JP6132458B2 - Easy-to-cut pouch - Google Patents
Easy-to-cut pouch Download PDFInfo
- Publication number
- JP6132458B2 JP6132458B2 JP2011136154A JP2011136154A JP6132458B2 JP 6132458 B2 JP6132458 B2 JP 6132458B2 JP 2011136154 A JP2011136154 A JP 2011136154A JP 2011136154 A JP2011136154 A JP 2011136154A JP 6132458 B2 JP6132458 B2 JP 6132458B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- pouch
- easy
- cut
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、粉末洗剤、液体洗剤、柔軟剤などのトイレタリー用品や、食用油、インスタントコーヒー、粉ミルク、お茶などの食品等を収納する詰め替え容器に関する。より詳しくは、開封時に直線状の開口部を容易に形成することが出来る易カット性のパウチに関する。 The present invention relates to a refill container for storing toiletries such as powder detergents, liquid detergents and softeners, and foods such as edible oil, instant coffee, powdered milk and tea. More specifically, the present invention relates to an easy-cut pouch capable of easily forming a linear opening when opened.
液体洗剤やシャンプーなどのトイレタリー用品や、食用油、調味料、インスタントコーヒーなどの食品は、それぞれ使いやすい形状の専用容器に収納されている。
専用容器は、構造もしっかりしており、従って高価であることから、内容物が無くなった段階で、繰り返し使用することができるように、内容物のみを詰め替える詰め替え容器入りの製品が別途販売されていることが多い。
Toiletries such as liquid detergents and shampoos, and foods such as edible oils, seasonings, and instant coffee are each stored in dedicated containers that are easy to use.
The dedicated container has a solid structure and is therefore expensive, so a product with a refill container that refills only the contents is sold separately so that it can be used repeatedly when the contents are gone. There are many.
例えば液体洗剤の容器は、洗剤を使用する時にその都度適切な量を計量して取り出す必要があるため、計量カップに注ぎやすいように、注出口にノズルを備えた剛性のあるプラスチック容器が、繰り返し使用容器として用いられている。この容器に対して、内容物を補充するための詰め替え用の容器としては、軟包装フィルムからなる柔軟な容器に、注出口を形成した容器や、口栓を取付けた容器が一般的に使用されている。 For example, liquid detergent containers need to be weighed and taken out each time they are used, so a rigid plastic container with a nozzle at the spout is repeatedly used to make it easier to pour into a measuring cup. Used as a container. In contrast to this container, as a refilling container for replenishing the contents, a flexible container made of a flexible packaging film, a container in which a spout is formed, or a container attached with a stopper is generally used. ing.
詰め替え用の容器も、もっぱら安価に製造することに重点を置くあまり、詰替え操作における利便性を十分に考慮したものでは、必ずしもなかった。たとえば、従来のパウチの場合、開封線を誘導するような特別な加工がなされていない開口部できれいに開封出来る距離は長くても3cm程度であり、それ以上の距離を開封すると開封線が曲がったりパウチの表裏で離れてきたりして内容物を排出し易い直線状の開口部とならないことが多かった。
したがって、通常のパウチにおいて長い距離をカットすることが必要な寸法の場合には、表裏の包装材に傷やレーザー加工を施してカットラインを誘導する等の補助加工が行なわれてきた。
その他に包装材とするフィルム自体に延伸等の手段により引裂きの方向性を持たせて一方向のみに開封しやすいパウチとする方法もいろいろ用いられてきた。
Refill containers have not always been given sufficient consideration to the convenience of refilling operations because the emphasis was placed solely on manufacturing inexpensively. For example, in the case of a conventional pouch, the distance that can be opened cleanly at the opening that has not been specially processed to guide the opening line is about 3 cm at the longest. In many cases, the opening does not become a straight opening that is easy to discharge the contents by moving away from the front and back of the pouch.
Therefore, in the case of a dimension that requires a long distance to be cut in a normal pouch, auxiliary processing has been performed such as inducing a cut line by scratching or laser processing the front and back packaging materials.
In addition, various methods have been used in which the film itself as a packaging material is given a tearing direction by means of stretching or the like to make it easy to open in only one direction.
この問題に対して特許文献1では、 開封に際して手切れ性に優れ、かつ防湿性に優れた包装材料を提供するために、無機物を減圧下で被着させた、厚みが8〜20μmの二軸配向ポリエチレンテレフタレートフィルム、と該フィルムの無機物被着面側に接着層を介して積層した、厚みが8〜20μmの二軸配向ポリエチレンテレフタレートフィルム、及び該フィルムの非無機物被着面側に直接又は接着層を介して積層した、フィルム厚みが15〜60μmのポリエチレンを主成分とするヒートシール性フィルムを含む積層フィルムを用いた易引裂性防湿包装材料で構成する詰め替え容器が提案されている。
To solve this problem,
特許文献2では、 所望の位置から手指で容易に開封することができ、包装工程や流通段階での破袋を防止するとともに、衛生性にも優れ、しかも良好な外観を有する易開封性包装袋を提供するために、 プラスチックフィルムをヒートシールした密封包装袋において、ヒートシール部の端縁に長さが0.01mm以上0.5mm未満の切り込みを設けることにより易開封性包装袋を構成することが提案されている。
In
しかしながら、特許文献1に記載された詰め替え容器は、開封時の引裂き方向による引裂き抵抗の差を主に使用するポリエチレンテレフタレートフィルムの縦横方法の延伸差に
より実現しており、直線的な開封を可能にするためのシーラントフィルムの引裂きと切断の方向性に関しては考慮されていない。
シーラントフィルムに引裂き性を与えるための添加剤としては無機フィラー等がよく使われるが、この場合は被膜強度や接着強度が通常のシーラントフィルムよりも劣るためにとくに800g程度以上の重量の内容物の包装には不向きであった。
また、同様の目的でのシーラント層ポリエチレンへの添加樹脂としては、ノルボルネンとエチレンをメタロセン触媒にて共重合した環状オレフィンコポリマー(COC)も挙げられるが、シーラント層樹脂中に単に配合させただけではやはり通常のシーラントフィルムよりも強度的に劣るため問題解決には至らなかった。
However, the refill container described in
An inorganic filler or the like is often used as an additive for imparting tearability to the sealant film. In this case, since the film strength and the adhesive strength are inferior to those of a normal sealant film, the content of a weight of about 800 g or more is particularly required. Not suitable for packaging.
