acid by exposure. The component (B) is not particularly limited, and those that have been proposed as acid generators for chemically amplified resists can be used.
Examples of such acid generators include onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators, bisalkyl or bisarylsulfonyldiazomethanes, and diazomethanes such as poly (bissulfonyl) diazomethanes. Examples include an acid generator, a nitrobenzyl sulfonate acid generator, an imino sulfonate acid generator, and a disulfone acid generator. Of these, it is preferable to use an onium salt acid generator.

  Examples of the onium salt-based acid generator include a compound represented by the following general formula (b-1) (hereinafter also referred to as “(b-1) component”) and a general formula (b-2). A compound (hereinafter also referred to as “(b-2) component”) or a compound represented by the general formula (b-3) (hereinafter also referred to as “(b-3) component”) can be used.

［式中、Ｒ^１０１、Ｒ^１０４〜Ｒ^１０８はそれぞれ独立に置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、または置換基を有していてもよい鎖状のアルケニル基である。Ｒ^１０４、Ｒ^１０５は、相互に結合して環を形成していてもよい。Ｒ^１０６〜Ｒ^１０７のいずれか２つは、相互に結合して環を形成していてもよい。Ｒ^１０２はフッ素原子または炭素数１〜５のフッ素化アルキル基である。Ｙ^１０１は単結合または酸素原子を含む２価の連結基である。Ｖ^１０１〜Ｖ^１０３はそれぞれ独立に単結合、アルキレン基、またはフッ素化アルキレン基である。Ｌ^１０１〜Ｌ^１０２はそれぞれ独立に単結合または酸素原子である。Ｌ^１０３〜Ｌ^１０５はそれぞれ独立に単結合、−ＣＯ−又は−ＳＯ_２−である。Ｍ’^ｍ＋はｍ価の有機カチオンである（前記式（ｂ１−１）の化合物におけるカチオンを除く）。］

[Wherein, R ¹⁰¹ and R ^{104 to} R ¹⁰⁸ each independently has a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. A chain alkenyl group which may be present. R ¹⁰⁴ and R ¹⁰⁵ may be bonded to each other to form a ring. Any two of R ^{106 to} R ¹⁰⁷ may be bonded to each other to form a ring. R ¹⁰² is a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. Y ¹⁰¹ is a single bond or a divalent linking group containing an oxygen atom. V ^{101 to} V ¹⁰³ are each independently a single bond, an alkylene group, or a fluorinated alkylene group. L ^{101 to} L ¹⁰² are each independently a single bond or an oxygen atom. L ^{103 to} L ¹⁰⁵ are each independently a single bond, —CO— or —SO ₂ —. M ′ ^{m +} is an m-valent organic cation (excluding the cation in the compound of the formula (b1-1)). ]

{Anion part}
-Anion moiety of component (b-1) In formula (b-1), R ¹⁰¹ represents a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, Alternatively, a chain alkenyl group which may have a substituent.

(Cyclic group which may have a substituent)
The cyclic group is preferably a cyclic hydrocarbon group, and the cyclic hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group.
The aromatic hydrocarbon group for R ¹⁰¹ is the aromatic hydrocarbon ring mentioned for the divalent aromatic hydrocarbon group for Va ¹ in the formula (a1-1), or an aromatic compound containing two or more aromatic rings. Examples include an aryl group in which one hydrogen atom is removed, and a phenyl group and a naphthyl group are preferable.
The cyclic aliphatic hydrocarbon group for R ¹⁰¹ is a group obtained by removing one hydrogen atom from the monocycloalkane or polycycloalkane mentioned as the divalent aliphatic hydrocarbon group for Va ¹ in the formula (a1-1). And an adamantyl group and a norbornyl group are preferable.
In addition, the cyclic hydrocarbon group in R ¹⁰¹ may contain a hetero atom such as a heterocycle, and is specifically represented by the general formulas (a2-r-1) to (a2-r-7). include-containing cyclic group, a heterocyclic group mentioned for other less - lactone-containing cyclic group, -SO ₂ respectively represented by the general formula (a5-r-1) ~ (a5-r-4) to be It is done.

Examples of the substituent in the cyclic hydrocarbon group of R ¹⁰¹ include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, and a nitro group.
The alkyl group as a substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as a substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as a substituent include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.
As the halogenated alkyl group as a substituent, a part or all of hydrogen atoms such as an alkyl group having 1 to 5 carbon atoms, for example, methyl group, ethyl group, propyl group, n-butyl group, tert-butyl group, and the like And a group substituted with a halogen atom.

(A chain alkyl group which may have a substituent)
The chain alkyl group for R ¹⁰¹ may be either linear or branched.
The linear alkyl group preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. Specifically, for example, methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decanyl group, undecyl group, dodecyl group, tridecyl group, isotridecyl group, tetradecyl group Group, pentadecyl group, hexadecyl group, isohexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, icosyl group, heicosyl group, docosyl group and the like.
The branched alkyl group preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10 carbon atoms. Specifically, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, Examples include 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like.

(Chain-like alkenyl group which may have a substituent)
The chain alkenyl group for R ¹⁰¹ may be either linear or branched, preferably has 2 to 10 carbon atoms, more preferably 2 to 5, still more preferably 2 to 4, more preferably 3 Is particularly preferred. Examples of the linear alkenyl group include a vinyl group, a propenyl group (allyl group), and a butynyl group. Examples of the branched alkenyl group include a 1-methylpropenyl group and a 2-methylpropenyl group.
Among the above, the chain alkenyl group is particularly preferably a propenyl group.

Examples of the substituent in the chain alkyl group or alkenyl group of R ¹⁰¹ include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an amino group, and the cyclic group in R ¹⁰¹ described above. Can be mentioned.

Among these, R ¹⁰¹ is preferably a cyclic group which may have a substituent, and more preferably a cyclic hydrocarbon group which may have a substituent. More specifically, a phenyl group, a naphthyl group, a group obtained by removing one or more hydrogen atoms from a polycycloalkane, and lactones represented by the above formulas (a2-r-1) to (a2-r-7), respectively. The containing cyclic group, the —SO ₂ -containing cyclic group represented by the general formulas (a5-r-1) to (a5-r-4), respectively, and the like are preferable.