In addition, as a resin added to the sealant layer polyethylene for the same purpose, a cyclic olefin copolymer (COC) obtained by copolymerizing norbornene and ethylene with a metallocene catalyst may be mentioned, but simply by adding it to the sealant layer resin. The problem was not solved because it was inferior in strength to a normal sealant film.
また、特許文献2で提案されている易開封性包装袋は、従来開封のきっかけとして用いられていたIノッチ、Vノッチ、Uノッチなどのノッチ(切欠き)から開封した際に、開封開始直後からパウチの表裏で開封線の位置が二股になり、そのまま最後まで二股になった状態で切り取られて行く事が起こりやすく直線状の開口部を形成できないという問題があった。
In addition, the easy-open packaging bag proposed in
上記の事情に鑑み、本発明は一般的に用いられているシーラント樹脂を使用して、開封時に直線状の開口部を容易に形成することが出来る易カット性のパウチを提供することを課題とする。 In view of the above circumstances, an object of the present invention is to provide an easily cut pouch capable of easily forming a linear opening at the time of opening using a sealant resin that is generally used. To do.
引裂き性と切断性に優れたシーラント層として、ラミネート層とシール層で、引裂き性と切断の方向性に優れた材料であるCOCを含む中間層を挟んだ多層構成とすることで、易カット性、シール性、ラミネート性の物性を損なわないシーラント層とした。さらに落下時の耐衝撃性を上げるために柔軟性を補強するC6またはC8のLLDPEを加えることで、カットの直線性、易開封性を保持したままで物性面を強化したシーラント層とした。
またパウチの開封及び切り取りのきっかけとなるノッチを一の字状の複数の傷からなる多数配列のノッチとすることによって開封作業及び切り取り作業を容易にすることが可能となった。
As a sealant layer with excellent tearability and cutability, it is easy to cut by adopting a multilayer structure with an intermediate layer containing COC, which is a material excellent in tearability and cutting direction, between the laminate layer and the seal layer. In addition, a sealant layer that does not impair the physical properties of sealing properties and laminating properties was obtained. Further, by adding C6 or C8 LLDPE which reinforces the flexibility in order to increase the impact resistance at the time of dropping, a sealant layer having a strengthened physical property surface while maintaining the linearity and easy opening of the cut was obtained.
In addition, the opening and cutting operations can be facilitated by making the notches that trigger the opening and cutting of the pouch into a plurality of notches made up of a plurality of single-shaped flaws.
すなわち、本発明の請求項1に係る発明は、シーラント層と延伸フィルムを少なくとも積層してなる積層体を表側フィルム及び裏側フィルムとし、これら表側フィルムと裏側フィルムとを、延伸フィルムを外側に位置するように重ね、端部をヒートシールして形成された内容物が800g以上のパウチであって、
前記延伸フィルムがMD方向に直線状に引裂かれるフィルムであり、
開封部の幅が10cmから25cmである該延伸フィルムの引裂き方向のパウチ両端にのみ、複数本の一の字状の傷が設けられており、かつ、これら複数本の一の字状の傷が千鳥足に配列されており、
これら複数本の一の字状の傷で構成されるノッチをノッチ領域が上下に幅を有して形成している開封開始部が設けられており、
該シーラント層が、内側のラミネート層、中間層、及び外側のシール層の三層構造を有しており、内側のラミネート層としてC4−LLDPEで表されるリニア低密度ポリエチレン、中間層としてC4−LLDPE及びCOCで表される環状オレフィンコーポリマー、外側のシール層としてC4−LLDPEからなり、
ラミネート層/中間層/シール層の層比がそれぞれ0.5〜2/1〜5/0.5〜2の範囲であり、
多数配列のノッチはパウチ両端のシール部から0.5mm以上はみ出した位置の幅10mm以上の領域に配列されてなる
ことを特徴とする易カット性パウチである。
That is, in the invention according to
The stretched film is a film that is torn linearly in the MD direction,
A plurality of one-letter-shaped scratches are provided only on both ends of the pouch in the tear direction of the stretched film having a width of the opening portion of 10 to 25 cm, and the plurality of one-letter-shaped scratches are provided. It is arranged in a staggered foot,
An opening start portion is provided in which a notch region is formed with a width above and below a notch composed of a plurality of one-letter-shaped scratches,
The sealant layer has a three-layer structure of an inner laminate layer, an intermediate layer, and an outer seal layer, and a linear low density polyethylene represented by C4-LLDPE as an inner laminate layer, and C4- as an intermediate layer. A cyclic olefin copolymer represented by LLDPE and COC, and C4-LLDPE as an outer sealing layer,
Range der laminate layer / intermediate layer / layer ratio of the seal layer, respectively 0.5 to 2 / 1-5 / 0.5-2 is,
The notch of multiple arrangement | sequence is an easily cutable pouch characterized by being arranged in the area | region of width 10mm or more of the position which protruded 0.5mm or more from the seal part of the pouch both ends .
パウチを構成する積層体の延伸フィルムの延伸方向のパウチ両端に開封開始部が設けられていることによって延伸フィルムの延伸方向にカットして開封する場合の易カット性と直線カット性は保持されているが、この場合でもシーラント層が伸びてカットライン近傍にヒゲ状に残ることがあり、直線カット性を確保することができない場合があった。
シーラント層にCOCを用いることによってヒゲ状のカット断面のない直線カット性が実現できることは知られているが、COCのみではシール強度が低く特に重量物の包装に用いる場合には包装材としての強度が不足気味であった。
本発明のパウチにおいては、通常シーラントに用いるC4−LLDPEをCOCに混合して用いることで直線カット性と必要なシール強度を満たすことができるようになった。
Easy opening and straight-line cutting properties are maintained when opening and opening in the stretching direction of the stretched film by providing opening opening portions at both ends of the pouch in the stretching direction of the stretched film of the laminate constituting the pouch. However, even in this case, the sealant layer may be stretched and remain in the shape of a beard in the vicinity of the cut line, and the linear cut property may not be ensured.