In formula (b-1), Y ¹⁰¹ represents a single bond or a divalent linking group containing an oxygen atom.
When Y ¹⁰¹ is a divalent linking group containing an oxygen atom, Y ¹⁰¹ may contain an atom other than an oxygen atom. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms.
Examples of the divalent linking group containing an oxygen atom include an oxygen atom (ether bond: —O—), an ester bond (—C (═O) —O—), and an oxycarbonyl group (—O—C (═O). )-), Amide bond (—C (═O) —NH—), carbonyl group (—C (═O) —), carbonate bond (—O—C (═O) —O—), etc. A combination of a non-hydrocarbon oxygen atom-containing linking group and an alkylene group; and the like. A sulfonyl group (—SO ₂ —) may be further linked to the combination. Examples of the combination include linking groups represented by the following formulas (y-al-1) to (y-al-7), respectively.

［式中、Ｖ’^１０１は単結合または炭素数１〜５のアルキレン基であり、Ｖ’^１０２は炭素数１〜３０の２価の飽和炭化水素基である。］

[Wherein, V ′ ¹⁰¹ is a single bond or an alkylene group having 1 to 5 carbon atoms, and V ′ ¹⁰² is a divalent saturated hydrocarbon group having 1 to 30 carbon atoms. ]

The divalent saturated hydrocarbon group for V ′ ¹⁰² is preferably an alkylene group having 1 to 30 carbon atoms.

The alkylene group for V ′ ¹⁰¹ and V ′ ¹⁰² may be a linear alkylene group or a branched alkylene group, and a linear alkylene group is preferred.
Specific examples of the alkylene group in V ′ ¹⁰¹ and V ′ ¹⁰² include a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene Groups [—CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH - ₃₎ CH ₂ alkyl groups such as, trimethylene group (n- propylene _{group) [- CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 -, - CH 2 CH (CH 3) CH ₂ - and the like alkyl trimethylene group; tetramethylene _{[-CH 2 CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 CH 2 - alkyl tetramethylene group and the like; pentamethylene group _{[-CH 2 CH 2 CH 2 CH} 2 CH 2 -] , and the like.
Moreover, some methylene groups in the alkylene group in V ′ ¹⁰¹ or V ′ ¹⁰² may be substituted with a C 5-10 divalent aliphatic cyclic group. The aliphatic cyclic group is preferably a divalent group obtained by further removing one hydrogen atom from the cyclic aliphatic hydrocarbon group of Ra ′ ^{3 in} the formula (a1-r-1). 1,5-adamantylene group or 2,6-adamantylene group is more preferable.

Y ¹⁰¹ is preferably a divalent linking group containing an ester bond or an ether bond, and linking groups represented by the above formulas (y-al-1) to (y-al-5) are preferred.

In formula (b-1), V ¹⁰¹ represents a single bond, an alkylene group, or a fluorinated alkylene group. The alkylene group and fluorinated alkylene group for V ¹⁰¹ preferably have 1 to 4 carbon atoms. ^Examples of the fluorinated alkylene group for V ¹⁰¹ include groups in which some or all of the hydrogen atoms of the alkylene group for V ¹⁰¹ have been substituted with fluorine atoms. Among ^{them, V 101} is preferably a single bond, or a fluorinated alkylene group having 1 to 4 carbon atoms.

In formula (b-1), R ¹⁰² represents a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. R ¹⁰² is preferably a fluorine atom or a C 1-5 perfluoroalkyl group, and more preferably a fluorine atom.

As a specific example of the anion part of the component (b-1), for example,
When Y ¹⁰¹ is a single bond, fluorinated alkyl sulfonate anions such as trifluoromethane sulfonate anion and perfluorobutane sulfonate anion can be mentioned; when Y ¹⁰¹ is a divalent linking group containing an oxygen atom, the following formula (an An anion represented by any one of (-1) to (an-3).

［式中、Ｒ”^１０１は、置換基を有していてもよい脂肪族環式基、前記式（ｒ−ｈｒ−１）〜（ｒ−ｈｒ−６）でそれぞれ表される基、又は置換基を有していてもよい鎖状のアルキル基であり；Ｒ”^１０２は、置換基を有していてもよい脂肪族環式基、前記式（ａ２−ｒ−１）〜（ａ２−ｒ−７）でそれぞれ表されるラクトン含有環式基、又は前記一般式（ａ５−ｒ−１）〜（ａ５−ｒ−４）でそれぞれ表される−ＳＯ_２−含有環式基であり；Ｒ”^１０３は、置換基を有していてもよい芳香族環式基、置換基を有していてもよい脂肪族環式基、又は置換基を有していてもよい鎖状のアルケニル基であり；Ｖ”^１０１は、フッ素化アルキレン基であり；Ｌ”^１０１は、−Ｃ（＝Ｏ）−又は−ＳＯ_２−であり；ｖ”はそれぞれ独立に０〜３の整数であり、ｑ”はそれぞれ独立に１〜２０の整数であり、ｎ”は０または１である。］

[Wherein R ″ ¹⁰¹ represents an aliphatic cyclic group which may have a substituent, a group represented by each of the above formulas (r-hr-1) to (r-hr-6), or a substituent. A chain-like alkyl group which may have a group; R ″ ¹⁰² represents an aliphatic cyclic group which may have a substituent, the above formulas (a2-r-1) to (a2-r); lactone-containing cyclic group represented respectively by -7), or the formula (a5-r-1) ~ (a5-r-4) with -SO ₂ respectively represented - be-containing cyclic group; R ¹⁰³ is an aromatic cyclic group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a chain alkenyl group which may have a substituent. ^{There; V "101} is an fluorinated alkylene ^{group; L" 101} is, -C (= O) - or -SO ₂ - a and; v "0 to 3 are each independently Is an integer, q "are each independently an integer of 1 to 20, n" is 0 or 1. ]

The aliphatic cyclic group which may have a substituent of R ″ ¹⁰¹ , R ″ ¹⁰² and R ″ ¹⁰³ is preferably the group exemplified as the cyclic aliphatic hydrocarbon group in R ¹⁰¹ . Examples of the substituent include the same substituents that may be substituted for the cyclic aliphatic hydrocarbon group in R ¹⁰¹ .

The aromatic cyclic group which may have a substituent in R ″ ¹⁰³ is preferably the group exemplified as the aromatic hydrocarbon group in the cyclic hydrocarbon group in R ¹⁰¹ . , R ¹⁰¹ and the same substituents that may be substituted for the aromatic hydrocarbon group.

The chain alkyl group which may have a substituent in R ″ ¹⁰¹ is preferably the group exemplified as the chain alkyl group in R ^101. The chain in R ″ ¹⁰³ has a substituent. The good chain alkenyl group is preferably the group exemplified as the chain alkenyl group in R ¹⁰¹ . V ″ ¹⁰¹ is preferably a fluorinated alkylene group having 1 to 3 carbon atoms, and particularly preferably —CF ₂ —, —CF ₂ CF ₂ —, —CHFCF ₂ —, —CF (CF ₃ ) CF ₂ —. , —CH (CF ₃ ) CF ₂ —.

-Anion part of component (b-2) In formula (b-2), R ¹⁰⁴ and R ¹⁰⁵ may each independently have a cyclic group which may have a substituent or a substituent. Examples thereof include a good chain alkyl group or a chain alkenyl group which may have a substituent, and examples thereof include the same as those described above for R ¹⁰¹ in formula (b-1). However, R ¹⁰⁴ and R ¹⁰⁵ may be bonded to each other to form a ring.
R ¹⁰⁴ and R ¹⁰⁵ are preferably a chain alkyl group which may have a substituent, and are a linear or branched alkyl group, or a linear or branched fluorinated alkyl group. It is more preferable.
The chain alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 7 carbon atoms, and still more preferably 1 to 3 carbon atoms. The number of carbon atoms of the chain alkyl group of R ¹⁰⁴ and R ¹⁰⁵ is preferably as small as possible within the range of the above carbon number for reasons such as good solubility in a photosensitive resin solvent. In addition, in the chain alkyl group of R ¹⁰⁴ and R ^105, the greater the number of hydrogen atoms substituted with fluorine atoms, the stronger the acid strength, and against high-energy light and electron beams of 200 nm or less Since transparency improves, it is preferable. The proportion of fluorine atoms in the chain alkyl group, that is, the fluorination rate is preferably 70 to 100%, more preferably 90 to 100%, and most preferably all hydrogen atoms are substituted with fluorine atoms. Perfluoroalkyl group.
In formula (b-2), V ¹⁰² and V ¹⁰³ are each independently a single bond, an alkylene group, or a fluorinated alkylene group, and each of them is the same as V ¹⁰¹ in formula (b-1). Can be mentioned.
In formula (b-2), L ^{101 to} L ¹⁰² each independently represents a single bond or an oxygen atom.

-Anion part of (b-3) component In formula (b-3), R < ¹⁰⁶ > -R < ¹⁰⁸ > may have the cyclic group which may have a substituent, and a substituent each independently. Examples thereof include a good chain alkyl group or a chain alkenyl group which may have a substituent, and examples thereof include the same as those described above for R ¹⁰¹ in formula (b-1).
L ^{103 to} L ¹⁰⁵ are each independently a single bond, —CO— or —SO ₂ —.

{Cation part}
In the formulas (b-1), (b-2) and (b-3), M ′ ^{m +} is an m-valent organic cation other than the cation in the compound of the formula (b1-1), and in particular, a sulfonium cation Or it is preferable that it is an iodonium cation, and the cation respectively represented by the following general formula (ca-1)-(ca-4) is especially preferable.

［式中、Ｒ^２０１〜Ｒ^２０７、およびＲ^２１１〜Ｒ^２１２は、それぞれ独立に置換基を有していてもよいアリール基、アルキル基またはアルケニル基を表し、Ｒ^２０１〜Ｒ^２０３、Ｒ^２０６〜Ｒ^２０７、Ｒ^２１１〜Ｒ^２１２は、相互に結合して式中のイオウ原子と共に環を形成してもよい。Ｒ^２０８〜Ｒ^２０９はそれぞれ独立に水素原子または炭素数１〜５のアルキル基を表し、Ｒ^２１０は置換基を有していてもよいアリール基、アルキル基、アルケニル基、又は−ＳＯ_２−含有環式基であり、Ｌ^２０１は−Ｃ（＝Ｏ）−または−Ｃ（＝Ｏ）−Ｏ−を表し、Ｙ^２０１は、それぞれ独立に、アリーレン基、アルキレン基またはアルケニレン基を表し、ｘは１または２であり、Ｗ^２０１は（ｘ＋１）価の連結基を表す。］

[Wherein, R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent, and R ^{201 to} R ²⁰³ , R ²⁰⁶ to R ²⁰⁷ and R ^{211 to} R ²¹² may be bonded to each other to form a ring together with the sulfur atom in the formula. R ^{208 to} R ²⁰⁹ each independently represent a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, and R ²¹⁰ is an aryl group, alkyl group, alkenyl group, or —SO ₂ — containing an optionally substituted substituent. A cyclic group, L ²⁰¹ represents —C (═O) — or —C (═O) —O—, Y ²⁰¹ each independently represents an arylene group, an alkylene group or an alkenylene group, and x represents 1 or 2 and W ²⁰¹ represents a (x + 1) -valent linking group. ]

Examples of the aryl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² include an unsubstituted aryl group having 6 to 20 carbon atoms, and a phenyl group and a naphthyl group are preferable.
The alkyl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² is a chain or cyclic alkyl group and preferably has 1 to 30 carbon atoms.
The alkenyl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² preferably has 2 to 10 carbon atoms.
Examples of the substituent that R ^{201 to} R ²⁰⁷ and R ^{210 to} R ²¹² may have include an alkyl group, a halogen atom, a halogenated alkyl group, a carbonyl group, a cyano group, an amino group, an aryl group, and an arylthio group. And groups represented by the following formulas (ca-r-1) to (ca-r-7).
The aryl group in the arylthio group as a substituent is the same as that described for R ¹⁰¹ , and specifically includes a phenylthio group or a biphenylthio group.

［式中、Ｒ’^２０１はそれぞれ独立に、水素原子、置換基を有していてもよい環式基、鎖状のアルキル基、または鎖状のアルケニル基である。］

[Wherein, R ′ ²⁰¹ each independently represents a hydrogen atom, an optionally substituted cyclic group, a chain alkyl group, or a chain alkenyl group. ]

The cyclic group which may have a substituent of R ′ ^201, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent are as described above. In addition to the same groups as those described above for R ^{101 in} formula (b-1), a cyclic group which may have a substituent or a chain alkyl group which may have a substituent may have the above formula ( Examples thereof include the same acid dissociable groups represented by a1-r-2).

^{R 201 ~R 203, R 206 ~R} 207, R 211 ~R 212 , when bonded to each other to form a ring with the sulfur atom, a sulfur atom, an oxygen atom, or a hetero atom such as nitrogen atom, carbonyl _{group, -SO -, - SO 2 -} , - SO 3 -, - COO -, - CONH- , or -N _(R N) - (. the _{R N} is an alkyl group having 1 to 5 carbon atoms), etc. You may couple | bond through the functional group of. As the ring to be formed, one ring containing a sulfur atom in the ring skeleton in the formula is preferably a 3- to 10-membered ring, particularly a 5- to 7-membered ring, including the sulfur atom. preferable. Specific examples of the ring formed include, for example, thiophene ring, thiazole ring, benzothiophene ring, thianthrene ring, benzothiophene ring, dibenzothiophene ring, 9H-thioxanthene ring, thioxanthone ring, thianthrene ring, phenoxathiin ring, tetrahydro A thiophenium ring, a tetrahydrothiopyranium ring, etc. are mentioned.