It is known that COC can be used for the sealant layer to achieve straight cut without a beard-like cut section, but COC alone has low sealing strength, especially when used for heavy-weight packaging. There was a shortage.
In the pouch of the present invention, C4-LLDPE, which is usually used for a sealant, can be mixed with COC and used to satisfy the linear cut property and the required seal strength.
本来、シーラント層に含まれる中間層の厚みがシーラント層の厚み中の大きな部分を占めるほどカット性が向上して開封時に切れやすい袋とすることが出来るが、中間層の厚みが大きすぎるとシール強度は低下する。ラミネート層/中間層/シール層の層比をこの範囲にすることによって必要なシール強度と同時に直線状の直線カット性を両立させることがより確実に可能となった。 Originally, as the thickness of the intermediate layer contained in the sealant layer occupies a larger portion in the thickness of the sealant layer, the cut property is improved and the bag can be easily cut at the time of opening. The strength decreases. By setting the layer ratio of the laminate layer / intermediate layer / seal layer within this range, it becomes possible to more surely achieve both the required seal strength and the linear straight-line cut property.
本発明の請求項2に係る発明は、中間層に含まれるCOCの配合量が10重量%から40重量%の範囲であることを特徴とする、請求項1記載の易カット性パウチである。
The invention according to
中間層に含まれるCOCの配合量が10重量%未満であると開封時に袋が切れにくくなり、40重量%より多いと隣接する層との層間剥離が起こりやすくなるので、この間の範囲とすることで必要なシール強度と同時に直線状の直線カット性を両立させることがより確実に可能となった。 If the amount of COC contained in the intermediate layer is less than 10% by weight, the bag is difficult to break when opened, and if it exceeds 40% by weight, delamination between adjacent layers is likely to occur. Thus, it has become possible to achieve both the necessary seal strength and the linear straight line cut performance more reliably.
複数本の一の字状の傷による多数配列のノッチから開封することにより開封のきっかけとなる位置が多少ずれた場合でも、容易に開封を開始することが出来て易開封性を効果的なものとする。
延伸方向に直線状に引裂かれる延伸フィルムと直線状に引裂くことの出来るポリエチレンを用いた積層体を用いて開封部をたとえば10cmから50cm必要とする広幅のパウチを作成し、このパウチの両側端シール部の開封位置にシール部から内側へはみ出した多数配列のノッチが設けられていることによって、開封をスムースに行なうことが出来るばかりでなく、シールからはみ出した位置にもノッチ加工がしてあることから切り取りもスムースに行なうことが出来る。
Even if the position that triggers opening is slightly shifted by opening from multiple notches due to multiple single-letter-shaped scratches, opening can be started easily and effective opening is effective. And
Using a stretched film that is torn linearly in the stretching direction and a laminate that uses polyethylene that can be torn linearly, create a wide pouch that requires an opening of, for example, 10 cm to 50 cm, and both ends of the pouch By providing a large number of notches that protrude from the seal part to the inside at the opening position of the seal part, not only can the opening be performed smoothly, but also the position that protrudes from the seal is notched. Therefore, cutting can be performed smoothly.
多数配列のノッチをパウチ両端のシール部から0.5mm以上はみ出した位置の幅10mm以上の領域に配列することによって、開封の開始を容易に始めることが出来るのみならず、パウチの表裏できれいに揃ってカットされず二股に裂けてしまった場合の開封終わりも切り取り易くすることが出来る。 By arranging a large number of notches in a region with a width of 10 mm or more that protrudes 0.5 mm or more from the seal part at both ends of the pouch, it is possible not only to easily start opening, but also to neatly align the front and back of the pouch. It is also possible to make it easier to cut the end of opening when it is not cut and split into two.
本発明の請求項3に係る発明は、多数配列のノッチを構成する一の字状の傷それぞれの長さは0.1mm〜5mmの範囲であることを特徴とする、請求項1または2に記載の易カット性パウチである。
The invention according to
ノッチを構成する一の字状の傷それぞれの長さを上記の範囲とすることによって、開封時のカットの開始直後の直線性の保持が容易になる。 By setting the length of each single-shaped flaw constituting the notch within the above range, it becomes easy to maintain linearity immediately after the start of cutting at the time of opening.
以上のように、本発明の易カット性パウチによれば、
シーラントフィルムに引裂き性を与えるための添加剤としてシーラント層ポリエチレンへの無機フィラーやCOC等の樹脂の添加だけでは通常のシーラントフィルムよりも強度的に劣る問題と、開封時にパウチの表裏で開封線の位置が二股になり、そのまま最後まで二股になった状態で切り取られて行く事が起こりやすく直線状の開口部を形成できないという問題を解決して、一般的に用いられているシーラント樹脂を使用して、開封時に直線状の開口部を容易に形成することが出来る易カット性のパウチを提供することが可能となった。
As described above, according to the easy-cut pouch of the present invention,
As an additive for tearing the sealant film, the addition of an inorganic filler or resin such as COC to the sealant layer polyethylene alone is inferior in strength to that of a normal sealant film. Using a commonly used sealant resin to solve the problem that the position is bifurcated and it is easy to be cut off with the bifurcated position to the end, making it impossible to form a linear opening. Thus, it is possible to provide an easy-cut pouch capable of easily forming a linear opening at the time of opening.
とくに本発明のスタンディングパウチ用途のシーラント層構成は、一般的に用いられているC4−LLDPEとCOCを用いて、ラミネート層、中間層、シール層に分けて多層にすることで、ラミネート強度、易カット性、シール強度の物性を損なわないシーラント
フィルムの提供を可能とした。
In particular, the structure of the sealant layer for the standing pouch application of the present invention is a laminate layer, an intermediate layer, and a seal layer, which are generally used in C4-LLDPE and COC. It has become possible to provide a sealant film that does not impair the physical properties of cut and seal strength.