R ^{208 to} R ²⁰⁹ each independently represent a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, and when formed into an alkyl group, they are bonded to each other to form a ring. May be formed.

R ²¹⁰ may have an aryl group which may have a substituent, an alkyl group which may have a substituent, an alkenyl group which may have a substituent, or a substituent. -SO ₂ - containing cyclic group.
The aryl group in R ^210, include unsubstituted aryl group having 6 to 20 carbon atoms, a phenyl group, a naphthyl group.
The alkyl group for R ²¹⁰ is preferably a chain or cyclic alkyl group having 1 to 30 carbon atoms.
The alkenyl group for R ²¹⁰ preferably has 2 to 10 carbon atoms.
The —SO ₂ — containing cyclic group which may have a substituent in R ²¹⁰ is the same as the “—SO ₂ — containing cyclic group” of Ra ^{21 in} the general formula (a2-1). The group represented by the general formula (a5-r-1) is preferable.

Y ²⁰¹ each independently represents an arylene group, an alkylene group or an alkenylene group.
Examples of the arylene group for Y ²⁰¹ include a group in which one hydrogen atom has been removed from the aryl group exemplified as the aromatic hydrocarbon group for R ¹⁰¹ in the above formula (b-1).
Examples of the alkylene group and alkenylene group for Y ²⁰¹ include the same aliphatic hydrocarbon groups as the divalent hydrocarbon group for Va ¹ in the general formula (a1-1).

In the formula (ca-4), x is 1 or 2.
W ²⁰¹ is a (x + 1) valent, that is, a divalent or trivalent linking group.
The divalent linking group in W ²⁰¹ is preferably a divalent hydrocarbon group which may have a substituent, and examples thereof include the same hydrocarbon groups as Ya ²¹ in the general formula (a2-1). The divalent linking group in W ²⁰¹ may be linear, branched or cyclic, and is preferably cyclic. Of these, a group in which two carbonyl groups are combined at both ends of the arylene group is preferable. Examples of the arylene group include a phenylene group and a naphthylene group, and a phenylene group is particularly preferable.
^Examples of the trivalent linking group in W ²⁰¹ include a group obtained by removing one hydrogen atom from the divalent linking group in W ²⁰¹ , a group in which the divalent linking group is further bonded to the divalent linking group, and the like. Can be mentioned. The trivalent linking group in W ²⁰¹ is preferably a group in which two carbonyl groups are bonded to an arylene group.

  Specific examples of suitable cations represented by the formula (ca-1) include cations represented by the following formulas (ca-1-1) to (ca-1-63), respectively.

［式中、ｇ１、ｇ２、ｇ３は繰返し数を示し、ｇ１は１〜５の整数であり、ｇ２は０〜２０の整数であり、ｇ３は０〜２０の整数である。］

[Wherein, g1, g2, and g3 represent the number of repetitions, g1 is an integer of 1 to 5, g2 is an integer of 0 to 20, and g3 is an integer of 0 to 20. ]

［式中、Ｒ”^２０１は水素原子又は置換基であって、置換基としては前記Ｒ^２０１〜Ｒ^２０７、およびＲ^２１０〜Ｒ^２１２が有していてもよい置換基として挙げたものと同様である。］

[Wherein R ″ ²⁰¹ is a hydrogen atom or a substituent, and the substituent is the same as the substituents that R ^{201 to} R ²⁰⁷ and R ^{210 to} R ²¹² may have. is there.]

  Specific examples of suitable cations represented by the formula (ca-3) include cations represented by the following formulas (ca-3-1) to (ca-3-6).

  Specific examples of suitable cations represented by the formula (ca-4) include cations represented by the following formulas (ca-4-1) to (ca-4-2).

As the component (B), one type of acid generator described above may be used alone, or two or more types may be used in combination.
When the photosensitive resin composition of this invention contains (B) component, 0.5-60 mass parts is preferable with respect to 100 mass parts of (A) component, and, as for content of (B) component, 1-50 A mass part is more preferable, and 1-40 mass parts is still more preferable. By forming the content of the component (B) within the above range, pattern formation is sufficiently performed. Moreover, when each component of the photosensitive resin composition is dissolved in an organic solvent, a uniform solution is obtained, which is preferable because storage stability is improved.

<Basic compound component; (D) component>
The photosensitive resin composition of the present invention is also referred to as an acid diffusion controller component (hereinafter referred to as “component (D)”) in addition to the component (A) or in addition to the components (A) and (B). ) May be contained.
The component (D) acts as a quencher (acid diffusion controller) that traps acid generated by exposure from the component (B) and the like.
The component (D) in the present invention may be a photodegradable base (D1) (hereinafter referred to as “(D1) component”) that is decomposed by exposure and loses acid diffusion controllability. A non-corresponding nitrogen-containing organic compound (D2) (hereinafter referred to as “component (D2)”) may be used.

[(D1) component]
By forming the photosensitive resin composition containing the component (D1), the contrast between the exposed portion and the non-exposed portion can be improved when forming the photosensitive resin pattern.
The component (D1) is not particularly limited as long as it is decomposed by exposure and loses acid diffusion controllability, and is a compound represented by the following general formula (d1-1) (hereinafter referred to as “(d1-1) component”). ), A compound represented by the following general formula (d1-2) (hereinafter referred to as “(d1-2) component”) and a compound represented by the following general formula (d1-3) (hereinafter referred to as “(d1- One or more compounds selected from the group consisting of “3) component”) are preferred.
The components (d1-1) to (d1-3) are decomposed in the exposed portion and lose acid diffusion controllability (basicity), and thus do not act as a quencher, and act as a quencher in an unexposed portion.

［式中、Ｒｄ^１〜Ｒｄ^４は置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、または置換基を有していてもよい鎖状のアルケニル基である。ただし、式（ｄ１−２）中のＲｄ^２における、Ｓ原子に隣接する炭素原子にはフッ素原子は結合していないものとする。Ｙｄ^１は単結合、または２価の連結基である。Ｍ^ｍ＋はそれぞれ独立にｍ価の有機カチオンである。］

[Wherein Rd ^{1 to} Rd ⁴ are a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain which may have a substituent. Of the alkenyl group. However, a fluorine atom is not bonded to a carbon atom adjacent to the S atom in Rd ² in the formula (d1-2). Yd ¹ is a single bond or a divalent linking group. M ^{m +} is each independently an m-valent organic cation. ]

{(D1-1) component}
During Anion formula (d1-1), Rd ¹ is have an optionally substituted cyclic group which may have a substituent chain alkyl group or a substituted group, Or a similar chain alkenyl group to the same as R ¹⁰¹ .
Among these, Rd ¹ may have an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a substituent. A chain hydrocarbon group is preferred. The substituent that these groups may have is preferably a hydroxyl group, a fluorine atom or a fluorinated alkyl group.
The aromatic hydrocarbon group is more preferably a phenyl group or a naphthyl group.
The aliphatic cyclic group is more preferably a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane.
As the chain hydrocarbon group, a chain alkyl group is preferable. The chain alkyl group preferably has 1 to 10 carbon atoms, and specifically includes a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, and a nonyl group. A linear alkyl group such as a group or decyl group; 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group And branched chain alkyl groups such as 2-ethylbutyl group, 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group, and the like.

When the chain alkyl group is a fluorinated alkyl group having a fluorine atom or a fluorinated alkyl group as a substituent, the fluorinated alkyl group preferably has 1 to 11 carbon atoms, more preferably 1 to 8 carbon atoms. The fluorinated alkyl group, which is more preferably ˜4, may contain an atom other than a fluorine atom. Examples of atoms other than fluorine atoms include oxygen atoms, carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms.
Rd ¹ is preferably a fluorinated alkyl group in which some or all of the hydrogen atoms constituting the linear alkyl group are substituted by fluorine atoms, and the hydrogen atom constituting the linear alkyl group It is preferable that all are fluorinated alkyl groups (linear perfluoroalkyl groups) substituted with fluorine atoms.

  Preferred specific examples of the anion moiety of the component (d1-1) are shown below.

-Cation part In formula (d1-1), Mm ⁺ is an m-valent organic cation.
The organic cation of M ^{m +} is not particularly limited, and examples thereof include those similar to the cations represented by the general formulas (ca-1) to (ca-4), respectively, and the formula (ca-1- Cations represented by 1) to (ca-1-63) are preferable.
As the component (d1-1), one type may be used alone, or two or more types may be used in combination.

{(D1-2) component}
· During anion formula (d1-2), Rd ² is has an optionally substituted cyclic group which may have a substituent chain alkyl group or a substituted group, A chain alkenyl group which may be the same as R ¹⁰¹ .
However, a fluorine atom is not bonded to a carbon atom adjacent to the S atom in Rd ² (not fluorine-substituted). Thereby, the anion of (d1-2) component turns into a moderate weak acid anion, and the quenching ability of (D) component improves.
Rd ² is preferably an aliphatic cyclic group which may have a substituent, and a group in which one or more hydrogen atoms have been removed from adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane or the like. (It may have a substituent); it is more preferably a group obtained by removing one or more hydrogen atoms from camphor or the like.
The hydrocarbon group of Rd ² may have a substituent, and examples of the substituent include a hydrocarbon group (aromatic hydrocarbon group, aliphatic hydrocarbon group) in Rd ¹ of the formula (d1-1). The same thing as the substituent which may have is mentioned.

  Preferred specific examples of the anion moiety of the component (d1-2) are shown below.

-Cation part In formula (d1-2), Mm ⁺ is an m-valent organic cation, and is the same as Mm ⁺ in formula (d1-1).
As the component (d1-2), one type may be used alone, or two or more types may be used in combination.

{(D1-3) component}
During Anion formula (d1-3), Rd ³ is have an optionally substituted cyclic group which may have a substituent chain alkyl group or a substituted group, A chain alkenyl group that may be the same as R ^101, and is preferably a cyclic group containing a fluorine atom, a chain alkyl group, or a chain alkenyl group. Among them, a fluorinated alkyl group is preferable, and the same as the fluorinated alkyl group for Rd ¹ is more preferable.

In formula (d1-3), Rd ⁴ may have a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. Examples of the chain alkenyl group include those similar to R ¹⁰¹ .
Among these, an alkyl group, an alkoxy group, an alkenyl group, or a cyclic group which may have a substituent is preferable.
The alkyl group in Rd ⁴ is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, specifically, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group. Tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like. A part of the hydrogen atoms of the alkyl group of Rd ⁴ may be substituted with a hydroxyl group, a cyano group, or the like.
The alkoxy group in Rd ⁴ is preferably an alkoxy group having 1 to 5 carbon atoms. Specific examples of the alkoxy group having 1 to 5 carbon atoms include methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n- Examples include butoxy group and tert-butoxy group. Of these, a methoxy group and an ethoxy group are preferable.

Examples of the alkenyl group in Rd ⁴ include those similar to R ¹⁰¹ described above, and a vinyl group, a propenyl group (allyl group), a 1-methylpropenyl group, and a 2-methylpropenyl group are preferable. These groups may further have, as a substituent, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms.

Examples of the cyclic group for Rd ⁴ include the same groups as those described above for R ^101, and one or more hydrogen atoms are removed from a cycloalkane such as cyclopentane, cyclohexane, adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. An alicyclic group or an aromatic group such as a phenyl group or a naphthyl group is preferred. When Rd ⁴ is an alicyclic group, the photosensitive resin composition dissolves well in an organic solvent, thereby improving the lithography properties. Further, when Rd ⁴ is an aromatic group, in the lithography using EUV or the like as an exposure light source, the photosensitive resin composition is excellent in light absorption efficiency, and sensitivity and lithography characteristics are improved.

In formula (d1-3), Yd ¹ represents a single bond or a divalent linking group.
The divalent linking group in Yd ¹ is not particularly limited, but may be a divalent hydrocarbon group (aliphatic hydrocarbon group or aromatic hydrocarbon group) which may have a substituent, or a hetero atom containing 2 Valent linking groups and the like. These may be the same as those exemplified in the description of the divalent linking group of Ya ²¹ in the formula (a2-1).
Yd ¹ is preferably a carbonyl group, an ester bond, an amide bond, an alkylene group, or a combination thereof. The alkylene group is preferably a linear or branched alkylene group, and more preferably a methylene group or an ethylene group.

  Preferred specific examples of the anion moiety of the component (d1-3) are shown below.

-Cation part In formula (d1-3), Mm ⁺ is an m-valent organic cation, and is the same as Mm ⁺ in formula (d1-1).
As the component (d1-3), one type may be used alone, or two or more types may be used in combination.

As the component (D1), only one of the above components (d1-1) to (d1-3) may be used, or two or more may be used in combination.
The content of the component (D1) is preferably 0.5 to 10 parts by mass, more preferably 0.5 to 8 parts by mass, with respect to 100 parts by mass of the component (A). More preferably, it is part by mass.
When the content of the component (D1) is not less than the preferable lower limit value, particularly good lithography characteristics and a photosensitive resin pattern shape can be obtained. On the other hand, when it is not more than the upper limit value, the sensitivity can be maintained well and the throughput is also excellent.