さらにそのシーラント層を延伸ポリエステルフィルムのような易カットPETと組み合わせることによって易開封性と開封の直線性を要求されるパウチの提供を可能とした。
さらに、パウチの耐衝撃性を上げるためにC6またはC8のLLDPEをさらに組み込むことにより易開封性と開封の直線性を保持したままで重量物の包装も可能な衝撃に強いパウチの提供を可能とした。
Furthermore, by combining the sealant layer with easy-cut PET such as a stretched polyester film, it is possible to provide a pouch that requires easy-opening and linearity of opening.
Furthermore, by further incorporating C6 or C8 LLDPE in order to increase the impact resistance of the pouch, it is possible to provide an impact-resistant pouch capable of packaging heavy objects while maintaining easy opening and linearity of opening. did.
次に、図面を参照して本発明の易カット性パウチの実施形態の例を説明する。
図1は本発明の易カット性パウチの一例の平面略図を示したものである。図1(A)はスタンディングパウチの場合を示している。他の形式のパウチの例として図1(B)には三方パウチの平面略図を、図1(C)にはガゼット袋の外観略図を示した。
本発明は他にもさまざまな形式のパウチに適用できるが、ここでは主にスタンディングパウチの場合を例に説明する。
Next, an example of an embodiment of the easy-cut pouch of the present invention will be described with reference to the drawings.
FIG. 1 shows a schematic plan view of an example of the easy-cut pouch of the present invention. FIG. 1A shows a case of a standing pouch. As an example of another type of pouch, FIG. 1B shows a schematic plan view of a three-way pouch, and FIG. 1C shows a schematic appearance of a gusset bag.
The present invention can be applied to various other types of pouches. Here, a case of a standing pouch will be mainly described as an example.
また、図2は本発明の易カット性パウチに用いる積層体の断面略図を示したものである。図2(A)は上面がパウチ外側とした積層体の断面を、図2(B)は積層体を構成するシーラント層の断面を示した。 FIG. 2 is a schematic cross-sectional view of a laminate used in the easy-cut pouch of the present invention. FIG. 2A shows a cross section of the laminate having the top surface outside the pouch, and FIG. 2B shows a cross section of the sealant layer constituting the laminate.
本発明の易カット性パウチは、シーラント層(6)と延伸フィルム(5)を少なくとも積層してなる積層体(1)を表裏に用いて延伸フィルム(5)を外側に配置して重ねた端部をヒートシールして形成されたパウチである。
ヒートシールされた端部は底部シール部(4)および左右の側面シール部(2)からなり、底部シール部(4)は底部端面から高さ(f)の位置で折り返された底テープ(図示せず)を挟み込んだ形でシールされている。パウチ天面は内容物充填後にヒートシールされる予定でありこの段階では封止されていない。
The easy-cut pouch according to the present invention has an end in which a stretched film (5) is arranged on the outside using a laminate (1) formed by laminating at least a sealant layer (6) and a stretched film (5). This is a pouch formed by heat-sealing the part.
The heat-sealed end portion comprises a bottom seal portion (4) and left and right side seal portions (2). The bottom seal portion (4) is a bottom tape folded back at a height (f) from the bottom end surface (see FIG. (Not shown). The top of the pouch will be heat sealed after filling the contents and is not sealed at this stage.
延伸フィルム(5)の延伸方向(この場合は左右方向)のパウチ両端に開封開始部としてノッチ(12)が設けられている。ノッチの形状はIノッチ、Vノッチ、Uノッチなどの切欠きでもよいが、図3に示したような多数配列のノッチ(13)の方がより望ましい。
この場合の多数配列ノッチのはみ出し長さ(a)はパウチ両端の側面シール部(2)から0.5mm以上はみ出した位置であり、多数配列ノッチ領域上下幅(b)は幅10mm以上であり、一つのノッチ長さ(c)は0.1mm〜5mmの範囲であることが易カット性を確保する上で望ましい。
多数配列ノッチを構成する個々の一の字状の傷の配列方向は、開封方向に平行な方向のみに限られず、たとえば千鳥足状に配列したものであってもよい。
Notches (12) are provided as opening start portions at both ends of the pouch in the stretching direction (in this case, the left-right direction) of the stretched film (5). The shape of the notch may be a notch such as an I notch, a V notch, a U notch or the like, but a multiple array of notches (13) as shown in FIG. 3 is more desirable.
In this case, the protruding length (a) of the multi-array notch is a position protruding 0.5 mm or more from the side seal portions (2) at both ends of the pouch, and the vertical width (b) of the multi-array notch region is 10 mm or more in width. One notch length (c) is preferably in the range of 0.1 mm to 5 mm in order to ensure easy cutability.
The arrangement direction of the individual single-letter marks constituting the multiple arrangement notch is not limited to the direction parallel to the opening direction, and may be arranged in a staggered pattern, for example.
上記のようなパウチは周知の方法によって作成することが可能である。たとえば厚さ12μmの延伸ポリエチレンテレフタレート(PET)フィルム/ウレタン系接着剤層/厚さ60μmの易カット性シーラント層からなる積層体を使用し、常法により袋の両側縁及び底テープを挟んだ底部をヒートシールすることにより、図1(A)に示す形状のスタンディングパウチを作成し、つぎに、このスタンディングパウチの側面ヒートシール部の近傍に、パウチの端縁から内方に向かって端縁に対して略垂直に、直線状の切り込みを設けることにより多数配置のノッチを形成することで作成することが出来る。
The pouch as described above can be produced by a known method. For example, using a laminate composed of a stretched polyethylene terephthalate (PET) film with a thickness of 12 μm / urethane adhesive layer / an easily cut sealant layer with a thickness of 60 μm, and sandwiching both side edges of the bag and the bottom tape in the
本発明の易カット性パウチに用いる積層体(1)の延伸フィルムとしては、例えば、ポリエチレンテレフタレート樹脂(PET)、ポリエチレンナフタレ−ト樹脂(PEN)、ポリブチレンテレフタレート樹脂(PBT)などのポリエステル樹脂、ナイロン−6、ナイロン−66などのポリアミド樹脂(PA)、ポリカーボネート樹脂(PC)、ポリアクリロニトリル樹脂(PAN)、ポリイミド樹脂(PI)、ポリビニルアルコール樹脂(PVA)、ポリ塩化ビニリデン樹脂(PVDC)、エチレン−ビニルアルコール共重合体樹脂(EVOH)などの延伸フィルムなどのいずれかが使用できる。また、延伸フィルムの厚さは、通常、加工性を考慮して10〜150μmの範囲内で適宜選択される。
フィルムの延伸は二軸あるいは一軸のどちらでもよいが、開封時に必要な方向での易カット性を得るためには開封方向での延伸の程度が直角方向での延伸の程度よりも大きいことが必要である。
Examples of the stretched film (1) used in the easy-cut pouch of the present invention include polyester resins such as polyethylene terephthalate resin (PET), polyethylene naphthalate resin (PEN), and polybutylene terephthalate resin (PBT). , Nylon-6, nylon-66 and other polyamide resins (PA), polycarbonate resins (PC), polyacrylonitrile resins (PAN), polyimide resins (PI), polyvinyl alcohol resins (PVA), polyvinylidene chloride resins (PVDC), Any of stretched films such as ethylene-vinyl alcohol copolymer resin (EVOH) can be used. In addition, the thickness of the stretched film is usually appropriately selected within a range of 10 to 150 μm in consideration of processability.
The film may be stretched either biaxially or uniaxially, but in order to obtain easy cutability in the direction required at the time of opening, the degree of stretching in the opening direction needs to be greater than the degree of stretching in the perpendicular direction. It is.
シーラント層(6)には、例えば、低密度ポリエチレン樹脂(LDPE)、中密度ポリエチレン樹脂(MDPE)、高密度ポリエチレン樹脂(HDPE)、直鎖状低密度ポリエチレン樹脂(L−LDPE)、ポリプロピレン樹脂(PP)、エチレン−プロピレン共重合体(EP)、エチレン−αオレフィン共重合体、エチレン−アクリル酸共重合体(EAA)、エチレン−メタクリル酸共重合体(EMAA)、エチレン−アクリル酸メチル共重合体(EMA)、エチレン−アクリル酸エチル共重合体(EEA)、エチレン−メタクリル酸メチル共重合体(EMMA)、アイオノマー樹脂、エチレン−酢酸ビニル共重合体(EVA)などの樹脂、またはこれらの樹脂を成膜化したフィルムを使用することができる。通常はシール適性からLLDPEがよく用いられる。 Examples of the sealant layer (6) include a low density polyethylene resin (LDPE), a medium density polyethylene resin (MDPE), a high density polyethylene resin (HDPE), a linear low density polyethylene resin (L-LDPE), and a polypropylene resin ( PP), ethylene-propylene copolymer (EP), ethylene-α olefin copolymer, ethylene-acrylic acid copolymer (EAA), ethylene-methacrylic acid copolymer (EMAA), ethylene-methyl acrylate copolymer Resin such as coalescence (EMA), ethylene-ethyl acrylate copolymer (EEA), ethylene-methyl methacrylate copolymer (EMMA), ionomer resin, ethylene-vinyl acetate copolymer (EVA), or these resins Can be used. Usually, LLDPE is often used because of its sealability.
LLDPEとしてはC4−LLDPEで表されるリニア低密度ポリエチレンが用いられる。α−オレフィンの炭素数によって柔軟性が異なり炭素数4(以下C4)よりも炭素数6(C6)、炭素数8(C8)の方がLLDPEが柔軟になることから、重量物の包装の場合にとくに問題になる特性である落下強度の向上のために、C6−LLDPEで表されるリニア低密度ポリエチレン又はC8−LLDPEで表されるリニア低密度ポリエチレン又はをシーラント層(6)の各層に配合することがある。 As the LLDPE, linear low density polyethylene represented by C4-LLDPE is used. In the case of heavy-weight packaging, LLDPE is more flexible when the number of carbons is 6 (C6) and 8 (C8) than 4 (C4). In order to improve the drop strength, which is a particularly problematic property, linear low density polyethylene represented by C6-LLDPE or linear low density polyethylene represented by C8-LLDPE is blended in each layer of the sealant layer (6). There are things to do.
本発明の易カット性パウチに用いる積層体(1)のシーラント層(6)は単層ではなく、図2(B)に断面を示したように容器外側から順にラミネート層(9)、中間層(10)、シール層(11)の少なくとも3層からなる。
中間層(10)がシーラント層(6)の易カット性を発現する上でおもな役割を果たし、中間層(10)のみでは不足することがある接着剤層(8)とのラミネート強度とヒートシール時のシーラント層同士のシール強度をラミネート層(9)とシール層(10)で補強するという構成である。
中間層(10)はC4−LLDPEに易カット性に優れた環状オレフィンコーポリマー(COC)を配合した中間層を含んでなる層でありシーラント層の開封時の直線状の直線カット性の保持に貢献するCOCを含むことによって開封時のヒゲ等の発生を防止する機能を有する。
The sealant layer (6) of the laminate (1) used in the easy-cut pouch of the present invention is not a single layer, but a laminate layer (9) and an intermediate layer in order from the outside of the container as shown in the cross section of FIG. (10) It consists of at least three layers of a seal layer (11).
The intermediate layer (10) plays a major role in expressing the easy-cut property of the sealant layer (6), and the laminate strength with the adhesive layer (8) that may be insufficient only with the intermediate layer (10) The seal strength between the sealant layers at the time of heat sealing is reinforced by the laminate layer (9) and the seal layer (10).
The intermediate layer (10) is a layer comprising an intermediate layer in which C4-LLDPE is blended with a cyclic olefin copolymer (COC) excellent in easy cutting properties, and maintains the linear straight-cut property when the sealant layer is opened. By including COC that contributes, it has the function of preventing the occurrence of whiskers and the like at the time of opening.