  The manufacturing method of said (d1-1) component and (d1-2) component is not specifically limited, It can manufacture by a well-known method.

  The content of the component (D1) is preferably 0.5 to 10.0 parts by mass and more preferably 0.5 to 8.0 parts by mass with respect to 100 parts by mass of the component (A). 1.0 to 8.0 parts by mass is even more preferable. When it is at least the lower limit of the above range, particularly good lithography characteristics and a photosensitive resin pattern shape can be obtained. When the amount is not more than the upper limit of the above range, the sensitivity can be maintained satisfactorily and the throughput is excellent.

((D2) component)
(D) component may contain the nitrogen-containing organic compound component (henceforth (D2) component) which does not correspond to the said (D1) component.
The component (D2) is not particularly limited as long as it functions as an acid diffusion control agent and does not correspond to the component (D1), and any known component may be used. Of these, aliphatic amines, particularly secondary aliphatic amines and tertiary aliphatic amines are preferred.
An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 12 carbon atoms.
Examples of the aliphatic amine include an amine (alkyl amine or alkyl alcohol amine) or a cyclic amine in which at least one hydrogen atom of ammonia NH ₃ is substituted with an alkyl group or hydroxyalkyl group having 12 or less carbon atoms.
Specific examples of alkylamines and alkyl alcohol amines include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decylamine; diethylamine, di-n-propylamine, di- -Dialkylamines such as n-heptylamine, di-n-octylamine, dicyclohexylamine; trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine , Trialkylamines such as tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decylamine, tri-n-dodecylamine; diethanolamine, triethanolamine, diisopropanolamine, Li isopropanolamine, di -n- octanol amines, alkyl alcohol amines tri -n- octanol amine. Among these, a trialkylamine having 5 to 10 carbon atoms is more preferable, and tri-n-pentylamine or tri-n-octylamine is particularly preferable.

Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be monocyclic (aliphatic monocyclic amine) or polycyclic (aliphatic polycyclic amine).
Specific examples of the aliphatic monocyclic amine include piperidine and piperazine.
As the aliphatic polycyclic amine, those having 6 to 10 carbon atoms are preferable. Specifically, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5. 4.0] -7-undecene, hexamethylenetetramine, 1,4-diazabicyclo [2.2.2] octane, and the like.

  Other aliphatic amines include tris (2-methoxymethoxyethyl) amine, tris {2- (2-methoxyethoxy) ethyl} amine, tris {2- (2-methoxyethoxymethoxy) ethyl} amine, tris {2 -(1-methoxyethoxy) ethyl} amine, tris {2- (1-ethoxyethoxy) ethyl} amine, tris {2- (1-ethoxypropoxy) ethyl} amine, tris [2- {2- (2-hydroxy Ethoxy) ethoxy} ethyl] amine, triethanolamine triacetate and the like, and triethanolamine triacetate is preferable.

As the component (D2), an aromatic amine may be used.
Aromatic amines include aniline, pyridine, 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, diphenylamine, triphenylamine, tribenzylamine, 2,6-diisopropylaniline, N-tert-butoxy. And carbonylpyrrolidine.

(D2) A component may be used independently and may be used in combination of 2 or more type.
(D2) A component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component. By setting it as the above range, the shape of the photosensitive resin pattern, the stability over time, and the like are improved.

(D) A component may be used individually by 1 type and may be used in combination of 2 or more type.
When the photosensitive resin composition of this invention contains (D) component, it is preferable that (D) component is 0.1-15 mass parts with respect to 100 mass parts of (A) component. It is more preferably 3 to 12 parts by mass, and further preferably 0.5 to 12 parts by mass. When it is at least the lower limit of the above range, lithography properties such as LWR are further improved when a photosensitive resin composition is used. Further, a better photosensitive resin pattern shape can be obtained. When it is not more than the upper limit of the above range, the sensitivity can be maintained satisfactorily and the throughput is excellent.

<Optional component>
[(E) component]
In the present invention, the photosensitive resin composition includes an organic carboxylic acid and a phosphorus oxoacid as an optional component for the purpose of preventing sensitivity deterioration, improving the photosensitive resin pattern shape, stability with time, etc. And at least one compound (E) selected from the group consisting of derivatives thereof and derivatives thereof (hereinafter, referred to as component (E)) can be contained.
As the organic carboxylic acid, for example, acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, salicylic acid and the like are suitable.
Examples of phosphorus oxo acids include phosphoric acid, phosphonic acid, and phosphinic acid. Among these, phosphonic acid is particularly preferable.
Examples of the oxo acid derivative of phosphorus include esters in which the hydrogen atom of the oxo acid is substituted with a hydrocarbon group, and the hydrocarbon group includes an alkyl group having 1 to 5 carbon atoms and 6 to 6 carbon atoms. 15 aryl groups and the like.
Examples of phosphoric acid derivatives include phosphoric acid esters such as di-n-butyl phosphate and diphenyl phosphate.
Examples of phosphonic acid derivatives include phosphonic acid esters such as phosphonic acid dimethyl ester, phosphonic acid-di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester.
Examples of phosphinic acid derivatives include phosphinic acid esters and phenylphosphinic acid.
(E) A component may be used individually by 1 type and may use 2 or more types together.
(E) A component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component.

[(F) component]
In the present invention, the photosensitive resin composition may contain a fluorine additive (hereinafter referred to as “component (F)”) in order to impart water repellency to the photosensitive resin film.
Examples of the component (F) include JP 2010-002870 A, JP 2010-032994 A, JP 2010-277043 A, JP 2011-13569 A, and JP 2011-128226 A. The described fluorine-containing polymer compound can be used.
More specifically, examples of the component (F) include a polymer having a structural unit (f1) represented by the following formula (f1-1). As the polymer, a polymer (homopolymer) consisting only of the structural unit (f1) represented by the following formula (f1-1); a structural unit (f1) represented by the following formula (f1-1); A copolymer with the structural unit (a1); a structural unit (f1) represented by the following formula (f1-1); a structural unit derived from acrylic acid or methacrylic acid; and the structural unit (a1) It is preferable that it is a copolymer. Here, as the structural unit (a1) copolymerized with the structural unit (f1) represented by the following formula (f1-1), 1-ethyl-1-cyclooctyl (meth) acrylate or the formula (a1) -2-01) is preferred.