中間層に含まれるCOCの配合量は開封時に袋が切れにくくなることを防止し、隣接する層との層間剥離が起こりやすくなるも防止するためには10重量%から40重量%の範囲であることが望ましい。
シーラント層(6)の総厚は特に限定されないが、密封性、生産性、コスト等の観点よ
り通常30μm〜150μm程度、好ましくは60μm〜80μm程度、引裂き強度は1〜10gとすることが望ましい。
また、シーラント層(6)に含まれるラミネート層(9)/中間層(10)/シール層(11)の層比はそれぞれ0.5〜2/1〜5/0.5〜2の範囲であることが望ましい。総厚が60μm〜80μmの範囲でのシーラント層の代表的な構成としては、表1のような例を示すことが出来る。
Although the total thickness of the sealant layer (6) is not particularly limited, it is usually about 30 μm to 150 μm, preferably about 60 μm to 80 μm, and the tear strength is 1 to 10 g from the viewpoints of sealability, productivity, cost, and the like.
The layer ratio of the laminate layer (9) / intermediate layer (10) / seal layer (11) contained in the sealant layer (6) is in the range of 0.5-2 / 1-5 / 0.5-2, respectively. It is desirable to be. As a typical configuration of the sealant layer in the total thickness range of 60 μm to 80 μm, examples shown in Table 1 can be shown.
シーラント層(6)の各層にシーラント被膜の柔軟性を高める目的でC4に加えてC6あるいはC8のLLDPEを添加する場合は易カット性と落下強度の兼ね合いから、配合比がラミネート層(9)とシール層(11)にあってはC4−LLDPE70%〜90%+C6−LLDPE10%〜30%、中間層(10)にあってはC4−LLDPE30%〜50%+C6−LLDPE10%〜30%+COC10%〜20%であること、またはラミネート層(9)とシール層(11)にあってはC4−LLDPE70%〜90%+C8−LLDPE10%〜30%、中間層(10)にあってはC4−LLDPE30%〜50%+C8−LLDPE10%〜30%+COC10%〜20%であることが望ましい。
In the case of adding C6 or C8 LLDPE in addition to C4 for the purpose of enhancing the flexibility of the sealant film in each layer of the sealant layer (6), the blending ratio of the laminate layer (9) For the sealing layer (11), C4-LLDPE 70% to 90% + C6-
延伸フィルム(5)と、シーラント層(6)とを接着剤層(8)を介してラミネーションして積層体(1)を作成する方法としては、例えば、ドライラミネーション方法などの公知の方法を使用することができる。
前記ドライラミネーション方法に使用する接着剤は、一般的に、ポリウレタン系、ポリアクリル系、ポリエステル系、エポキシ系、ポリ酢酸ビニル系、セルロース系、その他などのラミネート用接着剤を使用することができる。
As a method for producing the laminate (1) by laminating the stretched film (5) and the sealant layer (6) through the adhesive layer (8), for example, a known method such as a dry lamination method is used. can do.
As the adhesive used in the dry lamination method, generally, an adhesive for laminating such as polyurethane, polyacrylic, polyester, epoxy, polyvinyl acetate, cellulose, or the like can be used.
本発明の易カット性パウチはパウチを構成する延伸フィルム(5)の延伸方向のパウチ両端に開封開始部(ノッチ)が設けられている。ノッチの形状は通常側面シール部(2)から先端を内側に向けて設けられた鋭角の切欠き(12)(図1参照)であるが、パウチの易開封性をより確実にするために、図3に示すような多数配列のノッチ(13)を設けることが出来る。
この多数配列のノッチ(13)は開封方向であるパウチ両側面の開口部近辺の領域に設けられ、たとえば図3に示すような複数の一の字状の傷の集合体である。
The easy-cut pouch of the present invention is provided with opening start portions (notches) at both ends of the pouch in the stretching direction of the stretched film (5) constituting the pouch. The shape of the notch is usually an acute notch (12) (see FIG. 1) provided from the side seal part (2) with the tip facing inward, but in order to make the easy opening of the pouch more reliable, Multiple arrays of notches (13) can be provided as shown in FIG.
The multiple array of notches (13) are provided in a region near the opening on both sides of the pouch in the opening direction, and are, for example, a collection of a plurality of single-letter-shaped scratches as shown in FIG.
図3(A)は本発明の易カット性パウチのスタンディングパウチの場合の例の正面略図であり、図3(B)は多数配列のノッチ部分の拡大図である。多数配列のノッチ(13)はパウチ上部の両側の側面シール部(2)の近傍に設けられている。
この多数配列のノッチ(13)は側面シール部(2)だけでなくそこから内側にはみ出した領域にも設けられており、この場合の多数配列ノッチのはみ出し長さ(a)はパウチ両端の側面シール部(2)から0.5mm以上はみ出した位置であり、多数配列ノッチ領域上下幅(b)は幅10mm以上であり、一つのノッチ長さ(c)は0.1mm〜5mmの範囲である。
FIG. 3A is a schematic front view of an example of the standing pouch of the easy-cut pouch of the present invention, and FIG. 3B is an enlarged view of notches in a multi-array. Multiple notches (13) are provided in the vicinity of the side seals (2) on both sides of the upper part of the pouch.
The multiple array of notches (13) are provided not only on the side seal portion (2) but also in the region protruding inward from the side seal portion (2), and the protrusion length (a) of the multiple array notches in this case is the side surface of the pouch at both ends. It is a position protruding 0.5 mm or more from the seal part (2), the multi-array notch region vertical width (b) is 10 mm or more, and one notch length (c) is in the range of 0.1 mm to 5 mm. .
多数配列のノッチを構成する複数の一の字状の傷は金属刃による加圧やレーザー加工等の周知の方法で設けることが出来る。
一つのノッチすなわち一の字状の傷の長さが5mmを超える場合には、このような多数配列ノッチを設けた箇所のヒートシールの耐久性確保と内容物の浸透防止の点から、ヒートシール部の幅を広くする必要があり、また多数配列ノッチの外観も悪くなるとともに、加工部のざらつきが大きいため、包装工程や流通段階で易開封加工部から破袋する可能性がある。一方、0.1mm未満の傷を設けることは、刃物による機械的な加工限界を超えるものとなり、加工精度の管理は困難である。
A plurality of one-letter-shaped scratches constituting a plurality of notches can be provided by a known method such as pressing with a metal blade or laser processing.
If the length of a single notch, i.e., a single-shaped flaw, exceeds 5 mm, the heat seal is used to ensure the durability of the heat seal at the location where such multiple array notches are provided and to prevent the penetration of the contents. It is necessary to widen the width of the portion, and the appearance of the multi-array notch is also deteriorated, and the roughness of the processed portion is large, so that the bag may be broken from the easy-open processing portion in the packaging process or the distribution stage. On the other hand, providing a scratch of less than 0.1 mm exceeds the mechanical processing limit of the blade, and it is difficult to manage the processing accuracy.
<実施例1>
図1(A)に示した形状で幅(d)250mm、高さ(e)160mm、底部折り返し高さ(f)50mmの寸法のパウチを作成した。
パウチを構成する表裏の積層体としては、易カット延伸PETフィルム(12μm)/印刷層/接着剤層/易カットシーラント層(60μm)からなる構成とした。
易カットシーラント層はラミネート層(C4−LLDPE)(20μm)/中間層(C4+COC25%)(20μm)/シール層(C4−LLDPE)(20μm)からなる構成とした。
<Example 1>
A pouch having a shape shown in FIG. 1A and having a width (d) of 250 mm, a height (e) of 160 mm, and a bottom folded height (f) of 50 mm was prepared.
The laminate of the front and back constituting the pouch was composed of an easily cut stretched PET film (12 μm) / printing layer / adhesive layer / easy cut sealant layer (60 μm).
The easy-cut sealant layer was composed of a laminate layer (C4-LLDPE) (20 μm) / intermediate layer (C4 + COC 25%) (20 μm) / seal layer (C4-LLDPE) (20 μm).
上記の積層体を用いてパウチを作成して以下の試験を行なった。
1.易カットシーラント層の延伸方向(MD)延伸方向に直角方向(TD)の引裂き強度2.パウチを開封して引裂いたときの表裏積層体の切断端面のズレ(表裏の引裂きズレ)3.パウチを開封して引裂いたときのMD方向とTD方向の引裂き強度
4.パウチに水900mlを封入して高さ1mから落下させた時の破袋回数(落下強度 n=6)
結果は表2、表3に示した。
A pouch was prepared using the above laminate and the following tests were performed.
1. 1. Tear strength in the direction perpendicular to the stretch direction (MD) stretch direction of the easy-cut sealant layer (TD) 2. Displacement of the cut end surface of the front and back laminate when the pouch is opened and torn (front and back tearing displacement) 3. Tear strength in MD and TD direction when the pouch is opened and torn Number of bag breaks when 900 ml of water is sealed in a pouch and dropped from a height of 1 m (drop strength n = 6)
The results are shown in Tables 2 and 3.
<実施例2>
易カットシーラント層の中間層の配合に重量比で25%のC6−LLDPEを加えたほかは実施例1と同様にしてパウチを作成し試験を行なった。
結果は表2、表3に示した。
<Example 2>
A pouch was prepared and tested in the same manner as in Example 1 except that 25% by weight of C6-LLDPE was added to the blend of the intermediate layer of the easy-cut sealant layer.
The results are shown in Tables 2 and 3.
<実施例3>
易カットシーラント層の中間層の配合に重量比で25%のC8−LLDPEを加えたほかは実施例1と同様にしてパウチを作成し試験を行なった。
結果は表2、表3に示した。
<Example 3>
A pouch was prepared and tested in the same manner as in Example 1 except that 25% by weight of C8-LLDPE was added to the composition of the intermediate layer of the easy-cut sealant layer.
The results are shown in Tables 2 and 3.
<比較例1>
易カット延伸PETフィルムをPETフィルムに代えて、易カットシーラント層をC4−LLDPEとしたほかは実施例1と同様にしてパウチを作成し試験を行なった。
結果は表2、表3に示した。
<Comparative Example 1>
A pouch was prepared and tested in the same manner as in Example 1 except that the easy-cut stretched PET film was replaced with a PET film and the easy-cut sealant layer was C4-LLDPE.
The results are shown in Tables 2 and 3.
<比較例2>
易カットシーラント層をC4−LLDPEとしたほかは実施例1と同様にしてパウチを作成し試験を行なった。
結果は表2、表3に示した。
<Comparative example 2>
A pouch was prepared and tested in the same manner as in Example 1 except that the easy-cut sealant layer was C4-LLDPE.
The results are shown in Tables 2 and 3.
<比較例3>
易カット延伸PETフィルムをPETフィルムに代えたほかは実施例1と同様にしてパウチを作成し試験を行なった。
結果は表2、表3に示した。
A pouch was prepared and tested in the same manner as in Example 1 except that the easy-cut stretched PET film was replaced with a PET film.
The results are shown in Tables 2 and 3.
以上の結果より、一般にシーラントとして用いられているC4−LLDPE層よりも本発明の構成に用いられた易カットシーラントの方が直線カット性と引裂き強度において優れていることが分かる。
また、この易カットシーラントと易カット延伸PETフィルムをカットの方向を揃えて組み合わせることで包装体にして開封した場合、直線カット性と易カット性の効果が高め
られることが分かった。
また、落下強度の結果から実施例1のLLDPEがC4のみの場合よりもC6あるいはC8を加えた実施例2,3の場合の方が衝撃に対する強度は高いことが分かった。
From the above results, it can be seen that the easy-cut sealant used in the configuration of the present invention is superior in linear cut property and tear strength than the C4-LLDPE layer generally used as a sealant.
Moreover, when this easy-cut sealant and the easy-cut stretched PET film were combined in the same cut direction and opened as a package, it was found that the effects of straight-cut property and easy-cut property were enhanced.
Moreover, it turned out that the intensity | strength with respect to an impact is higher in the case of Example 2, 3 which added C6 or C8 rather than the case where LLDPE of Example 1 is only C4 from the result of drop strength.