［式中、Ｒは前記同様であり、Ｒｆ^１０２およびＲｆ^１０３はそれぞれ独立して水素原子、ハロゲン原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基を表し、Ｒｆ^１０２およびＲｆ^１０３は同じであっても異なっていてもよい。ｎｆ^１は１〜５の整数であり、Ｒｆ^１０１はフッ素原子を含む有機基である。］

[Wherein, R is the same as defined above, and Rf ¹⁰² and Rf ¹⁰³ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, Rf ¹⁰² and Rf ¹⁰³ may be the same or different. nf ¹ is an integer of ¹ to 5, and Rf ¹⁰¹ is an organic group containing a fluorine atom. ]

In formula (f1-1), R is the same as described above. R is preferably a hydrogen atom or a methyl group.
In formula (f1-1), examples of the halogen atom for Rf ¹⁰² and Rf ¹⁰³ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. Examples of the alkyl group having 1 to 5 carbon atoms of Rf ¹⁰² and Rf ¹⁰³ include the same as the alkyl group having 1 to 5 carbon atoms of R, and a methyl group or an ethyl group is preferable. Specific examples of the halogenated alkyl group having 1 to 5 carbon atoms of Rf ¹⁰² and Rf ¹⁰³ include a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with a halogen atom. Can be mentioned. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. The inter alia ^{Rf 102} and ^{Rf 103,} a hydrogen atom, a fluorine atom, or an alkyl group of 1 to 5 carbon atoms is preferable, a hydrogen atom, a fluorine atom, a methyl group or an ethyl group, preferred.
In formula (f1-1), nf ¹ is an integer of ¹ to 5, preferably an integer of 1 to 3, and more preferably 1 or 2.

In formula (f1-1), Rf ¹⁰¹ is an organic group containing a fluorine atom, and is preferably a hydrocarbon group containing a fluorine atom.
The hydrocarbon group containing a fluorine atom may be linear, branched or cyclic, and preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms. The carbon number of 1 to 10 is particularly preferable.
The hydrocarbon group containing a fluorine atom preferably has 25% or more of the hydrogen atoms in the hydrocarbon group fluorinated, more preferably 50% or more fluorinated, and 60% or more. Fluorination is particularly preferred because the hydrophobicity of the photosensitive resin film during immersion exposure is increased.
Among ^these, as ^{Rf 101,} particularly preferably a fluorinated hydrocarbon group having 1 to 5 carbon atoms, a methyl _{group, -CH 2 -CF 3, -CH 2} -CF 2 -CF 3, -CH (CF 3) 2 _{, -CH} 2 _-CH 2 _-CF 3, and most preferably _{-CH 2 -CH 2 -CF 2 -CF 2} -CF 2 -CF 3.

(F) As for the weight average molecular weight (Mw) (polystyrene conversion reference | standard by a gel permeation chromatography), 1000-50000 are preferable, 5000-40000 are more preferable, and 10000-30000 are the most preferable. If it is below the upper limit of this range, it has sufficient solubility in a photosensitive resin solvent to be used as the photosensitive resin, and if it is above the lower limit of this range, it is resistant to dry etching and the cross section of the photosensitive resin pattern. Good shape.
The dispersity (Mw / Mn) of the component (F) is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and most preferably 1.2 to 2.5.

(F) A component may be used individually by 1 type and may use 2 or more types together.
(F) A component is used in the ratio of 0.5-10 mass parts with respect to 100 mass parts of (A) component.

  In the present invention, the photosensitive resin composition further contains an optional miscible additive, for example, an additional resin, a dissolution inhibitor, a plasticizer, a stabilizer, and a colorant for improving the performance of the photosensitive resin film. Further, an antihalation agent, a dye and the like can be added and contained as appropriate.

[(S) component]
In the present invention, the photosensitive resin composition can be produced by dissolving the material in an organic solvent (hereinafter sometimes referred to as (S) component).
As the component (S), any component can be used as long as it can dissolve each component to be used to form a uniform solution. Conventionally, any one of known solvents for chemically amplified resists can be used. Two or more types can be appropriately selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone (MEK), cyclohexanone, methyl-n-pentyl ketone (2-heptanone), methyl isopentyl ketone; ethylene glycol, diethylene glycol, propylene glycol, di- Polyhydric alcohols such as propylene glycol; compounds having an ester bond such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, dipropylene glycol monoacetate, the polyhydric alcohols or compounds having the ester bond Monoalkyl ethers such as monomethyl ether, monoethyl ether, monopropyl ether, monobutyl ether or monophenyl ether Derivatives of polyhydric alcohols such as compounds having an ether bond such as propylene glycol monomethyl ether acetate (PGMEA) and propylene glycol monomethyl ether (PGME) among these; cyclic ethers such as dioxane, , Methyl lactate, ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate, etc .; anisole, ethyl benzyl ether, cresyl methyl Ether, diphenyl ether, dibenzyl ether, phenetole, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene, mesitylene And aromatic organic solvents such as dimethyl sulfoxide (DMSO).
These organic solvents may be used independently and may be used as 2 or more types of mixed solvents.
Of these, PGMEA, PGME, γ-butyrolactone, and EL are preferable.
Moreover, the mixed solvent which mixed PGMEA and the polar solvent is also preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA and the polar solvent, preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. It is preferable to be within the range.
More specifically, when EL or cyclohexanone is blended as the polar solvent, the mass ratio of PGMEA: EL or cyclohexanone is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. . Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3.
In addition, as the component (S), a mixed solvent of at least one selected from PGMEA and EL and γ-butyrolactone is also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
(S) The usage-amount of a component is not specifically limited, It is a density | concentration which can be apply | coated to a board | substrate etc., and is suitably set according to a coating film thickness. Generally, it is used so that the solid content concentration of the photosensitive resin composition is in the range of 1 to 20% by mass, preferably 2 to 15% by mass.

≪Structure including phase separation structure≫
The present invention provides a structure including a phase separation structure manufactured by the above-described method for manufacturing a structure including a phase separation structure.
The structure having the phase separation structure of the present invention comprises a substrate, a neutralized film, a photosensitive resin, and a phase separated block copolymer.
In the structure having the phase separation structure of the present invention, the description regarding the substrate, the neutralized film, and the block copolymer is the same as described above.

  The structure having the phase separation structure of the present invention is characterized by having a phase separation structure comprising a phase 4a and a phase 4b on the photosensitive resin pattern 3 and the neutralization film 2, as illustrated in FIG. To do.

  EXAMPLES Hereinafter, although an Example demonstrates this invention more concretely, this invention is not limited to a following example.

The following compounds (1) to (5) were synthesized by a conventional method, and polymer compound 1 was synthesized by a conventional method.
Polymer compound 1:
(1) / (2) / (3) / (4) / (5) = 31.9 / 29.2 / 13.0 / 16.7 / 19.2
Mw = 7600, Mw / Mn = 1.62

  The following compound (B) -1 is 7.5 parts by mass, the following compound (D) -1 is 4.5 parts by mass, the following polymer compound (F) -1 ( (Molar ratio: 1 / m = 77/23), Mw is 23100, Mw / Mn is 1.78), 3.0 mass, propylene glycol monomethyl ether acetate / propylene glycol monomethyl ether / cyclohexanone = 45/30/25 It mixed and melt | dissolved in the mixed solvent of (mass ratio), and the photosensitive resin composition 1 with a solid content concentration of 2.5 mass% was prepared.

Example 1
[Formation of photosensitive resin pattern]
An organic antireflection film composition “ARC29A” (trade name, manufactured by Brewer Science Co., Ltd.) is applied onto an 8-inch silicon wafer using a spinner, and baked at 205 ° C. for 60 seconds on a hot plate and dried. Thus, an organic antireflection film having a film thickness of 82 nm was formed.
Next, a resin composition (styrene / methacrylic acid 3,4-epoxycyclohexylmethane) adjusted to a concentration of 0.5 to 1.0 mass% using PGMEA as a neutralization film on the organic antireflection film. / Methacrylic acid propyltrimethoxysilane = copolymer with a molecular weight of 40,000 consisting of 75/20/5) using a spinner, and baking and drying at 250 ° C. for 1 minute to obtain a film thickness of 10 nm. A layer made of the oxidization film was formed on the substrate.
Then, the photosensitive resin composition 1 is applied onto the layer made of the neutralized film using a spinner, pre-baked (PAB) on a hot plate at 110 ° C. for 60 seconds, and dried. Thus, a photosensitive resin film having a film thickness of 65 nm was formed.
Next, an ArF immersion exposure apparatus NSR-S609 (manufactured by Nikon Corporation; NA (numerical aperture) = 1.07, Cross pole (in / out = 0.78 / 0.97) with Polaro), ArF excimer laser, Irradiated. Then, PEB treatment was performed at 95 ° C. for 60 seconds. Furthermore, solvent development is carried out with a 2.38 mass% TMAH aqueous solution (trade name: NMD-3, manufactured by Tokyo Ohka Kogyo Co., Ltd.) at 23 ° C. for 13 seconds, followed by water rinsing with pure water for 30 seconds, followed by shaking off and drying. went.
Subsequently, post-baking was performed on a hot plate at 205 ° C. for 60 seconds.

  As a result, in Example 1, a photosensitive resin pattern (line and space pattern) having a line width of 30 nm, a pitch width of 98 nm, and a film thickness of 10 nm was formed on the neutralization film.

  Next, a block copolymer of PS-PMMA (Mw 42,400, PS / PMMA composition ratio (molar ratio) 55/45, dispersity 1.07, period 26 nm so as to cover the neutralized film portion and the photosensitive resin pattern. ) PGMEA solution (2% by mass) was spin-coated (rotation number 1500 rpm, 60 seconds). The substrate coated with the PS-PMMA block copolymer was annealed by heating at 240 ° C. for 60 seconds in a nitrogen stream to form a phase separation structure.

  As a result, in Example 1, a structure including a phase separation structure along the direction of the line and space pattern on the neutralized film and the photosensitive resin pattern could be manufactured.

Example 2
A structure including a phase separation structure was manufactured by the same method as in Example 1 except that a line and space pattern having a line width of 30 nm, a pitch width of 98 nm, and a film thickness of 11 nm was formed on the neutralization film.

  As a result, also in Example 2, a structure including a phase separation structure on the neutralized film and the photosensitive resin pattern could be manufactured.

Comparative Example 1
An attempt was made to produce a structure including a phase separation structure by the same method as in Example 1 except that the layer made of the neutralization film was not formed on the substrate.
As a result, the block copolymer applied on the photosensitive resin pattern and the organic antireflection film could not be phase separated.

Comparative Example 2
A structure including a phase separation structure was produced in the same manner as in Example 1 except that the photosensitive resin composition 1 was not used to form a photosensitive resin pattern.
As a result, it was possible to manufacture a structure including a phase separation structure on the entire surface of the neutralization film, but the disordered lamellar pattern and the phase separation structure facing the same direction as in Examples 1 and 2 were It was not obtained.

Comparative Example 3
A structure including a phase separation structure was manufactured in the same manner as in Example 1 except that a line and space pattern having a line width of 30 nm, a pitch width of 98 nm, and a film thickness of 22 nm was formed on the neutralization film.

  As a result, a structure including a phase separation structure along the direction of the line and space pattern could be manufactured on the neutralized film, but a structure including the phase separation structure on the photosensitive resin pattern was Not manufactured.

Comparative Example 4
A photosensitive resin pattern (line and space pattern) having a line width of 30 nm, a pitch width of 98 nm, and a film thickness of 65 nm was formed by the same method as in Example 1 except that the post-baking temperature was set to 100 ° C. for 60 seconds. A structure containing a phase separation structure was produced in the same manner as in Example 1.
As a result, a structure including a phase separation structure along the direction of the line and space pattern could be manufactured on the neutralization film, but a structure including a phase separation structure on the photosensitive resin pattern was obtained. Was not manufactured.

DESCRIPTION OF SYMBOLS 1, 11 ... Substrate 2 ... Neutralization film layer 3 containing surface treatment agent ... Photosensitive resin pattern 4, 13 ... Layers 4a, 13a containing block copolymer 4 From block _B comprising layers 4b, 13b ... _{P A} of blocks consisting of a layer 12 ... undercoat agent layer 14 ... resist pattern

Claims (2)

Forming a neutralized film containing a surface treatment agent having affinity with any polymer constituting the block copolymer on a substrate;
A photosensitive resin film is formed on the neutralized film by using a photosensitive resin composition that generates acid upon exposure and changes its solubility in a developer due to the action of the acid, and then exposed and developed. Forming a photosensitive resin pattern;
Forming a layer containing a block copolymer to which a plurality of types of polymers are bonded so as to cover the photosensitive resin pattern and the neutralized film on the photosensitive resin pattern;
Phase-separating the layer containing the block copolymer on the photosensitive resin pattern and the neutralized film, and forming a phase separation structure on the photosensitive resin pattern and the neutralized film;
Have a, the photosensitive resin pattern, the manufacturing method of a structure that contains a phase separation structure in which the height from the substrate surface and less than 22 nm.   The method for producing a structure according to claim 1, wherein in the step of forming the photosensitive resin pattern, baking after development is performed at 180 ° C or higher.