<実施例4>
図3(A)に示した形状で幅(d)250mm、高さ(e)160mm、底部折り返し高さ(f)50mmの寸法のパウチを作成した。
パウチを構成する表裏の積層体としては、易カット延伸PETフィルム(12μm)/印刷層/接着剤層/易カットシーラント層(60μm)からなる構成とした。
易カットシーラント層はラミネート層(C4−LLDPE)(20μm)/中間層(C4+COC25%)(20μm)/シール層(C4−LLDPE)(20μm)からなる構成とした。
<Example 4>
A pouch having the shape shown in FIG. 3A and having a width (d) of 250 mm, a height (e) of 160 mm, and a bottom folded height (f) of 50 mm was produced.
The laminate of the front and back constituting the pouch was composed of an easily cut stretched PET film (12 μm) / printing layer / adhesive layer / easy cut sealant layer (60 μm).
The easy-cut sealant layer was composed of a laminate layer (C4-LLDPE) (20 μm) / intermediate layer (C4 + COC 25%) (20 μm) / seal layer (C4-LLDPE) (20 μm).
上記の積層体を用いてパウチを作成して長さ1mmの一の字状の傷が千鳥足に配列された多数配列のノッチを加工した。こうして得られたパウチに家庭用粉末洗剤を充填し開口部をヒートシールした。
多数配列のノッチの加工位置は、パウチの側面シール部から内側にはみ出した寸法をa(mm)、配列の領域上下幅をb(mm)とした場合に以下の6種類の形状で行い、このパウチを用いて引裂き性のモニター評価をおこなった。評価項目は開封時の切り取りの際引っ掛かった人数(各10名中)とし、結果は表4に示した。
形状1:a=0mm、b=15mm
形状2:a=0.3mm、b=15mm
形状3:a=0.5mm、b=15mm
形状4:a=3mm、b=3mm
形状5:a=3mm、b=8mm
形状6:a=3mm、b=10mm
The processing positions of the multiple arrays of notches are the following 6 types of shapes when the dimension protruding inward from the side seal part of the pouch is a (mm) and the vertical width of the array area is b (mm). A tear evaluation was performed using a pouch. The evaluation item was the number of people caught in the cut at the time of opening (out of 10 people), and the results are shown in Table 4.
Shape 1: a = 0mm, b = 15mm
Shape 2: a = 0.3mm, b = 15mm
Shape 3: a = 0.5mm, b = 15mm
Shape 4: a = 3mm, b = 3mm
Shape 5: a = 3 mm, b = 8 mm
Shape 6: a = 3 mm, b = 10 mm
この結果、本発明の易カット性パウチの易カット性を発現させるためには、多数配列のノッチの加工位置は、パウチの側面シール部から内側にはみ出した寸法を0.5mm以上、配列の領域上下幅を10mm以上とすればよいことが分かった。 As a result, in order to express the easy-cut property of the easy-cut pouch of the present invention, the processing positions of the multiple array of notches have a dimension that protrudes inward from the side seal portion of the pouch and the region of the array. It was found that the vertical width should be 10 mm or more.
本発明の容器はトイレタリー製品、液体洗剤、柔軟剤、ハンドソープなど以外にも、詰め替えの必要な用途の容器として広く用いることが出来る。 The container of the present invention can be widely used as a container for applications requiring refilling in addition to toiletries, liquid detergents, softeners, hand soaps, and the like.
a…多数配列ノッチはみ出し長さ
b…多数配列ノッチ領域上下幅
c…一つのノッチ長さ
d…パウチ幅
e…パウチ高さ
f…底折り返し高さ
1…積層体
2…側面シール部
3…底部折り曲げ線
4…底部シール部
5…延伸フィルム
6…シーラント層
7…印刷インキ層
8…接着剤層
9…ラミネート層
10…中間層
11…シール層
12…ノッチ
13…多数配列のノッチ
a ... multiple array notch protrusion length b ... multiple array notch region vertical width c ... one notch length d ... pouch width e ... pouch height f ...
Claims (3)
前記延伸フィルムがMD方向に直線状に引裂かれるフィルムであり、
開封部の幅が10cmから25cmである該延伸フィルムの引裂き方向のパウチ両端にのみ、複数本の一の字状の傷が設けられており、かつ、これら複数本の一の字状の傷が千鳥足に配列されており、
これら複数本の一の字状の傷で構成されるノッチをノッチ領域が上下に幅を有して形成している開封開始部が設けられており、
該シーラント層が、内側のラミネート層、中間層、及び外側のシール層の三層構造を有しており、内側のラミネート層としてC4−LLDPEで表されるリニア低密度ポリエチレン、中間層としてC4−LLDPE及びCOCで表される環状オレフィンコーポリマー、外側のシール層としてC4−LLDPEからなり、
ラミネート層/中間層/シール層の層比がそれぞれ0.5〜2/1〜5/0.5〜2の範囲であり、
多数配列のノッチはパウチ両端のシール部から0.5mm以上はみ出した位置の幅10mm以上の領域に配列されてなる
ことを特徴とする易カット性パウチ。 A laminate formed by laminating at least a sealant layer and a stretched film is used as a front-side film and a back-side film, and the front-side film and the back-side film are overlapped so that the stretched film is located outside, and the end is heat-sealed. The pouch is over 800g
The stretched film is a film that is torn linearly in the MD direction,
A plurality of one-letter-shaped scratches are provided only on both ends of the pouch in the tear direction of the stretched film having a width of the opening portion of 10 to 25 cm, and the plurality of one-letter-shaped scratches are provided. It is arranged in a staggered foot,
An opening start portion is provided in which a notch region is formed with a width above and below a notch composed of a plurality of one-letter-shaped scratches,
The sealant layer has a three-layer structure of an inner laminate layer, an intermediate layer, and an outer seal layer, and a linear low density polyethylene represented by C4-LLDPE as an inner laminate layer, and C4- as an intermediate layer. A cyclic olefin copolymer represented by LLDPE and COC, and C4-LLDPE as an outer sealing layer,
Range der laminate layer / intermediate layer / layer ratio of the seal layer, respectively 0.5 to 2 / 1-5 / 0.5-2 is,
An easy-cut pouch characterized in that the multiple notches are arranged in a region having a width of 10 mm or more at a position protruding 0.5 mm or more from the seal portion at both ends of the pouch.